Search Documents

By C. G. Rhodes, D. Kramer

High-field critical transport current density (J) measurements at 4.2 °K as a Junction of applied magnetic field (H) were made on samples of cold-rolled and annealed columbium with H parallel to J. Microscopic examination of the samples revealed a well-defined planar fiber structure produced by the cold rolling. J was found to he lower when fibers are parallel to the direction of magnetic field penetration than when they are perpendicular. This effect may he a consequence of the interaction of flux movement with fiber boundaries. THE severe changes in microstructure brought about by cold working superconductors leads to profound changes in their superconducting behavior. In particular, the ability of a superconductor to carry a transport current with zero resistance (the maximum value of this current density will be called "J" in the presence of large external magnetic fields (to be referred to as "H") is greatly influenced by the microstructure. In the case of columbium, LeBlanc and Little1 and Autler et a1.2 have observed an increase in J due to cold work. LeBlanc and Little also observed an anisotropy in J in cold-rolled columbium strips, which Hake et al.3-6 have shown to depend upon the angle between H (H ? J) and the rolling plane. An increase in J due to cold work has been found in a variety of high-field superconducting alloys3'4'7-9 as has the anisotropy effect.10 First explanations of why cold work raised J invoked the idea that dislocations carried the high-field supercurrents,8,11 since cold working drastically increases the dislocation density and presumably the number of supercurrent paths. However, recent ideas on the nature of high-field superconductivity together with new experimental evidence reveal that the bulk of certain superconductors can remain superconducting in high fields while carrying high transport currents. These later developments have been discussed by Berlin-court and Hake12 and a comprehensive review has been prepared by Berlincourt.13 According to the ideas of Gorter14 and Anderson,15 one would expect that the influence of microstructure on high-field supercurrent density will depend on tine interaction between microstructure and penetrating flux and on the direction of the Lorentz

Jan 1, 1965

By H. H. Hausner, O. V. Roman, F. V. Lenel, G. S. Ansell

The radial shrinkage during sintering of cylindrical compacts and loose aggregates of copper powder was measured. It was found to be nonuni-form from top to bottom of the samples and to depend upon the method of supporting them. The non-uniformity is due to the effect of gravity forces during sintering. Since gravity has an effect in sintering without externally applied stresses, no sharp dividing line can be drawn between conventional sintering and hot pressing. RECENT investigations of the sintering behavior of compacts1 and of loose powder aggregates2 have indicated that forces, other than those arising from surface tension effects, may play a role in shrinkage. In compacts it was shown that residual stresses from the pressing operation influence shrinkage behavior. In loose powder aggregates gravity forces due to the weight of the powder affect the ratio of shrinkage in the vertical and the horizontal direction. The main effort in the work reported here was to show that gravity plays a role also in the sintering of compacts. A few additional experiments were made confirming the effect of gravity in the sintering of loose powder aggregates. EXPERIMENTAL PROCEDURE Compacts and loose powder aggregates were prepared from irregularly shaped, electrolytic copper powder. Prior to use the powders were reduced 30 min at 400°C in dry hydrogen to remove surface oxides. Then the -325 mesh size fraction was separated from the -100 + 325 mesh fraction. The compacts were pressed at a pressure of 10,000 psi from 50 g of powder in a hardened steel die, 1 in. in diam. The height of the compacts was 0.725 i 0.005 in. An effort was made to get as uniform a green density distribution in the compacts as possible. The walls of the die were lubricated with a suspension of 3 pct of zinc stearate in acetone and the compacts were pressed using double action by first pressing the powder at 1200 psi with the die barrel supported, then removing the sup- ports and pressing to final pressure of 10,000 psi with the die barrel floating. The pressure was maintained for 10 sec. The compacts were sintered at a temperature of 925°C, generally for 1 hr. In order to maintain uniform temperature they were sintered in boats made from cylindrical copper blocks. The blocks were 2 in. in diam, either 2 or 2 1/2 in. long and, split to form the body of the boat and a lid. The body of the boat contained a cavity 1 3/8 in. wide, 1 in. deep and either 2 1/8 or 1 3/8 in. long. The longer cavity accomodated two samples, the shorter one only one sample. The uniformity of temperature distribution within the boats was checked with thermocouples welded to the top and bottom of the samples. The maximum variation between top and bottom temperatures was i 1/2°C. The actual sintering temperature was held constant within ±2°C. In order to determine the effect of gravity forces, i.e., the weight of the compacts, upon shrinkage, they were supported in the following ways during sintering: a) Full Bottom Support. The compacts rested either on a flat alundum disk or on alundum powders. b) Partial Bottom Support. The compacts rested on a graphite cylinder, 0.3 in. in diam which formed a projection on a larger graphite disk. It is difficult to balance the compact on the small projection. To avoid having the compact tip, a small hole was drilled through the compact and through the graphite disk and its projection. The graphite disk was then suspended from the lid of the boat by a thin iron wire which passed through the holes in the disk and the compact. c) Top Support, first type. A hole 3/32 in. in diam was drilled diametrically through the green compact 3/16 in. from the top of the compact. The compact was sintered suspended from an alundum rod (thermocouple protection sleeve) inserted into the hole. d) Top Support, second type. A hole was drilled axially through the center of the compact. The upper part of the hole from the top surface of the compact one fourth of the way down was 1/16 in. in diam; the lower part of the hole from the bottom surface three fourth of the way up was 3/32 in. in diam. The compact was suspended from the lid of the boat by an iron wire passing through the upper part of the hole and then tied into a knot. The loose powder aggregates were made by filling l in. deep, l in. diam cylindrical graphite molds with -325 mesh powder. To achieve uniform density in all the loose powder aggregates, the powders were settled in the molds by placing the

