Search Documents

By NRMR Bhargava

With the increasing use of lead-free solder alloys, low melting point alloy is often required due to the heat- sensitive parts or substrates in modern electronic devices. For such demand of low melting point, the nanostructure lead- free solder alloy, having excellent metallurgical characteristics and a melting point of <215oC, were developed by mechanical attrition of conventional lead free solder alloys (Sn-Ag-Cu, Sn-Ag and Sn-Cu). The decrease in melting point due to nanosize effect was calculated theoretically as function of particle size and the theoretical results were compared with experimental values measured by differential scanning calorimetry. The newly developed alloys have eutectic composition of Sn-3.5Ag-0.7Cu, Sn-3.5Ag and Sn-0.7Cu and the melting point depression found to be 5.10C, 4.10C and 6.20C when the bulk alloys reduced to 80 nm, 92nm and 96nm sizes respectively.

Jan 1, 2009

By Nan Wang

Based on the commercial computational fluid dynamics software, Fluent, the fluid flow and temperature field in an iron-bath reactor were simulated numerically, and the effects of top-blown and side-blown operating parameters on the mixing time of iron bath, distribution range of oxygen in top space, and post-combustion ratio were investigated. The simulated results showed that the mixing time of iron bath increased initially and then decreased with the increase of inclined degree and immersion depth of side-blown lance. The distribution range of oxygen became wider as pulling the top lance away from the iron bath. Furthermore, post-combustion ratio was reduced given the top lance was too close the bath. The simulation results provide theoretical base for the process optimization of iron-bath reactor and further development of new type iron-bath smelting reduction process.

Jan 1, 2009

By Katsuyoshi Kondoh

The utilization of silica particles originated in rice husks as reinforcements of magnesium composites was discussed. By using the solid state reaction of rice husk silica particles with magnesium powder, P/M magnesium based composites dispersed with the magnesium silicide (Mg2Si) and magnesium oxide (MgO) were fabricated. High-purity silica particles were originated from rice husks, one of the major agricultural wastes, via the citric acid leaching treatment and combustion in air. The effects of the silica particle characteristics such as size, crystalline and porous structures, on the reactivity of silica and magnesium to synthesize Mg2Si intermetallic were discussed. Amorphous silica was more useful for this reaction than crystalline one. The reactivity of rice husk silica was superior to that of the conventional mineral silica particles because of not only its amorphous structure but the larger specific surface area due to their pore structures. In the case of the green compact of the mixture of the rice husk silica and Mg powder, the silica particle size was not effective on the reactivity because the coarse particles were fractured into fine ones by cold compaction. The distribution of Mg2Si intermetallics of magnesium powder composites consolidated by SPS process was investigated by XRD and SEM-EDS analysis. Their mechanical and physical properties were also evaluated in detail.

Jan 1, 2009

By Cem Colakoglu

In this study, nickel containing iron alloys were produced by carbothermal reduction of lateritic nickel ores obtained from Manisa - Caldag region of Turkiye in order to investigate the reaction mechanism of nickel and cobalt. In the experiments, the lateritic ore containing 1.58 wt.% Ni and 0.12 wt.% Co was calcined in a semi-pilot scale rotary furnace at 1100°C for 1 hour. Then, a mixture of calcined ore and metallurgical coke was reacted in sintered alumina crucibles using a graphite resistance tube furnace at different time (0- 60 min) and temperature (1500-1600°C).

Jan 1, 2009

By M. I. Brasileiro

The use of experimental design to the study of mixtures has found a wide range of applications, even in laboratory scale or in industrial development works. The aim of this work was to maximize granite sawing waste content in ceramic tiles using experimental design. Based on the raw materials, specific formulations were developed using the experimental design. The raw materials were mixed and sample bodies were produced using uniaxial pressing. The sample bodies were fired and characterized in terms of water absorption, mechanical strength and X-ray diffraction. Regression models were adjusted relating the water absorption and mechanical strength with the amount of raw materials. The results showed that the methodology of experimental design maximize the content of wastes incorporated in ceramic tiles formulations. Formulations containing up to 40% of waste can be used for the production of ceramic tiles.

Jan 1, 2009

By Hongyang Cao

The iron constituents selectively separated from the modified copper slags by magnetic separation and flotation.were studied. The results of magnetic separation for modified copper smelting slags show that the grinding size, current intensity and dispersant agent had great influence on grade, and recovery ratio of TFe in preparation concentrate; The results of flotation for magnetic concentrate show that the positive flotation of sodium oleate negatively upgrade the grade of magnetic concentrate, but the reverse flotation of lauryl amine and soluble starch are effective. The grade of TFe can reach 54% and the recovery ratio can reach about 90% in magnetic concentrate, when the grinding size is 45.8µm and the current intensity is 2.5A. The optimal effect is obtained by using lauryl amine as collector and soluble starch as depressant to reverse flotate magnetic concentrate, and the grade of TFe is upgraded 2.37%.

