Search Documents

By J. G. Y. Chow, S. B. McRickard

The tensi1e properties of Ferrovac iron have been studied from 4° to 300°K. The stress required for macroscopic yielding was found to he constant below approximately 50°K. The effect of mechanical twinning on this low -temperature stress plateau was investigated. The onset of twinning occurs in this iron between 130° and 150°K and depending on its previous thermal history the twinning-stress curue may drop below or remain above the vield-stress curves as the temperature is lowered. Twinning has been shown to initiate slip in quenclzed iron at low temperatures. In no instances, however, did the onset of twinning alter the continuity of the yield stress -tempwature curve. Our data shows that carbon inhibits twinning and slip at low tem-peratures. This observation nay be used to explain the ductile-to-brittle transition in iron. The effect of fast neutron irradiation on yielding and embrittlement in iron and Fe-C alloys is offered as supporting evidence for this viewpoint. THE mode of yielding in iron at low temperatures was studied in an attempt to find an expression based on a single mechanism to describe the thermal dependence of the yield stress of iron. There are two types of inflections observed in the variation of the yield stress with temperature in iron and Fe-C alloys. The first is associated with ductile behavior and consists of a region extending 50" to 100°K above absolute zero in which the yield stress is independent of temperature. The second is observed in more brittle materials such as Fe-C alloys and irradiated iron and consists of an abrupt discontinuity in the yield curve as the temperature is lowered through a ductile-to-brittle transition point. The temperature dependence of the yield stress for iron with four grain diameters as found in this study is shown in Fig. 1. To varying degrees all the curves appear to flatten or approach an asymptotic value as the temperature is lowered below 50°K. Several other investigators1,2 have observed a plateau in the yield stress of iron and steel at low temperatures and in 1956 Louat3 presented a theory which contained an explanation for this behavior. In a subsequent exchange with Erickson and Low4'5 who attributed the plateau to the onset of mechanical twinning Louat8 showed that twinning first occurs in iron and steel tested in tension at temperatures as high as 140°K which is well above the observed plateau in yield stress. Furthermore he pointed out that both twinning and slip are basically dislocation processes and that with modified parameters his original theory still applied when deformation is initiated by twinning. Variables which affect the ductile-to-brittle transition in iron are test temperature, strain rate, composition and grain size.7 LOW,8 Hahn et al.,9 and Hull10 have provided evidence which links brittle fracture at a given temperature with the specimen grain size and the onset of twinning. In fact, Hull equates the brittle fracture stress to the twinning stress. On the other hand brittle fracture has been observed in the absence of twinning and priestnerl1 has given a fracture criterion which is valid whether or not fracture is preceded by extensive twinning. The data presented here clarify the role of twinning in the low-temperature deformation of iron. Strong evidence is given that the amount and distribution of interstitial impurities such as carbon are of

Jan 1, 1965

By J. Szekely

The paper discusses simultaneous heat conduction and diffusion. These problems may arise in slag-metal kinetics and in connection with rapid heating or cooling of specimens. A mathematical formulation is given and it is shown that the transients due to either the variability of the diffusion coefficient with temperature, or thermal diffusion, are unlikely to be important for molten or solid metals and slags. The negligibility of these effects is due to the large values of the ratio thermal diffu-sivity/molecular diffusivity. In many problems relating to transport-controlled metallurgical kinetics the diffusion process is accompanied by the transfer of heat; large-scale metal refining or metal reduction may be quoted as examples. It has been shown that due to turbulent mixing in these systems the relevant transport phe- nomena are best described in terms of "surface renewal models" which require the solution of the unsteady-state diffusion equation.1-1 Problems involving simultaneous diffusion and heat conduction are also encountered in the laboratory in connection with rapid heating or cooling of specimens. The effect of variable temperature on diffusion may be twofold: a) in the absence of "cross effects" the problem, due to variable temperature, is that of diffusion with a variable diffusion coefficient; b) if the Soret Effect is nonzero, thermal diffusion must also be taken into account in the formulation. Although information is available on thermal-diffusion transients in a steady-temperature gradient,4'5 little work has been done on the effect of unsteady temperatures on either the diffusion coefficient or on thermal diffusion.' In the following a formulation is given and solutions presented with a view of examining the areas where these effects may be important.

Jan 1, 1965

By H. C. Burghard, F. R. Brotzen

Experiments were performed to determine the effects of mechanical vibrations on ordering in CuAu. The effects of 5, 10, and 15 kc vibrations were investigated over a range of ordering temperatures of 280° to 360°C. A decrease in the rate of ordering was observed at all frequencies and ordering temperatures. THE effects of mechanical vibrations on certain solid-state reactions have been noted by several investigators. In 1930, Mahoux' reported a substantial increase in the case depth of a steel sample nitrided under the influence of mechanical vibrations over that of an unvibrated sample. Similarly, an accelerating effect of vibrations on the diffusion of chromium in steel was noted. Guillet, in the same year, confirmed the results of Mahoux. More recently Schenck and schmidtmann3 studied the effects of low-frequency, alternating loads on the diffusion of carbon in steel. The results of their experiments, conducted at 500 cycles per min and large strain, (0.2 pct), indicated an acceleration of the process. These workers also reported an increase in case depth of a sample vibrated at 430 kc during a carburizing treatment. Effects of high-frequency vibrations on solid-state reactions have also been investigated by Gudzoff and Gavze6 and Fairbanks and Dewez.7 The former reported an acceleration of the age-hardening process in aluminum alloys. The latter noted changes in the structure and mechanical properties of steel annealed under the influence of vibrations. On the other hand, Altenburg4 and Ehringer5 have given some theoretical reasons and experimental evidence as to the improbability of any effect of vibrations on diffusion. Comprehensive surveys of the effects of vibrations on metallurgical reactions are given by Hiedemann' and Bergmann.9 None of the above investigations led to a physical description of the effects of mechanical vibrations on solid-state reactions. In the present study an attempt was made to gain an understanding of the influence of vibrations on nucleation and diffusion. The order-disorder transformation was chosen for investigation since its mechanism has been extensively discussed in the literature. Moreover, the progress of the transformation may be easily followed by observation of electrical resistance changes. EXPERIMENTAL PROCEDURE The specimens used for the experimental observation of ordering rates were prepared from 50 at. pct Cu-Au alloy wire.* Each specimen consisted of a 0.02-in. diam wire approximately 10 in. long to which two copper potential leads were silver soldered, 2 1/2 in. apart, near one end of the wire. A 1/8-in. diam by 1/4-in. long steel stub was silver soldered

