By F. A. Veer, W. G. Burgers, B. H. Kolster

Starting-- from Cu-Si diffusion couples a study of diffusion in the intermetallic compound Cu3Si of the Cu-Si system has been made. Mmker experiments showed copper to be the diffusing element. From the rate of growth of the Cu3Si phase diffusion coefficients were derived. The activation energy for diffusion is 18.6 kcal per mole. The couples show some interesting microscopic features, for which a tentative explanation is given. THE synthesis of dimethyldichlorosilane, (CH3)2SiC12, an important compound in the manufacture of methyl-silicones, takes place at the surface of a thin Cu3Si layer deposited on a mass of silicon particles."' By passing CH3C1 vapor at about 350°C, silicon atoms are consumed from Cu3Si in forming the volatile silane molecules, thus leaving copper atoms at the surface. It is well-known that copper acts as a poison for the above-mentioned reaction by catalyzing the dissociation of methylchloride.' However, no poisonous effect is observed, at least not before most of the silicon from the particles is converted into silane.3 This would be understandable, if either the copper atoms diffuse through the Cu3Si deposit to the underlying silicon or silicon atoms diffuse in the reverse direction to the copper, both processes resulting in the formation of new Cu3Si and so ensuring the proceeding of the reaction. In this paper experiments are described, demonstrating copper to be the diffusing element. Also a very low activation energy for the diffusion is observed. EXPERIMENTAL The silicon used contained 1 ppm Mg and 1 ppm Cu; the copper was spectroscopically pure (Fe: 2 ppm; Ag, Mg, Si: 1 ppm). The copper and silicon samples were prepared in the form of blocks of approximately 10 by 10 by 5 mm with two parallel sides by spark-machining. The blocks were ground on emery paper (grit 600), etched (copper with nitric acid, silicon with a 4:l nitric acid:hydrofluoric acid mixture), and cleaned with alcohol. As the brittleness of the silicon did not allow a welding procedure to prepare the diffusion couples, the copper and silicon blocks were pressed together in a steel clamp. The pressure exerted by the clamp brought about contact between the parts of the couple and so ensured proceeding of the diffusion. The couples were heated in a vacuum furnace (about 10"5 Torr). The temperature was stabilized within 1 pct. After a heat treatment a section parallel to the direction of diffusion was examined in the microscope and in the X-ray scanning microanalyzer. To determine whether copper or silicon is the diffusing element marker experiments were carried out using tungsten wires with a 20-p diam. EXPERIMENTAL RESULTS Figs. 1, 2, 3, and 4 give micrographs of diffusion zones of Cu/Si couples. Analysis by the electron mi-croprobe of the Cu/Si samples after a definite heat treatment revealed the existence of only one intermetallic phase as can be seen from the line scan shown in Fig. 5. From the X-ray diffraction pattern it could be deduced that this phase was CU 3 Si.4 Even when diffusion zones of considerable width (up to 600 p) were obtained, no other phases occurring in the Cu-Si system could be detected, neither by the electron microprobe nor by X-ray diffraction analysis. The optical anisotropy of the Cu3Si phase made it possible to observe the columnar shape of the crystal-

Jan 1, 1969

By Joseph R. Stephens

Deformation substructures of' polycrystalline tungsten, W-2, 9, and 24 pct Re, and W-3 pct Ta were studied by tra?zsrnission electron microscopy. The stress-strain curve for unalloyed tungsten showed gradual yielding followed by work-hardening. Electron nzicrographs indicated a gradual increase in dislocation density with increase in strain up to 5.0 pct. Dislocations, although frequently jogged, were straight over moderate distances and were in a randorn array. Stress-strain curves for alloy specimens of W-2 and 9 pct Re and W-3 pct Ta exhibited a drop in stress at yielding followed by only slight work-hardening. Electron micrographs of these specimens after strains of 0.05, 0.1, and 0.5 pct revealed no change in dislocation substructure from the unstrained specimens. After 2.0 pct strain, the three alloys exhibited dense networks. W-3 pct Ta was characterized by straight, frequently jogged dislocations comparable with the dislocation structure in unalloyed tungsten after a similar amount of strain. In contrast, W-2 pct Re exhibited dislocations that contained widely spaced jogs, while W-9 pct Re had developed a cell structure after the relatively srnall strain of 2.0 pct. The W-24 pct Re alloy contained a few dislocations after 0.1 pct strain, while after 0.5 pct strain twins were evident. Dislocation slip bands apparently preceded the twins. The stress-strain curve for the alloy indicated that twinning commenced after approximately 0.25 pet strain. These results indicate that the primary effect of low rhenium concentrations (2 and 9 pct) in tungsten is to increase dislocation multiplication after macroyielding by reducing the Peierls-Nabarro force (lattice resistance to dislocation motion). The dislocation bands that precede twins in W-24 pct Re may be caused by localized internal stresses resulting fro a metastable structure, for example, clustering of rhenium atoms. The effect of high rhenium additions (22 a 65 pet* Rproperties of tungsten. Klopp, Witzke, and Raffo5 reported bend transition temperatures as low as -100°F (200°K) for dilute electron-beam-melted W-Re alloys tested in the worked condition. Recrystalliza-tion increased the bend transition temperature, but alloys with 2 to 4 pct Re were still markedly superior to unalloyed tungsten. Fractographic examinations of tungsten and W- 3 pct Re and W- 5 pct Re alloys by Gilbert 6 revealed that these low rhenium alloys showed a greater tendency toward cleavage failure than did tungsten. Garfinkle 7 showed that rhenium additions, up to 9 pct, to (100) oriented tungsten single crystals increased the proportional limit stress and decreased the flow stress and the rate of work-hardening. In addition, while deformation in unalloyed (100) oriented crystals apparently involved both (110)100) and (112) slip, crystals with rhenium contents of 5 andpct or more deformed primarily by (112) slip. The mechanism by which high and low rhenium additions affect the mechanical properties of tungsten is still not well-established. The present investigation was undertaken to determine by transmission electron microscopy the effects of low rhenium additions, 2 and 9 pct, and a high rhenium addition, 24 pct, on dislocation substructure in the early stages of deformation of polycrystalline electron-beam-melted tungsten. Unalloyed tungsten and a W- 3 pct Ta alloy were included for comparison. EXPERIMENTAL PROCEDURES Materials. Triple electron-beam-melted tungsten, W-2, 9, and 24 pct Re, and W- pet Ta were used for this investigation. Chemical analyses of the cast ingots are given in Table I. A description of the starting metal powders and melting and fabrication pro-cedures for unalloyed tungsten and the W-Re alloys is reported.5 The W-3 pet Ta alloy was processed in a similar manner. Compression specimens measuring 0.300 in. (7.6 mm) in length by 0.130 in. (3.3 mm) in diam were machined from swaged rods. All alloy specimens were annealed in a vacuum of 8 x 10- 6 Torr (10'2iVper sq m) for 1 hr at 3600°F (2255°K). The recrystallized grain size ranged from 0.06 to 0.08 mm diam for the alloy specimens. Unalloyed tungsten was annealed at 2400° F (1589°K) for 1 hr to produce a recrystallized grain diameter of approximately 0.12 mm. Specimens were electropolished in a 2 pet NaOH solution to a diameter of 0.125 in. (3.18 mm) to remove surface notches resulting from grinding and to improve reproducibility of t data. The ends o the compression specimens were ground flat, parallel to each other, and perpendicular to the longitudinal axes with 4/0 emery paper. Compression Tests. The compressive stress-strain apparatus used for compression tests is described in detail by Stearns and Gotsky.9 Room-temperature compression tests were conducted at a crosshead speed of 0.01 in. per min (0.25 mm per min).

