By Bernard Scheiner

A number of wells were drilled at two phosphogypsum stacks, one at P-21 owned by IMC and the other at Agrico's South Pierce Stack. Each well was sampled, and composites representing 5-ft increments were leached with synthetic rainwater to determine the extent of metal and nonmetal migration. To simulate what was occurring in the stack, composite samples were placed in a column, so that the column represented the stack in miniature form. Leaching experiments showed that both metals and nonmetals moved down the column when water was added to the top of the column. Data obtained from P-21 showed that with time the concentration of metals and nonmetals reached equilibrium values. The concentration of Ca, SO4, F, Si, and PO4 were -600 ppm,~1,500 ppm, 32 ppm, 14 ppm, and 22 ppm, respectively. Column leaching of South Pierce material, representing 0 to 55 ft of stack, showed that after 355 in. of water, the stack was near equilibrium values down to the 33-ft level. With continued addition of water, the portion of the stack at equilibrium would continue to increase and eventually reach the values observed for P-21. The test showed that the sulfate concentration of the effluent from the stack would never reach the USEPA standard value of 250 ppm. During the leaching test, it was determined that the permeability of the phosphogypsum in the columns was 0.000103 cm/sec. This number was used in the modeling. The data obtained from the leaching experiments cast some doubt on the practice of entombment now being practiced for closure of phosphogypsum stacks. The data clearly shows that with time, the amount of material leaching from the stack is low in concentration, with only the calcium and sulfate at higher levels. When a stack is closed at an existing operating plant, allowing rainwater to fall on the stack and capturing the solution in the existing pond system would eliminate the need for covering the stack, since with time the closed stack would continue to leach and at some point reach the equilibrium values of the P-21 stack. Entombment means that the leachable material in the stack will always be there and will require monitoring forever. Allowing rainwater to decontaminate the stack may be the best environmental solution to the problem.

Jan 1, 1999

By J. M. Scharer, Bruce E. Halbert, Lysane Bouduc, Douglas B. Chambers, Jennifer L. Kirkaldy, Carol M. Pettit

Io contrast to acid mine drainage (AMD), neutral mine drainage (NMD) has not yet received widespread attention. Metal and sulphate concentrations can be elevated and of concern in neutral drainage from waste rock and tailings. In the present paper, metal release in high ionic strength mine drainage at neutral pH is evaluated at several mine sites. Specific factors including oxidation rates, buffering capacity, and hydrology are also addressed and their effect on the production of contaminated NMD from mine wastes is evaluated. Case studies are presented involving current seepage water quality and predictive geochemical modelling to illustrate the possible time frame and magnitude of the contamination.

Jan 1, 2000

By G. Bjorling

The opening oxidation of a hydrometallurgical treatment of natural sulphides must for several reasons be so controlled that a maximum of the sulphide sulphur is transformed into elemental. If the oxidation is performed at low pressure and moderate temperatures and with mild reagents such as diluted nitric acid (or ferric or cupric chloride) the just mentioned condition is realized and it has been found possible to conduct the reaction so that solutions are obtained from which the metals can be recovered and the reagents required for the dissolution are regenerated. Experiments in laboratory scale with nitric-acid promoted oxidation have shown that this method is applicable to several types of raw materials, and in combination with electrodialysis both for partial neutralization and for final regeneration of the circulating acid can the requirements of low consumption of chemical reagents and formation of harmless residues be well fulfilled. The metals can be recovered as cathodic deposits or as hydroxides, and the method should be applicable also for low grade ores and concentrates. Although oxidation of sulphides by ferric or cupric ions has the advantage that it can be performed in open vessels it seems well worth the complication of working with nitric acid promotion in a low-pressure autoclave. Also complex sulphidic, oxidic and metallic materials can be treated.

