By G. E. Tardiff, A. A. Hendrickson

THE objectives of this communication are to present the solid-solution strengthening data for silver-base zinc single crystals and to evaluate the importance of strength contributions from several mechanisms through the use of this data combined with that for the silver-base aluminum case.' Some features of the yield point behavior of silver-base zinc crystals were previously reported.' Silver-base zinc alloys were prepared by induction melting 99.99 pct Ag with 99.9 pct Zn in high-purity graphite crucibles contained in argon-filled quartz tubes. After the first melting, the ingots were cut into short lengths, redistributed in the molds, and remelted in order to reduce solute-concentration variations. Alloy single crystals were then grown from the melt through the use of a modified Bridgeman technique which consisted of lowering the graphite crystal mold through a hot zone at a rate of 3/8 in. per hr. As in the melting operation, the molds were contained in argon-filled quartz tubes. Gage lengths 2 cm in length were introduced by both spark machining (circular cross sections) and abrading and acid etching (rectangular cross section) followed by electropolishing (a comparison of the critical resolved shear-stress values prepared by the two techniques showed no differences in strength values). The final cross-sectional areas of the crystals were approximately 5 sq mm. Prior to testing, the crystals were annealed at 600°C for 20 hr in argon atmospheres, furnace-cooled, and lightly electropolished. Crystal orientations were determined using the back-reflection method. The tensile testing was done on a Model FM Instron at a strain rate of 1(T4 per sec. Test temperatures of 77", 200°, and 400°K were attained by immersing the specimens in liquid nitrogen, dry ice-acetone mixtures, and silicone oil, respectively. The critical resolved shear-stress (CRSS) values for silver-base zinc crystals as a function of composition and testing temperature are given in Fig. 1. It will be noted that the CRSS for silver-base zinc solid solutions, as in the silver-base aluminum1 case, depends on temperature in a manner typical of fcc solid solutions: at high temperatures (-300°K and above), the CRSS is relatively temperature-independent but becomes strongly dependent on temperature at lower testing temperatures. A reasonable picture of solid-solution strengthening for silver-rich solutions at room temperature based on "direct" strengthening mechanisms3 is as follows. Since silver alloys have low stacking-fault energies, extended dislocations are expected and it is possible that Suzuki locking4 makes the major contribution to the room-temperature solute strengthening. This provides essentially temperature-independent strengthening since thermal motions of the dislocation line are not large enough to aid the dislocation in escaping the solute atmosphere extending over the fault width. An estimate of the

Jan 1, 1964

By T. A. Read, M. S. Wechsler, D. S. Lieberman

A theoretical analysis of the austenite-martensite transformation is presented which predicts the habit plane, orientation relationships, and macroscopic distortions from a knowledge only of the crystal structures of the initial and final phases. THIS paper presents a new theory of the formation of martensite. This theory makes possible the calculation of the austenite planes on which the martensite plates form, the orientation relationship between the austenite and martensite crystal axes, and the macroscopic distortions which are observed. The only input data needed are the crystal structures and lattice parameters of the austenite and martensite. Considerable effort has been devoted over the past thirty years to the development of an understanding of the crystallographic features of martensite reactions. Much of this work has been done on steels and iron-nickel alloys, for which a great deal of data has been accumulated concerning the shape and orientation of the martensite plates, the relative orientations of the austenite and martensite crystal axes, and the observable distortions which result from transformation. These observations are reviewed in refs. 1, 2, and 3. The first major step toward an understanding of these phenomena was made in 1924 by Bain,' who showed that the a body-centered cubic structure can be produced from the 7 face-centered cubic structure by a contraction of about 17 pct in the direction of one of the austenite cube axes and an expansion of 12 pct in all directions perpendicular to it. Since that time, most of the efforts at further interpretation have been made by investigators who have worked from the phenomenological data, incorporating some of the information from the lattice properties, and have sought an analysis into likely deformations which would produce the observed results."- "11 but the three most recent papers on the subject have already been reviewed in some detail." Machlin and Cohenl0 measured the components of the distortion matrix and verified that the habit plane is a plane of zero distortion and rotation for the (259) case. They showed that the measured distortion matrix, when applied to the parent lattice, does not yield the product lattice and hence some inhomogeneous distortion must occur. Frank,u working from the lattice properties and taking some clues from the observations, considered the correspondence of close-packed rows and planes in the austenite and martensite. He predicted substantially the observed lattice relationship and habit plane for certain steels which have a (225) habit. Geisler12 suggested that there is a natural tendency for the habit plane to be a (111) and postulated certain slip processes to account for the fact that the experimentally observed habit plane is irrational and deviates from the assumed one. The present work differs from previous treatments of martensite formation in that it permits calculation of all the major manifestations of the process. Habit plane indices, orientation relationships, and observable distortions are all calculated from a knowledge of the crystal structures of the initial and final phases alone. The calculations contain no adjustable parameters. The agreement found between calculated results and the observations reported in the literature constitutes powerful evidence in favor of the mechanism of martensite formation proposed. The theory is applicable to systems other than steel (as is discussed later in this paper) which exhibit a diffusionless phase change but because of the wide-spread interest in the austenite-martensite transformation, particular attention will be given to the iron-base alloys. For other systems which undergo a similar face-centered cubic to face-centered tetragonal transformation, the mathematical treatment is identical with that presented here. Hence the theory successfully describes the transformation in the indium-thallium alloy.'" Homogeneous Transformation to Martensite The distortion which any homogeneously transforming volume of austenite undergoes in order to become martensite is shown in Fig. 1, as was first suggested by Bain.' (This distortion will hereafter be referred to as the "Bain distortion.") This specification of a contraction along one cube axis ;ombined with an expansion in all directions perpendicular to this axis describes what is properly called the "pure" distortion associated with this transformation. The distinction between a "pure" and an "impure" distortion plays an important part in the discussion which follows. A "pure" distortion is characterized by the existence of at least one set of orthogonal axes fixed in the body which are not rotated by the distortion. (These are called the "principal axes" of the distortion.) No such set of axes exists in the case of an "impure" distortion. On the other hand, an impure distortion can always be represented as the result of a pure distortion combined with the rotation of the specimen as a rigid body. For a given impure distortion the corresponding pure distortion