Jan 1, 1969

By D. Webster

It has been found that cold work and annealing treatments greatly retard subsequent grain growth and re-crystallization in thoria-dispersed nickel and NiCr. It is suggested that this is due to cavities which form at the particle-matrix interface durilzg cold work. Some of' the cavities formed are stable at elevated temperatures and prevent the mouement of large-angle grain boundaries. The movement of these boundaries at elevated temperatures is known to start recrystal-lization and when they are pinned by voids recrystal-lization is made more difficult. TD Nichro,me had a maximun resistance to recrystallization when the initial structure was coarse-grained and had a low dislocation density. A precipitation reaction occurred between 700° and 1200° F in cold-worked TD Nichrome. It has been shown by Grant and his coworkers1-3 that a large part of the strength of dispersion-hardened materials is a result of the cold-worked structure produced during fabrication. In a comparison of the strength of cold-worked copper with and without an oxide dispersion, Grant4 has demonstrated that there is little difference in strength at room temperature. The function of the dispersion is essentially to maintain the cold-worked structure at higher temperatures than is possible in the base material. The dispersion accomplishes this by making recrystallization more difficult. The mechanism by which this is achieved is discussed in this paper. The fabrication history of the material has been found to greatly influence recrystallization behavior and this aspect is discussed in some detail. I) MATERIAL Three different thoria-dispersed materials were examined. 1) DuPont 2 pet thoria-dispersed nickel (TDNi) in 0.050-in. seeet. Thoria particle size is in the range 100 to 2500A. 2) DuPont 2 pct thoria-dispersed nichrome (20 pet Cr, 80 pct Ni) (TDNiC) in 0.125-, 0.060-, and 0.040-in. sheet. In the as-received condition these sheets have

Jan 1, 1969

By P. R. Sahm, T. V. Pruss, D. A. Gandolfo

Cb 3 Sn powders were hot-pressed to estahlish densi-fication conditions and assess the possible use of such compacts in multiphase structures with ceramic or magnetic inclusions. Superconducting transition temperatures, Tc, were measured as a function of powder particle size, pressing temperature, and second-phase admixtures. The highest transition temperatures were found in coarse powder (5 to 500 u) compacts and were only weakly depended on pressing temperatures up to 1200°C. Fine powders (below 5 p), however, both single-phase CbsSn and Cb3 Sn-composites, showed a stronger dependence on hot-pressing temperatures. While Al2 O3 phase admixtures did not affect T, much more, a Pronounced T, degradation was observed upon the addition of ferrimagnetic Fe2 Mno. 5 Zno.5 O4 powders. Likewise, critical current densities, Jc, at 4.2° K were lowered appreciably in the ferrite doped samples, whereas the neutral A1203 inclusiow gave slightly improved Jc values. MULTIPHASE structures in electronically active materials have recently gained in interest as pointed out by Galasso in a review article.' In superconductors the most widely reported group are eutectic alloys which have been mostly investigated with respect to the proximity effect.2"4 In addition, "artificial eu-tectics", for example in the form of mercury-vycor glass sponge5 or fine niobium wires imbedded in a copper matrix,= have been prepared to attain higher critical fields and critical current densities. The idea was to enhance flux pinning phenomena by second-phase inclusions or ho1es. 7 Flux pinning should also be possible by the introduction of insulator inclusions into a superconducting matrix. Ceramic-metal combinations are most easily produced by hot pressing (= pressure sintering), as it permits an almost unlimited selection of material combinations. Cb 3 Sn has been prepared by vapor phase growths or in the form of thin films. Large compacts must be sintered,1° however, and normally present difficulties. At temperatures below 1350°C insufficient densities are obtained and at higher temperatures the loss of tin due to dissociation upsets the stoichiometry. Hot pressing is a natural approach to circumvent the problems, since one can obtain satisfactory densities despite low sintering temperatures. This work was mostly concerned with establishing conditions to hot press Cb3 Sn and Cb3 Sn multiphase structures (= composites), because no data are presently available, and to evaluate these with respect to their transition temperatures. However, a few measurements on critical current densities were also carried out, in particular to assess the value of ferrimagnetic inclusions. I) EXPERIMENTAL PROCEDURE The experimental procedure involved the preparation of feed material and powders, hot pressing, and evaluation of the resulting ingots. As no attempts were made to synthesize Cb3Sn from the elements during hot pressing, feed material had to be produced. For this purpose, a stoichiometric Cb-Sn powder mixture was compacted into a 3-cm-diam ingot (80,000 psi) and then inserted into a quartz tube and evacuated. Rf heating was employed. Above the tin melting point (230°C) liquid tin was forced out of the ingot, but was pulled back by capillary action after approximately 0.5 hr of continuous pumping at 700°C. Thus, it appears that evacuation at this temperature caused desorption of impurity gas creating wetting surfaces which, later on, favored alloying at relatively low temperatures. After a presintering period of 17 hr at 800°C, the quartz tube was tipped off and sealed into another such larger-diameter tube which, in turn, was connected to a pump system. This configuration permitted a temperature treatment at 1400°C, carried out for 65 hr, without collapsing of the glass walls or unfavorable chemical interaction of Cb3Sn with the quartz. The resulting material was