Jan 1, 1973

By R. J. Roman

The results of column leaching tests on 3 different mixed oxide/sulfide ores from a Chilean deposit are presented. The 3 samples contained different ratios of oxide copper minerals to chalcocite and chalcopyrite. The results of the column leach tests are interpreted in light of the shrinking core model for coarse particle leaching. The copper recovery from the oxide minerals and the sulfide minerals each conforms to the shrinking core model with the total recovery equal to the weighted average of the individual minerals. The use of column test results to predict field heap leaching results using the multi-mineral shrinking core model is discussed.

Jan 1, 1993

By Lee Y. K, Walker G. S, Bronswijk V. W

The effect of leaching three samples of Mt Weld ore with a-hydroxysulphonic acid [(CH3)2(COH)SO3H] was assessed. Apatite present in the samples was found to be readily soluble but calcination up to 600¦C was required to increase the solubility of crandallite. Increasing the calcination temperature increased dissolution of both phosphate and alumuuum. The optimum SO2 content in solution for the dissolution of crandallite ores was found to be lower than for apatite.

Jan 1, 1991

By S. P. Fleming

An acid mine drainage sludge containing 0.26% nickel, 0.21 % cobalt and 4.5% manganese was leached in a one-liter reactor with sulfuric acid in the absence and presence of sodium sulfite. The effects of temperature (25°C and 52°C) and sodium sulfite concentration (up to 0.03 molar) on the leaching rate were particularly investigated. The leaching rates of nickel and cobalt with sulfuric acid have been determined to be controlled by diffusion through product layer. It has been found that effective leaching conditions to give more than 90% extraction of nickel, cobalt and manganese while keeping the iron extraction below 10% come with an elevated temperature and a low sodium sulfite concentration at pH 3; for example, 52°C and 0.01 molar sodium sulfite.

Jan 1, 1992

With shortage of sulfide nickel ores, laterite ore was paid more attention by scientists. Because its grade is commonly lower than sulfide nickel ores, laterite ore can not be utilized effectively be-coming the bottleneck of study. Leaching laterite ores from Yuanjing, Yunnan province, organic ac-ids show better selective than sulfide acid in nickel and cobalt recovery. Organic acid has low de-pendent on pH, keeping leaching capability even higher than 3. On the other side, when pH up to 2, sulfide acid can not leach laterite ores any more. After four kinds of organic acid leaching laterite ores, besides citrate, malate and succinate have good leaching and effectively selective capability. Especially, succinate has the best selective leaching capability of nickel and cobalt in four kinds of organic acids for latter anion purification and separation. Isolated from waste water with sugar, Aspergillus niger (zs1) has great capability to produce organic acids and vigorous growth. Laterite ores have been respectively processed by direct-leaching and indirect-leaching. Indirect-leaching gives a better result than direct-leaching. Extraction of nick-el by indirect-leaching reaches 44.3%, far more than that of direct-leaching. Moreover extraction of nickel at pulp density of 5% is higher than that at pulp density of 10%, reaching 63% in 11 days and extraction of cobalt also is 48.1% in the same period. Compared with nickel and cobalt, iron gives low extraction in solution, containing organic acids produced by Aspergillus niger .

Jan 1, 2014

By Fathi Habashi

OXIDE ORES can be divided into two groups: 1) Simple oxides (Table 3.1). 2) Complex oxides. Those ores containing minerals composed of two oxides; an acid oxide (Cr2O3, Nb2O5, etc.), and a basic oxide (CaO, FeO, MnO), as shown in Table 3.2.

