By John W. Buch

IN my review a year ago I pointed out that a small coal-mining companies as well as large had decided that the so called ?central shop? was a benefit. These central shops replaced in a large measure the commercial shops operated by those who have no direct connection with production of cod. Central shops in this time of salvage and major repairs have proved their worth. In addition, many of the larger companies had in their central shops equipment available for the production of many thousands of parts for our vast war machine and, as subcontractors, are doing this type of work. This is a real contribution to the war endeavor. Lack of new supplies has resulted in exhaustion of those stocks formerly stored or hidden in underground shanties. This means that the small stock of repair parts likely LO be available to any mine

Jan 1, 1943

By Lyon F. Terry

SPEED-UP of production of crude oil and its products, accompanied by rising prices and the organization of the industry on a war basis, featured the economic aspects of petroleum in 1941. Early in the year American tankers were urgently requested by the British to replace losses and offset slower transit under convoy. Some forty American owned tankers were first assigned to Britain and an additional forty-odd ships were transferred during the summer. This threatened to reduce our transportation facilities from Gulf ports to the Eastern seaboard below requirements, especially should sinkings have increased and the British needed more ships. Co-ordinator Ickes began preparations for restricting gasoline consumption in the Eastern district and plans were formulated for the construction of an emergency trunk pipe line from Texas to New York and Philadelphia refining centers, and for a gigantic tanker-building program. Sales of new oil-heating units in the East practically ceased. The companies were urged to transport as much oil as possible by tank car and by October 140,000 barrels of oil per day were reaching the East Coast district by rail, sufficient to meet 8 per cent of total requirements. But British sinkings from July through October decreased 63 per cent compared with the four months ended June 30, Britain began the return of tankers, the construction plans were dropped, and the threatened shortage was thus averted.

Jan 1, 1942

By N. I. Fisher, J. Shepherd

Abstract-Statistical studies have been carried out on structural geological data collected across a large zone of roof failure 600 m (1968 ft) wide and at least 800 m (2642 ft) long in the Greta coal seam at Aberdare East Colliery. Two swarms of hundreds 2 of minor, normal faults with throws commonly between 3 and 300 mm in the room and pillar workings are broadly coincident with roof failure. The faults have been classified into dip slip and oblique and strike slip types. Roof conditions have been classified into good; troublesome with subclasses scaly, heavy, gutter falls and wide, flat-roofed falls; and severely failed with subclasses very heavy roof, gutter falls and dome falls. Troublesome conditions are defined as those in which the height of the fall is less than or equal to 0.3 m, and severely failed conditions as those in which the fall height is greater than 0.3 m. Comparison of faults, roof conditions and mining rate on a shift basis indicates that faults and roof failure are much more important than machine breakdowns in reducing mining rate. The effect of faults on roof conditions has been quantified using a concept called the "zone of influence, " a rectangular area around a fault in which the fault has potentially deleterious effects. The spatial comparison of fault "zones of influence" with areas of roof failure using Spearman's rank correlation coefficient shows that, while normal dip slip faults do not appear to be associated with roof failure, oblique slip and strike slip faults appear to be associated with roof classed as severely failed. The "zone of influence" of an oblique slip fault may extend up to 3 m on each side of it in the headings and up to 1.14 m in the cut-throughs. The fault "zone of influence" has geomechanical implications for the design of mine openings and possibly represents the maximum length of a cantilevered roof beam likely to fail during mining, owing to a fault. Roof conditions could possibly be predicted in blocks of virgin coal if the type of fault could be identified in oriented drill cores.