Jan 1, 2009

By Won C. Park

Experiments showed changes in the mineral content of dolomitic oil shale at temperatures and exposure times which bracket conditions encountered during in situ retorting. Laboratory results correlate with cores from a spent in situ retort at Occidental&apos;s Logan Wash test site at Garfield County, Colorado. Dolomite, CaMg(CO3)2, decomposes rapidly to form periclase, MgO, calcite, CaCO3, and CO . Both calcite and periclase are intermediate products that can be stabilized by CO atmosphere at lower temperatures, while steam accelerates the formation 2 of silicates. The decarbonation of calcite appears to involve a direct reaction with both quartz and periclase in forming these silicates. Decarbonation preceeds the formation of akermanite, Ca2 MgSi 207, and diopside, CaMgSi 206, within several hours of heating and is followed by the nucleation of forsterite Mg2SiO4, and monticellite, CaMgSiO4. Under in situ retorting conditions, akermanite and diposide are the major minerals above 800°C. Equilibrium is not attained within 200-300 hours. In situ retorting temperatures above 800°C for extended periods of time should reduce potential ground water leaching by the formation of silicate minerals. These silicates are less soluble than free lime, magnesium or alkali oxides. There is a corresponding decrease in the natural pH of these silicates from approximately 12 down to 7.5 to 9:

Jan 1, 1981

By A. Broussaud

An original methodology has been developed for steady state simulation of selective grinding and mineral liberation in rod and ball mills. Three fundamental aspects of the methodology are presented successively : modeling ore texture, modeling grinding and its selectivity, and modeling mineral liberation. The methodology for modeling ore texture includes the conversion of 2D data into 3D reconstructed information and the use of the BILCO coherent material balance software. The models for grinding Simulation are classified into three levels, corresponding to three levels of available experimental data. All models account for grinding selectivity and for variations of engineering para-meters and operating conditions. An algorithm has been introduced to forecast mineral liberation, compatible with accurate simulation of selective grinding, which generates reasonable results.

Jan 1, 1987

By D. C. Lynch

While a sizable amount of data exist as to the activity and distribution of minor elements between matte and metal, there has been no unifying theory presented delineating the form of dissolution of these elements in molten sulfides. In order to alleviate that deficiency the literature concerning the behavior of As, Sb, Bi and Pb in mattes is reviewed. Models present in the literature, regarding the thermochemical behavior of minor elements, are tested, and new models are presented and evaluated using thermodynamic theory. The results of those analyses are used to predict optimum conditions for the volatilization of minor elements. The dearth of data on the behavior of minor elements in nickel mattes requires that this review focus on copper- iron mattes. An effort is made, however, to utilize basic knowledge regarding nickel sulfides and the interaction of nickel with the minor elements to predict the behavior of those elements in nickel-copper and nickel-iron mattes.

Jan 1, 1993

By Jeffrey D. Winterton

Keywords: Copper, ion exchange, sulfonic acid, bis-picolylamine, ion exchange modeling, ion exchange kinetics As part of an investigation into the feasibility of using ion exchange resins to recover copper from aqueous waste streams generated during the manufacturing of semiconductor devices, the uptake of copper onto two ion exchange resins was investigated. The resins studied were DOWEX G-26, a standard gel type sulfonic acid resin, and DOWEX M4195, a macroporous chelating resin with a bis-picolylamine functional group. The equilibrium and kinetic behavior of the uptake of copper were investigated over a range of copper concentrations with constant sulfate concentration and different levels of acidity. The homogeneous structure of the G-26 resin yields equilibrium relationships that fit the Langmuir equation, and equilibration times of less than 30 minutes. The uptake behavior of M4195 is complicated by the need to absorb co-ions to maintain electroneutrality, resulting in uptake profiles that change character with increasing copper concentrations, and extended equilibration times.

Jan 1, 2005

By W. J. Mitchell

During the months of April and May 1992, the Phelps Dodge Hidalgo smelter underwent a major turnaround. This was the third such turnaround in the life of the facility which was commissioned in 1976. During the third furnace campaign, the smelter processed 5.2 million tons of concentrate producing 2.6 billion pounds of anode copper over a 7.5 year period. The critical path on the fifty-nine (59) day turnaround schedule was the reconstruction of the Outokumpo flash furnace which integrated some modifications with standard rebuild practices. Modifications included incorporation of horizontal cooling jackets throughout the furnace settler as well as the installation of castable refractory in the reaction and uptake shafts.