Jan 1, 1954

By J. Mote, P. Ward Flynn, J. E. Dorn

The effect of strain and strain rate on the critical resolved shear stress for prismatic slip in specially oriented single magnesium crystals was determined over a range of temperatures in an effort to identify the thermally activated strain-rate controlling dislocation process. Below about 450°K prismatic slip was preceded by twinning and fracturing. Above 450°K extensive prismatic slip was obtained followed by fracturing. Neither the Peierls&apos; mechanism nor the dislocation intersection mechanism can account for the observations. The data, however, are in good agreement with the dictates of Friedel&apos;s theory for cross slip to the prismatic plane. PREVIOUS investigations on single and polycrys-talline magnesium have resulted in the identification of the mechanisms of plastic deformation summarized in Table I. The-only well-confirmed mechanisms are {0001}, (1010}, (1011) slip plus (1012) twinning. The other twinning modes were only tentatively established and additional investigations are required to further confirm their operation. As noted in Table I, slip in this hexagonal close-packed metal invariably occurs in the direction of greatest atomic density, revealing that the Burger&apos;s vector for-active slip dislocations is always given by b = a/3<1210>. Slip is easily induced on the basal plane, and recent investigations have shown that the strain-rate controlling mechanism at low temperatures is the thermally activated intersection of the glide dislocations with dislocations threading the basal plane. In contrast, very little is known about prismatic slip. It has been reported to be active at points of stress concentration in polycrystals below

