Search Documents

By H. C. Fiedler

Heats of high purity iron containing 3.1 pct Si and be -tween 0.0003 and 0.0295 pct N were prepared by vacuum melting ad then pouring while in a nitrogen atmosphere with the pressure between 0 and 90 psi. Strip from a heat with 0.0184 pct N underwent complete secondary recrystallization during the final anneal. Heats with less nitrogen had too few Si3N4 particles to restrain normal grain growth, and the heat with higher nitrogen had too many particles to allow complete secondary recrystallization. In the hot-rolled structure, Si3N4 precipitates only at the grain boundaries, with the consequence that annealing after hot-rolling diminishes the ability to subsequently undergo secondary recrystallization. In contrast to this behavior, ALNprecipitates uniformly in the hot-rolled structure. Under 1 atm of nitrogen, Si3N, in 3.1 pct Si-Fe dissociates between 900" and 950°C; the solubility of nitrogen increases from 0.0010 pct at 900" to 0.0030 pct at 1200°C. The solubility of nitrogen in Si-Fe has been the subject of many investigations. Corney and Turkdogan1 heated a 2.83 pct Si alloy in nitrogen and found the solubility, under 1 atrn of nitrogen, to be 0.0019 pct at 900°C. They claimed that Si3N4 did not form in the alloy above 705°C in 1 atrn of nitrogen. Fryxell et al.2 heated samples of 3.25 pct Si-Fe containing 0.0025 pct N over a range of temperatures and then analyzed for total nitrogen by vacuum fusion and for nitrogen in solution by a modified Kjeldahl technique. At 900°C, they reported the solubility of nitrogen in equilibrium with Si3N4 to be 0.0011 pct. pearce9 found the solubility of nitrogen at 900°C under 0.95 atrn of nitrogen to be 0.0017 pct in a 3.06 pct Si alloy. He reported that Si3N4 does not form above 770°C in 1 atrn of nitrogen. Although internal friction measurements have given somewhat higher values for the solubility,4-6 if the solubility of nitrogen is as low as has been reported by most investigators, and if Si3N4 is stable up to at least 945°C at 1 atrn pressure of nitrogen as reported by Seybolt,7 a small amount of nitrogen in properly processed Si-Fe should be effective in promoting secondary recrystallization. The requirement is that in the final heat treatment there be enough small, well-dispersed particles of Si3N4 to restrain normal grain growth. Fast8 has obtained secondary recrystallization by nitriding high-purity 3 pct Si-Fe after hot-rolling to a thickness of 0.118 in., followed by processing to 0.012 in., and annealing. A large amount of nitrogen, 0.076 pct. was introduced during the nitriding heat treatment, but he has since reported9 that "a few hundredths of a percent" is sufficient. Small amounts of aluminum10 or vanadium" nitride are capable of promoting secondary recrystallization. Heats containing as little as 0.010 pct A1 or 0.042 pct V and from 0.006 to 0.009 pct N underwent complete secondary recrystallization at final gage, whereas heats with lesser amounts of aluminum or vanadium did not.l2 To be reported is the behavior of nitrogen in high-purity 3.1 pct Si-Fe, and the relation of this behavior to the ability to undergo secondary recrystallization. PROCEDURE Ingots weighing 1 lb were made by vacuum melting high-purity electrolytic iron (A104, Glidden Co.) and high-purity silicon (Monsanto Co.). The latter was used in preference to ferrosilicon to insure a low aluminum content. The design of the melting furnace permitted pouring with the furnace atmosphere either below or above atmospheric pressure. Accordingly, at the completion of melting, nitrogen was admitted to the desired pressure and the heat then immediately poured. The ingots were sound, with no indication of porosity. In Table I are listed the heats investigated, the nitrogen pressure at pour, and the nitrogen and oxygen contents as determined by vacuum fusion with a platinum bath at 1850°C, a procedure which insures measurement of the total nitrogen.13 In addition, all heats contained 3.1 pct Si and not more than 0.002 pct C, 0.003 pct S or 0.005 pct Al. It was subsequently found that the quantity of nitrogen contained in the heats in Table I does not necessarily represent that obtained under equilibrium conditions. For example, the ingot poured immediately after 1 atrn of nitrogen was admitted to the chamber contained 0.0093 pct N, whereas an ingot poured 3 min after the nitrogen was admitted contained 0.021 pct N and another poured after a 6-min delay contained 0.029 pct N. While some bleeding of the hot top occurred in the latter instance, the ingot when examined in cross section appeared sound. The ingots were heated to 1325°C in hydrogen and rapidly rolled to 0.080 in. in 3 passes. The roll speed of the final pass was reduced so as to increase the quenching effect of the rolls. The hot-rolled pieces were processed both as-hot-rolled and after heating for 3 min at 900°C in hydrogen. After cold-rolling to 0.026 in., the strips were heated for 2 min at 900°C in hydrogen, then cold-rolled to the final gage of 0.012 in. The loss of nitrogen in going from the ingot to cold-rolled strip was no more than 10 pct. The final heat treatment, which was for the purpose of develop-

Jan 1, 1970

By Sydney H. Ball

AMERICAN consumption of industrial diamonds has increased five fold in the past 25 years and today accounts for 15 to 20 percent of the world's sale of rough diamonds. In another decade the value of industrial diamonds sold may well equal or exceed that of gemstones. It is generally understood that industrial diamonds are one of the strategic minerals being stocked by the Government in the present crisis to ensure rapid and efficient armament production. Diamond die making is a trade largely confined to artisans in Switzerland and in certain parts of France. Today, in addition to turning out pilots, we should train expert artisans in diamond die making, for thousands of miles of tremendously small-gauge wire will be needed to make the instruments by which the efficiency and safety of these pilots is assisted.

Jan 1, 1941

By Willard R. Jillson

Within the last ten years Kentucky has become celebrated for its low-sulfur bituminous coals. Prior to this time, many investigators had discnvered the abundance of this coal but the fact was unknown to the general public until the last extension of Kentucky's mountain railroads' was completed. The coals of. Kentucky are, broadly, separated into two geographic units—the eastern and the western coal fields. On a basis of their sulfur content these coal fields fall into three units, which are indicated on the accompanying map, by numbers, 1, 2, and 3. The area marked 1, the very southeastern part of the state, shows the lowest sulfur, all coals being averaged. In this field the maximum is 1.04 per cent. and the minimum as low as 0.68 per cent.—both averages and not individual analyses, which would of course show much greater variation. Included in this group are the following counties: Lawrence, 0.87 per cent.; Martin, 0.75 per cent.; Johnson, 0.73 per cent.; Magoffin, 0.87 per cent.; Floyd, 0.88 per cent.; Pike, 0.68 per cent.; Knott, 1.04 per cent.; Perry, 0.77 per cent.; Letcher, 0.80 per cent.; Leslie, 0.70 per cent.; Harlan, 0.79 per cent.; Knox, 0.86 per cent.; and Bell, 0.92 per cent. The total average sulfur content for these thirteen counties is 0.82 per cent. Bordering the restricted low-sulfur field of eastern Kentucky is the No. 2 belt (slightly darker), 'which is commonly known as the western border of the eastern coal field. Here the maximum sulfur is 2.91 per cent. and the minimum 1.05 per cent. Again these are averages and not individual analyses. The counties in this group are: Greenup, 2.60 per • cent.; Boyd, 1.67 per cent.; Carter, 1.07 per cent.; Morgan, 1.40 per cent.; Wolfe, 1.83 per cent.; Lee, 2.93 per cent.; Breathitt, 1.85 per cent.; Owsley, 1.09 per cent.; Jackson, 1.06 per cent.; Rockcastle, 2.30 per cent.; Clay, 1.09 per cent.; Laurel, 1.08 per cent.; Pulaski, 2.24 per cent.; Whitley, 1.05 per cent.; McCreary, 1.50 per cent.; and Wayne. The sulfur percentage average for this area including fifteen important counties is 1.65 per cent. In the western Kentucky field, the great increase in the percentage of sulfur is at once apparent. Ohio County with 3.78 per cent. is the highest and Hancock with 2.87 per cent. is the lowest. The percentages by counties is as follows: Hancock, 2.87 per cent.; Henderson, 3.22 per cent.; McLean, 3.27 per cent.; Muhlenberg, 3.31 per cent.; Hopkins,

