By Nelson Severinghaus

Mineral fillers have been defined as inert materials that are included in a composition for some useful purpose. Because this definition and the scope of this review are not specific- indeed, exceptions abound-accurate total statistics are unavailable. One source estimates the total production in the United States in 1971 at 5 million tons valued at $200 million, averaging $40.00 per ton. Included are a broad group of minerals-asbestos, barite, bentonite, calcium carbonate, clays, diatomite, feldspar, micas, silica, talc. Additional references will be made to synthetic mineral-derived fillers such as aluminum hydrate, precipitated calcium carbonate, and pyrogenic and precipitated silicas and silicates. A section on related uses at the end of this chapter covers absorbents and filters. Mineral fillers can be included in compounds to accomplish a variety of final results. Hardness, brittleness, impact strength, compressive strength, softening point, fire resistance, surface smoothness, electrical conductivity, and a host of other physical characteristics may be modified by the inclusion of fillers. These effects are the result of properties of the fillers, including chemical activity, hardness, particle size, shape and distribution, surface structure, color, density, and refractive index. To facilitate an overview of the mineral filler industry, this chapter will review the general usage of fillers, the inherent characteristics that intensify their utilization, and similarly their manufactured characteristics. Major using industries will then be examined in detail. Specific information on deposits and processing for industrial minerals will be found in the appropriate commodity chapter. The chart in Table 1, updated from the 3rd edition of Industrial Rocks and Minerals, illustrates the major mineral fillers (both natural and manufactured) and their more important end uses.

Jan 1, 1975

By H. S. Martin

The Phosphate Recovery Corporation operates three flotation plants, Nos. 1 and 2 concentrators about three miles northeast of Mulberry, Florida, and No. 3 plant at Wales, Tennessee. These plants represent the first commercial phosphate flotation operation and are also believed to be the largest nonmetallic flotation operation in the world at the present time. The details of this paper will be confined to plant No. 2, this being the newest and largest concentrator in Florida, and the flow sheet being practically the same as at plant No. 1. The No. 3 plant has been operated but a short time and has been shut down since December, 1932, on account of the decrease in phosphate rock production. The phosphate washers usually are located centrally on a known deposit so that about two hundred acres of ground can be mined economically to each washer location. The washers are moved to new areas when the distance becomes too great for economical pumping. The flotation plants are built either adjacent to a washer, so that current debris may be utilized, or on the site of a former washer where there is sufficient accumulated debris available for mining, and the flotation plants must also be moved from time to time. Most of the water used in the Florida flotation plants is recovered after passing through a circulating system where most of the fine suspended matter is settled out, but some make-up water is obtained from deep wells near the plant. Power is obtained from the Tampa Electric Co. through the distribution facilities of the International Agricultural Corporation. Flotation concentrate is hauled from the plant by trolley over the International Agricultural Corporation's trolley system, to the drying plant at Prairie, one mile northwest of Mulberry. Ore Treated In the pebble phosphate district of Florida, the phosphate mineral, or collophane, is usually found in horizontal beds of varying thickness

Jan 1, 1935

By R. D. Pehlke, J. V. Gluck

AS a portion of a general study of liquid-metal thermodynamics, high-temperature galvanic cells were used to study the effect of added dilute solutes on the activity of zinc in dilute solution with molten bismuth in the range 450° to 650°C. 1,2 The cells were of the type The experimental procedures have been described previously.1 In the course of studies conducted in the bismuth-rich corner of the systems Bi-Zn-Au and Bi-Zn-Cu, marked discontinuities were observed in the electromotive force-temperature relations for a number of the experimental compositions. Above the discontinuity temperatures, the relations, which were linear, exhibited slopes similar to the binary alloy of the same mole fraction zinc, as shown in Figs. I and 2. Below the discontinuity temperatures, the slopes were markedly different, but the relations remained linear. In general, as the amount of the third eletnent was increased, the slope of the lower portion of the relations tended to become less positive. The slopes of electromotive force-temperature relations reflect the entropy of mixing of zinc and, therefore, the occurrence of a discontinuity marks the transition between two different equilibrium situations involving the solution of zinc. A number of other investigators3-5 have used such observations to determine liquidus boundaries in binary alloys. Since the upper portions of the ternary electromotive force-temperature relations of this study had the same slopes as the binary alloys, the discontinuities are interpreted as marking the transition between the single-phase liquid region and the underlying two- and three-phase regions. Reference to the Zn-Bi equilibrium diagram6 confirms that the binary alloys were single-phase liquids at the experimental temperatures. Fig. I shows the electromotive force-temperature relations for the alloys containing Bi-Zn-Au and Fig. 2 shows similar relations for the Bi-Zn-Cu alloys. In the lower portion of each figure, the temperature of the discontinuity is plotted vs the mole fraction of the added solute at the various levels of zinc concentra- tion. Cross-plots from these curves at constant temperature permitted the construction of the partial liquidus surface isotherms shown in Figs. 3 and 4.

