By I. Zaplatynskyj, G. C. Kuczynski

SINCE the excellent studies of metal powder compaction executed by Kamm, Steinberg, and Wulff, no work on the subject has appeared in the technical literature. Kamm et al. were the first to investigate quantitatively the distribution of density in a powder compact, as a function of pressure, height and diameter of the die, powder particle size, etc. For this purpose they devised a very ingenious method. They inserted a thin lead grid into a die and then filled the die with powder. During cold pressing, the lead grid -moved downward. Due to its deformability it followed closely the downward descent of the adjacent powder. The die was then radiographed and, from the deformations of the grid openings measured on the radiographs, the density in the vicinity of each opening was evaluated. Their findings led them to the conclusion that the friction on the side walls of the die is a major controlling factor of the density distribution inside the cold pressed powder compacts. However, it is difficult to conduct tests similar to those of Kamm, Steinberg, and Wulff in a processing plant laboratory, which usually lacks the necessary expensive radiographic equipment. The purpose of this note is to describe a method which makes it possible to determine the density distribution in green powder compacts with the same accuracy as the lead-grid method but which is far simpler and faster and requires only standard laboratory equipment. Instead of using a lead grid, the hardness at selected points of the sectioned compact is determined. If the relationship between hardness and density is known the density distribution is readily obtained. This relationship is easily found from measuring hardness and densities of thin compacts. In such compacts the density, for all practical purposes, is constant throughout. The method was tested on a Plast nickel powder, grade FlA-A20, kindly supplied by Plast Metals Co. Thin compacts (height to diameter ratio 0.2) were pressed in a single action cylindrica1 die at various pressures. The density of the compacts was determined by weighing and by measuring the height and diameter with a micrometer. Subsequently the Rh hardness was determined. Up to ten readings were taken on each specimen. The difference in hardness readings on each compact was never greater than three corresponding to about 0.1 g per cu cm uncertainty in density. By varying the compaction pressure of the samples, a whole scale of densities was obtained allowing construction of a set of density-hardness calibration curves. To test the method several compacts of different height were pressed under varying pressures. Die walls were always well lubricated. After pressing, the compacts were mounted in bakelite and halved by grinding, and hardness readings taken along the diameters of the specimens. The distance between adjacent indentations was about 2.5 mm. After hardness readings were translated into densities, contour maps of densities of the compacts were prepared. One of them is reproduced in Fig. 1. The areas encompassed by the curves are labeled with numbers representing the density in g per cu cm of those regions. In Fig. 2 the same results are re-plotted to emphasize the radial density changes at various depths. The results thus obtained confirm the findings of Kamm, Steinberg, and Wulff kentioned previously. They are recapitulated here briefly. 1—The densest part of a compact pressed from one side is at the outer circumference at the top and the least dense part at the bottom, at the outer circumference. Figs. 1 and 2 show this clearly. 2—The density near the cylindrical surfaces of the compact decreases uniformly with height from top to bottom. 3—The density variation increases with the height to diameter ratio. References R. Kamm, M. A. Steinberg, and J. Wulff: Trans. AIME (1941) 171,'R. p. 439 ;MetaLs Technology (February 1941). R.p. Kamm, M. A. Steinberg, and J. Wulff: Trans. AlME (1949) 180, 2R.P. 694; MetalS Technology (December 1948).

Jan 1, 1957

By G. W. Brownell, H. T. F. Lundberg, R. W. Pringle, K. I. Roulston

The rapid improvement of the airborne scintillometer and the perfection of its efficiency for counting low energy gamma radiation has made it possible to work out a technique to map in great detail the radiation pattern at the earth's surface. On such maps low radiation over certain areas appears to indicate the existence of oil accumulations, forming a pattern similar to that obtained by the geo-chemists. RADIOACTIVE analyses of samples from the surface of oil fields were carried out more than 10 years ago in Alberta by the alpha particle ioniza-tion chamber technique,' but large enough tracts could not be covered in these investigations to make possible any evaluation of the method as a means of oil exploration. Considerable interest has recently been revived, however, as a result of certain striking advances which have been made in the instrumentation available -for the measurement of radioactivity. It is the object of this paper to indicate the nature of these improvements in radiation technology and then to describe the attempts that have been made to interpret the radioactive patterns obtained in the course of airborne recordings with the new instruments. Since the survey can be carried out from the air and records can be accumulated over vast areas in a short time, the result may easily lend itself to statistical treatment. Areas have been surveyed in Alberta, British Columbia, Saskatchewan, Quebec, Texas, New Mexico, Nebraska, Colorado, Utah, and Montana. Producing fields in Alberta and West Texas have been flown over several times in different directions, Fig. 1. The operations were then extended into unknown territory and drill holes were put down on the anomalies which looked promising. The results from these drillings were encouraging and have given hopes for the development of an entirely new method of oil exploration. Any large scale method for the survey of radioactive anomalies must be based on the measurement of gamma rays, as beta and alpha rays have much too short a range to be of any significance. Thus the essential improvement which has made the present stage of this work attainable is the development of new highly sensitive detectors for gamma radiation. In the past the only detectors of any consequence that were available were the ionization chamber and the geiger counter, but both of these suffer from the defect that only a small proportion of the gamma rays passing through the counter are detected, possibly 0.1 to 0.2 pct. The recent development of the scintillation counter2,3 has completely transformed the situation and has had a considerable impact on many branches of nuclear technology. The detection of alpha particles in zinc sulphide screens by visual observation of the individual scintillations which these particles produce dates back to the early spinthariscope of Rutherford and Crookes, but the combined use of an appropriate scintillating phosphor and photomultiplier tube had to await the technical development of the latter many years later. With this development came the modern era of the scintillation counter and a knowledge of phosphors which have a large light output under the bombarding action of gamma radiation. Some of these phosphors are relatively dense and are capable of stopping a large proportion of the incident gamma radiation. As the sensitive region is the whole volume of the crystal, a very high detection efficiency, 50 pct or more, can be obtained for medium energy gamma rays. Scintillation counters for geological purposes were first developed in 19494-6 in an attempt to utilize this remarkable improvement in efficiency, which has the attractive consequence that only a small portion of the normal background of the counter is due to cosmic radiation. In 1949 tests were made in northern Saskatchewan by Lundberg Explorations Ltd. with portable scintillation counters which gave excellent results in the search for uranium and served to indicate unknown uranium deposits in areas previously closely surveyed with geiger counters. Portable scintillometers (registered in Canada) are now commercially available and in regular use,' and the adaptation of the instrument to radioactivity oil well logging has also been very successful.8 Initial attempts to measure radioactivity from aircraft with scintillation counters were made during this period in the same area and yielded most encouraging results. It would be appropriate to consider some specific requirements for airborne investigations. The essential problem to be met in the detection of any radioactive source is the necessity of obtaining a signal greater than the statistical fluctuations of the background counting rate for the instrument. It is possible to show that Nt>2k2 is the condition for detectability of a signal where N = average background counting rate for the detection. t = time constant of the counting rate meter, used to determine the average number of counts arriving in a certain predetermined time interval. N' = average source counting rate at the detector. k = N/N', and N>>N'. Sample values are given in Table I. Assume that the aircraft carrying the equipment is travelling at 120 mph, in which case it will cover 176 ft in 1 sec. Assume also, as a first approximation, that a point source target is in range when the air-