Jan 1, 1962

By Jim D. Mote, Eugenia M. Howard, Willis L. Barmore, John E. Dorn

The effect of stress and temperature on the creep rate of Ag-33 at. pct A1 and Ag-33 at. pct Al-1 at. pct Zn for prismatic slip was determined over a range of temperatures from 440º to 700°K. The alloys exhibited a brief initial inverted transient creep over which the creep rate increased slightly to a steady-state value which depended only on the stress and temperature, regardless of the previous strain history. The steady-state creep rates were found to be given by: where the activation energy is independent of the stress and strain and agrees fairly well with that estimated for diffusion. The observed creep behavior was shown to be in qualitative agreement with a model based on the stress-induced local disordering in the vicinity of a dislocation. OVER the past fifteen years, considerable progress has been made in correlating the experimen-entally observed plastic behavior of pure metals over each temperature range with one or more of a series of theoretical strain-rate controlling dislocation mechanisms. Despite the current interest in the plastic behavior of intermediate phases and inter metallic compounds, however, very little has been done in identifying the operative dislocation mechanisms in these materials. It is anticipated that the plastic behavior of intermediate phases can be rationalized in terms of the same dislocation mechanisms that are appropriate to pure metals and a solid solutions, provided the additional complexities arising from crystal structure, bonding, long-range order, short-range order, and defect lattices are taken into account. As part of a more extensive investigation on the plastic behavior of intermediate phases, Mote, Tanaka, and Dorn1 recently reported on the effect of temperature on the yield strength for prismatic slip in the hexagonal Ag-33 at. pct A1 intermediate phase as recorded in Fig. 1: Over Region I the deformation was observed to take place as a result of the thermally-activated Peierls mechanism, and over Region II the athermal disordering mechanism applied. The experimental data at that time, however, were not sufficiently extensive to identify the thermally activated mechanisms operative over Region III. It is the purpose of this investigation to attempt to identify the mechanisms that are operative over this high-temperature region. It will be shown that the same mechanism operates all over Region Ill, although the activation energy for this mechanism is in good agreement with that for diffusion, the process cannot be attributed either to the motion of jogged screw dislocations or the climb of edge dislocations. The results, however, are in good qualitative agreement with stress-induced disordering localized at dislocations. EXPERIMENTAL PROCEDURE The alloys studied in this investigation were prepared from silver, aluminum, and zinc (each of purity greater than 99.995 pet) by induction melting under an argon atmosphere and chill casting in a copper mold. Rectangular bar single crystal specimens (1/4 by 1/8 in. in cross-sect ion) of Ag-33 at. pct Al were grown in vacuum by a modified Bridgman technique. Similar Ag-33 at. pct Zn specimens were produced by an identical technique employing an argon atmosphere. The specimens were so oriented that the angle 90-Xo between the tensile axis and the normal to the prismatic plane and the angle A, between the tensile axis and the slip direction were 45 ± 1 deg. The effect of a change in temperature on the creep rate and a change in stress on the creep rate were determined over the temperature range

Jan 1, 1963

By B. W. Howlett, M. B. Bever, Somnath Misra

The heats oj- formation at 0°C of the compounds AuSn,, AuSn2, AuSn, and the £ phase were measured in a metal -solution calorimeter with liquid tin or a liquid Sn-Bi alloy as solvent. The melting point, heat of fusion, and heat capacities near the melting point of- the compound AuSn in the solid and liquid state were measured in a constant temperature gradient calorimeter. The free energy and entropy of formation of the compound AuSn at its melting point and at 298 °K were calculated from the experimental results and published data. The heats of formation are discussed in relation to the nature of the compounds. The heat capacity below the melting point, heat of fusion, and entropy of fusion of AuSn are interpreted in terms of processes oc-curring before melting. The atomic arrangement in liquid Au-Sn alloys and the bonding in the intermediate phases of. the Au-Sn system are discussed in the light of the measured thermodynamic properties. THE available thermodynamic information on the intermediate phases in the Au-Sn system consists of the heats of formation of the compounds AuSn4, AuSn2, and AuSnly2 and of one composition of the < phase2 besides values of the heat content of the compound AuSn from 0" to 635".&apos; However, the heats of formation refer to different temperatures ringing from 90" to 450°C. Also, the reported error limits of some of the values are large and several inconsistencies are apparent. In the investigation reported here the heats of formation of the compounds AuS-, AuSnz, and AuSn and of three compositions of the < phase were determined for a single reference temperature of 0°C by liquid metal-solution calorimetry. The compound AuSn, which is the only congruently melting intermediate phase in this system, was further investigated in a constant temperature gradient calorimeter by measuring its heat of fusion, melting point, and heat capacity in the solid and liquid states near the melting point. From these data and published free energies of the liquid of composition Au~n,&apos; the free energies of formation of the compound AuSn at the melting point and at 298°K were calculated. The results shed light on the solid-liquid transition of AuSn and on the atomic bonding and state of association of gold and tin in the solid and liquid phases. 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Samples. Stoichiometric amounts of gold and tin, each 99.99+ pct pure, were melted in evacuated Vycor capsules (12 mm ID). The melts were maintained approximately 150°C above the liquidus for about 12 hr and shaken repeatedly. Samples of the compound AuSn were cooled slowly to room temperature. Melts of the other phases, all of which solidify by peritectic reactions, were transferred to the narrow end (5 mm ID) of the capsule, which was then quenched into iced brine. The solidified samples were annealed in the unopened capsules for 10 days at 30" to 50° C below the respective solidus temperatures. The absence of microsegregation and second phases was confirmed by metallographic examination. At least two batches of each composition were prepared. 1.2) Solution Calorimetry. The heats of formation were determined by liquid metal-solution calorimetry. In this technique, the difference between the heat effects on dissolution in a liquid metal, or alloy bath, of the compound and a mechanical mixture of its annealed components, adjusted for changes in composition of the bath, is the heat of formation of the compound at the temperature from which the samples are added. Details of the equipment and technique have been described."&apos; A tin bath at 300" or 350°C was used with the compounds AuSn,, AuSnz, and AuSn. The high gold content of the £ phase would have caused it to dissolve with an appreciable exothermic heat effect. In order to achieve thermal compensation, the samples were added from 0°C to a bath at 350°C consisting of 66.2 wt pct Bi (99.999+ pct pure), balance Sn (99.99+ pct pure). This solvent gives thermal compensation because gold dissolves exothermically in tin and endothermically in bismuth. The calorimeter was calibrated by adding from 0°C approximately 0.015 g-atom of the solvent.