Jan 1, 1970

By P. L. Sibrell

The U.S. Bureau of Mines has tested cyanide leaching for recovery of palladium (Pd) from spent petroleum processing catalysts. Three different catalyst samples were supplied by a spent-catalyst processor. These catalysts consisted of a zeolite base and contained 0.4 to 0.7 pct Pd. During alkaline cyanide leaching, the catalysts exhibited ion-exchange properties due to their zeolite matrices. Hydrogen ions were released from the zeolite in exchange for sodium ions in solution, resulting in a significant decrease in solution pH. This could present a safety hazard because of the potential for release of toxic hydrogen cyanide gas. A pretreatment .step where the catalysts were contacted with a 1.0M sodium hydroxide solution was found to prevent the pH shift from occurring. Following the sodium hydroxide pretreatment, two stages of leaching at 160 °C with solution containing 1 pct sodium cyanide and 0.1M sodium hydroxide gave at least 75 and up to 95 pct Pd recovery. The Pd was quantitatively recovered from the leach solution by thermal decomposition in an autoclave at 250 °C for 1 h. The Pd content of the precipitate was over 50 pct. Thermal decomposition also decreased the total cyanide content of the barren solution to less than 0.2 mg/L. The catalyst leach residues passed the Federal Toxicity Characteristic Leaching Procedure and the California Waste Extraction Test, indicating that landfill disposal of the leach residues would be acceptable.

Jan 1, 1995

By Fathi Habashi

THE MINERAL monazite (µ?v??e?? = to be alone) is a rare earth phosphate containing some thorium and small amounts of uranium. It is widely distributed in the earth's crust. It occurs in small proportions in granites. Table 7-1. Mineralogical analysis of Rosetta black sands, U.A.R. (Nakhla, 1958). [Black sands Concentrate Augite 10.8 - Calcite 1.1 - Felspar 0.1 - Garnet 1.8 - Hornblende 2.4 - Ilmenite 50.7 8.0 Magnetite 15.3 Monazite 1.1 84.3 Quarz 7.3 - Rutile 1.0 0.5 Titanite 0.2 - Zircon 7.3 7.1 Others 1.0 0.1 100.0 100.0]

Jan 1, 1970

By Jack S. McPartland

Historically, research on thiosulfate leaching of precious metals ores has been focused on processing of difficult to treat ores. Thiosulfate leaching of ores and concentrates containing sulfide minerals, copper, manganese and preg-robbing carbon constituents has been evaluated. Cyanide leaching is generally considered an efficient, environmentally acceptable means for processing of non-refractory precious metal ores, Consequently, commercial processing of finely disseminated, oxidized precious metal ores is normally accomplished using alkaline cyanide leaching. Recent changes in regulatory climate have, however, called into question the acceptability of cyanide leaching in a number of locations worldwide. In some cases where the use of cyanide is being questioned, thiosulfate leaching may provide an acceptable alternative. Developments in thiosulfate leaching of precious metal ores are reviewed in this paper.

Jan 1, 1999

By D. L. Leach

This report covers laboratory experiments simulating in situ copper recovery from primary sulfide ores in sulfuric acid systems pressurized with oxygen. Copper extraction and acid consumption data are correlated with temperature in the range 50-150°C and quenched pH in the range 0.25-2. Adverse changes in the chemical composition of the leach solution and the formation of gangue-mineral alteration products and secondary sulfides can severely limit the extraction of copper above 90°C. Keeping the pH below the self-buffered value of about 2 and the temperature below about 110°C produces the maximum extraction rates. Forcing the pH too low not only results in excessively high acid consumption but may also limit the extraction of copper at temperatures above 100°C.

Jan 1, 1975

By R. L. Braun, D. L. Leach

Laboratory experiments simulating in-situ copper recovery from primary sulfide ores in sulfuric acid systems pressurized with oxygen are reported. Copper extraction and acid consumption data are correlated with temperature in the range 50 to 150°C and quenched pH in the range 0.25 to 2. Adverse changes in the chemical composition of the leach solution and the formation of gangue-mineral alteration products and secondary sulfides can severely limit the extraction of copper above 90°C. Keeping the pH below the self-buffered value of about 2 and the temperature below about 110°C produces the maximum extraction rates. Forcing the pH too low not only results in excessively high acid consumption but may also limit the extraction of copper at temperatures above 100°C.

