By E. S. Bumps

A series of macrographs are presented for the purpose of graphically recording the strain phenomenon that accompanies the energy transition in the Charpy impact testing of a mild steel that is susceptible to strain aging. STRAIN patterns in mild steel Charpy impact specimens were obtained in order to determine whether, on the first appearance of plastic strain during deformation, the initial fracture cracks appear in the region of plastic strain or in the elasti-cally deformed regions between. Although this attempt to locate the initiation of cleavage was not successful, the observed strain patterns illustrating various stress conditions in partially deformed Charpy specimens are presented along with a discussion of the possible dependence of transition energy on the yield phenomenon. Earlier work on the development of strain patterns in mild steel have been reported by Fry1 and later by Jevon.2 Harris, Rinebolt, and Raring3 observed characteristic strain markings on the surface of Charpy V-notch impact specimens fractured above and below the transition temperature which they presented schematically. It is intended that the strain figures presented here will add to the literature a graphic correlation of strain with transition energy in impact specimens. Samples of % in. round hot rolled, 0.20 pct C steel were machined to standard 0.394 in. sq, V-notch Charpy impact specimens. Preliminary testing involved determination of transition temperature, Fig. 1, using a Sontagg impact tester. These data were subsequently used to select temperatures above, within, and below the transition range at which specimens were partially deformed. Partial deformation was obtained by either varying the energy or the testing temperature, see Table I. Macroscopic strain figures shown in Figs. 2 to 19 were produced by several metallographic repolish-ing and etching steps. The macroetchant used was as follows:4 120 g HCl, concentrated; 100 ml water; and 90 g cupric chloride. Strain figures were obtained on the outer surface and on sections through the central portion of the impact specimens in order to determine an approximation of the volumetric strain pattern. In the tensile strain figures reported by Jevon, it was found that strain etching would not work immediately following strain unless the material was heated to 200°C. The impact strain patterns presented here were obtained without this heating, but the specimens were not etched until ten months after straining. This confirms a discussion of Jevon's paper, in which it was pointed out that strain figures can also be developed after aging for long periods of time at room temperature. Hardness of the strained and unstrained portions, revealed by the etched pattern, was explored using R, impressions converted to R, hardness values. Discussion of Results In the impact test, as in the tensile test, some parts of the specimen yield and deform plastically, while other regions are deformed only elastically. The plastic deformation bears a relation to the imposed stress pattern. In the strain figures presented here, the plastically deformed regions are the dark etching ones. The strain figures are always symmetrical because the stress state in the Charpy-type specimen under impact loading is symmetrical. The difficulties encountered to produce initial cracks are intimated in Figs. 2 and 4. At a temperature of —75ºF, the stress was not sufficient to pro-

Jan 1, 1953

By D. Weinstein

Yieldilzg in annealed arc-cast molybdenunz in torsion was studied as a function of strain rate and tem-perature. The temperature dependence of the yield point for different strain rates was used to calculate a heat of activation for the yield point. The heat of activation was not a constant but was approximately a linear function of the stress at yield. It is proposed that the rate effect in yielding is determined in part by a site place-change of C (or other interstitial atom) in the metal. THE low-temperature embrittlement phenomenon in metals and alloys has been known to exist for a long time. Although a transition from ductile to brit-tle behavior has been observed in some close-packed hexagonal metals1 and a face-centered cubic alloy, the most common class of metals exhibiting this be-havior has a body-centered cubic lattice structure. For example, a ductile to brittle transition has been observed in iron,3 molybdenum,4 chromium,5 colum-bium,6 and tungsten.7 In the present investigation, molybdenum specimens were tested in torsion over a wide range of temperatures at three widely separated strain rates, and the temperature for onset of embrittlement was determined. Characteristic of body-centered cubic metals and closely associated with plastic deformation is the appearance of a sharp upper and lower yield point. Theoretical explanation of the yield point in iron and low-carbon steel is due to Cottrell,8 who attributes the phenomenon to the pinning of dislocations by the formation of impurity atmospheres around the dislocations. These atmospheres tend to lock the dislocations and make them more difficult to move. The stress required to move a dislocation and thereby cause plastic deformation is greatly increased, and thus an upper yield point is observed. In addition, theoretical analysis,9 as well as experimental observations, show that the upper yield point is strongly a function of temperature. The upper yield point is observed to decrease with an increase in testing temperature, and above a certain temperature (-700° K in iron) it no longer appears. This is consistent with the concept that thermal vibrations will help free a dislocation from its atmosphere, so that the external stress required to free a dislocation from its pinning atmosphere decreases with increasing temperature. Furthermore, with increasing temperature the equilibrium concentration of impurity atoms around a dislocation decreases exponentially with the result that the dislocation is less firmly pinned. In Cottrell's theory of yield point a static model is visualized in which the pinning atmospheres, particularly interstitial atoms, are immobile, and the dislocations are anchored to stationary positions in the lattice. However, experiments1,7 show the upper yield point to be time-dependent or a function of the rate of straining, a high strain rate causing a high upper yield point. Present theory does not adequately account for the rate dependence of the yield point, and the exact function of the interstitial atom is not under stood. Nevertheless, observation of the temperature dependence and rate dependence strongly suggests that the upper yield point phenomenon is due to the interaction between dislocations and pinning atoms, and that a diffusion mechanism is important in determining the yield point.

