An expression for the distribution ratio of arsenic between slag and copper matte or liquid copper was developed by both, an extension of the Reddy-Blander moderl for deriving a priori the arsenic capacity, and by a relationship between the arsenic capacity and the arsenic distribution ratio. In this study, the a priori arsenic capacities in the FeO-SiO2, CaO-SiO2,MgO-SiO2, FeO-CaO-SiO2, FeO1.5-CuO0.5-MgO-SiO2, FeO-FeO1.5-CuO0.5-CaO-Mgo and FeO-FeO1.5-CuO0.5-CaO-Mgo-SiO2, slags were calculated at 1573 K. The a priori arsenic distribution ratio between the FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slag and copper matte mn (Lx, )' and between the FeO-FeO1.5-SiO2 or FeO-FeO1.5-CuO0.5*-CaO-Mgo slag and liquid copper (Ls/cua) were calculated. The model calculated data are found to be in good agreement with the reported experimental data. The availability of reliable thermodynamic data for slag components and impurities in the slag-matte- metal system is essential for the accurate prediction of impurity capacities and distribution ratio data. The arsenic distribution ratio model developed here, can be extended for predication in multi-componet slags and mattes or liquid metal, and thereby may lead to the development of new slag systems for the efficient removal of arsenic in the copper smelting, converting and refining processes,

Jan 1, 2003

By Thomas Gliick, Jianming Lu, David Dreisinger

"The recovery of manganese from the Boleo project of Baja Mining is via an acid oxidation and acid reduction process in seawater. Manganese as manganese dioxide is leached into solution as manganese sulphate with the addition of sulphur dioxide gas as a reductant and then precipitated as a manganese carbonate. The use of the manganese carbonate intermediate to produce electrolytic manganese metal (EMM) has been extensively studied. The manganese carbonate can be used in place of natural (MnC03) or reduced ores (MnO) of manganese as a feed to the EMM plant. Manganese carbonate can be dissolved in spent electrolyte from manganese plating, followed by purification using ammonium sulphide precipitation of minor elements and then electrowinning in a selenium free process. The results of small cell testing of manganese electrowinning are reported.IntroductionThe Boleo Project of Baja Mining is a greenfields development currently under construction approximately 5 km north of the town of Santa Rosalia, Baja California Sur, Mexico. The Boleo property is held by the Mexican company, Minera y Metalurgica del Boleo S.A. de C. V. (MMB). MMB is owned 70% by Baja Mining Corp. and 30% by a consortium of Korean companies consisting of KORES - Korea Resources Corporation, LS Nikko Copper, Hyundai Hysco, SK Networks and lljin Copper.The Boleo deposit has Measured and Indicated resources of264.7 million tonnes grading 1.50% copper equivalent (CuEq) & Inferred resources of 159.9 million tonnes grading 1.15% CuEq. The calculation of copper equivalent is based on a combination of metal prices and predicted metallurgical recoveries (Table I). The metallurgical recoveries have been confined by extensive bench and pilot plant testing. Proven and probable reserves are available at Boleo to provide for more than a 30 year mine life. Initially, 25 years of mine life and 23 years of process plant operation have been scheduled in the February 2010 Technical Report Update (www.sedar.com)"

Jan 1, 2012

By René Winand

Due to chemical and electrochemical behavior of the most common additives in copper electrorefining i.e. gelatine, thiourea and chloride ions, it is essential to simulate as far as possible true industrial practice while performing laboratory experiments. The three additives must be studied simultaneously, and added continuously to the electrorefining cell. Ratio electrolyte volume to cathode area; ratio bleed flow to cathode area; hydrodynamic conditions; residence time of electrolyte in the cell; current density; electrolyte and soluble anode must be as near as possible to industrial ones. Experiments performed in the author's laboratory show that under these conditions, reproducible results can be obtained at normal industrial current density and at high current density as well. Problems are however still encountered when developing a sensor for additives monitoring, due to electrolyte redox potential and to substrate influenced thin layer deposition.