Jan 1, 1954

By S. W. MEALS

TWENTY million people in this country and Canada in nearly four million homes can give thanks to our Creator for natural gas, that most wonderful natural fuel with which Dame Nature has so bountifully blessed us. It is a clean, healthy and cheerful fuel, made up almost entirely of carbon and hydrogen. There is no residue, no waste and there are no objectionable constituents; an ideal fuel for the home. It operates like magic, open the valve and it is there for your needs, winter or summer, night or day. You are not required to place your order 30 to 90 days in advance and you do not need to pay for your winter's supply in advance. No ashes to worry about, no flues or chimneys to clean, nor kindling wood to store or bother the housekeeper. We who have been so blessed do not realize what it would mean to be without it. If in place of opening a valve we had to go to the woodshed or coalhouse and then build our fire-carry out the ashes-well, some of us I am afraid would be late reaching our offices and perhaps would miss our hot cakes for breakfast. One cubic foot of gas produced from the White Sand formation contains 1130 B.t.u. and weighs 47/1000 lb.; there are about 24,000 B.t.u. in 1 lb. of gas. Temperatures of over 3400 deg. Fahr. have been obtained with natural gas. Not only is it a superior fuel for the home but it has no equal for use in many large manufacturing industries, especially with the making of glass, pottery and open-hearth steel. In an open-hearth furnace, properly constructed, 5000 cu. ft. will melt one ton of steel. It requires 1/3 ton of bituminous coal gasified in a producer to do the same work, or about 40 gal. of tar or fuel oil, or 11,000 cu. ft. of by-product gas.

Jan 1, 1926

By C. W. Robinson

Transportation is the minerals business. Once upon a time the geologist, the engineer and later the metallurgist reigned supreme, but the leading role in mineral development today is the economist-especially the transportation economist. Obviously this trend is more important for large volume, low value mine-to-market movements of such commodities as iron ore, phosphate, potash, coal and petroleum. But, transportation is of sufficient importance to all mining activities to be included in forward planning. Civilization has been influenced by transportation developments to an extent little understood or appreciated. Although industrialists are capable of intelligent historical analysis of this phenomenon, too frequently they have failed to project, or anticipate those changes in transportation techniques which will influence the pattern of industrial growth.

Jan 1, 1971

By J. S. Aronofsky, H. J. Ramey

Potentiometric model studies of the five-spot water flood to determine the influence of mobility ratio upon injection or production histories are described. The results suggest a method for the correlation of data from field pilot tests for the estimation of an effective mobility ratio and its effect upon field water floods. The effect of the well spacing-to-well radius ratio upon production histories is presented. A method of accounting for this factor is suggested. The influence of injection (or production) rates and injection and production well pressures upon production histories is shown. The five-spot well pattern was investigated for water-to-oil mobility ratios of 0.1 to infinity. INTRODUCTION It has been well established that mobility ratio has an important effect upon flood patterns.1,2,3,4,5 It should be equally apparent that injection and production histories must also be influenced by mobility ratio. However, none of the articles referred to above mention the importance of being able to predict the effect of well pressures (or injection rates) during the entire time history of a waterflood operation. A complete description of production histories (the terms "injection" and "production" are synonymous for the steady-state model under consideration) would provide values for well pressures and interface positions at any time for a specified injection rate. conversely, if the waterflood problem is specified in terms of a constant injection well pressure, then it would be desirable to know the injection rate and interface positions at any time. This paper describes the results of potentiometric model studies which were used to analyze the influence of mobility ratio on injection or production histories. A method is presented for calculating production histories over a range of ratios of well spacing-to-well radius. The basic method described in this paper to evaluate production histories is to: (1) determine interface position as given in Ref. 1, and (2) measure electrical current and voltage drop for each interface position. It should be mentioned that the current state of knowledge on flood patterns as affected by mobility ratio shows that significant discrepancies exist between the results of various investigators2,3,4,5. It is beyond the scope of this paper to discuss the reasons for such discrepancies. However, the method of determining production histories presented in this paper could be applied to any of the swept-area patterns presented in the literature. All results given in this paper are based on a set of swept areas obtained by the potentiometric method. Potentiometric analyzer technique is adequately described in the literature, but the basic assumptions involved in work of this nature bear repetition. It is assumed that: 1. A distinct oil-water interface exists in the reservoir; only water is mobile in the region behind the interface (water zone) and only oil is mobile in the region ahead of the interface (oil zone). 2. There is a fixed mobility value, (k/µ) w associated

Jan 1, 1957

By Ronald C. Koo

THE effect of grain size on the mechanical properties of the bcc metals has been a subject of intensive theoretical and experimental study.'-l5 Quantitative relationships have been established experimentally between yield stress and grain size and between the ductile-brittle transition temperature and grain size in a number of metals.6"15 Much significance has therefore been attached theoretically to the grain size dependence. In all these experiments, different grain sizes were always achieved by annealing specimens at various temperatures. The implicit assumption was that any change in the dislocation substructure or in the distribution of impurities which might occur simultaneously with the production of various grain sizes had only a negligible effect on the mechanical properties. The validity of this assumption, however, is questionable. transformation in iron-nickel alloys is actually an extraneous phenomenon due to inadvertent compositional changes in the martensite if the heating rate is not sufficiently rapid. This complication can be avoided by up-quenching for the reversal treatment,5 and then the stabilization does not appear. Clearly, the lattice imperfections and strengthening produced by the reverse transformation are not responsible for the marked stabilization which has been observed by other investigators in these alloys. Data will be presented in this note to show that, at least in recrystallized tungsten of commercial purity, the difference in the ductile-brittle transition temperature of specimens annealed at various temperatures is more a result of a variation in the distribution of impurities rather than of the difference in grain size produced by the anneal. Ductile-brittle transition temperatures in tension were determined on powder-metallurgy tungsten specimens recrystallized at various temperatures. Tensile specimens having a gage length of 1.50 in. and gage diam of 0.18 in. were recrystallized at 1450°, 2000°, 2350°, 2550°, 2750°, or 2800" for 30 min in a vacuum furnace at a pressure of 1 x 10"5 mm of Hg and then tested at a constant extension rate of 8 x 10 per sec in an argon atmosphere from 100" to 800". Typical quantitative analyses of impurities are given in the Table. These results show that, within the precision of the analyses, see Table, annealing did not result in any detectable change in the impurity contents of the specimens, nor was there any detectable difference in purity between specimens having large differences in grain size annealed at the same temperatures . The results of the tensile tests yielded three distinct ductile-brittle transition curves approximately 225' apart. As shown in Fig. 1, data of specimens annealed at 1450°C and those of specimens annealed at 2000°C (O) fell on Curve A. Data of specimens annealed at 2350" and 2550°C fell on Curve B, and those of specimens annealed at 2750" and 2800°C fell on Curve C. The decrease in ductility with increase in annealing temperature became so pronounced that one third of the specimens annealed at 2750" and two thirds of the specimens