Jan 1, 1963

By H. Margolin, A. Coucoulas

Fused alumina or silica crucibles were used as the containing vessel. X-ray powder photographs were taken with CrKcll radiation and the use of Straumanis type Norelco cameras of 114.6 mm diam. Crystallographic data for these compounds are shown in Table I. These results are in agreement with others of this series reported previousiy by Wernick and Geller.l The abnormally large atomic volume of Eu and Yb metal3 is manifested in EuAl2, and YbAl2, when one compares them with the compounds reported in Ref. 1. However, the behavior of Yb in the Ni compound is the same as that observed in Ni5Yb having the Cu5Ca structure.4 Thus, it appears that Yb has a valence closer to 3 only in the Ni compounds; i.e.. the 2s and Id electrons are lost to the conduction band.1,4 Europium in EuAl2 appears to have a valence closer to 2. In previous work.' X-ray patterns of ingots of NdCo2 indicated a multiphase material with faint indication of the presence of a phase having the MgCu2 structure. It was thought that NdCo2 formed peri-tectically from the melt, resulting in a multiphase system when cooled under nonequilibrium conditions. An X-ray pattern of a sample from a melt cooled more slowly than in past work showed that the major phase was NdCo2. The lattice constant, Table 1, is in excellent agreement with the value one can predict from the data of Ref. 1. One of the other phases was identified as Co5Nd. The author wishes to thank J. H. Wernick for his guidance in this work, and D. Dorsi for the preparation of these compounds. 'J. H. Wernick and S. Geller: AIME Trans., in press. 'J. H. Wernick and S. E. Haszko: to be published. 'F. H. Spedding and A. II. Daane: Progress in Nuclear Energy, Series 5, Eds.: H. M. Finniston and J. P. Howe, McGraw-Hill Book Co., 1956. 'S. E. Haszko: to be published. 'J. H. Wernick and S. Geller: unpublished work. 6J. 11. Wernick and S. Geller: Acia Cryst., 1959, vol. 12, p. '162. A reinvestigation of the lattice parameters of Ti-Sn alloys by the present authors has revealed consistently hiher c and a values than those obtained by Worrier. The difference is most pronounced in the c-parameters which are, therefore, used as a basis of comparison. This discrepancy was not due to air contamination, since precautions were taken to exclude this possibility. Specimens for Debye-Scherrer photograms were prepared by arc-melting 15-g buttons of Bureau of Mines titanium and 99.99 pct Sn, with compositions of 6, 8, 10, and 12 at. pct Sn. These buttons were forged under an oxygen-acetylene torch to 1/8-in. sq rods to produce relatively fine grained material. Scale and some surface were ground off, and the rods, after wrapping in molybdenum and titanium sheet, were vacuum annealed 15 min at 800 °C to remove hydrogen. Heat treatment of one of the samples at 875°C to produce ß and reveal a at the surface showed no surface contamination. Following the vacuum treatment, the specimens were wrapped in molybdenum and annealed for 1 week at 800°C under two atmospheres of argon. After water-quenching, the rods were ground so that the thickness tapered to 0.1 mm at the tips. The ground specimens were then recapsuled as previously and reannealed 1 hr at 800°C to remove cold work. The

Jan 1, 1961

By R. D. Daniels, T. W. Wood

The tensile properties of columbium and Cb-H alloys containing up to 455 ppm H were studied as a function of temperature and strain rate. Hydrogen, introduced into columbium at elevated temperatures, using a thermal -equilibrium technique, embrittled columbium most severely at about —77°C. This elnbrittle ment occurred even at hydrogen concentrations of an order of 20 ppm. At higher temperatures, the hydrogen tolerance of columbium increased in relation to the increased solubility of hydrogen in tile metal. Below this temperature hydrogen tolerance, as determined by ductility and fracture stress, increased slightly. Strain rate had little effect on the tensile results for cross-head speeds over the range 0.002 to 2.0 in. per min. Strain aging during the tensile test appears to explain the ductility mininmum at —77°C. The apparent increase in hydrogen tolerance at lower temperatures is attributed to the low mobility of hyhogen. Experiments were performed in which samples were prestrained in tension at room temperature and tested to failure at —196°C. Results suggest that hydrogetz segregation to preformed crack nuclei can cause subsequent embrittlement even at temperatures where hydrogen mobility is too low to cause embrittlement in a normal tensile test. COLUMBIUM is an example of the class of bcc metals with ductile-brittle transition temperatures sensitive to the presence of interstitial atom contaminants. Hydrogen is one of these embrittling contaminants. The embrittling effect of hydrogen is less potent, perhaps, in columbium than in some of the other bcc refractory metals, but it is still a problem of both theoretical and practical interest. Unlike hydrogen in iron and steels, hydrogen in columbium is exothermically rather than endo-thermically occluded. The embrittlement process in exothermic systems has not been studied as extensively as that in endothermic systems, especially at hydrogen concentrations below the limit of solubility. The purpose of this investigation was to evaluate the embrittlement process in initially pure columbium as a function of hydrogen content, temperature, and strain rate. The Cb-H phase diagram, according to Albrecht et al.,1 is shown in Fig. 1. Columbium reacts exothermically with hydrogen producing a solid solution at concentrations of less than about 250 ppm (parts per million by weight) H at room temperature. At concentrations above the highly temperature-dependent solvus a second phase is formed. Like many similar hydrogen-metal systems,2 his system exhibits a miscibility gap with respect to hydrogen solution. Albrecht found the critical temperature of the miscibility gap to be about 140°C, the critical concentration to be 0.23 atom fraction hydrogen, and the critical pressure to be 0.01 mm Hg. Above 140°C there is a solid solution of increasing lattice constant extending across the phase diagram. Hydrogen concentrations of particular interest in this investigation were those below the limit of solubility in columbium. At hydrogen concentrations above the limit of solubility, columbium will contain the hydrogen-rich second phase and will be brittle under most testing conditions because the hydride generally precipitates as platelets with coincident matrix lattice strains.1'3 At hydrogen concentrations below the limit of solubility, the tensile behavior of columbium is expected to be more sensitive to the interrelationships between hydrogen concentration and mobility and the testing variables such as temperature and strain rate. Literature references to the hydrogen embrittlement of metals, especially ferrous alloys and titanium alloys, are too voluminous to mention. It is only recently, however, that detailed studies of the hydrogen embrittlement of columbium have been undertaken. Wilcox et a1.4 studied the strain rate and temperature dependences of the low-temperature deformation behavior of fine-grained are-melted columbium (1 ppm H) and the effect of hydrogen content (1,9, and 30 ppm H) on the mechanical behavior of columbium at a series of temperatures for a single strain rate. A strain-aging peak was ob-served at about -50°C which was attributed to the presence of hydrogen in the metal. Eustice and carlson5 studied the effect of hydrogen on the ductility of V-Cb alloys at a series of temperatures over the range -196° to 25°C. Pure columbium was embrittled by 20 ppm H which produced a ductility transition at approximately -70°C. Ingram et al.6 studied the effect of oxygen and hydrogen on the tensile properties of columbium and tantalum. A minimum in the notched-to-unnotched tensile ratio of hydrogenated columbium was obtained at about -75°C, but because of the relatively large hydrogen content employed (200 and 390 ppm) the ductility

