By Ning Wang, Tengfei Guo, Wanyan Li, Hanjie Wen, Hannian Gu, Zehai Li

Red mud has been reported as a potential resource for lithium. To investigate the leaching behavior of lithium, a lithium-rich red mud was neutralized with hydrochloric or oxalic acid and then leached with acetic acid. When red mud was neutralized using dilute hydrochloric acid, about 58 to 60 percent of lithium was leached with 25 percent acetic acid at 95 °C for 60 min, while more than 95 percent of sodium and 85 percent of calcium were dissolved in the leachate solution. When oxalic acid was used to neutralize red mud prior to acetic acid leaching, lower lithium leaching efficiencies of about 42 to 47 percent were observed. Nevertheless, these leaching efficiencies of lithium were close to that of calcium and much higher than those of sodium under the same conditions. In this study, 25 percent (v/v) of acetic acid at 85 °C for 60 min was demonstrated to be the optimum conditions for lithium extraction from oxalic acid-neutralized red mud using acetic acid. The results are useful and of interest for lithium recovery and purification from red mud.

By Ning Wang, Tengfei Guo, Wanyan Li, Hanjie Wen, Hannian Gu, Zehai Li

Bauxite residue (red mud) is an alkaline waste derived from the industrial process for extraction of alumina from bauxite ore. Some bauxite residues contain considerable concentrations of critical metals, for example, rare earth elements. Lithium in red mud was also reported as a potential resource. In the current study, a Li-rich red mud was leached using acetic acid to investigate the leaching behavior of lithium followed by neutralizing with hydrochloric or oxalic acid. By neutralizing red mud using diluted hydrochloric acid (0.01 mol/L), 58.04–60.27% of lithium was leached using 25% acetic acid at 95 °C for 60 min. In the meantime, more than 95% of sodium and 85% of calcium were also dissolved in the leachate solution. While oxalic acid (0.5 mol/L) was used to neutralize red mud prior to acetic acid leaching, lithium performed lower leaching efficiencies (42.41–46.88%) in comparison of using of hydrochloric acid–neutralized red mud. Nevertheless, these leaching efficiencies of lithium were close to that of calcium and much higher than those of sodium under the condition. In this study, 25% (v/v) of acetic acid, at 85 °C for 60 min, was demonstrated as optimum conditions for lithium extraction from oxalic acid–neutralized red mud using acetic acid. The results would be useful and of interest for lithium recovery and purification from red mud.

By Ning Wang, Tengfei Guo, Wanyan Li, Hanjie Wen, Hannian Gu, Zehai Li

Bauxite residue (red mud) is an alkaline waste derived from the industrial process for extraction of alumina from bauxite ore. Some bauxite residues contain considerable concentrations of critical metals, for example, rare earth elements. Lithium in red mud was also reported as a potential resource. In the current study, a Li-rich red mud was leached using acetic acid to investigate the leaching behavior of lithium followed by neutralizing with hydrochloric or oxalic acid. By neutralizing red mud using diluted hydrochloric acid (0.01 mol/L), 58.04–60.27% of lithium was leached using 25% acetic acid at 95 °C for 60 min. In the meantime, more than 95% of sodium and 85% of calcium were also dissolved in the leachate solution. While oxalic acid (0.5 mol/L) was used to neutralize red mud prior to acetic acid leaching, lithium performed lower leaching efficiencies (42.41–46.88%) in comparison of using of hydrochloric acid–neutralized red mud. Nevertheless, these leaching efficiencies of lithium were close to that of calcium and much higher than those of sodium under the condition. In this study, 25% (v/v) of acetic acid, at 85 °C for 60 min, was demonstrated as optimum conditions for lithium extraction from oxalic acid–neutralized red mud using acetic acid. The results would be useful and of interest for lithium recovery and purification from red mud.

By K. N. Han

The leaching behavior of palladium in ammoniacal solutions was investigated by using the rotating-disk technique in an autoclave. The study included the effects of rotation speed, temperature, oxygen pressure, composition of ammoniacal solutions and catalysts on the overall leaching rate. The dissolution of palladium in ammoniacal solutions was discussed in terms of the thermodynamics and a kinetic model. Even though the Eh-pH diagram suggests that palladium metal can dissolve in ammoniacal solutions at room temperature, it was found that the dissolution was very slow at temperatures below 100 °C but was significantly improved at higher temperatures. It was also found that the rotating speed of the palladium disk had no effect on the leaching rate. The apparent activation energy was found to he 69.7 kJ/mole. Based on the results obtained, it was concluded that the dissolution of palladium is controlled by chemical reaction.