Jan 1, 1962

By James H. Bechtold

The yield strength of annealed tungsten was found to have a strain rate exponent 12 times as great as that of low carbon steel. The effects of temperature and strain rate could be correlated through the Zener-Hollomon parameter with a heat of activation associated with yielding of 32,000 cal per g-atom. This heat of activation is independent of strain although both the temperature and strain rate dependence of the yield strength vary with strain. MOST metals have mechanical properties that are relatively insensitive to strain rate, especially at temperatures below that at which creep is important. In iron and molybdenum," however, relatively large strain rate effects are observed in the temperature range where the rapid increase in yield strength occurs which leads to the ductile to brittle transition. In this temperature range Zener and Hollomon' have suggested that the effects of strain rate and temperature T on the yield strength could be correlated through a single parameter, P, in the following manner where Q is a heat of activation characteristic of the metal and associated with some unspecified relaxation process. They also observed that if the temperature is restricted to a relatively narrow range— below room temperature for steel—that the logarithm of the yield strength could be expressed as a linear function of the logarithm of P. From this relation the logarithm of stress should be a linear function of the logarithm of the strain rate at constant temperature: where r will be referred to herein as the strain rate exponent. At a constant strain rate the logarithm of stress should be a linear function of l/T, ay(e = C) ~ eT [4] where q = Qr [5] and is referred to herein as the temperature exponent. These equations have been found to relate the effects of temperature and strain rate on the yield strength of molybdenum in the temperature range wherein the ductile to brittle transition occurs, —75° to +150°C.2 Bechtold and Shewmon3 have shown recently that the ductile to brittle transition in annealed tungsten occurs in the temperature range +150° to +350°C. In this temperature range the yield strength in-

Jan 1, 1957

By S. R. Maloof

In 1945, Hollomon' showed that after plastic yielding and prior to necking under simple tension, both ferrous and nonferrous materials are approximated by an equation of the following form: where, a = true stress K = strength coefficient 5 = true strain n = strain hardening exponent If a material is stress free, a plot of log o vs log 6 would be expected to be a straight line, the slope of which is the strain-hardening exponent (n) and the intercept on the ordinate axis for 6 = 1. is the logarithm of the strength coefficient K. It can be easily shown that the strain-hardening exponent in the above equation is equal to the total uniform elongation prior to necking. Thus, one can determine the total uniform elongation prior to necking from such a plot and, as pointed out by C. W. MacGregor, 2 it is the amount of strain prior to necking which determines the extent to which a material may be deep drawn. In the view of the current interest in the fabrication of beryllium shapes, it was thought that a knowledge of the strain-hardening exponent of cross-rolled beryllium sheet would be of general interest. Load-strain data after yielding and prior to necking was taken from the work of Greenspan,3 converted to true stress and true-plastic strain, and plotted on log-log paper as shown in Fig. 1. The value of Young's modulus E for beryllium was taken as 43 . l06 psi. The slope of this plot gave a value of 0.212 for the strain-hardening exponent (n) and the intercept on the ordinate axis a value of 105,000 for K. The total uniform elongation is thus 21.2 pct, in excellent agreement with the value estimated by Greenspan (about 20 pct). Furthermore,

Jan 1, 1960

By H. Brandhorst, C. G. Dunn

THE main purpose of the present note is to provide further information on the effect of orientation on strain-induced grain boundary migration in sheet material. A secondary purpose is to draw attention to the presence of a possible (hkl) dependent surface energy driving force, when the two grains of a bicrystal specimen have different (hk2) planes at the gas-metal interface, and to suggest means of eliminating this effect from the strain effect. If two grains A and B of a bicrystal have specific surface energies ? A and ? B respectively, there exists a driving force for grain boundary migration equal to 2(? B - ? A)/t, where t is the thickness of the specimen.' When t is quite small and the residual strain energy densities €A and €B of grains A and B, respectively, adjacent to the boundary are nearly equal, it is possible that the surface effect may be larger than the strain effect. he difference € B - € A gives a driving force per unit area of grain boundary due to an applied strain.)2 However, with increasing t the surface effect decreases while the strain effect presumably remains constant. Therefore, at some sufficiently large value of t, it is possible to ignore surface energy driving forces.* On the other hand, the surface effect is eliminated for all value of t when both grains have the same (hkl) orientation or have identical values of surface energy. Although the previous study provided information on the effect of orientation on strain-induced erain boundary migration,' no orientations with the (100) plane in the plane of the sheet were included. The present paper provides information of this kind. A seed crystal reorientation technique4 was used to prepare a large bicrystal of silicon iron (3 1/4 pct Si) consisting of two (100) grains in the (100) [001] and (100) [Oil] orientations. After a cold rolling strain (7 pct reduction to 3/4 mm final thickness), small specimens were prepared as before2 and then annealed in hydrogen. The boundary migration was such that the grain in the (100) [011] orientation always grew. After overnight anneals at 1100° or 1000°C, none of the initial (100) [001] grain remained. An anneal of 30 min at 950°c, however, provided information on the start of boundary migration. Fig. 1 shows both the initial position (lower line) and the final position (upper curved line) of part of the boundary, as revealed by thermal grooves. In a different area, part of the final boundary was not revealed by thermal grooves; the rate of boundary migration presumably was too high for the growth front to be defined by the time dependent thermal grooving process. In another area there was a vacated intermediate position connected to the initial position of the grain boundary. This indicates that only part of the boundary

