By J. M. Steininger

The mechanism of flotation of sphalerite with sulthydryl compounds of different acidities has been interpreted in terms of chemisorption of unionized collector molecules on hydroxylated zinc surface sites. At a constant collector concentration of 1.5 x 10 -4 M, the upper pH limit of flotation has been found to be directly and closely related to the negative logarithm of the collector acidity constant, pKa The experimental results indicate that flotation is prevented when about 95% of the collector is ionized. At low pH, collector adsorption decreases because of the reduction in number of hydroxylated zinc surface sites. These two effects explain why sphalerite does not float with the more acidic sulfhydryl compounds. Typical anionic collectors for sulfide minerals are short chain xanthates or dithiophosphates which are nearly completely ionized in the generally alka- line flotation circuits.1,2 Flotation mechanisms have therefore been usually interpreted in terms of ionic collector adsorption and competition with ionic depressants of the same sign as the collector. A few attempts have been made, however, to consider adsorption of neutral collector molecules. Contact angle measurements obtained by Wark and cox3 have been interpreted by Cook and Nixon4 as representing adsorption of the free acid molecules on sulfide minerals such as pyrite, galena, chalcopyrite, and sphalerite. Cook and Nixon tried to show that the free acid concentration of the collector was substantially constant along the curves relating collector addition and minimum pH for bubble adherence. However, in a review of the subject,5 Sutherland presented new data on the flotation of pyrite with mercaptobenzothiazole which did not support the hypothesis of constant concentration of either collector ions or collector free molecules. He further showed that, with the assumption of constant occupation of surface sites, both theories lead to relations between pH and collector addition having similar mathematical expressions. In fact, with the more likely assumption of variable occupation of surface sites which results in more complex relationships, it appears impossible to

Jan 1, 1968

By L. Seigle, R. Resnick

An inert-marker movement experiment indicates that the ratio of the intrinsic diffusion coefficients DC:DTa = 80:l in TaC at 2500°C. Measurements of the diffmion coefficient of carbon in nonstoichiometric TaC at temperatures from 1700° to 2700°C reveal that Dc increases with decreasing carbon content, but much less than expected from the probable change in vacancy concentration with carbon content. A diffusion process involving two simultaneously operating mechanisms is postulated, and shown to be theoretically feasible. The average value of the carbon diffusion coefficient is given by DC = 0.18 exp[(-85,000 ± 3000)/RT] sq cm per sec over the composition range 46 to 49.5 at. pct C. BECAUSE of their high melting points and hardness, the carbides of the IV, V, and VI group transition metals, along with those of uranium, have attracted considerable interest for applications at high temperatures. In these applications the reactivity of the materials is important, and, since rates of diffusion within the compounds influence reactivity, a knowledge of diffusion kinetics and mechanisms is desirable. While many investigations of the mechanical and electrical properties of these compounds have been made, only two fundamental investigations of diffusion in the carbides are known. Chubb, Getz, and Townleyl measured the diffusivity of carbon and uranium in UC, and Gel'd and Liubimov2 measured the diffusivity of carbon and niobium in NbC. This paper describes an investigation of the diffusion of carbon in tantalum monocarbide and, in particular, the influence of carbon deficiency on this process. Tantalum carbide melts at approximately 3800°C, which makes it one of the highest melting materials known. The compound exists over a rather wide range of carbon Content.3-7 At the peritectic temperature, 3240°C, the phase extends from about 36 to 50 at. pct C. Although the compound can exist with a substantial carbon deficiency, the high carbon phase boundary remains near the stoichiometric composition over the entire temperature range; i.e., no carbon excess is observed. The structure of TaC is the NaCl type wherein carbon atoms normally occupy the octahedral sites in a somewhat expanded fcc lattice of tantalum. Decrease of the lattice parameter with decreasing carbon suggests that the removal of carbon introduces octahedral vacancies into the lattice. I) EXPERIMENTAL DETAILS AND RESULTS Inert-Marker Experiments. In a compound such as TaC the interstitial element would be expected to diffuse more rapidly than the metal. This was confirmed by an inert-marker experiment, following Srnigelskas and irkeendall.8 Ideally, the markers should be placed at the interface between a slab of low-carbon TaC and graphite, and their movement during subsequent inter-diffusion measured. Unfortunately, no solid could be found which is unreactive in contact with carbon at the high temperatures employed in these experiments. In order to circumvent this problem, a specimen was designed in which the markers consisted of several small canals running just below the surface of a tantalum slab. This specimen was prepared by machining grooves on the surface of the tantalum slab and then diffusion-bonding a thin plate of tantalum to the slab over the grooves. The surface of the plate was then ground down until the distance between the canals and surface was as small as possible (about 0.01 cm). Thus, the canals would lie entirely within the TaC phase after a short period of diffusion. The diffusion anneal consisted of immersing the metal sample in high-purity graphite powder and heating for approximately 10 hr at 2500°C under vacuum. At this temperature, the vapor pressure is sufficiently high and the transfer of carbon from graphite sufficiently rapid to allow the surface of the diffusion sample to attain the stoichiometric carbon concentration very quickly. Conclusions regarding the relative diffusion rates of carbon and tantalum in the compound layers (TaC and Ta2C) can be drawn from the location of the canals after the diffusion anneals. If the growth of the layers is governed mainly by the diffusion of carbon, as expected, the canals should remain close to the sample surface. If the diffusion of tantalum contributes appreciably to formation of the compound layers, the distance from the markers (canals) to the surface should increase. Fig. 1 shows, diagrammatically, the appearance of the specimens after diffusion, and Table I presents the depth below the surface at which the