Jan 1, 1920

By B. W. Levinger

THE system Ti-CI- has been studied by several investigators." ' Though titanium and chromium are completely miscible at high temperatures, an intermediate phase of the approximate atomic proportions TiCr, has been identified at various compositions between 60 and 68 wt pct Cr. The structure of this phase was established as the cubic C15 (MgCu2) type with 24 atoms per unit cell and a lattice parameter 6.929 kX.2 During a study of the ternary system, Ti-Mo-Cr,5 the existence of a high temperature modification of the TiCr, phase was discovered. In a series of alloys annealed at 1300°C and containing from 60 to 70 wt pct Cr and 5 pct Mo, a new phase was present which did not correspond to either ß solid solution or TiCr,. By trial, the new phase was identified to be of the hexagonal C14 (MgZn2) structure with 12 atoms per unit cell. Further work showed that the hexagonal structure was. in fact, also present in binary Ti-Cr alloys quenched from high temperatures. To make the identification more certain, the intensities of the various reflections were calculated assuming a composition TiCr2 and C14 structure. Table I lists reflection planes, interplanar distances, calculated intensities, and a comparison of these values with the lines of a binary Ti-Cr alloy (66 pct Cr) annealed for 20 min at 1385°C and water quenched. Since high angle lines were more diffuse, the correspondence between visually observed and calculated intensities was not as good at these angles. Lattice parameters were computed to be a = 4.922 kX, c = 7.945, c/a :- 1.614. The corresponding interatomic distances are: titanium to titanium distance, 3.00:, kx, chromium to chromium distance, 2.43, kX, titanium to chromium distance, 2.88,, kX. These compare to 3.00, 2.45, and 2.87 kX in the cubic phase, respectively.' The atomic positions in the C14 structure are as follows: Titanium 1/3, 2/3, Z; 1/3, 2/3, 1/2: 2/3, 1/3, i; 2/3, 1/3, (1/2-z); Chromium 0, 0, 0: 0, 0, 1/2; 2x, 2, 1/4; 232, x, %; X, 22, 1/4; X, 2x, 3/4; x. x, 1/4; x, x, 3/4; The values of x and z were calculated for the alloy mentioned and found as follows: z — 0.061, x = 0.165. The values assumed in the intensity calculations were those for an ideal close-packed lattice or z = 1/16, x = 1/6. Work in the Ti-Mo-Cr system indicates that y2 the hexagonal modification of TiCr2, is the stable phase above 1300°C, while y1 with the cubic structure is stable below 1000°C. X-ray examination of a number of alloys annealed at intermediate temperatures showed that the hexagonal and cubic phases can coexist. Alloys quenched from 1000°C and annealed at 1100" and 1200°C showed small amounts of y2 at the higher temperature. A considerable amount of y, seemed present, however, in cast alloys annealed at 1100°C. It further appears that there is a small but definite solubility range for both phases in the ternary system. Acknowledgment The results of this paper represent work carried out in conjunction with a project sponsored by Watertown Arsenal, Contract No. DA-11-022-ORD-272. References 'M. K. McQuillan: Journal Inst. Metals (1951) 79, p. 379. 2 P. Duwez and J. L. Taylor: Trans. ASM (1952) 44, p. 495. W. J. Van Thyne,. H.. D. Kessler, and M. Hansen: Trans. ASM (1952) 44, p. 974. 1 F. B. Cuff, N. J. Grant, and C. F. Floe: Trans. AIME (1952) 194, p. 848; Journal of Metals (August 1952). Unpublished Research, Armour Research Foundation. "H. J. Wallbaum: Ztsch. Krist. 103, p. 391.

Jan 1, 1954

By M. N. Pathasarathi, P. A. Beck, T. J. Koppenaal

EARLIER work1 indicated that in rolled and annealed copper the volume fraction of the cube-texture component may increase on continued isothermal annealing. Merlini found2 that in rolled copper the well-known increase in the amount of cube-oriented material with increasing annealing temperature3 is concurrent with grain growth, which takes place after recrystallization is complete. It was found that both in copper2 and in aluminum4 the texture resulting from primary recrystallization, even if this is followed by some grain growth, may in general comprise, in addition to the cube-texture component, four symmetrical texture components of the general type (123)[412], i.e., components not very far from the ideal orientations of the rolling texture. The volume fraction of the cube-texture component increases on further annealing at the expense of these four components.' The present work was undertaken to study quantitatively the increase in the volume fraction of the cube-texture component in the course of normal grain growth, under varying conditions. Since the grain-gr3wth behavior of A1-Mn alloys has been already investigated in some detaiL5 an A1 + 0.8 pct Mn alloy was chosen for this work, in which the extent of normal grain growth can be effectively controlled by the inhibiting effect of a dispersed second phase. EXPERIMENTAL PROCEDURE High-purity aluminum of the following composition was used: A1 99.997 pct, Cu 0.0004 pct, Fe 0.0005 pct, and Si 0.001 pct. A high-purity A1-Mn master alloy was prepared by dehydrating manganese chloride at 500°C and reacting it with molten high-purity aluminum at 750°C in a graphite crucible.5 The Mn metal reduced from the salt by the molten aluminum goes into solution in the latter. The master alloy? containing 13 pct Mn, was solidified under conditions suitable for minimizing segregation. An ingot of the final alloy, to be used in the experiments, was per pared by melting high-purity aluminum and the necessary amount of master alloy in a graphite crucible, and by pouring the molten alloy into a graphite mold preheated to 700°C through a box containing graphite baffles designed to intercept most of the aluminum oxide films floating in the melt. The melt was then solidified by placing the mold on a water-cooled copper plate and by keeping the top of the mold hot, in order to minimize piping. The 6 1/2 in. long, 11/4-in.diam ingot consisted largely of a single crystal. Chemical analysis showed that there was little segregation from the bottom (0.83 pct Mn) to the top (0.81 pct Mn). Spectrographic analysis of the ingot showed that the impurity content remained essentially the same as that of the aluminum used. The ingot was processed so as to obtain a uniformly small grain size. without banding. The ini-tial steps of rolling in the form of a flat bar and of annealing, down through a thickness of 0.4 in., are shown in Table I. At this point the bar was cut into four sections, each approximately 3 in. long, which were processed separately as shown in Table If. The table also gives the penultimate grain sizes obtained in each section by annealing prior to the final rolling of 90 pct RA. During the final rolling the strips were reversed end to end between passes. Annealing treatments were given in a salt pot furnace, with the temperature controlled to 1°C. All annealing of section "6s" was carried out above the solvus point to avoid the formation of second-phase precipitate. The penultimate annealing was sufficiently short to give a relatively fine grain size in spite of the high temperature. Section "6L" was processed in a similar manner, except that the penultimate annealing was much longer, so as to allow considerable grain growth. Section "4" was given the two final