Jan 1, 1960

By J. F. Pashak, T. E. Leontis

The effects of zirconium on the properties of sand cast Mg-rare earth metal alloys were discussed in detail in an earlier publication.' It was shown that a significant improvement in strength properties at temperatures up to 400°F resulted from the zirconium addition. In general, the properties of cast Mg-Didymium-Zr alloys were superior to the corresponding alloys containing Mischmetal and the optimum rare-earth level was approAmately 3 pet. Jessup, Emley, and Fisher have also shown the advantages of didymium in Mg-rare earth-Zr alloys, 2

Jan 1, 1961

By R. Steinitz, J. L. Orehotsky

An analysis was made of the influence of floating molten zone traversal on the purification of tungsten rods and the effect of this purification on the brittle -to-ductile transition temperature. The major impurities detectable in the original rods, i.e., molybdenum and oxygen, were reduced by zone refining from 30 to 3 Ppm. Changes in the trace amounts of other impurities could not be quantitatively determined since they were below the limit of detection. Tensile tests on 3-mil wires, drawn from these rods and recrystallized to 17,000 grains per sq mm, showed a transition temperature of 60°C for the zone Purified and 175°C for the original material. 1 HE brittle-to-ductile transition temperature is manifest mainly in the bee metals, iron,' molybdenum, chromium,3 tungsten,4 and niobium. Since many of these metals cannot be fabricated at room temperature in a commercially pure annealed poly-crystalline state, a considerable amount of work has been done on evaluating the influence of purification on the transition temperature in order to determine indirectly whether the fabricability of these metals can be improved by removing impurities. Smith and Rutherford8 showed that the transition temperature of iron is lowered significantly by zone purification. Working with chromium, Edwards, Nish, and wain7 found also that purification appreciably lowered the transition temperature. A similar evaluation has so far not been reported for tungsten, probably because of the difficulties in obtaining tungsten in a purified polycrystalline state. carlson8 and, more recently, schadler9 have purified tungsten rods by floating zone traversal, but after zone traversal, their rods were single crystals. To obtain high-purity polycrystalline tungsten, a technique has to be round for transforming the zone-purified single crystal material into a suitable polycrystalline structure. The purpose of this investigation was to obtain zone-purified tungsten in a suitable polycrystalline state and then to evaluate the effect of zone purification on the transition temperature.

Jan 1, 1962

By B. Ramaswami, Y. Nakada, R. Schaefer

EARLY investigations1 of the tensile properties of fcc single crystals did not reveal the easy glide region of crystals with axial orientations inside the standard stereographic triangle. With the production of high-purity metal, a region of easy glide became known1 Consequently, modern work of fcc single crystals ordinarily uses high-purity metal. In order to determine whether further purification of aluminum beyond 99.992 pct purity would result in significant alteration of the tensile properties of single-crystal specimens, metal was zone-refined and crystals grown from the purified material were compared to crystals grown from the original material. Some similar studies were made of gold and silver crystals. Aluminum. The material to be zone-refined was cast into bars 1/4 by 1/2 by 8 in. A zone, approximately 1-1/2 in. in length, was passed over each bar eighteen times at a rate of 6 in. per hr. Melting and stirring were carried out by an induction heater under a vacuum of approximately 10"5 mm Hg, the metal being held in a graphite container. he last 3 in. of each processed bar were then cut off and discarded. No quantitative determination of purity was made, but the effectiveness of the zone refining was tested by a method first suggested by Walton, Tiller, Rutter, and winegard3 depending on the relation between cell structure and impurity content. Rutter and Chalmers4 have shown that a cellular substructure is associated with the presence of impurities during solidificatibn, and have shown how solute rejection at the freezing interface can lead to such an association. Thus the observation of cells gives evidence of impurities being present. To look for cells, the last quarter of a zone-refined bar was cut off, remelted, and grown rapidly into a single crystal. It was then heavily electropolished and thermally etched.~ Cells were revealed by the presence of many parallel rows of etch pits. The same process was carried out with material from the first half of the bar, but no cells were detected. These observations give evidence that a significant amount of impurity material was moved to the "dirty" end of the zone-refined bars. Further indication of purification was obtained from recrystallization experiments. It was found that, after cold rolling to a 97 pct reduction in thickness, the material from the pure end of the bar re-crystallized at room temperature, but the material from the "dirty" end did not. Other investigators6 have previously reported that zone-refined aluminum recrystallized at room temperature. The purified material was cast into 1/4 by 1/4 in. bars, and seeded crystals were grown in a (100) orientation and in a single slip orientation where the Schmid factor is m =2. The crystals were then cut to the desired length, annealed for 24 hr at 610°C, furnace-cooled, and etched in Tucker's etch. The crystals were tested in a floor-model Instron machine, using a gage length of 4 in. and a strain rate of 1/2 pct per min. The resulting curves are shown in Fig. 1. It is seen that the differences between the curves for zone-refined and original-purity materials are small. These differences are within the scatter observed for crystals of the original purity. In particular, the zone refining does not significantly affect the onset of the different "stages" of the curves.