Jan 1, 1967

By Ivan E. Goodner, Charles H. Fulton

THE subject of the constitution of copper-iron mattes has received considerable attention in recent years by Keller,1 Bolles,2 Hofman,3 and Gibb and Philp.4 Still more recently Friedrich, Röntgen, Wiedmann, Heyn and Bauer, and Leroux have published, in some instances, elaborate researches on the various systems of the sulphides, and the sulphides and their respective metals, which enter into the constitution of mattes, and have added very greatly to the knowledge of the subject. The work of Friedrich has been especially fruitful. But to date no effort has been made to correlate the data obtained in the latter researches and apply then to the study of the product called " matte," which is made in such large quantities by copper and lead-smelters. In this paper we propose to determine, by metallographic and chemical means, the constitution of copper-iron and copper-lead mattes in the light of the recent data above mentioned. We do not discuss copper-nickel mattes or speisses (artificial arsenides). The paper is divided into three sections I. A review and discussion of the various binary systems of the metallic, sulphides, and the binary systems of various metals and their respective sulphides entering into the constitution of mattes; also a discussion of the physical and chemical properties of these sulphides. II. A description of the results obtained from the chemical and metallographic examinations of the samples of copper-iron and copper-lead-iron matte obtained from various plants.

Nov 1, 1908

By R. Salter, C. K. Chase

Although Asarco's Silver Bell Unit, 40 miles west of Tucson, Ariz., is known primarily for copper production, molybdenite is also produced as a byproduct in the 8000 tpd flotation mill. The Silver Bell ore comes from two pits approximately two miles apart. Copper mineralization is essentially chalcocite resulting from two to three-fold secondary enrichment in a highly altered zone. A typical porphyry copper deposit, Silver Bell ore is of medium hardness. The ore consists of about one part molybdenum to 65 parts of copper. In the copper concentrate which is the starting point for separate molybdenum recovery, the ratio is also one part molybdenum to 65 of copper. Molybdenum mineralization is primary. Enrichment is not evident but it is notable that the molybdenite is more common in the more siliceous, harder rocks. The actual molybdenite occurs as diversely oriented flakes of fairly constant grain size, mostly in fractures associated with quartz veins. Most of the mineral appears unoxidized; secondary coatings on the molybdenite flakes are fortunately rare. In May 1962 a modified, improved version of the molybdenite circuit was put into operation.

Jan 7, 1964

By John V. Beall

Early this year at the University of Arizona in Tucson, a survey was made of student opinion about the minerals industry. Over 100 of the three page questionnaires were completed and these were analyzed by the following categories: 40 Mining Engineering students, 20 Geological Engineering with 2 Geophysical Engineering students, 15 Geology students, 7 Metallurgical Engineering, 26 Underclassmen, 29 Graduate students and a composite of 84 total students. Not all of the results of the survey were predictable. After graduation there is a strong preference toward going to work in the mineral industries. The next most popular options, but trailing the first choice greatly, was graduate work or employment in another industry. A smattering of other choices were for teaching, government or research. None checked the box for drop out.

Jan 1, 1971

Two sessions during the recent AMC Mining Convention in Los Angeles, September 23-26, served to update industry personnel on the status of health and safety regulations in the US. As reflected by the American Mining Congress resolution on mine safety and health, "Based on experience with the federal Coal Mine Health and Safety Act of 1969 and the federal Mine Safety and Health Act of 1977, (AMC) does not believe that laws designed to force compliance with regulations through the imposition of criminal or civil penalties will result in safer mines. (AMC) feels that the government's participation will be much more productive if greater emphasis is placed on research, training, and inspections aimed primarily at assisting operators and employees in recognizing and eliminating hazardous conditions and practices.

