By Carl E. Swartz

For many years kettles used in the melting and refining of lead and other nonferrous metals and alloys have been made of cast iron. The logic of this probably lies in the fact that cast iron has been known as a material of construction for vessels of this type much longer than steel, and satisfactory fabrication from it has been more easily accomplished and better understood. As the capacity of lead refineries has increased, it has been only natural to increase the size of kettles. Today kettles of 150 to 250 tons are not uncommon. As the size of the kettles increased and better shapes were designed, the uniformity of material of construction became more important. Records kept over comparatively long periods of time have shown that the length of service of kettles has not been uniform. Many causes contribute to this and the importance of each has not yet been evaluated. Kettle design, kettle setting, method of firing and material of construction have been changed from time to time to obtain better service, but the variation in length of service is still great. A kettle may fail during the first few heats or may last through more than one thousand heats. The purpose of this article is not to present the conclusions of a finished piece of research on kettle manufacture and use, but to present a series of observations made over considerable time in the hope that others will publish data and that all may be correlated into a logical scheme which will result in better service and longer kettle life.

Jan 1, 1931

By Carl Swartz

FOR many years kettles used in the melting and refining of lead and other nonferrous metals and alloys have been made of cast iron. The logic of this probably lies in the fact that cast iron has been known as a material of construction for vessels of this type much longer than steel, and satisfactory fabrication from it has been more easily accomplished and better understood. As the capacity of lead refineries has increased, it has been only natural to increase the size of kettles. Today kettles of 150 to 250 tons are not uncommon. As the size of the kettles increased and better shapes were designed, the uniformity of material of construction became more important. Records kept over comparatively long periods of time have shown that the length of service of kettles has not been uniform. Many causes contribute to this and the importance of each has not yet been evaluated. Kettle design, kettle setting, method of firing and material of construction have been changed from time to time to obtain better service, but the variation in length of service is still great. A kettle may fail during the first few heats or may last through more than one thousand heats. The purpose of this article is not to present the conclusions of a finished piece of research on kettle manufacture and use, but to present a series of observations made over considerable time in the hope that others will publish data and that all may be correlated into a logical scheme which will result in better service and longer kettle life.

Jan 1, 1931

A development drilling and bulk sampling program should furnish the following information: (1) geology of the mineralized zone, (2) quantitative data on grade and tons of material within pertinent cutoff limits, (3) physical size and shape of the deposit and areas underlain by waste as well as ore, (4) mineralogical and metallurgical characteristics of the ore, (5) physical characteristics of the ore, (6) bulk samples for metallurgical testing and grade, (7) data on factors that affect mining operations, such as ground water and ground conditions. The method and equipment best suited for a particular drilling job depend upon the geologic features of the mineral deposit to be tested.

Jan 10, 1967

1. What Is a Rock Burst? . . . . 569 Jack Spalding . . 569 A. F. Robertson . 569 W. R. Crane . 569 G. S. Rice......569 P. J. Shenon........... 569 L. C. Graton........... 569 2. What Are the Causes of Rock Bursts? 573 Jack Spalding..........573 A. B. Yates and P. J. Shenon 574, 578, 592, 596 A. F. Robertson . . . . . 575, 595 W. R. Crane. ... 579 G. S. Rice.........582 Oscar Weiss .........582 P. B. Bucky..........582 P. H. Bird.....588, 592, 593, 595 M. K. Hubbert.........593 G. Wheeler.......... .593 B. F. Tillson........593, 595 T. T. Read............594 3. How Can Rock Bursts Be Prevented?. 597 Jack Spalding..........597 A. B. Yates and P. J. Shenon ... 598 A. F. Robertson.......599 W. R. Crane....... .602 G. S. Rice............602 Page 4. How Can Rock Bursts Be Predicted?. 602 Jack Spalding.........602 A. F. Robertson.......602, 603 A. B. Yates and P. J. Shenon ... 602 W. R. Crane......602 G. S. Rice......602 B. F. Tillson...........603 5. How Can Rock Bursts Be Controlled? 603 Jack Spalding..........603 A. F. Robertson.......603 W. R. Crane...........604 A. B. Yates and P. J. Shenon 604 Oscar Weiss........605 G. S. Rice......- 604, 609 R.D.Hoffman..609, 610 R. D. Hall..........609 R. H. Cromwell . . 609 P. J. Shenon...........609 P. B. Bucky......609, 611 B. F. Tillson.........609, 611 A. B. Yates...610, 611 P. H. Bird.......610 6. General Discussion........ 611 Jack Spalding.......... 611 R. D. Parker....... . 616 C. Baring Horwood........ 618 P. B. Bucky........... 619 Foreword This symposium brings together points of view, experiences and ideas on rock bursts from a goodly portion of the globe. Some conceptions, particularly those regarding the necessity of depth, have been fairly well shattered, as we find that they are present in the water tunnels of New York, on the surface at marble quarries in Vermont, and in the coal mines of the United States, as well as in the deep mines of the South African and Kolar gold fields, and in the nickel, copper and gold mines of Canada. Their occurrence under such a variety of conditions is, therefore, a challenge, which, if successfully met and overcome,