Jan 1, 1969

By Robert D. Pehlke, Weldon L. Daines

The reduction of manganese oxide from a basic slag by silicon dissolved in liquid iron at steelmaking temperatures was studied to determine the rate-controlling step for the process. The experiments were carried out under an argon atmosphere in a resistance-heated vertical-tube furnace. The two liquid phases, slag and metal, were held in zirconia crucibles. Sampling and chemical analysis of the slag phase led to time-concentration curves for the system. Results obtained by varying parameters such as temperature, stirring rate, concentration, and melt geometry defined the limiting reaction mechanism. The reduction of manganese oxide by silicon is a fast reaction and reached equilibrium within 90 min. The rate of stirring has a marked effect on the reaction rate, while, on the other hand, the effect of temperature is very small. This identifies the rate-controlling step as diffusion rather than interfaciul chemical reaction. The variation of other parameters revealed that a) diffusion of manganese in the iron phase is the slow step, b) the value of D/6 for manganese in iron at 1550°C is 7x 10-4 cm per sec, c) the energy of activation for the apparent rate constant is 7 kcal per mole, and d) increasing the amount of silicon in the iron decreases the diffusion coefficient of manganese. THE equilibrium relations pertinent to the reduction of manganese oxide from a steelmaking slag by silicon dissolved in liquid iron have been studied, but little is known about the mechanisms that control the rate of the process. The purpose of the present investigation was to study the rate of reduction by silicon and to determine the rate-limiting step. The effects of stirring rate, temperature, composition, and melt geometry were investigated as a means of identifying the controlling step. On the laboratory scale, relatively little work has been done in the area of slag-metal kinetics, primarily because of the problems confronted in attempting to contain liquid slags and metals in laboratory crucibles at steelmaking temperatures. Since graphite is an ideal material for a crucible, several investigations have been carried out on the reduction of various oxides from a slag by carbon in graphite-saturated iron and on the transfer of sulfur between a slag and graphite-saturated iron. Most of this work has been performed in induction furnaces. Studies where the container was not graphite are extremely limited. A single kinetic study of manganese transfer between molten iron and basic slags was carried out by Sano, Shiomi, and Matsushita.' These investigators prepared calcium oxide and titanium oxide crucibles to contain the two-phase system. Only a few experiments were carried out and the results had to be treated qualitatively. Despite the paucity of kinetic data, a large quantity of information is available in the literature concerning the thermodynamics2-12 and physical properties'3-21 of the slags containing manganese oxide and the dilute liquid iron alloys containing manganese and silicon which were involved in this research program. EXPERIMENTAL METHOD A vertical-tube resistance-heated furnace was used in this investigation to study the slag-metal reaction Although most previous slag-metal studies were carried out in induction furnaces, a resistance furnace has several advantages including better control of temperature and stirring rate. Hence, a resistance furnace was selected for this study, and its design is shown schematically in Fig. 1. Slip-cast, fine-grained, low-porosity, lime-stabilized cubic zirconia crucibles were used for the kinetic experiments. The crucibles were 4 1/2 in. high and 2 1/8 in. OD with a 1/16-in. wall. The crucibles were only slightly

Jan 1, 1969

By N. J. Grant, B. C. Giessen, U. Wolff

With the aid of the splat-cooling technique of rapid quenching, metastable alloy phases based on antimony ad bismuth have been prepared. At room temperature, simple cubic phases were found in the Sb + Au, 56 + Yd, and Sb + Ni systems. Another phase was retained in the Au-Bi system at -190°C; in this systent, a microcrystalline phase and a rhombohedrally distorted phase were also observed. The crystal chemistry of these phases is discussed in terms of their valence electron concentration range. A remarkable five-step Phase sequence was found upon heating and equilibration of certain metastable Au-Bi alloys. USING the splat- cooling technique of rapid quenching from the liquid,' a large number of metastable intermediate alloy phases have been prepared in recent years. Thus, Hume-Rothery phases of the hexagonal type based on the valence electron concentration have been produced in systems where they are missing in equilibrium, e.g., Ag-Ge 1 or AU-Sb. 3 In a comprehensive study of metastable alloys based on tin, simple hexagonal metastable y phases were found, raising the total of stable and metastable y phases from 3 to 13. 4 In the In-Bi system, five new metastable intermediate phases were retained.' In most cases, the new metastable phases have some crystal chemical characteristics in common: a) They have rather simple, elementlike structures with few atoms per unit cell, e.g., y phase,4'5 or the metastable primitive cubic phases in the Ag-Te and and Au-Te systems.= b) Their structures are often related to those of the terminal phases, or to elements that are straddled in their position in the periodic table by the constituent elements; this is the case for metastable ß (In-Bi) with the structure of white ß Sn,' or metastable a (Cd-sn). 4 c) They seem to represent the crystal structures appropriate to certain average group number (AGN) ranges in which no or few single-phase structures exist in equilibrium. These average group number ranges can probably be equated in the case of many elements of the Ba(Zn)-Bs(As) groups with the averaged valence electron concentration. In the present work, the splat-cooling technique has been applied to the alloys of antimony and bismuth. In equilibrium, neither element forms intermediate alloy phases with other B elements from groups Bl(Cu) to B4(Si) that contain more than 66.7 at. pct of Sb or Bi, respectively, e.g., AUSb 2. 7 Thus, antimony- or bismuth-rich phases, which might be closely related to antimony or bismuth, and which would reflect struc- tural changes occurring on alloying with small amounts of addition elements, do not exist. Also, the terminal solubility of antimony and bismuth for all B metals is very small. It was therefore of interest to investigate the influence of enforced, nonequilibrium solid solution of addition elements in antimony and bismuth on their crystal structures. It was found that additions of group B 2-B4 metals act distinctly differently than additions of group T 10 and B1 metals. The latter set of additives will be treated here. EXPERIMENTAL TECHNIQUES Alloy preparation and splat-quenching followed closely the procedures described in Refs. 1, 4, and 5; they consisted of the preparation of master alloys from high-purity starting materials (99.99+ pct) and blast-atomizing of 20-mg quantities onto copper sheets. The resulting approximately 1 to 5 u thick foils were investigated by X-ray diffraction. The cooling rates obtained are of the order of 107 to 10 8 C per set,'" causing solidification to proceed at a rat; of approximately 100 cm per sec.' Powder patterns of the resulting fine-crystalline materials were taken with filtered CuK, radiation. For antimony alloys the substrates were held at room temperature and for bismuth alloys at -190°C both during splat foil deposition and X-ray investigation. Annealing treatments at several

Jan 1, 1969

By G. D. Rieck, G. H. G. Vaessen, D. L. Vogel

Both doped and undoped tungsten single crystals exhibit hardness anisotropy with respect to the direction of testing in each of the crystallographic phes investigated. The hardness anisotropy of undoped single-crystal tungsten is rather pronounced in (001) and (110) planes but very minor in (111) planes. The anisotropy in (122) planes of the doped and drawn tungsten after recrystallization is in accordance with a previously published concept of a stringlike distribution of the doping material in the metal. ANISOTROPY in mechanical properties of single-crystal tungsten was investigated by Rose et al., Garlick and Probst,2 and Beardmore and Hull. 3 Although data on the Vickers microhardness of tungsten have been published (see, e.g., Boosz 4 and the references cited by him), no data on the microhardness anisotropy are available. We report, therefore, some of our own results on the microhardness and its anisotropy. The microhardness has been determined of the following samples. A) Polycrystalline tungsten samples taken from: 1) powder metallurgical tungsten "normally" doped with potassium-silicon-aluminum oxides (final contents inppm: K, 100; Si, 100; Al, 20; Cr, 20; Fe, 50; Mo, 400; Ni, 10) and in the form of: a) a 10-mm-diam swaged ingot annealed at 1600°C, the grain sizes varying between 15 and 250 p; b) a sheet rolled at about 800°C and recrystallized at 2000°C7 the grain sizes varying between 15 and 150 p; c) a 2-mm-diam swaged rod, as-worked, with elongated grains (average diameter of about 25 , lengths up to 1 mm); 2) undoped electron-beam-melted tungsten with very large grains (contaminations in ppm: K < 10; Fe < 20; Cr < 10; Cu < 0.1; Ni not detectable; inter-stitial~ not determined). B) Single-crystal samples taken from: 1) pure tungsten grown on a Pintsch wire by the van Arkel procedure (main contaminations inppm: Mo, 100; Si < 10; Cu and Fe, 2; A1 < 2; interstitials not determined); 2) zone-melted undoped tungsten (analysis as under A2); 3) large crystals in secondary recrystallized tungsten