Jan 1, 1963

By J. O. Betterton, D. S. Easton

A detailed investigation was made of the phase diagram of silver-zirconium, particularly in the region 0 to 36 at. pct Ag. The system was found to be characterized by two intermediate phases Zr2Ag and ZrAg and a eutectoid reaction in which the -zirconium solid solution decomposes into a-zirconium and Zr2Ag. It was found that impurities in the range 0.05 pct from the iodide-type zirconium were sufficient to introduce deviations from binary behavior, and that with partial removal of these impurities an increase in the a-phase solid solubility limit from 0.1 to 1.1 at. pct Ag was observed. The phase diagram of the silver-zirconium system is of interest as an example of alloying a transition metal from the left side of the Periodic Table with a Group IB element. Silver would normally act as a univalent metal, its filled 4d-shell remaining undisturbed during the alloying. However, there is a possibility that some of the 4d electrons might transfer to the zirconium. An insight into such a question can occasionally be obtained by comparison of phase diagrams. The silver-zirconium system forms part of a more complete review of various solutes in zirconium in which these valency effects were studied.' Earlier work on the silver-zirconium system was done by Raub and Enge1,2 who investigated the silver-rich alloys. After the start of the present experhents, work on this system was reported by Kemper3 and by Karlsson4 which for the most part agrees with the phase diagram presented here. EXPERIMENTAL PROCEDURE The alloys were prepared by arc casting on a water-cooled, copper hearth with a tungsten electrode and in a pure argon atmosphere. Uniform solute composition was attained by multiple melting on alternate sides of the same ingot. Progressive improvements in the vacuum conditions inside the apparatus during the course of the experiments reduced the Vickers hardness increase of the pure zirconium control ingot from 10 to 20 points, observed initially, to negligible amounts at the end of the experiments. Such hardness changes in zirconium are a well known indication of purity. For example, -01 wt pct additions of oxygen, nitrogen, and carbon increase hardness by 6, 10, and 3 VPN respectively. '9' Further verification that the final casting technique did not add a significant quantity of impurities was obtained when pure zirconium was arc cast and then isothermally annealed in the vicinity of the allotropic transition. The transition was always observed to take place over the same temperature range as in the original crystal bar. The alloy ingots were annealed in sealed silica capsules for times and temperatures which varied between 1 day at 1300°C and 60 days at 700°C. The best method found to prevent the reaction of the zirconium with the silica was foil wrapping of molybdenum or tantalum. With this method, samples of pure zirconium were found to be unchanged in hardness after annealing for 3 days at 1200°C. In most of the experiments the protection of these foils was supplemented by an additional layer of zirconium foil inside the molybdenum or tantalum foil. The alloys, foil, and the capsule were outgassed at pressures in the range 10 to l0-7mm Hg in the temperature range 800" to 1100°C before each anneal in order to remove hydrogen and other impurities, and to provide a suitable container for the high purity, inert atmosphere, which is essential in the annealing of zirconium. The temperature measurements were made with Pt/Pt + 10 pct Rh thermocouples calibrated frequently during the experiments against the melting points of zinc, aluminum, silver, gold, and palladium. For the longer anneals the sum of various temperature errors was generally well within ± 2°C. For short-time anneals and during thermal analysis the overall temperature error is considered to be within ± 0.5°C. The compositions of the alloys from the quenching experiments were determined by chemical analysis at Johnson Matthey and Company, Ltd., under the direction of Mr. F. M. Lever. The actual metallo-graphic samples were individually analyzed in every case, and prior to the analyses two or more sides of each specimen were examined to insure that the specimen was not segregated. The sum of the solute and solvent analyses was in each case within the range 99.9 to 100.1 pct. In the course of the experiments, minor impurities in the range 0 to 500 ppm were found to have significant effects on the zirconium-rich portion of the phase diagram. Similar effects had been encountered previously in other zirconium phase-

Jan 1, 1959

By D. Kunstelj, M. Stubicar, A. Tonejc, A. Bonefacic

A. Bonefafcic, D. Kunsfeli, M. Stubicar, and A. Tonejc The present communication is concerned with the variation of the texture in aluminum wires with die angle and temperature, at constant speed of extrusion. Experiments were carried out concurrently on refined samples, with a stated purity of 99.997 pct pure A1 and commercial samples of 99.5 pct Al. Ingots of refined aluminum samples were machined to 30-mm-diam by 150-mm-long billets. These billets were transformed to 5-mm-diam wires by drawing. The final form, suitable for examination, was obtained by extrusion through conical-face dies with a 1-mm hole diam and extrusion ratio 5:l in diam. The initial form of the commercial aluminum samples was drawn wire 5 mm in diam. These samples showed a poorly defined texture with (111) as a major and (001) as a minor component. A similar defined texture appeared in the refined aluminum samples after drawing to 5 mm diam. Conical-face dies with different angles (defined by the axis and the generating line of the cone) were used in our experiments. The values of the angles were 27, 35, 45, 57, 63, and 90 deg. The extrusion container was fitted with a heating element and controller permitting temperatures up to 600°C to be maintained within i5"C. Extrusion was performed at 250°, 300°, 350°, 400°, and 500°C at constant speed (approximately 1 mm per sec) and constant die reduction. The extrusion product was a wire 1 mm in diam and approximately 20 cm long. In order to remove the surface layer with the "conical" texture and to reduce the absorption by the X-ray examination of the samples, the extruded wire was etched to 0.22 mm in diam. Experiments were performed in the middle sections of the 20-cm-long wires. In addition to the die of l-mm hole diam, dies with a 1.5-, 0.7-, 0.6-, 0.5-, and 0.4-mm hole diam and 63-deg die angle were constructed. In our experiments we did not find in these ranges any important difference concerning the texture of the extruded wires and we continued our work solely on the 1.0-mm die. The diffracted X-rays (Cu K radiation) were recorded photographically. Diffracted intensities were measured on the (111) reflection with a microphotometer. The relative amounts of texture components were determined from the areas under the diffracted maxima. We found the texture of extruded aluminum wires to be strongly influenced not only by the temperature of extrusion and the purity of the sample but also by the form of the die. It is generally admitted that cold-drawn aluminum wires have mainly a (111) texture with a small amount of (001) component, Table I of Ref. 1. In our experiments with wires extruded in conditions represented by Fig. 1, in some cases a single (001) texture was obtained. If these wires were drawn repeatedly at room temperature, X-ray measurements revealed a duplex (001)-(111) fiber texture. Further drawings increased the (111) and decreased the (001) texture component. In Fig. 1 the percentage of material oriented with (001) parallel to the extrusion direction is represented as a function of the temperature and the die angle (a), for commercial and refined aluminum samples, respectively. From these diagrams we may draw the following conclusions. The slope of the die (a) influenced more strongly the texture at the lower rather than the higher temperatures. Again, a stronger influence was found in the case of the commercial in comparison with refined aluminum samples. In the case of the commercial aluminum samples the amount of material with (001) texture increases with increasing wire temperature in an approximately linear manner. This effect is less pronounced in the pure aluminum samples, with the exception of the die with a = 45 deg. In this case the (001) texture decreases with increasing temperature, as shown in Fig. 1. Component (001) is more pronounced in higher-purity aluminum samples. Our experiments led to the conclusion that both (001) and (111) components are essentially stable in extruded aluminum wires. As we obtained a single (001) texture starting with a sample of drawn wire in which the (001) component was very weak, our experiments revealed that the (001) component is not a remnant of the initial texture; this is in disagreement with the findings of Vandermeer and McHargue.1 We gratefully acknowledge discussions with Professor M. Paic. 1 R. A. Vandermeer and C. J. McHargue: Trans. 7MS-AME, 1964, vol. 230, p. 667.