Jan 1, 1967

By J. B. Morrow, D. H. Davis

THERE are two general approaches to the problem of increasing profits from an operation. One is to lower expense; the other is to raise income. Mechanical preparation of coal may be used for either purpose but a prudent consideration of many details must precede any decision lest the results be negative instead of positive. It is quite possible that any net gain will result from a combination of the two. Since mechanically prepared coal invariably is a better product qualitatively than a hand-picked coal from the same mine, it is a reason- able expectation that the customer will be willing to increase the producer's income by paying a higher price. Or there may be the possibility that a combination of mechanical mining plus mechanical cleaning will give a lower over-all production cost for the coal in the railroad car. More likely, there will be found a combination of these two factors. From the customer's point of view, the competitive delivered cost per B.t.u. considered in relation to such incidental factors as dust nuisance, handling properties, ash disposal, and ash fusibility determines what he will pay. In a bulk tonnage product such as coal, freight is a very considerable part of the delivered fuel cost, and obviously freight paid on incombustible ash has no economic attractions. INCENTIVE FOR CLEANING Coal is prepared in four major ways: 1 (I) by screening or sizing, (a) by mixing or blending, (3) by cleaning, including hand picking and mechanical cleaning, (4) by dustless treatment. By a combination of any or all of these methods, coal can be prepared to standard specifications. It is easily possible to have good cleaning and still get a poor final product because of faulty screening or mixing,

Jan 1, 1943

By HOWARND N. EAVENSON

THE year 1930 resembled the preceding one in the coal industry in continuing the era of falling prices and 'of the abandonment of unprofitable mines. Practically all coal prices fell, and in the steam sizes during the last half of the year this was particularly true, due to the small industrial demand. No new mines of any size were opened in the bituminous coal industry, but there was a steady increase in the number of cleaning plants of all kinds built in all fields. It is estimated that at least nine million tons per year were added to the previous total of washed coal. The largest washing plant started during the year was that of the Buckeye Coal Co., at Nemacolin, Pa., with a capacity of 650 tons per hour. Fig. 1 shows - the mixing-bin, conveyor galleries, washing-plant and skip hoist, and Fig. 2 the 120-ft. Dorr thickener for collecting the 48-mesh material from the wash water. Dryers are used for drying the steam coal product. The following statement by J. R. Campbell shows the effect of cleaning on Pittsburgh coal in Greene County: "With the advent of the 650-t.p.h. efficient washing plant in Greene County at the Nemacolin mine of the Buckeye Coal Co., it has undoubtedly been demonstrated that the potential coking-metallurgical coals of the county can be brought within the pale of the highest grade high-volatile coals for steel manufacture. A few months' operation indicates that 9% per cent ash in the raw coal can be easily reduced to under 7 per cent ash in the washed coal and the sulfur from 1.60 per cent in the run of mine to 1.20 per cent sulfur in the washed coal.