Jan 1, 1965

By B. D. Cullity, S. S. Hsu

The stress distribution at the surface of a twisted cylinder is analyzed along the boundary of a slip plane of arbitrary orientation and this analysis is applied to the torsion of cylindrical crystals of magnesium. A criterion for slip is developed and the critical resolved shear stress of magnesium in torsion is found to be 0.038 kg per sq mm. The mechanism of torsional deformation in magnesium and aluminum is described, as well as the relaxation of a twisted crystal at elevated temperatures. THERE has been considerable fundamental study A of the mechanism of slip occurring during deformation in tension and compression but comparatively little attention has been paid to the mechanism of torsional deformation. This paper is concerned with the way in which a single crystal deforms in static torsion and with the phenomenon of untwisting which a twisted crystal undergoes during annealing. Particular attention is paid to the application of the critical resolved shear stress law to torsional deformation. Probably the most likely mode of torsional deformation that can be imagined consists of rotation of one part of the crystal relative to another on the active slip plane. Here the most interesting feature is the slip direction. If a cylindrical single crystal is twisted about its axis and if, to consider the simplest case, the active slip plane is normal to the specimen axis, then the direction of gross slip at any point must always be at right angles to the radius drawn to that point. It follows that the crystallographic direction of slip must be continually changing, in sharp contrast to slip in tension which occurs in a crystallographically constant direction. Extensive investigations of slip in torsion have been made by Gough and his associates.&apos; They made torsional fatigue tests on metal single crystals belonging to a number of different crystal systems and observed, with a microscope, the appearance of slip lines on the surface and of strain markings on the transverse cross section of cylindrical specimens. They concluded that the critical resolved shear stress law was just as valid in torsion as in tension, in the sense that slip occurred on that plane and in that direction in which the resolved shear stress was a maximum. They also established that the operative slip planes and directions were the same as in tension. They did not, however, measure the critical resolved shear stress in torsion nor, in fact, did they establish that a critical value of the resolved shear stress was necessary for the initiation of slip. Their investigations were, moreover, restricted to torsional fatigue tests which necessarily involve small strain amplitudes. Wilman,&apos; studying crystal growth and the abraded surfaces of crystals, observed crystal fragments

Jan 1, 1955

By R. L. Fullman, J. W. Cahn

A method is derived for obtaining the distribution of sphere diameters and plate thicknesses (or pearlite spacings) from size distribution functions obtained along randomly oriented lines. The method described offers several advantages over existing methods. IT is often of interest to measure not only the average particle size but also the distribution in sizes of particles dispersed in an opaque material, such as an alloy. Particles of a single size will exhibit a range of apparent sizes on the plane of polish. If the sample contains a distribution of particle sizes, the distribution of observed sizes on the plane of polish is related to the distribution of actual particle sizes by an integral equation, For example, a distribution of sphere sizes, N(r),

Jan 1, 1957

By R. W. Heckel, J. H. Smith, H. W. Paxton

The habit plane of proeutectoid cementute precipitated from austenite was studied using a two-trace surface (analysis coupled with a direct X-ray back-reflection determination of the orientatzon of the parent Matrix. The results were the same as those obtained by earlier workers1 - 2 who used Indirect methods to determine the orientation of the matrix. The data indicate that a range or habit planes in the parent phase is operative which is not in agreement with accepted existing theories. In 1933, Mehl, Barrett. and smith1 obtained a non-unique result in a study of the Widmanstätten habit plane of proeutectoid cementite. Their data are shown in Fig. 1. These results were verified by Greninger and Troiano,2 although they did not pre-sent any data. Both of these investigations relied upon indirect methods of determination of the matrix lattice orientation. Theoretical considerations of Widmanstatten precipitates have usually proved or assumed an orientation relationship between matrix and precipitate; the habit plane expressed relative to the matrix is generally unique, although it may be irrational.3 Opinion is divided as to the factors influencing the choice of habit plane. Mehl4 felt that a nucleus which was plate shaped to minimize strain energy and surface energy during its formation could maintain this shape by the point effect of diffusion; the