Jan 1, 1946

By Frederick Laist

I. EXPERIMENTAL FLOTATION CONCENTRATION INTRODUCTION EARLY in 1914 it was decided to test, on a fairly large scale, the treatment by flotation of Anaconda slime and mill tailing. For this purpose a standard-type Minerals. Separation machine was installed at the Washoe Reduction Works during May and June, 1914. This was followed by the. installation of a full-size Callow pneumatic machine plant. Experiments were also made, on a smaller scale, with the Froment, the Towne, the Fields, and the Anaconda flotation machines. The last-named machine was developed at this plant. In addition to the tests made in the standard-type Minerals Separation machine some tests were made using a Minerals Separation machine of the sub-aeration type. During the series of experiments a large variety of oils was tested. Experiments were also conducted using both round-table feed and tailing to determine whether it would be better to displace the round tables by flotation for the treatment of the slime, or to supplement the round tables by flotation of the round-table tailing. A series of tests was also made on the treatment of the mill tailing by grinding followed by flotation to determine the relative merits of flotation and leaching for the treatment of this product. In addition, flotation tests were made on mixtures of mill tailing and slime. The round-table feed referred to above is the total slime from the mill. It contains about 35 per cent. colloidal solids and approximately 90 to 95 per cent. of the total solids will pass through 200 mesh (0.067 mm.). It assays from 2.3 to 2.6 per cent. Cu. The mill tailing referred to above is the total discard from the mill, exclusive of the slime. It is all finer than 2 mm. and about 90 to 95 per cent. will remain on 0.25 mm. It assays about 0.60 per cent. Cu. A brief summary of the experimental flotation results follows:

Jan 3, 1916

By Albert E. Wiggin, Frederick Laist

Early ill 1914 it was decided to test, on a fairly large scale, the treatment by flotation of Anaconda slime and mill tailing. For this purpose a standard-type Minerals Separation machine was installed at the Washoe Reduction Works during May and June, 1914. This was followed by the installation of a full-size Callow pneumatic machine plant. Experiments were also made, on a smaller scale, with the Froment, the Towne, the Fields, and the Anaconda flotation machines. The last-named machine was developed at this plant. In addition to the tests made in the standard-type Minerals Separation machine some tests were made using a Minerals Separation machine of the sub-aeration type. During the series of experiments a large variety of oils was tested. Experiments were also conducted using both round-table feed and tailing to determine whether it would be better to displace the round tables by flotation for the treatment of the slime, or to supplement the round tables by flotation of the round-table tailing. A series of tests was also made on the treatment of the mill tailing by grinding followed by flotation to determine the relative merits of flotation and leaching for the treatment of this product. In addition, flotation tests were made on mixtures of mill tailing and slime. The round-table feed referred to above is the total slime from the mill. It contains about 35 per cent. colloidal solids and approximately 90 to 95 per cent. of the total solids will pass through 200 mesh (0.067 mm.). It assays from 2.3 to 2.6 per cent. Cu. The mill tailing referred to above is the total discard from the mill, exclusive of the slime. It is all finer than 2 mm. and about 90 to 95 per cent. will remain on 0.25 mm. It assays about 0.60 per cent. Cu. A brief summary of the experimental flotation results follows:

Jan 1, 1917

Human engineering was the keynote of the thirty-ninth annual meeting of the American Society of Mechanical Engineers, which was held in New York, December 3-6. This note was sounded by President Charles T. Main in his address at the opening session and was carried through by all the speakers. In his survey of the year's work, he said that more than 6000 names of engineers were furnished the Government for filling a wide variety of positions. In addition to the 1400 members in service, two members of the council of the society are in uniform in France and one, as a distinct war service, is in charge of one of the largest shipyards. After giving other ways in which the Society has helped the Government, President Main called attention to the necessity for thoroughgoing efforts to increase production and the settlement of questions involving industrial relationships. At the following meeting, President Adams of the American Institute of Electrical Engineers called attention to the necessity of meeting labor in a progressive way, facing labor questions fairly and squarely, as the real interests of labor cannot be separated from those of the engineer. Charles E. Knoeppel, discussing "Industrial Organization as It Affects Executives and Workers," said the problem of the cost of living might be settled in two ways: 1, there must be more producers, and 2, there must be a greater amount supplied by those now producing. The first solution is practicable, he said, if labor is allowed shorter hours, better conditions, and a remuneration that will attract workers. The second can be employed by eliminating waste, standardizing conditions, setting fair tasks, and allowing men to earn an amount that will compensate them for' their skill and cooperation. Dudley R. Kennedy of Philadelphia, employment manager of the American International Shipbuilding Corporation, said the human-engineering phase of the country's industrial development had generally been overlooked. "We hardly yet know what competition means; we will learn it within a few years. Permit me to prophesy that the executive of the next decade will be the man who best knows men. He will be an originator, a handler of men as individuals, a handler of men in the mass, a leader not a driver, a very human man. The science of human engineering is here to stay. The study of human characteristics is the most enduring, as well as the most fascinating in the world, and still the most complex."

Jan 1, 1919

By AIME

AS with Phil Kraft, referred to on this page last month, travel has always held a great fascination for Raymond Frank Baker and for that reason he determined to become a geologist. He had heard that geologists travel and that was what he wanted to do. Now as chief geologist for The Texas Co. his early wish has been fulfilled-he spends almost one third of his time journeying' from one oil field to another. Mr. Baker was born in New Haven, Conn., on Jan. 11, 1892, and went through the public schools in New Britain. A stalwart New Englander, he attended Yale and in 1912 received a degree in civil engineering. For a year following this he worked as a civil engineer for the New York Central Railroad, but his early urge to travel widely could not be satisfied here. So in 1913 he re-entered Yale and until 1916 studied mining and economic geology. He had a little taste of field work, which later became so enjoyable to him, in the summer of 1915 when he worked with the U. S. Geological Survey as a geologic aid. In 1916 he made his first contact with The Texas Co. when he entered their Tulsa office as a geologist. This early career was interrupted by service in the