Jan 1, 1931

By Ralph H. Sweetser

IN the recent world-wide deflation of commodity prices the coal industry, including both anthracite and bituminous coal, had reached a level where the actual delivered market prices received by the operators were usually less than the cost of production. Many steel companies and public utilities, operating their own "captive" mines, could have bought coal during the past three years for less money than the true cost of coal produced at their own properties. Competition within the coal industry itself was cruel to the point of profitless operation, and the competition of other forms of fuel was bearing heavily on the coal producers. They were thus forced into methods of production and utilization that they had hitherto ignored; there had been almost complete absence of any appreciation (by the bituminous operators especially) of the necessity of real research work in finding better methods of preparing coal for specific uses, and in finding new and profitable uses for different kinds and grades of coal.

Jan 1, 1933

By AIME AIME

SOME 65 members of the Institute, including most of the Local Section delegates and several Directors and officers, were on hand for the Annual Business Meeting of the Institute held in the Engineering Societies Building on Monday, Feb. 21, at 4:30 p.m., immediately following the second session of the Local Section Delegates Conference. President Mathewson presided. The meeting was largely taken up with the presentation of committee re- ports, discussion of which was invited. F. E. Wormser presented the report of the Admissions Committee ; Philip Kraft, Papers and Publications Com-

Jan 1, 1944

By A. F. Buddington

INTRODUCTION EVER since a genetic connection between many ore deposits and magmas began to be widely recognized, some two-score years ago, there has been much discussion of the complex and intricate problem of the genetic association of specific kinds of mineralization with specific kinds of igneous rocks. General discussions of the latter problem and pertinent data have been given by S. F. Emmons, Kemp, Lindgren, Niggli, Rastall, Spurr, Vogt, and others. In this paper no attempt is made to deal with mineral deposits genetically associated with volcanic rocks, but only with those presumed to be related to exposed intrusive masses. The writer is indebted to E. S. Bastin, F. F. Grout, Edward Sampson, and to the members of the committee in charge of the preparation of the volume, for a critical reading of the manuscript and many worth-while suggestions.

Jan 1, 1933

By W. J. Rude

LARGEST of the known commercial deposits of pebble phosphate are those found in Polk County, Florida. The phosphate bed, commonly known as the matrix, will consistently average 6 to 9 ft. in depth, and is found under 3 to 60 ft. of over-burden. The phosphate pebbles, white and black in color, varying greatly in grade, are found imbedded in a matrix of sand and clay; and range in size from the fines to pebbles 1 1/2 in. in diameter, although the average coarse size is approximately 1/2 in. in diam¬eter. On some of the washers all material under 14 mesh is lost. High-grade phosphate (75 per cent plus of bone phosphate of lime, CasP2Oa) is generally soft, the pebbles breaking up during the mining operation and in pumping; low-grade phosphate, 67 to 69 B.P.L., is black in color with hard pebbles with no loss encountered in pumping.