Jan 11, 1979

By Robert E. Sorenson

EXPLORATION for deep-seated orebodies in the Silver Belt area of the Coeur d'Alene mining district is complicated by meager surface expressions of diagnostic criteria, lack of knowledge of the significance of specific alteration phenomena, and the great expense involved in the exploration for ore shoots, the tops of which often occur near sea level elevation or below and as much as 4000 ft or more below the surface. Except for the early studies of Ransome and Calkins in 1903 and 1904,[1] little geological work was done in the Coeur d'Alene district for many years, and it is only during the last 15 to 20 years that complete and careful geological mapping has been applied to most of the mines in the area. Much early information, which now would prove invaluable, is lost in hundreds of miles of caved and inaccessible mine openings not mapped by mining geologists. In more recent years mining geology has become a tool of greater use in the district, and some measurable progress is being made in the accumulation of observations that are adding gradually to the knowledge of ore deposits in the district.

Jan 7, 1951

By Robert S. Williams

NO new ferrous alloys have been produced in the last five or six years that are as outstanding contributions to civilization as were the high-speed steels of the early part of the century or the stainless steels announced at the close of the World War. There have been, however, many developments of major importance having to do either with modifications of existing alloys or with new methods of treatment of older iron or steel alloys. Only a limited number of these new developments can be discussed and their selection does not necessarily imply that these are the most important but merely that they are of general interest rather than perhaps of greater importance in highly specialized fields.

Jan 1, 1939

By H. O. Hofman

Jan 1, 1896

By Gerald J. Anderson

The Marquette District of Central Northern Michigan is the oldest of the Lake Superior iron districts with a mining history dating from 1852 up to the present. The total production of all types of ore through 1965 was 338,120, 146 long tons. Emphasis up to the 1950's was on mining the direct shipping ores; however, demands for higher-grade and better-structured ores in the last decade has resulted in a complete shift in emphasis to beneficiating the lowgrade Negaunee Iron-formation to produce high-grade iron ore pellets. The Precambrian sediments of the Marquette Range have been correlated with the Animikie Series of the Thunder Bay District, Ontario, and are contained in a westward plunging synclinorium that is approximately 3 3 miles in length and 3 to 6 miles in width. -The rock unit of major economic importance is the Negaunee Iron-formation that reaches a thickness of 2500 feet near the City of Negaunee. The primary iron content of the Negaunee Iron-formation averages 26 per cent, whereas the altered iron-formation approximates 31 per cent. The Negaunee Iron-formation has been divided into three principal types: diagenetic, oxidized, and metamorphic. The ores produced to date fall into four categories: high-grade soft ores, high-grade hard ores, siliceous ores, and concentrates and agglomerates (pellets). The soft ores generally are found in synclines and in fault-trough structures, bounded by mafic dikes along at least one side, and are mainly found in the basal portion of the Negaunee. In contrast, the hard ores occur in the uppermost portion of the Negaunee and are controlled by structural features such as folds, faults, and dikes. Iron-formation that has undergone diagenetic and metamorphic alteration makes up the main beneficiating ore types. Studies on the Negaunee Iron-formation have played an important role in the formulation of many of the theories on the origin of the Precambrian iron-formations.

Jan 1, 1968

By Vernon A. Mrak

The Powder River Basin of northeast Wyoming was the first area in the state to receive attention during the early days of uranium exploration. Although the uranium occurrences are many and widespread, most of the known ore deposits are quite small and difficult to mine. As a result of this, detailed regional exploration in the Powder River Basin has been neglected. The uranium ore deposits occur in that part of the Wasatch Formation that is of earliest Eocene age, and they are scattered over an area of about 400 square miles. All uranium ore deposits are associated with red beds or altered sandstones within the Wasatch Formation. Uranium ore was first shipped from the region in 1953. Total production through June of 1965 is 506,257 tons of uranium ore containing 1,922,527 pounds of U3O8. The average grade of ore is about 0.19 per cent U3O8. The major producing area of the Powder River Basin is the Monument Hill district where about 91 per cent of the basin's total uranium ore has been mined. The source of uranium is presumed to have been the Oligocene, Miocene, and perhaps Pliocene tuffaceous rocks that once overlay the area. Joints, fractures, and permeable beds or zones were the passageways for the migration of uraniferous waters from the overlying beds to the Eocene host rocks.