Jan 1, 1961

By C. N. Reid

Slip-line studies on deformed chromium single cvystals showed the usual bcc behavior. At room temperatuve, cross slip was prevalent—slip was not confined to a given plane, but the slip direction was (111). At -10O0K, slip occuvred on (110) planes, twins on(112) planes, and cleavage on (1001 planes. A single-crystal tensile specimen with an axis close to [011] showed a pronounced yield drop and high strain rate sensitivity which zclere used to derive relevant parame tevs in a dislocation dynamics treatment. Transmission electron microscope studies confirmed the existence of (110) slip planes and showed ecidence of loops punched out by precipitates and of grown-in dislocations promoting tangling. OF recent years experimental studies have been made of the deformation characteristics of single-crystal molybdenum and tungsten, but very little has been published on the behavior of single-crystal chromium. During a study of the mechanical properties of chromium, single-crystal studies were made which have already been partially described.&apos; However, additional information was generated which was not directly relevant to the main theme of Ref. 1, and, therefore, was not reported. In view of the need for complete documentation of deformation modes, the experimental observations made on the deformation of single-crystal chromium are summarized here, together with an electron-microscope study of the associated dislocation structures. It was found that, in terms of the deformation modes, chromium is a conventional bcc metal, showing a very pronounced yield-point phenomenon. Further, it was found that the flow strength of these crystals is very sensitive to the strain rate. Finally, the crystals were observed to contain many unidentified precipitates, which often were associated with prismatic dislocation loops. EXPERIMENTAL METHODS Single crystals were grown from rods of wrought chromium by the method of zone annealing. Rods of "1/4in.-diam were supported vertically in an argon atmosphere while an induction coil was moved up the rod at 1 in. per hr. The power was adjusted to just below that required for melting, and the process produced single crystals in about 30 pct of the rods used. The orientations of the crystals, in general, lay near [011] and are summarized in Fig. 1. Before this treatment, the wrought material contained 35 pprn C, 68 ppm O, and 12 ppm N.* An analyzed single crystal *Usual metallic impurities found in iodide chromium are: Al, 5 ppm; Ca, A ppm; Cu, 2 ppm; Fe, 75 ppm; Yg, 0.5 ppm; Yn, < 3 ppm; Mo, < 3 ppm; Ni, 4 ppm; Si, < 20 ppm; Ti, < 1 ppm; V, 4 ppm; Zr, < 3 ppm. contained 10 pprn C, 79 ppm O, and 50 pprn N. Tension and compression specimens were shaped from the crystals by mechanical grinding, followed by the electrolytic removal of about 0.010 in. from the surface in a perchloric/acetic acid bath. All specimens had a gage length of 0.75 in., and tension specimens had a diameter of 0.100 in., while that of the compression samples was 0.200 in. Mechanical tests were carried out at a rate of 1.3 pct per min, and temperatures below 0°C were attained by means of a nitrogen cryostat similar to that of Wessel.2 EXPERIMENTAL RESULTS Modes of Deformation. In addition to the tensile properties of these crystals, which are described in Ref. 1, deformation markings on the surface were studied. Crystals A and F, Fig. 1, were deformed in tension at 300°K to 10 and 16 pct strain, respectively. The surfaces contained visible slip lines, about 1 C( apart, composed of both straight and wavy segments. They did not define a single plane, and so determination of the slip plane was not possible. However, the slip direction was deduced by comparing the axial orientations of the crystals before and after deformation. Fig. 2 is representative, and shows that the axis ro-

Jan 1, 1968

By C. Gatlin, F. Armstrong, K. E. Gray

This paper presents some preliminary results of two-dimensional cutting tests of dry limestone samples at utmospheric pressure. Cutting tips having rake angles of + 30°, + 15", 0°, - 15" and - 30" were used to make cuts on Leuders limestone samples at six depths of cut ranging from .005 to ,060 in. at cutting speeds of 15, 50, 109 and 150 ft/min. The vertical and horizontal force components on the cutting tips were recorded with an oscilloscope equipped with a polaroid camera. Motion pictures of the cutting process at camera speeds of 5,000 to 8,000 frames/sec were taken at strategic points in the variable ranges. The movies provide considerable insight into the brittle failure mechanism in rocks. It appears that chip-generating cracks usually have an initial orientation which is related to the resultant of the externally applied forces. The latter part of the crack curves upward toward the free surface being cut, this part being governed by some type of cantilever bending or prying. The linear and angular motion of the loosened chips also indicate the tensile nature of brittle failure. Analyses of the forces on the cutting tips indicate that: (I) relatively small increases in vertical loading result in large cut-depth increases for sharp tips (rake angles 2 0"); (2) tool forces increase at an increasing rate as the rake angle decreases, particularly for rake angles < 0"; and (3), for the range of this study, rate of loading had little effect on the maximum forces. Both the movies and visual inspection of the cuttings indicated that the volume of rock removed by chipping was much larger than that by any grinding mechanism, even for tips having negative rake angles. Cutting size increases with increased cut depth and rake angles, and decreases slightly at high cutting speeds, the depth of cut having by far the most influence. The amount of contact between the rock and the cutting tip was always less than the depth of cut and rarely exceeded 0.010 in. even for cuts of 0.060 in. INTRODUCTION The planing (or slicing) of various materials with a fixed blade has long been practiced by workers in many industries. For example, the farmer&apos;s plow, the carpenter&apos;s plane and the housewife&apos;s paring knife all employ this basic action. The casual observer might suspect that something so common must be quite simple; however, as in all problems involving the failure of materials, such is not the case. Industries concerned with the machining of metals have long studied these problems, and their literature on the subject is voluminous. Despite these efforts, basic knowledge is not very advanced, as may be noted from recent and comprehensive analyses of their literature.12 Metals are more subject to analysis by classical theories of elasticity and/or plasticity than are rocks, since their elastic constants and strengths are reasonably well established in many cases. In spite of this relative "simplicity", Hill9 refaces his discussion with an admission that the mathematical solution to the machining problem is not known. Photoelastic studies of both machining and milling have been performed and are discussed thoroughly by Coker and Filon.4 Rotary drilling of rocks with fixed blade or drag bits has long been practiced by the mining and petroleum industries, and considerable study has been given to defining their cutting action in terms of the pertinent variables. Essentially all the published mechanistic research on drag-bit drilling has been performed by mining engineers and has been concerned only with rocks in the brittle state. Fairhurst5-7 has worked extensively in this area and employed photographic techniques quite similar to those reported here, except at much lower speeds. His studies showed the periodic or cyclical nature of the brittle failure mechanism, in which instantaneous loads on the bit varied from some maximum value to near zero. Goodrichs has presented further data on the subject as well as a qualitative description of the process. Again the postulated mechanism is cyclical, with alternate chipping and grinding periods. The ploughing of coal is a practiced method and has been studied in some detail by English mining engineers."" Their findings have considerable general application to drag-bit drilling. Evans," in particular, has extended Merchant&apos;s metal-cutting theory" to brittle materials with some success, although certain aspects of his theory are open to question. Fish13 has recently summarized nearly all the published works concern-

