By E. T. Turkdogan, P. Grieveson

Experimental results are presented for the rate of solution of nitrogen in a iron in the temperature range 750° to 873°C and in 6 iron in the temperature range 1410° to 1470°C. It is shown that the rate controlling process is diffusion of nitrogen into the iron. The diffusiting of nitrogen in a and 6 iron is derived from the results, and the temperature dependence of the diffusivity is represented by the equation D = 7.8 x e- 18,900/RT sq cm per sec. The solubility of nitrogen in a and 6 iron, in equilibrium with 1 atm pressure of nitrogen, has been measured. Using these results and other available data, it is found that the variation of the logarithm of nitrogen solubility with the reciprocal of absolute temperature is nonlinear. In an Appendix, some results of Darken and Smith are presented for the rate of solution of nitrogen in iron using ammonia + hyidrogen mixtures. These data also support the view that diffudsion of nitrogen in iron is the rate-controlling process when ammonia + hydrogen mixtures are used. A considerable effort has been made to obtain data on the solubility1-5 and diffusivity of nitrogen in a iron6-l2 because an understanding of the effect of nitrogen on the properties of steel must be based on an accurate knowledge of the properties of nitrogen in pure iron. However, no information is available concerning the kinetics of solution of nitrogen in a and 6 iron. Recently the authors13 have investigated the rate-controlling mechanism operating in the kinetics of solution of nitrogen in y iron. This study was directed to determine the rate-controlling processes for similar reactions with a and 6 iron as well as to establish values for the solubility of nitrogen in equilibrium with nitrogen gas in a and a iron. EXPERIMENTAL The procedure used in experiments to determine the rate of solution in cylindrical iron rods was the same as that described in a previous communication.13 Ferrovac E grade iron used in all experiments contained the following impurities in weight percent: C, 0.005; Mn, 0.001; P, 0.002; S, 0.006; Si, 0.006; Ni, 0.025; Cr, 0.002; V, 0.004; W, 0.02; Mo, 0.01; Cu, 0.001; Co, 0.01; 0, 0.007. After cleaning the surface, the iron rods were treated in an atmosphere of purified hydrogen for 17 hr before the reacting gas was introduced for known experimental times. After quenching, the samples were sectioned radially and analyzed for nitrogen. In addition to experiments using rods, iron foils were used in the measurements of solution rates of nitrogen in a iron. The foils of two different thicknesses were prepared by cold rolling Ferrovac E grade iron cylindrical rod to 0.051 and 0.152 cm. Foil samples were used in a rectangular form 5 cm long and 1.25 cm wide. The specimens were thoroughly cleaned of surface oxide with fine emery cloth and degreased with carbon tetrachloride immediately before entry into the furnace. The experimental procedure was the same as that used in the study with rods. At the completion of an experiment, the foil samples of the nitrogenized iron were analyzed for nitrogen after discarding 0.3 cm from the perimeter of the specimen. Iron foils were nitrogenized and denitrogenized in the a and 6 range with a gas mixture of 95 pct N and 5 pct H for times varying from 5 min to 2 hr. Results obtained for the average composition of nitrogen in iron for these experiments are presented in Fig. 1. Prior to the denitrogenization experiments, the samples were saturated with nitrogen at 1000°C and 0.67 atm N, giving a uniform nitrogen concentration of 0.0204 pct. According to the known a-y phase boundary in the Fe-N system,14 this composition lies within the ferrite region at temperatures 750" to 850°C. Use of this initial nitrogen content insured that reaction occurred between the gas and a single solid phase, a iron. Examples of the results for the mean concentrations of nitrogen in cylindrical iron rods, 0.356 cm radius for both the a and 6 ranges are given in Fig. 2. Typical examples of the results obtained for the radial distributions of nitrogen in rods are presented in Fig. 3. It appears that the results for radial distributions can be extrapolated to constant surface compositions which agree with the equi-

Jan 1, 1964

By I. Iwasaki, K. Adam

The oxidation behaviors of simple and complex chloride systems of copper, iron, nickel, cobalt, and manganese in a stream of oxygen were investigated using a thermogravimetric analysis technique. Their reaction mechanisms are discussed from stoichiometry, thermodynamic feasibility, and X-ray diffraction analysis of reaction products. The results are used to determine an optimum operating temperature of the selective oxidation step in a chlorination process for producing nonferrous metal chlorides, elemental sulfur, and ferric oxide from copper-nickel sulfide flotation concentrates.