Jan 1, 1947

By M. Bevis, A. F. Acton, P. C. Rowlands

Defor~nation twinning and transformation twinning modes most likely to be operative in Fe-Ni and Fe-Ni-C martensites have been determined using a new theory of the crystallography of deformation t~inning.~ This analysis shows that potentially important conventional and nonconventional twinning modes1 have been omitted in previous analyses. Discussion is given on the relevance of the predicted twinning modes to the lattice invariant shear associated with the martensite transformation in steels and to anomalous deformation twinning in Fe-Ni-C martensites. THE two most important criteria which appear to govern operative twinning modes in metallic structures1 are that the magnitude of the twinning shear should be small and that the twinning shear should restore the lattice or a multiple lattice in a twin orientation. The latter criterion ensures that the shuffle mechanism required to restore the structure in a twin orientation is simple. These criteria have been adhered to in the prediction of twinning modes2"6 in bcc and bct single-lattice structures with axial ratios in the range y = 1 to 1.09 as, for example, encountered in martensite occurring in steels. Refs. 2 and 3 in particular consider the martensite transformation in steels and the twinning modes in these cases relate to transformation twinning, and hence the lattice invariant shear associated with the martensite transformation. The list of twinning modes which can be compiled from these sources is incomplete and the ranges of magnitude of shear considered could be unrealistically small, particularly in the case of deformation twinning. The latter consideration is supported by the fact that twinning modes with magnitudes of shear large compared with the smallest shear consistent with a simple shuffle mechanism have been established in, for example, the single-lattice structure mercury7 and the multiple-lattice structure zirconium.&apos; In addition the anomalous deformation twins reported by Ftichrnan4 to occur in a range of Fe-Ni-C martensites still remain unexplained. It is clear that a comprehensive analysis of twinning modes likely to be operative in martensite In steels is required. The results of the application of a new theory of the crystallography of deformation twinningg to these structures are presented in this paper. The theory has been used to determine all shears which restore the lattice or a multiple lattice in a new orientation with magnitude of shear up to a required maximum. The orientation relationships between parent and twinned lattices are not restricted to the classical orientation relationships of reflection in the twin plane or a rotation of 180 deg about the shear direction. PREDICTED TWINNING MODES Twinning modes which restore all or one half of lattice points to their correct twin positions will be referred to as m = 1 and m = 2 modes, respectively. These modes are the most likely to describe operative modes in single lattice structures. The bcc m = 1 and m = 2 modes which have magnitudes of shear s in the range s < 2 and s < 1, respectively, have been given10 and are reproduced here in Tables I and 11. Detailed discussion of the crystallography of these modes and cubic modes in general will be discussed elsewhere (~evis and rocker, to be published). The four twinning elements Kl, &,ql,7)2 as well as the magnitude of shear s are given for each twinning mode, and the twinning modes are given in order of increasing shear. Two twinning modes are given in each row of the tables, the twinning mode Kl, Kz, ql, q2 and the reciprocal twinning mode with elements Kl = K,, Ki = Kl, q: = q2, and 17; = ql. The m = 1 and m = 2 twinning modes which describe twinning shears with small magnitudes of shear and simple shuffle mechanisms in bct crystals with -y = 1 to 1.09 are given in Tables I11 and IV, respectively. On increasing the symmetry of the tetragonal lattice to cubic, that is making y = 1, all modes listed in Tables 111 and IV must reduce to crystallographically equivalent variants of the modes given in Tables I and 11, respectively, or become twinning modes with both shear planes as symmetry planes in the cubic lattice and hence not considered in Tables I and 11. With the exception of this last type of mode only those tetragonal twinning modes which reduce to modes 1.1, 1.2, 2.1, and 2.2 of Tables I and I1 are considered in Tables 111 and IV. For values of y in the range -y = 1 to 1.09 the tetragonal modes and the corresponding cubic twinning modes have approximately the same magnitude of shear. The twinning modes listed in Tables 111 and IV are therefore by the criteria given above the most

Jan 1, 1969

By Charles H. Hopkins, J. M. Lohr

A commercial development requiring a suitable alloy or alloys for sealing into various grades of glass made it desirable to have a more exact knowledge of the expansion characteristics of the nickel-iron alloys than appeared in the published literature. The expansion of the more common types of glass under consideration varies from 2.7 to 10.4 X 10-6 per degree Centigrade, over the range 20" to 400&apos; C. For reference, the t,hermal expansion curves of several types of glass used for sealing by the lamp and tube industries are given (Figs. 1 and 2). This paper covers a detailed investigation of the thermal expansion of a series of nickel-iron alloys in which the nickel content varies from 30 to 70 per cent. Particular stress is laid on the alloys that contain between 40 and 55 per cent Ni.

Jan 1, 1939

By Charles H. Hopkins, J. M. Lohr

A commercial development requiring a suitable alloy or alloys for sealing into various grades of glass made it desirable to have a more exact knowledge of the expansion characteristics of the nickel-iron alloys than appeared in the published literature. The expansion of the more common types of glass under consideration varies from 2.7 to 10.4 X 10-6 per degree Centigrade, over the range 20" to 400&apos; C. For reference, the t,hermal expansion curves of several types of glass used for sealing by the lamp and tube industries are given (Figs. 1 and 2). This paper covers a detailed investigation of the thermal expansion of a series of nickel-iron alloys in which the nickel content varies from 30 to 70 per cent. Particular stress is laid on the alloys that contain between 40 and 55 per cent Ni.