By P. S. Roller

P. S. ROLLER,*College Park, Md.-The author introduces the idea of a grind limit, or lower size limit of the particles formed directly by grinding, and this is stipulated to be 0.70 micron. I wonder where all the particles come from that lie between the resolving power of the microscope and 0.7 micron, which are seen under a microscope in examining a sample of grind? There is also introduced the idea of excess fines; this is all right in itself but the author&apos;s quantitative definition seems to be virtually impossible to justify, and, moreover, is obscure. Just why E, the excess fines, should he defined as the distance between an F line and a y line is hard to follow, and just where the distance should be measured does not appear to be stated, as it should be since the F and y lines intersect and the distance between will depend upon where that distance is measured. The basis of the presentation is the relation of log weight against log size that was "discovered" by Schuhmann. While this relation is implied to fit, the only evidence that I can see is a slightly irregular line in Fig. x between 2 per cent and 18 per cent by weight and then a precipitous drop at 18 per cent away from any sort of straight line. Some of the conclusions are rather startling. It is stated that E, the excess fines, remains constant for all the comminution products of any particular material, except that it may decrease for some coarse crusher products. No reason is given for this assertion. One would, on the contrary, expect that excess fines, if such a concept is permissible, would generally vary with different conditions instead of being constant. Again, "as much net energy is required to reduce a ton of quartz to particles of the grind-limit diameter (namely, of course, 0.7 micron) by grinding as is required to melt the quartz." This would require many data to prove, but no proof is given; any consideration would reveal the impossibility of such a result. Still further, ore samples "ground to widely different sizes, and with different circulating loads and different size distributions or product, show the same production of new surface area per revolution of the mill, when this grind limit is used." This statement is confuted by ordinary experience, which teaches that grinding efficiency varies generally with the condition of material. For example, the cushioning effect of fines is widely accepted, while the inefficiency of a ball mill when the feed is too coarse is also well known. R. SCHUHMANN, JR.," Cambridge, Mass. Contrary to Mr. Bond&apos;s stand, there is a great deal of miscellaneous experimental evidence that comminution does not stop at around 0.7 micron, nor does it cease consuming energy at that point. Comminution is in fact recognized as an important method of producing colloids., Mechanical comminution methods were used by von Weimarn6 to produce colloidal dispersions of a variety of solids, including the minerals chalcocite, galena, hematite, stibnite. Utzino7 gives average particle sizes ranging from 0.02 to 0.09 micron for colloids produced by mechanical comminution of several crystalline solids. Andreasen and Berg&apos; have ground

Jan 1, 1941

By P. S. Roller

P. S. ROLLER,* College Park, Md.-The author introduces the idea of a grind limit, or lower size limit of the particles formed directly by grinding, and this is stipulated to be 0.70 micron. I wonder where all the particles come from that lie between the resolving power of the microscope and 0.7 micron, which are seen under a microscope in examining a sample of grind? There is also introduced the idea of excess fines; this is all right in itself but the author&apos;s quantitative definition seems to be virtually impossible to justify, and, moreover, is obscure. Just why E, the excess fines, should be defined as the distance between an F line and a [?] line is hard to follow, and just where the distance should be measured does not appear to be stated, as it should be since the F and [?] lines intersect and the distance between will depend upon where that distance is measured. The basis of the presentation is the relation of log weight against log size that was "discovered" by Schuhmann. While this relation is implied to fit, the only evidence that I can see is a slightly irregular line in Fig. I between 2 per cent and 18 per cent by weight and then a precipitous drop at 18 per cent away from any sort of straight line. Some of the conclusions are rather startling. It is stated that E, the excess fines, remains constant for all the comminution products of any particular material, except that it may decrease for some coarse crusher products. No reason is given for this assertion. One would, on the contrary, expect that excess fines, if such a concept is permissible, would generally vary with different conditions instead of being constant. Again, "as much net energy is required to reduce a ton of quartz to particles of the grind-limit diameter (namely, of course, 0.7 micron) by grinding as is required to melt the quartz," This would require many data to prove, but no proof is given; any considera¬tion would reveal the impossibility of such a result. Still further, ore samples "ground to widely different sizes, and with different circulating loads and different size distributions or product, show the same production of new surface area per revolution of the mill, when this grind limit is used." This statement is confuted by ordinary experience, which teaches that grinding efficiency varies generally with the condition of material. For example, the cushioning effect of fines is widely accepted, while the inefficiency of a ball mill when the feed is too coarse is also well known. R. SCHUHMANN, JR.,* Cambridge, Mass.¬Contrary to Mr. Bond&apos;s stand, there is a great deal of miscellaneous experimental evidence that comminution does not stop at around 0.7 micron, nor does it cease consuming energy at that point. Comminution is in fact recognized as an important method of producing colloids.5 Mechanical comminution methods were used by von Weimarn6 to produce colloidal dispersions of a variety of solids, including the minerals chalcocite, galena, hematite, stibnite. Utzino7 gives average particle sizes ranging from 0.02 to 0.09 micron for colloids produced by mechanical comminution of several crystalline solids. Andreasen and Berg8 have ground

Jan 1, 1941

By P. S. Roller

P. S. ROLLER,* College Park, Md.-The author introduces the idea of a grind limit, or lower size limit of the particles formed directly by grinding, and this is stipulated to be 0.70 micron. I wonder where all the particles come from that lie between the resolving power of the microscope and 0.7 micron, which are seen under a microscope in examining a sample of grind? There is also introduced the idea of excess fines; this is all right in itself but the author&apos;s quantitative definition seems to be virtually impossible to justify, and, moreover, is obscure. Just why E, the excess fines, should be defined as the distance between an F line and a y line is hard to follow, and just where the distance should be measured does not appear to be stated, as it should be since the F and y lines intersect and the distance between will depend upon where that distance is measured. The basis of the presentation is the relation of log weight against log size that was "discovered" by Schuhmann. While this relation is implied to fit, the only evidence that I can see is a slightly irregular line in Fig. I between 2 per cent and 18 per cent by weight and then a precipitous drop at 18 per cent away from any sort of straight line. Some of the conclusions are rather startling, It is stated that E, the excess fines, remains constant for all the comminution products of any particular material, except that it may decrease for some coarse crusher products. No reason is given for this assertion. One would, on the contrary, expect that excess fines, if such a concept is permissible, would generally vary with different conditions instead of being constant. Again, "as much net energy is required to reduce a ton of quartz to particles of the grind-limit diameter (namely, of course, 0.7 micron) by grinding as is required to melt the quartz." This would require many data to prove, but no proof is given; any consideration would reveal the impossibility of such a result. Still further, ore samples "ground to widely different sizes, and with different circulating loads and different size distributions or product, show the same production of new surface area per revolution of the mill, when this grind limit is used." This statement is confuted by ordinary experience, which teaches that grinding efficiency varies generally with the condition of material. For example, the cushioning effect of fines is widely accepted, while the inefficiency of a ball mill when the feed is too coarse is also well known. R. SCHUHMANN, JR.,* Cambridge, Mass.-Contrary to Mr. Bond&apos;s stand, there is a great deal of miscellaneous experimental evidence that comminution does not stop at around 0.7 micron, nor does it cease consuming energy at that point. Comminution is in fact recognized as an important method of producing colloids.5 Mechanical comminution methods were used by von Weimarn6 to produce colloidal dispersions of a variety of solids, including the minerals chalcocite, galena, hematite, stibnite. Utzino7 gives average particle sizes ranging from 0.02 to 0.09 micron for colloids produced by mechanical comminution of several crystal-line solids. Andreasen and Berg8 have ground