Jan 1, 1969

By R. G. Ward, D. R. Gaskell

Using the maximum bubble pressure technique, the densities of iron silicates at 1410°C have been measured blowing helium, nitrogen, and argon. By ensuring equilibrium between the melt and the blowing gas with respect to oxygen potential and by minimizing tempcrature cycling of the furnace, iron precipitation in the melt has been prevented. Thus the previously reported effect of blowing-gas composition on the densities of the melts has been eliminated. Consideration of the oxygen densities of the melts gives an indication of the structural changes accompanying composition change. The density-composition relationship of iron oxide-silica melts in contact with solid iron has been the subject of several investigations1-7 and considerable disparities exist among the various results obtained. Of these investigations, all except one5 have employed the maximum bubble pressure method. In the most recently reported of these investigations1 the density-composition relationship obtained blowing nitrogen differed from that obtained blowing argon. The measured densities obtained under nitrogen were greater than those obtained under argon, the difference being a maximum at the pure liquid iron oxide composition and decreasing with increasing silica content. This observation rationalized the disparities existing among the results of the earlier investigations, showing that two lines, one for nitrogen and the other for argon, could be drawn to fit all the earlier results. No explanation for this phenomenon could be offered. Chemical analysis of rapidly quenched samples of melt for dissolved nitrogen, and direct weighing measurements, excluded solution of nitrogen in the melt from being the cause of the increase in density. The range of blowing gases was extended by Ward and Hendersons who measured the density of liquid iron oxide bubbling helium, nitrogen, neon, argon, and krypton. The measured density was found to decrease smoothly with increasing atomic number of the bubbling gas. The work reported here is a continuation of the program initiated by Ward and Sachdev7 to study the densities in multicomponent melts in which the iron oxide-silica system is the solvent. As such it is necessary to explain or eliminate the anomalous densities of iron silicates under different atmospheres, and the present rede termination was carried out towards this end. EXPERIMENTAL The maximum bubble pressure method of density determination was again employed and the experimen- tal apparatus used was essentially the same as that used by Ward and Sachdev.7 A molybdenum-wound resistance furnace heated an ingot iron crucible of internal diameter 1 in. containing a 2-in. depth of melt. The bubbling gas was blown through a 1/4 -in.-diam mild steel tube onto the end of which was welded a 2-in. extension of 1/4 -in.-diam ingot iron rod, drilled out to 5/32 in., and chamfered to an angle of 45 deg. The blowing tube was introduced to the furnace through a sliding seal and its position was controlled by a vertically mounted micrometer screw which allowed the depth of immersion to be determined with an accuracy of ± 0.01 cm. A Pt/Pt-10 pct Rh thermocouple was located below the crucible and temperature control was effected initially by means of an on-off controller and later by a saturable core reactor. The bubble pressure was determined by measurement of a dibutyl phthalate manometer using a cathetometer. PREPARATION OF MATERIALS Iron oxide was produced by melting ferric oxide in an inductively heated iron crucible in air. The liquid was quenched by pouring onto an iron plate. Silica was prepared by dehydrating silicic acid at 650°C for 12 hr. RESULTS Before any measurements of the density of a melt were made, the density of distilled water at room temperature was measured bubbling helium and argon. Both gases gave the density as 1.00 ± 0.01 g per cu cm which showed that the density of the manometric fluid (dibutyl phthalate) was not affected by contact with the blowing gas. With the furnace controlled by an on-off temperature controller an attempt was made to measure the density of pure liquid iron oxide by bubbling argon. The furnace atmosphere gas and bubbling gas were dried over magnesium perchlorate and deoxidized over copper turnings at 600°C. It was found that the pressure required to blow a bubble at a given depth increased slowly with time, and thus it was impossible to obtain a unique value for the density of the melt. Inspection of the blowing tube after removal from the furnace showed that rings of dendritic iron had precipitated from the melt onto the immersed part of the tube. This is shown in Fig. l(a) where the various "steps" correspond to different depths of immersion. The precipitation of iron was considered to be due to one or both of two possible causes: i) The composition of the liquid iron oxide is that of the liquidus at the temperature under consideration and can be expressed by the equilibrium

Jan 1, 1968

By George Simkovich

It was hypothesized that solid-state point defects should alter the flotation properties of solids. Tests conducted on pure AgCl and AgCl doped with CdC12 show that atomic point defects exhibit an important role in the floatability of AgC1. Tests conducted on PbS doped with Ag2s or Bi2S3, also show that the defect structures resulting from these dope additions, i.e., a combination of electronic and atomic point defects, contribute significantly to the flotation of PbS. IT has been established that flotation occurs only when a finite contact angle exists between a solid and a gaseous bubble.' This angle, measured through the liquid phase, is expressed by the equation where the are inter facial free energies and the subscripts S, G, and L represent solid, gas, and liquid phases, respectively. As is seen in Eq. [I] three interface free energies, sG, sl, and GL, enter into the contact angle equation. Therefore, any variation in these energies which sufficiently varies the contact angle will, in turn, vary flotation processes. Changes made in any of the phases concerned, i.e., gas, liquid, or solid phase, are reflected through the changes occurring in two of the surface energy terms. Thus, a change in the liquid composition would be noted in sL and GL, and it is this phase, the liquid, which is most frequently altered in flotation studies., Changes in the solid phase must be reflected through the changes occurring in the sG and sL terms. In particular, it is hypothesized that changes in the surface concentrations of point defects in the solid-phase will alter the sG and sL terms which, in turn, will be reflected by flotation results. As an illustration of this hypothesis one may consider the defect structure and the flotation of AgC1. The bulk defect structure of AgCl is essentially one involving equal number of cation vacancies and interstitial cations.3 Upon adding CdC1, to AgC1, a greater number of silver ion vacancies are created in the bulk of the crystal.4 On the surface of the crystal the smaller binding forces and the free space accomodations may also allow for the creation of "surface interstitial anions", which will be designated as ad-anions. Thus, the point defect structure of the surface of AgCl doped with CdCl, will consist of cation vacancies and/or adanions. If the molecular forces responsible for the surface energies, ?SG and ?sL, are significantly altered by the presence of these surface point defects, then differences in flotation results will be noted as the concentration of these defects is varied. The defects present in AgCl are predominantly atomic in nature. In the case of PbS both electronic and atomic defects are present.5 This compound conducts electrically by either electrons or electron holes depending upon whether excess lead or excess sulfur is present. Upon disolving BiS3 in stoichio-metric PbS, one increases the concentration of cation vacancies and the number of electron carriers in the bulk of the crystal.5" At the surface, the possibility of ad-anions must also be considered. Conversely, upon dissolving AgS in stoichiometric PbS one increases the concentration of interstitial cations and the number of electronhole carriers in the bulk of the crystal.5,6' At the surface the interstitial cations will be designated as ad-cations. Thus, the point defect structure of the surface of a PbS crystal doped with Bi2S3 will consist of a number of cation vacancies and/or ad-anions and an excess of electrons. Conversely the point defects on the surface of a PbS crystal doped with Ag2S will consist of a number of ad-cations and an excess of electron holes. Again, as in the case of AgC1, should the molecular forces responsible for the magnitude of the interface free energies, ?sG and ?sL, be significantly altered by the presence of these surface defects then significant differences in flotation results will be noted as the concentration of these defects is varied. EXPERIMENTAL To test this hypothesis flotation tests were conducted on pure and doped AgCl and on PbS doped with either Bi2S3 or Ag2S. Preparation of the AgCl samples was performed as follows: AgCl and weighed amounts of CdC1, were melted in a porcelain crucible. The melt was then forced through a capillary tube and the particles emitted solidified in air as they fell about 1.5 meters. Spherical particles, -0.50 + 0.25 mm, were separated from the remaining solidified material

Jan 1, 1963

By Tilden Cummings

The extractive mineral industries share a number of common characteristics and basic problems which are completely different from those associated with manufacturing and mercantile operations. These industries now supply about 95% of the inanimate energy consumed in this country, and share with agriculture in providing virtually all of our basic raw materials. Mineral producers, like farmers, are subject to the economic hazards of fluctuating markets and prices. Unlike farmers, however, they cannot renew the productivity of the earth, but must seek continually for new sources of supply. The necessity for exploration and development of new reserves, to replace those used up by production, introduces additional factors of economic risk. These operations require the expenditure of large amounts of capital, often well in advance of any assurance of profitability. Commercial banks that understand these special problems can provide a variety of constructive financial services to the mineral industries. The history of cooperation between banks and mining enterprises has yet to be written, but there is every indication that it would encompass a period of hundreds of years. Records refer to depository and lending services by the early European private bankers involving precious metals and jewels. Many of the exploratory voyages to the Far East and the New World were organized with the financial backing of wealthy syndicates, some of which also provided banking services, in the hope of finding new sources of gold and other precious minerals. In the United States many large banks are closely identified with the development of some of the larger mineral deposits such as the Mesabi Range and the gold fields of California.