Jan 1, 1939

By Ross W. Smith, Salim Akhtar

INTRODUCTION Flotation of oxide minerals, particularly silicates, with cationic collectors differs substantially from classic flotation of sulfide minerals using sulfhydryl collectors. In the case of cationic flotation of these minerals, in general: 1. There is a greater importance of electrostatic interaction between mineral and collector. 2. Longer-chained collectors are required; as a rule at least 10 carbons must be present in the hydrocarbon chain. 3. Moderate concentration of collector is required. 4. Attachment between collector and mineral appears to be less strong even though the system may exhibit a large contact angle. 5. Required conditioning time before flotation is usually relatively short. 6. There is sensitivity to slimes. 7. The collectors usually possess frothing power. 8. Selectivity of cationic collectors for specific minerals is usually poor. Almost any of the oxide and silicate minerals may be floated using cationic collectors. However, specific response to these collectors varies with mineral type. The following classes and minerals are

Jan 1, 1976

By Alfred Boyles

"HEREDITY"&apos; in cast iron has been a subject of much discussion. Numerous experimenters have found that the properties of gray iron may vary greatly without corresponding variations in composition or thermal treatment. The main structural difference in such cases is in the size and distribution of the graphite flakes and the explanations given usually attribute this difference to some chemical element not shown by ordinary analysis or to some physical factor, such as inclusions in the melt. It cannot be said that any of these theories is completely satisfactory. Much remains to be learned about cast iron and for this reason a study of the material was undertaken as a part of the program of fundamental research at Battelle Memorial Institute. A review of the literature indicated that very little systematic work had been done on the mecha-nism of freezing in cast iron. The experiments described below are largely concerned with that problem.

Jan 1, 1937

By C. R. Wohrman

A MELT of pure electrolytic iron with about 0.4 per cent. sulfur and 7 per cent. manganese was prepared in connection with a study of inclusions in iron. The alloy darkened rapidly when etched with a 10 per cent. alcoholic solution of nitric acid, and microscopic examination revealed the presence of a semimartensitic, semi-Widmanstättian structure (Figs. 1 and 2) closely resembling the structures found by Benedicks in his artificially prepared "meteoric iron." 1 The structures found by Benedicks were readily explained by the presence in his alloy of the two well known iron-nickel solid solutions, taenite and kamacite, and of their eutectoid (?) aggregate, plessite. By analogy, one would infer the existence of similar phases in the iron-manganese alloy just described, such as inference being strengthened by the similarity displayed in many ways by nickel and manganese in their effects on iron. IRON-MANGANESE ALLOTS ARE REGARDED AS HOMOGENEOUS Heterogeneity of iron-manganese alloys has not been recognized heretofore, judging from the data of standard metallographic books and those of original papers. In fact, iron and manganese are quite generally regarded as completely miscible in the solid state. Dr. Rosenhain,2 for example, writes: Alloys of group (a), of which those of gold-silver, iron-manganese, and copper-nickel are examples, when allowed to crystallize sufficiently slowly to attain their condition of final equilibrium, present a microstructure exactly similar to that of a pure metal-the homogeneous character of the molten solution is in that case so completely maintained that the microscope cannot detect the presence of any second constituent.