Jan 1, 1995

By Józef Czemecki

Polish copper concentrates are characterized by high levels of impurities, particularly Pb and As. Two technologies are being used for copper concentrate smelting at KGHM Polska Meidz S.A., namely the shaft furnace process (Legnica Copper Smelter, Glogów I Copper Smelter) and a single-stage process for direct to blister concentrate smelting in a flash furnace (Glogów II Copper Smelter). Both technologies are used at different physical and chemical conditions which results, in different impurities behavior. The paper presents flow sheets for copper production in a plant using the shaft furnace process and in another in which a single stage flash process is used. The metals distribution in particular semi-products is given as well as a method for elimination of impurities from the copper production cycle. Methods are also discussed for alloy and matte converting and copper refining to obtain low Pb and As concentrations in anode copper (0.3% Pb and 1500 ppm As maximum) that are being used in the KGHM Polska Meidz plants. Useful co-operation between the plants using different technologies, aimed at the limiting the effect of undesired impurities on the quality of blister copper produced, is also described.

Jan 1, 1998

By Lztok Peruš, Goran Kugler, Matevz Fazarinc, Milan Tercel

"Hot deformability of M42 tool steel additionally alloyed with cobalt and molybdenum was investigated. Hot-compression tests were carried out in the temperature range 850 °C -1200 °C, at strain rates range 0.001--6s-l up to strain of0.9. Field-emission scanning electron microscope and optical microscopy were used for characterization of microstructure of deformed samples, which revealed a very complex precipitation of carbides that strongly depends on the soaking temperature, the soaking time, the stress state, the deformation temperature as well as on the strain rate. Gathered data was used to calculate the processing parameters such as process maps, apparent activation energies and strain hardening exponents. For better understanding of thermodynamical properties of the studied steel a simultaneous thermal analysis was conducted. Furthermore the analysis of phase equilibrium was calculated using Thermo-Cale software. On the basis of these studies the optimal soaking temperature and process windows were determined.IntroductionHot workability ofledeburitic tool steels is important economic factor. This means that for each tool steel individuallysafe range of hot working parameters should be revealed. Publications in the literature with regard to the hot workability of tool steels are rare and therefore more information from this research area is desired.The relatively low hot workability of ledeburitic tool steels, i.e. steels in which the solidification is completed by a eutectic transformation of the residual interdendritic liquid to austenite and various alloy carbides (ledeburitic carbides), is usually characterized by the production of surface and internal cracks during the hot deformation."

Jan 1, 2013

By Brent W. Madsen

The acid-ferric sulfate leaching of low-grade sulfide copper mine waste provides more than 10 percent of the U.S. supply of new copper, but recoveries and leaching rates are very low. In Federal Bureau of Mines research to improve the leaching process, experiments on 5- to 10-ton lots of mine-run ore were more revealing than bench-scale tests on fine ore. This report discusses the results obtained by leaching run-of-mine and minus 6-inch plus 112-inch samples of low-grade chalcocite-bearing mine waste. The samples were leached for 461 days and 61.6 and 37.7 percent of the copper was extracted from the minus 6-inch plus -112-inch and run-of- mine samples, respectively. A mixed kinetics model was applied successfully to the leaching of the sample with the fines removed where bulk solution transport was not rate controlling. The model, when applied to the run-of- mine ore, gave somewhat higher predicted copper extractions than experimentally determined. Subsequently, oxygen was introduced into the run-of- mine ore, leaching continued for an additional 312 days, and an additional 53.0 percent of the copper was extracted. Before the leaching experiment was dismantled and the residue sampled, the ore was treated with sulfur dioxide and its permeability was improved markedly. The results of each of these procedures are interpreted in relation to the attendant condition of the test.