Jan 1, 1977

By J. E. Murphy, Y. Topkaya, R. E. Johnson, B. R. Palmer, D. K. Dysinger, R. B. Bhappu, A. E. Clark

The U.S. Bureau of Mines utilized a central composite experimental design to investigate leaching kinetics of pure chalcopyrite in the sulfuric acid-oxygen system. The six factors studied were oxygen pressures of 150, 300 and 450 PSI, leach temperatures of 35O, 65O, and 95O C, oxygen-to-chalcopyrite mass ratios of 0.5, 1.0 and 1.5, leach times of 8, 16 and 24 hours, initial acid strengths of 0.6, 1.2 and 1.8 g H,SO,/g chalcopyrite and pyrite to chalcopyrite mass ratios of 0, 1, and 2. Chemical analysis and oxygen consumption measurements indicatedthat leaching occurs through three consecutive reactions. Temperature was the primary determinant of leach rate and solution acidity was the primary determinant of oxygen consumption, sulfur oxidation, and activation energy.

Jan 1, 1993

By J. G. van der Watt

Due to increasing concerns of global rare earth element shortfalls in the near future, possible alternative sources of rare earth elements have recently become of economic interest. One such alternative is decanting acid mine water originating primarily from abandoned old mines in the Witwatersrand region of the Republic of South Africa. In this study, a novel way of rare earth element removal from the acid mine drainage was employed, making use of bentonite clay, which has very good adsorbent properties, as a rare earth element carrier material. The process can be economically viable only, if the elements can be selectively removed from the bentonite clay carrier material so as to yield reusable clay. Acid leaching was proposed to liberate the adsorbed rare earth elements from the bentonite clay. Accordingly, acid leaching experiments were performed to study the desorption of three commonly-found rare earth elements, namely neodymium, samarium, and dysprosium, from bentonite clay in the presence of sulphuric and hydrochloric acid. It was established that the three rare earth element species could be selectively removed as a group from iron, magnesium, and manganese metals through the careful manipulation of the pH. An investigation into the kinetic aspects of the rare earth element desorption process from the bentonite clay was also undertaken. The applicability of various kinetic models such as zero-order, pseudo first-order, pseudo second-order, elovich, parabolic diffusion, and power function were tested to describe the time-dependent desorption of rare earth elements from bentonite clay. It was determined that the pseudo second-order kinetic model represented the dissolution processes for neodymium, samarium, and dysprosium from bentonite clay the most accurately.

Jan 1, 2012

By M. Walawalkar, C. K. Nichol, G. Azimi

Rare earth elements (REEs) are essential to the production of technologically advanced products, including wind turbines, electric and hybrid cars, automotive catalytic convertors, hand held electronic devices, and military defense systems. Their application in environmentally beneficial technologies puts them at a high priority for ameliorating environmental concerns. Because of their increasingly high demand and limiting resources, it is highly beneficial to find new sources for them. The present study is focused on leaching REEs from a phosphate based fertilizer by-product, known as phosphogypsum (PG). Global estimated world production of PG is about 240 million tonnes that is stored in the form of wet stacks adjacent to fertilizer production facilities, occupying vast amounts of land. PG also contains trace metals, which are detrimental to the environment, and hence it is crucial to monitor these stacks. We obtained our PG sample from Agrium Inc. (a fertilizer manufacturing company in Canada). We performed a comprehensive characterization of the PG sample and found that it predominantly contains Y, La, Ce, Nd, and Sm. For leaching purposes, we used hydrometallurgical acid leaching techniques. We investigated three acids over a range of operating conditions such as acid concentration, temperature, solid-to-liquid ratio, and residence time. We achieved an average leaching of 81% with hydrochloric acid as leachant using operating conditions that can be easily replicated in industrial settings. If our process is implemented, not only will it reduce the size of the existing PG stacks (mitigating their environmental risks), but also enable the development of new innovative routes for extracting REEs, making countries like Canada less vulnerable to supply disruptions.