Jan 1, 1927

By N. A. Gokcen, S. Fujishiro

THE pressures of Mn(g) in equilibrium with Mn7C3 and graphite have been measured by McCabe and Hudson&apos; and Butler, McCabe, and paxton2 by means of graphite, zirconia, and Ta-Mo Knudsen cells. The details of corrections in their measurements were somewhat different from those of the authors;3&apos;4 hence, further independent results at higher temperatures seemed to be warranted. The stoichiom-etry of Mn7C3 in equilibrium with graphite and its stability up to the vicinity of 1373 °K have been satisfactorily established by Kuo and persson5 (See also Hansen and Anderko).&apos; The method of investigation has been described elsewhere in detail.3&apos;4 The carbide was prepared in the manner described by McCabe and Hudson. In order to avoid possible reactions with refractory oxides, only graphite cells were used for the effusion experiments. The authors&apos; results are the runs M-1, M-2 and M-3 listed in Table I, together with those of McCabe and co-workers. The heat capacity, c;, of Mn7C3 is not known; therefore McCable et al. plotted their data as log P vs 1/T and the results were only expressed first&apos; as, and later2 as logP=- -14220+6.06 without further thermodynamic calculations. However, it is possible to estimate closely the necessary heat capacity as follows: When H; - &98 of CrC, or MnO, is plotted vs x, corresponding to various compounds, with temperature as the parameter, it is seen that the relationship is represented by a line of very small curvature. This relationship is also followed by other compounds which do not exhibit solid state phase transformations. In view of the fact that chromium and manganese have the atomic numbers of 24 and 25 respectively, it is reasonable to assume that H; - H;ae vs x for MnC, follows the same type of lines as those for CrC, for which adequate data are available.7 Similar correlations appear to be valid for oxides of two neighboring metals for which reliable data are available. The procedure is thus to move the lines for CrC, vertically (parallel to the axis of HT - H298) until they coincide with the points for MnC1/3, the only carbide of manganese whose H; - HO298 has been

Jan 1, 1963

By A. C. Milner

In a gold standard world which possesses insufficient metal to meet the every-day needs of all, confidence becomes the vital factor, the very foundation upon which the machinery for the expansion of gold into currency, and credit, rests. The gold supply, affected by many influences, moves constantly from one point to another, but not always to that point where it is most needed. In the period 1928-1930, the combined gold holdings of the United States and France increased $1,370,936,-000, and this with new gold adding only $600,000,000 to the monetary gold stock.Theref ore, the gold stocks of other countries must have been depleted during the period by $770,936,000. This uncontrolled shifting throws the delicately adjusted instrumentalities of both credit and commerce out of equilibrium. If a given nation&apos;s gold stock shifts so as to bring it substantially below the legal reserve ratio set up against it for currency issues, the effect can easily extend to the currency issues and banking credit volume of one or more nations which may have based their gold exchange standards upon the gold stock of such nation. Thus the substitution of paper based on gold in place of the actual gold is an inflation of the currency, which carries through into an uncontrolled pyramiding upon the entire machinery of credit based on gold. In 1929 Europe, South America, Africa and Asia had overissued currency based on gold. America, Oceanica and Japan, which have not overissued their gold currencies, would in normal times require their entire present gold stocks and, as Continental Asia is largely upon a silver credit basis, from a domestic standpoint, it would appear that the gold problem is not so much one of maldistribution, as it is one of inadequate supply. It would appear that some method of increasing greatly the velocity of gold, within the safe reserve point, should be devised, or that silver, of which estimates indicate that 7,000,000,000 oz. are available for

Jan 1, 1931

By W. Mostowitsh

I. Introductory LEAD sulphate occurs as anglesite, and is formed in every roasting of lead sulphides or sulpho-salts containing lead. In smelting in the blast furnace an ore containing natural or artificial lead sulphate, a large part of the sulphur present goes to the formation of the intermediary product matte which requires further treatment for the recovery of the values it contains. It is therefore of importance to study the behavior of lead sulphate at elevated temperatures, both without and with reducing agents, especially as the information available gives data which are more or less conflicting. II. Decomposition of Lead Sulphate by Heat The dissociation of PbSO4 into PbO and S03 or S02 and 0 has been discussed by many metallurgists. The following data are considered to be representative. Doeltz and Graumann1 found that PbSO4 was not affected by heat at 800° C.; that dissociation began at 900° C., and was rapid at 1,000° when the salt lost in 1 ½ hr. 14.3 per cent. of its weight, the dry salt containing 26.43 per cent. SO3. Hofman and Wanjukow2 summarize their work upon the dissociation of metallic sulphates with the statement that the decomposition of PbSO4 begins at 195° C., but progresses very slowly, with the formation of the basic salt 6PbO.5S03 at 705°; that this salt undergoes a transformation at 847°, begins to be decomposed at 888°, to sinter at 896°, and to fuse at 910°; rapid dissociation begins at 952°, and is accompanied by volatilization of PbO; retardations at 958° and 962° indicate an acceleration of decomposition which, however, is not complete. Proske3 found that PbSO4 gave off at 900° C. in 30 min. only 0.63 per cent. of its SO3, and that the loss increased with