Jan 1, 1976

By Erwin Flender, Preben N. Hansen, Peter R. Sahm

"Until now FDM-Techniques have been widely used for Modeling Solidification Processes in Castings. Often a rigid, regular type of enmeshment (cubes, , --) have been used. This has the advantage of low CPU-costs, but the disadvantage of a zig-zag presentation of the interface between the casting and the mold. The last point is the reason why FEM-Techniques, giving the possibility of a true presentation of the shape in the enmeshment, are increasingly used. The disadvantage is the high CPU-costs. In this paper, a technique is presented, which uses the FDM-Mesh with the zig-zag presentation of shape and ADI-Algorithms to calculate temperatures and gradients. The new idea is that the calculated parameters are not presented related to the mesh in which they are calculated, but displayed using the true shape of the casting. Such an advantage of both low CPU-costs and shape correct presentation of the calculated results are achieved. IntroductionThe main reason for using a regular type of enmeshment is that it gives the possibility, via ADI-Algorithms, of obtaining a very fast FDM-Technique. The technique presented by P.R. Sahm and P. N. Hansen (1984), and also used by E. Flender (1985), is numerically so stable that average time steps, at least 200 times larger than the limit given by the explicit FDM-Technique, can be applied. To obtain reasonably good results, average time steps in the range of 20 to 50 times the explicit limit seems to be applicable. It should be pointed out,however, that FDM-Techniques can be used on arbitrary nets, the disadvantages being the same as for the FEM-Techniques. This has, among others, been discussed by P.R. Sahm and P.N. Hansen (1984)."

Jan 1, 1986

By Georgios N. Anastassakis, Nickolaos Georgiou

"Soil contamination by oil as well as by other organic pollutants poses a major problem to the environment. Various methods have been used to remove organic contaminants from soil, such as: biological, thermal, chemical and physical. Methods based on Mineral Processing principles have also been used (cyclone separation, gravimetric separation, attritioning and washing). This paper studies the possibility to remove a rich-in-contaminant soil fraction by applying flotation. The contaminated soil was artificially prepared by mixing soil with diesel fuel. Sodium dodecylsulfate (SDS) and a tertiary amine (TA) were used as collectors. The effect of collector quantity added and conditioning time was studied. The results showed that the removal of a rich-in-contaminant soil is feasible while a clean fraction is also obtained. In several cases, the removal of oil-contaminated soil approaches or reaches 100%. Introduction Human activities are intimately associated with environmental pollution to the air, water and soil, as well. Soil pollution from inorganic and organic compounds is of equal importance with that of air and water, as it results in soil degradation and its concomitant problems with respect to meeting the human needs (house building, agriculture etc). Heavy metals along with their compounds are encountered among the most usual soil inorganic pollutants. The corresponding organic soil-pollutants are oil, oil-derivatives, pesticides, various aromatic (benzene, phenols, cresols, toluene etc) and poly-aromatic (naphthalene, anthracene etc) hydrocarbons, as well as various other organic compounds (pyridine, cyclo-hexane etc). Oil remains the basic energy source sharing 38% of the global needs, being followed by coal and gas with a share of 26 and 21% correspondingly [1]. The entire activities related with oil production, transport and consumption promote pollution in the air, water and soil. Consequently, soil pollution from oil is favoured at refineries, storage sites (due to possible pipe and tank leakage, tank cleaning works, loading and transportation) and, finally, at the oil-selling sites. Oil (or diesel-oil) fuel is a mixture of hydrocarbons, with 10-20 carbon atoms in the chain of each. It is mainly composed of paraffins, naphthenes and various aromatic compounds. In general, oil is composed of 20-30% in aromatic compounds, 5-6% in naphthenes and the rest is paraffins [1]."

Jan 1, 2008

By Ann M. Hagni

Flash reduction of zinc oxides is an alternative, environmentally safe method to leaching and electrowinning for zinc recovery. Zinc and lead are volatilized in a flash reactor, a non-hazardous residue is generated, and the fuel source is inexpensive coal in the flash reduction process. Results from experimental laboratory tests yielded low zinc recovery for this process. Mineralogical and textural characterization of the residues from the flash reduction tests for different feed materials and temperatures were conducted to determine the cause for the low zinc recovery. Reflected light microscopy, cathodoluminescence microscopy, scanning electron microscopy-energy dispersive spectroscopy, and X-ray diffraction were utilized in this applied mineralogical research. The original zinc calcine is composed primarily of fine-grained, iron-bearing zincite particles, 25-40 um in diameter, in a porous texture. Pellets processed at 1150°C were found to produce reaction rims of franklinite-magnetite-jacobsite solid solution that are 125-200 um thick and surround cores of unreacted iron-bearing zincite in a Zn-Fe-Si-Ca glass matrix. The reaction rims have subsequently oxidized to form an outer 10 ~m thick rim of hematite. Slags from calcines processed at 1275°C are primarily triangular particles with porous centers, cenospheres, and spheres of iron-bearing zincite, in addition to rectangular particles composed of non-porous franklinite-magnetite solid solution cores with iron-bearing zincite rims. Slag particles from calcine processed at 1200°C are predominantly 100-250 ~m triangular-shaped, spheres, and cenospheres containing fine-grained franklinite and franklinite-magnetite solid solution in an iron-bearing zincite matrix. Slag from calcine processed at 1300°C are also predominantly 1 00-250 um triangular-shaped, spheres, and cenospheres but contain coarser-grained iron-bearing zincite. The zincite in the penets and the slags typically contain 10-20% iron. Based upon these mineralogical observations, it is concluded that the significant amounts of iron in the zincite prevent volatilization of the zinc in the flash reduction process.