Jan 1, 1962

By F. Forscher

Pronounced porosity, decreasing with distance from the fracture surface, is found in the necked region of tensile specimens tested at room temperature or liquid nitrogen temperature. A hydrogen solution treatment followed by a quench prevents pore formation in tests at —196°C, but has little effect on tests made at room temperature. Reduction of area values at —196°C are strikingly improved by the same treatment, but show no improvement in room temperature tests. The experimental results support the hypothesis that strain-induced porosity results with hydride initially present or, in material containing less than 50 ppm H, with hydride precipitated by strain aging. ZIRCONIUM'S advent as an engineering material in nuclear reactor construction has brought forth many investigations concerned with the properties of this metal and its alloys. Some attention has been given to the ductility of the metal.1, 2 Particularly, the effect of hydrogen on the impact strength was noted," indicating a pronounced dependence of ductility on the hydrogen content and its distribution in the metal. Micro graphic:' and X-ray diffraction studies' have shown that a precipitated hydride phase causes embrittlement in zirconium,' which implies a distinctly different mechanism from that causing hydrogen embrittlement in steels."-' In the latter case, it is assumed that atomic hydrogen diffuses to rifts, where it forms molecular hydrogen under such internal pressures that it causes the rifts to enlarge, leading to fracture. Thermo-dynamic studies of the Zr-H system8, 9 also indicate that the internal pressure of molecular hydrogen would be too low to cause any damage to the zirconium at room temperature, and the formation of a zirconium hydride (d phase) is favored." It is noteworthy that this phase has a face-centered-cubic structure and nearly 18 pet larger molar volume than close-packed-hexagonal a-zlrconlum' Other features of the ductility of zirconium are the absence of a typical cup-cone failure upon tensile testing, a pronounced strain-induced porosity in the necked region of a tensile bar, Fig 1, and the associated spongy appearance of the fracture surface A tremendous improvement in ductility at liquid nitrogen temperature can be observed following a heat treatment that retains the commonly present quan- tities (10 to 50 ppm) of hydrogen in solution. Such tests show a typical cup-cone failure and the absence of strain-induced porosity, Fig. 2. The present paper reports results of an investigation into the causes of strain-induced porosity in zirconium. Room temperature tensile fractures of mild steel, aluminum, and titanium have also been examined for strain-induced porosity. In each case porosity could be detected, but the amount was orders of magnitude less than was found in zirconium. Of the three metals, titanium showed the strongest effect. Material, Specimens, and Preparation The greater part of this investigation was done on Westinghouse crystal bar zirconium, are-melted, forged, and hot-rolled. Chemical analyses of the hot-rolled plates are given in Table I, along with those of the Foote crystal bar zirconium used in this work. The specimens were machined from the hot-rolled plate (1550°F) of 1/2 in. thickness and subsequently heat-treated according to one of the treatments shown in Table IS. All specimens were machined round, the longitudinal axis in the rolling direction, with a gage

Jan 1, 1957

By John W. Weeton, Max Quatinetz, Robert J. Schafer

Nickel powders of 1-, 0.4-, and 0.2- average particle size were combined with 0.05- p MgO powder. Oxide was added in quantities of 4, 12, and 20 vol pct. The mixtures were vacuum hot pressed and extruded at 2100°F. In spite of a general tendency to growth of oxide particles during processing, dispersions of fineness comparable to those of Sintered Aluminum Powder, SAP, were achieved. A small amount of oxide considerably improved 1800°F stress-rupture strength, but further oxide addition resulted in a decrease of strength. RECENTLY there has been much speculation concerning the requisites for strong and stable dispersion-strengthened alloys. The nature of the dispersed phase, the stability of the alloys, and variables influencing the mechanical properties of alloys have been given consideration. Such topics have been reviewed by Bunshah and Goetzel. Of the many parameters related to the mechanical properties of dispersion alloys, mean free path between dispersed particles (a measure of the fineness of the dispersion), particle size, and vol pct of the dispersed phase have been shown to be very important. Generally, strength increases with decreasing mean free path, and there is an optimum vol pct of dispersed phase. Just how fine a dispersion ought to be is somewhat open to debate, but Irmann, Lenel, Backensto, and Rose, Gregory and Grant,4 and others have shown in the original SAP-type alloys, aluminum plus aluminum oxide alloys, that better strength is generally obtained with finer dispersions and the best strengths were obtained when the mean free path was less than . Further, Cremens, and rant' showed that in nickel plus aluminum oxide alloys, stress-rupture strength at 1500°F was definitely increasing with decreasing mean free path. In their investigation, however, the finest dispersions that were produced were about 2.0 mean free path. To determine the potential of the nickel plus oxide type of product, it would be neces- sary to obtain dispersions analogous to those of SAP alloys; namely, ones where the mean free path between oxides is less than . Unfortunately, however, it is very difficult to produce extremely fine dispersions of oxides in metals other than those which naturally form refractory oxide skins. There are several approaches to this problem including such procedures as mechanical mixing, internal oxidation, reduction of mixed oxides, and metal deposition from solution. Work at the Lewis Research Center has shown that metal powders 0.1p or finer could be produced by ball milling, when selected grinding aids were utilized.' Because these unusually fine powders were available, it was an initial objective of this study to determine if by mixing of these fine Ni powders with various amounts of MgO (0.05) a fine dispersion of MgO in Ni comparable to those in Al-Al203 might be achieved. A second objective was then to attempt to relate the parameters of structure to 1800°F stress-rupture strength of the alloys. Nickel powders of 1-, 0.4-, and 0.2-p average particle size were combined with 0.05- average particle size MgO powder. This oxide was added in quantities of 4, 12, and 20 vol pct. The mixtures were hot pressed and extruded at 2100°F.

Jan 1, 1962

By W. G. Moffatt, J. Wulff

BRAZED joints and their strength have for some time been of great practical as well as theoretical interest. A good summary of the previous work in this field may be found in the reports of the Armour Research Foundation. In spite of excessive scatter in test data, the fact that the strength of a brazed joint may exceed the ultimate strength of the brazing material itself by many times continues to be of interest and of value in engineering. That this is qualitatively due to plastic constraint of the brazing material by the faying surfaces of the base metal is not in dispute, yet no complete interpretation of the data exists. The purpose of the present work is not to provide such a new interpretation, but to report new experimental data which we hope may lead to a better understanding of the important variables concerned. The work of Bredz' definitely shows that the thinner a brazed joint is, the greater is its strength. Dianeter of a joint has seldom been taken into