Jan 1, 1969

By M. T. Hepworth, A. K. Stewart

Iron containing 0.1 pct A1 and -0.9 pct P by weight was internally oxidized in the temperature range 900° to 1300° C, where the bcc structure is stabilized by phosphorous. By measuring the depth of penetration of oxygen with time in an internally oxidized zone for an imposed surface oxygen potential, oxygen permeability was determined. The dgfusion coefficient of oxygen in iron was then calculated using known solubility data, yielding the expression: where Do is the diffusion coefficient of oxygen in bcc iron in sq cm per sec and T is temperature in OK. RECENTLY Hepworth, Smith, and Turkdoganl measured the diffusivity of oxygen in bcc iron and reported the temperature dependence of diffusivity from data determined in the a, and 6 temperature ranges. Subsequently Swisher and Turkdogan&apos; have measured the diffusivity of oxygen in fcc iron. Internal oxidation techniques were employed by these investigators and in this current study. The analysis of this technique is developed by wagner3 (presented in English by Hauffe4 and Rapp 5). In this present study bcc iron stabilized by phosphorous was used to determine oxygen diffusivity in the temperature range 900° to 1300°C. Meijerin 6 has studied oxygen permeability in this temperature range using bcc iron stabilized with 5 pct Sn. Other inves- tigators who have studied oxygen permeability in bcc iron at other temperatures are Schenck et al., 7 Bohen-kamp and Engell, 8 and Bradford. EXPERIMENTAL Electrolytic iron of 99.99 pct purity was alloyed to contain 0.897 pct P and 0.093 pct Al. The maximum weight percent phosphorous required to stabilize bcc iron between 910" and 1392°C is 0.51 pct as determined by Haughton,10 0.42 pct by Roquet and jegaden," and 0.58 pct by vogel,12 with the latter value preferred by Hansen.13 Microprobe analysis indicated that there was no segregation of the phosphorous either before or after permeability studies; therefore, the quantity of phosphorous added was assumed to be sufficient to stabilize the bcc structure. Furthermore, the permeability results of studies on this alloy agreed substantially with interpolated values from previous data on bcc iron.&apos; An ingot of the Fe-P-A1 alloy was hot-rolled to a l-in.-thick slab. Specimens were machined to dimensions: 13/8 by $ by 1/4 in. The experimental apparatus and procedure used have been described before.&apos; A constant oxygen potential was established by passing argon and hydrogen through a column of oxalic acid dihydrate, which has a water vapor pressure which is well-known as a function of temperature. Slab specimens were exposed to a gas mixture sufficiently lean in oxygen to prevent the formation of a surface oxide for predetermined temperature for selected times. The specimens were then quenched, sectioned, and examined metallo-graphically. All quenched specimens were iron-plated to provide protection from the outside sample edge during polishing. Fig. 1 shows a typical microstruc-ture for a specimen oxidized at 953°C for 48.00 hr at a water vapor-to-hydrogen pressure ratio of 0.20. DISCUSSION AND RESULTS The following equation was derived by Hepworth et al.&apos; from Wagner&apos;s kinetic expressions for internal oxidation:

Jan 1, 1969

By R. E. Fryxell, E. C. Duderstadt, P. K. Conn

Permeation rates for nitrogen through are-cast tungsten were measured in the temperature range 1800° to 2600°C at nitrogen pressure differentials of 1.0 and 0.1 atm. Gas chromatography was used to measure the quantities of nitrogen which permeated through 0.26-and 0.53-mm-thick membranes. Permeation rates were proportional to the difference between the square roots of the nitrogen pressure on each side of the membrane and inversely proportional to membrane thickness, indicating that atomic nitrogen was the difjusing species and that diffusion was the rate-limiting step of the process. Permeation coefficients calculated from the rates may be represented by the equation: where P is expressed in the units cu cm (stP)-mm per 1/2 sq cm-min-atm"&apos; and 70.0 * 0.8 is the activation energy in kcal per mole of permeating species. In a previous paper&apos; permeation rates were reported for hydrogen and for oxygen through tungsten. The permeation cells used for the hydrogen measurements were suitable for measuring nitrogen permeation under similar conditions, so the study was extended to include nitrogen. Permeation rates of nitrogen through the polycrys-talline arc-cast tungsten membranes were measured in the temperature range 1800" to 2600°C using two membrane thicknesses and two nitrogen pressure differentials. Permeation coefficients were calculated and the activation energy of the process determined. THEORY For diatomic gases which dissociate prior to diffusion, the quantity of gas which permeates through a membrane or wall at an elevated temperature where bulk diffusion is the rate-limiting step of the process is given by the equation: where: q = total amount of gas permeating a membrane, P = temperature-dependent permeation coefficient, A = area of membrane, t = time, p1 = gas pressure of high-pressure side, p2 = gas pressure of low-pressure side, and d = thickness of membrane. When bulk diffusion is the rate-controlling step, and the solubility of the gas obeys Henry&apos;s law, a further relationship is that, for any given temperature and pressure, the permeation is the product of diffusivity and the amount in solution. The permeation coefficient, P, is temperature-dependent according to the equation: where: Po = permeation constant, Q = activation energy, R = gas constant, and T = absolute temperature. EXPERIMENTAL PROCEDURES Cell Design and Experimental Apparatus. Two of the permeation cells used for the previous measurements of hydrogen permeation are shown in Fig. 1. Each consisted of a cylindrical chamber divided into two parts by a permeation membrane fabricated from high-purity (>99.9 pct W) wrought tungsten sheet made from vacuum arc-cast tungsten. The membrane in one cell was 0.26 mm thick and the other was 0.53 mm. The fabrication of these cells was described previously.&apos; The permeation cells were mounted vertically in a high-temperature tungsten resistance furnace and the membranes and the center portions heated to test temperatures. Temperatures were measured by sighting an optical pyrometer on the edge of the membrane through a small hole in a tungsten plate which was fastened to the side of the cell. This arrangement provided an approximate black-body condition and eliminated the need for emittance corrections. Appropriate corrections were made for the quartz window through which the temperatures were measured. Argon gas flowed through the 10-liter volume of the furnace at the rate of 4.7 liters per min. An impurity

