By W. Petruk

The behaviour of galena, chalcopyrite and tetrahedrite during floration of a fine-grained base metal ore from New Brunswick was investigated by image analysis study of the mill concentrates and tailings. The minerals were analyzed to determine the grades and recoveries as related to free and unliberated mineral grains and their size distributions. The results show that only 37 wt % of the galena was liberated but 88 wt % of the free galena was recovered, indicating good mill performance for the lead. The lead recovery was 65 wt %, with the main loss due to unliberated galena. Most of the unliberated galena lost to mill tailings is so fine-grained that galena liberation and Pb recovery would not improve significantly by re-grinding. Chalcopyrite liberation was 56 wt % but only 75 wt % of the free chalcopyrite was recovered. Copper recovery was 45 wt %, with the chalco-pyrite loss in the mill tailings being both as large free grains, and as small and large unliberated grains. It was calculated that copper recoveries could be improved about 8 to 10 wt % by changing the concentrator operations and by regrinding. Concentrator operations hive already been modified and copper recoveries have improved about 5 wt %. About 29 wt % of the silver was lost to tailings mainly as both free and unliberated, large and very small, Silver-bearing tetrahedrite grains. It was calculated that about 25 wt % of the silver in the tailings might be recovered by improved milling conditions and by regrinding.

Jan 1, 1981

By S. Ozbilen

"Al-Li binary alloys with nominal Li contents of0.15, 1.1and2.8 (in wt%) were aged naturally at room temperature for two months, aged at low temperatures ( 65 and 1 OOEC) for up to 2 months and aged artificially at 190EC for 4 days after water quenching to 25EC following solutionizing at 530EC for 20 minutes. Ageing behavior of these binary alloys were studied by Vicker's Hardness measurements and DSC thermal analysis. Thermal analysis results indicate the formation of GP zones of Al-Li system in Al-2.8wt%Li binary alloy. In the same alloy, rapid quenching from one phase region (a) gives rise to precipitation of small o' particles in a matrix (a) with still high supersaturation. During ageing of this alloy below lOOEC an additional transformation, i.e., GP zone formation occurs proceeding at a very high rate which is described on the basis of the theoretical analysis for the quenched Al-Li system proposed by Khachaturyan et al [6]. Ageing at temperatures below 11 OEC takes place slowly by the formation of small d' particles of lower thermal stability than the quenched-in d precipitates in addition to GP zones resulting in an increase in hardness compared to water quenched samples. During artificial ageing, GP zones transform by dissolution to d' precipitates while d' particles already in the microstructure coarsen during under aged condition at which hardness increases with time till peak aged condition.IntroductionIn binary Al-Li alloys the d' (Al3Li) fully coherent internally ordered inetastable phase of Li2 structure with a=0.4038d [1-5] forms homogeneously between 120 and 190EC before the formation of stable d' (A!Li) phase and cause the superior mechanical properties. This is due to an appreciable age hardening effect resulting because of the d' precipitation during ageing [1]. The response of d' to decomposition and its formation kinetics have been studied previously and it is believed that the decomposition of the a-supersaturated solid solution occurs in a two stage process; i.e., a 6 d' (Al3Li) 6 d(A!Li). Khachturyan et al [6] theoretically investigated precipitation of the d' phase and gave an interpretation of the transformation paths of the quenched Al-Li alloys. They predict that the disordered supersaturated solid solution congruently orders, and then the uniformly ordered solution decomposes into ordered regions that differ in Li-content. Finally, ordered d' phase forms in the disordered matrix."

Jan 1, 1998

By N. Kanari

The kinetics of oxychlorination of MgO by Cl2+O2 was studied in the temperature range of 850 °C - 1025 °C, using thermogravimetric analysis. The effects of C12/02 ratio, gas velocity, temperature and partial pressure of reactive gases on the reaction rate were investigated. The oxychlorination process was characterized by an apparent activation energy of about 214 kJ/mol. The reaction orders with respect to C12+O2. C12 and O2 at 950 °C were about 0.65.0.98, and -0.37, respectively. Some data about oxychlorination kinetics of MgO, Cr2O3, and MgCr2O4 contained in chromite were compared. Efficiency of using oxychlorination for the removal of iron oxides contained in magnesia was demonstrated.