Jan 1, 1985

By J. S. Pascover, J. K. Abraham

The influence of the early stages of precipitation on the kinetics and structure of martensite formation in Fe-27Ni and Fe-29.5Ni alloys containing from 0 to 10 pct Ti was examined with X-ray and electron microscopy techniques. The formation of a coherent, ordered preprecipitate had a profound stabilizing effect on the austenite. The Ms was decreased by increased titanium content and aging time up to a critical time. When the critical aging time was exceeded, the Ms was observed to increase markedly. The formation of the clusters was insuppressible and the volume fraction of clusters formed during the quench was a function of the titanium content. Martensite resulting from transformation of the clustered austenite is tetragonal with the c/a ratio increasing with titanium content. A model for the tetragonality is suggested. The morphology and substructure of the m artensite is inter-preted in terms of the above information and the cur-rent models of twinned martensite. ThE ramifications of precipitation in austenite to the properties of austenite have been the subject of numerous investigations. The current research is concerned with the influence of precipitation in austenite on the kinetics and structure of subsequent marten-site formation. In a previous investigation, Abraham et al.1 followed the aging reaction in an Fe-29.5Ni-4.2Ti* (at. pct) alloy using an X-ray diffraction technique. This technique, employing a Guinier camera, provided kinetic measurements through observation of the side band position as a function of aging time. The salient results of this work were: 1) The initiation of precipitation was not suppressed by quenching, i.e., there was a finite cluster zone size at zero aging time; and 2) The hardness of the aged austenite correlated extremely well with the zone size. During the previous work it was noted that the mar-tensite formed after aging was tetragonal, substanti-ating an earlier observation.2 Systematic investiga-tion revealed that the martensite was tetragonal in both the solution-treated then quenched, and the solu-tion-treated, aged, and quenched condition, and, furthermore, that a marked stabilization of the austenite occurred as a function of aging time. The present work is concerned with documenting the tetragonality and the stabilization phenomena as well as the ob- served microstruction with a suggested rationale for the behavior noted. EXPERIMENTAL PROCEDURE The compositions of the alloys are listed in Table I. The analyses were performed after the solution treatment of the strip material. Nickel was determined using the standard dimethy1-glyoxime procedure whereas titanium was determined colorimetrically with hydrogen peroxide and volumetrically by titrating with ferric iron. The materials were melted in a 5-lb vacuum induction furnace, cast into 2-in.-diam ingots, and forged in a temperature range of 950. to 1200°C to 1/2-in. slabs. The three higher titanium containing materials cracked during forging; therefore, to get the alloys into strip form, slices 1/8 in. thick were cut from the slab, homogenized 4 hr at 1150°C, then cold-rolled to a 0.04-in. thickness. The remaining slabs were hot-rolled, homogenized 4 hr at 1065"C, then cold-rolled to a final thickness of 0.03 in. All of the heat treatments were performed under a protective atmosphere of argon. The Ms temperature for most of the alloys is below room temperature; therefore, it was possible to solution treat, quench to room temperature, polish, and then observe the transformation optically on a cold-stage microscope. To determine the effect of aus-tenitizing temperature on Ms, eight of the alloys were treated at two temperatures, 1025" and 1120°C. No measurable variations in Ms were noticed. The remaining alloys were treated at 1025°C. The specimens, : by 5/16 by 0.03 in., were austeni-tized in a vertical tube furnace under a dynamic argon atmosphere. The bottom of the tube was submerged in water for quenching purposes. The question of stabilization that may be operating at room temperature was investigated and found to be negligible. Many of the specimens were held at room

Jan 1, 1970

By George Krauss, M. Cohen

The reverse martensitic transfomzation (i.e., the conversion of martensite to austenite on heating) was investigated in Fe-Ni alloys containing 30.5 to 33.5 wt pct Ni. The reversed austenite was found to be sufficiently distorted to exhibit marked differences in mechanical properties and to undergo recovery and re crystallization on further heating. In particular, the yield strength of the reversed austenite was as much as 2.5 times higher than that of the virgin austenite: with five cycles of the direct and reverse martensitic transformation, the yield strength was 2.6 times higher. There was an accompanying decrease in strain-hardening capacity and in stable ductility or uniform elongation. The recrystallization was observed to follow sigmoidal kinetics, but was characterized by an abnormal1y large temperature dependence which was evidently due to carbon segregation at the migrating grain boundaries. Upon recrystallization, the strength Properties reverted to those of the virgin austenite, but the ductility did not fully recover until the annealing temperature was further raised to dissipate the carbon segregation at the grain boundaries. The transformation of reversed austenite to produce second-generation martensite resulted in an unusually imperfect structure, thereby leaditg to additional strengthening. Horlleuer, the martensitic phase was much less responsive in this respect than was the austenite. MOST martensitic transformations are capable of undergoing a reverse transformation back to the austenitic phase on heating.&apos; This reaction, like the direct transformation to martensite on cooling, is usually athermal. In analogy with the Ms andMf temperatures for the martensitic transformation (where M, > Mf), the reverse transformation is characterized by the As andAf temperatures (where As<Af). It is well-known that the finish (Af) of the martensite-to-austenite reaction on heating may occur at a temperature where austenite is not stable relative to other phases in the equilibrium diagram.&apos; Reverse martensitic transformations have been found to influence the properties of the parent austenitic phase in a number of ferrous alloys. The austenite thus produced after one or more reversals is significantly altered in strength, microstruc-ture, diffusivity, and annealing characteristics compared to well-annealed, virgin austenite. The first detailed observations of such phenomena were made by Wasserman3 on an Fe-30 wt pct alloy. He found that the reversed austenite (i.e., austenite formed by the reverse martensitic transformation) was much stronger than the original austenite, and the second-generation martensite (i.e., martensite produced from the reversed austenite) was somewhat stronger than the first-generation martensite. On heating the reversed austenite, recrystallization occurred in a manner similar to that of a cold-worked metal; the Laue spots sharpened and the strength decreased.4 In recent years, Russian workers have shown considerable interest in these reverse martensitic transformations. Most of such investigations5-10 have been concerned with the stabilization of reversed austenite relative to subsequent martensitic transformation, and because of its unusual nature, this phenomenon will be discussed in detail elsewhere." On the other hand, the annealing behavior of reversed austenite and the attendant variation in properties have received little attention beyond the experiments of Wasserman.3,4 Gridnev eta1.,8 in one of the few such studies. followed the hardness change of reversed austenite as a function of time at three annealing temperatures. The marked strengthening of austenite achieved by the reverse martensitic transformation has been referred to as "transformation strengthening" by Wasserman3,4 and as "phase hardening" by Malyshev et a1.7,9,10 to differentiate it from hardening produced by cold working. Both groups of investigators noted that further strengthening of the austenite could be attained by repeated or cyclic transformations, but the first cycle resulted in the most pronounced effect. Evidence of the altered microstructure of reversed austenite has been reported by Maximova and Nikonorova6 and by Edmonson and KO.12 The former found that reversed austenite was much more sensitive to etching than the original austenite, and the latter authors observed a (&apos;ghost" structure resembling martensite in certain areas of the reversed austenite. Enhancement of the self-diffusion rate in reversed