Jan 1, 1965

By M. E. Glicksman, G. S. Ansel

It has been shown by Walton and Chalmers,&apos; that the mechanism of the development of solidification textures in castings involves the preferential growth of dendrites along certain crystallographic directions as determined by the influence of prevailing heat-transfer conditions. Specifically, this growth is parallel to the direction of heat flow. The purpose of the present investigation was to determine the applicability of this mechanism to: 1) commercially pure aluminum (99.75 pct) solidified to coarse columnar crystals, 2) an aluminum-silicon casting alloy (5.25 Si, 0.38 Fe, 0.02 Cu, 0.10 Ti, 0.002 S) cast to a fine-grained structure under complex and reproducible heat transfer conditions. PROCEDURE AND RESULTS 1) Specimen Preparation—Using a technique similar to that employed by Northcott and Thomas,2 samples were melted in the directional solidification mold, Fig. 1, by heating the entire assembly to 670° C. The mold was then end cooled using a water jet. From considerations of harmonic analysis, the likely distribution of isotherm normals encountered by the growing crystals is shown in Fig. 1. 2) Orientation Analysis—The pure aluminum sample froze to large columnar crystals, nucleated close to the metal diaphragm, with the growth direction parallel to the mold axis. Using the back-reflection Laue technique, the growth direction of these crystals was determined to be a <100>, which coincided within 53 deg to the mold axis. Metallographic examination of the relatively fine-grained aluminum-silicon sample revealed a dendritic mode of growth having its primary dendrite arms along isotherm normals. Back-reflection Debye-Scherrer patterns, taken with the specimen rotating about its cylinder axis, yielded rings displaying symmetrical arcing, thus proving that the sample did, indeed, possess the solidification texture inferred from the preliminary metallographic examination. To determine the extent and orientation of the texture in the aluminum-silicon alloy, a density distribution of the (111) poles of the sample was plotted using the transmission Debge-Scherrer

Jan 1, 1960

By T. H. Courtney, G. W. Pearsall, J. Wulff

The mechanism, of the decrease in transition temperature of Nb3Sn was studied. Presintered Nb3Sn powder compacts were heated in a dynamic vacuum at elevated temperatures. Loss of tin resulted from these heat treatments and transition temperature as a function of tin loss was discontinuous at a critical value of tin loss. In general, decreases in transition temperature were correlated with deviations from AS a class, the A15 structure-type (also known as Cr3O or ß W) compounds have the highest superconducting transition temperatures.&apos; In this class are stoichiometry and presence of vacancies in niobium sites. The effect of vacancy distribution on the physical properties of Nh3Sn is considered. It is concluded that the close-packed atomic A chain in the A3B A15 structure must be preserved both in coutinuity and direction if good superconducting properties are to he obtained. tempting to associate these high transition temperatures with the most unique crystallographic feature of the A3B structure: the three close-packed, orthogonal chains of A atoms.&apos;0"&apos; There are at least three principal mechanisms by which the perfection of these "A-atom chains" could be interrupted: changing stoichiometry, inducing disorder, or introducing vacancies. Departures from stoichiometry in either direction in V3Ga lower the transition temperature.7&apos;8 In niobium-

Jan 1, 1965

By J. O. Brittain, E. P. Lautenschlager, D. A. Kiewit

Compression tests were run in the temperature range of 700° to 900°C ox 0&apos; phase NiAl intermetal-lic alloys of several grain sizes. At these temperatures the minimum strengths were observed at the stoichiometric composition. While significant increases in strength occurved in both the low-nickel (vacancy) and high-nickel (substitutional) regions, the highest strengths were found in the high-nickel region. During deformation serrated flow was sometimes observed in the low-nickel alloys. After deformation transgranular cvacking and deformation striations were observed in all compositions tested. AS part of a general investigation of the properties of NiAl inter metallic compounds, a preliminary study of the role of point defects upon plasticity was made by high-temperature compression tests on ß&apos; NiAl specimens of several grain sizes and compositions. ß&apos; NiAl is an intermetallic compound having a CsCl structure and a rather wide range of composition from A1-45 at. pct to 60 at. pct Ni.1 According to Bradley and Taylor2 and to cooper,&apos; it possesses a defect lattice in which departures from stoichiometry in the direction of decreased nickel content lead to the presence of vacant nickel sites (although Cooper&apos;s work indicates that a small amount of substitution also occurs) whereas departures on the high-nickel side lead to substitution of nickel on aluminum sites. NiAl forms congru-ently from the melt at approximately 1650°C,1 and thus has a higher melting point than either of its component elements. Up to this time, although this and other high-melting intermetallic compounds have been suggested for elevated-temperature usage,4 only the hardness4 and a few tensile-strength measurements5 have been reported for NiAl at high temperatures. In the present investigation the effects of composition upon the compressive-strength properties in a range of 700° to 900°C have been measured for NiAl of several grain sizes. EXPERIMENTAL PROCEDURES The alloys were made as described elsewhere6 from an A1-46.8 at. pct Ni master alloy furnished by the International Nickel Co. with additions of high-purity nickel and aluminum. The charges were vacuum-induction-melted in A12O3 crucibles with small amounts of helium added to the atmosphere to suppress vaporization. They were cooled slowly from the melting temperature to achieve uniform grain size. In order to refine the as-grown grain size a special rolling technique was developed. Alloys were packed into 0.10-in. wall-type 302 stainless-steel tubes which were partially filled with magnesium oxide to prevent bonding between the alloy and the steel jacket. The ends of the tubes were closed by hot forging, and the packets were then hot-rolled. The alloys with greater than 50 at. pct Ni were rolled at 1100°C, but it was found necessary to increase the temperature to 1350° C before alloys with less than 50 at. pct Ni would roll without cracking. With these temperatures, reductions as high as 48 pct were achieved in a single pass. The rolled alloys will hereafter be referred to as "fine grained" whereas the as-grown material will be designated "coarse-grained&apos;&apos;. The compression specimens were made by cutting square cross-sectional pieces, approximately 3/16 by 3/16 by 1/2 in., with a water-cooled diamond cut-off wheel from the as-grown or the rolled alloys. Specimens were ground to their final dimensions by polishing through 3/0 grit silicon carbide papers. The final shape was a rectangular parallelepiped of square cross section having a height-to-width ratio of 3:1. Compression testing was carried out in a compression rig of our own design mounted on an In-stron Floor Model. The specimen chamber could be heated to 1000°C and was controlled within ±2°C. The compression rig was enclosed within a bell jar and was maintained at a 50 µ of mercury vacuum throughout the duration of the test. The test cham -ber was heated from room to test temperature within 15 min. Specimens were then held at the test temperature 30 min prior to testing. Previous experiments indicated that no grain growth would occur within this time. An Instron Variable Crosshead speed unit was used to adjust for small variations in specimen lengths in order to have a constant initial strain rate, €, for all specimens of a group. For the fine-grained specimens the strain rate was changed rapidly at constant temperature by a factor of 10 with the speed lever on the Instron. For a given € the compression data was analyzed in terms of true plastic strain (E) and true compressive stress (0).