Jan 1, 1995

By B. L. Chulu

In the carbothermic reduction of lead sulfate to produce lead, the inclusion of soda ash (Na,CO,) in the charge provides for the control of sulfur dioxide in the effluent gas. An important mechanism in the process appears to be the carbothermic reduction of the sodium carbonate whereby sodium gas and carbon monoxide are produced. These intermediates then participate in the reduction of the lead sulfate to produce lead metal and stable sulfur species in the molten slag phase. In addition, there is some evidence that the presence of lead metal in the charge may also serve to increase the lead recovery in the process. These aspects were investigated by conducting laboratory-scale smelting tests with small charges (;3g), at 1173°K(9000C). Recovery did not exceed 74w% and the role of incipient lead metal in the charge could not be clearly assessed.

Jan 1, 1993

By J. R. Kiji

The Cerro Matoso S.A. mine and smelter, in the Cordoba lowlands of northwestern Colombia, consist of a dedicated laterite nickel mine, ore blending, drying and an RKEF process to produce high-quality ferronickel. At a project investment of $400M, first production of ferronickel was in September 1982, and in its inaugural year CMSA produced 6,150 tons of contained Ni from a mined ore grade of 3.2% Ni. Initial operational difficulties resulted in a number of furnace run-outs, which impacted ramp up to design ore throughput of 128 dry t/h Since then CMSA has steadily incorporated process improvements and initiatives to take the single line operation to an ore throughput of 175 dry t/h. A second 175 dry t/h line was added in 2001 (investment of US$ 300M) to consolidate CMSA as one of the world's lowest cost Ni producers with an installed annual production capacity of 50-55,000 tons Ni. The most recent addition is commissioning of Phase I of an ore-upgrading project to counteract the effect of declining ore grades. Keywords: Laterite, ferronickel, pyrometallurgy, smelter.

Jan 1, 2004

By Ross Baldock, Ross Andrews, Gu Helin, Lan Xu, Markus Reuter, Song Xingcheng

"A commercial lead smelter using Outotec Ausmelt TSL Technology has been successfully commissioned and put into operation at Yunnan Tin Company Ltd operations near Gejiu City, in Yunnan Province, China. The plant was commissioned in July 2010 after three years in the design and construction phase. The process uses a three stage batch process to produce lead bullion and zinc fume, and a slag that is low in metal values. The paper provides details of this lead smelting project, including the theoretical evaluation of the multi-stage process chemistry, engineering design, plant commissioning and the final operation. Comparison of the design targets and actual performance of the plant is emphasized. The fast ramp-up to full production of the largest Ausmelt TSL lead furnace built to date is highlighted.IntroductionIn 2002, Ausmelt and Yunnan Tin Company (YTC) successfully commissioned a smelter to modernise the Yunnan Tin smelter in Gejiu City, Yunnan Province, China. A single Ausmelt furnace was installed by YTC to process tin concentrate and revert materials, to produce YT Brand tin product. The advanced Ausmelt Technology furnace at YTC replaced seven existing reverberatory furnaces and provided a flexible, energy efficient and environmentally beneficial system to complement the world leading refinery facilities of YTC."