Jan 1, 1964

By D. I. Bardos, A. M. Bardos, Paul A. Beck

The approximate effective silicon radii in ternary Laves phase alloys with transition elements and silicon were found to range between 1.16 and 1.21A, i.e., considerably smaller than the atomic radius calculated for elemental silicon. The atomic radii were found to increase with the size of the transition element atoms in the structure. It has been noted by Aronsson1 that silicon in solid solution in iron, cobalt, and nickel has an effective CN 12 atomic radius of approximately 1.20Å, a value very much smaller than the CN 12 radius of 1.34Å derived from the interatomic distances in elemental silicon.7 The unusually short metal-silicon interatomic distances in transition element monosilicides and disilicides have been also pointed out by various investigators.1 A similar tendency was observed by Nevitt in Cr3O type silicides.2 Recent work on Laves phases in ternary systems of silicon with transition elements4"8 suggested that extensive Laves phase fields may occur in such systems.8 It has been pointed out by Laves7 that the MgCu2 and MgZn2 type structures lend themselves particularly well for the determination of the effective radii of the component atoms. In these AB2 phases the B atoms are arranged in close packed straight lines, and their distances are related in a simple manner to the lattice parameters.8 The present work was undertaken in order to find out whether or not the B transition element in such AB2 Laves phases can be replaced to an appreciable extent by silicon. In cases where extensive substitution proves to be possible, the "average atomic radius for the B site" at various silicon contents was to be determined, and the effective atomic radius of silicon calculated by extrapolation to complete replacement of the B component by silicon. The following ternary systems were studied: Ti-Mn-Si, Ti-Fe-Si, V-Co-Si, V-Ni-Si, Nb-Fe-Si, Nb-Co-Si, Ta-Fe-Si, Ta-Co-Si, and Mo-Fe-Si. In all of these alloy systems, the Laves phase solid solutions were found to extend over a considerable range of silicon content. As previously reported,4"8 in the V-Co-Si, V-Ni-Si, and Mo-Fe-Si ternary systems Laves phases do occur, even though there are no corresponding binary Laves phases. In stabilizing the Laves phase, silicon acts as if it were decreasing the effective electron concentration of the alloy.8 A more detailed study of the boundaries of the Laves phases in the V-Co-Si and V-Ni-Si systems has been made and will be published elsewhere. In both cases, the elongated Laves phase fields extend parallel to the B-Si side of the composition triangle, clearly showing that silicon is substituting for cobalt, respectively, nickel over a wide range of compositions. The binary Laves phases NbCo2 and TaCo2 have the cubic MgCu2-type structure. It was found that, in both ternary systems with silicon, again the MgZn2-type hexagonal Laves phase is stabilized and that this phase extends to high-silicon contents. In each ternary system at least three Laves phase alloys of the composition A(B1_xSix)2 were used, x here denoting the fractional substitution of the B-transition element atoms by silicon. The alloys, listed in Table I, were prepared by arc melting in argon. Each specimen was water quenched after a homogenizing anneal of 3 days at 110(FC, except for the Mo-Fe-Si alloys, which were annealed at 1200°C. Metallographic examination showed that most of the homogenized alloys consisted of a single phase, although some had minor amounts of a second phase, as shown in Table I. X-ray diffraction patterns were prepared using an asymmetrical focusing camera of large resolution and Fe Ka radiation. The patterns were indexed, and the lattice parameters of the hexagonal Laves phases were determined from the available diffraction lines of highest indices: (213), (205), and (313). The lat-

Jan 1, 1963

By W. Hume-Rothery

IN recent interesting papers,1,2 Bardos et al. have described ternary Laves phases of the type A2(BsSi) and A4(B5Si3) where A = titanium vanadium, niobium, and so forth, and B = manganese, iron, cobalt, or nickel; other more complex formulae have also been established. In these phases, silicon plays the part of the smaller B atom of a Laves phase AB2, and the interatomic distances show that the effec- tive silicon radii lie between 1.16 and 1.21Å, and are thus very much smaller than the metallic radius of silicon for CN = 12. It does not seem to have been pointed out that these small atomic radii are almost the sape as the normal covalent radius of silicon (1.174Å). If, therefore, silicon acts as an acceptor of electrons as suggested by Bardos et al.,1 it appears to do so, not by the building up of a negatively charged silicon ion which would be large, but by the formation of what are very nearly or may be actually normal covalent bonds. Since a covalent bond contains two electrons, its formation would reduce the number of electrons available for bonding in other parts of the structure, and in this way the effect of silicon in stabilizing the o phase at high electron concentrations might be understood.