Jan 1, 1965

By J. O. Brittain, E. Lautenschlager

An investigation was conducted on fine grained airon wire to measure the influence of the temperature of deformation on strain aging near room temperature. Specimens were deformed various amounts at 77°, 195°, or 273°K and aged. The strain aging was followed by either internal friction or return of the yield-point measurements. The results show that strain aging occurs in three stages. During the first stage there is small, almost immediate return of the yield point. The solute carbon concentration, as mesured by internal friction, remains constant in stage I but is lower than the concentration in the unstrained condition. In the second stage, the solute concentration decreases while the magnitude of the yield point increases. In the third stage, the solute atoms continue to drain from the solution, the yield point approaches a maximum, and the strain-hardening coefficient and flow curve increase. The kinetics of the strain aging reaction are not the same for the two sets of measurements since the internal friction results lag behind the yield-point measurements. However, the strain-aging kinetics measured at 44° and 64°C showed no effect due to the difference in initial deformation temperature; nor were the strain aging kinetics influenced by low-temperature anneals at 77°, 195°, and 273°K. 1 HE object of this investigation was to measure the effect of initial deformation temperature on the strain aging of a-iron by tensile tests (i.e., return of the yield point) and internal friction methods, to correlate the results of the two measuring methods, and to measure the effect of low-temperature annealing (<273°K) after low-temperature deformation upon strain aging. The experiments were performed on fine-grained a-iron wire containing 0.02 wt pct c.l According to Thomas and Leak,&apos; return of the yield point and internal friction are similar measures of strain aging since both are dependent on solute atoms leaving the solid solution. The decrease in internal friction as a function of aging time is indicative of the removal of solute atoms from the solid solution, while the return of the yield point as a function of the aging time gives the rate of arrival of solute atoms at the dislocations. According to Cottrell and Bilby,3 during aging the solute atoms create an "atmosphere" which locks the dislocations and causes a return of the yield point on subsequent testing. It has been shown that after low-temperature neutron bombardment, a-iron goes through a stage of recovery at low temperatures which can be attributed to the annealing of iron interstitials&apos; and/or vacancies.4 If, after low-temperature deformation, there is an interaction during a low-temperature anneal between mobile point defects and the solute atoms (i.e., carbon atom interaction with vacancy or iron interstitial), it is possible that some solute atoms will be found at defect sites other than dislocations. Such changes in the sinks for the carbon atoms might be expected to alter the strain-aging kinetics sufficiently to be detected by either inter-

Jan 1, 1962

By F. V. Lenel, J. A. Dromsky

The influence of thermal and mechanical treatments upon the elevated-temperature stability, the microstructure, and the mechanical properties of aluminumaluminum oxide alloys is investigated. Compacts from atomized and flake aluminum powders were sintered at temperatures just below the melting point of aluminum in a vacuum of 10-4 Torr for several hours and were then hot-extruded. During this treatment the hydrated oxide present on the surface of the powder particles decomposes, the water vapor produced reacts with the aluminum forming additional oxide, and the hydrogen developed is removed by diffusion to the surface. Extrusions of compacts so treated are stable at temperatures up to the melting point of aluminum and do not form blisters and internal defects typical of extrusions from untreated powder. Electron micrographs of extrusions from unsintered compacts show long parallel oriented platelets typical of the IN previous investigations1,2 the properties and structure of aluminum alloys were described which had been produced by cold compacting aluminum powder and then hot pressing and extruding the compacts. Both the structure and the properties of these alloys differ significantly from those of commercially produced aluminum-aluminum oxide alloys. When commercial alloys are produced, they are given a sintering treatment in air at about 600°C between cold compacting and hot pressing.3 During this treatment the hydrated oxide, which forms the coating on the aluminum-powder particles from which the alloys are prepared, is decomposed.4 The chemically bound water which is released reacts with the aluminum and forms aluminum oxide and hydrogen. Most of the hydrogen is eliminated by hydrated oxide skins on the original powder particles, while the oxide particles in extrusions from sintered compacts are broken up. The strength of extrusions from treated powder is somewhat lower, but their ductility is considerably improved over that of extrusions from untreated powder. The slip-trace patterns on electron microgvaphs of extrusions which had been strained in tension before replication indicated that the grain size of the extruded alloys was approximately the same as that of the original powder particles. Coarse-grained alloys were produced by severe cold work and annealing of the extrusions. They have significantly lower room-temperature strength, but about the same ductility as the vacuum-sintered fine-grained alloys. The size and shape of oxides in the coarsegrained alloys is similar to those of the fine-grained alloys, but the particles are somewhat more uniformly distributed. diffusing to the interior or exterior surfaces of the compact, but it is difficult to eliminate all of it because the solubility of hydrogen in solid aluminum is very low even near its melting point. Extruded alloys which are not sintered before hot pressing and extrusion appear quite sound upon metallo-graphic examination, but develop severe surface blistering and internal fissuring when they are heated to elevated temperatures after extrusion. Fissures and blisters have been observed even in commercial alloys which had been sintered in air, although they are much less severe.&apos; Because of the importance of this sintering treatment it was studied in this investigation in a modified form, using vacuum sintering rather than sintering in air, to insure more complete elimination of occluded hydrogen. The technique is described and the effect of the treatment upon the structure of the alloys is documented. It has been known for some time that extruded aluminum-aluminum oxide alloys are very finegrained, but an exact delineation of grains in electron micrographs has not been possible. In the conventional metallographic-etching techniques etchants attack the interface between the second-phase particles and the matrix in the alloys much