Jan 1, 1941

By M. C. Smith, W. V. Green, D. M. Olsen

The creep-rupture behavior of commercial powder-metallurgy molybdenum rod is reported in the temperature range 1600" to 250O°C, at stresses up to 9000 psi and times up to 1 month. The effects of temperature, stress, and grain growth are discussed. Rupture time is fitted to the Larson-Miller parameter and compared to lower-temperature and higher-stress results reported by pugh.1 BECAUSE of its high melting point, molybdenum should retain useful strength to relatively high temperatures. Combined with its ready availability in the United States, this makes it attractive for many applications in missiles, rockets, and so forth—wherever its susceptibility to oxidation can be tolerated or overcome. The mechanical properties of molybdenum rod in the temperature range —200" to 1540°C have been reported by pugh,&apos; Bechtold,&apos; Parke,3 and Carriker and Guard.4 Madden and chen5 have measured the tensile properties of molybdenum single crystals in vacuum up to about 2500°C. As one further step in evaluating its mechanical usefulness, the constant-load creep-rupture properties of commercial powder-metallurgy molybdenum rod have been investigated in the range 1600" to 2500°C. MATERIAL TESTED Creep specimens were machined from 1/2-in. round commercial molybdenum rod, manufactured from powder by pressing, sintering, and swaging. Spectrochemical analysis of the rod showed "traces" (less than 0.01 pct) of silicon, aluminum, chromium, iron, and zirconium, and "faint traces" (less than 0.001 pct) of manganese, magnesium, cobalt, and nickel. Carbon content was 130 to 200 ppm, nitrogen was 110 to 180 ppm, and oxygen 30 to 35 ppm. A typical microstructure of the as-received rod is shown in Fig. 1. Room temperature tensile properties for five specimens strained at about 0.015 in. per in. per min are shown in Table I. CREEP SPECIMENS USED The specimens used for creep-rupture testing are illustrated in Fig. 2. The 1/4-in.-diam gage section was 3/4 in. long, and terminated at shoulders 5 mils high. These shoulders served as fiducial marks for optical strain measurements. Surface finish on the gage section was 16pin. r.m.s. One specimen, for a "long-time" test described below, was modified by dividing the 3/4-in. gage length into three 1/4-in. long sections with individual diameters of 0.250, 0.230, and 0.210 in., each terminating in a pair of fiducial shoulders. TESTING PROCEDURE The constant-load creep-testing machine used has been described by Smith, Olson, and Brown.6 In it the specimen is held vertically on the axis of a cylindrical tantalum or tungsten heater tube by threaded molybdenum or tungsten grips. Both specimen and grips are heated by radiation from the heater-tube, which is heated by its own electrical resistance. The bottom specimen grip is held at its lower end by a clevis pin. The testing load is applied to the specimen through the upper grip by means of hanging weights, a constant force-multiplication lever system, and a pull rod sealed to the chamber lid by a bellows. The incandescent specimen is viewed by an external optical system through slots in the heater-tube and radiation shielding, and an enlarged image of it is projected on a ground-glass screen. Gage-length measurements are made on this image with a pair of cathetometers. Thorium oxide coatings were applied to the threaded ends of most specimens, to prevent diffusion-welding of specimens to grips during testing. Without such a coating welding usually occurred, and grips were often broken by subsequent efforts to remove the tested specimens.

Jan 1, 1960

By W. D. Forgeng, R. E. Grace

The rate of copper corrosion in liquid lead was studied as a function of flow rate and temperature in a closed isothermal loop system between 350" and 500°C. Kinetic data were interpreted with the Nernst-Brunner equation and the Chilton-Colbum mass transfer analogy to heat transfer. Over the range of temperatures and flow rates employed the solution rate constant varied from 2 x 10-3 to 20 x 10-3 cm per sec. The rate constant was found to vary with the 0.76 power of the Reynolds number in the range 7500 < Re < 40,000. The results of this investigation indicate that the Cu-Pb corrosion process is controlled largely by diffusion across a boundary layer. particularly at the higher temperatures. The effective boundary layer for diffusion is found to be approximately three to four times smaller than the momentum boundary layer. CORROSION by liquid metals has long been a problem during melting, static containment, and casting. Recently, considerable emphasis has been placed on the understanding of liquid metal corrosion mechanisms in an effort to prevent mass transfer and eventual failure in liquid metal heat exchangers and in liquid-metal-fueled nuclear reactors. The present investigation was conducted to determine the relationships which exist between corrosion kinetics and hydrodynamic conditions in an isothermal loop containing a simple liquid metal-solid metal corrosion system. The Cu-Pb system was chosen for its simplicity and ease in handling. Previous isothermal Cu-Pb corrosion studies1-3 have been conducted in both static and dynamic systems but not under conditions which allow easy "scale-up" to engineering systems, such as liquid metal heat exchangers. On the other hand, most liquid metal loops which have been used to evaluate mass transfer rates4 have been driven with temperature gradients under conditions of natural convection and unknown flow rates. The primary contributions of this research are twofold: 1) to evaluate the design of a simple isothermal loop corrosion system and 2) to investigate liquid metal corrosion behavior under well-defined hydrodynamic conditions. MATERIALS AND EXPERIMENTAL WORK The apparatus used to measure the Cu-Pb corrosion rates is shown schematically in Fig. 1. The loop system consisted of 1) a reservoir made of Type 316 stainless steel containing a centrifugal pump and 2) stainless-steel tubing containing a removable copper test section. The copper test section was OFHC hard-drawn tubing, 11.0 0.05 cm in length and 0.775 ±0.005 cm ID. A Type 316 stainless-steel venturi meter* was inserted in place of the copper test sec- tion in order to determine the lead velocity as a function of pump speed at each temperature. The Cu-Pb system was chosen for this study because the solubility of copper in liquid lead is large enough to measure accurately but small enough that the diameter of the copper tubing was not changed significantly by corrosion. There are no intermediate phases formed in the system, and the solid solubility of lead in copper is vanishingly small so that back-diffusion cannot occur. Molten lead (corroding grade; 99.94+ pct Pb, 0.0015 max pct Cu) was charged from an auxiliary melting furnace into the system under an argon cover to minimize oxidation. The lead was then maintained at constant temperature by a stirred molten salt bath in which the loop was immersed to a depth just above the lead level in the reservoir, Fig. 1. The total volume of lead in the system was 320 2 cu cm.