Jan 1, 2012

By Adam Powell, David Dussault

"Electric Field-Enhanced Smelting and Refining is a process for driving the reaction between carbon in hot metal and iron oxide in slag, for example, in a steelmaking reactor. This process involves inserting electrodes into the slag and metal phases, such that the overall reaction FeO + C -> Fe + CO is separated into two half-cell reactions: Fe2+ + 2e· -> Fe at the cathode in the slag, and C + O 2 • -> CO + 2e· at the anodic slag-metal interface. Without the electrodes, the reaction is very slow, but with electrodes, the additional surface area available to the ferrous ions for reduction accelerates the reaction even without any applied bias. When a bias is applied to the electrodes, the electric field across the slag further accelerates the overall reaction.With or without applied bias, the process is first-order in the ferrous ion concentration, and limited by ferrous ion transport to the cathode. To complicate matters, as the liquid iron is reduced at the cathode, the Mullins-Sekerka instability leads to formation of dendrite-like liquid iron fingers which grow into the slag. Because of this, the design of the cathode can have a significant effect on the overall process kinetics, and understanding of the dynamics of these fingers and of their effect on mass transfer is necessary for the intelligent design of the overall process and the cathode in particular.Toward this end, a detailed mesoscopic two-phase slag-metal model is presented here which describes multi component diffusion in the slag and fluid flow in both phases in the vicinity of the cathode. Diffusion in the slag is driven by chemical and electrical potentials. The phase boundary is modeled as a diffuse interface using a phase field approach. Because this electrochemical reaction occurs at high-temperature, the kinetics of charge transfer and adsorption through the double layer are fast relative to transport, permitting the use of simple linear reaction kinetics. This also eliminates the need to discretize the double layer, with the result that charge neutrality may be assumed everywhere in the domain. Introducing electric field dependence of the gradient potential and well height coefficients in the free energy function allows the model to capture electrocapillarity at the interface."

Jan 1, 2001

By N. A. Warner

Fundamental studies on the reaction of limestone or dolomite at high temperature with S02 are extended to the realm of large scale primary copper smelting. Whereas flue gas desulfurisation in the electric power utility industry is concerned with S02 concentrations normally less than 0.5 percent, high temperature smelting gases can have S02 levels approaching 100 percent. The reaction involved is very exothermic so proposals are made in this paper for returning the heat generated in sulfur fixation directly back to the copper smelting process. This integration leads to metal production with lower energy requirements than current technology. The anhydrite reaction product can either be disposed of locally with minimum adverse environmental impact or upgraded to a value-added product. It is assumed, of course, that no viable market exists to support sulfuric acid production.

Jan 1, 1996

By Hong N. Vu, Jitka Jandova

"Gypsum and limestone methods were examined in this study to process zinnwaldite wastes originating from dressing Sn-W ores mined in the Czech Republic. These wastes containing 0.20-0.30% Li and 0.10-0.20% Rb were subjected to magnetic separation to obtain a zinnwaldite concentrate with 1.36% Li and 0.94% Rb. It was observed that processing of the zinnwaldite concentrate with gypsum resulted in almost 96% recovery of Li into aqueous liquors, whilst rubidium extraction was only 25%. At the same time, it is possible to extract almost 92% Li and Rb from the identical zinnwaldite concentrate if the concentrate is processed by limestone method. Lithium carbonate, a final product of both methods was recovered from the refined sulphate solution using K2CO3 as a precipitation agent and/or from unrefined hydroxide solution using gaseous CO2. In the continuation of this study, rubidium will be separated from carbonate solutions after Li2CO3 precipitation as RbAl(SO4)2, an intermediate for Rb2CO3 production. IntroductionLithium is used as an alloying constituent in lightweight alloys, as a heat transfer medium in nuclear reactors and as a component in primary and secondary batteries. With the development of a new generation of electric vehicles, the lithium demand will dramatically grow. Lithium chemicals find extensive application in many industrial branches such as metallurgical, glass, ceramic and pharmaceutical industries. Rubidium compounds are predominantly used in psychiatry and medicine, in magneto-optic modulators, solid-state lasers, phosphors and components of electrolytes for fuel cells. The four most important lithium minerals are amblygonite, spodumene, petalite, and lepidolite. Spodumene LiAlSi2O6 (6.0-7.5% Li2O) and petalite LiAlSi4O10 (3.5-4.5% Li2O) belong to aluminosilcate minerals. Lepidolite (Li.Al)3(Al.Si)4O10(F.OH)2 (3.30-7.74% Li2O), lithium mica, is the most important representative of the mica minerals, a subgroup of the aluminosilicates. It frequently contains 3–5% Rb2O and eventually caesium. Zinnwaldite, which has the general formula K(Li.Al.Fe)3(Al.Si)4O10(F.OH)2 (2-5% Li2O), is regarded as a variety of lepidolite with a high iron content. Commercial amblygonite is a complex phosphate (Li.Na)Al(F.OH)PO4 (up to 9.88% Li2O), however, its deposits have not been commercially exploited because of their small size. Natural brines with a high lithium chloride content are important in the industrial production of lithium [l]"