Jan 1, 1958

By George Krauss, M. Cohen

The reverse martensitic transfomzation (i.e., the conversion of martensite to austenite on heating) was investigated in Fe-Ni alloys containing 30.5 to 33.5 wt pct Ni. The reversed austenite was found to be sufficiently distorted to exhibit marked differences in mechanical properties and to undergo recovery and re crystallization on further heating. In particular, the yield strength of the reversed austenite was as much as 2.5 times higher than that of the virgin austenite: with five cycles of the direct and reverse martensitic transformation, the yield strength was 2.6 times higher. There was an accompanying decrease in strain-hardening capacity and in stable ductility or uniform elongation. The recrystallization was observed to follow sigmoidal kinetics, but was characterized by an abnormal1y large temperature dependence which was evidently due to carbon segregation at the migrating grain boundaries. Upon recrystallization, the strength Properties reverted to those of the virgin austenite, but the ductility did not fully recover until the annealing temperature was further raised to dissipate the carbon segregation at the grain boundaries. The transformation of reversed austenite to produce second-generation martensite resulted in an unusually imperfect structure, thereby leaditg to additional strengthening. Horlleuer, the martensitic phase was much less responsive in this respect than was the austenite. MOST martensitic transformations are capable of undergoing a reverse transformation back to the austenitic phase on heating.&apos; This reaction, like the direct transformation to martensite on cooling, is usually athermal. In analogy with the Ms andMf temperatures for the martensitic transformation (where M, > Mf), the reverse transformation is characterized by the As andAf temperatures (where As<Af). It is well-known that the finish (Af) of the martensite-to-austenite reaction on heating may occur at a temperature where austenite is not stable relative to other phases in the equilibrium diagram.&apos; Reverse martensitic transformations have been found to influence the properties of the parent austenitic phase in a number of ferrous alloys. The austenite thus produced after one or more reversals is significantly altered in strength, microstruc-ture, diffusivity, and annealing characteristics compared to well-annealed, virgin austenite. The first detailed observations of such phenomena were made by Wasserman3 on an Fe-30 wt pct alloy. He found that the reversed austenite (i.e., austenite formed by the reverse martensitic transformation) was much stronger than the original austenite, and the second-generation martensite (i.e., martensite produced from the reversed austenite) was somewhat stronger than the first-generation martensite. On heating the reversed austenite, recrystallization occurred in a manner similar to that of a cold-worked metal; the Laue spots sharpened and the strength decreased.4 In recent years, Russian workers have shown considerable interest in these reverse martensitic transformations. Most of such investigations5-10 have been concerned with the stabilization of reversed austenite relative to subsequent martensitic transformation, and because of its unusual nature, this phenomenon will be discussed in detail elsewhere." On the other hand, the annealing behavior of reversed austenite and the attendant variation in properties have received little attention beyond the experiments of Wasserman.3,4 Gridnev eta1.,8 in one of the few such studies. followed the hardness change of reversed austenite as a function of time at three annealing temperatures. The marked strengthening of austenite achieved by the reverse martensitic transformation has been referred to as "transformation strengthening" by Wasserman3,4 and as "phase hardening" by Malyshev et a1.7,9,10 to differentiate it from hardening produced by cold working. Both groups of investigators noted that further strengthening of the austenite could be attained by repeated or cyclic transformations, but the first cycle resulted in the most pronounced effect. Evidence of the altered microstructure of reversed austenite has been reported by Maximova and Nikonorova6 and by Edmonson and KO.12 The former found that reversed austenite was much more sensitive to etching than the original austenite, and the latter authors observed a (&apos;ghost" structure resembling martensite in certain areas of the reversed austenite. Enhancement of the self-diffusion rate in reversed

Jan 1, 1962

By V. A. Phillips, M. Safdar Ali

The tensile properties of Cu-0.20 pct Al, Cu-0.45 pct Mg, Cu-0.27 pct Cr, and Cu-0.22 pct Be solid-solution alloys were studied at -196°, 18°, 2509 and 500°C on wires internally oxidized at 900°and 1000°C. Internal oxidation produced marked increases in yield strength relative to pure copper, particularly at low temperature. The yield strength decreased with increase in temperature to a much greater extent than predicted by current theories of dispersion hardening. The strengthening effect of internal oxidation persisted throughout the entire stress-strain curve, but since a marked loss of ductility occurred at all test temperatures, only modest increases in tensile strength were realized. INTERNAL oxidation involves the preferential oxidation of a baser solute in a relatively noble solvent by diffusion of oxygen into the solid. Since the process is diffusion controlled, it is expedient to carry it out at a high temperature often approaching the melting point. The amount of solute is limited and the oxidation conditions adjusted so that oxygen diffuses inwards to meet the solute causing reaction to progress inwards and form subscale instead of only sur face scale. The reaction can be made to occur throughout the thickness of thin material producing a fine dispersion of oxide inside the metal. C. S. Smith1"3 appears to have been the first to recognize the true nature of the process of internal oxidation. Although extensive kinetic and metal-lographic studies followed by Rhines and coworkers,4-5 Chaston7 andMeijering and Druyvesteyn8 working independently were the first to report hardening effects due to internal oxidation. These results prompted detailed studies of the effects of internal oxidation on the hardness, tensile, creep, and fatigue properties of a number of alloys by G. C. Smith and coworkers9-12 in England, on hardness by Gottardi13 in Italy, and on hardness and tensile properties by wood14 in the U.S.A. Publications dealing with other aspects of internal oxidation will not be reviewed here. Internal oxidation of solutes having a high affinity for oxygen provides a means of obtaining very fine dispersions stable in a suitable atmosphere at temperatures well above those at which most age harden ing precipitates coalesce. The process therefore offers a method of producing thin sheet and wire of possibly outstanding creep resistance. The size limitation might be overcome by internally oxidizing porous powder compacts made from alloy powder before final sintering. PREPARATION OF ALLOYS The alloy ingots, which were approximately 5 1/2 in. long by 1 in. diam, were made up in a high-frequency furnace, using as raw materials OFHC copper, 99.99 + pct Al, high-purity magnesium, and master alloys of Cu-4.19 pct Be and Cu-10 pct Cr. The alloys containing aluminum and magnesium were melted ii closed high-purity graphite crucibles and solidified in the crucible which was lowered partly Out of the coil to give a hot-top effect. The alloys containing beryllium and chromium were made by melting in vacuo in alumina-lined sillimanite crucibles. The magnesium, chromium, and beryllium