Jan 1, 1961

By N. S. Stoloff, R. G. Davies

A study has been made of the efject oj different dislocation-precipitate interactions upon the temperature dependence of the flow stress of aged Ni-14 at. pct A1 alloy. It is observed that when the dislocations bow between widely spaced (-20004 coherent Ni3Al particles the flow stress decreases with increasing temperature in the normal way. However, when the dislocations cut closely spaced (-5004 particles the flow stress is independent of temperature from -100 to 600°C, due to a balance between softening of the matrix and an increase in strength of the particles with increasing temperature. The retention of strength at high tempera-tures of commercial nickel-base alloys, which are strengthened by the precipitation of a phase based upon Ni3Al, is thought to be due to the unusual strength properties of Ni3Al. The flow stress of Ni3Al increases continuous1y from -196"C to a maximum at -600"C. It is concluded from a series of thermal-mechanical tests that the sevenfold increase in flow stress over this temperature interval is due to a lattice effect and is not diffusion-controlled. The flow stress of precipitation- or dispersion-hardened materials depends on the resistance to dislocation motion within the matrix and the extra energy required for dislocations to bow between or to cut particles. If the dislocations bow between the particles or if the strength of the cut particles is constant with temperature, then the flow stress of the precipitation-hardened alloy must decrease with increasing temperature due at least to the decrease in elastic modulus of the material. There will be softening also from thermally activated cross-slip or climb, offering an additional degree of freedom for dislocations to avoid particles. For example, in the case of nickel containing a dispersion of thoria,&apos; which most probably deforms by dislocations bowing between particles, the flow stress decreases by about 50 pct between 25" and 650°C. In A1-Cu alloys2 aged to produce the 8" precipitate, dislocations cut the particles, and the flow stress decreases by about 20 pct between -269" and 25°C. However, many commercial high-temperature nickel-base alloys, for example Inconel-X and Udimet-700, exhibit little or no decrease in flow stress with increasing temperature up to about 700°C. A characteristic feature of these alloys is that they are strengthened by the precipitation of a phase based upon Ni3A1. Guard and westbrook4 and flinn&apos; have shown that Ni3Al (and alloys in which a third element such as molybdenum or iron is substituted for part of the aluminum) is unusual in that the hardness and flow stress increase with temperature to a maximum at about 600°C. For the flow stress of a precipitation-hardened alloy to be independent of temperature we propose that the particles must be cut by dislocations moving through the matrix and that the strength of the particle must increase with increasing temperature. Theories of precipitation hardening do not take into account the flow stress of the dispersed particles that are cut during deformation; the only dissipative process usually considered7 is the creation of interface within the particle and between the precipitate and matrix. The purpose of the present investigation has been to study in detail the temperature dependence of the flow stress of a nickel-base alloy strengthened by the precipitation of Ni3Al in two structural conditions such that when deformation occurs it does so by dislocations a) bowing between the particles and b) cutting the particles, respectively. A simple binary Ni-14 at. pct A1 alloy was chosen because considerable information is already available for this system concerning phase equilibria and precipitation reactions and rates.&apos; Dislocation-precipitate interactions in the binary alloy should be similar to those in the more complex commercial alloys. In addition, the mechanical and physical properties of NisAl were studied in detail in the hope of elucidating the mechanism by which the strength increases with increasing temperature up to 600°C. EXPERIMENTAL PROCEDURE For the study of the effect of precipitation of Ni3A1 upon the temperature dependence of the flow stress, an alloy containing 14 at. pct A1 was utilized; a Ni-8 at. pct A1 solid-solution alloy was employed as a comparison material. Vacuum-cast ingots were hot-rolled at 1000°C and cylindrical compression samples, 0.20 in. diam by 0.40 in. high, were prepared from the 1/4-in.-diam rod. Specimens were recrystallized and solution-treated at 1000°C for 1/2 hr and then water-quenched. A preliminary study revealed that, when the Ni-14 at. pct A1 alloy was aged for 1 hr at 700°C, significant precipitation hardening was obtained, and that the structure was free from grain boundary discontinuous precipitation; an overaged condition was produced by annealing the aged specimens at 850°C for 1 hr. To circumvent the difficulties involved in the hot rolling and swaging of Ni3A1, compression samples,