Jan 1, 1962

By M. J. Sinnott

WITH the advent of nodular iron as an engineering material, considerable interest has been shown in developing this material for various applications. Generally the strength, hardness, or ductility are the more common properties used for design purposes but occasionally applications involving a knowledge of the thermal conductivity of the material is required. A search of the literature showed, rather surprisingly, that relatively little work has been done on this property for all types of cast iron. Insufficient data are available on thermal and electrical conductivities to develop the Weidemann-Franz ratio, or the Lorentz relationship, for estimation purposes. There are no data on nodular irons and the published data on malleable irons are quite sketchy. For these reasons the conductivity of the group of nodular irons listed in Table I were measured. Irons I to IV were made in such a fashion as to maintain the carbon and alloy content essentially the same while varying the silicon content. Test specimens were cut from the mid-section of 4-in. keel castings. Iron V is a commercial casting of nodular iron. The test specimen of this iron was cut from the center of a large cast billet 3x10x26 in. All alloys were tested in the as-cast condition. A microstructural examination showed that each iron had spheroidal graphite but the size and distribution varied with the silicon content of the iron. The spheroid size decreased while the number of graphite nodules increased as the silicon content of the iron was increased. The matrix structures of each iron consisted of pearlite and ferrite with the proportions varying from predominantly pearlite in the low-silicon iron to mostly ferrite in the high-silicon iron. The commercial heat, iron V, was predominantly pearlite probably because of its higher manganese and phosphorus content. Two methods for measuring the thermal conductivity were used. The first was a modification of the techniques described by Powell and Hickman and Van Dusen and Shelton,² the second method was a simpler technique described by Jakob and Hawkins." Since the agreement of both methods as tested on two sets of duplicate samples was excellent, the simpler experimental technique was used. The results of the measurements are given in Table II along with a summary of the microstructural constituents. These conductivity data indicate that as the percentage of silicon increases there is a corresponding decrease in the thermal conductivity even though the structure is changing from pearlitic to ferritic. Such a change in microstructure is usually accompanied by an increase in conductivity. A third factor involved in the behavior of these irons is the size and distribution of the graphite nodules. The relative amounts of graphite do not change greatly but the size and distribution do. Generally graphite improves the conductivity but in the present case such an effect is probably masked by the alloying effect from the silicon and its dispersion through the matrix. The thermal conductivity of the nodular irons studied is less than that of regular foundry irons by some 10 to 30 pct and is less than that of regular malleable irons.&apos; The cause of the decreased conductivity is probably the more highly alloyed fer-rites obtained in these irons and the changed mode of distribution of the graphite as compared to the regular foundry irons. References R. W. Powell and M. J. Hickman: Journal Iron and Steel Inst. (1946) 154, No. 2, p. 99. &apos;M. S. Van Dusen and S. M. Shelton: U. S. Bur. Standards Journal of Research, RP668 (1934) 12, p. 429. ³M. Jakob and G. A. Hawkins: Elements of Heat Transfer and Insulation. 2nd Ed. (1950) New York. John Wiley and Sons. &apos; J. W. Donaldson: Journal Iron and Steel Inst. (1933) 128, No. 2, p. 255.