Jan 1, 2016

By H. Razavizadeh

The recovery of copper from oxide ores containing from 2% to 4.1% acid-soluble copper from the Sarcheshmeh mine in Kerman province of Iran was investigated by agitation leaching in sulfuric acid media. Quartz, as a major constituent, and malachite, as the major copper mineral, were identified in the ore by X-ray diffraction (XRD) and microscopic studies. A series of leaching experiments on the ore was performed over a concentration range of 10 to 20 g/L and temperatures from 15° to 50°C for a maximum of 3 hours. An initial high dissolution of copper was followed by a very slow reaction. By increasing acid concentration and temperature, the dissolution rate of copper was accelerated. However, by increasing acid concentration, the acid consumption of ores was also increased. Surface morphology of solid residues at various leaching times was examined with a scanning electron microscope (SEM). All SEM micrographs of the partially reacted particles displayed a needle structure. The kinetic studies showed that the malachite dissolution rate could be modeled in two stages. About 85% of the malachite dissolution occurred in Stage 1, while the remaining 15% occurred in Stage 2. The data obtained for the leaching kinetics indicate that the dissolution for Stage 1 was a diffusion-controlled reaction with an activation energy of about 20.6 kJ/mole, and the dissolution for the Stag 2 was a chemical-controlled reaction with an activation energy of about 87.6 kJ/mole.

Jan 1, 2008

By S. Jolivet, A. Klöfverskjöld, P. Latostenmaa, B. P. Wilson, M. Lundström, P. Halli

Doré slag is secondary product of copper electrore fining anode slime treatment. The slag consists mainly of different slag formers, such as borax and silica based minerals together with soda and traces of sealing materials. However, Doré slag also contains metals present in the anode slime, such as Ag, Cu, Bi, Sb and Te. At some plants, slag cleaning has been conducted utilizing conventional grinding and flotation circuits in order to enrich the content of precious metals in the slag [1]. Nevertheless, the routine consideration of the slag as a secondary raw material has so far not been adopted on an industrial scale. The current study presents the preliminary results of the nitric acid and chloride leaching of antimony from Doré slag. Chemical and mineralogical analyses (SEM-EDS, AAS, XRD) were performed for the raw material, leaching residue, and leaching solution in order to ascertain the metal recovery and kinetics during leaching.

Mar 1, 2017

By Fathi Habashi

SELENIUM AND tellurium are by-products of electrolytic copper refining. Copper anodes contain 0.01-0.2 % Se and up to 0.04 % Te; during electrolysis these deposit as a slime at the bottom of the cell. Such slimes contain 2-15% Se and 0.5-8 % Te, as selenides and tellurides of gold, silver, and copper. The following compounds have been identified in the slimes: (Ag, Au)Te2, Ag2Se, Ag2Te, CuAgSe, Cu2Se, Cu2Te. Anodic slimes from copper electro¬lytic refining are a grayish black powder, minus 200 mesh. When this complex mixture is decomposed in an acid medium, elemental selenium and tellurium can be obtained, while in an alkaline medium, both metals go into solution. Acid leaching The slime is charged in acid digesters of 800-900 lb capacity, heated to 260°C with 78 % H2SO4, for 8-12 hr. During digestion the following reactions take place:

Jan 1, 1970

By Fathi Habashi

CLAYS CONTAIN the mineral kaolinite, a hydrated aluminum silicate. It is an important potential raw material for aluminum, especially for those countries possessing no bauxite deposits. Therefore, there is no surprise to find a large volume of research done for the recovery of aluminum from clays. Kaolinite (Al203?2 SiO2?H20) contains 39.8% A1203; 46.3 % SiO2, and 12.9 % H2O. The analysis of a good-quality dried clay of an Eastern Canadian siliceous shale is shown in Table 8-1.

Jan 1, 1970