Jan 1, 1999

By Stephen M. Testa

Several methodologies are available for the remediation of contaminated soils including bioremediation, vapor extraction, chemical fixation, incineration and direct disposal. A proven innovative and cost effective alternative for the fixation of contaminated soils is via cold-mix Environmentally Processed Asphaltm (EPA"'). EPAm methodology utilizes contaminated soil as an ingredient in an industrial process to produce a commercially viable product. Petroleum hydrocarbon and metal affected soil is incorporated with a water-based asphalt emulsion and varying amounts of aggregate to produce a range of cold-mix asphaltic products that fulfills the requirements of a variety of end uses. This viable and creative use which is within the intent and spirit of current regulations in producing, in lieu of a landfill waste, an end product for use as a berm, road base, liner, or other site specific application. Consideration of certain engineering and environmental factors including durability, stability, chemical resistance and ageing, biological resistance, permeability, leachability and geochemical aspects suggests that cold-mix asphalt incorporation of affected soil will perform more than adequately under normal conditions for a long period of time.

Jan 1, 1994

By M. J. Adam

The U.S. Bureau of Mines is investigating the partitioning of selected complex minerals into simple phases using sulfidation reactions. Successful partitioning of complex mineralogy to simple phases may afford an opportunity to improve selective extraction of mineral constituents of economic value. The research has shown that complex minerals, such as chalcopyrite (CuFeS2) and pentlandite [(Fe,Ni)9Se]' may be partitioned to the simpler phases covellite (CuS) plus pyrite (FeS2) and vaesite (NiS2) plus pyrite (FeS2), respectively. Demonstrations of these reactions were verified through long-react ion-time (24 h or more) experiments, but basic rate investigations and modeling were not included in the previous research. This report describes research aimed at determining the rate at which the complex mineral CuFeS2 converts to the simple sulfides CuS plus FeS2. Small samples of CuFeS2 were blended with elemental S prior to thermal treating under an He atmosphere for time periods up to 4 h. Products from each treatment period were characterized using metallography, chemical analysis, X-ray diffraction (XRD), and scanning electron microscopy (SEM). Results of the investigation revealed a rapid conversion of CuFeS2 to CuS plus FeS2 early in thermal treatment periods. As the reaction occurred, a CuS rimming of particles was observed which separated the reacting species (CuFeS2 and S) and caused a considerable decrease in transformation rate.

Jan 1, 1991

By Frame Ritzert, Dennis Keller, Vijay Vasudevan, David Arenas

"An investigation was conducted to describe topologically close packed (TCP) phase instability as' a function of composition in the advanced ·Ni-base superalloy Rene N6. TCP phases are detrimental to overfill high-temperature performance of Ni-base superalloys because of their brittle nature and because they deplete the Ni-rich matrix of potent solid solution strengthening elements. Thirty-four variations of polycrystalline .Rene N6 determined from a design-of-experiments approach were cast and homogenized at 13 l5°C for 80 hours followed by exposure at 1093°C for 400 hours to promote TCP formation. The alloys had the following composition ranges in atomic percent: cobalt 10.61 to 16.73, Mo 0.32 to 1.34%, W 1.85 to 2.52%, Re 1.80 to 2.11%, Ta 2.36 to 3.02%, Al 11.90 to 14.75%, and Cr 3.57 to 6.23%. Physical and chemical characteristics of all microstructures obtained were described using various analytical techniques. From these observations, a mathematical description of TCP occurrence (s and P phase) was generated for polycrystalline Rene N6.IntroductionNi-base superalloy single crystals represent the state-of-the-art for turbine engine airfoil application as they offer the best balance of properties to allow for the high operating temperatures required: for efficient engine operation.1 Current trends in alloy design take advantage of improved creep rupture strength with the addition .of higher levels of refractory elements. 2 In .particular, the addition of significantly higher levels of Re in third generation superalloys is key for both microstructural stability and creep rupture strength. 3 While the presence of the refractories is thought to provide strength benefits from solid solution hardening, a tendency for alloy instability in the form of topologically-close-packed (TCP) phases or secondary reaction· zone (SRZ) ·phenomena accompanies the high refractory content. 3 The formation of these phases in sufficient amount is detrimental to the overall high temperature performance of Ni-base superalloys because of their brittle nature and because they deplete the Ni-rich matrix of potent solid solution strengthening elements.4 The tendency for a particular composition to form TCP may not be immediately known since the precipitation of TCP phases in Ni-base superalloys is nucleation controlled, thereby requiring long times at elevated temperatures to precipitate. 5 They preferentially nucleate along the octahedral planes of the Ni-base superalloys, usually in areas of refractory metal enrichment at grain boundaries or inside dendrites.5-6 In Rene N6, two closely related TCP phases, a and P, have been observed.2"