Jan 1, 1965

By H. C. Fiedler

The development of cube-on-edge secondary re crystallization texture in Si-Fe strip depends upon the ability of inclusions, such as manganese sulfide, to restrain nomal grain gvowth. The ability of inclusions to perform this function is shown to depend upon their size and distribution. The desired uniform dispersion of many small inclusions is obtained by controlling the cooling rate from above the solution tempmature of the inclusions or, alternatively, by drastic 'quenching from above the solution temperature followed by heat treating at a lower temperature. The development of the cube-on-edge secondary recrystallization texture in Si-Fe strip depends upon both establishing the proper primary recrystallization texture and having inclusions to restrain normal grain growth. It has been suggested that the first requirement is met with a texture which, though weak, is near (110)[001]. A mechanism for secondary recrystallization originally proposed by ielsen' is consistent with the presence of this primary texture. It is visualized that a secondary grain appears where two adjacent grains happen to be sufficiently similar in orientation to be capable of behaving as a single large grain. This pair of grains will grow at the expense of its smaller neighbors as a consequence of its having lower grain boundary free energy. Other explanations of the origin of the secondary recrystallization texture have been offered,' and it can be concluded that the mechanism is not fully understood. Nevertheless, it is apparent that operationally the necessary primary recrystallization texture is obtained simply by interposing an anneal during the cold reduction to final gage. The role of inclusions in the development of the secondary recrystallization texture has been demonstrated by May and Turnbull4 in a comparison of a high-purity heat and a heat containing manganese sulfide. They showed that the driving force for secondary recrystallization is inversely proportional to the diameter of the matrix grains and that the function of the inclusions is to maintain a small matrix grain size. Other inclusions, such as various sul- fides,')' silicon nitride,8 and vanadium nitride,' titanium carbide,'' and vanadium carbide," have been shown to be effective in promoting secondary recrystallization to the cube-on-edge texture. There is also evidence that silica inclusions in Si-Fe strip made by powder-metallurgy techniques perform this function.' This report is concerned with the second of the two requirements for secondary recrystallization, namely the importance of the metallurgical control of the size and therefore number of inclusions. While the concepts involved are simple, they are fundamental to the making of this material. EXPERIMENTAL PROCEDURE A heat containing 3.27 pct Si, 0.026 pct S, 0.06 pct Mn, and 0.004 pct C was made in an air induction furnace from electrolytic iron, 98 pct ferro-silicon, electrolytic manganese, and iron sulfide. The heat was divided between graphite and baked-sand molds with a cavity 2-5/8 by 5 in. and with walls 2-3/4 in. thick. Slabs, 1 in. thick and 2-5/8 by 5 in., were cut from the ingots and hot-rolled either in the as-cast condition or after one of the heat treatments described later. After pickling, the 80- to 100-mil-thick hot-rolled band was, unless otherwise noted, heat-treated for 5 min at 900°C before being cold-rolled to 25 mils. After a heat treatment of 1 to 3 min at 860°C, the strip was cold-rolled to 12 mils, the final thickness. The percent cube-on-edge texture was determined by dividing the maximum torque as averaged from four samples by the maximum torque of a 3-1/4 pct Si-Fe single crystal having the (110) plane in the plane of the sample. The torque measurements were made in a field of 1000 oe on 1-in.-diam disks. RESULTS AND DISCUSSION The importance of the thermal history of the ingot is evident in Fig. 1 from the appearance of strips heat-treated in a temperature gradient. The sample

Jan 1, 1964

By E. Teghtsoonian, A. R. Causey

THE fact that the surface plays an important role in the plastic deformation of a single crystal has been demonstrated by several investigators. The surface conditions have been altered using oxide films,1'2 alloyed metal layers,3, 4 deposited metal films,' and polycrystalline layers.677° The resulting effects on the initiation and subsequent plastic deformation have been investigated extensively except for the case of a single crystal surrounded by a polycrystalline layer of the same material. The purpose of this paper is to describe an investigation of the effect of a polycrystalline surface layer on the yield stress, the critical resolved shear stress, and the work-hardening slope of tin single crystals. The tin single crystals used in this study were grown from the melt using material having an initial purity of approximately 99.999 + pet with lead and iron the major impurities. Fig. 1 shows the orientation of the (110)[001] slip system with respect to the crystal surfaces. The crystals had a 1/4 by 1/4 in. cross section and a gage length of 2 in. The polycrystalline surface layer was produced by abrading the single-crystal specimens with emery paper. Fig. 2 shows the broken Debye rings obtained from the deformed surface. The thickness of the layer was controlled by the number of passes on different grades of paper and was determined by electropolishing in dilute HC1, until the grains produced by the abrasion had all been removed. Metal-lographic examination showed that the grain size varied with depth, increasing from 10 µ right at the surface to 40 µ in the interior of the layer. The yield stress, critical resolved shear stress,

Jan 1, 1965

By Nicholas J. Grant, Raymond E. Cairns

A high-purity chromium, made by solid-state extrusion, and a series of molten, extruded, dilute alloys containing carbon, oxygen, nitrogen, and sulfur were studied to establish the effects of composition, cooling rate, grain size, strain rate, and prior strain on the transition temperature for brittle THE transition from ductile to brittle fracture with decreasing temperature remains of extreme interest especially among the refractory metals, such as tungsten, molybdenum, and chromium, which have relatively high transition temperatures. Fracture, yield stress, and hardness. Tension tests at a strain rate of 0.015 per min were generally utilized. Results are interpreted in terms of the quantity of each element retained in solid solution. Of these elements, chromium has been studied the least, but deserves additional attention because of its superior oxidation resistance for high-temperature use. In the past, impurity elements which have received attention are carbon, nitrogen, oxygen, and sulfur;'-' of these, nitrogen has usually been considered to be the most detrimental. Unfortunately, because of different levels of both specific and total impurity content, and because of the many different test and evaluation techniques used, a clear, definitive picture of brittle fracture in chromium has not been forthcoming. However, many