Jan 1, 1968

By E. N. Harshman

Uranium mining and milling are rather new industries in Wyoming and South Dakota, but, in the past 15 years, ore valued at more than $400,000,000 has been mined and milled in the region. The major uranium deposits are in structural and/ or erosional basins or on the flanks of uplifts. The principal host rocks are medium- to coarse-grained sandstones that were deposited in continental or brackish-water environments and were derived in large part from the granitic cores of the uplifts and the sedimentary rocks that flank the cores. The ages of the host rocks range from Cretaceous to Miocene, but more than 95 per cent of the known reserves in the region are in rocks of early Eocene age. The bulk of the ore in the region is unoxidized and lies below the water table; some oxidized ore has been mined in the Powder River Basin and Black Hills districts. The unoxidized ore comprises pyrite, uraninite and/ or coffinite, marcasite, hematite, jordisite(?), and selenium. Minerals in the oxidized ore include hydrous uranium carbonates, phosphates, and sulfates and hydrous uranium and/ or vanadium silicates. The deposits are in the form of ore rolls that contain from a few hundred to a few hundred thousand tons of ore, ranging in grade from 0.1 per cent to 1.0 per cent U3O8. The rolls are at the margins of large tabular bodies of sandstone that has been altered by the orebearing solutions. The deposits are believed to have resulted from the interaction of an alkaline; oxidizing, ore-bearing ground water and a reducing environment. Exploration guides include the spatial relations of ore to altered sandstone, favorable lithology in the host rock, the content of certain elements and/ or compounds in ground water, and the relation of deposits to major paleodrainages.

Jan 1, 1968

By William Fink

NICKEL is used as an alloying element in several complex commercial aluminum alloys, among which are found some very interesting proper-ties, such as relatively high strength at elevated temperatures, relatively low coefficient of expansion, the absence of permanent growth, ability to take a good polish, and a bright, pleasing as-cast surface. For that reason the aluminum-nickel system was included in the list of binary aluminum systems that are being studied as a preparation for the investigation of more complex commercial alloys. This paper is the fifteenth of a series from the Research Laboratories of the Aluminum Company of America reporting the results of investiga-tions of equilibrium relations in aluminum-base alloys of high purity. The aluminum-nickel equilibrium diagram from 0 to 18 per cent nickel was determined, using the purest material available.

Jan 1, 1934

By E. R. Darby

When bronze is melted in open-flame furnaces a considerable amount of slag is formed during the melting operation. This slag may be incidental to the melting practice or it may be formed intentionally by slag-forming constituents added to the furnace charge to provide a covering for the melted metal When this slag is removed from the furnace, it contains, in addition to the free metal carried with it by the skimming operation, a considerable amount of metal as oxide either combined or mechanically mixed with it. By the usual crushing and washing methods this metallic oxide generally goes to the tailings pile, so diluted by other foundry waste that its recovery is economically impossible. If this furnace slag is not inixed with other foundry waste, practically all of the metal oxide as well as the free metal may be recovered by some form of smelting operation. The first side of the problem to be considered is the amount of slag produced. It may not be true that the majority of foundries have no record of the amount of slag made, but it is certainly true that a very great many either have no record or pay little attention to it. Usually the collection of furnace slag for one normal week's run will be sufficient to determine the advisability of its being handled in a different manner from the crushing and concentrating generally employed. If a large representative sample of the accumulation is crushed and concentrated and the recovery compared with the results of a careful assay, it will be found that a large percentage of the total metal content was lost in the washing process. The percentage of loss will be greater than the metallic oxide content, as some free metal in extremely fine particles always is carried away in grains of slag. From such a comparison, it may be determined whether or not the slag should be melted, sold or treated as before. An example of an actual test of this kind is given below. In a foundry melting 50,000 to 80,000 Ib. of bronze per day, a week's accumulation of furnace slag and ladle skimmings amounted to 16,500 1b.—over three times as much as the foundry superintendent estimated before the accumulation was made. Two tons of this material was taken as representative of the lot. This was ground through a thoroughly cleaned ball-mill and concentrated over a Wilfley table. The