Jan 9, 1978

By N. F. Fiore, M. C. Mangalick

DISLOCATION damping in single crystals is orientation dependent.&apos; If dislocations are distributed uniformly over all the slip systems in a crystal, and if each dislocation contributes identically to the damping process, then a damping loss or decrement 6 arises. In fact, however, for a crystal of axial direction (hkl), dislocations on certain slip systems are oriented to make a larger contribution to the damping loss than are dislocations on other slip systems. Thus the measuring damping, 6 (hkl) is proportional to an orientation factor (hkl), which weights the ability of each slip system in the crystal to contribute to the total damping. If it is assumed that dislocations are distributed uniformly on all slip systems, then for a given orientation of an fcc crystal this factor is determined2,3 by the three nonzero elastic constants Cll, C12, and C44 and the density p. In this communication measured values of elastic constants for two Fe-18Cr-Ni alloys are reported, and the dislocation damping results on two different orientations of each alloy are analyzed for orientation dependence. Elastic constants were determined by measuring the ultrasonic velocities of one longitudinal and two shear waves in (110) direction of the fcc crystals.4 Variation of velocities with the change in orientation is very small for (110) orientation,3 and so this direction is ideal for orientation factor and comparative damping measurements. Experimental Procedures. The nominal compositions of the alloys studied are given in Table I. These alloys were vacuum-melted and vacuum-cast from high-purity materials at U.S. Steel Applied Research Laboratories. The single crystals were grown by the modified Bridgeman technique. The specimens were homogenized at 1350°C for 20 hr, cut to shape and size with a spark cutter, and then annealed at 1100°C for 20 hr prior to use. In the KHz frequency range, the Marx composite piezoelectric oscillator was used to obtain the damping. The ultrasonic pulse technique was used to measure the ultrasonic velocities and the attenuation in the MHz frequency range. M.c.mANGALICK,-- StudentMemberAIME,formerly Research Assistant, University of Notre Dame, is now with Casting Laboratory, Chase Brass and Copper Co., Cleveland, Ohio. N. F. FIORE, Associate Member AIME, is Assistant Professor, Department of Metallurgical Engineering and Materials Science. University of Notre Dame, Notre Dame, Ind. This communication is part of a Ph.D. thesis presented by M. C. MANGALICK to the Graduate School of the University of Notre Dame. Manuscript submitted May 20. 1968. IMD Elastic Constants. Table I gives the values of the ultrasonic velocities. Values of C11, C12, and C44 calculated from these velocities are also given in Table I, and it is evident that there is very little variation in C11, C12, and C44 with nickel content. This slight variation may be attributed to inaccuracies in velocity measurements and practical differences in the orientations of the specimens. For example, in B the time interval for vl was 2.4 ± 0.05 sec giving an error in v1 of 0.235 x or 0.005 in. per sec. The elastic constants obtained by pulse technique were tested by calculating E<110>, Young&apos;s modulus for the (110) direction, from the equation: This value was compared with the value computed from the resonance bar measurements in which where fr is the resonance frequency and I, is the length of the specimen. In all cases, the values calculated from the ultrasonic velocity measurements

Jan 1, 1969

By J. F. Kemp

The use of nickel-steel has directed increasing interest of late towards the deposits of nickel, and at the same time the parallel advance in our knowledge of the basic igneous rocks has rendered these deposits a subject of important geological inquiry. Investigations have led to some views, more or less new, on the igneous origin of certain ores, which, though not universally accepted, have a growing number of adherents. In Europe, the mines in Norway have been especially suggestive subjects of study, and others somewhat less generally known have also added their testimony; while in this country the great economic importance and scientific interest of the developments in the Sudbury district of Canada, have furnished the principal texts for the discourses that have appeared among us. The purpose of the present paper is to set forth these views through the medium of one interesting ore-body, of which but little has been written ; and, by the description of another, to place in contrast two different geological associations in which nickeliferous pyrrhotite occurs, and to indicate a generalization, based upon these different geological characters, and justified by the experience so far gained. To Prof. J. H. L. Vogt, of Christiania, Norway, is due the chief credit for the revival of interest in the geology of nickel. His important contributions* of recent date have made generally available

Jan 1, 1895

By N. I. Fisher, J. Shepherd

Statistical studies have been carried out on structural geological data collected across a large zone of roof failure 600 m (1968 ft) wide and at least 800 m (2642 ft) long in the Greta coal seam at Aberdare East Colliery. Two swarms of hundreds of minor, normal faults with throws commonly between 3 and 300 mm in the room and pillar workings are broadly coincident with roof failure. The faults have been classified into dip slip and oblique and strike slip types. Roof conditions have been classified into good; troublesome with subclasses scaly, heavy, gutter falls and wide, flat-roofed falls; and severely failed with subclasses very heavy roof, gutter falls and dome falls. Troublesome conditions are defined as those in which the height of the fall is less than or equal to 0.3 m, and severely failed conditions as those in which the fall height is greater than 0.3 m. Comparison of faults, roof condition and mining rate on a shift basis indicates that faults and roof failure are much more important than machine breakdowns in reducing mining rate. The effect of faults on roof conditions has been quantified using a concept called the "zone of influence," a rectangular area around a fault in which the fault has potentially deleterious effects. The spatial comparison of fault "zones of influence" with areas of roof failure wing Spearman&apos;s rank correlation coefficient shows that, while normal dip slip faults do not appear to be associated with roof failure, oblique slip and strike slip faults appear to be associated with roof classed as severely failed. The "zone of influence" of an oblique slip fault may extend up to 3 m on each side of it in the headings and up to 1.14 m in the cut-throughs. The fault "zone of influence" has geomechanical implications for the design of mine openings and Possibly represents the maximum length of a cantilevered roof beam likely to fail during mining, owing to a fault. Roof conditions could Possibly be predicted in blocks of &gin coal if the type of fault could be identified in oriented drill cores.

Jan 1, 1979

By K. Fallenius

Since 1970 a new series of pneumo-mechanical flotation machines has been developed by Outokumpu Oy. The cells have a completely new type of mechanism based on a recently-developed theory of conditions necessary for dispersion of large amounts of air. The mechanism was developed in 3 cu m cells and scaled to 16 cu m cells. Rotor and stator description, scale-up theory, and practical experience with the 16 cu m cell are presented.