Jan 1, 1954

By G. R. Love, M. L. Picklesirner

THE use of color adds a new beauty, power, and versatility to metallography. This has been amply demonstrated in a number of public exhibits and on the walls of corporate, government, and university metallographic laboratories around the world. Indeed, in a number of cases, the color not only is of esthetic value but is scientifically essential to the competent examination of particular samples and systems. Optical strain analysis,&apos; determination of true grain size in U-A1 alloys: phase identification in Nb-base alloys,3 analysis of transformation rates in heat-treated Nb-Zr alloys,4 measurement of solidification segregation in cast Nb-Zr alloys,&apos; study of the intermediate phases in Nb/Sn diffusion couples,6 investigation of the oxidation kinetics at various surface orientations in single crystals,7&apos;8 and a number of other research efforts9&apos;10 would have been vastly more difficult without the extra clarity and distinction introduced by color—either the colors resulting from particular polarized light techniques or the interference colors obtained by oxidation. It is unfortunate that the beauty of colored micro-structures cannot be shared more widely, but the economics of publishing a technical magazine apparently prohibits color plates except under extraordinary circumstances. It is doubly unfortunate that no convenient, general method exists for communicating the information available in colored microstructures to the scientific community. True, in some instances the color changes observed are dramatic enough that direct black and white photography is adequate. In photoelastic stress analysis, several orders of interference fringes may be produced and it is frequently desirable to suppress the color effects (use monochromatic light) to simplify interpretation. On the other hand, relatively minute color variations may be readily detectable by eye, be of considerable assistance in interpreting a structure, and yet be enormously difficult to reduce to an unambiguous black and white print. In order to illustrate a possible compromise or solution to the above problems, we wish to show three black and white photographs of the same region of an Nb/Sn diffusion couple whose interpretation depends heavily upon use of color techniques. These micro-structures were obtained from a section through a rod consisting of commercial-purity niobium tubing filled with 99.995 pct Sn (melt-filled in 10"6 Torr vacuum). The composite rod, measuring 500 mm long, was bent into a hairpin shape and inserted into water-cooled copper grips in a vacuum high-temperature furnace. The rod was outgassed for 2 hr at a furnace temperature of 800°C and was further heated by self-resistance using a 2.2-kva ac power supply. The rod was raised to 1910°C over a 4+-hr period, held for 15 min, slow-cooled to 1500°C over a -hr period, and free-cooled to room temperature (all temperatures were measured with W5Re/W26Re thermocouple). Throughout the heat treatment the ambient pressure was kept below 8 x lo-&apos; Torr. Metallographic preparation of the sample was completely conventional except that it was necessary to extend the grinding steps to remove damage in the brittle NbsSn phase introduced by sectioning. No satisfactory chemical or electrochemical etch has been found for these diffusion couples; of those which have been tried, any that attack the niobium-rich phases at all attack the tin-rich phases disastrously. However, the final polishing steps did produce a slight relief effect and this, coupled with anodizing, yielded excellent clarity in the microstructures for direct observation. The anodizing voltage was chosen to give maximum change in color per unit change in composition. In this case, indeed normally, this maximum sensitivity occurred in the blue-to-red color range. The pure niobium tube wall anodized to a relatively bright blue

Jan 1, 1967

By ERNEST A. HERSAY

ACCURATE ore-sizing with screens is drawing attention to certain details that now, more than ever before, require attention. There are many tests that must be preceded by careful sizing. The assayer often could profit by a more careful selection of screens. In milling, more attention is given the slimes produced. Cement-manufacturers are pulverizing and screening finer than they formerly did, and others are reducing materials to fine sizes at high cost, with screens used to govern the fine¬ness of the pulverized product. Fine screens are expensive, easily injured by mis-use, are carried in stock sparingly by most dealers, and are handled often by those who know little about them except their designated number. More attention, on the whole, needs be given the actual size of the mesh-openings, and less emphasis placed upon any custom or conventionality in numbering. An effort to classify wire screens, in this respect, leads at once into computations, where one is confronted with details of sizes and standards, of different wires, different gauges, and different customs. There is always uncertainty about the exact working-size of a screen until one gives the matter special attention, and devotes more time to it than its simplicity seems to demand. To know only the number is not sufficient for all uses. Often, in sets, superfluous sizes are used; and sizes are omitted that are of critical importance. In wire screens, the use of different standard sizes of wire makes important differences in dimensions that must be taken into account. The dealer usually grades screens by the number of openings per linear dimensions, regardless of the size of the openings or of the wire. Certain 100-mesh screens in use are found, by measurement, to he actually coarser than others of 90-mesh, a result which is due, of course, to the use of larger

May 1, 1906

By J. F. Wolff

CARL ZAPFFE, Brainerd, Minn. (communication to the Secretary*).¬Unless one has actually directed explorations for iron ore, it is doubtful whether the importance of Mr. Wolff&apos;s paper, the value of the information contained, and the large amount of detail work involved in what is set forth can be fully appreciated. It is indeed rare to get such a com-

Jan 3, 1917

By W. A. Thomas

Steam is, and doubtless always will be, the basic power in the anthracite industry, either directly applied through engines and pumps or electrically. The rapidity with which electric power is being applied to the mining and preparation of anthracite leaves little doubt as to its utility and economy. There is practically no operation, except possibly the drilling of hard rock, that has not been successfully electrified and the matter of drilling is handled economically with electrically driven compressors and the standard compressed-air drills. Conservation and the seemingly ever-increasing cost of production, justify careful consideration of the possible results of the more extensive use of electric power in the industry. It is not planned to discuss, herein, the relative economies of individual applications but to consider the relative economy and flexibility of steam and electric power. The reports available for the year 1920 indicate a production of slightly over 80,000,000 tons of anthracite, of which 8,843,500 tons were used for power and heating purposes; in other words, over 11 per cent. of the production was used at the mines. Some of this was used to generate electric power at the mines, about 160,000,000 kw-hr., while 150,000,000 kw.-hr. was purchased from the public utility companies. One large producer, who is buying some electric power and generating some, used over 13 per cent. of the production for power and heating at the mines. Another producer, where considerable electric power is generated on the properties, is using less than 9 per cent. of the output for power and heating. One of the largest producers has a fuel consumption of over 15 per cent. of the output, besides which considerable power is purchased. A careful study of the field indicates that steam-operated plants use upwards of 13 per cent. of the production for power and heating, while electrically operated plants use about 1 per cent. for heating; so that, for steam-power purposes at least 12 per cent., or 268.8 Ib., are used for power out of each ton produced. In the complete electrification of anthracite mining operations, no set rule can be given for the power requirement, in kilowatt-hours per ton, as conditions vary widely in the matter of pumping, ventilation, and transportation, but the following cases are given as a basis of determining a range and a possible average power requirements:

Jan 1, 1922

By Mark J. Klein, A. H. Clauer

The Snoek peak induced by solute nitrogen in chromium was studied. A rapid quenching rate is required to maintain nitvogen in solution in sufficient concentrations to be detectable by internal-friction techniques. An expression for the tertninal solubility, c, of nitrogen in weight pevcent is log,,c = -4130/T + 1.05. The diffusion of nitrogen in zhromium determined by internal friction is SNOEK&apos;S theory1 of the stress-induced ordering of interstitial solute elements in the bcc lattice has been used to deduce information on the behavior of interstitials in a number of bcc metals. Under the proper conditions, internal-friction studies of "Snoek peaks" permit a determination of diffu-sivities, solubilities, and precipitation kinetics of interstitial elements. Internal-friction studies of this type have been reviewed by Nowick,&apos; Wert,= Powers and Doyle,4 and others. The behavior of interstitial atoms in Group V-A metals and iron has been rather extensively studied in this way, and results are reasonably self-consistent. However, the study of interstitial elements using internal friction in the Group VI-A metals—tungsten, molybdenum, and chromium—is much less clear. Thus far, internal-friction studies have revealed a peak in tungsten tentatively attributed to carbon5 and a peak in chromium associated with nitrogen. In chromium, Bungardt and Preisendanz6 observed a peak at 180°C for a frequency of -1 cps which they associated with nitrogen. More recently, de Morton7 determined the diffusivity of nitrogen in chromium from studies of a nitrogen peak at 160°c for a frequency of -1 cps and from elastic aftereffect measurements. The objective of this investigation was to study the nitrogen peak in greater detail, to obtain information on the behavior of nitrogen in chromium. This information is of interest because nitrogen is known to have an embrittling effect on chromium. However, efforts to deduce the role played by nitrogen in influencing the mechanical behavior of chromium are handicapped by lack of information on its behavior and distribution in chromium. EXPERIMENTAL PROCEDURES The chromium wires used in these studies were drawn from arc-melted iodide-chromium stock that had been extruded, swaged, and centerless-ground to 0.25 in.-diameter rods. Internal-friction measurements were made in an evacuated torsional pendulum similar to the one described by Kê,8 utilizing wires 0.048 to 0.030 in. in diameter. A series of analyses of the fabricated wires showed that the major impurities were approximately 100 ppm Fe and a combined interstitial content of 50 to 100 ppm C, O, N, and H. A typical interstitial analysis of the wires after processing is 15 ppm C, 2 ppm H, 50 ppm O, and < 5 ppm N. Interstitial concentrations were determined by vacuum-fusion, combustion-conductimetric, and micro-Kjeldahl analyses. In general, vacuum-fusion analysis yielded a lower nitrogen concentration than did micro-Kjeldahl analysis. For consistency, the nitrogen concentrations reported in this investigation were determined by the former method. Heat treatments were carried out by encapsulating the specimens in quartz tubes containing argon. The fabricated wires were annealed at 1150°C for 1 hr to produce uniform recrystallized grain size of about 0.015 mm. Nitrogen and carbon were added to the fabricated wires by encapsulating them in a quartz tube containing ammonia or methane, and annealing them at 1150°C for 48 hr. In some instances, carbon was also introduced by coating the wires with carbon black prior to annealing.

Jan 1, 1965

By Joseph E. Pogue

In 1920, 531 million barrels of crude petroleum were coi~sumed in the United States. As imposing as this figure is, the fact that the domestic consumption of crude petroleum has increased at an average rate of 10 per cent. a year for the past decade is more striking. Will this rate of increase in demand continue? If so, the year 1930 will call for 1260 million barrels of petroleum—a staggering volume. On the other hand, may we expect the demand for petroleum to grow as rapidly as it did when the automotive industry was having its most phenomenal expansion? If not, to what extent will the growth of oil requirements decrease? When and to what degree will the petroleum industry become affected by the economic law of diminishing returns? Obviously, this matter requires careful analysis, especially as both national and industrial planning must be predicated upon present estimates of the requirements of the future. The purpose of this paper, accordingly, is to project, as closely as present limitations of knowledge permit, the course of the demand for petroleum in the United States over the next ten years. At first, the problem of estimating the future of a demand as complex as that for petroleum might appear insoluble. Fortunately, hon~ever, therc are several scientific methods of approaching the problem, centering around a study of rates of industrial growth, which lend considerable hope that the requirements of the immediate future in this field may be approximated with sufficient closeness to have practical value as a basis of action. Growth oF Petroleum Demand The demand for crude petroleum is the resultant of the demands for the products made jointly from this substance—gasoline, kerosene, gas and fuel oil, and lubricating oils. The demands for these have grown at