Jan 1, 1964

By David V. Ragone, Richard E. Balzhiser

The liquidus uranium concentration in the U-Bi system is given by the following expression for the temperature range 400° to 800°C: No break was observed in the curve over this temperature range. The partial molar enthalpy change for uranium in the liquidus reaction, UBi2— U + 2Bi, was found to equal 12,300 cal per g mole. Copper produced a continuous decrease in the liguihs uranium concentration at 600°C. The presence of copper in the solvent was observed to affect the uranium activity coefficient according to the following expression: duced no change in the liquidus combosition below 0.6 at. pct Pd. Higher palladium concentrations sharply depressed the uranium concentration. SOLUTE behavior in molten alloys has been shown to be strongly influenced by the presence of additional species. Much attention has been given to such phenomena in iron-base systems where a number of alloying elements and/or impurities are likely to be present in small but significant quantities. Frequently, the interaction of these solutes has altered their thermodynamic behavior to the extent that reaction equilibra are appreciably influenced. Consequently, much of the information available for binary behavior must be reevaluated when additional components are likely to be present. Similar interactions can be expected to occur in bismuth-base solvents. Interest in the use of bismuth solutions of uranium as reactor fuels has stimulated investigators to explore the effect of various elements on the liquidus uranium concentration. Criticality requirements necessitate close control of the uranium concentration which, at the anticipated operating temperature of 500°C, approaches saturation. Consequently, elements which suppress the liquidus concentration could produce serious reactivity problems. Since the fuel solution is cer- tain to contain additives, such as magnesium and zirconium, for corrosion inhibition as well as small concentrations of fission products and corrosion products, a better understanding of the possible interaction phenomena is mandatory. This need stimulated experimental programs at the Brookhaven National Laboratory and elsewhere to determine precisely the liquidus uranium concentration in the bismuth-rich portion of several ternary systems. Early experimental efforts were directed toward an accurate dcmtermination of the U-Bi liquidus over the temperature range from 300&apos; to 800°c. As shown in Fig. 1, the results to date exhibit considerable scatter. The investigations of Bareis,&apos; Teitel,2 Greenwood,3 and Cotterill and hon4 agreed well below 700°c. Greenwood and Teitel extended their studies to higher temperatures but failed to concur in their results. A more recent study by Schweitzer and weekss at Brookhaven National Laboratory between 300&apos; and 725°c, produced values 15 pct lower

Jan 1, 1962

By J. S. Kirkaldy, R. J. Brigham

AS part of a program to investigate the diffusive properties of dilute ternary austenites we have made a determination of the effect of chromium on the activity of carbon in ? iron. Samples of pure iron and Fe-Cr alloys were simultaneously equilibrated at 1000°C with atmospheres of controlled CO/CO2 ratio following the procedures of Darken and Gurry 1 and smith.&apos; The 0.020 in. thick samples were analysed for carbon by microcombustion analyses3 to yield a set of isoacti-vity curves. The latter were converted to activity coefficient (standard state at infinite dilution) plots by combination with Smith&apos;s data2 for the activity of carbon in pure iron. Table I shows the compositions of the base alloys used while Fig. 1 shows the experimental results superimposed on a set of curves generated by the relation In?C=6.9NC- 10.7 Ne In the notation of wagner4 the interaction parameter is the second coefficient on the right, Sgr = - 10.7 This can be compared with a rather inaccurate value deduced from the transient equilibrium diffusion data of Kirkaldy et al.&apos; as The authors are indebted to the American Iron and Steel Institute for financial support. This material is condensed from a B.Sc. Thesis submitted to Mc-Master University by R.J.B.