Jan 1, 1998

By C. M. Egert, S. Rajic

"We have developed a monolithic micro-spectrometer suitable for a variety of sensing applications including industrial process monitoring. The device consists of a solid structure with a volume less than 6 cubic centimeters. All optical components of the spectrometer including two aspheric mirrors, a diffraction grating, and entrance and exit surfaces are fabricated onto the surface of the structure. All light paths are internally contained within the structure. The result is a small, rugged spectroscopic sensor ideally suited for use as a process monitor. Due to its monolithic nature the device requires no post-fabrication alignment; nor can it be knocked out of alignment during use. Although many materials and thus wavelength regions were possible, the prototype device discussed here was produced in PMMA by precision diamond turning. However, lower cost manufacturing approaches involving injection molding are under development to produce an affordable sensor.Due to its rugged monolithic design, small footprint, and low cost the monolithic micro-spectrometer is ideally suited for distributed monitoring applications often required for industrial processes. It is expected that modified versions of this sensor designs will be required for specific applications so as to maximize the performance and resolution over the operating range. For example, the prototype device described here operates over a wavelength range of 500 nm to 1000 nm. The performance of this device as a real-time surface monitoring sensor will be discussed in detail. Our approach of using wavelength dependant scattering resulted in the reduction to practice of a miniature, monolithic, rugged, low-cost, micro-instrument in a sensor sized package. The process sensor applications community has been faced by the cost versus performance issue. Simple go/no-go sensors are typically inexpensive but they provide very limited and sometimes dubious data. Scaled down traditional instruments offer very good measurand information but are typically cost prohibitive, fragile, and still relatively large. This work will bridge the gap between these two extreme sensing alternatives."

Jan 1, 1997

By Saeid Pournaderi, Ahmet Geveci, Ender Keskinkilic, Yavuz A. Topkaya

There are mainly three commercial nickel laterites in Turkey: Gordes, Caldag and Sivrihisar. The first two appear in Western Anatolia. The third one, Sivrihisar (Yunusemre) laterites have been found in the first decade of the millennium, in the Central Anatolia region of Turkey. Since then, mining facilities have been continued in Yunusemre. Calcination, prereduction and smelting of Sivrihisar laterites have been extensively studied and published. In the current work, some results of the studies related to characterization of Sivrihisar laterites will be presented.