Jan 1, 1976

By J. A. Putnam, A. D. K. Laird

In laboratory research on the behavior of oil, gas and water in porous materials, no direct method has been devised to measure saturation without disturbing the flow. Indirect methods involving various forms of radiation have been developed for measuring one or two components. The X-ray absorption method for two components has been described previously1-3. The possibility of three component measurement has also been mentioned1. Since two component measurement still requires considerable care to insure accuracy, the fact that three components can be measured satisfactorily is not generally appreciated. The fraction of the energy of an X-ray beam of one wavelength transmitted through a material is given by the transmission factor. in which 1 is the beam&apos;s path length through the fluid. p is the fluid density, and 1,. is its mass absorption coefficient. Eq. 1 implies that all parts of the beam pass through equal amounts of the fluid. Practical applications are, therefore, limited to systems in which the fluid is distributed so that I varies negligibly over the cross-section of the beam. Typical variations of the transmission factor with X-ray tube potential arc shown in Fig. 2 from which experimental points have been omitted for clarity. The X-ray absorption of low pressure gases in a core is practically zero so it cannot he distinguished from that a vacuum by instruments that will differentiate between liquids. The transmission factor of a gas in a core is. therefore, unity. Consequently, the saturation of only one gaseous component can be found. If two fluids completely fill a core, their two saturations add to unity and, therefore, only one value of the transmission factor, T, is needed to determine both of them. When two liquids do not completely fill the core, their saturations do not add to unity and transmission factors at two wavelengths must be measured. At one of these wavelengths, 7 for one liquid must be different from T or the other liquid. The change of T for one liquid us the wavelength is changed between the two values must be different from the corresponding change of T in the other liquid. The two values of fluid saturation will also give that of the gas because the three saturations must add to unity. In Fig. 2 it can be seen that there are many large differences of T between various oil solutions and water solutions at any one potential, and between potentials for any one solution. Consequently, conditions for optimum accuracy of measurement of the saturations of a gas and two liquids can be chosen. Once the operating potentials have been selected, however. it is more convenient to cross plot the data from Fig. 2 on transmission factor-solution concentration coordinates for the chosen potentials, as shown in Fig. 3. Fig. 3 was used to plan the experimental procedure for Core N-38-1. Since the voltage control at 45 kv was good, the slopes of the curves in Fig. 2 at this potential would cause little error. At low potentials, however, the voltage control was not good, so 33 kv was chosen because the small slopes of the curves made voltage control less critical. The lowest strength beam that could be measured reasonably at 33 kv corresponded to a minimum T factor of 0.385. Fig. 3 shows that both 4.80 weight per cent of cadmium chloride in water and 24.0 per cent of iodobenzene in crystal oil had this T value, and, consequently, were indistinguishable to the X-rays at 33 kv. Thus, at 33 kv, the liquid saturation was given by the same curve regardless of the relative amounts of oil and water solutions present. This simple calibration curve from which the gas and liquid saturation can be read, is shown in Fig. 4. Fig. 3 also shows that at 45 kv, T for the aqueous solution is 0.610. and that T for the oil solution is 0.220. These values were transferred to Fig. 4 to give the triangular calibration plot from which the brine and oil saturations can be found, after the gas saturation has been determined at 33 kv.

By R. J. Evans, A. G. Revesz

Silicon films have been grown by chemical reaction on (111) silicon substrates. The surfaces were examined by various microscopic and interfero-metric methods. Surface structures are classified into two groups depending on whether the angles between the bounding planes and the (111) surface are small (<3 deg) or large (> I0 deg). A layer-gvowth mechanism is postulated to explain the topography and the influence of growth parameters. Growth proceeds by lateral expansion of the (111) layers in (211) directions, thereby forming steps. The step edges are perpendicular to the direction of expansion and are thus along (110) directions. Step bunching md surface nucleation both play an important role in modifying the flow pattern and in the step regeneration. These are influenced ver?) much by impurities, especially oxygen. Although the growth is a result of a surface-controlled ga: reaction, it is very similar to growth from an impure solution. OVERGROWTH ("epitaxial growth") of silicon is important and widely used. During the past years several investigators have observed various topographical features or so-called faults on the grown films. A study of the surface morphology gives some insight into the growth mechanism. I) EXPERIMENTAL Silicon films have been grown on silicon substrates by a method described by Theuerer.&apos; Silicon is formed by reduction of SiCl, in hydrogen. The rate of incidence of SiC1, was varied between 5 x 10"6 and 2 x 10&apos;4 moles min-&apos; cm-&apos;. The mole fraction of Sic4 in the Hz-SiCL mixture was about 5 x X Both the rate of incidence and the mole fraction were calculated on the assumption that the Hz bubbling through the SiC1, reached equilibrium saturation. Assuming uniform velocity distribution, the linear velocity of the gas in the reactor tube was estimated to be 2 cm sec-l. The temperature of deposition was varied between 1070" and 1260°C. Chemically polished p-type silicon wafers of 20 to 100 ohm cm resistivity were used as substrates. These were within 1/2 deg of a (111) orientation. The thickness of the grown n-type film was determined by two methods: a) measurement of the depth of the p-n junction taking into account the junction shift due to diffusion, b) measurement of the traces of stacking-fault tetrahedra on the (111) plane.&apos; The agreement between the two methods was better than 20 pct. The rate of growth varied between 0.2 and 4.0 pmin-&apos;. The formed films were examined by reflection and light-section microscopy, and by multiple-beam interferometry. Phase-contrast illumination revealed height differences of about 30A. For measuring heights greater than 1 p a light-section microscope3 was used. The resolution by multipke-beam interferometry4 was between 50 and 100A. Crystallographic directions on the surface were determined by X-ray and from the orientation of etch pits and stacking faults as revealed by Dash etch (I part HI?, 3 parts HNOJ, and 12 parts CH3COOH). Some specimens have been investigated by electron microscopy. Platinum-shadowing and carbon-replica techniques were used to show the fine topography and reflection diffraction to determine the structure of the grown layers. 11) RESULTS The topographical features can be classified into three groups. he first group is comprised of fine ridges (striations). The second group consists of structures, which are bounded by planes making angles of less than 3 deg with the (111) surface. They are, therefore, vicinal planes. Structures which closely resemble growth or etch pyramids from the third group would normally be bounded by perfect low-index crystallographic planes. In this case they are deformed. The angles between the bounding planes and the (111) surface are generally larger than 10 deg. The fine ridges are present, even on the smoothest surfaces, as shown in Fig. 1. They are along a (110) direction. The height differences could not be resolved with interferometric techniques. The basic characteristic structures of the second group are depressions and hillocks. These are bounded by three planes, two of them with larger slopes than the third one. The edges between the planes, as projected to the (111) surface, point in (211) directions. Various habits of these structures are shown