Jan 1, 1964

By J. B. Coher, M. B. Bever

COLD work destroys long-range order, as was first observed by Dehlinger and Graf.1 Dahl2 showed that the mechanical disordering caused by cold work produces changes in those properties that are affected by long-range order. The existence of order has a marked effect on tile manner in which an alloy deforms and therefore on its mechanical properties.L' The relation between order and deformation behavior however, is only beginning to be understood. Seemann and G1ander4 suggested that cold work reduces an ordered alloy to a kind of gruel of antiphase domains. According to Cottrell,5 superdis-locations and pairs of dislocations in a slip plane connected by a strip of anti-phase domain boundary provide deformation mechanisms which do not change the state of order. In general, however, slip may be expected to produce new domain boundaries and destroy order if dislocations move on intersecting planes or cut through existing domain boundaries. The yield strength of an ordered alloy may pass through a maximum with decreasing domain size.5"7 The reduction of domain size resulting from cold work may, therefore, lead to a maximum in strength properties. Flinn8 suggests that dislocations can climb by short-range diffusion during deformation and thus can generate domain boundaries not only on slip planes, but also on other planes which will be those with the lowest domain-boundary energy. It has long been known that the rate of strain hardening of an alloy in the ordered state is larger than in the disordered state.3'9 Also the slip bands in ordered CU3, AU10 and Ni3Mn" are finer than in the disordered alloys. The stress which causes initial yielding in Cu,Au passes through a maximum with decreasing domain size.6'12 A maximum has also been observed in the hardness of ordered Ni3Mn as a function of strain.' These observations suggest, but do not prove, that domain size reduction occurs during deformation. According to Fisher13 slip destroys short-range order and thus the strength of an alloy is related to the degree of short-range order present. Rudman and Averbach14 and Averbach et a1.,15 demonstrated that cold work reduces short-range order in copper-gold and gold-silver alloys. Destruction of long-range and short-range order by cold work implies slip on an appreciable fraction of planes. Yielding of an alloy in which short-range order exists or antiphase domain boundaries are present should be discontinuous because the first dislocations moving across the slip plane meet with the largest resistance.5 Such discontinuous yielding has been observed in CU3AU6,16 and Cuzn.l7 This phenomenon, however, can also be explained by mechanisms not involving order.b The published investigations of the effects of cold work on alloys with long-range or short-range order have not been covered thoroughly in reviews of order-disorder phenomena. These investigations, therefore, will be listed here. They have been concerned with strength properties> 2,3,6,8,9,12,16-21 electrical resistivity,2,4,18,19,21-26: thermoelectric power, magnetic properties,2,18,21,26 and X-ray strain'1,2,14,15,27,28 The slip systems and the appearance of the microstructure after deformation in ordered and disordered alloys have also been investigated. 6.10.ll,l7,23,29,30 The alloys used in these investigations were copper-gold. 1-4,6,9,10,14,16,18 23-26,28,29 copper-zinc. L7. 19. 20,30 nickel-manganese,2 11,21 iron-aluminum. iron-nickel,' copper palladium,4,18,22 gold-silver.4,18,22 and palladium-silver-copper.4 In the work reported here. the changes in properties of polycrystalline Cu3Au were investigated as functions of strain in wire drawing and rolling. Specimens were heat treated before deformation

Jan 1, 1961

By Harry A. Lipsitt, Douglas Y. Wang

A fatigue study in completely reversed axial tension-compression has been perforried on high-purity titanium and on three high-purity alloys of titanium. The alloys each contain approxi7nately 0.75 at. pct of a single interstitial element; carbon, nitrogen, and oxygen, respectivley. The results corroborate a previously published theory which proposed that strain aging under alternating stress was responsible for the fatigue limit behavior of certain alloys. The present data indicate that in these alloys an increasing strain-talline aging effect under alternating stress is provided by oxygen, carbon, and nitrogen, respectively. CURRENT research on the nature of the fatigue limit in metals suggests that the presence of a fatigue limit in metallic materials is a manifestation of strain aging that occurs under alternating stress.lm5 A comprehensive theoretical model based on the above hypothesis has been developed to explain the existence of a fatigue limit.' This model also provides increased insight into several other fatigue phenomena as under stressing, overstressing, and coaxing effects. The theory, as well, provides equal understanding for those cases where no real fatigue limit is observed. Briefly, this theory assumes that the S-N curve for a pure metal is a smooth function of the applied stress, and the effect of adding an element that is soluble (or forms a precipitate) in the pure metal is simply to shift the S-N curve to the right. If the added element confers the power to strain age, the result is a further shift of the S-N curve, this time upward and to the right. Since strain aging is not expected to be a strong function of stress, and since damage per cycle is known to be quite stress dependent, it is to be expected that there will be some limiting lower stress at which the strengthening due to strain aging will balance the damage due to crack propagation. This stress is the fatigue limit. The position of the fatigue-limit knee was thought to be a function of the magnitude of the strain-aging effect on both the finite and infinite life portions of the S-N curve. Although the strain aging hypothesis seems to be reasonably valid for bcc materials,2'6 it needed to be tested for both fcc and cph metals. This report is the first of a series concerning the fatigue-limit behavior of titanium with varying amounts of the interstitial solutes (C, N,, and 4) that are known to cause static strain aging in titanium. Yield-point effects have been reported for polycrys-talline high-purity titanium alloys containing either carbon, nitrogen, or oxygen.7'9 These effects were observed at testing temperatures in the range 100 to 300'. In addition yield-point and strain-aging effects have been reported for single crystals of titanium containing 0.1 wt pct C plus N.' These yield points were observed over a wide temperature range, but no room-temperature aging occurred. Aging at 180' was required to cause the return of the yield point. The magnitude of the yield phenomena in titanium containing interstitials is not expected to be as large as is observed in bcc metals because of several factors. Titanium has a very high chemical affinity for oxygen and nitrogen. The thermodynamic stability of solutions of oxygen or nitrogen in titanium is recognized. Lattice parameter measurements of titanium containing arbon, oxygen,1° or nitrogen" show that the "c" parameter is expanded more than the "a" parameter, but that up to about 2 wt pct this results in an insignificant change of the axial ratio 'c/a." Ehrlich" has shown that the sites occupied by interstitial atoms in titanium are spherically symmetrical and therefore a lattice expansion, at a constant c/a ratio, results in a simple dilation of the interstitial site. Such a dilation involving no shear has been shown to react only with edge components of dislocations.13 This causes only a weak pinning action. Shear stresses would be anticipated locally when only one of the two interstitial positions was occupied. The carbon atom will cause a symmetrical distortion of the lattice whereas the oxygen and nitrogen atoms have, in addition, the previously mentioned chemical affinity of titanium for these elements. These factors will result in a considerably smaller reduction of free energy upon the association of interstitial atoms with dislocations, and therefore a much weaker pinning than has been observed for the bcc metals. These considerations would lead to the hypothesis that of the interstitial elements considered here carbon would cause the strongest pinning effect in titanium where the amount of interstitial in solution is constant. This hypothesis will be borne out in the analysis of the present results.