Jan 1, 1960

By G. K. Manning, E. R. Stein, E. E. Underwood

Columbium, carbon. and nickel additions were made to iron-base alloys with 20 pct CY. The effects on microstructure, precipitation-hardening characteristics, and High-temperature properties were investigated by means of metallographic, hot-hardness, and magnetic measurements. An austenitic alloy consistilzg of Fe-20Cr-14Ni-0.8C-2.5Cb had higher hot-lzaciness at 1700°F than the other alloys investigated. Its favorable standing is attributed to an enhanced interaction of Cb and Cr4C particles dispersed within a stable austenitic matrix. FOR the past 20 years, cobalt- and nickel-base alloys have been used for the more stringent high-temperature applications because of their excellent creep resistance. Although their performance is quite satisfactory, other base materials must be considered for large tonnage, low-cost applications such as for the automotive gas turbine. Iron-base alloys are also used extensively, but at somewhat lower temperatures, primarily because of the instability of particles or because precipitation occurs at relatively low temperatures. Since unusual stability has been reported for Fe-Cb and Cb-C compounds.1-3 it was hoped that effective amounts of these compounds could be taken into solution at temperatures just below the melting range, then precipitated upon reheating. Actually, strengthening was found to occur by both precipitation hardening in some alloys and by phase transformations in others. Among the alloys investigated, that with the best high-temperature properties owes its strengthening to a combination of carbide particle interaction and a relatively stable austenitic matrix. EXPERIMENTAL PROCEDURES Small preliminary melts of about 100 g were made in a vertical Glotube furnace, using alundum crucibles and an argon atmosphere. Alloys weighing 35 lb were melted in a basic-lined induction furnace, also under argon. The compositions of the alloys are given in Table I. The nickel-free alloys were usually ferritic, while those containing nickel were generally austenitic. Depending upon the particular heat treatments, or the combination of alloying elements, two-phase alloys of ferrite and austenite could be obtained. In the following text, however, the nickel-free or nickel-bearing alloys are referred to simply as either ferritic or austenitic alloys respectively. The small ingots were swaged at 2000°F, in steps, to rods of approximately 3/16-in. diam. The large ingots were forged at 2100°F to 1-in. sq bars. No difficulties were encountered in swaging or forging any of the alloys to as much as 90 pct reduction in area. For heat treating at temperatures above 2000°F, specimens were sealed in quartz tubes under a partial pressure of helium. No special precautions were found to be necessary at lower temperatures. Intermetallic compounds in the preliminary alloys were identified by means of X-ray diffraction measurements. Correlation of these results with micro-structural characteristics (such as color, shape, size, and location) of the compounds aided in their identification. Magnetic susceptibilities were also obtained at room temperature with a Magne Gage instrument after the various heat treatments. To

Jan 1, 1962

By I. B. Cadoff, J. C. Bilello, R. Rosenberg

Diffiusion of magnesium into the surface of LiF crystals to controlled depths and subsequent heat treatments provided a wide range of surface zone harahesses and structure, The bend strength of the LiF crystals was increased by as much as an or-dev of magnitude. Ductility was achieved when dislocation generation occurred in the diffusion zone or when dislocations penetrated to the surface from the intevior. A critical surface hardness of 130 to 140 kg per sq mm was found helozu which generation could take place in the diffusion zone and ahoue which the zone was impenetrable, This hardness was obtainable by several methods, among them the aging of quenched MgF2 -LiF solutions to produce MgF, precipitation. Maximum hardness was ohtained in quenched specimens with no visihle evidence of MgF,. Diffusion-zone formation followed a parabolic rate law and an activation energy of 20.9 kcal per mole was obtained for the process. RECENTLY, the properties of ionic crystals as related to surface condition have been receiving much attention, specifically the transitions between ductile and brittle behavior. Originally Joffe 1 showed that NaCl crystals could be made ductile by immersion in water and related this to the elimination of surface microcracks. Aerts and DeKeyser 2 and Gorur 3&apos; have subsequently shown that ionic crystals are inherently ductile and are embrittled through contact with air. Machlin and Murray4 hypothesized that a layer of NaCIO3 produced by contact of ozone with NaCl induced embrittlement by acting as a barrier to outward dislocation flow. westwood,&apos; Rosenberg and Cadoff,9 and Bilello and cadoff&apos; have reported surface strengthening of LiF crystals by coating with a magnesium compound and then heat treating for adherence. The major effect of the coat was to inhibit dislocation-slip lines from reaching the specimen surface. westwoods showed microcrack formation and fracture to be caused by slip-band interactions at the surface. The material presented in this paper is an extension of the work reported earlier by Bilello, Rosenberg, and cadoff&apos;6,7 and illustrates the wide range of surface properties and bulk behavior obtainable by use of heat-treated magnesium-diffused surface regions in LiF crystals. EXPERIMENTAL PROCEDURE The LiF single crystals were obtained from the Harshaw Chemical Co. Some batch to batch variation was observed; therefore all specimens for a given test series were cleaved from the same crystal. The typical dimension used was 1 by 0.1 by 0.40 in. Surface damage resulting from cleavage was removed by chemically polishing in a 2 pct NH4OH solution. Each group of specimens was given a vacuum anneal at 700°C for 4 hr to provide a base standard for measuring comparative effects of various surface treatments. To produce the reacted surface zone, the annealed specimens were immersed in a boiling suspension of MgF, in doubly distilled HzO, agitated slbwly for 30 sec, removed, and dried at room temperature. Uniform coatings of MgF, were deposited with a thickness of approximately 5 mils. It should be noted that this technique can be modified for use with crystals which are soluble in water by using boiling absolute alcohol as the dissolving medium. This was found effective for the coating of NaCl with MgF2. The diffused surface zone was obtained by annealing the coated samples at elevated temperatures in a vacuum of lob4 mm Hg. Penetration depth was controlled by varying the annealing time from 1/2 to 28 hr. After heat treatment, the samples were tested for bend strength and hardness. Load was applied by four-point bending in a hard-beam testing jig. Four-point rather than three-point bending was used to provide a wide area of constant stress and to minimize the effect of localized inhomogenities in the specimen. The deflection rate was 8 x min-&apos; and the distance between knife edges was 1/4 in. Load-time curves were obtained from a chart recorder coupled to the machine and converted to resolved shear stress on the shear plane vs deflection, as plotted in the figures. The unstressed portions of the sample outside of the two outer knife edges were used for the microhardness studies. Microhardness measurements were made with a Bergsman tester attached to a Reichert metallograph. All hardness impres-