Jan 1, 1969

By F. F. Schmidt, H. R. Ogden, E. S. Bartlett

Continuing tantalum alloy development studies have been concerned with a more detailed investigation of promising binary, ternary, and more complex tantalum alloys containing Groups IV-A, V-A, VI -A. VII-A, and VII-A metal additions. A primary objective of these studies was to improve the elevated temperature strength of tantalum with minimum degradation of fabricability and low-temperature ductility by alloying. Several alloys were found to exhibit hot tensile strengths in the excess of 25, 15, and 10 ksi at 2700°, 3000°, and 3500°F, respectively, combined with excellent cryogenic toughness and ductility. Particularly outstanding in this respect are alloys in the system Ta-Mo-W. Ternary parameter curves describing hot-strength, low-temperature ductility, recrystallization temperature, weld ductility, and fabricability are presented for the Ta-Cb-V, Ta-Hf-W, Ta-Mo-Hf, Ta-Mo-V, Ta-Mo-W, and Ta-V-W systems. At present, only four metals qualify for large scale structural applications at temperatures above about 1800°F. These are tungsten, tantalum, molybdenum, and columbium. Research and development work on these refractory metals has progressed to the point where efforts are now primarily directed toward the improvement of high- and low-temperature mechanical properties through alloying. High melting point combined with excellent low-temperature ductility, fabricability, toughness, weldability, and high solubility and tolerance for both substitutional and interstitial solutes are important attributes of tantalum. Conversely, its high density and relative scarcity compared with other refractory metals are the major deterrents to the use of tantalum. Early studies in the Battelle alloy development program established base line data on the mechanical and metallurgical properties of high-purity tantalum.&apos; These studies were extended to include a preliminary investigation of the effects of various alloying elements on the established base properties.2,3 Recent studies involved a more detailed investigation of promising binary alloys containing Cb, Hf, Mo, Os, Re, Ru, and W, and ternary Ta-Cb-V, Ta-Hf-W, Ta-Mo-Hf, Ta-Mo-V, Ta-Mo-W, and Ta-V-W alloys. Results of major importance obtained are given in this article. EXPERIMENTAL PROCEDURES Electron-beam-melted tantalum (Wah Chang) and high-purity alloying elements were consolidated as 150-g ingots by multiple nonconsumable arc melting under a partial atmosphere of helium. Homogeneity of the button ingots was checked radiographically. Alloy buttons measured about 1-1/2 to 1-3/4 in. in diam by about 0.35 and 0.50 in. thick. Nominal alloy compositions were checked on each alloy button by weighing after arc melting. In most instances, weight losses were within 3 pct of the total weight charged. Subsequent chemical analyses on a number of selected alloys showed interstitial contents to range as shown below: Range of Interstitial Content, ppm 0 C N H 25-75 50-100 10-50 1-5 Metallic alloying additions were found to agree well with nominal compositions based on weight change data. Fabrication directly from the cast button to sheet was conducted at low (75° to 900°F), intermediate (1800° to 2000°F), or high (3000°F) temperatures, depending upon alloy content and hardness. Evacuated stainless steel or molybdenum packs were used for fabrication at intermediate and high temperatures, respectively. The temperature required to complete recrystal-lization in one hour was determined by hardness measurements and metallographic observations (longitudinal test sections) after vacuum annealing at 180°F intervals in the range 2010° to 2910°F. All mechanical property evaluations were conducted on recrystallized sheet, nominally 0.04 in. thick. Weldability of the various alloys was screened using manual TIG welding techniques. Bend ductility (bend axis perpendicular to weld axis) was the criterion used for evaluation. Tensile specimens employed 0.200 by 1 in. gage lengths, and bend test specimens measured about 1 by 1/4 in. Low-temperature tensile tests were conducted using a crosshead speed of 0.02 in. per min up to the point of yielding, and 0.05 in. per min to fracture. High-temperature tensile tests were conducted in vacuum using a crosshead speed of 0.01 in. per min

Jan 1, 1963

By L. Stone, H. Margolin

The Ti-C-N and Ti-C-O systems were investigated in the temperature range from 500° to 1400°C and in the composition range up to 2 pct C and 5 pct N or 0. Characteristic isothermal sections at 800°, 900°, 1000°, and 1300°C are presented. The Ti-N-0 system was studied in the temperature range from 900&apos; to 1400°C with alloys containing up to 6 pct total alloying content. Characteristic isothermal sections at 1000° and 140O°C are presented. Melting-point data for all three systems are also included. THIS paper reports on one of a series of investi-gations which have been conducted on the phase diagrams resulting from interstitial alloying with iodide titanium. The other investigations involved delineation of the binary systems with carbon,&apos; nitrogen and boron,h and oxygen. The Ti-0 binary system has also been investigated by Bumps et al.&apos; In varying degrees, each of these interstitial elements has been shown to stabilize the low temperature a modification of titanium1-5 and each forms a face-centered cubic TiX compound (henceforth designated 6). In addition, the Ti-N and Ti-0 systems reveal a low temperature tetragonal phase (6) formed by a peritectoid reaction between a and TiX Experimental Procedure The development of experimental techniques for the study of titanium alloy systems has, to a large extent, become standardized. In this investigation, the equipment and procedures described in detail by Cadoff and Nielsenl have been used. Arc Melting: In general, binary alloys with carbon, nitrogen, and oxygen, prepared in the composition range of interest in this investigation, show negligible composition changes during arc melting. However, the possibility of the formation of some gaseous combination of alloying elements such as CO, CN, or NO during the preparation of these ternary alloys was considered. Calculations showed that the evolution of only 0.05 gram of such a gas would be detectable as a pressure change in the closed system used during preparation of these alloys. Such pressure changes were not observed. Consequently, nominal compositions have been used in plotting the data. The compositions of the materials used in the preparation of the alloys are shown in Table I. After melting for 3 to 5 min at 275 to 350 amp, the alloys were checked for homogeneity by microstruc-tural examination. Alloys containing up to 1 pct C were homogeneous in the presence of less than 3 pct N or 0. At higher alloying contents, some inhomo-geneities in the carbon distribution became evident. Alteration of the melting procedure toward longer times and higher currents did not improve the homogeneity of these alloys. Ti-N-0 alloys were homogeneous in the range to about 3 or 4 pct total alloying addition. Beyond this, almost all of the specimens showed as-cast microstructures consisting only of the phase. Consequently, inhomogene-ities could not be detected by examination of micro-structures. Ten alloys from each of the systems were analyzed for two of the elements present (oxygen being omitted in all cases and titanium being omitted in the Ti-C-N alloys). In all cases the analyses were found not to be sufficiently precise to serve as criteria for the total composition of these alloys. On the basis of phase distribution in heat-treated alloys, however, it appears that carbon is distributed throughout the alloys most uniformly, with oxygen and nitrogen following in that order. Heat Treatment: Specimens for heat treatment were wrapped in titanium sheet before sealing in the argon-filled quartz capsules. Heat-treatment times varied from 100 hr at 800°C to 0.5 hr at 1400 °C. After heat treatment the specimens were quenched by breaking the capsule in water. With the exception of alloys in the low composition region, heat treatment did not have an appreciable effect on the as-cast microstructures. Metallography: Following heat treatment, the specimens were prepared for metallographic examination by grinding on emery paper and electrolytic polishing. For the majority of the specimens a 10-sec etch with Remington "A" agent (25 pct HNO3, 25 pct Hf, and 50 pct glycerin) adequately