Jan 1, 2008

By Hideki Yamamoto

A new technology to convert fluoride gas (C2H2F4 : R-134a) contained in the exhaust gases from semiconductor manufacturing plants and refrigerators directly into a harmless substance have been established, thus, presenting a new concept for the disposal of fluoride gases such as CFCs that are associated with the global warming. Experimental results verify that chemical reactions with metal compounds can take place at substantially lower temperatures of 700- 800K as compared with combustion treatment temperatures of 1200-1500K. The reaction product is mainly metal fluoride, which chemically is a harmless material. Furthermore, this process is compact, easily controlled, safe and has low running costs. This paper deals with a new chemical reaction method for the harmless disposal of gases effecting the global warming.

Jan 1, 2003

By Tiejun Chun, Jian Pan, Deqing Zhu, Vinicius Mendes

"Fine manganese fines are characterized by large amount and low price compared to lump manganese ores. However, fine manganese must be agglomerated as EAF (electric arc furnace) feed. In this paper, high quality fired pellets were produced by simulating grate-kiln process to supply the feed for EAF from some imported manganese ore fines containing high combined water. Manganese ore fines assaying 44.47wt%Mn, 5.89wt%Fe, 12.09%LOI and with 72.7wt% ranging between 0.5mm and 8mm, are pretreated up to the particle size of 84.7wt% passing 0.074mm by HPGR (high press grinding roller) twice in open circuit. The finely ground manganese fines were mixed with 1.2wt% bentonite, balled at 15% moisture for 7min in disc pelletizer. The drop numbers, compressive strength and thermal shock temperature of green balls reach 11 times/0.5m, 11 N/pellet and 360oC, respectively. After the green balls drying in the oven, the dry pellets were preheated at 1050oC for 12 min and then fired at 1300oC for 12 min in electric tube furnace. The compressive strength of fired pellets reaches 2621 N/pellet. Therefore, these pellets are high quality burden for blast furnace or EAF due to high mechanical strength and high Mn grade of 49.11wt% and low detrimental elements.IntroductionManganese, mainly using as deoxidizing agent, desulfurization agent and alloying elements, is widely used in the steel company. With the rapid development of iron and steel industry in China, domestic manganese ores cannot meet the requirement, resulting large quantities manganese ores import to China [1-4]. Compared to lump manganese ores, fine manganese ores containing high combined water are characterized by large amount and low price. However, they must be agglomerated as EAF (electric arc furnace) feed. There are three ways to agglomerate the manganese fine ores, sintering, briquetting and pelletizing [5-6]. Compared to the other two methods, pelletizing technology possesses the following superiorities, such as uniform size distribution of product, stabilizing chemical composition of product and lower energy consumption in producing. Therefore, pelletizing is a superior way to treat the fine manganese ores [7]. The systematic research of producing manganese oxide pellets by fine manganese ores containing high combined water was studied in this paper."

Jan 1, 2011

By Batric Pesic

The interactions of mineral-pyrite with T. ferrooxidans were studied by using a cyclic voltametry technique. The interactions with bacteria were carefully examined during the entire growth stage of bacteria (fermentation). Several very important discoveries were made. For example, the pyrite surface invariably drastically changed its properties at the second day of fermentation. Beyond two days of fermentation, the cyclic voltamograms were insensitive to convective diffusion produced by stirring. The SEM study revealed that bacteria populated the pyrite surface at an extremely high density levels. The high density of bacteria, and the solid reaction products formed on the pyrite surface created conditions for pore diffusion which explained why the CVs became insensitive to convective diffusion in solution (stirring).