Jan 1, 1999

By K. N. Han, X. Xie

The dissolution behavior of palladium powder in thiourea solutions was investigated. The variables studied were temperature, stirring speed and the concentrations of thiourea, acid and ferric ion. Palladium was found to be soluble in thiourea solutions in the presence of an oxidant such as ferric ion. The dissolution of palladium in thiourea solutions was believed to be chemical-reaction controlled, with an apparent activation energy of about 25.3 kJ/mol.

Jan 1, 1997

By D. Hong, K. N. Han

The leaching behavior of rhenium in ammonium iodide solutions with iodine as oxidant was studied. Experiments were carried out in an autoclave to investigate the effects of stirring speed, temperature, solution pH, and iodine and iodide concentrations on the dissolution of rhenium. It was found that a high temperature and a high solution pH were essential for the efficient leaching of rhenium. The dissolution rate was found to be dependent upon the concentration of iodine and iodide. It was concluded that the dissolution of rhenium under the conditions studied was controlled by the mass transfer of iodine with an apparent activation energy of 15.8 kJ/mole.

Jan 1, 1999

By D. Yu, T. A. Utigard, M. Barati

"Sulfation roasting of nickel concentrate to generate water-soluble metal sulfates was investigated as an alternative process to smelting for the recovery of valuable metals. The kinetics of dissolution of various species of the calcine in three leachants was studied; hot water, dilute HCl, and concentrated HCl. The results indicated that dissolution of sulfates by hot water at 90 ºC is achieved within 30 minutes. In order to increase the recovery of the valuable metals, acid leaching is necessary due to the existence of ferrite in the calcine.INTRODUCTIONInvestigations on the sulfation roasting of nickeliferous sulfide ores or concentrates were mainly carried out in 1950’s to 1990’s to generate water soluble non-ferrous metal sulfates followed by metal recovery by leaching (Stephens, 1953; Thornhill, 1954, 1961; Fletcher and Shelef, 1964a, 1964b; Fletcher and Hester, 1964; Frankiewicz, 1977; Norrgran, 1983). Commercialization of the sulfation roasting process was only performed by Falconbridge Ltd. (Thornhill, 1961; Boldt, 1967), which employed a sulfation roast process on nickeliferous pyrrhotite at 680 oC where Ni, Cu, and Co were leached and Fe2O3 was produced for the iron industry. In 1965, 118,342 tons of pyrrhotite was processed, however because of the huge SO2 emissions (no acid plant) relative to the nickel production and the poor economics, this plant was shut down.Nickel production from sulfide ores via pyrometallurgical means, especially the electric furnace smelting process, is a major emitter of SO2 to the environment and a big energy consumer (Warner, Diaz, Dalvi, Mackey, Tarasov and Jones, 2007). Nowadays, due to the more stringent environmental regulations as well as the need to reduce energy consumption, metal production by sulfation roasting is gaining more attention as an alternative process to smelting. The main focus of this paper is to investigate the extent and rate of leaching of valuable metals from the sulfation roasted nickel calcine, aiming to maximize the metal recovery and minimize the dissolution of iron species."

Jan 1, 2012

By E. Fried

Cemented paste backfill (CPB) is an innovative tailings management method that consists in returning considerable amounts of mine tailings into the underground mine openings. The filled stopes thus participate to the ground support that allows maximizing orebody extraction and a safer environment for the mine workers. There are also significant environmental advantages of using CPB. Indeed, up to 50% of the concentrator tailings can be backfilled, leading to a smaller volume of problematic waste materials to be managed at the surface. Once the CPB is placed, or when the mine is flooded at its end-life, the backfill is subjected to underground water flows that may leach and spread the pollutants (mainly metals, sulphates, and acidity) which can contaminate the underground waters. The aim of this study is to characterize the leaching properties of CPB material and to identify the cement phases that ensure the metal fixation. A laboratory procedure was implemented consisting in the preparation of various paste backfill mixtures using sulphide-rich and sulphide-free materials, different types of binder, and mixing waters having various sulphates, copper and zinc concentrations. After 90-days curing time, the samples were submitted to column leaching tests. The CPB materials were flushed each day with 100 ml of deionised water during 100 days. The collected leachates were then analyzed for pH, Eh, electric conductivity and chemical composition. For some samples, a differential acid neutralisation test was carried out. The objective of this experiment is to dissolve selectively the hydrated phases by adding incremental acid concentrations. By analyzing punctually the equilibrated solutions, the composition of the dissolved phases and their metal content can be estimated. The leaching test results showed that the pH of the leachates remains alkaline during the test period. When the pH decreases under 10 (after 30 days), different behaviours in terms of chemical element release (especially for zinc) were observed. During the test, the oxidation of pyrite seems to slow down, probably due to passivating phenomena. Moreover, the differential acid neutralisation test results allowed a better understanding of the CPB mineralogy and the Zn-bearing cement phases. Zinc and the other metals seem to be fixed within a calcium-magnesium silicate.