Jan 5, 1965

By M. D. Banus, M. B. Bever, A. K. Jena

Measurements of the heat effects on addition of various solid phases of InSb to a solution calorimeter have confirmed the existence of a new high-pressure plzase InSbQII), which was jormed at 37 kbar and 623°K. The heats of formation of InSbQ), InSbfl), and InSb(111) have been measured and the heats of transjormation of InSb(1) to InSb(1l) and InSb(Iii) and of 'InSb(ll) to InSb(iiI) at atmospheric pressure and 78°K have been determined independently. Other thermodynamic properties of these phases, the phase boundary InSb(i)/InSb(ll), and the relative positions of the triple points are calculated. The pressure-Dolume term is shown to be more critical than the internal energy difference in making the phase InSbQ) less stable than InSb(II) at high pressures. Observations on partially transformed specimens suggest that the transformation of' metastable InSb (III) takes place in the two steps InSb(lll) — InSbQI) and InSbQI) — InSb(l). The compound InSb can exist as several phases depending on the temperature and pressure. The phase InSb(I), which is a semiconductor having the zinc-blende structure, transforms into the phase InSb(11) at a pressure of about 23 kbar and room temperature.'-3 The phase InSb(II) has the 6 tin structure,4-6 is metallic, and becomes a superconductor below 2.lok7 An orthorhombic phase of InSb has been reported to occur above a pressure of approximately 30 kbar at room temperature.' This phase is also a superconductor below about 3.4k9 The phase InSb(I1) is retained at atmospheric pressure if it is quenched to 78°K under pressure,6,7 but tends to transform at higher temperatures and does so explosively above approximately 210ok,7 A value of the heat of transformation of InSb(1) to InSb(II) at 210°K and atmospheric pressure has been reported.' A concurrent publication'0 reports evidence for a new solid phase InSb(III), which was formed by annealing InSb above 58 1°K at 37 kbar, above 560°K at 52 kbar, and above 473°K at 65 kbar. Specimens of InSb(II1) had a superconducting transition temperature of 4.lo ± 0.1oK. X-ray diffraction patterns also indicated the presence of a new phase. In this communication, thermodynamic properties of the phases InSb(I), InSb(II), and InSb(II1) are reported and discussed. The phase boundary InSb(I)/InSb(II) and the relative positions of the triple points are calculated. 1) EXPERIMENTAL 1.1) Preparation of Specimens. Specimens of the high-pressure phases of InSb were prepared in a belt-type high-pressure chamber by a tichnique described in detail elsewhere.'' Charges of 0.6 to 0.8 g of Cominco semiconductor grade InSb were used. The temperatures were measured with a chromel-alumel thermocouple, the hot junction of which was within 0.5 mm of the specimen. The specimens were heated under a pressure of 37 kbar for 1 hr at 723°K (which is well above the liquidus) and quenched to room temperature. One set was annealed at 523°K and another set at 623°K for 20 to 24 hr. These annealing temperatures were chosen because 523°K was below and 623°K was above the temperature of the transformation of InSb(II) to InSb(1Tl) at 37 kbar.10 The specimens were then cooled to 125°K by passing liquid nitrogen through the jacket of the belt die before the

Jan 1, 1968

By N. Mungan

A study was made of the effects of wettability and interfacial tension on the immiscible displacement of a Iiquid by another Iiquid from porous media. The influence of viscosity ratio was also investigated. Porous media used were polytetrafluoroethylene (TFE) cores prepared by compressing TFE powder under different pressures. lt is shown that displacement of a wetting by a nonwetting Iiquid is always less efficient than the displacement of a nonwetting by a wetting fluid, all other things being equal. In the former case, the recovery efficiency can be increased substantially by either reducing the interfacial tension or increasing the viscosity of the displacing fluid. A qualitative discussion is given on the implications of this work to the recovery of crude oil by water flooding. INTRODUCTION The high cost of oil exploration and new recovery schemes makes it imperative that waterflooding be conducted under conditions favoring most efficient oil recovery. To improve oil recovery by waterflooding, it is essential that the role played by interfacial forces in the entrapment of residual oil be studied and understood. Interfacial phenomena in natural rock, connate water and crude oil systems are very complicated because of the complexity of the natural liquids found in petroleum reservoirs, because of our inability to adequately describe the geometrical structure of the porous media and because of a lack of understanding of physical and chemical interactions between the liquids and surface of the pores. The problem becomes further complicated when one tries to elucidate the role of interfacial phenomena in fluid flow. Numerous studies of the displacement of oil by water under different interfacial tension or wet-tability conditions have been made.lm3 These studies have been performed in silica, alundum or sandstone systems using water and paraffin oil and also some surface active material to control the interfacial tension s and the contact angle 0. Unfortunately, the high energies of various interfaces involved favor adsorption and orientation of the surface active material at the interfaces. Also the surface active material concentration at the interfaces exceeds that in the bulk of the liquid phases. Such surface excess may cause the surfactant distribution, the contact angle and the interfacial tension to differ from their measured static equilibrium values and makes interpretation of the displacement experiments difficult. Furthermore, as changes in s also lead to changes in cos 0, the role played individually by one of these parameters in the displacement becomes obscured by the effect of the other. To circumvent these difficulties, a low surface energy solid and true solutions or pure liquids should be used. Use of a low surface energy solid minimizes adsorption and orientation effects at the solid-liquid interfaces. By controlling s and cos 0 through use of selected pairs of pure liquids or true solutions rather than by surfactants, the adsorption effects at liquid-liquid interfaces are eliminated. In the present study TFE cores were used as the porous media. Liquids used were water, sucrose solutions, paraffin oils and benzyl, n-butyl and isobutyl alcohols. The interfacial tension was varied from 40 to 1.1 dynes/cm by suitably choosing the liquid pair. A surface active material was added to the water-oil system only in the case where interfacial tension of 0.5 dyne/ cm was desired. No precise changes of cos 0 were attempted. However, either the displaced or the displacing liquid could be made the one which preferentially wets the TFE surface. Using sucrose solutions and blends of paraffin oils proved to be a convenient way of changing the viscosity ratio between the displaced and displacing liquids. The present investigation examines the effect of interfacial tension, wettability and viscosity ratio on the immiscible liquid-liquid displacement from porous media. Observed data permit a