Jan 1, 1962

By F. Seitz

STAFF: Editor, Gerhard Derge Carnegie Institute of Technology Schenley Park Pittsburgh 13, Pa. Editorial Assistant, M. A. Redmerski Managing Editor, James J. Burke THE METALLURGICAL SOCIETY: John Chipman, President; W. R. Hibbard, Jr., Post-President; C. C. Long, Vice-President; T. D. Jones, Treasurer; R. W. Shearman, Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: R. Maddin, Chairman; Dennis Carney, J. C. Fulton, J. H. Hollomon, T. B. King, C. C. Long, W. 0. Philbrook, J. D. Sullivan, David Swan, and F.L. Vogel. Review and selection of manuscripts is under the supervisian of the following Publications Committees: Extractive Metallurgy D ivis ion: T. 0. King, Chairman; S. J. Dick inson, R. P. Hermsdorf, R. Schuhmann, Jr., and H. H. Kel logg. Institute of Metals Division: F. L. Vogel, Choirmon; R. L. Smith, Vice Chairman; R.W. Balluffi, J. H. Bachtold, A Servi, C.D.Graham, Jr., C. G. Goetzel, F. E. Joumot, Jr., G. E. Pellissier, Paul Gordon, Jock Washburn, Harold Margol in, A. U. Seybolt, I. R. Kromer, R. A. Meussner, R. W. Guard, M. Harmon, J. N. Hobstetter, Dean Starr, P. Shewmon, R. Gordon, J. 0. Betterton, and E. Morgan. Iron and Steel Division: W. 0. Philbrook, Chairman; F. C. Langenberg, C. W. Sherman, J. Wagstaff, and E. J. Whittenberger. Published bimonthly by the American lnstitute of Mining, Metallurgical, and Petroleum Engineers, Inc., 29 West 39th Street, New York 18, N. Y. Telephone: PEnnsylvania 6-9220. Subscription $20 per year for non-AIME members in United States and North, South, and Central America; $25, foreign; $5 for AlME members. Single copies, $4.00, single copies foreign, $5.00. The AlME is not responsible for any statement made or opinion expressed in its publications . . . Copyright 1959 by the Americon Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AlME New York ... Indexed in Engineering Index, Industrial Arts Index, and Chemical Abstracts . . .Second class postage paid at New York, N. Y. , ond Ann Arbor, Mich. Volume 215, Number 3

Jan 1, 1960

By Gilbert L. Eggert

The effects of reactor irradiation on age hardening in a Cu-2 wt pct Be alloy have been investigated in two neutron-energy ranges. During some of the irradiations, specimens were exposed to high-energy fission neutrons which passed through a boron-10 shield; during other bombardments, the boron-10 was omitted and specimens were irradiated in a reactor thermal column, or the fuel configuration was modified to increase the thermal-neutron flux at a location in the core. Differences in length, X-ray diffraction angle, and hardness indicated that low-energy neutron irradiation made a small contribution to changes in the measured properties. The influence of defects generated by knock-om with less than the Brinkman critical energy or by prompt (n,y) recoil is suggested as the cause of this effect. EXPERIMENTS designed to test the effects of reactor irradiation on the properties of age-hardening alloys have to the present time employed fluxes un-differentiated according to neutron energy. Billing-ton and Siegell in 1950 were the first to perform such an experiment and to compare the results with those obtained by thermal aging. These authors concluded that precipitation in a Cu-2 wt pct Be alloy was not enhanced by the radiation. However, 4 years later, Murray and Taylor,2 working with specimens of the same Cu-2 wt pct Be alloy, reported that an increase in density, hardness, and resistivity which followed reactor irradiation resembled changes associated with thermal aging at about 100°C. (It should be noted that these authors reported that higher aging temperatures caused a decrease in resistivity.) cupp3 reported hardness results similar to those of Murray and Taylor. Koppenaal4 showed that irradiation-enhanced precipitation and irradiation defect hardening were not simply additive but that they acted separately in an irradiated alloy. Kernohan et a1.,5 working with Ni-Be, offered evidence that beryllium was removed from solid solution by reactor irradiation and suggested that the mechanism was one of increased diffusion through the use of vacancies in the structure. piercy6 also found that more precipitate particles were formed by fission-neutron irradiation of a Cu-Co alloy which contained a small amount of particles before irradiation. He proposed that the additional particles were caused by an appreciable amount of diffusion during the final cooling of displacement spikes. The retrogression of extant precipitate particles found by Murray and Taylor2 and Boltax7 as well as piercy6 indicated that nuclei were dissolved within a high-energy spike region and, upon resolidification of the perturbed volume, new nuclei precipitate and grow by enhanced diffusion. Bleiberg et al.' and Konobeevski et al.' explained phase changes obtained by irradiating fissionable alloys in terms of retrogression and re-precipitation in regions of high-energy spikes. Parsons and Balluffi10 used electron microscopy to verify that crystallization did indeed occur in displacement spikes which were formed in amorphous germanium by fast-neutron irradiation. The concept that low-energy neutron irradiation might cause structure-sensitive property changes in semiconductors by atomic recoil associated with the (n, y) reaction was first proposed by Schweinler" and walker." This thesis was tested by Cleland and crawford" and found to be valid. Coltman et al.14 exposed a variety of pure metals to thermal-neutron irradiation at cryogenic temperatures and attributed the resulting resistivity changes to the action of defects created by (n, y) recoil. The present work was undertaken to extend the concepts of Schweinler," walker," and Coltman et al.I4 to the case of an age-hardening alloy and to determine whether or not the action of defects produced by thermal-neutron irradiation would en-hance age hardening. EXPERIMENTAL PROCEDURE Omeea West Reactor Irradiations.* Thermal-