May 1, 2007

Due to complex mineralogical and chemical interactions of the value and gangue mineral phases present in uranium-containing lateritic ores, deleterious pulp gelation which impacts on value metal recovery sometimes occur during atmospheric leaching. In this study, the leaching behavior and particle interactions of selected oxide (hematite, quartz) and clay minerals (muscovite, chlorite), which constitute predominant host gangue phases of typical lateritic uranium ores are investigated to provide basic, mechanistic understanding of temporal pulp gelation phenomenon. Isothermal, batch leaching with H2SO4 was carried out on concentrated dispersions (30 ? 57 wt.%) of single minerals at pH 1 and 25 or 70 °C and their concomitant solution, speciation and rheology (shear yield stress, viscosity) were characterized. It is clearly shown that despite the high oxide content of lateritic ores, the pulp chemistry and rheology is largely affected by the incongruent leaching behavior of more reactive, acid-consuming aluminosilicate clays. Furthermore, time- and temperature-dependent alumino-silicate species polycondensation interfacial reactions are shown to be responsible for the enhanced particle interactions, reflecting strong pulp rheology in agitation and pumping. If not properly mitigated, high pulp shear yield stress and viscosity have a striking impact on processability and hence, value metal recovery.

Sep 1, 2012

By G. T. Lapidus, A. Garcés, O. J. Restrepo

"Colombian nickel laterites have historically been processed by pyrometallurgy. However, due to the depletion in ore grades, alternative processes are required. Hydrometallurgical processes, such as pressure acid leaching, have been proposed as alternatives to extract nickel from deposits with suitable characteristics. Such a leaching process requires high concentrations of acid to achieve acceptable extractions, and is not selective. In this study, an alternative aqueous alkaline glycine system has been employed to evaluate the leaching behaviour of a Colombian nickel laterite which contains 1.15% Ni, 0.12% Co and 41.1% Fe. Additionally, the effect of the addition of chloride ions, the use of a reducing agent and the application of a pre-treatment to improve the extraction of nickel were evaluated. Extractions of 4.63% Ni, 42.16% Co and 0.33% Fe were obtained using a 1M solution of glycine at pH 9. In addition, an increase in nickel extraction from 4.63% to 25.68% was achieved by applying a pre-treatment to the sample. The results show that even though nickel dissolution was much slower than in acid leaching, it was selective over other metals such as iron, proving the proposed method to have potential as a process for the extraction of nickel from Colombian laterites.INTRODUCTION Before 2010, most of the industrial operations used pyrometallurgical processes for the extraction of nickel, mainly in saprolitic regions of deposits, with greater contents of the metal. Nevertheless, due to the gradual depletion of such deposits, different hydrometallurgical processes have been studied as alternatives to process those nickel laterites with low grade and those which present problems of refractoriness due to the presence of acid consuming materials (McDonald & Whittington, 2008; Oxley & Barcza, 2013; Wang et al., 2012). However, such leaching processes require high concentrations of acid to achieve acceptable extractions and they are not selective. Facing lateritic nickel ore deposits containing high levels of acid consuming materials, an alkaline leaching medium becomes an advantageous alternative over acidic media, due to the increase in selectivity and decreased corrosiveness and reagent consumption (Tanda, Eksteen, & Oraby, 2017). Unlike conventional acidic reagents used for metal recovery, alkaline reagents can selectively dissolve the desired metal, leaving in the solid residue other elements such as iron, magnesium and aluminum, which are problematic in subsequent stages of metals separation and recovery. Furthermore, there are no serious corrosion problems associated with alkaline leaching, even at higher reagent concentrations, or at elevated temperature and pressure (Ntumba Malenga, Mulaba-Bafubiandi, & Nheta, 2015)."