Jan 1, 1964

By S. E. Bronisz, J. O. Brittain

Experiments have been carried out to study the effect of an applied stress on strain aging in steel. It was found that the stress-induced strain aging reaction proceeds rapidly in the temperature range of 0° to 60°C. The variation of stress-induced strain aging with plastic strain, aging time, and temperatures is reported. The activation energy for the stress-induced strain aging was found to be 10,000 cal per mol for the steel used in this investigation. VARIOUS observations1-5 have been made of the influence of an applied stress upon the yielding of iron and steel. However, there have been only cursory studies of the effect of an applied tensile stress upon strain aging in iron and steel1,2 The following represents the results of a preliminary study of strain aging as influenced by the application of an external tensile load during the aging process. For the most part, previous experimental work on strain aging can be classified into two parts. First, the experimental technique involved a direct determination of mechanical properties of a suitable specimen that has been plastically deformed to a constant strain and aged generally at a temperature of the order of 200°C, with the aging times varying from about 1/10 to 2 hr.6-8 The second classification of strain aging experiments involves an indirect determination of strain aging by means of physical property such as electrical resistivity or internal friction as a function of the aging time at a constant temperature and strain.9-12 The latter results have

Jan 1, 1961

By T. A. Read, H. K. Birnbaum

Deformation of AuCd alloys having the 8 (orthorhombic) and (3" (tetragonal) structures occurs by the stress induced motion of twin boutdaries. A restoring force acts on displaced twin boutdaries as a result of internal energy increases in the volume through which the boundaries are displaced. The phenomonology of the twin boundary motion is described and a mechanism for twin boundary motion and the restoring force is proposed. A time-dependent stabilization behavior of the twin boundaries, which is observed after the twins are formed by the diffusionless phase transformations, is described. THE AuCd 8 phase (ordered bcc structure) exhibits a transformation to a phase having an orthorhombic structure, 8&apos; (space group D&apos;), for compositions in the vicinity of 47.5 at. pct Cd and to a phase having a tetragonal structure, 8" (point group 4/m, m,m), for compositions in the vicinity 50.0 at. pct Cd. Both transformations are diffusionless, occur on cooling at 60" and 30OC, respectively, and are crystallo-graphically reversible.&apos; They are accompanied by an inhomogeneous deformation which was observed to be twinning in the low-temperature phase. 3&apos;4 The transformations may occur by a "single interface" or by "multiple interfaces."5&apos;6 In the "single interface" transformation, the twinned product phase consisted of two twin orientations as shown in Fig. 1. In the multiple interface transformation the product phase contained "domains" each of which contained two twin orientations, Fig. 2. Deformation of specimens containing transformation twins was achieved by motion of the twin boundaries. Releasing the applied stress resulted in the displaced twin boundaries returning towards their initial positions. This "pseudo-elastic" behavior of the boundaries varied with time after the formation of the twin boundaries by the transformation.

Jan 1, 1961

By M. R. Louthan

The susceptibility of titanium to stress orientation of hydride precipitates was investigated. It was determined that, when hydride precipitation occurred in titanium under an applied tensile stress of 30,000 psi, the hydrides precipitated on the titanium habit plane oriented most nearly perpendicular to the stress axis. Stress orientation of the hydride platelets occurred because the precipitation of the lower density hydride phase perpendicular to the stress axis caused expansion of the matrix in a direction that tended to relieve the applied stress. The Ti-H system has received considerable study in recent years, mainly because of concern over the effects of hydrogen on the mechanical properties of titanium. The amount of hydrogen present in commercial titanium is now quite low and should have no appreciable effect on its mechanical properties; however, many titanium applications require ex- posure to hydrogenous atmospheres under conditions in which hydrogen pickup is likely. In such cases continued exposures may cause the hydrogen content to increase to the extent that titanium hydride does precipitate as a second phase. The hydride phase has been shown 1,2 to have an adverse effect on the mechanical properties, particularly the impact properties, causing reductions in strength and ductility. BACKGROUND The behavior of titanium is often quite similar to that of zirconium and zirconium-base alloys, and the technology developed on one metal can often be applied to the other. Marshall and Louthan3,4 have shown that Zircaloy is susceptible to stress orientation* of zirconium hydride platelets, and that the platelet orientation has a pronounced effect on the mechanical properties of Zircaloy. They showed that when zirconium hydride precipitated in Zircaloy under an applied stress the hydride platelets tended to be aligned parallel to a compressive stress and perpendicular to a tensile stress. They also showed