Jan 1, 1967

By L. W. Reynolds, R. F. Campbell, K. G. Carroll, S. H. Ballard

Based on metallographic and X-ray data probable equilibrium conditions from 1340" to 2400°F are presented for the composition range investigated. These are correlated with investigations of Takei and Kuo. Provision is made for existence of Mo, C and (Fe, Mo)2,C, carbides heretofore omitted in diagrams in this composition range. These carbides and (Fe, Mo),C, in equilibrium with ferrite and austenite, restrict the austenite and austenite + ferrite fields to lower carbon contents and higher temperatures than in the Fe-C system. OK groups of steel of different molybdenum content, but with approximately the same carbon variation in each group, Table I, were studied. The alloys were melted in an acid-lined 30-lb high-frequency induction furnace, and the ingots forged to l-in. rounds, which were then ground to 0.75-in. diam. To minimize chemical segregations a short length of each bar was given a high-temperature heat treatment as listed in Table I. Specimens 0.062 to 0.125-in. thick were thereafter cut from the homogenized bars for heat treatment to determine phase changes in the alloy. Heat treatments were performed in either a lead bath or muffle-type electric furnace, depending upon the temperature required. Maximum temperature variation was * 2" F in the lead bath and * 5"F up to 1900°F and +8"F above 1900°F in the electric furnace. Adequate protection of the specimen from the oxidizing atmosphere in the electric furnace was obtained by sealing the specimen in either a pyrex or a silica capsule which was evacuated or not as circumstances required. For austenitizing followed by quenching to an isothermal temperature, the specimen was placed in a closed-end refractory tube the mouth of which, extending beyond the furnace, was connected to a vacuum pump. The specimen could be withdrawn from this tube and quenched as desired. IDENTIFICATION OF PHASES The principal method of identification of phases was metallographic examination conducted on surfaces well removed from exposure to lead or atmosphere effects during heat treatment. Hardness measurements (Dph/lOkg) were also made on these surfaces. The etching reagents used and their effects are listed in Table II. Martensite and ferrite were readily recognized by their customary appearance after etching with saturated picral or 1 pct nital. The presence of liquid at high temperature was indicated by curved interfaces characteristic of boundaries between solid and melt, by intergranular pools of dendritic areas in a carbide matrix, and by a black network coincident with austenite grain boundaries. Examples of these structures are shown in Figs. l(a) and (0). The types of carbide which were attacked by the electrolytic chromic acid etch and the alkaline KMnO, etch, Table 11, were identified by X-ray analyses of extracted carbides of five alloys. Carbide residue was obtained from a metallographic specimen by etching the specimen for 24 hr in hydrochloric-picric acid in alcohol (grain-size reagent), after which the carbides, standing in relief, were scraped from the surface of the specimen and mounted on a glass slide. Diffraction patterns were obtained with a Philips spectrometer using iron-filtered cobalt radiation. Figs. 2, 3, 4, and 5 illustrate typical etching behaviors with chromic acid and alkaline KMnO,. Chromic acid attacked Mo,C as shown in Figs. 2(a) and (b)-but not (Fe, Mo),C, Fig. 3(b). Alkaline KMnO, attacked (Fe, Mo),C, Fig. 3(c), and also attacked M0,C. In accordance with these behaviors, a typical differentiation of coexisting Mo,C and (Fe, Mo),~ is shown in Figs. 4(a) and (b). The carbide (Fe, Mo),,C, could not be obtained free of other coexisting carbides for etching experiments. The behavior. however. of coexisting carbides identified by x-ray diffraction as Mo,C ind (Fe, Mo),,C, indicate that (Fe, Mo)23C6 is not etched by chromic

Jan 1, 1961

By B. J. Reid, J. N. Greenwood

It has been shown1 that cavities are formed in the grain-boundaries of copper and 70:30 brass (as well as in magnesium) by the application of tensile stresses at elevated temperatures. For a given rate of strain, cavities are formed in brass at a lower temperature than in copper, and they are larger; it was thought that this earlier onset of cavitation in the alloy might be caused by the distortion produced in the metal lattice by the alloying element. If the cavitation is caused by the vacancy-migration mechanism, ' the distortion of the lattice would reduce the energy required for vacancy formation, and thus provide vacancies more readily to assist in the cavitation process. It was decided to study a range of alloys to find out whether increasing amounts of an alloying element would cause any progressive increase in, or modification of, the cavitation in copper. Nickel was chosen for this purpose, since it is soluble in copper throughout the whole range of alloys. A further advantage was its low vapor pressure, which enabled the preparation of the alloys in vacuum and the consequent reduction of their hydrogen content. It has been suggested that cavities may be nucleated by the migration of hydrogen atoms to the less regular atomic spacing at the boundary, and their combination to form molecules. The latter being too large to diffuse back into the lattice, form stable cavities into which vacancies could condense. PREPARATION OF ALLOYS All alloys, ranging from pure OFHC copper to 43.7 at. pct of nickel (carbonyl), were prepared in a vacuum furnace employing high-frequency induction heating. When a charge was melted, vigorous gas evolution occurred initially, after which the pressure was reduced to 10-4 mm Hg, using an oil-diffusion pump. After remaining molten for a further 1/2 to 1 hr to aid degassing, the melt was allowed to solidify in the crucible. In this way contamination by gases evolved from the surface of a separate mold was avoided. The list of alloys prepared is shown in Table I. The percentage of hydrogen present in the OFHC copper was reduced from 0.0054 at. pct to 0.0012 at. pct, as measured by a vacuum-fusion method. The alloys were cold-rolled to 0.03-in.-thick strip, and were homogenized in vacuum for 1 hr at 900°C after every 30 pct reduction. At a thickness of 0.05 in., the strip was held at 450°C for 24 hr under high vacuum (10-5 mm Hg) in an attempt to reduce the hydrogen content still further. Tensile specimens were prepared with a gage length of 1 in., and were finally annealed for 2 hr at 800°C to give an average grain diameter of 0.1 mm. TENSILE DEFORMATION The specimens were deformed in a tensile straining machine operated by a synchronous motor at a constant rate, equivalent to 1.7 pct per hr on a 1-in. gage length. The specimen and grips were contained in a vacuum jacket. A pressure of 10-2 mm Hg was maintained, which was sufficient to prevent surface tarnishing of a specimen held at 650°C for 24 hr. Tests were made between 20. and 650°C and the temperature was controlled to within ±3° over the gage length. The load was measured by the deflection of a cantilever spring. a) Mechanical Properties-The ductility curves shown in Fig. 1 fall into two groups. Figs. 1(a) and (b) for copper and the 5 pct nickel alloy, respectively, show a continuous fall in ductility with a steep fall between 200° and 400°C. Figs. l(c) to (f) show the same sudden loss of ductility between 200° and 400°C. With higher temperatures, however, there is a recovery in ductility values to a maxi-