Jan 1, 2017

By M. B. Shongwe, R. K. K. Mbaya, C. K. Thubakgale, P. Mendonidis

"A low-grade nickel-bearing ore was pre-concentrated on a SB40 laboratory model Falcon Concentrator. Three size fractions, -212+125, -125+75 and -75 µm were tested with the intent to upgrade the nickel content by reducing their content of fine silica, which becomes amorphous during leaching. Separation of silica from nickel-bearing magnesium silicate minerals; hornblende, clinochlore and talc, was more efficient in the finer particle sizes, -125+75 and -75 µm, and at high G-forces. For these two size fractions, nickel was upgraded from 0.06 to 0.07%, with a reduction in silica content from 52.12 to 50.71%. Leaching of feed samples prior to pre-concentration resulted in the formation of amorphous silica, indicative of the presence of fine silica in the samples. Leaching of nickel from the -125+75 µm fraction increased with increasing G-force and feed pulp percent solids, while that of -75 µm was not influenced. The optimum nickel recovery was 15.68% to the Falcon underflow, using the feed size fraction of -75 µm, 30 G and a feed pulp solids content of 10% solids, after 120 minutes of treatment.INTRODUCTION A low-grade South African nickel-bearing ore with about 0.06% Ni was previously studied for atmospheric pressure acid leaching using sulphuric acid. The study was motivated by the continuing search for methods to treat of low-grade ores, which appear to be an increasingly important source of valuable metals as a result of a declining production from rich sulphide ores. Nickel is a base metal that is used as an alloy in steelmaking and chemical industries because of its resistance to corrosion (Haudet et al., 2015). Nickel laterite ores with grades lower than 1.50% Ni are considered to be complex ores, accounting for 70% of the global nickel reserves (MacCarthy et al., 2016). Their complex nature may be attributed to the indefinite mineralogy of these ores, in which nickel may occur in more than one mineral host. In some cases, nickel may be finely disseminated in the ore. The grade of such an ore and complex mineralogy do not justify the application of pyrometallurgical methods for extraction of nickel (Zhu et al., 2012). This suggests that there is a need for less expensive alternative methods of extraction. This study investigates the application of centrifugal gravity concentration, using the Falcon concentrator, followed by leaching to determine the effect of pre-concentration of the ore prior to extraction by atmospheric pressure leaching with sulphuric acid."

Jan 1, 2017

The leaching characteristics of a number of Australian uranium ores were determined under acid and alkaline conditions. Ores from the Ranger, Nabarlek and Koongarra deposits in the Northern Territory were readily leached in dilute sulphuric acid. Suitable processing conditions were: leaching at 35-40°C, pH 1·52·0 and redox potential -475 mV for periods of 16-24h with ore ground to 50 per cent -200 mesh CB.S.S.). Ore from the Roxby Downs deposit in South Australia required leaching at 55°C and a redox potential of -650 mV to achieve a satisfactory recovery. All ores contained refractory minerals which were not leached under conventional conditions, limiting uranium extraction to 86-96 per cent.Carbonate leaching of carnotite in calcrete ores from Yeelirrie and Lake Way in Western Australia yielded uranium extractions of at least 98 per cent. Leaching rates were considerably faster than those reported for other applications of alkaline leaching as the slow oxidation step was not required.

Jan 1, 1979

By H. Manurung, I. M. Bendiayasa, W. Astuti, and H. T. B. M. Petrus, F Anggara, K. C. Wanta

The leaching kinetics of cerium (Ce) and yttrium (Y) in sodium-hydroxide-digested non-magnetic coal fly ash using acetic acid were investigated. The variables analysed were pH, solid-to-liquid ratio (S/L), and temperature. The results show that cerium and yttrium's maximum recovery was 57.33% and 58.36%, respectively, under leaching temperature of 90°C for Ce and 60°C for Y at pH of 1,74 and 10 g/mL solid-liquid ratio in 240 minutes. Increasing the leaching time to more than 120 minutes did not significantly improve the results. After the magnetic separation process, the ICP-OES analysis shows a slight increase in the concentration of cerium and yttrium on nonmagnetic components. The XRD and ICP-OES analysis for the sample before and after silicate digestion shows that 40% silicate was dissolved. The calculation of apparent activation energies of leaching using the Arrhenius law for the leaching of cerium and yttrium gives 22.72 kJ/mol and 35.84 kJ/mol, respectively. The kinetic leaching model of cerium and yttrium all fit Dickinson's new shrinking core model. The calculation results show that the leaching reaction is controlled by combining interface transfer and diffusion across the product layer.