Jan 1, 1963

By L. C. Brown, J. S. Kirkaldy

AS part of a program to investigate the diffusive properties of dilute ternary austenites, we have made a determination of the effects of cobalt on the activity of carbon in y iron. Samples of pure iron and Fe-Co alloys were equilibrated at 1000°C in controlled CO-C02 atmospheres, following the procedure of R. P. smith.&apos; The 0.010-in.-thick samples were analyzed for carbon by microcombustion analysis2 to give a set of isoactivity curves. The latter were converted to activity-coefficient (standard state at infinite dilution) plots by combination with Smith&apos;s data&apos; for the activity of carbon in pure iron measured in a CO-C02 mixture. Table I shows the composition of the base alloys used, while Fig. 1 shows the experimental results superimposed on a set of curves generated by the relation In the notation of Wagner,&apos; the interaction parameter is the second coefficient on the right, Eq. [I] adequately correlates the experimental points for those alloys which were prepared from electrolytic iron by arc-melting (2,4, and 7 pct Co). The results for the 10 pct Co alloy (supplied by Crucible Steel Co.) do not correlate with the others. In fact, the experimental points for this alloy correspond to an interaction parameter of It is possible that the interaction parameter is a function of concentration for large cobalt additions, but we are inclined to attribute the discrepancy to the presence of a significant amount of aluminum added to this alloy for deoxidation purposes (Table I). Preliminary measurements for the system Fe-C-A1 have indicated an interaction parameter of Which implies that the effect of aluminum in solution on the carbon activity is sixty times greater than the effect of an equal weight percentage of cobalt. These observations cast some doubt on the precision of the results of Chandhok, Hirth, and Dulis who used this same 10 pct alloy for their experiments, obtaining an interaction parameter of E = 2.2. There is considerable doubt as to the activity of a plane Fe-C system. Using a CH4-Ha mixture, Smith obtains cg = 6.1 for the effect of carbon on the activity of carbon in austenite, rather than the value of 8.9 given in Eq. [I]. The use of CHa-Ha mixtures has recently been questioned by Kaufman, Radcliff, and cohens who state that there is some possibility that other hydrocarbons are formed. Fortunately, the determination of the interaction parameter is not sensitive to the coefficient of Nc. For example, using the CHI-H2 results we obtain a value which is almost the same as that obtained using the CO-CO, results. The authors wish to thank Mr. E. J. Dulis of the Crucible Steel Co. of America for supplying us with samples of the 10 pct Co alloy used in their original work. Financial assistance from the American Iron and Steel Institute is gratefully acknowledged.

Jan 1, 1963

By R. H. Edsal, G. Horvay

The transient one-dimensional heat-conduction equation is solved for two semi-infinite media, at different initial temperatures, brought into (poor) thermal contact. It is shown that the two interface temperatures gradually approach the well-known, instantaneously assumed, common interface temperature of the case of zero contact resistance. The present analysis, with slight modifications, may be used in fair approximation also for the class of problems involving a change of phase. One particular application of the boundary value problem solved in this paper concerns the determination of the temerature distribution in metal castings and molds.P This problem has been treated extensively by analytical methods (see e.g., the literature listed in Refs. 1 to 4) by electrical analogs (see e.g., Refs. 11 to 14) and also by experimental methods (see the literature listed in Refs. 4, 5), but prior to the work of Pellini and Ruddle the experimental results were rather unreliable. Immediate motivation for the work described in this paper was to better understand the results of Pellini,&apos; which are typified by the curves of Fig. 1. Pellini cast 20-in. high, 7-in. sq steel ingots into cast-iron molds of various thicknesses. He measured the temperatures at mid-height, at a number of stations in the casting and the mold, and obtained the cooling curves shown in Fig. 1. The most conspicuous thing about Fig. 1 is the large temperature discontinuity at the interface between casting and mold, due presumably to the shrinking away of the casting from the wall and the attendant creation of an airgap, as the casting cools. Such a contact resistance slows down the anticipated freezing rate; an analytical prediction of this is of much interest in foundry practice. The determination of the effect of contact resistance in the presence of a change of phase will be dealt with, by an approximate method, in a separate paper.&apos; In the present paper the much simpler problem is considered in which there is contact resistance but no change of phase. This problem frequently arises in the analysis of aircraft structures.+ It can initial temperature, and may be regarded as semi-infinite. We suppose the thermal properties in the two media to be time, temperature, and space independent; there are no sources or sinks within the media. In Fig. 2(a) we illustrate, schematically, the case of no contact resistance. The semi-infinite media "0" and "2:&apos; initially at temperatures 8 (- m) and 8(+ -), respectively, are brought into contact at time t =0. A common interface temperature 8,i = is instantaneously established, and thereafter remains constant. Temperature curves are drawn for three instants of time. When there is contact resistance between the two media, the temperature equalization occurs as sketched in Fig. 2(b). Fig. 2(c) illustrates a temperature curve, using the dimension-less notation Barber-Weiner-Boley6 have stated the equations [23a, b] given below, which govern the heat transfer in the two media, and solved them for a rather complicated special case. In their example both media "O" and "2" are finite, are insulated at their far ends, and there is steady heat input into medium 2. In Eq. [27] we give the general solution of the most important special case, where the two media are semi-infinite and there are no sources or sinks. In this case the results may be stated in simple closed form. In Fig. 3, to be discussed in the next section, we illustrate the variation of the interface temperature when steel at 2760" is brought into contact with iron at 100". This example, if we disregard the effect of the heat of fusion, is comparable to Pellini&apos;s experimental results, Fig. 1. (Unfortunately, however, experimental determination of the interface temperatures was difficult to carry out, and hence Fig. 1 is not very accurate near the interface.) In Figs. 4 and 5 of the following section, we similarly compare Pellini&apos;s sandcasting tests with analytical results for the case where steel at 2760" is brought into contact with sand at 100". It will be pointed out that, insofar as the interface temperatures are concerned, heat of fusion has a minor effect, and so the present approximation, with small modifications, may be

Jan 1, 1961

By Paul E. Blackburn, Joan B. Berkowitz-Mattuck, Edward J. Felten

The oxidation behavior of MOSi2 has been studied between 450° and 650°C, the temperature region where "pesling" occurs. Disintegration ("pest-ing") of MoSi2 is shown to occur in the presence of oxygen, but not nitrogen, carbon dioxide, carbon monoxide. or argon. The rate of disintegration is extremely sensitive to oxygen pressure. The crack density of polycrystalline MoSi2 increases ivith lime at temperature. All kinds of cracks are observed: THE excellent oxidation resistance of MoSi, at temperatures of 1000 to 1700°C promises to have important technological benefits. However. the ap- Ihose which are confined within a single grain, those that ci&apos;oss grain boundaries transversely, and those that follow grain boundaries. Laue photographs verify the existence of Iranscryslalline cleavage. Single crystals of MOSi2 do not "pest". Tlrcd solrlbility of oxygen in MoSi2 is extremely low, no lattice changes being observed as a result of exposure of MoSi2 to oxygen in the "pest" temperature range. plicability of MoSi2 is somewhat restricted by the occurrence of a completely destructive oxidation of the intermetallic phase at intermediate temperatures (300" to 6003C). This phenomena was ternled to be the "MoSi2 pest" by Fitzer who first observed it.&apos; Molybdenum disilicide is a metallic material in both physical appearance and electrical properties.