Jan 1, 1965

By R. S. Craig, W. E. Wallace, G. S. Kamath

The destruction of long-range order in Mg-Cd, has previously been thought to occur as a second order process. In the present work a variety of X-ray diffraction techniques are employed to show that in this case and in Mg-Cd alloys containing frorn 20 to 33 1/3 at. pct Mg the process more nearly resembles an ordinary first order phase transformation. It is found that the ordered alloy, which occurs as a single phase at lgw temperatures, transforms with increasing temperature into a Cd-enriched disordered (P) phase and an Mg-enriched ordered (a) phase. The interval over which these two phases coexist under apparently equilibrium conditiovs extends from 25" to 87°C content. At 33 1/3 at. pct Mg the two-phase region has disappeared. Measurement of the long range order parameter, s, for the ordered phase in MgCd, (from superlattice line intensities) shows that it disorders only very slightly before it is transformed into the p form. Kinetic experiments reveal that when the a phase is formed frorn the p phase by suitably quenching so as to suppress phase segregation, the transformation is essentially complete and the a phase has acquired its equilibrium value of S in less than 1 min. In an earlier investigation carried out in this Laboratory1 the rate of disordering of the MgCd3 superlattice was determined over an extensive range of temperature. The process was found to be first order and the rate constant, k, was established. At the lowest temperatures studied k was found to increase exponentially with temperature. At higher temperatures, however, it passed through a maximum and for the 100 deg interval below the point at which the superlattice was destroyed k was observed to decrease with increasing temperature. The various theoretical treatments1-3 of order-disorder phenomena lead to a negative temperature coefficient for k near the superlattice critical temperature but this region for MgCdB seemed unusually wide. Detailed analysis of the point indicated&apos; that either the long-range order parameter, S, for MgCda varied with temperature in an anomalous way or the disordering in this instance is more complex than in the cases which have been treated theoretically. The original objective in the present work was simply to determine S vs temperature for MgCda to ascertain whether the disordering was in conformity with theoretical expectations.2° In an early stage of the work it was noted, however, that under equilibrium conditions ordered (a) and disordered (0) phases coexist in MgCd, over a considerable range of temperature. Since on thermo- dynamic grounds the coexisting phases must differ in composition, the investigation was enlarged to permit the compositions of the two phases in MgCd3 to be determined and to establish the extent of the two phase regions for alloys containing from 20 to 33 1/3 at. pct Cd.

Jan 1, 1963

By J. B. Newkirk

Results of a Debye-Scherrer X-ray investigation are given which show that the order-disorder transformation is a first-order or heterogeneous reaction in Cu-AU alloys with compositions near CuAu. Evidence was found for conventional tie-line segregation across a usual type of two-phase field separating the ordered and disordered fields in the Cu-Au equilibrium phase diagram. The horizontal and vertical widths of the two-phase fields are about 3 atomic pct and 20°C, respectively, at 43 and 54 atomic pct Au. No evidence for the existence of an ordered structure based on a stoichiometric composition of Cu3Au2 could be found. ALTHOUGH the modern theories relating the de-Agree of order of binary alloys to temperature and composition have met with considerable success, the nature of the transformation from the disordered state to the ordered state and vice versa has never been well understood. It has been assumed by some&apos; that this is a second-order transformation, that is, a homogeneous change of state. Others2 hold that the transformation is first-order and that the effects characteristic of heterogeneous phase transformation apply. Since this subject is discussed in detail in a recent paper,&apos; the arguments will not be repeated here. The present paper summarizes an experiment which was designed to distinguish between these two viewpoints for the case of Cu-Au alloys near the composition CuAu. The Cu-Au system is an important one because it furnishes prototype alloys, the behavior of which has formed the basis of much of the present-day order-disorder theory. It has recently been shown- hat in alloys near Cu3Au there is a temperature range within which the ordered and disordered states coexist in equilibrium and are distinguishable as separate phases. Therefore, the transformation must be first-order for these alloys. A similar demonstration for alloys near CuAu, however, has been lacking. Experimental Method Essentially the experiment consisted of equilibrating Cu-Au samples at various temperatures, quenching them in water to retain the high temperature states, and then examining them at room temperature for the coexistence of the ordered and disordered structures. The thermal gradient method of heat treatment- as used because it was important that all temperatures over the transformation range should be represented in the test. Briefly, this method consisted of holding a wire of the desired composition, sealed under vacuum in Pyrex, in a known temperature gradient for a long enough time to allow each part of the wire to assume the crystal structure characteristic of the temperature at which it was held. The temperature gradient was produced by inserting into an ordinary wire-wound cylindrical laboratory furnace, an 18 in. length of 1/8 in. ID ceramic tube which was heavily wrapped with asbestos. The furnace power was controlled by a Tag-liabue Celectray controller and a chromel-alumel thermocouple with the junction located on the heating elements. During the equilibrating treatment the widest variation of temperature within the gradient tube was approximately 4°C at the highest temperature. The temperature at various places within the tube was determined, before inserting