Nov 6, 2024

Refractory copper ores (CROs) in central Africa contain copper minerals that are locked up in a micacious solid matrix or associated with carbonate, sulfide and phosphate minerals. Several researchers have reported that the recovery of copper from CRO material by an acid-leaching process is not economically feasible, due to the presence of excess gangue-acid-consuming minerals such as calcites, dolomite, asbolane and iron oxides. Since the proportion of acid-insoluble copper (CuS) is about 28% of total copper and total free sulfur is extremely small, sulfide flotation was considered unfavorable. Consequently, hundreds of millions of tons of CRO material have been stockpiled specifically at the Nchanga Mine of Zambia. In terms of copper distribution in CRO material, a significant portion of total copper exists as carbonates (39%) and oxides (17%), while 28% of the copper is acid-insoluble (CuS). The rest of the copper is in the form of carbonates (16%) and (hydr) oxides (17%). This means that only about 72% of total copper is recoverable through the non-oxidative acid-leaching process. In this study, batch leach tests were performed on CRO solids (d95 = 95%) to establish the gangue acid consumption values at different feed pH values and to evaluate the leaching characteristics of copper, manganese and iron within the CRO material. Subsequently, continuous leach tests were performed on CRO solids (106 um, 80% passing) using optimum leach conditions derived from batch tests. This paper aims to show that sustainable copper recovery can be achieved by selecting leaching conditions whereby gangue acid consumption (GAC) values become significantly small and the final concentration of manganese and iron in the leach solution are appreciably low.

Jan 1, 2011

Refractory copper ores (CROs) in central Africa contain copper minerals that are locked up in a micacious solid matrix or associated with carbonate, sulfide and phosphate minerals. Several researchers have reported that the recovery of copper from CRO material by an acid-leaching process is not economically feasible, due to the presence of excess gangue-acid-consuming minerals such as calcites, dolomite, asbolane and iron oxides. Since the proportion of acid-insoluble copper (CuS) is about 28% of total copper and total free sulfur is extremely small, sulfide flotation was considered unfavorable. Consequently, hundreds of millions of tons of CRO material have been stockpiled specifically at the Nchanga Mine of Zambia. In terms of copper distribution in CRO material, a significant portion of total copper exists as carbonates (39%) and oxides (17%), while 28% of the copper is acidinsoluble (CuS). The rest of the copper is in the form of carbonates (16%) and (hydr) oxides (17%). This means that only about 72% of total copper is recoverable through the non-oxidative acid-leaching process. In this study, batch leach tests were performed on CRO solids (d95 = 95%) to establish the gangue acid consumption values at different feed pH values and to evaluate the leaching characteristics of copper, manganese and iron within the CRO material. Subsequently, continuous leach tests were performed on CRO solids (106 um, 80% passing) using optimum leach conditions derived from batch tests. This paper aims to show that sustainable copper recovery can be achieved by selecting leaching conditions whereby gangue acid consumption (GAC) values become significantly small and the final concentration of manganese and iron in the leach solution are appreciably low.

Nov 1, 2011

By G. Merrington, B. J. Alloway

Tailings from three historical mining areas in the UK were leached in columns under a simulated weathering programme which was chosen to represent periods of 1 and 2 years at 3 different ambient temperatures. The total concentrations of Cd, Cu, Pb and Zn in the primary ore minerals present in the tailings showed only a limited correlation with metal concentrations in the leachate. The leachate from columns of tailings that were maintained at a temperature of 25 (+/-3) degrees C contained, on average, 50% more Pb and 75% more Cu than leachate from tailings that were maintained at a temperature of 10 (+/-3) degrees C. The pH values of leachates from all three types of tailings at 25 (+/-3) degrees C were 0.2 units lower than those from columns maintained at 10 (+/-3) degrees C. The concentration of Cd and Zn in the tailings leachates showed no marked difference at the different temperatures. The composition of the leachate was found to be dependent on the type of gangue mineral, the presence of other sulphide minerals and the formation of secondary iron minerals. A comparison of the concentrations of heavy metals in the leachates produced in the laboratory with those in leachates that were collected in the field over a similar period of time from two of the mine sites showed that concentrations were of a similar order.