Jan 1, 1965

By B. Lustman

IT has been known for a number of years that the addition of certain alkaline-earth and rare-earth metals to nickel-chromium base electric resistance alloys causes marked increase in their oxidation resistance as measured in an intermittent oxidation test similar to the ASTM—B 76-39 test. However, the mechanism whereby such additions confer protection is still unknown. On the basis of the experimental observation that the increase in life in intermittent tests of nickel-base alloys is proportional to the atomic radius of the added element, Hessen-bruchl has proposed that the added metal ions occupy holes in the oxide lattice which prevent diffusion of nickel ions in the oxide. Horn2 has postulated that the effect of such additions is to accelerate the rate of diffusion of chromium atoms in the metal and thus to favor the formation of Cr2O3 scales. Hickman and Gulbransen3 concluded from electron diffraction observation that the addition of the elements in question results in the formation of a barrier to the diffusion of nickel ions to the surface. In connection with some experiments conducted to develop a test for the resistance to oxidation of alloys in massive form under conditions of intermittent heating and cooling, some features of the oxidation of nickel-chromium base alloys were revealed which may serve to elucidate the mechanism of protection conferred by rare-earth and alkaline-earth elements. Specimens of cylindrical shape 0.360 in. diam x 0.37 in. long were placed in alumina thimbles and inserted into and withdrawn from a Globar-heated furnace operating at 2150°F at 7.5-min intervals. The weight of oxygen absorbed as well as the weight of oxide spalled were measured at intervals. With the particular experimental conditions used, the specimens in a 7.5-min cycle were at temperature for 2 min which corresponds to the heating time of the ASTM test. The weight changes of similar specimens under conditions of continuous heating in air at 2150°F were also measured. The specimens after oxidation were examined metal- lographically and samples of the spalled oxide collected for X-ray diffraction identification of the phases. The specimens used were from the same lot of material used by Hickman and Gulbransen3 and had the compositions shown in table 1. Included in table I are results of ASTM life tests on the materials in the form of wires. These materials, their composition and the ASTM life test data thereon were all supplied by F. E. Bash of the Driver-Harris Co. It may be noted that alloy 13246 of 80 pct nickel, 20 pct chromium nominal composition showed the shortest life in the ASTM test; alloy 12246 with the addition of small amounts of the elements zirconium, calcium, and aluminum, intermediate life; and alloy 12046 with the further addition of silicon, the longest life. In fig. 1 are shown the results of intermittent oxidation tests made on bulk specimens at 2150°F as well as continuous tests conducted at the same temperature. Duplicate tests were made on each specimen. The ordinate scale, inches of metal oxidized, was derived from the experimentally observed weight gain of oxygen by assuming the scale to be entirely Cr2O3. It may be noted that the metal-loss curves during intermittent oxidation show a constant or continuously increasing rate of weight

Jan 1, 1951

By H. C. van Elst

Ultrahigh-speedphotographic and electronic meth-ods were applied to an investigation of details of brittle-fracture propagation in steel. The brittle fractures studied were obtained in steel plate with the aid of a Robertson apparatus. It was found that a brittle fracture proceeds by discrete steps ranging from 30 mm near the stop temperature to less than 2 mm at lower temperatures. The halting FROM prior metallographic observations of brittle fracture in steel&apos; it could be concluded that the distribution of mechanical twins along a brittle fracture was similar to the distribution of mechanical twins induced by explosive deformation. It was therefore assumed that a running brittle fracture created stress waves, cf. Refs. 2-7. An emission of stress waves by a brittle fracture, however, seems only conceivable if the fracture propagates by discrete steps. For this reason a study of the details of times between successive steps drop in this tem-perature region from 20 usec to about 1 psec. The stepwise propagation mechanism is accompanied by an intermittent emission of stress waves of the order of 100 to 200 kg per sq mm. These stress waves seen1 to play an important role in the mechanism of brittle fracture as will be discussed. brittle-fracture propagation was undertaken to investigate the possible determination of the fracture steps and the emitted stress waves associated with the assumed mechanism. The more practical object of this work is the development of a test method for the determination of the ductile-brittle transition in small specimens. This has special advantages for the study of irradiation damage in steel. In this test method, which will be published in a following paper, the stress waves emitted by an actual brittle fracture are reproduced with explosive or electrical means and are then transmitted through small specimens at various temperatures. In the present paper only the results of the brittle-fracture study will be reported.

Jan 1, 1964

By Y. C. Liu

THE existence of mechanical twins in bcc metals has long been known. With recent intensive interest in the mechanism of twin formation and its role in plasticity and crack initiation, a study of the general Characteristics of twin intersection appears pertinent. The scope of the present note will be limited to the crystallography of the twin intersections of (112) twins, without consideration of its mechanism, movement of atoms, crystal structure, or the strain energy involved at such an intersection. The twinning elements of (112) twins are considered to be K1 = {112}, n1 = (111) and K2 = {112}, n2 = (111) with a twin shear of 0.707. The crystallographic features of twin intersections have been worked out in detail by Cahn.1 The present work applies the general principles postulated by Cahn to the intersections of (112) twins. The basic conditions for the twin intersection are: 1) The trace of crossing (A) and the secondary (C) twins in the planes of the crossed twin (B) must be parallel. 2) The direction (n1) and magnitude (s) of shear must be identical in the crossing and secondary twins. Also the sense of shear must be the same. These two conditions have to be fulfilled in order to maintain geometrical continuity at the twin interfaces. Fig. 1 shows the perspective representation of how these two conditions are fulfilled at the intersection. This type of intersection will be named Type-I. It is the purpose of this note to point out the existence of another type of intersection, Type-II, as shown in Fig. 2. In this type of intersection, the crossing twin A remains straight and the crossed twin B has been bent. The two conditions laid down by Cahn must also be met. This leads to the following corollary conditions: 1) The interface between twins B and C must be parallel to the twin habit of crossing twin A. 2) n1c must be parallel to n1A. 3) The twin shear (s) of twin C must be exactly equal to and in the same sense as that of crossing twin A. Thus, in order for the Type-II intersection to take place, the twining elements of secondary twin C must fulfill the above three conditions with respect to crossing twin A. Let K1 of crossed twin B be (112). All indices of the matrix can therefore be converted into new in-