By R. W. Smith

Many industries such as the cement industry handle large quantities of limestone and clay slurries. However, at present very little is known about the flow properties, such as friction loss due to flow of slurries in pipelines. This lack of knowledge has made it often very difficult to calculate the total dynamic head of a proposed slurry handling system, and therefore has often made the selection of correct size slurry handling equipment difficult. Because of lack of knowledge about slurry flow a study of slurry flow theory has been made at the Portland Cement Association's Research and Development Laboratory with the idea of developing a method whereby friction losses due to slurry flow may be predicted for any size pipeline. The flow equations developed have been checked by pilot plant size equipment. DERIVATION OF FLOW EQUATIONS It has been known for some time that limestone and clay slurries handled in cement plants do not flow in the same manner as a Newtonian fluid such as water. When a Newtonian fluid flows the shear stress at any flow velocity is proportional to the rate of shear. This phenomenon can be illustrated by a line (Figure 1). The viscosity of the fluid is the slope of the curve. Thus, the flow properties of the material may be characterized by a single materials constant: viscosity. When a non-Newtonian fluid with the type of characteristics exhibited by limestone and clay slurr-ries flow, a similar curve can be constructed (Figure 2). This graph is a shear diagram of a Bingham plastic non-Newtonian fluid. It should be noted that with the Bingham(1) plastic type of flow viscosity, the slope of the curve, is still an important materials constant. In addition, however, there is another materials constant, namely the yield stress of the material. One way to visualize this constant is to consider it as the amount of energy that must be put into a Bingham plastic material to start it flowing.

Jan 1, 1961

By R. B. G. Yeo

Pronounced isothermal martensite formation at room temperature was measured dilatometrically in a steel containing 0.01 pct C, 24.9 pct Ni, 0.26 pctAl, 2.58 pct Ti and 0.25 pct Cb. It is shown that martensite will form isothermally if stabilization of the austenite-martensite transformation is eliminated by removal of carbon. The decarburization of two iron-nickel alloys allows isothermal transformation to martensite to occur at temperatures above their athermal Ms temperatures. In an Fe-22.4 pct Ni alloy, at the 0.008 pct C level, the Ms temperature during air cooling is 85°F higher than that during- water quenching-. At the 0.15 pct C level this difference is reduced to only 5°F. The introduction of carbon causes stabilization during air cooling which lowers the Ms temperature virtually to the same level as determined during mate?. quenching. Thus in the 0.15 pct C alloy, the Ms temperature is almost independent of cooling rate. It is suggested that rival theories of martensite formation should be reexamined in alloys of sufficiently low carbon and nitrogen content to eliminate the complication of stabilization. The Ms temperature of a steel containing 0.01 pct C, 24.9 pct Ni, 0.26 pct Al, 1.58 pct Ti and 0.15 pct Cb, solution treated at 1500°F and air cooled as 1/8-in. diam specimens, was found to be 57 °F. 1 However, when held for several hours at room temperature the steel hardened slightly and became appreciably ferromagnetic. Isothermal transformation to martensite was first revealed by Kurdjumov and Maksimova2 in an iron-base alloy containing 0.6 pct C, 6.0 pct Mn and 2 pct Cu. Most of the other studies of isothermal martensite have also been confined to highly alloyed steels which transform at subzero temperatures; for instance, DasGupta and Lement, 3 Cech and Hollomon, 4 Machlin and Cohen,5 Shih, Averbach, and Cohen.6 Averbach and cohen7 noted a rapidly decaying volume increase at room temperature in a steel containing 1 pct C, 1.5 pct Cr and 0.2 pct V. cina8 and Marshall, Perry, and Harpster9 have described the isothermal transformation to martensite at room and subzero temperature in stainless steels. Kurdjumov10 has recently reviewed the subject, noting that the isothermal formation of martensite can be observed only in the temperature range somewhat below Ms or below -50°C. The isothermal formation of martensite may be characterized as follows: 1) It occurs in steels of widely different compositions, the main prerequisite being a low transformation temperature. 2) The transformation occurs by the formation of new plates and not by the growth of old ones. 3) The isothermal transformation is suppresed by stabilization during slow cooling or holding at temperatures near room temperature. However, the factors governing this mode of transformation are still not fully understood. The formation of martensite isothermally suggests an activated process. The early theories of martensite formation did, in fact, utilize classical nucleation concepts. Kurdjumov 11 first proposed the presence of thermally activated nuclei of different sizes and compositions which would grow if they reached critical size during cooling. This treatment was enlarged and developed quantitatively by Fisher, Holloman, and Turnbull12,13 and was later reviewed by the latter two authors.14 Fisher15 associates Ms with a nucleation rate of one per cc per sec. At slightly higher temperatures the nucleation rate is so low that isothermal formation of martensite is not observed in reasonable times. At slightly lower temperatures the nucleation rate is so high that it could not be suppressed by rapid cooling. By judicious use of parameters Fisher 16 was able to obtain good agreement between classical nucleation theory and the incubation times of martensite formation.4 However the application of these principles to martensite formation in iron-nickel alloys15 predicts that an alloy containing about 30 pct (31 at. pet) Ni would not transform. The presence of an Ms temperature at -223° C in an alloy containing 34.1 pct (33 at. pct) Ni led Kaufman and cohen17 to reject the hypothesis of homogeneous nucleation in favor of the reaction path theory originally proposed by Cohen, Machlin and Paranjpe.18 This theory conveniently explains the formation of martensite athermally but becomes labored when dealing with isothermal formation. Kaufman and cohen19 did explain the isothermal activation of embryos by assuming it to be a result of the expansion of their boundary dislocation loops but this treatment predicts an upper temperature limit of isothermal martensite formation.