Jan 8, 1993

By Elizabeth Edwards, Radhakrishnan Mahadevan, Vladimiros G. Papangelakis, Srinath Garg, Kurtis Judd

Mineralogical characterization of the tailings showed the deportment of Ni to be similar in the Vale and Glencore tailings, with 60% of the total Ni locked in pyrrhotite, and the balance 40% associated with pentlandite. The overall Ni dissolution was correlated with the individual dissolution extents of pyrrhotite and pentlandite as functions of four leaching regimes: ‘anoxic acid’ (with and without pH control), ‘oxic acid’ (oxygen sparging), ‘oxic acid’ (air sparging), and ‘oxic ferric’ (air sparging). The results showed that the maximum Ni dissolution was obtained during the pH controlled oxic acid leach with oxygen sparging at pH 1.5, while the anoxic acid leach at pH 1.5 resulted in minimum Ni dissolution (10–15%) from pyrrhotite. An overall Ni mass balance showed that pyrrhotite and pentlandite dissolve simultaneously in the presence of Fe(III) and oxygen, in contrast to the preferential dissolution of pyrrhotite in the absence of Fe(III). Sulphur mass balances revealed that the yield of elemental sulphur is maximized (65%) during the oxic Fe(III) leach at pH 0.6. Furthermore, the kinetics of Ni leaching and elemental sulphur formation from pyrrhotite tailings leached with ferric sulphate between 55–80°C was investigated at constant oxidation-reduction potential. Elemental sulphur yield increased with increasing temperature, but no observable trend could be linked to ferric or ferrous ion concentration.

Jan 1, 2017

By S. S. Cook, S. E. Paulson

The US Bureau of Mines is conducting core leaching experiments with sulfuric acid on oxide copper ores from the Cyprus Casa Grande and Asarco/Freeport Santa Cruz deposit in Arizona to further the understanding of the leaching process in supergene copper ores as it relates to in situ mining. Leach solutions from atacamite mineralization contained 5 to 30 g/L (0.05 to 0.28 oz/gal) copper and few extraneous ions. Leachant from chrysocolla ores, with grades similar to the atacamite, contained 2 to 9 g/L (0.02 to 0.08 oz/ gal) copper and abundant extraneous ions. Quartz and K-feldspar had no impact on leach solution composition at any acid concentration up to 40 g/L - (0.39 oz/gal) while illite and sericite had minimal impact. Biotite, calcium-rich clay, and limonite have a significant impact on solution chemistry when there is abundant free acid in solution. High acid concentra¬tions increase acid consumption in ores with abundant biotite and limonite gangue. High acid concentrations can be used in ores with quartz, K feldspar, and sericite gangues without increasing acid consumption per unit of copper removed.

Jan 1, 1990

By Sterling S. Cook

The U.S. Bureau of Mines is conducting core leaching experiments with sulfuric acid on oxide copper ores from the Cyprus Casa Grande and ASARCO Santa Cruz deposits in Arizona to further our understanding of the leaching process in supergene copper ores as it relates to in situ mining. Leach solutions from atacamite mineralization contained 5 to 30 g/l copper and few extraneous ions. Leachant from chrysocolla ores, with grades similar to the atacamite, contained 2 to 9 g/l copper and abundant extraneous ions. Quartz and K-feldspar had no impact on leach solution composition at any acid concentration (up to 40 g/l) while illite and sericite had minimal impact. Biotite, calcium-rich clay and limonite have a significant impact on solution chemistry when there is abundant free acid in solution. High acid concentrations increase acid consumption in ores with abundant biotite and limonite gangue. High acid concentrations can be used in ores with quartz, K-feldspar, and sericite gangues without increasing acid consumption per unit of copper removed.

Jan 1, 1988

By R. D. Groves, G. M. Potter, T. H. Jeffers

Experiments on ammonium carbonate leaching of native copper ores crushed to 1-inch size showed that in 30 days 55 percent of the copper was extracted from 0.7 percent copper conglomerate-type ore, and 85 percent was extracted from 2.1 percent copper amygdaloid-type ore. Cupric ions were not necessary to initiate leaching, and dilute solution containing only 2.2 grams per liter NH3 and 1.9 grams CO, was a suitable solvent. Copper was recovered from the leach liquor by solvent extraction and electrolysis of the strip solution. Cyclic testing of the leach-solvent extraction-electrolytic procedure is in progress on a 6-ton charge of minus 12-inch conglomerate-type ore assaying 2.2 percent copper. Oxygen is metered to the closed leach vessel as required by the leaching reaction. Initial copper dissolution was much slower than from minus 1-inch ore, but the leaching rate then markedly improved.

Jan 1, 1974