Jan 1, 1993

By S. Djaroudib

Keywords: iron recovery, hematite, hydrolysis, polyvinylpyridine The precipitation of hematite (Fe2O3) from ferric chloride media at ambient pressure and at temperatures below 100°C was studied as part of a program to recover a marketable iron product form metallurgical processing streams and effluents. Hematite was formed in preference to ferric oxyhydroxides (e.g. ß-FeO?OH) by controlling the precipitation conditions, especially by adding Fe2O3 seeds. The extent of the hydrolysis reaction was found to depend primarily on temperature and on the free-acid concentration. As to the latter, the controlled addition of an adsorbent of free acid, in our case the anionic resin polyvinylpyridine (PVP), was shown to allow for the nearly complete removal of iron as readily filterable Fe2O3. The hematite product typically contains = 63% Fe and = 1.5% Cl, and its composition does not change appreciably upon repeated cycling using regenerated PVP.

Jan 1, 2005

By Taegong Ryu

A thermal plasma process was used to synthesize nanosized tungsten carbide -cobalt composite powder, in which ammonium paratungstate and cobalt oxide were reacted with a gas mixture containing CH4, H2 and Ar. The reduction and carburization of vaporized precursors produced nanosized tungsten carbide (WC1-x) - cobalt composite powder, which sometimes contained small amounts of W2C and/or W phase. The effects of gas composition, plasma torch power, and the flow rate of plasma gas on the product composition and grain size were investigated. The grain size of synthesized tungsten carbide powder was less than 20 nm. The synthesized composite powders were also subjected to a hydrogen heat treatment to fully carburize WC1-x, W2C, and W phases to the WC phase as well as to remove excess carbon in the product. Finally nanosized WC-Co composite powder of grain size less than 50 nm was obtained.

Jan 1, 2009

By Z. Sun, H. A. Davies

"Current understanding of the mechanisms by which glassy and crystalline thin ribbons are formed in high speed continuous casting processes is considered. A computer model of the combined heat and momentum transfer during melt spinning has been developed. The influence of roll velocity and of heat transfer coefficient (between the melt and the roll) on the temperature and velocity distributions within the melt puddle is analysed and the thickness of the extracted ribbon computed. The relative importance of heat and momentum transfer under different conditions is assessed and differences between the casting of crystalline and amorphous strip highlighted.IntroductionHigh speed continuous casting of thin metallic ribbon and strip is currently of considerable interest both to metal processers and to those studying process mechanisms. The practical interest arises both from the potential economic benefits to be gained from a shorter and more energy-efficient production route and from the ability to obtain extended and uniform thin strip having a metastable microcrystalline or amorphous structure with enhanced or unique properties. The latter arise from the rapid solidification associated with the cooling of very thin sections of melt brought into intimate thermal contact with one or two rapidly moving heat sinks.The principal processes for casting thin strip include free jet, chill-block melt-spinning (GBMS) (1), melt drag (MD) (2), planar flow casting (PFG) (3) and twin-roll casting (TRG) (4). For the first three of these, all essentially variants of melt-spinning, melt flows through a nozzle onto the circumferential surface of a rapidly rotating roll, whereas for TRG the melt passes into the nip between two contra-rotating rolls. We shall be concerned in this paper with the single-roll melt spinning processes only. For these, a puddle is established where the melt contacts the roll surface and the length of this puddle l is a function of the process conditions, notably the circumferential velocity of the roll Us and the volumetric flow rate of the melt Q. The contact time between any point on the roll surface and this puddle, or residence time eR(= l /Us) determines the thickness of ribbon t extracted from the puddle. This thickness, in turn, partly governs the cooling rate T and the amount of undercooling in the melt and thus the microstructure of the solidified ribbon."

Jan 1, 1986

By A. Gibson

Most methods for the treatment of scrap printed circuit boards do not reclaim the components in working order as the boards are either fed to a copper smelter, to recover the valuable elements, or, simply landfilled. This work reports the dissolution of the solder in fluoroboric acid containing Ti4+ ions which was particularly selective for solder, allowing the components to be recovered. The solder was subsequently electrowon from the leachant. The boards were then shredded and the copper dissolved in ammonium sulfate and, then treated via solvent extraction to give an electrolyte suitable for electrowinning. The remainder of the metals were dissolved aqua regia, silver remained unattacked by the aqua regia, palladium precipitated as Pd(NH4)Cl6 in the presence of zinc and nickel, the gold was removed by solvent extraction and precipitated as nanoparticles. The aqua regia was then diluted and the zinc and nickel separated by solvent extraction.