Jan 1, 1959

By F. A. Crossley

The additions: o, Sn, Zr, Cb, Mo, and V were studied for their effects on the a/a + Ti3A1 boundary of Ti-A1 base ternary alloys. These additions were chosen because of their importance to commercial titanium alloy practice—oxygen as the major impurity (in terms of influence on mechanical properties) and the others as major alloying additions. The composition and temperature ranges of investigation varied according to the system as shown in Table I. The principal means of investigation was light-microscopy. The basis of the ternary studies was the recently determined titanium-rich end of the Ti-A1 system.' MATERIALS, METHODS, AND PROCEDURES Ingots were prepared in 15 g size for all alloys except those of the Ti-Al-Mo and Ti-A1-V systems which were prepared in 20 g size. These alloys were prepared from high-purity, electrolytically refined titanium obtained from the Bureau of Mines, Boulder City Metallurgical Laboratory, Boulder City, Col., and Chicago Development Corp., Riverdale, Md., for the 15 g and 20 g ingots, respectively. The alloying additions were obtained from commercial sources, and were at least of 99.9 pct purity, except the V-15 wt pct A1 master alloy for vanadium additions. This alloy was of 98.2 pct purity; the major impurities were 0.37 wt pct Fe and 0.38 wt pct Si. The ingots were prepared by multiple melting in a nonconsum-able-electrode arc furnace. The ingots were covered with Markal coating "CR-T22" (Markal Co., Chicago) to protect them from scaling. Markal coating is applied as a slurry of solids in a volatile carrier liquid. The coated article is air dried. Upon heating to the hot working temperature the coating fuses to form a glassy, protective film. The ingots were heated to 1000°C and rolled to 0.16 in. thickness, reheating after each pass. The glassy film was removed by sand blasting. Ten mils were removed from all surfaces by grinding and/or pickling (3 pct HF, 30 pct HN03, balance water). Grinding was always followed by pickling to remove traces of the grindmg medium. Hydrogen removal was accomplished by vacuum annealing at 1000°C for 2 hr to a final pressure of about 0.02 µ Hg. This was followed by annealing in evacuated Vycor bulbs (800°C, 2 hr, ice brine quenched (IBQ)) in order to maximize ductility. The materials were then lightly pickled and cold rolled to 0.12 in. thickness or cracking, whichever occurred first. After rolling, 1/2 by 1/4 in. specimens were cut for the equilibration anneals given in Table 11 and carried out as previously described.1 Final polishing of the specimens for metallographic examination was done by electrolytic means. Specimens were first examined without etching under bright field and polarized light illumination, for this is the only means of detecting the "two-phase" phenomenon.1,2 The term "two-phase syndrome" refers to Ti-A1 al-loys which appear on the bases of their chemical, phys-ical, and mechanical properties, to be two-phase, but are actually single phase and inhomogeneous in composition. Since processing and heat treatment of the alloys of the first group were completed before the two-phase syndrome was discovered, a number of the specimens were found to exhibit this phenomenon—80 pct of those of the Ti-Al-Zr system, 5 pct of those of the Ti-Al-Sn system, 30 pct of those of the Ti-Al-Zr system. The affected specimens were homogenized by heating above the ß transus temperature and quenching. The heat treatment and working schedules to accomplish this are given in Table 111. After rolling, specimens were pickled (3 pctHF, 30 pct HNO3 in water) to remove 1 to 2 mils from the

Jan 1, 1970

By H. F. Webster, C. G. Dunn

Rolling md annealing procedures are described for developing the (110) preferred orientation in tantalum for use as a thermionic-emission materinl where electrodes of a uniform high work function are needed. The development of a (110) [001] annealing texture is also reported. A preferential growth process due to low (110) gas-metal surface energy is considered in explanation of the observed growth of (110) grains. ThE growth of (110)-oriented grains in thin strips of rolled zone-refined tantalum, previously discussed briefly,' is reported together with more recent information on the formation of a (110)[001.] annealing texture, i.e., one where the [001] direction of each grain lies close to the rolling direction. The development of tantalum sheet with a (110) preferred orientation (position of [001 ] directions unspecified) is of importance as a thermionic-emission material in thermionic-energy converters. Since therm ionic-emission properties of cesium-coated crystals vary over a wide range depending on (hkl) a2-7 a single (hkl) preferred orientation is more useful than either several preferred orientations or none. Furthermore, the (110) preferred orientation yields the highest thermionic-emission density for a cesium coverage of less than a monolayer.5-7 A consideration of the stability of the grain structure needed at high operating temperatures suggests that the preferred orientation itself should be produced by annealing processes. Information on annealing textures in tantalum, however, is rather limited. Pugh and Hibbard 8 obtained (111)[112] and (lll)[112] components in a 1400°C recrystallization texture in 95 pct cold-rolled foil; these components were enhanced on annealing at 2500°C. Muller9 rolled 99.97 Ta to 90 pct reduction in thickness in the final stage and noted only a slight sharpening of the rolling texture, with some intensification of the (111)[112] component upon annealing at 1200°C. The experimental procedure followed in the present work stemmed from the idea of using possible differences in (hkl) surface energies to provide a small driving force for growth of grains having the lowest (hkl) surface energy.l0* This would mean using high-purity tantalum processed into thin sheet form and annealed at high temperatures either in a noncontaminating atmosphere or in one producing additional sample purification. EXPERIMENTAL Zone-Refined Tantalum. National Research Corp. tantalum in the form of 1/8-in.-diam rod and of 99.98 purity (53 ppm 0, 15 ppm N, and 8 ppm C) was zone-melted four times. The traversing speed was 4 mm per min. Such treatment increased the resistance ratio, R293k/R20K , where R293K is the resistance of the specimen at 20°C and R20K the re-resistance at liquid-hydrogen temperature, from a value of 25 for the initial rod to 175 for the zone-refined rod (the increase in the resistance ratio provides a measure of purification11,12). Part of a zone-refined rod was rolled unidirec-tionally to a strip 0.003 in. thick and 0.28 in. wide. Samples were given anneals in the range 1300" to 2100°C using ac conduction heating in an oil-free vacuum system. Recrystallization to small grains appeared to be complete at 1300°C. Large grains were formed at higher temperatures, but these were not entirely strain-free, some grains showing asterism in Laue X-ray patterns and some displaying a range in orientation. Part of the difficulty was caused by thermal expansion of the tantalum strip as it was held between fixed supports. However, in a different arrangement with the tantalum freely suspended in a tantalum can, high-frequency induction heating in vacuo at about l0-6 Torr produced

Jan 1, 1964

By L. H. Robinson

Triaxial compression tests on Indiana limestone indicate that chemical additives in the pore fluids can increase or decrease the strength in plastic failure but not in brittle failure. Tests using a series of the sodium salts of dicarboxylic acids show that odd-number carbon-atom chains decrease the yield strength as much as 3.0 x 10 3 psi, and even-number carbon-atom chains increase the yield strength as much as 9.0 x 102 psi. ,The most effective chemical (sodium citrate) decreased the yield strength of Indiana limestone from 16.0 x 103 to 12.0 x 103 psi. The chemical additives investigated have no influence on microbit drilling rate when drilling with zero differential pressure. However, when drilling at a 2.0 x 103-psi pressure differeniial and using an odd-number carbon chain compound as the circulating fluid, the roller bit drilling rates were slower than with water whereas the drag bit drilling rates were faster. One even-number carbon chain compound added to the circulating fluid produces the opposite effect: the roller bit drilling rate is slightly faster than with water and the drag bit slower than with water. INTRODUCTION A Russian book by Rehbinderl published in 1944 generated much interest in the possibility of aiding and accelerating the destruction of solids by the action of a liquid in which the solids are deformed. This book describes a process in which microcracks are generated during elastic deformation. To describe this process, the rock is divided into three zones: (1) the zone in which the destruction takes place, (2) the predestruc-tion zone (an affected area immediately below the destroyed zone) and (3) the undisturbed specimen. Consider a load applied normally to a surface of an infinite slab of rock. Immediately below the point of application of the load, the rock is destroyed by compression or shear forces. Below this area of destruction, because of a great number of discontinuities ranging from defects to weak points in crystals of discontinuities in crystal latices, very small cracks are created in or between the crystals (often referred to as microcracks). Upon removing the load, the broken rock in the destroyed zone could be removed. In the lower predestruction zone, however, the microcracks in and between the crystals could disappear by the process of rehealing, i.e., the molecular attraction from one side of the crack to the other side being sufficient to completely eliminate the crack. Thus, a large number of these microcracks possibly exist only for a relatively short period of time. The concept of small cracks being generated within the crystals of a rock is not unreasonable. If the rock matrix is deformed below the yield point, some of the defects present within the crystalline structure could start small cracks through the interior of the grains. Upon removal of the load, these microcracks reheal (or the newly generated surfaces come back together) so that all evidence of cracks completely disappears. Under various types of loading, and in various types of fluids, the rehealing of these cracks would be time dependent. If a liquid adhered to the surface of a rock, it could penetrate into the microcracks and thus delay or prevent the rehealing process. This suggests that the prevention of healing of the microcracks may be dependent upon the wetting characteristics of the solid. Thus, rocks which are water-wet should be more easily destroyed in water than in nonpolar hydrocarbon liquid. Adsorption of a liquid could also reduce the free surface energy which could explain the decrease in strengths of materials under nonrepetitive-type loading. Rehbinder's work prompted Boozer, Hiller and Serdengecti 2 to examine the effects of pore fluids on the deformation of rocks subjected to triaxial compression over a range of confining pressures, temperatures and strain rates. Fluids which strongly adsorbed on the rock grain surfaces decreased the strength of sandstone and limestone, which deformed plastically. For certain strain