Jan 1, 1963

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

CERTAIN titanium alloys when quenched to retain the 0 phase at room temperature show extensive transformation of 0 to martensitic a during deformation. Alloys of this type are usually characterized by low tensile yield strength, a large spread between yield strength and ultimate strength, and high uniform elongation. A previous investigation of this phenomenon concluded that the principal contribution of the martensitic transformation was to increase the amount of deformation prior to fail-

Jan 1, 1964

By R. H. Hiltz

Three titanium alloys, known to provide a mechanically unstable p structure after quenching, were selected as material for a study of the Origin and nature of stress-induced transformation. Data from hardness and tensile tests were used to study the initiation of marten site and the effect of the transfornation and transformation products on the mechanical properties of B titanium, particularly the stress-strain relationships. With the exception that the materials investigated showed a natural aging reaction in the P condition, their behavior is analogous to that of&apos; stress-transforming stainless steels. The transformation starts after initial yielding and is essentially complete just prior to .maximum loading. Once initiated, the martensite itself is capable of propagating the transformation. The deforn-ing materials show low strength, high ductility, and a high strain-hardening exponent. In metallic systems which undergo a diffusionless transformation on cooling, it is possible to produce a similar transformatiorl by plastic deformation under special conditions. Dewez&apos; in delineating Ms temperatures for the titanium-rich end of most titanium binary systems:, established the point of intersection of Ms with room temperature for those particular alloys. Alloy compositions which would quench to mechanically unstable p were established from these data. The first investigation into the possibility of stress-induced transformation occurring in titanium met with little success. It was concluded that such a transformation in titanium was possible only under very special conditions. Continued effort in this direction, however, showed certain Ti-Mo binaries to be highly susceptible to this phenomenon. This fact was utilized by Liu to study the habit planes of martensite and by Machlin and wenig5 to study the effects of stress and plastic deformation on the P to a prime transformation in titanium alloys. The first investigation of the mechanical properties of these alloys was conducted by Holden and his coworkers at Battelle Memorial Institute.&apos; The potentiality of the alloys i3s sheet-forming material was recognized, and the data reappeared in a survey of this type of titanium material.? The initial optimism was tempered by the difficulties in obtaining homogeneous 2i-Mo alloys in commercial-size ingots. The increasing need for good sheet-forming material kept investigation in this direction active, resulting in the development of a commercial alloy of this type.&apos; This study was undertaken to obtain a clearer picture of the mechanism of stress-induced transformation in titanium. MATERIALS AND TEST PROCEDURE Three alloys were selected for this investigation: one a Ti-Mo alloy; another a Ti-Cr-Mo alloy, known to deform martensitically; and the third, a Ti-V alloy with an Ms below room temperature and an Md above room temperature, but known to contain w phase in the quenched condition. The compositions of these alloys are given in Table I. These alloys were cast as 5-lb experimental ingots, employing skull melting. The ingots were hot-forged into 1-in.-round bars. Two 72-in.-thick slices were cut from each bar for hardness testing; the remainder was cut into 0.252-in. tensile blanks. The tensile blanks and one hardness disc from each bar were heated in salt to a temperature 100°F above the 0 transus, held 2/2 hr, and brine quenched. X-ray analysis showed the pieces to be 100 pct 8.* *Omega cannot be distinguished from p by the technique employed. Tensile blanks were machined to size after this treatment. TO prevent transformation due to machining stresses, the shoulders and gage length were ground. True stress-true strain curves were

Jan 1, 1960

By C. J. Guntner, R. P. Reed

A commercial 18Cr-8Ni iron alloy (AISI 304L) was examined in tension at 300°, 76°, 20°, and 4°K. Continuous stress-strain recordings were made, X-ray analyses at periodic stress (strain) intervals were obtained, and the magnetic measurements were taken. From this data the percentage of martensitic products [bcc(a) and hcp (E)] was computed as a function of stress (strain). It was found thatup to 15 pct E phase forms at low temperntures. The amount of E formed increases to a maximum at about 5 pct strain, then decreases. This decrease indicates the additional transformation of E to a&apos;. The total amount of E and a&apos; was suppressed at constant stress (strain) at 4°K as compared to 76°K. It is proposed that the suppression of E and a&apos; is associated with the decreased mobility of extended dislocations at very low temperatures. The yield strength decreased as the temperature was depressed below room temperature and then increased rapidly near 4°K. SOME ferrous alloys which are austenitic (fcc ?) at room temperature appear to be unique in that two martensitic products (hcp e and bcc a&apos;) may form on cooling to lower temperatures or on application of mechanical stress. The most common room-temperature austenitic ferrous alloys are 18Cr, 8Ni stainless steels. Most aspects of the spontaneous transformations have been previously described for these steels.&apos; Several previous papers have described special aspects of the stress-induced transformations at low temperatures for the stainless steels, such as the existence of the hcp phase (c) after straining at 76oK,2-7 the morphology after straining using electron microscopy,7 and the decrease in E at higher strains at 76oK.4 However, for a complete representation, one must know the stress-strain characteristics and the dependence of both martensitic products on applied stress and temperature. It is the intention of this paper to provide that documentation. To accomplish this, continuous stress vs strain recordings were made at four temperatures: 300°, 76", 20°, and 4°K for annealed AISI 304L (a commercial 18Cr-8Ni alloy). At periodic stress intervals at each temperature the integrated X-ray line intensity of a selected peak for each phase (y, E, and a&apos;) was measured. In addition, photomicrographs of the strained surfaces were taken and magnetic measurements were made. The magnetic readings can be directly converted into percent a&apos;.&apos;,e With these measurements the percentage of each phase may be plotted as a function of stress (or strain) and test temperature. It was found that up to 15 pct E phase forms upon stressing the AISI 304L alloy at low temperatures. The E percentage increases abruptly after the alloy yields, but then decreases gradually at higher stresses. The rapid increase in e at 76°K is associated with an "easy-glide" portion of the stress-strain curve. The total amount of a&apos; + .G is suppressed below 76°K at a constant stress or strain. The yield strength decreases down to 76°K but increases rapidly below 20°K. EXPERIMENTAL PROCEDURE Tensile test specimens were cut parallel to the rolling direction from 0.1-in.-thick sheet. Continuous stress vs strain recordings were obtained at each test temperature (300°, 76o, 20°, and 4°K) using equipment and methods described elsewhere.&apos; The specimens which were used in the X-ray analysis were stressed to successive increments of strain at each temperature, analyzed at room temperature, then restressed at the test temperature. This procedure was repeated until approximately ten X-ray analyses had been performed with approximately 1.0 pct strain increments. The specimens had a reduced section 1 in. long, 1.2 in. wide, and 0.1 in. thick. They were electro polished prior to testing and after each strain increment. Table I lists the chemical composition, grain size, and hardness for the alloy which was used. This is the same alloy for which extensive mechanical-property tests3 and morphological studies of the spontaneous transformations&apos; have previously been made. For the low-temperature tests (76o and 4°K) below the Ms temperature the specimens were initially cooled to the test temperature, held for 1/2 hr, then warmed and X-rayed at room temperature. The results are listed in Table 11. From earlier work8 it was known that additional transformation on the second cycle would be considerably less (-0.1 pct