Jan 1, 1941

By J. W. Dougherty

THE Hollinger gold mine is in the Porcupine mining division, District of Cochrane, in the northern part of the Province of Ontario. The adjacent town of Timmins, with a population of 25,119, lies 490 miles by railway north of the city of Toronto. GEOLOGY The property is situated on the northwest limb of a major syncline, which pitches northeast at approximately 50°. The principal rocks of the Hollinger area are of pre-Cambrian age and consist of altered, schistose, Keewatin lava flows intruded by stocks of schistose, quartz-feldspar porphyry generally assigned to the Algoman period. The structure of the Keewatin series is extremely complex as a result of close folding and some faulting. The schistosity, trending north 70° east and dipping steeply to the southeast, is most highly developed along a subsidiary anticline in which the major porphyry bodies occur. The ore bodies, which exhibit three principal structures, consist of quartz veins and associated pyritized wall rock. Some lodes are com-posed of en echelon veins, others exhibit a main quartz body with branch-ing stringers and a third consists of a single definite lead. Gold, in a coarse visible form, may be confined to quartz in some ore bodies but in others it is finely divided and is found not only in quartz but also asso-ciated with pyrite in the adjacent wall rock. In many veins the dis-tribution of gold is such that there are several ore sections, separated by areas of low-grade material, in the same vein although its physical appearance remains unchanged.

Jan 1, 1940

By W. C. Ellis

NONFERROUS alloys upon which desirable properties can be conferred by heat treatment are becoming of increasing industrial importance. The alloys of copper with a constituent which has a solubility varying with temperature are materials of this character. Some of the constituents which are effective in producing a change in the mechanical properties of these alloys upon heat treatment are, according to Corson,1 nickel and silicon, iron and silicon, cobalt and silicon, and chromium and silicon. In addition to these elements, Gregg2 states that the combination of beryllium and silicon is effective in producing age-hardening characteristics in copper. The effect of these elements, however, as dispersion-hardening constituents in the copper alpha solid solutions does not seem to have been studied in any considerable detail. This paper deals with the heat treatment and properties of three alpha brasses containing 3 per cent. of nickel plus silicon in the proportion necessary to form the compound nickel silicide, Ni2Si. Some information of a preliminary nature in regard to the hardening by heat treatment of phosphor bronze containing the same percentages of nickel and silicon is included. The method of hardening the alloys, which is effective in increasing the tensile strength and proportional limit, is similar to that used in, the case of duralumin type aluminum alloys. It consists of a quench from a temperature at which the hardening constituent is in solid solution, followed by an aging at a lower temperature to precipitate the dissolved constituent in a dispersed condition. This results in an increased resistance of the alloy to deformation with an attendant improvement in the tensile properties.

Jan 1, 1929

By Charles W. Henderson

THE influence of mineral production on the development of the western United States has been profound. From 1848 to 1860, there was only gold production, the effect of silver began in 1860, and from then on both had a powerful influence. Lead production started in 1863, copper in 1863, and zinc in 1885, but was small until 1898. Gold alone was therefore the stimulus of the early settlement and exploration of the Western States.. But mineral deposits caused neither acquisition of territory nor determination of boundary lines. Arizona, California, Nevada, New Mexico, and parts of Utah, Wyoming, and Colorado were formally acquired from Mexico fourteen days after the actual date of the discovery (January 19, 1848)1.2 of gold at Sutters Mill, near the present town of Coloma, California (a discovery which, with the immediate new discoveries, aroused the world several months later) ; but the acquisition was by treaty (under negotiation for some time but signed February 2, 1848)3 in settlement of a war involving the boundaries of the grassy plains of Texas, an area at that time not known to contain any metals, and to date found to have but few metal deposits.4 The international boundary at 49º latitude for the far northwest states was determined by causes other than mineral deposits.

Jan 1, 1933

By Robert Anderson

ROUGHLY, a crack in a casting may be considered, for the moment, to be due to fracture of the alloy resulting from the stress set up by the contraction in volume on passing from the liquid to the solid state. Cracks may be external or surface, internal or deep-seated, or incipient or so-called strain cracks. Draws may appear as depressions, unevenness, and "pinching in" of the surface of a casting. Roughly, draws are due to contraction in volume and are governed largely by the same factors as cracks. A casting may be cracked, however, without being drawn. Shrinkage is a foundry term; it connotes the contraction in volume of a metal or alloy on passing from the liquid to the solid state. Pattern-makers' shrinkage is the total contraction in volume (including liquid, solidification, and solid shrinkage) that occurs when an alloy is poured into a mold. The contraction in volume of aluminum is one of the principal factors affecting the occurrence of cracks, as will be shown later, and the question of shrinkage and its control requires careful study in any treatment of cracking in castings. In the case of, sand and die castings, cracks have been attributed to a number of causes, but in the case of most light aluminum alloys, they are due to the large contraction in volume on freezing and the lack of its regulation or control. The most important factors are: (1) Contraction in volume; (2) composition of alloy; (3) quality of melting charge; (4) design of casting; (5) method of molding; (6) hardness of ramming; (7) method of gating; (8) hardness and characteristics of cores; (9) chills; (10) risers; (11) melting temperatures; (12) furnace used for melting; (13) pouring tempera-tures; (14) inclusions in alloys; (15) hot shortness of alloys; and (16) physical properties of alloys at high temperatures. Of these, the first, second, third, and eleventh to sixteenth involve ascertainable metallurgical facts; the remainder are largely matters of opinion, judgment and technical knowledge of men experienced in the production of castings.