Jan 1, 1964

By W. R. Hibbard

It has been proposed1 on the basis of slip and flow that the ideal deformation texture of drawn wire for face-centered cubic metals is a (111) direction parallel to the wire axis. Under these considerations, an intermediate [loo] texture is permissible but should eventually change to the stable [Ill] orientation. This theory does not explain why copper and its alloys containing up to about 30 pct nickel, 5 pct zinc and 1 pct aluminum were found to have a double [Ill], [100] texture, while alloys with at least 8 pct zinc and 2 pct aluminum developed essentially a single [Ill] texture.1,2 It does suggest, however, that the [loo] component of the former alloys should disappear with additional deformation.3 Some evidence exists to support this suggestion. Howald4 reported that annealed copper wire previously drawn 93.8 pct and 98.5 pct developed a single [Ill] texture. Since, in wire, the drawn and annealed textures are similar, these wires probably had a single [Ill] deformation texture before annealing. In addition, although cold rolled polycrystalline copper and 80-20 brass were found to form different types of pole figures,5,6 single crystals of these metals when rolled from the stable (110) [112] orientation were found to produce essentially the same polo figure.7.8 It may be, therefore, that while the addition of solute elements changes the path by which the final texture is obtained, the final texture is not changed. Experimental Results The wires remaining from the previous investigation1 already drawn about 50 pct reduction in diameter were further drawn to 86 pct and then to 96.4 pct total reduction in diameter. The textures were determined after these stages by transmission X ray photograms taken with a copper K-alpha beam rotated 0 degrees toward the wire axis. It was found that the ratio of the [111].] and [100] intensities of the double texture in copper and its alloys containing 0.94 pct aluminum, 30.70 pct nickel, 2.61 pct zinc and 4.99 pct zinc increased from about 3:l for the 50 pct reduction to about 9:l for the 86 pct reduction. After 96.4 pct reduction, these wires exhibited essentially a single [lll] texture. Summary Thus, the drawn wire deformation texture of copper and its alpha solid solution alloys containing aluminum, nickel or zinc is essentially a single [Ill] texture as predicted by theoretical considerations of slip and flow.&apos; For copper and its alloys containing up to about 1 pct aluminum, 5 pct zinc and at least 30 pct nickel, an intermediate [loo] component is found after about 50 pct reduction in diameter, but disappears after about 95 pct reduction in diameter. For alpha solid solution alloys containing at least about 2 pct aluminum and 8 pct zinc the single [Ill] texture is developed considerably more easily and is found after about 50 pct reduction in diameter. No explanation of this compositional effect is apparent. Similar work is contemplated for cold rolled and cold compressed alloys. References 1. w. R. Hibbard, Jr. and M. K. Yen: Trans. AIME 175, 126. Metals Tech., Feb. 1948, TP 2334. 2. W. R. Hibbard, Jr. and D. E. Trout, 11: Trans. AIME 185, 620. Jnl. of Melals, Sept. 1949, TN 18. 3. W. R. Hibbard. Jr.: Disc. of R. M. Brick&apos;s paper on Deformation Textures, ASM Symp. on Cold Working of Metals, Oct. 1948. 4. T. S. Howald: Disc. of Ref. 1. Trans. AIME, 175, 126. Melals Tech. Aug. 1948, TP 2449. 5. R. M. Brick, D. L. Martin and R. P. Angier: Trans. ASM (1943) 31, 675. 6. 0. Dahl and F. Pawlek: Zlsch. Melall. (1936) 28, 266. 7. C. S. Barrett and F. W. Steadman: Trans. AIME (1942) 147, 57. 8. J. E. Burke and C. S. Barrett: Trans. AIME 175, 106. Melals Tech., Feb. 1948. TP 2327.