Jan 1, 1954

By H. J. McQueen, G. C. Kuczynski

ThE useful properties of k6-Alfenol and the thermenol alloys (summarized by J. E. Nachman and W. J. Buehler&apos;) have encouraged research into those alloys which, having compositions near 25 at. pct Al, 75 at. pct Fe, undergo an ordering transformation between 500° and 550°C. The equilibrium diagram of the iron-rich iron-aluminum alloys was first determined by Bradley and Jay.2,3 They distinguished three structures: the disordered, which is bcc; FeAl, which is simple cubic with one Fe atom and one Al atom per lattice site; and Fe3Al, which is fcc with three Fe atoms and one Al atom per lattice site. This last structure may be conceived as eight body-centered cubes with Al atoms at the centers of alternate ones, so that Al atoms have only Fe as first and second nearest neighbors. Later, Osawa and Murata4 determined the boundaries of the different superlattice regions in the iron-rich Fe-Al solid solution by dilatometric and X-ray methods. Two of the six phases, which they found between 0 and 50 at. pct Al, were never identified by other workers. A. Taylor and R. M. ones,&apos; concurrently with and independently of this research, redetermined this diagram by measuring lattice parameters at temperature. Further reference will be made to their results. EQUILIBRIUM DIAGRAM A) Experimental Procedure—The alloys were prepared from NRC gas-free iron (99.9 pct Fe) and 99.99 pct Al. They were melted in alumina&apos; crucubles under vacuum in an induction furnace. If the ingots were unsound or showed more than a 3 pct weight loss, they were rejected. The ingots were homogenized at 1100°C for 24 hr before hot-rolling at 700" to 900°C from 1 in. to 0.25 in. thick. It is interesting to note that alloys containing more than 28 at. pct Al were able to take an 80 pct reduction of area in the ordered FeAl region. The dilatometer specimens and specimens for chemical analysis were cut from these plates. A Leitz dilatometer was used to measure the coefficient of linear expansion as a function of temperature. The specimens were slowly cooled from 900" to 300°C where they were annealed for 10 hr before slowly cooling to room temperature. The expansion was recorded photographically as the alloys were heated and cooled at 1.5oC per min between 100" and 1000°C. The magnetic measurements determining the Curie points were performed on the dilatometer specimens in the dilatometer, by using direct current in the furnace windings both to heat the specimen at 1.5°C per min and to serve as the primary coil. The regular specimen holder was replaced by a thin alundum tube on which was wound, as a secondary, a closely spaced coil of fine copper wire. A reversal of current in the furnace windings produced, in the secondary, an emf which was proportional to the induction in the specimen, and which could be detected on a galvanometer. In this way, it was possible to determine the Curie points of alloys to within * 5°C. B) Results and Discussion—The coefficients of linear expansion, as obtained from the dilatometer curves, are plotted as a function of temperature and composition in Fig. 1. Since in many cases the heating and cooling curves were superimposed, it was decided to measure slopes of heating curves only. Definite high peaks, due to the transformations, were observed on each curve between 400" and 520°C, and, for alloys containing more than 23 at. pct Al, a second set of smaller peaks at temperatures above 660°C. The sharpness of the peaks indicates that ordering to Fe3Al is a first-order reaction. The compositions and the temperatures of these peaks are listed in Table I. When these temperatures are plotted as a function of the composition, the result is the constitution diagram presented in