Jan 10, 1921

By Harry Klemic

Zirconium and hafnium minerals are used industrially both as minerals valuable for their chemical and physical characteristics and as ores of zirconium and hafnium. The principal zirconium-hafnium-bearing minerals, their composition, and their ranges in content of zirconium and hafnium dioxides are listed in Table 1. The supply of zirconium and hafnium is based almost entirely upon the supply of the minerals zircon and baddeleyite. Eudialyte may eventually also be of importance as a source of these elements. Zircon, which generally contains nearly 49% zirconium and between 0.4 and 1.5% hafnium, is the principal industrial mineral of this group. Baddeleyite, a commercially important but less abundant mineral, contains as much as 73% zirconium and 0.4 to 1.7% hafnium. Eudialyte has a wide range in content of these elements, but analyses of material from several localities indicate values of 6 to 11 % zirconium and 0.07 to 0.4% hafnium. Zircon is a mineral consisting principally of zirconium, silicon, and oxygen that crystallizes from magmas during the formation of igneous rocks. Zircon also occurs in veins and in metamorphic rocks. It is in the tetragonal crystal system. It commonly forms as small well-developed prisms having pyramidal terminations but also occurs as irregular-shaped grains. Zircon has a hardness of 7.5 on the Mohs' scale. Its specific gravity is commonly between 4.68 and 4.70 (Dana, 1932), but the specific gravity varies somewhat depending upon com- position and state of alteration. Zircon has no good cleavage directions and is brittle, breaking with a conchoidal fracture. Zircon of the composition ZrSiO, would contain 67.2% Zr02 and 32.8% SiO2. However, in addition to about 1 % of hafnium, minor amounts of thorium, uranium, rare earth elements, yttrium, calcium, magnesium, iron, aluminum, phosphorus, and hydrogen, and trace amounts of other elements are commonly present in the mineral (Frondel, 1957). Radiogenic lead and other daughter products from the radioactive decay of uranium and thorium also accrue in the mineral. Radiation damage to the structure of zircons that contain appreciable amounts of uranium and thorium may alter the internal structure of the crystals to