Jan 1, 1950

By Roland Kammel, Takeo Oki

A suspension electrolysis method has been developed which enabled a direct anodic extraction of zinc from zinc sulfide concentrate and simultaneously oxidized sulfide sulfur to elemental sulfur. The investigation was performed in a laboratory-scale electrolytic cell, where the zinc sulfide concentrate particles (chemical composition in weight percent: 61.1% Zn, 2.3% Fe, 30.6% S, 3.4% SiO2 were suspended with or without graphite powder in a dilute sulfuric acid electrolyte. The main parts of the cylindrical electrolytic cell are shown in [Fig. 1]. The cathode (1), a rod of aluminum, is set at the center of the cell. The anode (2), which consists of four plates, is mounted on the inner face of the cell wall. Both PbO2(Pb) and graphite anodes were used. The cathode compartment (3) is separated from

Jan 1, 1976

By H. R. Page, A. E. Jr Lee

From the inception of zinc retorting on a commercial scale in the United States in 1890,&apos; the retort employed has undergone wide variations in its composition and manufacture, facilitating in part equally remarkable improvements in furnace capacities. The early day hand made clay retort was charged with carbonates or silicates or with coarse dead roasted concentrates mixed with a large proportion of charge fuel resulting in a relatively low zinc burden and fired 24 hr in direct coal fired furnaces. Its modern counterpart is fabricated in hydraulic presses from clay mixtures containing sizeable amounts of either silicon carbide or silica flour, charged with sintered flotation concentrates to more than three times the early day zinc burden and fired 24 to 48 hr in gas fired furnaces. This paper does not attempt to describe in detail the early day clay retort practice as it is well outlined in treatises by Ingalls,2 Lodin,3 Liehig,4 Hofman5 and others. A brief review of clay retort practice is presented together with a description of the major developments since 1912. Clay Retorts The Belgian type retort, both in the circular and elliptical forms, has been used almost exclusively. Typical dimensions of press made clay retorts around 1910 are shown in Table 1. Variations in these dimensions were used at different plants according to local conditions to a maximum inside diameter of 9 in. and inside length of 54 in. However, the effective heat penetration in a 24 hr firing cycle and the tendency of the retort to bend limited the retort size. Use of the elliptical vessel was an attempt to present a stronger cross-section resisting the tendency to bend and to increase the burden without increasing the depth of heat penetration. One exception to the 48-54 in. length was the 60 in. retort used as early as 1905 at Palmerton by means of supporting the last 12 in. at the butt end with a specially designed furnace back-wall. This backwall construction with the 60 in. retort had been developed and used at Bethlehem by G. G. Con-vers and A. B. DeSaulles. An attempt was made at Blende, Colo. to use even larger retorts of the Rhenish type based on European practice and requiring much higher furnace temperatures. Satisfactory plastic clays capable of withstanding these temperatures were not available, and the plant never operated successfully. PREPARATION OF BATCH Composition of the clay retort by weight was 40 to 50 pct raw clay and the balance "grog." Generally speaking the mix consisted of 7 parts plastic clay to 9 parts grog by volume. Principal source of the clay used was the Cheltenham vein—sometimes referred to as "St. Louis city clay." A typical analysis was A12O3-31.0 pct, SiO2-50.0 pct, Fe2O3-2.5 pct, MgO-0.3 pct, CaO-1.5 pct and loss on ignition 14.0 pct. At the smelter the clay was weathered whenever possible and then crushed to 0.08 in. or finer. Grog consisted of calcined adobies, cleaned retort scrap and cleaned refuse fire brick such as old furnace brick, blast furnace linings, and others. Saggers from ceramic plants and calcined flint clay were later used. The grog materials were ground to 0.12 m. or finer. Occasionally coke dust up to 10 pct of the mix was substituted for a part of the grog following European practice.² Particle size of the grog has a major influence on the retort properties—the larger the grain, the better can the retort withstand thermal shocks, resist bending at furnace temperatures and resist corrosion from slag; the smaller the grain, the lower the loss of zinc vapor through the retort walls. Grog forms the skeleton of the retort, and the clay shrinks around its grains to act as a binder. In the drying process, the grog has a stabilizing effect on the drying rate, decreasing shrinkage and giving up previously absorbed water to the surrounding clay to minimize the danger of cracking or checking.² Grog and clay were mixed through a horizontal pug mill with 10 to 20 pct water added, depending on whether the retort was to be formed by hand or mechanically, more water being required for the hand process. The batch or "mud" extruded from the pug mill was cut in convenient lengths for handling, stacked in piles or in special rooms, covered with wet burlap and allowed to "rot" or age from 1 to 8 weeks to increase plasticity. HAND MOLDING If the retort was to be molded by hand, the mud was repugged after the rotting period and given to the molders. Their molds consisted of 3 sheet iron or wood cylinders, each one third the retort length and defining the outer shape of the retort. Beginning with the bottom section, mud was placed in the form and tamped with a rammer