Jan 1, 1923

By Joseph E. Pogue

In 1920, 531 million barrels of crude petroleum were coi~sumed in the United States. As imposing as this figure is, the fact that the domestic consumption of crude petroleum has increased at an average rate of 10 per cent. a year for the past decade is more striking. Will this rate of increase in demand continue? If so, the year 1930 will call for 1260 million barrels of petroleum—a staggering volume. On the other hand, may we expect the demand for petroleum to grow as rapidly as it did when the automotive industry was having its most phenomenal expansion? If not, to what extent will the growth of oil requirements decrease? When and to what degree will the petroleum industry become affected by the economic law of diminishing returns? Obviously, this matter requires careful analysis, especially as both national and industrial planning must be predicated upon present estimates of the requirements of the future. The purpose of this paper, accordingly, is to project, as closely as present limitations of knowledge permit, the course of the demand for petroleum in the United States over the next ten years. At first, the problem of estimating the future of a demand as complex as that for petroleum might appear insoluble. Fortunately, hon~ever, therc are several scientific methods of approaching the problem, centering around a study of rates of industrial growth, which lend considerable hope that the requirements of the immediate future in this field may be approximated with sufficient closeness to have practical value as a basis of action. Growth oF Petroleum Demand The demand for crude petroleum is the resultant of the demands for the products made jointly from this substance—gasoline, kerosene, gas and fuel oil, and lubricating oils. The demands for these have grown at

Jan 1, 1923

By R. M. Daelen

In recent years many new appliances have been introduced into German steel-works and rolling-mills for the purpose of improving working-methods, and of creating and maintaining increased production, and satisfying the ever-growing demand for metal of closely specified hardness, strength and form. One result of the improvements has been to aid very effectively in demonstrating the real superiority of ingot- over wrought-iron for almost every possible purpose, and in dispelling the last vestiges of prejudice unfavorable to the new metal. If, nevertheless, no marked decrease in the number of puddlingfurnaces has yet been noticed, the cause of their survival must be attributed to the greatly increased consumption of all kinds of ironmanufactures. Several large new works for the production of ingotiron are now, however, in course of erection in the Rhenish-Westphalian district, and upon their completion a rapidly diminishing output of wrought-iron may be anticipated. The present aim of all large works manufacturing ingot-iron is to work the molten blast-furnace pig into a finished product without any further fuel-consumption than is required to furnish steam for the rolling-mill. Though practice has established the feasibility of this principle, no works can yet point to its complete adoption, partly because of the limitations imposed by existing conditions and plant, and partly, also, on account of the highly-diversified character of the finished products. The Bessemer-works were the first to feel the influence of the basic process; but of recent years a similar influence has affected the open-hearth, and the owners of works possessing both a converterand an open-hearth plant are now seeking to arrange them for combined working, in charging as well as in casting. In small works the basic-lined reverberatory furnace is constantly gaining ground over the old puddling-furnace. The small basic converter, on the

Jan 1, 1891

By Noel H. Stearn

When the Age of Machinery was suddenly thrust upon civilization about the beginning of the 19th century, an unprecedented demand for mineral resources sprang up. This demand brought about the rapid development of the known ore deposits and the discovery of such other deposits as could be encountered by energetic and canny prospectors. Thus in the countries now reasonably accessible nearly all orebodies have been located except those which are totally concealed even from the eyes and "senses " of experienced and expert prospectors. The high rate of exhaustion of known ore deposits and the necessity of looking farther and farther ahead for raw materials as a matter of insurance on the stupendous capital outlays involved in mining, development, and conversion operations, have resulted in exceptional activity in three different fields of effort. The first is purely geographic. Prospectors are now penetrating the few hitherto inaccessible regions in the hope of stumbling upon exposed ore deposits or locating visible indications of their presence. The second is chemical. Industrial chemists and metallurgists are seeking to facilitate the exploitation of lower grade ores or to find methods of recovering valuable metals from common substances. In the third field of effort lie the activities of the economic geologist and the mining engineer, who endeavor to locate concealed ore deposits which would remain hidden from the prospector no matter how expert or conscientious he might be. Obviously the task which such a man must face is both exacting and indefinite, and the tools which he has heretofore been permitted to bring to it are, for the most part, abstract—a knowledge of certain fundamental principles and processes involved in the origin, occurrence, structure, and distribution of deposits of natural resources and of the rocks which form the environments of those deposits; and a process of reasoning by analogy supplemented by the use of the diamond drill, or such artificial exposure as the test pit, trench, shaft, or tunnel.

Jan 1, 1929

By Daniel M. MacNeil, Carle R. Hayward, Raymond L. Presbrey

At the February, 1916, meeting of the Institute, a paper presented by Hayward and Raymond gave the results of a study on the effect of time in tempering medium-carbon steel, when the following conclusions were reached: It is not fair to consider the question settled when only three specimens were used for each treatment, but the results obtained indicate that for reheating quenched medium-carbon steel to temperatures below 500" it is only necessary to heat it through. Longer heating has little or no effect on the tensile strength, ductility, or hardness. At temperatures above 500°, increasing the time of treatment causes a slight falling off in hardness and tensile strength with a corresponding increase in ductility. In the discussion of the paper these conclusions were attacked and evidence was presented that seemed to throw doubt on their accuracy. The authors, however, showed that this evidence was based on high-carbon or alloy steels and no facts regarding medium-carbon steel were presented. During this study the heat treatment was carried out in a small electric resistance furnace. It held nine specimens, but when these were placed in the furnace the temperature was lowered to such an extent that 30 to 40 min. were required to reach the desired heat. The authors pointed to this as a weak point in the investigation and it seemed wise to supplement the research by work on similar steel but using a different method of heating. This has been done and the results are given in the present paper. The Rhode Island Tool Co. coöperated by furnishing the steel and turning the tensile specimens. The steel used in this investigation came in three bars 3/4 in. in diameter; analyses are as follows: Carbon. MaNGanese, Phosphorus, Sulfur Bar NUmber PeR Cent. Per Cent. Per Cent. Per Cent. 1 0.46 0.56 0.010 0.055 2 0.44 0.58 0.007 0.042 3 0.48 0.58 0.007 0.048