Jan 1, 1954

By W. F. Domis, F. von Gemmingen, R. W. Whitmore, F. Garofalo

Constant-load creep-rupture tests at 1100°, 1300° and 1500°F were made on a Type-316, 18 Cr-8 Ni-ZMo, austenitic stainless steel to determine the relationship between ruptzire life and other aspects of creep behavior, The test program was designed on a statistical basis to check the variability of various creep properties and to determine emprically the dependence of minimutn creep rate and ruptzire life on initial stress, The dependence of the rupture life, tn, on the initial stress, a,, is found to be related to the stress dependence of the wrinimum creep rate, i,, and secondary creep strain, The instabilities or breaks found in the conventionual log - logt, plots can be traced to either a change in the linear dependence of log i, on log a, or to a change in secondary creep strain. In the alloy tested, rupture is found to be predowmanantly of the inter crystalline type, For this material, the secondary creep strain is -found to depend on the nature of the grain boundary precipitate, which affects grain boundary migration. It has been shown for a variety of metals and al tested at elevated temperatures under creep conditions that the empirical relationship exists between rupture life, tr, and minimum creep rate, i,. This relationship, in which C and a are in some cases independent of stress or temperature, shows in a general way that creep rupture depends on creep behavior prior to tertiary creep stage. To determine more fully the factors which control creep rupture requires, therefore, more knowledge of the relationship between rupture and creep behavior. To obtain such information, constant-load creep-rupture tests have been made on a Type-316, 18 Cr-8 Ni-2 Mo, austenitic stainless steel at 11000, 1300°, and 1500°F. These tests were designed on a statistical basis to determine the variability of the various creep properties measured and to determine empirically the stress dependence of minimum creep rate and rupture life. As a result of this work, various empirical relations have been established defining more closely the factor, C, in the relation between rupture life and minimum creep rate. This factor is found to be proportional to the amount of strain during secondary creep. The variation of secondary creep strain with rupture life and temperature is determined and its effect on rupture behavior discussed. The variability in minimum creep rate and rupture life is also dis- cussed and the dependence of these quantities on initial stress is interpreted. TEST MATERIAL AND TEST PROCEDURES The material tested is an austenitic stainless steel, AISI Type 316, of the following composition: C, 0.07 pct; Mn, 1.94 pct; P, 0.01 pct; S, 0.021 pct; Si, 0.38 pct; Cr, 18 pct; Ni, 11.4 pct; Mo, 2.15 pct; All 0.003 pct and N, 0.043 pct. The material was received as a hot-rolled 0.5-in. diam bar which was sectioned into 3.25 in. long blanks. Each blank was heat treated by holding 1/2 hr at 2000° F followed by water quenching. A 3/8-in. coupon was removed from each heat-treated blank and the microstructure was examined, the grain size determined, and the hardness measured. The microstructure was found to be uniform from blank to blank and the grain size was found to range from 4 to 6 ASTM numbers. Hardness, measured using a 20-kg load, varied between 127 and 148 Vpn. Tensile creep-rupture specimens having a 0.25 in. diam within a 1.5-in. reduced section were machined from the heat-treated blanks. Constant-load tests were made on these specimens at 1100°, 1300°, and 1500 F. Six specimens were tested at each stress level. Three creep-rupture machines were employed for tests at each temperature, two specimens being tested in each machine for each stress level. To minimize any effect due to local inhomogeneities along the length of the as-received bar the specimens were randomized before test. Each specimen was tested to rupture and in most cases an autographic extension-time curve was obtained. For very low stress levels at 1500°F no auto-

Jan 1, 1962

By AIME AIME

ALTHOUGH the present economic depression is felt in the petroleum industry, probably as much as in any other branch of American industry, the Petroleum Section of the Institute was well represented at the general sessions on Monday and at all of the seven division sessions on Tuesday, Wednesday and Thursday. The seven sessions of the Division were so arranged as not to conflict and thus permitted members to hear the programs of all sessions.* The first meeting of the Petroleum Division was held on Tuesday afternoon; a joint session on engineering research and production engineering. The following papers were presented:

Jan 1, 1931

By K. M. Rolls, F. W. Reuter, J. Wulff

The superconducting behavior and microstructural characteristics of a nominal Nb-40 wt pct Ti-0.239 wt pct O alloy were studied as a function of ther mo -mechanical processing treatment. Critical current density us applied transverse magnetic field was obtained for 0.010-in.-diam wires at 4.2°Kin steady fields 14 to 110 kG. Both optical metallogvaphy and transmission electron microscopy were used to delineate the micros tructures of the same wires. It wan found that a 1-hr 500°C precipitation heat treatment after cold drawing to final size led to the highest critical current density. Heat treatment at 600°C also led to a high critical current density, but the precipitate differs in kind and form from that at 500°C. The resistire critical field was also found to be sensitive to precipitation heat treatment since the effective composition of the superconducting phase changes. This is discussed in terms of the oxygen in interstitial solid solution. Two types of high-field superconducting wire are at present used in the construction of high-field superconducting solenoids. These types are solid-solution alloy wire such as Nb-Zr and Nb-Ti and composites of the brittle inter metallic compound Nb3Sn. The latter generally have a high super cur rent-carry ing capacity which is difficult to vary if properly made. The supercur rent- carry ing capacity of the former can be varied drastically and often predictably by suitable thermomechanical processing treatments. In general, the critical current density Jc of the solid-solution type of alloy is increased by cold work and by additions of interstitial elements along with aging heat treatments. The imperfections which result are be-iieved to be responsible for the observed increase in Jc. In 1962 Kneip and coworkers1 found that the critical faurrent density of Nb-Zr alloys could be increased by proper heat treatment preceded and followed by cold work. Betterton and coworkers2 using a Nb-25 at. pct Zr alloy found that small additions of oxygen or carbon enhanced the effect of this heat treatment. They suggested that the interstitials present aided precipitation in the alloy, leading to a filamentary structure with superior properties. If the precipitation heat treatment was omitted, interstitial additions had a negligible effect on Jc. wong3 showed that higher heat-treatment temperatures lowered Jc. Walker and co-workers,4 who studied microstructure (by transmission electron microscopy) as well as superconductivity, found that the Jc anisotropy introduced by cold rolling was itself affected by heat treatment. They were unable to clarify the relation between microstructure and critical current density, although evidence of precipitation was indicated. More recent investigation of Nb-Zr alloys,5,6 besides showing that structural defects and fiber ing due to cold work and precipitation serve to raise Jc, also elucidate important optically observable microstructural changes which occur upon precipitation. In these reports, coarsening of the microstructural features was found to decrease Jc. Vetrano and Boom,7 who studied Ti-20.7 at. pct Nb, found that Jc was increased to a maximum by a 415°C, 3-hr heat treatment following quenching from 800°C and cold working. Heat treatments can also affect the resistive critical field Hr. Final-size heat treatments of Nb-Zr wire can lower Hr drastically if gross phase decomposition occurs5&apos;* or moderately if the effects of cold work are eliminated without changing significantly the composition of the phase of interest.3,5,6,8 The percentage of oxygen which can be added to Nb-Zr alloys to enhance Jc is limited by the difficulty of subsequent cold drawing. Since Nb-Ti and Ta-Ti alloys in contrast can tolerate appreciably higher percentages of oxygen, it was decided to investigate the superconducting behavior of various alloys in these systems. The present paper describes the results of adding oxygen to a nominal 40 wt pct Nb alloy as a function of thermomechanical treatment. I) EXPERIMENTAL PROCEDURE A small alloy ingot was prepared from high-purity niobium, iodide, crystal-bar titanium, and Nb2O5 powder by arc melting on a water-cooled copper hearth in a gettered argon atmosphere. The ingot was turned and remelted fourteen times to insure homogeneity. After final melting and rapid cooling, it was machined round to 0.415 in. diam, jacketed in stainless steel, and cold-swaged to 0.117 in. diam. The jacket was removed and swaging continued to 0.051 in. diam followed by wire drawing in carbide dies to 0.010 in. diam. Although it was intended that about 1500 ppm O (by weight) be added, inert gas fusion analysis indicated a 2390 ppm 0 content, apparently due to additional oxygen pickup in the arc furnace. Even so, the alloy was sufficiently ductile to be cold-worked to greater than 99.9 pct reduction