Jan 5, 1916

By R. C. Patterson

In view of the circumstance that very few important changes have been made within the last 15 or 20 years in the equipment of rod and wire mills, the description of a new process introduced by Grenville Mellen, of LleweIIyn Park, N. J., to take the place of the present laborious system of producing rods of lead, zinc, brass, copper, aluminum, etc., may be interesting to members of the Institute. This new process consists in the production of cast rods at one operation in a small continuous casting machine. The hot liquid metal is transferred from the melting crucibles directly into an endless chain of mold blocks in the machine, where solidification takes place, and the rod comes out continuously in a solid form at one end as long as the molten metal is supplied. The operation of these mold blocks so as to produce a solid rod of uniform structure constitutes an important part of Mr. Mellen&apos;s invention. The machine (Figs. 1 and 2), 12 ft. in height over all, 2 by 3 ft. in horizontal cross-sectional area, and 6,000 Ib. in weight, has a framework of cast iron, holding in position two endless chains of mold blocks, which are made in sections and join in center alignment. The mold orifice is made up of these mold sections, into which the liquid metal flows. The molding chains are composed of steel blocks, grooved on one face to form the molding cavity, and linked together with flexible joints. Each block is carried on four rollers which guide the chain around the end sprockets and carry it in its course through the machine. The accuracy of alignment requisite to the production of a perfect rod in the mold groove formed by these sections is secured by careful machine work, and by building the four ways, down which the alignment takes place, so that two of the sides are fixed permanently, whiIe the opposite sides are held to their position by spring pressure. The guides carrying the molds, while in casting position, are water-cooled square tubes. The length of this machine is somewhat indeterminate. A certain amount of both time and cooling surface is required to solidify the metal jn the mold; and one may either use a long molding chain and run it fast, or a shorter chain and run it correspondingly slower. We have found,

Jan 1, 1916

By W. Mostowitsch

Lead sulphate occurs as anglesite, and is formed in every roasting of lead sulphides or sulpho-salts containing lead. In smelting in the blast furnace an ore containing natural or artificial lead sulphate, a large part of the sulphur present goes to the formation of the intermediary product matte which requires further treatment for the recovery of the values it contains. It is therefore of importance to study the behavior of lead sulphate at elevated temperatures, both without and with reducing agents, especially as the information available gives data which are more or less conflicting. 11. Decomposition of PbS04 by Heat The dissociation of PbSO4 into PbO and SO3 or SO2 and 0 has been discussed by many metallurgists. The following data are considered to be representative. Doeltz and Graumannl found that PbS04 was not affected-by heat at 800" C.; that dissociation began at 900" C., and was rapid at 1,000° when the salt lost in 1 1/2 hr. 14.3 per cent. of its weight, the dry salt containing 26.43 per cent. SO3. Hofman and Wanjukow2 summarize their work upon the dissociation of metallic sulphates with the statement that the decomposition of PbS04 begins at 195&apos; C., but progresses very slowly, with the formation of the basic salt 6PbO.5SO3 at 705"; that this salt undergoes a transformation at 847") begins to be decomposed at 888") to sinter at 896", and to fuse at 910"; rapid dissociation begins at 952") and is accompanied by volatilization of PbO; retardations at 958" and 962" indicate an acceleration of decomposition which, however, is not complete. Proske3 found that PbSO4 gave off at 900" C. in 30 min. only 0.63 per cent. of its 803, and that the loss increased with

Jan 1, 1917

By Richard Akerman, Frederick Prime Jr

[THE attention now being paid both in this country and Europe the greatest economy in the working of the blast furnace, and the eagerness with which all thoughtful men in the iron business look for any new information which will tend to throw light on this subject, is a quite sufficient excuse for presenting this paper to the American Institute of Mining Engineers.] I. It must be borne in mind that when two bodies unite to form a chemical compound, heat is almost always evolved. In order to