Jan 1, 1965

By J. W. Cunningham, M. J. Stultzman

THE demand for improved materials for high-temperature service has increased during the last few years. Iron,- nickel,- and cobalt-base alloys have been investigated extensively and many alloys with outs'tanding high-temperature strength have been developed. Considerable research has been directed toward improved methods of processing these alloys. The vacuum furnace as a tool for the purification and improved control of high-temperature alloys has been studied extensively and production units are in operation. The research covered by this paper studied the effects of casting in air, vacuum, or argon upon the elevated-temperature properties of two nickel- and two cobalt-base alloys. The alloys investigated were Stellite 31, He 1049, Udimet 500, and Guy Alloy. MELTING AND CASTING PROCEDURES Two heats of each of the four alloys under investigation were melted and investment cast under the following conditions: 1) Stellite 31 was melted and investment cast in air and in vacuum, with an argon atmosphere for pouring. 2) He 1049 was melted and investment cast in air and in vacuum, with an argon atmosphere for pouring. 3) Udimet 500 was melted and investment cast in vacuum with and without additions of zirconium and boron. 4) Guy Alloy was melted and investment cast in vacuum and in argon. The heats were all melted in induction furnaces equipped with preformed magnesia crucibles of 50-lb capacity. The air-melting furnace was powered by a spark-gap converter of 40 kw capacity. The vacuum-melting furnace was powered by a motor-generator set of 100 kw capacity. The argon heat of Guy alloy was melted in the vacuum melting furnace under an argon atmosphere. Virgin materials were used for preparing all heats except the air heats of Stellite 31 and He 1049. The charge for the air heat of Stellite 31 was a commercial blend of shot. The charge for the air heat of He 1049 was Stellite 6 shot plus those virgin materials necessary to give the desired composition. All of the materials used were of the same grade used com-

Jan 1, 1960

By J. P. Sheehan, W. R. Hibbard, M. Baeyertz

This paper deals with molybdenum modifications of 5140 steel that have the same hardenability but a better tolerance for phosphorus than the AISI-SAE 5140 grade. Lack of toughness in steels with higher than normal phosphorus contents is well known to metallurgists. This problem is troublesome even within normal phosphorus ranges, if the heat treatment or the design of the part or the service is critical. Under such unfavorable conditions and also in the case of phosphorus contents toward the upper side of the commercial range, the use of molybdenum to replace a part of the chromium in 5140 steel provides a factor of safety. The toughness of steel is variously exhibited in different mechanical tests; broadly the term is applied to the capacity of the steel to deform prior to fracture. Defined in this way, toughness is considered to be an inherent quality that depends upon the composition and structure of the steel, and also upon its temperature during deformation and fracture in the test. In the present state of our knowledge, the type of mechanical test needs to be included in any discussion of toughness, because the revelation of this quality in steel depends on the stress state and rate of stressing imposed by the test. In comparing the toughness of one steel with another by laboratory testing, it has long been customary to use notched tests that impose severe constmint to deformation, and then to test over a range of temperatures to obtain the so-called transition. At temperatures above the transition, the steel fails after considerable deformation and absorption of energy. Below the transition, less energy is absorbed as the steel fails largely by cleavage. The transition range itself is characterized by a more or less abrupt change in energy absorption and type of fracture. The conventional V-notch Charpy impact test has been used exclusively in the work covered by this report. For the steels under study, rather sharp transitions are obtained with this test, at testing temperatures that are easily obtained in the laboratory. The position of the transition on the testing temperature scale provides a rather sensitive index of the toughness of the steel, when the steels under study are similar in character as they are in this work. Turning to the metallurgical reasons for the greater toughness of one steel as compared to another, the authors propose to limit the discussion to the small field under study. Only one structural state is considered, tempered martensite of a hardness of about 28 Rockwell C or 269 Brinell. The study deals first with the loss of toughness in AISI-SAE 5140 steel caused by increasing the phosphorus content from about 0.020 to 0.040 pct. A second part of the work deals with counteracting this loss in toughness by replacing a part of the chromium by molybdenum. A series of molybdenum modifications was studied, in each of which the chromium was reduced sufficiently to duplicate the hardenability of 5140 steel. Phosphorus affects the toughness of steel in two ways. An inherent lack of toughness of phosphorus-bearing ferrite as compared to low phosphorus ferrite has often been noted. Jolivet and Vidall have shown that phosphorus has the same effect in tempered martensite in chromium steels. The other well known effect of phosphorus is to make steel susceptible to temper embrittlement. Temper brittleness is a loss in toughness brought about by tempering steel within a limited temperature interval somewhat below the A1 temperature. In most of the standard AISI-SAE alloy steels, this temperature interval is approximately 850-1100°F. Either of these types of loss in toughness is easily followed by the shift in the transition temperature obtained with the notched-bar impact test. The data to be presented show the beneficial effect of substituting molybdenum for a part of the chromium in 5140 steel with either moderate (0.020 pct) or high (0.040 pct) phosphorus contents. Both the inherent lack of toughness of phosphorus-bearing steel and temper brittleness are counteracted by this use of molybdenum. The work of Jolivet and Vidal mentioned above shows the detrimental effect of phosphorus on the toughness of tempered martensite in the absence of temper embrittlement, as well as the temper brittleness caused by phosphorus. They used two steels, essentially 0.25 pct C-1.4 pct Cr, with 0.044 and 0.013 pct P, respectively. The nonembrittled state was obtained by quenching in oil from 1610°F, then tempering for one hour at 1200°F and quenching in water. In this state the transition temperature range of the low phosphorus steel in the notched-bar impact test was below that of the steel with 0.044 pct P. An additional treatment of 24 hr at 975°F (that is, in the embrittling range) caused both steels to lose toughness, but the high phosphorus steel showed the greater embrittlement. Recently Hollomon2 has published a comprehensive survey and bibliography of the literature on temper brittleness, to which the reader is re-