Jan 1, 1975

By P. R. Sperry, P. A. Beck, J. Towers

Dahl and Pawlek1 found that electrolytic copper develops extremely coarse grains at 1000°C after about 90 pct reduction by rolling. This coarsening occurs only under conditions of penultimate grain size, deformation, and alloying which lead to the "cube" recrystallization texture.l,2,3,5 The peculiar angular shapes and straight grain boundaries of the coarse grains were noted by several investigator.1,4,5 On the other hand, coarsening in Fe-containing aluminum or in AI-Mn alloys8 does not depend on a "cube" (or any well developed) recrystallization texture. It is true that increasing deformation by rolling, and, therefore, an increasingly well developed re-crystallization texture, are associated with decreasing incubation periods of coarsening.6-7-8 Nevertheless, coarsening readily develops in aluminum even after only 30 pct reduction by rolling, where the recrystallization texture is very weak.6,8 Also, coarsening was observed by Jeffries9 many years ago in sintered thoriated tungsten, which presumably has no preferred orientation. In all these cases coarsening is associated with grain growth inhibition by a dispersed second phase.8,9 The annealing temperature has to be suficiently high to overcome the inhibition at a few locations. But if it is too high, growth starts at many points, and the resulting grain size becomes much smaller.9 Normally, the coarse grains are more or less equiaxed, and the boundaries have a typical ragged appearance.6.8 Cook and Macquarie4 demonstrated that, in addition to the texture-dependent coarsening previously found at 1000°C,l electrolytic tough pitch copper may also coarsen at 800°C after 50 pct reduction by cross rolling. The coarse grains formed under such conditions have rounded shapes and ragged boundaries, like those in aluminum. When the annealing temperature is higher, the tendency for their formation decreases. All these observations suggest that the coarsening at 800°C is associated with inhibition by a second phase. Actually, coarsening at 800°C after 50 pct reduction by cross rolling was observed only in tough pitch copper,4 which contains Cu2O particles. On the other hand, the texture-dependent 1000°C coarsening occurs in both tough pitch and oxygen-free copper;4 it does not appear to depend on the presence of a dispersed second phase. However, the interpretation of the 800°C coarsening in Cu after 50 pct rolling as an inhibition-dependent process, similar to the coarsening in A1-Mn alloys, is somewhat weakened by the fact that this coarsening was reported4 to occur only after cross rolling, and not after straight rolling. It was, therefore, decided to re-examine this question. A 1 in. diam electrolytic tough pitch copper rod, No. 2 hard drawn, was annealed for 20 min at 700°C, rolled to 0.5 in., annealed 10 min at 700°C, and straight rolled to 0.064 in. It was then given a penultimate anneal of 20 min at 500°C and it was cut into four sections, which were given final reductions by straight rolling as follows: A 30 pct reduction of area B 50 pct reduction of area C 70 pct reduction of area D 90 pct reduction of area Specimens cut from the four sections were finally annealed at 800°C in an oxidizing atmosphere. Strip A remained fine grained up to 10 hr, but the specimen annealed 12 hr consisted of only 2 large grains. Strip B had a few scattered large (1/2 to 3/4 mm) grains after 1 min, although the balance of the specimen consisted of fine grains of about 0.02 mm. After 5 min there were several 10 to 15 mm grains present, and after 1 hr strip B was completely coarsened. The coarse grains had the same characteristics (see Fig 1) as those obtained by Cook and Macquarie at 800°C after cross rolling. Strip C had several grains of 0.05 to 1 mm after 1 min, but it was still largely fine grained after 12 hr. After 48 hr it consisted entirely of grains of about 0.5 to 4 mm, with an extraordinarily large number of twin bands. Strip D remained com- pletely fine grained after 4 hr at 800°C. These results indicate that, in the deformation range of 30 to 70 pct reduction, the incubation period for coarsening as well as the rate of growth and the final size of the coarse grains decreases with increasing deformation. Similar

Jan 1, 1950

By AIME AIME

THE growth of the spirit of progress and mutual aid which motivated the founders of the Institute sixty years ago in Wilkes-Barre was vigorously demonstrated at the sixtieth anniversary meeting held there on May 22. Committees headed by Cadwallader Evans, "resident director" of the Institute, and Paul Sterling, chairman of the local section, had arranged for a full-day tour of the northern anthracite field, so that the hundred and fifty members and guests who had come for the celebration of the anniversary might see the changes and progress made in that field in recent years. More than forty automobiles were in line in the cavalcade which left the Westmoreland Club at nine- thirty. Operations visited were fully described in the May issue of MINING AND METALLURGY, so it is enough to say that after a seventy-five mile drive through the beautiful Susquehanna Valley and over the rolling green hills of northern Pennsylvania a stop was made for lunch at Forest City. Carey, Baxter and Kennedy, contractors at the stripping operations there, had provided, in the shelter of tents, a well-prepared luncheon and other refreshments. The return trip was made by way of Scranton, arriving at Wilkes-Barre at five- thirty.