Jan 1, 1950

By Paul J. Bennett, James E. Castle

The sillimanite family of minerals, including kyanite, sillimanite, and andalusite, are anhydrous aluminum silicates with the formula A12O3-SiO2. Dumortierite and topaz are also included in this group because they are closely allied in composition and thermal behavior. However, neither are mined commercially today. They are typical metamorphic minerals which are found in metamorphic rocks on every continent. Sillimanite minerals are prized chiefly for their refractoriness and are important components in a broad range of acid refractory products, especially in mortars and castables. World production of sillimanite minerals is currently about 400,000 tpy and has been increasing at the rate of 3 to 8% a year for many years (Anon., 1972). While these minerals have widespread occurrence, the consumption of sillimanite minerals is concentrated in the relatively few highly industrialized areas where refractories are manufactured, and which in turn are typically close to the major iron and steel producing regions of the world. Thus northern Europe,. England, the United States, and Japan are the principal consumers of refractories and sillimanite minerals. Of these countries only the US is a significant producer. Uses of Kyanite The following specifications are typical for the domestic kyanite industry: Raw Kyanite Concentrates Chemical Analysis 56% AI2O3 min 0.1% CaO max 42% SiO2 0.1% MgO max 1% Acid soluble 0.3% combined Fe2O3 alkali max 1.2% TiO2 max Available Sizes 35, 48, 100, 200, and 325 mesh The largest use for domestic kyanite, both raw and calcined, is in the manufacture of refractory mortars, cements, castables, and plastic ramming mixes. In these applications kyanite constitutes from 10 to 40% of the mixture, the balance being refractory clays and coarser grog materials. A certain proportion of raw kyanite is used to offset the shrinking of the clay binder, whereas the calcined kyanite is used in the coarser sizes for body. Certain high grade refractory shapes and kiln furniture are composed chiefly of graded sizes of calcined kyanite bonded with a little ball clay. In most applications, however, kyanite is used only to fortify the mix or as a minor ingredient. Some manufacturers of mullite brick use domestic calcined kyanite for the fine-grained portion of the brick, but seldom in quantities exceeding 10% by weight. Kyanite is used by ceramic manufacturers of wall tile and sanitary ware to offset shrinkage and cracking after firing. Indian kyanite has traditionally been used to make the coarse grog sizes needed for the manufacture of mullite brick, and for the grog portions of mortar, cement, and castable mixes. It has been largely replaced, however, by synthetic mullite, high fired flint, and diaspore clay or calcined bauxite for other applications. Indian kyanite has been available in lump as well as in granules and concentrates, as are sillimanite materials from India and South Africa. Andalusite is available as 8 mesh granules and as fines with chemical analyses not unlike those of domestic kyanites. From time to time and from place to place minor amounts of other aluminum silicate minerals such as dumortierite, topaz, and pyrophyllite have been made available at various prices and specifications, but have not been significant factors in the refractory industry. A mixture of kyanite and sillimanite of relatively fine grain-size and of low iron content was at one time offered to the molding sand industry by the Du Pont Co. as a byproduct from their deposits of heavy

Jan 1, 1983

By Per Kofstad, Hallstein Kjöllesdal

The oxidation behavior of niobium (columbium) has been studied in the temperature range 500° to 1200°C and at oxygen pressures of 760,100, 10, 1, and 0.1 mm of Hg. The work comprises kinetic studies of the oxidation as well as structural investigations of the oxidized specimens by means of X-ray diffraction, electron diffraclion, electron microscopy, and metal1ographic techniques. The oxidation reaction has a highly irregular temperature dependence and is unusually sensitive to changes in the oxygen pressure. The complex oxidation behavior is suggested to be due to formation of different Nb2O5 modifications in different temperature regions. During oxidation oxygen is also dissolved in the metal. Formation of oxide whiskers take place on the oxide surface at temperatures above approximately 800°C. VARIOUS aspects of the oxidation of niobium have been studied.l-12 The investigations show that niobium has a complex oxidation behavior, and the oxidation

Jan 1, 1962

By J. L. Rodda, M. L. Fuller

In connection with an investigation in this laboratory on the high-zinc side of the copper-zinc system, it was observed that well developed segregate structures of the Widmansttten type were formed when a secondary phase precipitated from the solid solution of copper in zinc. This paper presents an analysis of the crystallographic relationship between the segregate and the solid solution matrix. The data to be presented are an interesting addition to the literature on segregate structures in that the plane of segregation is one of the less densely populated planes. In agreement with the generalization of C. H. Mathewson and D. W. Smith&apos; the plane of segregation in the matrix contains the direction of closest atomic packing of the lattice. Furthermore, the matrix and the segregate are both hexagonal close-packed, which has not been reported hitherto in the 1iternture.l The increasing commercial importance of zinc alloys containing copper makes this fundamental study of value to the metallography of zinc alloys. Zinoeich Copper-zinc Alloys Copper enters into solid solution with zinc to at least 1.8 per cent at 400" C., according to W. M. Peirce.3 The solubility is less at lower temperatures. Thus a solid solution of copper in zinc, saturated at an elevated temperature, will precipitate the excess copper in a separate phase at a lower temperature, conditions of concentration, time, and temperature being suitable. The nature of these two phases has been established by the X-ray method of crystal analysis. Westgren and Phmgmén4 and also Owen and Preston5 have shown that the solid solution eta (7) is of the substitu-tional type with copper atoms replacing zinc atoms on the hexagonal