Jan 1, 1950

By J. P. Sheeha, W. F. Craig, M. Baeyertz

The loss in toughness caused by phosphorus within commercial ranges was studied in AISI-SAE 1340 steel and in molybdenum modifications of this grade. The replacement of part of the manganese by molybdenum in amounts which maintain the hardenability of the standard 1340 grade was shown to counteract to a marked degree the detrimental effects of phosphorus. THIS paper deals with the effect of phosphorus on the toughness of 1340 steel and with the effect on toughness of replacing part of the manganese by molybdenum while retaining the same hardenability as that of 1340. In previous work1 a progressive decrease in toughness was observed when the phosphorus content of 5140 was raised from 0.020 to 0.036 pct; that is, from a moderate phosphorus level to one higher but yet within the AISI-SAE specification for this grade. The structural condition of the steel was tempered martensite. Toughness was evaluated by the transition temperature determined by V-notch Charpy tests. Replacement of a part of the chromium in 5140 by molybdenum provided a factor of safety against loss of toughness caused by phosphorus, especially where the steel was cooled slowly after tempering. Scope of the Study: In view of the improved tolerance for phosphorus obtained by replacing a part of the chromium in 5140 with molybdenum, it seemed desirable to investigate the possibility of obtaining similar improvement in 1340 by replacing part of the manganese with molybdenum. Heats were made at different phosphorus levels, in a series that began with 1340 and ended with steels containing 0.32 to 0.35 pct Mo with 0.82 and 0.90 pct Mn. The analyses of the heats are given in table I. In order to facilitate later discussion, the 1340 heats have been placed together in the order of increasing phosphorus content, and the molybdenum modifications have been grouped according to phosphorus

Jan 1, 1951

By A. R. Elsea, C. C. McBride

HIGH-TEMPERATURE alloys, that is, alloys that are strong at high temperatures, have become increasingly important with the development of modern aircraft engines. Many alloys of this type are available. However, metallurgists do not have a clear understanding of the phases or structures which are responsible for these high-temperature properties. If these basic factors were understood, it might be possible to make better or cheaper alloys for service at high temperatures. For this reason, an investigation of the fundamental factors promoting high-temperature strength in alloys was started at Battelle Memorial Institute. This was to have included a study of the relationship between the structure and properties of cobalt-chromium base alloys of the vitallium type. It soon became clear that the structure of vitallium is quite complex and that the equilibrium diagrams which should explain these structures were unreliable. As a result, the cobalt-chromium binary diagram was determined as the first phase of this investigation1. This diagram is shown in fig. 1. During the study of the cobalt-chromium binary system, it was learned that these alloys may pick up considerable nitrogen when melted and heat treated in air. The extent to which nitrogen affects the various reactions in cobalt-chromium base alloys was not known, but there were indications that this impurity might be responsible for some of the erratic test results obtained for vitallium. Consequently, nitrogen was the first ternary addition studied. Thereafter the work was extended to ternary additions of iron and of nickel. This paper describes the investigation of the effects of nitrogen, iron, and nickel upon the reactions in cobalt-chromium alloys with 80:20 and 68:32 cobalt-chromium ratios. Experimental Work Alloy Preparation: A series of cobalt-chromium base alloys containing various amounts of the third element being studied were made for both the 80:20 and the 68:32 cobalt-chromium ratios. Electrolytic chromium, cobalt, and iron, and reagent-grade nickel powder were used as melting stock. Table I contains the chemical analyses of these materials. The charges were melted in alun-dum thimble crucibles which absorbed chromium oxide and effectively deoxidized the melts. These crucibles were supported by close-fitting graphite sleeves so that if they cracked during melting the metal would not be lost. Carbon increases, during

Jan 1, 1951

By P. Beardmore, A. H. Holtzman, M. B. Bever

Specimens of the alloy CU3AU in the ordered and disordered states were subjected to explosive loading at shock pressures in the range from 160 to 475 kbars. The resulting changes in the resistivity, stored energy, microhardness, and microstructure were determined. By comparing the effects of explosive loading on ordered and disordered specimens a separation of structura1 and configurational changes has been made. In the pressure range from 290 to 370 kbars, representing a small increment of strain, the degree of long-range order in the ordered alloy decreased sharply. This change is attributed to the generation of shear stresses in excess of the theoretical shear strength of the alloy. Disordered CU3AU under explosive loading behaves in a manner considered to be characteristic of fee solid-solution alloys generally. The response of metals to high-velocity deformation and, in particular, to explosive loading has attracted much interest in recent years.' In general, metals are substantially strengthened by the passage of shock waves although the permanent strains are small. Explosive loading induces this strengthening by causing the metal to undergo rapidly a transient strain in a narrow region, first in the shock front and then in the rarefaction wave, which releases the pressure. The transient strain is given by e = 4/3 In V/Vo, where Vo and v are the specific volumes in the uncompressed and compressed states.2 The process produces many defects, which account for the strengthening. For the investigation reported here, an ordered alloy was chosen because it was expected to give sensitive indications of the near-neighbor effects produced by shock waves. The ordered alloy CU3AU was of special interest because of past work on the effects of conventional deformation on this alloy.314 The disordered alloy was included as a standard for comparison and as an alloy typical of a solid solution containing short-range order. The effects of explosive loading were followed by measurements of the resistivity, stored energy, and microhardness, and by metallographic examination. EXPERIMENTAL PROCEDURES Preparation of Specimens. Part of an ingot of the alloy Cu3Au prepared previously4 was cold-rolled with several intermediate anneals in vacuum to a final thickness of 0.042 in. Specimens of dimensions 2.0 by 1.0 by 0.042 in. were machined from this strip. After a recrystallization treatment of 1 hr at 565oC, half of the specimens were disordered by heating in evacuated Pyrex capsules for 1 hr at 460°C and quenching into water. Although they contained short-range order, they will be referred to as 'disordered" to indicate the absence of long-range order. The rest of the specimens were cooled slowly from 380°C to induce long-range order. The grain size of the ordered and disordered specimens was 0.012 mm. Explosive Loading. This was carried out at the Eastern Laboratory, Explosives Department, E. I. du Pont de Nemours & Co., by a driver-plate procedure described elsewhere.2 Two ordered specimens were stacked alongside two disordered speci-

Jan 1, 1964