Jan 1, 1931

By K. G. Davis, P. Fryzuk

A study has been made of the effect of undercooling on the grain structure and solute distribution in small ingots of pure bismuth and of a 100 ppm Ag in bismuth alloy. Autoradiographic evidence shows that in undercooled melts a network of dendrites is formed throughout the melt immediately after nu-cleation. At large undercoolings the dendrites are very thin and closely spaced. The origin of the observed grain morphology can be explained on the basis of information about the mode of solidification revealed by the impurity substructure. WHILE a great number of studies of nucleation in undercooled molten metals have been made, comparatively little attention has been given to the mode of solidification from melts with large undercool- ings. Colligan and Bayles1 and Walker2 have measured the rate of advance of the solid-liquid interface in undercooled nickel melts, but the morphology of the solidifying material remained a matter of speculation. Fehling and Scheil3 have described the grain structure in ingots formed from undercooled melts of nickel, palladium, and copper, and a series of Ni-Cu and Ni-Pd alloys. At small undercoolings, equiaxed structures are observed, the grain diameter tending to increase as the temperature of nucleation is lowered. At greater undercoolings, a columnar structure is developed, while with still further undercooling there is a smaller grain size incorporating rather coarse subgrains. All-bright and Colligan4 examined the grain structure shown by ingots solidified from melts of nickel and of Ni-Ag alloy at an undercooling of 105°C, and concluded that considerable grain growth had taken place after solidification. The object of the present work is to correlate the mode of solidification from undercooled melts with both the grain structure and impurity segregation, using tracers to examine the latter.

Jan 1, 1965

By J. L. Taylor, P. Duwez

The phase boundaries in the ternary system Ti-Cr-Al have been established at 1800° and 1400°F for alloys containing more than 60 pct Ti. The martensite transformation temperature has been measured for the titanium-rich alloys. THE studies of binary alloys of titanium with the transition elements which have been published so far1-0 ndicate clearly that the solubility of these elements is always much greater in the high temperature body-centered cubic form of titanium (ß phase) than in the low temperature hexagonal form. In this category of alloying elements are iron, nickel, chromium, manganese, vanadium, molybdenum, tungsten, columbium, and tantalum. Although studies of the nontransition elements have been rather limited, early work on titanium binary alloys'" has shown that most of them were not very soluble in the a form, with the exception of aluminum, for which the solubility in a is about 25 pct.13, 12 In addition to this large solubility in a, aluminum is also soluble in ß titanium to the extent of about 35 pct and the transformation temperature from ß to a is raised with aluminum content. This effect is also typical of aluminum, in contrast with that found for the transition elements which lower the ß to a transformation temperature. Therefore, it may be anticipated that tprnarv titanium alloys with aluminum and any one of the transition elements will constitute a class of ternary alloys having characteristic features absent in alloys involving two transition elements. Chromium was chosen as a typical transition element for the present study because ternary alloys of Ti-Al-Cr commercially produced have been found to possess very interesting physical properties (MST-3 pct A1-5 pct Cr of Mallory-Sharon).'" Binary Systems The binary systems Ti-A1 and Ti-Cr have been established recently by several investigators. The data used in this investigation were taken from the complete diagram of Bumps, Kessler, and Hansen." This diagram agrees quite well with earlier investigations." For the Ti-Cr system, the phase boundaries at 1800" and 1400°F were taken from refs. 6 and 7. The binary system Cr-A1 has been studied recently by Bradley." This system is rather complex and contains not less than seven intermediate phases. The present study was limited to the titanium corner of the ternary system (less than a total of 40 pct Cr plus Al) and none of the phases present in the Cr-A1 binary alloys were found in the ternary alloys investigated. Experimental Technique Microscopic observation and X-ray diffraction measurements were used to identify phases and de-