Jan 1, 2016

By H. Y. Sohn, S. PalDey

"A new chemical synthesis process for the preparation of intermetallic compounds has been developed. It involves the vapor-phase reduction of mixtures of constituent metal chlorides by magnesium vapor to produce intermetallic compounds in the form of fine powder. The advantages of the process include (a) the use of inexpensive raw materials, (b) low reaction temperatures, and (c) products in the form of fine particles. Titanium and nickel aluminides were prepared by this method. The effect of AlCl/TiCl3 partial pressure ratio on the formation of different titanium aluminides was studied. A two-phase mixture containing 80 mol % of TiAl and 20 mol % of TiA13 formed at an AlC13/TiC13 ratio of 10. The amount of TiA13 was maximized to 72 mol% at an AlC13/TiC13 ratio of 16. The maximum conversion of the limiting chloride TiCl3 was 94 % . In the case of nickel aluminides, NiAI, NiAl3, and Ni2Al3 were formed by reducing mixtures of NiC12 and A1Cl3 vapors. The effect of the partial pressure ratios AlCl3/NiC12 and Mg/NiC12 on the formation of nickel aluminides was studied. The maximum content of NiAl obtained was 98 mol % . At the AlC13/NiC12 ratio of 19, a two-phase mixture of 17 mol% of NiAl and 83 mol% of NiA13 was produced. The product particles were very fine in the size range of 0.05 to 0.2 µm.A. IntroductionIntermetallic compounds are attracting much attention [1]. Titanium and nickel aluminides have attracted a great deal of attention from the aerospace as well as automobile industries because of their potential for high-temperature application (e.g., low density, good oxidation resistance, and high-temperature strength retention [2, 3]). Gamma TiAl and two-phase (TiAl and Ti3Al) alloys [4] are used for gas turbine engine rotational components as well as automobile exhaust valves. TiAl3 is one of the most extensively investigated aluminum-rich intermetallics. Nickel aluminides are attractive because of their low densities, relatively high melting point and good high-temperature strength properties. For example, Ni3Al shows increasing rather than decreasing yield strength with increasing temperature [5]."

Jan 1, 1998

The merging of flash smelting with spray converting in one single furnace is proposed as a continuous copper making process. The proposed process is expected to produce blister copper, clean slag and gas with high sulfur dioxide concentration. Some high grade matte is an intermediate product recycled within the proposed furnace, spray-atomized and converted. The thermodynamic equilibria of the simultaneous oxidations which take place during copper smelting and converting are discussed in order to establish the gradient of oxygen potential along the furnace required for smooth operation. The proposed process is a dynamic system designed to reach equilibrium only close to the slag skimming end of the furnace. The process feasibility is based on the predesigned significant difference between the rates of converting reactions in a finely dispersed system and the rates of deconverting reactions between immiscible liquid phases of restricted interface area. The converting of small stationary droplets of matte, in a silica saturated system, was studied in the laboratory for extremely short oxidation times (10 to 120 seconds). These experiments led to some interesting observations on reaction mechanisms and kinetic trends. The droplet size and the matte grade affected very strongly the oxidation rate and the proportion of the different products obtained.

Jan 1, 1976

By Chunyang Guan, Jilai Xue, Jun Zhu, Qiaochu Liu

"Al-Sc Alloys have showed many advanced properties for a wide range of industrial application, which is usually produced using thermal reduction process. This work is aimed to develop an electrochemical process to make Al-Sc alloy using industrial Hall aluminum reduction cells. The experiments have been carried out in a lab cell where NaF/AlF3-Al2O3-LiF as electrolyte, Sc2O3 as raw material, and liquid aluminum as cathode were used at operating temperature of 950 °C. The resulting Al contained 0.2 - 0.5 wt.% Sc that is the common range in its content for advanced applications. However, a small fraction of Sc was found from thermal reduction at Al melts interface. SEM-EDS and ICP-AES analysis showed a uniformed distribution of Sc at varying locations of the Al-Sc alloy sample. In addition, a higher Sc content in Al-Sc alloy can be obtained with introducing ultrasound through the cathode than that without it.IntroductionIn recent years, scandium has been investigated as an alloying element for aluminum alloys. With addition of a small amount of Sc, Al alloys can improve the strength, weld ability, resistance to re-crystallization and corrosion resistance [1-3]. Due to their advanced properties and potential applications, the demand for Al-Sc alloys will increase in the future. However, the difficulties in reduction technologies and the high costs in production process may limit their expansion in application areas.The current major method of producing Al-Sc alloys is to mix Sc into Al by melting Al-Sc master alloy. This alloying process has several technical problems, such as easy segregating and heavy burning loss, etc. The price of Sc metal or starting material is also high, so the mixing process is an expensive alloying method. Molten salt electrolysis is alternative method to prepare RE metal and RE alloys [4, 5]. It also can reduce the segregation of alloying elements. Sc2O3 is an ideal material as raw material with low price and decomposition voltage. Some work has proved that Al-Sc alloys can be obtained by electrolysis Sc2O3 directly in cryolite [6-8], or CaCl2 molten salt [9]."