Jan 1, 1969

By A. Totani, S. Nakajima, H. Okazaki

The phase diagram for the SnTe-SnSe system has been studied in the temperature range from 300° to 900°C by differential thermal and quenching techniques. The X-ray measurements were made on quenched specimens. High-temperature diffraction was also made to study the phase transition in SnSe. The system is proved to be of a eutectic type in which no intermetallic compound exists. The eutectic point is at the composition SnTeo.55 Seo.45. the eutectic temperature being 755°C. Solid solubility limits are SnTeo.6Seo.r and SnT eo. 3s Seo.6s at the eutectic temperature, and change almost linearly to SnTeo.aaSeo.lz and SnTeo.18 Seo.az as temperature decreases to 300°C. It was shown that the SnSe phase has a phase transition of the second order at about 540°C and that the transition temperature decreases with increase of the SnTe content. THERMOELECTRIC properties of tin telluride (SnTe) and tin selenide (SnSe) have been studied extensively in recent years. The variation of physical properties with composition could be of interest if these compounds form an appreciable crystalline solution. The purpose of present investigation is to confirm the formation of crystalline solution or intermetallic compound, if any, and to establish the phase diagram for this system. The crystal structure of SnTe is NaCl type with a cubic unit cell1 (a = 6.313A). The crystal of SnSe having an orthorh2mbic unit cellz (a = 11.496, b = 4.1510, and c = 4.4437A) is isomorphous with tin sulfide (SnS) which has a distorted sodium chloride structure. It has been known that SnSe has a phase at at 540°C; the transition has been assumed to be of the second order. As far as we know, only two studies on the SnTe-SnSe pseudobinary system have been reported. The conclusion obtained in these papers is that, in the composition regions near SnTe and SnSe, the system forms a crystalline solution of the SnTe structure and the SnSe structure, respectively, and that, in the intermediate region, both phases coexist. However, neither the variation of the solid solubility vs the temperature nor the liquidus and solidus were investigated. Hence present writers have attempted to determine the phase diagram of the system by differential thermal analysis (D.T.A.) and X-ray diffraction. EXPERIMENTAL Sample Preparation. Starting materials, SnTe and SnSe, were prepared by the direct fusion of commercially available high-purity (99.999 pct) elements. Stoichiometric amounts of each couple Sn-Te or Sn-Se were weighed into a clear fused silica ampule. After evacuation to a pressure below 10-3 mm Hg, the am- pule was sealed, and annealed at 900°C for 5 hr. The melt was quenched in water. X-ray analysis confirmed the formation of a single phase of SnTe or SnSe. The other samples, SnTel-,Sex were synthesized from these SnTe and SnSe by mixing them in the required ratio, followed by annealing at 900°C and quenching. These samples were used directly for D.T.A. For X-ray measurements, samples were annealed at 700°, 600°, or 500°C for 100 hr or at 300°C for 150 hr, and then quenched in water. It was found that the lattice constants of the SnTe phase annealed for 150 hr at temperatures above 500°C did not differ from those annealed for 100 hr at the same temperatures. However the X-ray phase analysis showed that at 300°C the annealing for 150 hr was necessary to attain a true equilibrium state. D.T.A. The solid-liquid equilibrium temperature was determined from D.T.A. measurements. The sample was sealed in an evacuated silica tube and molybdenum powders sealed in an another tube were used as a reference material. The sample and the reference tube were placed in a nickel block and were heated from room temperature to 900°C at a rate of 3°C per min and then cooled down at the same rate to 600°C. Thermocouples for these measurements were Pt-Pt. Rh (10 pct) and the error of temperature measurements was within + l0C. D.T.A. curves were obtained on a two-pen recorder and an automatic controller (PID type) was used for the program of heating and cooling. When temperature reaches the solidus from the low-temperature side, there appears an endothermic peak. The solidus temperature was determined by extrapolation of the straight portion of the starting flank of this peak to the base line. In a similar way, the liquidus temperature was determined from an exothermic peak on D.T.A. cooling curve. In the case of supercooling, if any, its degree can be estimated from the magnitude of the abrupt temperature rise. X-Ray . X-ray powder patterns were taken by a diffractometer using CuK, radiation. Since the SnSe crystal is cleaved easily, the powders become flaky when SnSe-rich samples are ground in an agate

Jan 1, 1969

By W. O. Philbrook, R. H. Spitzer, F. S. Manning

The steady-state operation of an isothermal, counter-current reactor in which a mouing bed of hematite particles is reduced by hydrogen has been modeled mathematically using a generalized single-particle kinetic formulation for topochemical reduction with formation of the intermediate oxides, wustite and magnetite. Reduction prof iles have been generated for various oper- REDUCTION of iron ore, as practiced industrially, approaches counter current, granular-bed operation. The total process is extremely complex. Quite under- ating conditions selected to demonstrate the influence of major variables such as gas and solid flow rates, bed length, and particle size. These profiles illustrate , among other things, that the reducing-gas requirement in a countercurrent bed hinges upon the iron-wüstite equilibrium or &apos;pinch-point" in much the same way as in a staged reactor. standably, nearly all research has been focused on reduction of single particles of oxide under controlled conditions. While this approach simplifies the problem by eliminating interparticle interactions, the remaining intraparticle transport and kinetic processes still constitute a most formidable challenge. Only within the last few years has knowledge of single-particle reactions been developed sufficiently to make modeling of counter current-bed reduction a realistic and useful study of process behavior. The authors have analyzed1"3 extensive laboratory

Jan 1, 1969

By D. H. Baldwin, R. E. Reed-Hill

Six compositions of polycrystalline ZY-0 alloys, containing up to 4.2 at. pct 0, were tested in tension between 77° and 600° K. The data obtained from each of the compositions corresponded closely to a rela-ion between yield stress and absolute temperature of the form In s/so = BT, where oo is the yield stress extrapolated to zero degrees and B is a constant. In agreement with others who have observed this relationship, it is shown that the activation energy may be expressed as Ho In so/s. In the present specimens Ho is approximately 18,000 cal per mole and is apparently independent of temperature and composition inside the limits of the investigation. It is also demonstrated that this form of activation energy cowesponds to a strain rate sensitivity parameter RT/Ho. Oxygen was also noted to have an effect upon the operative deformation mechanisms. With increasing oxygen concentration there was an increased tendency to observe both nonbasal slip and cross-slip phenomena. Oxygen does not seriously inhibit twinning more than it does slip. Twins were observed in all specimens tested. It is becoming increasingly evident that interstitial atoms in solid solution are able to interact strongly with mobile dislocations. Stein, Low, and seybolt,&apos; have shown that, if the carbon concentration in bcc iron is lowered below the solubility limit, its flow stress temperature dependence is markedly reduced. This suggests that carbon atoms in interstitial solid solution may be responsible for the pronounced temperature dependence of the flow stress normally observed in iron. This view has recently been challenged by Leslie and sober2 who observed a strong flow stress temperature dependence in iron to which a trace of titanium had been added in order to remove carbon atoms from solution. Since the interstitial concentration must be reduced below approximately 1 ppm in order to produce a pronounced effect on the flow stress temperature dependence,&apos; studies of the effect of interstitials on the flow stress in iron necessarily involve serious experimental difficulties in alloy preparation. There are other metals, however, in which strong effects of interstitial solutes upon both the flow stress and its temperature dependence are observed. Of particular significance is zirconium which, according to Domagala and Mcpherson, 3 is capable of dissolving 28.6 at. pct O. The O-Zr alloy system is an almost ideal system for studying the interaction of interstitial atoms with deformation modes since it is possible to form alloys capable of study over an extensive range of compositions. Mills has made such a study using single crystals oriented primarily for single prismatic slip4 and has found an effect of oxygen concentration on the flow stress temperature dependence analogous to that observed in iron due to carbon by Stein, Low, and Seybolt. The present paper is specifically concerned with the effect of oxygen on deformation in polycrystalline zirconium. Although plastic flow in this type of specimen is much more complex than that reported for the single-crystal work, and involves both slip (on several different types of planes) and mechanical twinning, the results of this investigation are in general agreement with the single-crystal observations concerning the effect of oxygen on the temperature dependence of the flow stress. In addition, they also demonstrate that oxygen affects the acting deformation systems. This is in contrast to single-crystal results4 that showed only single slip on a prism plane. EXPERIMENTAL PROCEDURE Material. High-purity hot-rolled zirconium strip, 0.2 in. thick by 4 in. wide, of 0.10-mm average grain diameter, was used for forming alloys. It was obtained from the Carborundum Metals Co., Akron, N.Y., whose analysis indicated the major impurities were, in wt ppm: Hf, 540, C, 145; Fe, 100; and 0, <80. The plate texture was similar to a wire texture, with basal planes generally parallel to the rolling direction and basal poles randomly distributed about the rolling direction. The heat treatments described below did not appreciably alter the basic texture. specimen Preparation. Small threaded-end tensile specimens were machined from the plate with axes perpendicular to the rolling direction. These transverse specimens had gage sections 1 in. long by 0.060 in. in diam. The small gage section diameter was dictated by the fact that the alloys were formed by dif-