Jan 1, 1962

By Walter Miller

PETROLEUM refining, like other industries in the United States in 1940, focused much attention on its duties and opportunities in the field of national defense. In counter-distinction to the situation during the World War; the industry is well constituted as LO existing equipment, processes, and capacity together with planned additions to handle any demands that may be made upon it by the defense program needs. Evident throughout was the growing sense of ability to manipulate oil molecules for the production of materials not hitherto considered as being available commercially from petroleum The development and application of catalytically-induced reactions on a broad front is one of the distinguishing characteristics of refining progress during the year.

Jan 1, 1941

By Frances H. Clark

IN a concern with the varied interests of the Western Union Telegraph Co., where practically all types of metals, both ferrous and nonferrous, are utilized, many types of failures of materials occur. These have to do not only with outside plant construction, such as corrosion and fatigue of line wire and cable, but also with inside plant equipment operating at such high speeds that rapid deterioration of metal. parts due to fatigue and wear results. Both corrosion and fatigue affect the life of copper wire so its normal life in any particular locality is largely dependent on the atmospheric conditions. Tensions vary widely owing to changes in temperature and ice and wind loadings and the wire is Subject to a great range of vibration caused by wind gusts aril vibration front trains or other heavy vehicles transmitted through the earth. High frequency low-amplitude vibrations are sometimes audible as singing in the wire. The other extreme is the vertical slashing or dancing of the wire observed during severe storms where amplitudes of 9, ft. or more at low frequencies have been observed.

Jan 1, 1942

By A. W. Asman

The problem of balanced design in a belt conveyor has been under constant study. Increased use of this method of transport in recent years has stimulated investigations. Conveyor belt, power transmission and other machinery should be adequate to perform the required service. All components of the belt conveyor should work as an efficient unit moving its load continuously between terminals. As part of a long term research project on belt conveyors, Hewitt-Robins established in 1954 a 2-year grant at Pennsylvania State University. Under terms of the grant, certain fundamental phenomena were to be studied. This work evolved a new concept in belt conveyor power determination based on the principle of belt tension. The Penn State contract furnished the foundation for later more detailed studies. From these most recent investigations, more specific factors were defined. In the final analysis, all of the data collected has been worthwhile in belt conveyor design. Units now operate over long distances at speeds of over 800 fpm. Long high lifts are commonplace. Where vertical or inclined shafts were the rule, belt conveyors receive first consideration. Although belt conveyors have moved forward rapidly, the future will see a tremendous gain in their use. The ideal test belt conveyor would be several thousand feet in length and have a maximum tension of at least 70,000 lb., Also, this conveyor should be horizontai and have a variable feed rate of more than one material. Data from such a field belt conveyor combined with laboratory information would permit accurate analysis. Since this type of conveyor was not available, many field locations were visited: An alternate would have been to erect a closed circuit system in the laboratory. Either method had limitations and the first was selected as having the best possibilities. Manufacturers of conveyor belting and machinery basically have been using the same horsepower formula. As more information became available from field installations, factors in the basic formula were modified. Practically all conveyors are designed today by adding together the horsepowers required to move the empty belt, move the load horizontally, and elevate the load. In selecting size of drive motor, the first two elements are relatively unimportant if the last is large. However, it is the combination of

Jan 1, 1961