Jan 1, 1922

By Daniel M. MacNeil, Raymond L. Presbrey, Carle R. Hayward

At the February, 1916, meeting of the Institute, a paper presented by Hayward and Raymond gave the results of a study on the effect of time in tempering medium-carbon steel, when the following conclusions were reached: It is not fair to consider the question settled when only three specimens were used for each treatment, but the results obtained indicate that for reheating quenched medium-carbon steel to temperatures below 500" it is only necessary to heat it through. Longer heating has little or no effect on the tensile strength, ductility, or hardness. At temperatures above 500°, increasing the time of treatment causes a slight falling off in hardness and tensile strength with a corresponding increase in ductility. In the discussion of the paper these conclusions were attacked and evidence was presented that seemed to throw doubt on their accuracy. The authors, however, showed that this evidence was based on high-carbon or alloy steels and no facts regarding medium-carbon steel were presented. During this study the heat treatment was carried out in a small electric resistance furnace. It held nine specimens, but when these were placed in the furnace the temperature was lowered to such an extent that 30 to 40 min. were required to reach the desired heat. The authors pointed to this as a weak point in the investigation and it seemed wise to supplement the research by work on similar steel but using a different method of heating. This has been done and the results are given in the present paper. The Rhode Island Tool Co. coöperated by furnishing the steel and turning the tensile specimens. The steel used in this investigation came in three bars 3/4 in. in diameter; analyses are as follows: Carbon. MaNGanese, Phosphorus, Sulfur Bar NUmber PeR Cent. Per Cent. Per Cent. Per Cent. 1 0.46 0.56 0.010 0.055 2 0.44 0.58 0.007 0.042 3 0.48 0.58 0.007 0.048

Jan 1, 1922

By T. E. Evans, C. T. Baroch

ZrB2 was produced in batches of 4 to 6 Ib by interaction of ZrO2, B4C, B203, and carbon at around 2000°C in a simple graphite resistance furnace. Techniques of production are discussed and the final design of a suitable furnace is described in detail. Several other borides were made by the same technique and the process appears to have possibilities for commercial production. N seeking out new hard and refractory com- pounds, many researchers have turned to the investigation of the borides and excellent papers have been published on the properties of these compounds. Few papers, however, have appeared on the techniques and problems concerned with the production of these high temperature substances. This report describes progress made in developing a method for preparing zirconium diboride, ZrB2, on a pilot plant scale. The literature of the borides and other refractory hard metals recently has been reviewed, annotated, and classified so completely&apos; that it is needless to attempt such an outline here. It is enough to say that three borides of zirconium have been reported: ZrB, ZrB2, and ZrB12.2 ZrB2 is the most stable of these and is especially stable in the presence of carbon up to and including its melting point of around 3000°C. Like most borides, it can be prepared in several ways. It can be prepared by synthesis of the elements, but these are expensive and difficult to produce in a high state of purity. Obviously, production directly from the oxides would have decided economic advantages. In electrolytic production such as that of calcium boride,:&apos; the product is recovered as a sludge mixed with electrolyte; and separation of product from adhering electrolyte and regeneration of the electrolyte is an involved and difficult process. The work on borides was started on a small scale in 1948. Late in 1949, Naval Ordnance expressed a specific interest in ZrB2 and the project then centered on this compound. After the usual experimental work necessary in a new field, ZrB2 of good quality was produced by heating mixtures of B4C, ZrO2, B2O3, and carbon to a temperature of about 2000 °C in a resistance-type electric furnace. Over 100 lb was made for experimental use tests, and the method of production probably could be expanded into a commercial operation. A similar process has been described by Kieffer and coworkers.&apos; The main chemical problems were the development of proper charges to insure complete reduction of the elements, determination of the proper temperature range at which these reductions took place, and adoption of techniques necessary to pre- vent inclusion of such impurities as carbon and nitrides. The mechanical problems consisted of developing a simple practical furnace that would attain the high temperatures required and permit use of a controlled atmosphere when necessary and determining of suitable refractories. Both problems were solved by designing a crucible resistance furnace. Crucible Resistance Electric Furnace Attempts were first made to produce ZrB2 in an electric arc furnace, but such a furnace would not provide the degree of carbon control required for producing clean graphite-free borides, so it was decided to try working in a crucible. Obviously, the furnace would have to be constructed of graphite, as the temperatures required are too high for other refractories or heating elements. Crucibles were made by hollowing out segments of graphite electrodes, which were fitted with a cover and clamped between two electrodes so that the current passing through the thin wall of the crucible would generate heat, using the principle of the Helberger crucible furnace."? Preliminary tests with this type of furnace were encouraging and led to the furnace design shown in Fig. 1. The essential components were a thin-walled graphite crucible resting on a graphite block, which formed the lower electrode assembly, and a top electrode assembly swung from a pipe column making contact with the top of the crucible. The space around the crucible was filled with graphite prepared from waste electrodes crushed to about ¼ in. This packing had excellent insulating properties, both electrically and thermally, and could be removed easily and quickly from around the crucible by means of an industrial vacuum cleaner. The largest resistor crucibles were machined from 8 in. electrode stock and were 26 in. long, with a side wall Yi in. thick and a 1 in. bottom. Temperatures were determined optically by sighting down a 1 in. hole drilled longitudinally through the top electrode and the crucible cover. Sealing this hole at the top was a water-cooled brass sight-glass assembly, shown in Fig. 2. An opening was provided for a light flow of helium to keep the sight opening clear of smoke, and a glass prism above the sight glass changed the line of sight to the horizontal for easier reading. More recently, the prism and optical pyrometer were replaced by a photoelectric recording pyrometer. At first the charges were placed directly in the resistor crucible but this meant that everything had to be withdrawn from the furnace every time the charge was emptied. Later, smaller crucibles were made up that could be placed inside the resistor