Jan 1, 1954

By James E. Little

(Wilkes-Barre Meeting, June, 1911.) OF the several extensive deposits of brown iron-ore in Cuba, including those of Mayari and Moa, that of Mayari was the first to be systematically explored, and was selected as the scene of the first operations in the development of this class of ore. Construction-work, begun in the spring of 1907, involved the building of 16 miles of standard-gauge railroad and two large double-track inclines, the installation of mining-machinery, a nodulizing-plant, power-plant, shops and shipping-facilities, and the dredging of an extensive basin for deep-draught vessels. Unusual weather-conditions delayed the completion of portions of this work so that the entire plant was not in operation until December, 1909. The ore in its natural state contains a very large percentage of water, which increases to some extent with the depth below the surface. Near the surface it is red in color, with somewhat granular structure. The color gradually changes with depth, finally reaching a bright yellow. The consistency also changes towards, the bottom to a clay-like, sticky mass. The relative proportion of red and yellow ore is quite variable; in some places the yellow reaches close to the surface, while in others the red extends almost to the underlying serpentine. Fig. 1 is a map showing the Mayari division of the Spanish-American Iron Co. The ore lies on an irregular plateau about 15 miles long and 5 miles wide at the widest point, entirely covered with pine trees and brush, which grow directly on the ore. The elevation at the northern extremity, which is approached by the railroad, is about 1,700 ft. above sea-level. At the southern end the general elevation is about 2,000 ft. Ore is removed by means of scraper-bucket excavators and steam-shovels, these machines loading into special standard-guage, side-dump steel cars of 100,000 lb. capacity. A short haul

Aug 1, 1911

By William Campbell

The structure of iron and steel, though the object of so much study and research for the past 25 years, is by no means thoroughly understood. In the first place, we have three or more distinct iron-carbon thermal diagrams, each with its own supporters, and each representing a theory of the structure and constitution of cast-iron. In the second place, by reason of the fact that austenite, the solid solution of carbon in iron, decomposes in the solid state into ferrite, or pure iron, and cementite (Fe3C), and that quenching from above this transition-range, no matter how rapid, cannot entirely prevent the change and thus preserve the austenite by itself at ordinary temperatures, it happens that under the microscope we find, in addition to the ferrite, Fe3C, and austenite, which the thermal diagram of steel requires, a series of transition-products with distinctive structures, to which have been given the names martensite, troostite, sorbite, etc. Now these transition-products, in addition to the solid solution, austenite, have been the source of much controversy, at times very bitter. One side would insist that, say, troostite was an entity, which the other side would deny, pointing out that it must be a transition-mixture, with a particular structure. That austenite was a solid solution of carbon in iron has been denied by one school; we have been told that Fe24C dissolved both Fe3C and Fe, and thus gave rise to a whole series of quenching-pro-ducts—all this in spite of the fact that no matter how the thermal diagrams differ in regard to cast-iron, they all agree in regard to the solid solution, austenite, for Fe24C finds no place on the diagram. Thus it happens that while the authorities fight both in regard to the iron carbon diagram and the structures met with in hard-

Jan 1, 1913

By K. A. Pauly

(Wilkes-Barre Meeting, June, 1911.) COMPRESSED air has been and is still very extensively used in connection with mining-operations, but its application in the past has been almost entirely confined to supplying power to underground machinery. Its introduction was due to the difficulty of taking care of the steam which is exhausted underground, rather than to any advantage in efficiency to be gained by its use. The ease with which electric power may be carried to the remotest parts of the mine and the high efficiency of the electric motor have long been appreciated by mine-operators, and electric power is now extensively used underground in the more recent developments, while many of the compressed-air engines in the older workings are being rapidly replaced by electric motors. Recently, however, it has been suggested to use compressed air for driving the large shaft-hoists, the air for the engines being supplied by electrically-driven compressors, and an installation of this character is being erected at Butte; Mont. It is the object of this paper to compare the compressed-air system of hoisting with the various electrical systems, from the stand-points of first-cost and cost of operation. However, before entering into a discussion of the various systems, it will be well to consider briefly the conditions affecting the choice of a system of hoisting in which electricity is the ultimate source of power. The power required by a mine-hoist is extremely intermittent and fluctuates between very wide limits, the all-day average consumption of power not exceeding from 5 to 15 per cent. of the maximum demand during hoisting. The cost of supplying power for such a fluctuating load is necessarily higher than that for supplying an equal amount of

Dec 1, 1911