Jan 1, 1969

Jan 1, 1969

By M. J. Marcinkowski, E. N. Hopkins

An investigation has been made of the ß(fcc) — a(hexagonal) transformation which occurs in lanthanum using both electrical resistivity and transmission electron microscopy techniques. It has been shown that the ß phase can be retained below the transformation temperature by rapid quenching but that the sample immediately begins to transform to the a phase. The transformation is observed to nucleate in the vicinity of inclusions. Based on the above observations, a detailed model of the transformation has been advanced which involves the nucleation of an extrinsic stacking fault bounded by a pair of Shockley partial dislocations in the vicinity of some heterogeneity, i.e., an inclusion. The stress field of the resultant dislocation pair acts to nucleate extrinsic faults in adjacent planes and leads quite naturally to the B-a conversion with a minimum of strain energy induced in the crystal. LANTHANUM possesses an fcc structure ß) (8) upon cooling transforms to a hexagonal modification (a) in much the same way as cobalt. The one exception, however, is that the stacking sequence of the closest packed planes in a La is ABAC ABAC, and so forth,1 whereas in cobalt it is ABAB, and so forth, i.e., hep. Mainly on the basis of transmission electron microscopy techniques, there seems to be little doubt that the 0 — a transformation in cobalt involves a dislocation mechanism2 although its exact nature still remains obscure. Although the ß - a transformation in lanthanum is somewhat more complex than that occurring in cobalt, it was thought that its very uniqueness would be helpful in understanding fcc — hexagonal transformations in general. Such a general understanding of these transformations is important since they represent what are perhaps the simplest of the martensitic class of transformations. The experimental techniques used were those of electrical resistivity and transmission electron microscopy. EXPERIMENTAL PROCEDURE The lanthanum used in this investigation was prepared by the calcium reduction of lanthanum fluoride in a tantalum crucible under an argon atmosphere as described by Spedding et al. The residual calcium was removed by vacuum remelting in a tantalum container. Portions of the metal were then analyzed by emission spectroscopy as well as vacuum fusion. The amounts of the various impurities that were found are listed in Table I. A portion of the lanthanum ingot was swaged at room temperature into 0.030-in.-diam rod for the resistivity samples while the remainder was rolled into 0.010-in.-thick sheet for the transmission electron microscopy phase of this investigation. In order to eliminate the plastic deformation induced in the samples during fabrication, they were sealed in evacuated tantalum lined quartz capsules and annealed for 1 hr at 700° C. Specimen resistances were measured using the conventional "four-wire" technique described by MacDonald, 4 employing a type K-3 Universal Potentiometer and a standard 0.001-ohm resistor, both manufactured by Leeds and Northrup Co. By taking into account all of the possible errors in the apparatus, it was felt that the absolute resistivities of the approximately 0.87-in.-long specimens measured are reliable to 3 pct. Resistances from room temperature to 700°C were measured using a vacuum furnace. In order to avoid sample contamination by the thermocouple, chromel-alumel leads were spot-welded into a tantalum shield which in turn was welded to the lanthanum specimen. Resistances below room temperature were obtained by transferring the sample to a helium gas-filled quench tube and slowly dripping liquid nitrogen into a surrounding dewar flask. A steady reduction of temperature to about —190°C was completed in about 23 hr, and the resistances were measured at various temperature intervals. As will be shown shortly, rapid quenching from above about 350°C was sufficient to suppress the B -a transformation initially but subsequent annealing at lower temperatures leads to a partial ß --a conversion. To investigate this aspect of the transformation, the samples were suspended in the hot zone of a helium-filled furnace from which they could be rapidly dropped into the quench tube mentioned previously which was now

Jan 1, 1969

By Ronald R. McNaughton

The most recent group of papers on the general subject of lead smelting were published in AIME Transactions, vol. 121, in 1936. The lecture deals with changes which have taken place in the Past 30 years in this industry. The subject matter covers the essential steps of charge preparation, sintering, blast furnacing, dross treatment, refining, and slag fuming together with the subsidiary or associated activities of analytical procedures, dust and fume collection, maintenance, and hygiene. IN 1936 the AIME published Transactions, vol. 121, entitled "Metallurgy of Lead and Zinc". In the preface to this volume the chairman of the Committee on the Reduction and Refining of Lead and Zinc, Carle R. Hay ward, said in part: ... since the World War few papers of major significance have appeared on the production and refining of lead and zinc, although many improvements in technique have been made, which have attracted little attention because they were merely developments of existing practice. Other changes of a more radical nature have also been made, but... they have been given little publicity. It seems appropriate, therefore, at this time that the AIME should sponsor a volume on lead and zinc metallurgy... . That the publication of this compilation was timely is attested by the rapidity with which the surplus stock was depleted. It has now become a collector&apos;s item. Although a comprehensive monograph on the occurrence, extraction, refining, and uses of zinc was published by the American Chemical Society in 1959,&apos; one could almost repeat Professor Hayward&apos;s words to describe the present situation in the literature of lead reduction and refining. So it is my intention today to discuss briefly some of the changes and improvements which have taken place in the metallurgy of lead in the interval since the publication of vol. 121. The lead blast furnace, which made its appearance in America about 1870, is still dominant in the reduction field. However there are other reduction methods in use today in special situations. In those rare circumstances where the material to be treated is very high grade, consideration might be given to the Bolidens electric furnace method2 or the Lurgi self-fluxing process3 or possibly to the rotary ore hearth. Each of these latter three processes makes use of the roast-reduction reactions with the result that fuel require-