Jan 1, 2012

By George Oprea, Tom Troczynski, Joe A. Rigby, Waiman Lo

The refractory lining of the tuyere line in Peirce Smith converters have usually much shorter life in service than the rest of the lining, above or below it. There are already recognized chemical, thermal and mechanical factors which contribute to the wear of the lining. Our study presents the experimental results on microstructural changes occurring on these tuyere line bricks in a nickelcopper converter. The experimental bricks, after use at the tuyere line, were investigated using SEM/EDS and XRD techniques, to identify the mineralogical changes due to interactions with the nickel-copper matte or fayalite type slag at the process temperatures. The microstructural changes were correlated with physical and mechanical properties of the brick before and after use and a wear mechanism was suggested. Although the matte does not theoretically react with the mineralogical components of the brick, a partial oxidation of the Ni-Cu sulphides was identified using a line analysis by SEM/EDS in the densified layer at the hot face, which allows for mineralogical changes at the matte-refractory interfaces, with a high probability of microcrack formation due to the thermal cycling during use. These microcracks were also identified to open through inter-granular fractures parallel to the hot face, which appeared to be the main cause of lost lining during use. The reactions between the fayalite slag and refractory brick could eventually play a role in chemical dissolution of the brick only in the superficial layer at the hot face, as no slag components were identified deep into the brick.

Jan 1, 2009

By D. W. Collins

The uptake of gold from halide solutions by activated carbon has been investigated using various techniques. Halide systems typically exhibit combined adsorption-reduction type behavior. In an attempt to gain more information about the nature of these processes, samples of synthetic highly-oriented pyrolytic graphite (HOPG) were contacted with aqueous solutions of gold-iodide. HOPG represents a model structure for activated carbon comprising of basal- plane sites, edge sites, and various defect sites. Two basic instrumental methods were used to examine the uptake of gold by HOPG. The first was standard X-ray photoelectron spectroscopy (XPS). The other involved several scanning probe techniques. XPS clearly indicated a preferred uptake of gold at edge sites. However, iodine appeared to be distributed on both basal-plane and edge sites. At low iodine additions, tapping mode AFM showed that clusters were concentrated along steps and surface defects. At high iodine concentrations, the HOPG surface was uniformly covered by iodine.

Jan 1, 1998

By Ragnhild Aune

In fire refining of copper, the affinities of various impurity elements on dissolved oxygen is of great significance. Further, in the design of oxygen probes in liquid copper, the influence of solute interactions on the activity of oxygen need to be considered in order to evaluate the oxygen concentration in molten copper. The present paper presents a series of measurements of the activities of oxygen in liquid Cu-M-o alloys (where M stands for Mn, Zn, As, Se or Te) carned out by the present group employing the solid electrolyte galvanic cell technique. Extreme care was taken to control the oxygen potentials in the inert gas atmosphere, and to keep the oxygen levels very low in the molten metal. The oxygen content was determined by analysis of the samples taken out from the melt. The results obtained showed that Mn has a strong negative influence on the activity coefficient of oxygen in liquid copper. A similar, but less prominent effect was observed in the case of Zn. Arsenic had no influence on the activity of oxygen in Cu (liq.). Se and Te had slight negative effect on oxygen activities in copper at XQ >10-5, while at lower oxygen levels the interaction coefficients were found to be positive. The results obtained were compared with empirical models for the calculation of interaction coefficients available in literature.