Jan 1, 1933

By D. H. Wertz, R. R. Furlong

A. E. LEE*—I would like to ask Mr. Neale if he has determined the moisture content of his dried retort. Also, has he ever experienced difficulty with bending in the dry room where the green wel retorts contain 17 pet moisture and are placed 3 in. apart? M. M. NEALE (replying for authors)— I cannot answer your first question as we have had no experience with that. Setting the retorts 3 in. apart, we had no trouble with bending. We thought we would, anticipated we would, but did not. L. P. DVVIDSON*—You mention,

Jan 1, 1950

By F. N. Rhines, W. S. Pellini

In many of the otherwise well established alloy phase diagrams the solidus curves (temperatures at which liquid first appears upon melting) have not been located accurately, chiefly because the experimental techniques that have been most popular for determining solidus temperatures have been both cumbersome and subject to large errors. C. E. Homer and H. Plummerl have described a sensitive and at the same time a very simple technique for locating the solidus curves in a number of alloys of tin. Their method consists simply in noting the temperature at which a specimen of the alloy ruptures under the influence of a light bending force. Although this method is not new, it has been little used for this purpose in the past; nevertheless, it appears so attractive in its possibilities of speed, simplicity, and precision that the investigations presently to be described were undertaken to verify its merits. The redetermination of the solidus and eutectic temperatures of the lead-antimony system was employed as a medium of experimentation. New values obtained in this way are believcd to be sufficiently precise to warrant a revision of the currently accepted lead-antimony phase diagram (Fig. I). Determinations of the solidus of the lead-rich lead-antimony alloy series have been published by X. S. Dean2 and by E. E. Schumacher and F. C. Nix. Their points are represented in Fig. I. In their work the solidus was not located at antimony collcentrations greater than 2 per cent; the curve was presumed to meet the eutectic horizontal at an antimony concentration of about 2.5 per cent. In the present studies the solidus has been traced to 3.5 per cent, where the eutectic horizontal is intersected (Table I and Fig. I). Within the range investigated by Dean and by Schumacher and Nix the agreement with their values is good. H. Seltz and B. De Witt,4 on the basis of activity measurements, have calculated that the intersection of the solidus and the eutectic reaction horizontal should lie at 3.86 per cent of antimony. The following determinations of the eutectic temperature have been reported: Roland-Gosselin,5 228°C.; Ewen,6 228OC.; J. E. Stead,7 24g°C.; Campbell,8 228°C.; W. Gontermann,9 245&apos; to 252°C.; R. Loebe,lo 245°C.; E. Heyn and 0. Bauer,ll 245°C.; H. Endo,12 250°C.; R. S. Dean,= 247&apos; to 258°C.; E. Abel, O. Redlich, and J. Adier,13 245°C.; W. Broniewski and L. Sliwowski,14 250&apos; to 252°C.; H. Seltz and B. De Witt,4 25o°C. A temperature of 247°C. appears to have been generally accepted in recent years; it is the value most frequently obtained by the method of cooling curves. Values below 247°C. have usually been obtained by inferior cooling-curve techniques; those above 250°C., by the method of heating

Jan 1, 1943

By W. S. Pellini, F. N. Rhines

In many of the otherwise well established alloy phase diagrams the solidus curves (temperatures at which liquid first appears upon melting) have not been located accurately, chiefly because the experimental techniques that have been most popular for determining solidus temperatures have been both cumbersome and subject to large errors. C. E. Homer and H. Plummerl have described a sensitive and at the same time a very simple technique for locating the solidus curves in a number of alloys of tin. Their method consists simply in noting the temperature at which a specimen of the alloy ruptures under the influence of a light bending force. Although this method is not new, it has been little used for this purpose in the past; nevertheless, it appears so attractive in its possibilities of speed, simplicity, and precision that the investigations presently to be described were undertaken to verify its merits. The redetermination of the solidus and eutectic temperatures of the lead-antimony system was employed as a medium of experimentation. New values obtained in this way are believcd to be sufficiently precise to warrant a revision of the currently accepted lead-antimony phase diagram (Fig. I). Determinations of the solidus of the lead-rich lead-antimony alloy series have been published by X. S. Dean2 and by E. E. Schumacher and F. C. Nix. Their points are represented in Fig. I. In their work the solidus was not located at antimony collcentrations greater than 2 per cent; the curve was presumed to meet the eutectic horizontal at an antimony concentration of about 2.5 per cent. In the present studies the solidus has been traced to 3.5 per cent, where the eutectic horizontal is intersected (Table I and Fig. I). Within the range investigated by Dean and by Schumacher and Nix the agreement with their values is good. H. Seltz and B. De Witt,4 on the basis of activity measurements, have calculated that the intersection of the solidus and the eutectic reaction horizontal should lie at 3.86 per cent of antimony. The following determinations of the eutectic temperature have been reported: Roland-Gosselin,5 228°C.; Ewen,6 228OC.; J. E. Stead,7 24g°C.; Campbell,8 228°C.; W. Gontermann,9 245&apos; to 252°C.; R. Loebe,lo 245°C.; E. Heyn and 0. Bauer,ll 245°C.; H. Endo,12 250°C.; R. S. Dean,= 247&apos; to 258°C.; E. Abel, O. Redlich, and J. Adier,13 245°C.; W. Broniewski and L. Sliwowski,14 250&apos; to 252°C.; H. Seltz and B. De Witt,4 25o°C. A temperature of 247°C. appears to have been generally accepted in recent years; it is the value most frequently obtained by the method of cooling curves. Values below 247°C. have usually been obtained by inferior cooling-curve techniques; those above 250°C., by the method of heating