Jan 1, 1969

By W. F. Hosford, E. W. Kelley

By testing polycrystalline specimens from textured plates which had Previously been used to provide materials for growing single crystals, it has been possible to relate the plastic anisotropy of textured materials to the deformation behavior of single crystals. The deformation studies have been conducted at room temperature on textured polycrystalline magnesium and binary Mg-Th and Mg-Li alloys. Variously oriented specimens of the textured materials were deformed in plane-strain compression and in uniaxial tension and compression. The stress-strain curves are similar in their general jorm of anisotropy and stress levels to those obtained on single crystals of the same alloys. The degree of anisotropy is lower, however, in the polycrystalline materials and correlates with the intensity of the basal texture. Yield loci for the textured materials appear reasonable in terms of the deformation mechanisms, and deviate sharply from the form predicted by the Hill analysis for aniso-tropic material. A N earlier study1 of single crystals has shown that magnesium and magnesium alloys with thorium and with lithium deform at room temperature primarily by basal slip, {10i2) twinning, and (1011) banding. The (10i1) banding mode is a combination of {10ll) twinning followed by (1012) twinning and basal slip within the doubly twinned material.2, 3 Magnesium with lithium can also deform by {1010)(1210) prism slip.1&apos;4&apos;5 Still other deformation modes have been reported for magnesium6-11 but these are considered to play a minor role in room-temperature deformation. In a polycrystalline material, plastic deformation must occur in the individual grains through the operation of one or more of the various deformation modes. Because the critical shear stress for basal slip is very low compared to the activation stresses for the other deformation modes,&apos; basal slip accounts for much of the deformation in the polycrystalline aggregate. However, since there are only two mutually independent basal slip systems, and because five independent systems must be active for an arbitrary shape change in any material,&apos;&apos; modes other than basal slip must account for some of the strain. The deformation of textured magnesium, like that of other hcp metals, must be controlled by the same mechanisms observed in single crystals. In strongly textured material, the form of the anisotropy should be similar to that of single crystals, and the degree of anisotropy should depend on the intensity of the texture. EXPERIMENTAL PROCEDURE The anisotropy of deformation was investigated through the use of plane-strain compression tests, as well as uniaxial tension and compression tests. Materials. Test specimens were cut from the three textured plates of magnesium which had previously been used to provide material for single crystals.&apos; These plates, furnished by Dow Chemical Co., had been reduced about 80 pct during the process of being hot-rolled to their final 1/4-in. thicknesses. The plates had the three respective compositions, pure magnesium, Mg-0.5 wt pct Th (0.49 pct Th by spectro-graphic analysis), and Mg-4 wt pct Li (3.84 pct Li by chemical analysis). Impurities other than iron were less than 0.0005 pct Al, 0.01 pct Ca, 0.001 pct Cu, 0.0006 pct Mn, 0.001 pct Ni, 0.003 pct Pb, 0.001 pct Si, 0.001 pct Sn, and 0.01 pct Zn. Iron was 0.001 pct in the pure magnesium, 0.002 pct in the Mg-0.5 pct Th, and 0.014 pct in the Mg-4 pct Li. The textures of the three plates were determined by X-ray diffraction utilizing only the reflection technique out to an angle of 50 deg from the sheet normal. The resulting basal pole figures are presented in Figs. 1, 3, and 5. Grain sizes in the plates were ASTM number 4 in the pure magnesium and number 7 in each of the alloys. Plane-Strain Compression Tests. Plane-strain compression specimens approximately $ in. thick by 4 in. wide by $ in. long were prepared for each of the three compositions. These specimens were prepared in a manner similar to that used for the single-crystal specimens of the earlier study.&apos; All polycrystalline specimens were stress-relieved at 500°F for hr as the final step in their preparation for testing. The testing procedure was identical to that used for the single crystals, involving compression in a channel and using 2-mil Teflon film as a lubricant. The specimens were tested in six orientations of interest, these being the six combinations of the rolling, transverse, and thickness directions of the material serving as loading, extension, and constraint directions in the plane-strain compression test. Each of the six orientations was assigned a two-letter identifying code. These are combinations of the letters (thickness direction), R (rolling direction), and T (transverse direction) with the first letter signifying the loading direction and the second letter the extension direction. For example, ZR specimens were compressed in the thickness direction while extension was permitted to operate in the rolling direction of the textured material. To facilitate comparison of the present work with that of the single-crystal study1 the orientations used for single crystals are given in Table I along with the polycrystalline orientations that most nearly correspond. To insure reproducibility, at least three duplicate

Jan 1, 1969

By M. T. Hepworth, T. P. Papazoglou

Hydrogen diffusion in hcp and bcc titanium in the temperature range 610° to 900°C was measured by reacting cylindrical specimens of high-purity titanium at constant temperature with small constant pressures of hydrogen of the order of a few Torr. In the range 0 to 6.7 at. pct H in hcp titanium, the diffusion coefficient D in sq cm per sec is given by: where T is in °K and R in cal per g-atom OK. Only three measurements of diffusivity in bcc titanium were made: at 900&apos; : the diffusivity in ß titanium was found to be 1.8 x 10-4 sq crn per sec. McQUILLAN1 has studied the constitution of the Ti-H system and reported the concentration of hydrogen as a function of pressure of hydrogen and temperature. He found hydrogen absorption was reversible and rapid at temperatures above 500°C in both crystallographic modifications, the a (hcp) phase and the ß (bcc) phase, with the latter phase stabilized by hydrogen additions. Wasilewski and Kehl 2 measured the diffusivity of hydrogen in hcp and bcc Ti-H alloys. For bcc alloys, they reacted cylindrical specimens of titanium with hydrogen gas at 1 atm pressure. They measured the rate of absorption of hydrogen isothermally on specimens ranging from zero hydrogen content when above the transformation temperature to hydrogen contents sufficient to stabilize the bcc phase when below the transformation temperature. By integrating Fick&apos;s second law for a cylindrical geometry, assuming a diffusion coefficient independent of composition, they calculated diffusivities as a function of temperature. In the range 650" to 1000°C their results in bcc titanium yielded the expression: where D is in sq cm per sec, T in OK, and R the gas constant in cal per g-atom-OK. Their studies on the hcp a phase were conducted by exposing long cylindrical titanium specimens to hydrogen at a sufficiently high pressure to establish a surface layer of fl phase 80 to 120 u thick for the duration of an isothermal experiment. Concentration profiles were then determined by hydrogen analysis from chips obtained upon machining quenched specimens. The diffusivity of hydrogen was then calculated yielding the expression: The present investigation was undertaken principally to redetermine the diffusivity data on a titanium by a direct absorption from the gas phase at sufficiently low hydrogen pressures to avoid the presence of a surface bcc phase and also to check the diffusivity data at low hydrogen concentrations in the bcc stmcture. EXPERIMENTAL PROCEDURE High-purity electrolytic sponge titanium (99.9 pct) of BHN 91 was arc-melted, forged, rolled, and machined into cylinders of final hardness, upon annealing, of BHN 92. Cylindrical specimens of two sets of dimensions were used: 1.524 by 2.931 cm and 1.905 by 3.663 cm diam and length, respectively. The experimental apparatus used for annealing specimens and for admitting known amounts of hydrogen at constant pressure is shown in Fig. 1. In a typical experiment, a specimen was lightly abraded with fine-grain silicon carbide, washed with water and detergent, and then thoroughly degreased with reagent-grade tri-chlorethylene and acetone. The specimen was suspended by a Chrome1 wire in the center of a quartz furnace tube, without contact with the tube, and heated to 925°C (as measured by a thermocouple adjacent to the specimen, outside the tube) for a period of at least 4 hr under a vacuum of from 10-6 to -7 Torr as measured by an ionization gage. The furnace temperature was then adjusted to the temperature chosen for the particular diffusion study and the specimen allowed to equilibrate thermally. Hydrogen was then ad-