Jan 1, 2003

By T. T. Chen

Raw anode slimes consisting primarily of PbSO4, AgCuSe, Cu3Se2, Cu2-x Se, Cu2O, CuSO4.5H2O, Sn arsenate and Sb-Bi-As oxide are batch-leached with electrolyte-O2 to dissolve Cu. During this process, Cu2O and CuSO4.5H2O are solubilized and the Cu in the selenides is leached with the formation of Ag2Se and Se. A small amount of Cu remains in the Ag2Se, Sn arsenate and Sb-Bi-As oxide. The decopperized slimes are repulped in Na2CO3 solution to convert most of the PbSO4 to NaPb2(CO3)2(OH). The Sn arsenate and Sb-Bi-As oxide partly react, but the Ag2Se is not significantly affected by the Na2CO3 solution. The NaPb2(CO3)2(OH) intermediate phase is dissolved in acetic acid to leave a final product consisting of Ag2Se, Se, Sn arsenate and Sb-Bi-As oxide, together with small amounts of PbSO4, NaPb2(CO3)2(OH) and various gangue constituents.

Jan 1, 1993

By J. M. Skeaff

As much as 100% of the gold and 67% of the silver in a sulphur-bearing hydrometallurgical leach residue have been transferred to copper metal at copper smelting temperatures by dissolving the partially calcined residue in an iron-bearing slag maintained in equilibrium with the liquid copper metal and matte phases. The precious metals can then be recovered by conventional refining techniques. Copper can be recycled at least four times without any detrimental effects on gold and silver transfers and recoveries. Apparent copper recovery in the .process can be over 100% because of the copper content of the residue. Based on slag analys.es, the overal1 recovery of gold in the copper metal and matte phases varies from 94% to 100% under all conditions investigated. On the? same basis, silver recovery varies .from 9S% ?to 99% under optimum conditions, but is only 4S% to 73% under other, less attractive conditions. Unaccounted for silver losses of' about 30% make it difficult to determine the major factors affecting ?silver transfer and recovery. A method for implementing the technology on a commercial scale at a Canadian copper/zinc smelter has been proposed. A preliminary economic assessment and comparison of the proposed pyrometallurgical process with conventional cyanidation indicates that either process is economically attractive for recovering gold and silver from leach residues. Although the capital costs are higher, the pyrometallurgical process is simpler, has higher recoveries, lower operating costs and no .potential environmental problems related to cyanide disposal.

Jan 1, 1989

By A. Warczok

The oxidation and smelting of chalcopyrite, bomite, chalcozine and pyrite has been studied under simulated flash smelting conditions. The results of copper sulphide oxidation show that under constant oxidation conditions, the degree of oxidation drops sharply when the particle size is increased above a given range. This critical size range varies typically between 200 and 500 pm depending on the oxygen content in the gas phase. For bomite, chalcopyrite and pyrite, the critical size range increases with increasing iron content in the mineral and with increasing oxygen content in the gas phase. The extreme case is observed for pyrite in pure oxygen, where there is no effect of the particle size on the degree of oxidization. Microscopical observations of the oxidized products show the influence of different factors on the mechanism of oxidation and fragmentation of the sulphide particles. Based on microscopical analysis and phase identification of the oxidized products, a model has been proposed for the oxidation and smelting of copper sulphide particles in suspended state. The mathematical model describing the sulphide particle oxidation is supported by the obtained results. Using this model, it is possible to describe the role of particular factors in the sulphide minerals oxidation.