Jan 1, 1943

By E. I. Larsen, F. R. Hensel

According to statements by Guertler1 Smith and Hamilton were the first to study the copper-titanium alloys, but owing to the presence of large amounts of impurities their data are inconclusive. M. A. Hunter and I. W. Bacon later investigated the electrical conductivity and the temperature coefficients at room temperature. The present writers reported their results2 in November, 1930. Recently Kroll published data on copper-titanium alloys3 which agree closely with those obtained by the authors. Material Tested The titanium used was in the form of square sintered rods, the analysis of which runs as follows: titanium, 95.4 per cent; silicon, 0.7; iron,l.8; aluminum, 1.4; copper, 0.1; manganese, 0.05. The ingots were prepared in a high-frequency induction furnace in air atmosphere. Their analyses are given in Table 1. Up to 5 per cent titanium the alloys could be forged. Above that amount they were red short and broke up easily. Owing to their rapid absorption of nitrogen and oxygen from the air, the alloys with the higher amounts of titanium tend to form surface films which greatly increase the casting difficulties, especially when small masses of metal are handled. It was, however, possible to prepare sound ingots up to 25 per cent titanium. Thermal and X-ray Investigation The cooling curves of some of the alloys are plotted in Fig. 1, and R tentative diagram constructed from these data is given in Fig. 2. From this it is evident that the solid solubility of copper for titanium is approxi-mately 4 to 5 weight per cent titanium at 878" C., which is the eutectic temperature. The melting point of copper is lowered gradually by adding

Jan 1, 1932

By H. R. Deeth, C. J. Koenig

About ten years ago nepheline syenite was introduced to the ceramic industry and the material has now found application in the various branches of the industry, namely, as a vitrifying agent in white-wares and as a source of alumina and alkalies in glasses, glazes, and porcelain enamels. Spencel described the early mining and processing developments regarding this material. Since the time of his article many research papers have appeared relating to the usage of nepheline syenite but little has been published relative to subsequent mining and processing methods. A complete indexed review of the literature was issued recently by Ohio State University.2 Since "Lakefield" nepheline syenite from Blue Mountain, Ontario (Fig I); is the only commercial ceramic-grade nepheline syenite now being marketed on this continent, discussion is limited to this operation carried on by American Nepheline Limited, Lakefield, Ont., and its subsidiary in the United States, American Nepheline Cory. at Rochester, N. Y. The Deposit Blue Mountain is a long ridge rising to an elevation of about 350 ft at its highest point above the surrounding country and extending for about six miles in a northeasterly direction across Methuen township, Peterborough County. The rock of the Blue Mountain central alkaline intrusive is fine grained, light colored and of even granitic texture. The solidified mass consists predominately of the minerals albite, nepheline and microcline in order of abundance. The average mineralogical composition for the deposit obtained by a study of 112 samples taken regularly over the whole formation is as follows:3 Volumetric Mineral Per Cent Albite.................... 54 Microcline................ 20 Nepheline................ 22 Muscovite................ 2 Mafics.................... 2 (Biotite, hastingsite, magnetite) Total................... loo The mineral nepheline (or nephelite) belongs to the feldspathoid group but is lower in silica content than are the feldspars. It is a silicate of soda, potash, and alumina (NaKAl2O32SiO2). Its presence with albite (Na2oA12O3 6SiO2) and microcline (K2O A12O3 6SiO2) gives the Blue Mountain deposit an alkali content of 15 pct and an alumina content of approximately 24 pct. While this huge alkaline mass is somewhat variable mineralogically, it has a uniform chemical composition. When the iron, mostly in the form of magnetite, is removed during processing, a remarkably uniform finished product is obtained. Geological surveying has disclosed many million tons of nepheline syenite in the Blue Mountain deposit. Diamond drilling in the area where mining is now being carried out indicates a block of about one million tons.

Jan 1, 1949