Jan 1, 1963

By R. P. Smith, L. S. Darken

FOR a high-purity iron-carbon alloy, the phases existing at equilibrium at temperatures slightly above the temperature of the metastable eutectoid are austenite and cementite (hyper-eutectoid) or austenite and ferrite (hypo-eutectoid) and those below the eutectoid temperature (carbdn content > 0.02 pct) are ferrite and cementite. Such an alloy, held in a carefully controlled and measured temperature gradient (about 1 cm per deg) which includes the eutectoid temperature, then quenched and examined metallographicall.y, provides a precise measure of the eutectoid temperature. The samples were hollow cylinders approximately 1.3 cm OD, 0.63 cm ID, and 2.5 cm long, which had been carburized to the desired carbon content at 1000°C with an appropriate hydrogen-methane mixture. In order to cool the samples to room temperature with a minimum change of carbon content and absence of cracks they were quenched in a Cerro Bend bath at 480°C, followed by a water quench to room temperature. Three cylinders were suspended in the furnace1 in a purified helium atmosphere, by a closed end, thin wall, silica tube which also served as a thermocouple well. The top and bottom cylinders served only as a means of making the temperature gradient along the center cylinder more uniform. The temperature was determined with a platinum-platinrhodium thermel calibrated by comparison with a thermel certified (* 0.5OC) by the National Bureau of Standards. After holding in the temperature gradient for 24 to 72 hr the samples were quenched in Cerro Bend at 480°C, followed by

Jan 1, 1960

By C. F. Floe, M. Cohen, M. B. Bever, V. G. Paranjpe

NITROGEN is becoming recognized as one of the important elements in ferrous physical metallurgy. Several investigations indicate that nitrogen plays a significant part in such phenomena as strain aging and temper brittleness. Nitrogen is known to be a powerful austenite stabilizer and may be a useful alloying element in stainless steels. The hard-enability of steels has been found to be increased by nitrogen. The nitriding and carbonitriding pro- cesses are examples of successful industrial application of nitrogen in ferrous materials. For a complete understanding of the various roles played by nitrogen in ferrous metallurgy a knowledge of the phase relations in the binary iron-nitrogen system is essential. The literature contains a variety of iron-nitrogen phase diagrams. Those suggested by Fry, Sawyer,² Epstein and his coworkers,³,4 Lehrer,5 Eisenhut and Kaupp, and Hägg7,8 differ significantly from one another. Moreover, the most recent of these investigations dates back about twenty years. A re-determination of the entire diagram, therefore, appeared desirable. In addition to the published phase diagrams, investigations have been carried out on portions of the iron-nitrogen system. Bramley and Haywood determined the composition and temperature of the iron-iron nitride eutectoid. The maximum solubility of nitrogen in a iron was investigated by Portevin and Seferian10 and by Diikstra. 11 Several investigators have determined the crystal structure of the various iron-nitrogen phases. In fact, Eisenhut and Kaupp6 and Hägg7 based their entire phase diagrams on the results of such studies. Epstein&apos; and Emmett12 reported lattice-parameter measurements on the E (hexagonal close-packed) phase. Osawa and Iwaisumi13 also studied the change in lattice parameters of the a, ? and E phases with nitrogen content. Brill" and Hägg7 showed that the y&apos; phase has an ordered structure, and Hendricks and Kostingsl5 suggested a structural relation between the E and phases. In a recent investigation Jackl6 arefully studied the super-lattice reflections from the y&apos; and phases. Experimental Procedure A large variety of experimental methods has been used by previous investigators in studying the iron-nitrogen system. These methods include thermal analysis, microscopic examination, X ray diffraction, magnetic measurements, dilatometric analysis and anelastic experiments. Thermal analysis is of low accuracy in determining changes in the solid state. This accuracy is further decreased for iron-nitrogen alloys since composition changes will occur during heating or cooling unless extreme care is taken to use a proper atmosphere. Metallographic methods are of small value . because homogeneous iron-nitrogen alloys of sufficient size can be produced only with great difficulty. The dilatometric method is open to the same objections as thermal analysis in that changes in composition may occur during heating and cooling. Lattice parameter measurements by X ray diffraction can be used satisfactorily for determining phase boundaries if cooling is fast enough to prevent structural changes. In view of the limitations of the various other techniques two methods only were adopted in this investigation, (1) X ray diffraction measurements, and (2) a controlled nitrogenizing method. The second method is an innovation for investigating the iron-nitrogen system, and will be described at length. Materials: All iron-nitrogen alloys were prepared from carbonyl iron powder of the analysis shown in table I. The average particle size was about 20

Jan 1, 1951

By C. F. Floe, M. Cohen, M. B. Bever, V. G. Paranjpe

P. Coheur and L. Habraken—We read this paper with great interest and are glad to congratulate the authors for their valuable work, supplying an important contribution to the mechanism of tempering on the carbides in vanadium steels. We are in a good position to appreciate this work since we have been studying, for more than a year, Cr-Mo steels of a composition similar, but less highly alloyed (namely 0.1 pct C, 3 pct Cr, 1 pct Mo). Our results are quite in concordance with the authors&apos;, however, we wish to point out that it is very interesting to use equally the electron microscope in order to observe the variations of microstructure in steels. We have studied simultaneously the evolution of the carbides in situ with the electron microscope, and, after extraction, again with the electron microscope, and then with X-rays. The first results which we have obtained have been communicated at the Congress of Delft (July 1949) and at the "Journees de la Metallurgie" in Paris (October 1949). These may be summarized as follows: After tempering with varying either the tempering temperatures or the tempering times, the carbides show two evolutions. The first one is connected to the carbides existing in the steels, principally in the boundaries of the grains. For some groups of steels these carbides may coalesce and for other groups they may

Jan 1, 1951