Jan 1, 1967

By Klaus Schwerdtfeger

The equilibria in the Cr-N system have been investigated in the temperature range 1100° to 1310°C by reacting chromium powder with Nz-Hz gas mixtures. The solubility of nitrogen in chromium in equilibrium with chromium subsitvide ("Cr,N") is given by Chromium subnitride is nonstoichiotnetric; its nitrogen content is always less than that corresponding to the formula CrzN. The lattice paranzeters of quenched samples have been measured; c, and a. parameters are found to increase with increasing nitrogen content. The growth rate of the subnitride layer on chromium plates was measured by a thermogravimetric technique, using a silica spring balance. The self-diffu-sivity obtained from the theoretical analysis of the parabolic rate constant is found to decrease with increasing nitrogen content, i.e., with decreasing vacancy concentration in the nitrogen sublattice. The intrinsic nitrogen diffuivity is derived from another series of rate measurements using "CrzN" plates; the intrinsic diffusivity, DN = 3.2 X 10-a cmZ sec-&apos; at 1200 C, is found to be essentially independent of- the subnitride composition. The concentration gradient was measured in a chromium subnitride layer by the X-ray method and found to be consistent with the derived diffusivity value. TWO chromium nitrides are known to exist:&apos; the nonstoichiometric subnitride "CrzN" and the nitride CrN. In the present work the kinetics of the formation of chromium subnitride from chromium and nitrogen have been investigated at 1100" and 1200°C. In additional experiments the relevant equilibria have been measured. The data are used to evaluate the diffusivity of nitrogen in chromium subnitride. Since chromium nitrides are often found in chromium-containing steels, the results are expected to be helpful in the interpretation of the chemical reactions between chromium steels and nitrogen. Equilibria in the Cr-N system have been determined by several investigators.2"3 The rate of nitriding of chromium was measured by Arkharov et a1 .&apos; in ammonia in the temperature range 800" to 1200°C. The parabolic rate law was observed. Due to the undefined nitrogen activity of the ammonia atmosphere, it is dif- ficult to interpret these rate data theoretically. An additional difficulty arises from the fact that the two-layer scale consisting of CrN and "Cr2N" was formed at the temperatures below 1030°C. The rate of nitriding of technical chromium (95 pct) was measured by Zaks in nitrogen at -1 atm in the temperature range 800" to 1300°C. EXPERIMENTAL METHODS The chromium samples were reacted with Nz-HZ gas mixtures in a vertical tube furnace, wound with Pt-10 pct Rh resistance wire. The gas-tight reaction tube was of high-purity recrystallized alumina. In nitrogen solubility measurements the nitrogen content of chromium was determined by the Kjeldahl method, on samples quenched in the cold part of the furnace. The nonstoichiometry of the subnitride and the nitriding rates were measured thermogravimetrically using a sensitive (+0.1 mg) silica spring balance. For the equilibrium measurements samples of 1 g of chromium powder contained in high-purity alumina crucibles were used. In order to remove most of the oxygen and nitrogen impurities from the chromium, the samples were initially annealed in purified hydrogen until a constant weight was obtained. The chromium plates (approximate dimensions 2 by 1 by 0.08 cm) used for the rate measurements were machined from ingots obtained by arc-melting of iodine-processed chromium. According to manufacturers&apos; specifications the purity of the chromium powder was 99.9 pct Cr and that of the iodine-processed chromium 99.99 pct Cr. Our own spectroscopic analysis of the chromium powder yielded 0.02 pct Fe, 0.05 pct Mn, 0.05 pct Si, and 0.02 pct Ti as major impurities with all the other detectable elements below 0.005 pct. The nitrogen partial pressure of the gas phase was controlled by mixing prepurified hydrogen and nitrogen with constant pressure head capillary flowmeters. Oxygen and water vapor were removed from the mixed gas by passing it through columns of platinized asbestos (450°C) and anhydrone. The gas flowed upward in the furnace with flow rates of 300 to 500 cu cm per min (25"~). Gas tightness of the furnace system was ensured by pressure checks at regular intervals. The furnace temperature was controlled electronically in the usual manner. The reported temperatures were measured with a Pt/Pt-10 pct Rh thermocouple and are estimated to be accurate within ±$C The X-ray measurements were made with a Debye-Scherrer camera and a diffractometer using chromium radiation {\Ka = 2.29092A). EQUILIBRIUM MEASUREMENTS The experimental results of the equilibrium measurements are contained in Tables I to In. Fig. 1 shows the solubility of nitrogen in solid chromium in the temperature range 1100" to 1310°C. In Figs.

Jan 1, 1968

By E. H. Bunce

CONTINUED progress in zinc metallurgy has been shown during 1933 by the adoption of new methods as well as the modernization of old processes and equipment, and by the initiation of new fields of activity for future advancement. The use of suspension roasting continued to grow as its advantages and adaptability became increasingly, apparent. The process developed by the National Smelting Co., Ltd., several years ago, of completely roasting on large sintering machines with utilization of the gas for acid manufacture has worked so successfully that an additional machine was installed during the year. At both the Swansea and the Avonmouth Works all of the ore for smelting is now roasted on the large sintering machines, thereby completely eliminating the old hearth-roasting furnaces. Work continued on obtaining partial purification of zinc ores from lead and cadmium by close control of conditions on the sintering machine, and in a few instances by chlorine additions to the ore before sintering. Ores so treated were either partially roasted or com-

Jan 1, 1934

By J. Gurland

THE microstructure of sintered carbides consists of particles of metal carbides, such as WC and TiC, embedded in a metallic binder which is usually a cobalt—or nickel-rich solid solution. One of the important factors influencing the strength of the alloys is the degree of dispersion of the carbide particles in the binder matrix. While it is generally accepted

Jan 1, 1960