Jan 1, 1990

By Seyed Mahdi Abbasi, Adel Sheikhhosseini

"This research was conducted to study the changes of microstructure, chemical composition and mechanical properties ofIN718 superalloy after adding aluminum to the ESR process slag. The experiments were performed in VIM and ESR furnaces. The results showed adding 1.5 percent aluminum to the slag increase lave phase in the IN718 samples from 0.34 percent in the base sample to 3.0 percent. It also indicated that the more increase of aluminum in slag cause decrease in the aluminum absorb yield in the superalloy.it is observed that increasing aluminum from 0.7 to 1.1 and then to 1.5 percent caused a decrease of absorb from 91.4 to 76.3 and 74.6 percent respectively due to increasing of aluminum oxidation. According to the results, tensile strength increased and ductility declined in the IN718 samples mainly because of rising the amount of y' volume fraction.IntroductionIN718 superalloy is an iron-nickel base superalloy with constant mechanical properties at medium at high temperatures. For the past seven years a considerable amount of time and effort has been expended by both suppliers and users in the study of Alloy 718 [ 1]. The interest in this material stems not only from the interesting metallurgy associated with the alloy, but with the large usage of the material in numerous applications In fact many people believe that the projected use of this alloy increase significantly over the next several years, The large use of Alloy 718 is the result of its performance in respect to high strength, good ductility, good repair weld ability and from its versatility of being supplied in various product forms. This superalloy is used in wide ranges of industries such as aerospace and gas turbines [2]. In the past more than 20 years many researchers did a lot of work to improve the structure stability of IN718 at high temperatures and intended to develop a new 718 type alloy to be used beyond 650 °C. One of the methods is to control and phase precipitation behavior by means of adjustment of Al, Ti and Nb contents. The other idea is to strengthen the matrix by altering the content of solid solution elements such as W and Co. The adjustment of these alloying elements can change phase precipitation behavior [3]. If detailed information dealing with phase precipitation behavior can be obtained before experimental work for alloy development, a lot of time can be saved and the development cost can also be reduced. In recent years, computer modeling based on experimental data plays an increasing role in alloy design and development. Adding Al to the Iron and Nickel increas the strength of superalloy by formation of y phase and subsequence formation of n phase. Ti in IN718 superalloy also helps the formation of MC carbides and gamma prime phase. Increasing Al/Ti and (Al + Ti)/Nb will lead to form finer particles of y'. More uniform distribution of the precipitates and enhancing stability of y' in IN718 superalloy [ 4]. Adding Al to slag of ESR process can reduce the oxide inclusions because of the strong tendency of Al to oxidation. In addition, tensile properties of IN718 superalloy improve. The most significant inclusions in IN718 superalloy are Alz03 and TiN that were found in agglomerate forms. Thermodynamic calculation results indicate that the effect of increasing Al shows a strong increase in solvus while phase solvus shows mildly decrease when Al level is less than 2%, after that it dramatically decreases [ 5]. Laves phase precipitation and the appearance of phase are occurred when Al content reaches 2%. In fact, when Al content is beyond 1.5%, phase has already precipitated in a considerable scale. Shows the fraction of increases greatly while the fraction of phase decreases remarkably with the increment of Al content. Based on thermodynamic theory, if these particles were not existed in the melt during cooling agglomeration would not accrue and the superalloy will be cleaned By adding Aluminum to the slag, the metal reacts with oxyge"

Jan 1, 2013

By John Hanna

The University of Alabama Mineral Resources Institute (MRI) has developed a unique process for selective fatty acid flotation of carbonate gangue from sedimentary apatites (francolite) in the pH range of 4-6, without collector conditioning of the pulp. The process, which does not require an apatite depressant, was modified to beneficiate a high MgO siliceous phosphate matrix from South Florida. The modified process includes two flotation stages, one for carbonate removal, as mentioned above, and the other for phosphate recovery from the siliceous gangue. The selective flotation separation of the carbonate and phosphate from siliceous constituents of the matrix at various pH levels and collector dosages are discussed. In the carbonate flotation stage, about 70% of the MgO was rejected in the froth, and the phosphate flotation stage produced concentrates analyzing about 31% P20S' 0.7% MgO and 4% acid insolubles. The overall P20S recovery in the two stages is about 85%.