Jan 1, 1969

By B. Chalmers, Stefan Wojciechowski

Rotary oscillation of the mold has been used to produce mechanical stirring of the melt during unidirectional solidification. Al-Cu alloys (1 to 4 wt pct Cu) were solidified to study the influence of alloy composition, temperature at which intensive cooling was initiated, and intensity of stirring on the temperature distribution in the sample, the resulting structure, and the copper microsegregation at the columnar to equiaxed transition. The Proposed explanation for the equiaxed solidification in stirred castings consists of the melting off of dendrite fragments, their partial remelting in hotter liquid, and the subsequent growth of the surviving part when the temperature of the melt is lowered. This may result in the formation of a crystal network, which can stop the growth of the columnar crystals and produce the equiaxed zone. It has long been known and many times affirmed that ultrasonic vibrations or relative motion of liquid and solid can significantly reduce the length of the columnar zone and refine the grains in the equiaxed zone in ingots and castings. Because of the technological importance of these phenomena many investigations have been conducted in which ultrasonic energy or mechanical vibration,1-6 electromagnetic stirring,7"10&apos;17 magnetic stirring,"&apos;12 or mechanical stirring13&apos;14 were used to produce the relative liquid-solid motion. More recently, the question of the importance of natural (or thermal) convection has been raised.15-l7 Several possible mechanisms have been suggested.l,8,18-20 They can be divided into two main groups. The first group includes such nucleation hypotheses as nucleation frequency enhancement due to cavitation at the mold wall or other surfaces; cavita-tion in the body of the liquid resulting from the pressure wave, or an agglomeration mechanism, which involves the formation of nuclei by the accretion of subcritical nuclei. The second group considers the grain-refining action to be due to crystal multiplication phenomena such as the removal of the dendrite fragments by viscous forces or by a high-pressure cycle following cavitation or by a melting-off process. Sbme recent investigations give good experimental support to the melting-off proposa1.21-23 The purpose of the present study was to examine the effect of mechanical stirring during the unidirectional solidification on the structure of alloy samples and on the solidification variables. The motion of the liquid was produced by rotary oscillation of the mold around its vertical axis.

Jan 1, 1969

By H. I. Aaronson, C. Laird

Cold rolling by 50 pct a A1-4 pct Cu alloy containing many 0&apos; plates has been found to accelerate markedly the transformation of 8&apos; to 0 upon further aging. Although the basic mechanism of this transformation remains unchanged by plastic deformation, the nuclea-tion kinetics of 8 become appreciably more rapid and also less dependent upon temperature. Particularly at lower aging temperatures, rounded idiomorphs replace several faceted rnorphologfes. The rates of growth of 9 idiomorphs in deformed specimens aged at 300°C are appreciably more rapid than simple volume diffusion control allows. This observation is shown to be explained by an excess vacancy, rather than by a dislocation Piping mechanism of growth. ThE rather complex phenomenology of the 8&apos; —8 transformation in Al-Cu alloys has been recently elucidated in considerable detail by means of transmission electron microscopy.&apos;-4 This technique was also employed in the present investigation in order to examine the effects of plastic deformation upon the transformation of 8&apos; to 8. The mechanism of the transformation in undeformed Al-Cu alloys has been established as the following sequence of events.1"4 The first step is the nucleation of 9 at (Y:8&apos; boundaries. Nucleation of a 0 crystal takes place, however, at only a very small proportion of the 8&apos; plates present. Each 0 crystal simultaneously consumes the host 8&apos; plate and the a! in the immediate vicinity, with growth into a being the rate-controlling process. The remaining 8&apos; plates are then dissolved as they fall under the concentration shadow of the growing 8 crystals. The evidence on the effects of plastic deformation upon these processes is intriguing, but much less detailed. The careful X-ray studies of Graf and Guinier have shown that the aging times required to form detectable amounts of 8&apos; and 8 are reduced by prior cold working. Thomas and Nutting confirmed these results by replication electron microscopy. Nile-shwar,* on the other hand, reported that creep deformation decreases the rate of formation of 0. While this difference may have been caused by the use of concurrent rather than successive deformation and ag- ing, the X-ray technique which he used was able to monitor only the 0 phase. It is thus possible that the times needed to form 8&apos; were increased moreg than the kinetics of 8&apos; — 8 transformation were accelerated. At 90 pct deformation by cold rolling, Graf and Guinier found that the usual 0&apos; —0 8 sequence is reversed: 0 forms first. von Heimendahl 10 confirmed this result with transmission electron microscopy. Pollard and Nutting, 11 and more recently Driver and Barrand, 9 having used the same technique, report that 9 also forms first during creep deformation. In the present study, the maximum amount of deformation was limited to 50 pct reduction by cold rolling in order to insure that 8 formed principally by the decomposition of . I) EXPERIMENTAL PROCEDURES This investigation was conducted on an Al- 3.93 pct Cu alloy, prepared as previously described. 4 Morphological and crystallographic effects of plastic deformation were studied in specimens annealed 6 hr at 548°C, quenched, and then aged for either 3 or 8 hr at 250°C to form large numbers of 0&apos; plates. After cold rolling to a 50 pct reduction in thickness, the

Jan 1, 1969

By J. P. Neumann, Y. A. Chang

Lattice parameter measurements of the hcp phase in the system Ag-A1 near the stoichiometric composition Ag2Al were carried out for specimens quenched from 825°K, annealed for 10 days at 453°K, and annealed for 100 days at 413°K. The three heat treatments resulted in the same lattice parameters at room temperature. None of the specimens showed any superlattice lines. The lattice parameters of this alloy were also measured at temperature from 77° to 750°K. An anomaly in the temperature variation of the lattice paramete.rs occurs in the region near 400°k, which may be associated with local ordering. FROM measurements of the diffuse scattering of X-rays, it is known that the [ phase in the system Ag-A1 near the stoichiometric composition Ag2A1 ex- hibits a considerable degree of short-range order at room temperature.&apos; Moreover, based on the position of the short-range order peaks a superlattice model had been proposed in the same study and it was suggested that lowering the annealing temperature to 420°K might result in long-range order. In the present study, the diffraction patterns and the lattice parameters of three differently heat-treated specimens, i.e., quenched from 825°K, annealed for 10 days at 453°K, and annealed for 100 days at 413°K, were determined from 77" to 750°K. The purpose of these measurements was to investigate 1) whether long-range order could be established by prolonged annealing and 2) whether the lattice parameters at room temperature depended on the heat treatment, since it had been proposed earlier2 that the lattice parameters in this phase are related to the atomic arrangement. 1) EXPERIMENTAL TECHNIQUES Silver and aluminum, both 99.99 pct purity, were melted in a zirconium oxide crucible under helium in

Jan 1, 1969