Jan 1, 1992

By Pengfu Tan

In order to understand and control the formation of dioxins and furans in iron ore sinter plants and to possibly avoid expensive end-of-pipe removal stages, thermodynamic calculations on the stability of PCDD/Fs have been combined with sinter process modeling by means of kinetic simulations and computational fluid dynamics. Three thermodynamic databases of PCDD/Fs, derived using the Group Additivity approach and two computational molecular modeling methods, MNDO and PM3, respectively, combined with the SGTE database have been used to model the PCDDIF formation and the PCDD/F isomer distributions in iron ore sintering. The results show very similar conditions for the PCDD/F formation using the different databases. Concerning the isomer distributions of toxic PCDD/Fs, the calculated data derived from the MNDO method showed optimum agreement with measured values from industrial furnaces. The thermodynamic calculations also proved that the isomer distributions found in combustion processes are equilibrium values, while the concentration ratio of PCDDs and PCDFs in the wind boxes does not represent an equilibrium state. A CFD model of iron ore sintering was developed including the kinetics of 15 relevant chemical reactions with the aim of describing the temperature fields and the gas flow patterns in the sintering bed. On the basis of these information and experimental observations reported in the literature possible pathways for the PCDD/F formation in sinter plants have been identified: PCDD/Fs are formed in the critical temperature region of 250 to 450°C below the combustion zone, are then carried downwards with the gas and condensed close to the bottom of the sinter bed. Transported to the discharge end with the solid mixture, they are again released into the gas phase when the flame front approaches the bottom. PCDD/Fs are also formed in the last wind boxes when the hot off-gases cool down and reach the critical temperature range. Consequently, methods to reduce the dioxin formation reactions are proposed including inhibitor addition to the sinter feed and off-gas quenching.

Jan 1, 2003

By Wade L. Karlsen

"Revision surgery to replace joints in the human body requires materials that are strong, long-lasting, and biocompatible. Metallic implants made of cobalt-chromium-molybdenum alloys are already popular because of their proven corrosion and wear resistance properties, but there is an on-going effort to economically improve their performance. Alloying with inert nitrogen can enhance the mechanical properties of the alloy, enhance its corrosion resistance, and elevate the temperature at which the metallic implants can be thermally treated, without increasing the threat to the human body. The current work has produced a high-nitrogen Co-Cr-Mo alloy through HIP consolidation of metal powders that have undergone nitriding in a mechanically fluidized bed. The already fine microstructure of the powders combined with the increased nitrogen content resulted in significant property gains in the consolidated materials.IntroductionMetallic implants made of cobalt-chromium-molybdenum alloys are already popular because of their proven corrosion and wear resistance properties, but there is an ongoing effort to improve their performance. Research on a Stellite 21 cobalt-chromiummolybdenum alloy has shown that nitrogen alloying can be desirable from several standpoints [l]. Firstly, it has indicated that nitrogen can enhance the mechanical properties of the alloy, which could allow more demanding implant designs. The same work also demonstrated that nitrogen can elevate the temperature at which the metallic implants can be thermally treated, which is desirable in situations in which surface textures are to be sintered to the implant to enhance its fixation properties. Finally, that research work discovered that, not only does nitrogen not harm the corrosion resistance of the cobalt-chromium-molybdenum alloys, but it may in fact enhance it. Combining this with the fact that small amounts of nitrogen are not considered a threat to the human body, makes nitrogen alloying an attractive alternative for enhancing the properties of Co-Cr-Mo."

Jan 1, 2000

By J. M. Demarthe

MINEMET RECHERCHE (IMETAL Group, formerly Le Nickel-Penarroya-Mokta) has studied on a laboratory scale and patented a new process to recover metal values -copper- from sulphide ores and concentrates. It combines a cupric leaching, solvent extraction and copper sulphate electrowinning according to the main following steps - A direct and selective leaching of copper sulphide ores or concentrates at atmospheric pressure with cupric chloride to form cuprous and ferrous chlorides and elemental sulphur. Pyrite remains in the sulphur residue. - The leach solution is separated into two parts -In the first one, air is injected to precipitate iron as goethite. The oxidation step can be easily realized at atmospheric pressure by maintaining an excess of cuprous and-ferrous chlorides in the liquor. Copper is extracted from the second part as cupric ion by an LIX reagent. Direct injection or air in the mixing chamber maintains good extraction conditions, so that only one mixer settler is required. - Iron, in the form of ferrous ion, is not coextracted. - Copper is stripped from the organic phase, transferred into a sulfuric phase and sent to sulphate electrowinning cells, which are now conventional in copper metallurgy. - Only electricity and air are required. After a feasibility study, the next step will be to develop it on a pilot and commercial scale.

Jan 1, 1976