Jan 1, 1956

By Eugene McAuliffe

TWO years ago the American Institute of Mining and Metallurgical Engineers made a memorable contribution toward a better understanding of the problems that have for many years confronted the coal industry. Specific suggestions toward betterment were then advanced, certain of which were taken up, amplified and endorsed by men who were conscien-tiously interested in the work of lifting this great industry out of the morass it has lain in for years. Two certain suggestions then made-provision for seasonal variations in railroad freight rates that would tend to encourage the purchase and movement of coal during the low summer production period, and provi-sion for the collection by the United States Government of all the facts surrounding the industry-were intro-duced in the form of legislation in the United States Senate by a member of that body, a man whose personal character, antecedents and business training put him above and beyond all suspicion of demagoguery; however, as the result of the insistent, vindictive opposition of the industry itself, these two bills, con-structive in their nature, were buried under an ava-lanche of misrepresentation. Today, with all mines that employ union labor at a stand still, the work of stabilizing the industry is yet before us. As aptly stated by Herbert Hoover, in March, 1920, when he was president of the Institute; An engineering organization is particularly the body to under-take this work. It is an economic problem, an engineering pro-blem within the ken of our experience; it is a problem that requires not only constructive thought but quantitative thought and wise social thought. The engineers of the United States occupy a position midway between capital and labor. They enter upon problems of this kind without prejudice either way, and they have that faculty of mind for quantitative thought, as distinguished from qualitative thought, that takes such problems as this out of the region of politics into the region of matter-of-fact solution.

Jan 5, 1922

By A. J. Garnier, N. H. van Lingen

Rock downhole is known to be lesc. drillable than when brought to the surface. This must be ascribed mainly to the presence under downhole conditions of a pressure differential across already made chips, which hinders their being lifted. The pressure differential has partly a static and partly a dynamic origin. Balling-up of bits is another consequence of this pressure differerztial. Reduction in penetration rate owing to an increase in the strength of the rock is governed by the difference between the mud pressure and the pressure of the for/nation pore liquid. Rotationally symmetric geostatic stresses have 170 effect on drillability. Fracture of rock when drilling will be brille in most cases. The above is supported by laboratory drilling experiments with drag bill and roller bits an elevated mud, pore, and confining pressures On rocks differing in strength and permeability. INTRODUCTION In oil well drilling drillability of rock is found to decrease with increasing depth of the hole. Naturally deep rock will be more compacted and, therefore, harder to drill than shallow rock of the same type. However, apart from this the drillability of a sample of deep and compacted rock brought to the surface is generally much higher than in its original location downhole. In view of the economic implications of this reduction in drillability, it seems worthwhile to analyze its causes. The origin clearly has to be sought in the difference of environment. The only conceivable factors would seem to be the presence of mud under pressure, the pressure of the formation pore liquid, and the overburden of the rock. Down the borehole the rock is compressed triaxially by mud pressure and overburden. It is well known that the strength of rock is increased when confined by external pressure1. Various authors have, therefore, ascribed the difference in drillability mainly to the strengthening of rock by triaxial compression. Another factor, mentioned by Bobo and Hoch5, is that forces. including "pressure differential forces", tend to hold a dislodged particle in place. However, the conditions determining their magnitude are not clarified nor is their effect on drilling rate assessed. In the laboratory, drilling experiments on pressurized samples of rock yielded evidence that pressure differential forces holding the chips down are the major factor in reducing rate at depth. This paper describes the experiments and shows how the results enable both a qualitative and a quantitative interpretation of the factors determining the effect of chip hold-down on drilling rate. The implication with respect to balling-up and jet action is also discussed. The greatcr part of the experiments were performed in the pressure vessel shown in Fig. 1. The spacc between the sample of rock and the vesscl is divided by "0" rings into three separate chambers. The rock sample is confined laterally by pressurized oil in thc middle chamber. Penetration of oil into the sample is prevented by partly jacketing it with brass foil. Thc pressure of the drilling fluid in the hole can be adjusted via the upper chamber. Permeable rock specimens arc water saturated before being drilled. With a properly plastering mud as drilling fluid the pressure of the pore water can be adjusted independently via the lower chamber.

By Paul Queneau

FROM the first days on the Norman beaches to the last days on the Elbe the Army Engineers of World War II lived off the countryside for the great bulk of the construction supplies needed for the fulfillment of their ultimate mission-to keep the army moving. To accomplish this end, vast tonnages of rock, timber, and steel were required in the construction of roads, railroads, and bridges. Combat Engineer battalions operated quarries under shell fire as a routine matter. An Engineer forestry company was decimated while cutting bridge timber on the Siegfried line. Oneof the more spectacular feats of the Army Engineers in obtaining construction materials was the operation of the Hadir Steel Works during the fall and winter o f 1944.

Jan 1, 1946