Jan 1, 2009

By C. E. M. Meskers

End-of-life Electronic and Electrical Equipment, o_cially called WEEE, is unjustly regarded as mainly a waste management problem. What is structurally overlooked is the enormous resource impact of these devices. EEE rep- resents a tremendous metal resource, which should be uti- lized through e_ective recycling, which has a much lower environmental footprint than primary production. The actual amount of end-of-life EEE recycled today is embar- rassingly low since insu_cient EEE is collected and part of the collected EEE is exported to developing countries, where it is largely not entering o_cial recycling systems. To achieve a global recycling society issues like technol- ogy, economics, life cycle structure, stakeholder aware- ness and legislation have to be addressed in a global, co-operative manner so that sustainable closed product cycles can be obtained. Requirements for a "global re- cycling society" are de_ned to address today&apos;s reality of global ows of used consumer products, taking into ac- count the likely needs of the future.

Jan 1, 2009

By Victor Raul Alarcon

The Ilo Refinery was commissioned in 1975, with a cathode production capacity of 150,000 tpy. In 1994, Southern Perú Copper Corporation (SPCC) purchased the Refinery from Minero Perú SA. Subsequently, in November 1999, Grupo Mexico acquired control of Southern Perú. The anode production facility is located at the Ilo Refinery. A number of effective operating and quality control practices have been developed that have improved anode quality, as well as increasing anode production capacity to 350,000 tpy. These, and other optimization actions have allowed for a current density increase from 213 A/m2 to 275 A/m2, while maintaining current efficiency at 98% and sustaining the high quality of the cathode. The paper will outline the scope of operational practices in the Anode Plant and provide some discussion on the Ilo Smelter modernization project, and the resulting impact on the existing anode plant.

Jan 1, 2005

By Ramona Prillhofer

Salt slag is a waste product produced by the recycling of aluminum. In most European countries (e.g. Austria, Germany) the landfill disposal of this waste is forbidden because the slag contains soluble salts and these represent a potential source of pollution to the surface and groundwater. Additionally, consisting metal and some compounds in the salt slag can react with water and resulting from this, noxious gases are generated. The recovery of useful materials from these wastes is accordingly both environmentally necessary and economically feasible. This study describes a complete recycling-process for the salt slag, which includes a leaching-cristallization-process to obtain the oxidic residue, a pyrometallurgical-step to clear the oxidic residue and finally an extensive characterization of the achieved products. Due to the increasing price of raw materials, the utilization of the oxidic residue into commercial products has been investigated and application possibilities will be discussed.

Jan 1, 2009

By Junli Xu, Xianwei Hu, Kaiyu Xie, Liangxing Li, Zhongning Shi, Zhaowen Wang, Bingliang Gao, Aimin Liu

Al-Ti master alloys were prepared by aluminothermic reduction between the dissolved titanium dioxide and aluminum in cryolite melts at 960oC. The kinetic analysis by differential scanning calorimetry indicated that the apparent activation energy of the reaction of reducing titanium dioxide by aluminium is 22.3 kJ/mol, and the reaction order is 0.5. The products were analyzed by means of X-ray diffraction, X-ray fluorescence, scanning electron microscopy and energy dispersive spectrometer. Results from X-ray diffraction showed that the phase compositions of produced alloys are Al and Al3Ti. In addition, Al-Ti master alloys containing 2-6 mass% Ti were formed at different reduction time of 2-5h in aluminothermic reduction experiment.

Jan 1, 2015

By M. Bilal Khan

Thermal stress relief by means of a typical heat treatment cycle (660oC for one hr) is compared with the one achieved through vibratory stress relief at resonant and multiple resonant frequencies for the D-406 HSLA material. Our analysis of the data is based on the microhardness profiles measured for the entire length of scales, namely, base metal, heat affected zone (HAZ) and the weld bead itself. The profiles obtained using the two techniques mimic each other, for an equivalent 70% stress relief level. The data are further qualified by impact testing wherein the zone of interest is projected in the retention groove to provide impact by the pendulum striker in the Charpy mode. Higher equivalent energy absorption in the treated specimens confirms the efficacy of the vibratory method. The present work rectifies earlier anomaly where heat treatment has been reported at 310oC for the same material.

Jan 1, 2009