By D. H. Shaffer, W. F. Harris, W. M. Hickam, M. H. Loeffler

Experiments have been performed on the quantitative addition to niobium of enriched isotopes 018 and 017 at the 0.1 - 40 micro-gram level and their subsequent recovery. A measured quantity of molecular oxygen of known isotopic concentration is added to niobium metal by oxidation. Recovery of the enriched isotopes as carbon monoxide is by the vacuum fusion technique. Quantitative determinations of the enriched isotopes are made in standard volumes at constant temperature using accurately calibrated micromanometers and the mass spectrometer as pressure measuring instruments. THE presence of low concentrations of nonmetallic impurities in metals can often adversely affect the physical properties of the metal. The increase in hardness and the embrittlement of refractory metals due to oxygen is well known. In metallurgical studies dealing with the diffusion rates or the effect of oxygen on the physical properties of refractory metals, it is often necessary to add small quantities of oxygen to the metal and later recover the total quantity present. It is desirable, therefore, to establish the accuracy with which microgram quantities of oxygen can be added to niobium and recovered by vacuum fusion. The successful addition of microgram quantities of oxygen to metals by the usual manometric techniques and the subsequent recovery by vacuum fusion is difficult because of the uncertainty in the accurate determination of the quantity of oxygen originally present in the metal and because of the chance of contamination by atmospheric oxygen. In order to minimize these uncertainties earlier workers have added quantities of O16 at levels much higher than the oxygen concentrations that are of interest.'-3 In order to eliminate the uncertainty associated with the O16 additions to metals at low microgram levels, experiments have been performed on the quantitative addition of oxygen highly enriched in O17 and O18 at the 0.1 to 40 pg level to niobium and the subsequent quantitative recovery of the isotopes by vacuum fusion. Since the natural abundance of O17 is 0.04 pct and of 0" is 0.2 pct this enriched oxygen provides a uniqueness from interference not achieved in earlier work.'-= A measured quantity of molecular oxygen of known isotopic concentration is diffused into the metal. Recovery of the isotopes in the form of carbon monoxide is by vacuum fusion. The total quantity of gas is determined in standard volumes at constant tempera- ture using accurately calibrated Consolidated Electrodynamics micromanometers and the mass spectrometer for pressure measurements. The molecular and isotopic composition is determined mass spectrometrically. APPARATUS A schematic of the oxygen addition apparatus is shown in Fig. 1. Take-offs are provided for the attachment of the isotope container and for sample bulbs which are used to transfer samples to the mass spectrometer. Metal valves are used throughout the system including the sample bulbs in order to achieve a vacuum of 10"6 mm Hg. Evacuation is accomplished with a 3-stage oil-diffusion pump backed by a mechanical pump. A liquid nitrogen trap is used to remove condensables and to prevent oil vapor from entering the system. A micromano-meter is used for pressure measurements. The furnace assembly is shown in Fig. 2. It consists of a quartz tube joined to the apparatus through a 40/W joint with Apiezon W low-pressure wax. The furnace cap, also a 40/W pyrex joint, is provided with a pyrex hook. The sample is suspended from this hook with a platinum wire. The total volume of the furnace section is 435 ml. All volumes were determined by expanding a known volume of gas at a known pressure into the evacuated system and re-measuring the pressure. Both the micromanometer used on the oxygen addition system and the micromanometer used on the mass spectrometer were compared to a precision

Jan 1, 1961

By J. Chipman, N. J. Grant, E. C. Roberts

An equilibrium study was made of the distribution of chromium and oxygen between liquid iron, containing less than 1 pct Cr, and simple slags of the CaO(MgO)-Si02-FeO-Cr& type in the temperature range 1526' to 1734OC. The effects of slag oxidation, temperature, and basicity were observed. IN spite of the fact that chromium is one of the most important alloying elements in steel, and exists in almost all steels as a significant residual element, little research has been done to determine its behavior in basic steelmaking processes. Considerably more work has been done under silica-saturated acid slag conditions. Korber and Oelsen,' Herasymenko,' and others have generally agreed that in acid steelmaking practice the chromium in the slag behaved as if it were present as the chrom-ous ion (CrO). Work by Hilty- ir, high chromium slags also indicated that chromium may exist as CrO. In basic slag systems no equilibrium data exist. Based on individual studies of basic open hearth and electric furnace practice, Bardenheuer," Rock-rohr,% nd HauckQ oncluded that: 1—chromium recovery increased with decreasing basicity, and 2— chromium recovery increased with increasing temperature, although the effect was small. In similar studies Yavioskii and Dzemyen' concluded that: 1— slag FeO is the most important variable, 2—the basicity of the slag has no effect on chromium recovery, and 3—slag viscosity is not high even when 20 pct Cr,O, is present. Lapitskii\ oncluded that chromium recovery improved as the basicity of the slag decreased and increased with increasing manganese in the metal. Regarding the effectiveness of CrZ08 as a base or acid in basic slags, both Kristofferseno and Trojer" reported that Cr,08 was an acidic component requiring neutralization as 2CaO-Cr,O,. Experimental Procedure The experimental apparatus and procedure used for the present research were similar in most details to those used by Winkler and Chipman" and were described in detail by them. A magnesia crucible was used, holding 60 to 80 lb of Armco iron which was decarburized with hydrogen to about 0.010 pct C. Since all the metal samples solidified without gas evolution, this carbon level was assumed not to be significant. Synthetic slags made by mixing pure oxides were used throughout the study. Temperatures were measured by means of calibrated W-Mo thermocouples and were checked by Pt-Pt-Rh thermocouples. The range of temperatures covered in this study was from 1526" to 1734°C. The chromium content of the iron was in the range 0.032 to 0.82 pct, although the bulk of the tests showed 0.04 to 0.2 pct. The slags were of the CaO(MgO)-SiO,-FeO-Cr,O, type in which the Cr,O, content was from about 2 to 20 pct, although most of the slags showed from about 2 to 10 pct. The FeO range was from about 10 to 65 pct. CaO and SiO, were in the range of about 5 to 45 pct each, yielding a rather wide range of basicity values. The first 12 heats were made without a sulphur addition, and with only 30 min allowed for slag-metal equilibrium to be reached. In previous research it had been shown that less than 30 min was adequate to achieve equilibrium in slags free of Cr2O8.11,14.15 A study of the present data indicated that some of the tests may not have reached equilibrium in this time; accordingly four additional heats were made in which at least 1 hr was permitted for equilibrium to be reached. For reaching

Jan 1, 1955