Jan 1, 1964

By F. D. Rosi

The plastic properties of extended silver and copper crystals of varying purity were studied as a function of crystal orientation in the early stages of flow. Variations in the gross shape of the shear stress-shear diagram and in the properties of critical Variationsshear stress and shear-hardening coefficient were correlated with changes in slip-band developments. The phenomenon of work hardening is discussed in terms of the existing dislocation theory. IT appears certain from the early studies on the deformation characteristics in metal crystals1-3 that plastic flow takes place in a preferred crystallo-graphic slip system which is determined by the geometry of the crystal (law of maximum shear stress), and that the value of shear stress for this system is independent of crystal orientation (law of critical shear stress). Experimentally, it has been demonstrated further that the law of critical shear stress can be extended to include extensive plastic flow.&apos; Thus, the shear-hardening coefficient, which is defined as the slope of the shear stress-shear curve, also is considered to be independent of orientation. It is noteworthy that deviations from this empirical shear-hardening law have been reported in cubic crystals whose initial orientation favors slip on more than two systems.&apos; Moreover, this law appears to have been derived from stress-strain data relating to relatively high values of shear strain (0.5 to 4), where widespread slip and complex distortions can be expected, regardless of crystal orientation. Since existing data indicate that the strain inhomogeneity in a crystal is manifested particularly in the early stages of flow, it would appear that a more exacting test as to the fundamental nature of the shear-hardening law would be to investigate systematically the shape of the stress-strain curve as a function of crystal orientation in the earlier stages of deformation. With regard to the general form of the shear stress-shear curve for cubic crystals, early studies show a parabolic hardening law, where the shear 1 stress is proportional to the square root of the shear-strain. Since this law was predicted theoretically by Taylor" in his original dislocation model for hard- ening, it has been accepted widely as a fundamental flow characteristic of cubic metals. However, it was recently pointed out by Masing6 hat the parabolic law is not the elementary form of hardening in cubic crystals, but instead is a consequence of complexities in the flow process (e. g., deformation bands and unpredicted secondary slip). Thus, in the very early stages of deformation (< 2 pct extension) where the occurrence of such complexities is unlikely, a different strain-hardening behavior might be anticipated. This view is supported by the recent work of Rosi and Mathewson7 on high purity aluminum where a linear law was obtained for extensions up to 2 pct. A linear hardening over a wider range of deformation also was reported by Rohm and Kochendorfer8 ho deformed aluminum crystals under conditions approximating pure shear. Even more pertinent is the recent evidence of Masing and Raffelsieper9 on high purity aluminum crystals. It was found that for crystals having initial orientations near a <l00> or <1ll> axis, a high hardening was obtained, whereas crystals with a <110> orientation exhibited a low and linear hardening curve followed by a region of more rapid hardening. Since much still remains obscure concerning the details of strain hardening as well as slip-band formation in face-centered-cubic crystals in the early stages of deformation, the present study was undertaken to evaluate the effect of crystal orientation on these two important manifestations of glide. It is important to note here that at the time of this study, Lucke and Lange11 presented information on the orientation-dependence of the shape of the strain-hardening curve in aluminum of various purities. Their work, which essentially represents an extension of that of Masing and Raffelsieper, in many respects is parallel to that of the present study. Experimental Procedure Production of Single Crystals: Single crystals of silver and copper of varying purity were used in

Jan 1, 1955

By C. G. Dunn, K. T. Aust

SEVERAL studies1-10 have reported a type of grain boundary migration which occurs when a strained grain grows into an adjacent deformed grain during annealing. Beck and Sperry called this phenomenon strain-induced grain boundary migration, since the observed boundary movement, which takes place in a direction away from the center of curvature, is apparently motivated by the excess free energy of strain hardening. However, little information has been obtained on the detailed structural changes accompanying such grain boundary motion. The problem of driving force for strain-induced boundary migration was considered by Dunn and Daniels,&apos; who used bent bicrystals of Si-Fe. They demonstrated that two grains of differing energy, in the form of subboundaries, behaved according to the concept that the low-energy grain would grow at the expense of the high-energy grain. Beck" reported experiments of Sperry for high-purity aluminum, which indicated that generally the particular grain of a pair which work-hardened more was invaded. The measure of work hardening here was

Jan 1, 1958