Jan 1, 1960

By G. P. Conard, R. C. Hall, J. F. Libsch

The 50 pct Fe-50 pct Co alloy undergoes a transformation from disorder to an ordered structure of the CsCl type reportedly in the vicinity of 732OC. During this process, the coercive force goes through a maximum, apparently as a result of strains associated with the coherent nucleation and growth reaction. This magnetic alloy also shows a marked increase in the ratio of residual to saturation induction, which is associated with annealing to a high degree of order with the continuous application of a magnetic field. The increase in ratio can be explained on the basis of a decrease in 90&apos; domain boundaries and, perhaps, by an increase in anisotropy resulting from lattice distortion. THE 50 pct Fe-50 pct Co alloy undergoes a disorder-order transformation which has been reported to occur in the vicinity of 732°C1,2 The ordered structure is the CsCl type.&apos; This magnetic alloy also shows a marked increase in the ratio of residual to saturation induction as a result of heat treatment in a magnetic field, sometimes called a response to magnetic anneal.&apos;-&apos; The purpose of this investigation was to study the course of the ordering reaction, the nature of the response to .heat treatment in a magnetic field, and the relation, if any, between ordering and the response. Procedure The method of approach in this investigation was to produce an initial structure as completely disordered as possible and then gradually to order the alloy by isothermal anneals at various temperatures under different conditions of the applied magnetic field. Magnetic, magnetostriction, and X-ray analyses were of primary importance in determining the property and structural changes resulting from the isothermal anneals. Rings of the 50 pct Fe-50 pct Co alloy were prepared from the elemental powders by a powder metallurgy technique, further details of which may be found in ref. 7. The initial structure was produced by annealing the specimens for ½ hr at 1000°C, cooling to and holding for ½ hr at 900°C (in the a range above the ordering temperature), and water quenching. Isothermal anneals were performed at 600°, 675°, 720°, and 740°C. For example, rings were heated to 600°C, held for a predetermined period of time, and cooled by natural cooling at a rate slightly slower than an air cool (average of 20" to 25°C per min). The tests (magnetic, etc.) were made after each heat treatment. All high temperature treatments were performed in a purified hydrogen atmosphere. The treatments at the various temperatures were carried out under one or more conditions of an applied field including 1—no field, 2—field of 20 oersteds applied on cooling only, and 3—field of 20 oersteds applied continuously during heating, holding, and cooling. Magnetic measurements were made using the standard Rowland ring technique8 with a maximum field strength of 100 oersteds. The magnetization curve, induction at 100 oersteds (B.), residual induction (Bt), and coercive force (Hc) were determined. All magnetic analysis data were based on an average of the results from three rings. A strain gage technique9 as used for the measurement of magnetostriction. The X-ray determination of the relative amount of ordered phase present was made on the ring specimen used for magnetic measurement. This was done by the back-reflection method using a rotating specimen (because of the large grain size) with unfiltered CoKa radiation and a 7 hr exposure time. Intensity measurements of the ordered line (300) were made by comparing visually the films so obtained with standard films prepared by exposing for different lengths of time a specimen given a long time anneal (high degree of order). Results In all instances the saturation induction (induction at 100 oersteds) was found to increase slightly with annealing time. This effect was small and appears to be the increase in saturation induction to be expected on ordering.10-13 The residual induction behavior was markedly influenced by the field condition during annealing, Figs. 1, 2. For the condition of no applied field, the ratio of residual to saturation induction remained essentially constant for short annealing times but showed a significant increase at longer times. With increasing annealing temperature, less time was required to produce this increase in the ratio. In the case of the 600°C anneals, the increase did not occur until approximately 20 hr, Fig. I, while on annealing at 740°C the increase was immediate, Fig. 2. Slight decreases in the ratio may be observed at 100 hr for specimens treated at 720°C and at 1 hr for those treated at 740°C. Specimens annealed in a field of 20 oersteds showed a residual to saturation induction ratio consistently higher than that for the specimens annealed without the field. The first anneal with the field (¼ hr) caused an abrupt increase in the ratio at all temperatures; thereafter, the increase in the ratio was generally similar for specimens annealed

Jan 1, 1956

By J. B. Newkirk, D. L. Martin, A. H. Geisler, R. Smoluchowski

A FUNDAMENTAL investigation of the mecha-nism of the ordering reaction and of the accompanying changes in properties has been undertaken, since an extensive study of this process could well contribute to the knowledge of phase transitions in alloys. Cobalt-platinum alloys were chosen for the study since they exhibit interesting and unusual permanent magnet properties.1,2. In addition, the ordering reaction in cobalt-platinum alloys is a convenient one to study experimentally because of the high maximum ordering temperature, the large difference in the X-ray scattering power of cobalt and platinum atoms, and the relative ease with which the alloys can be plastically worked into wire and strip. In the early stages of this study, it became apparent that the published phase diagrams&apos;, &apos; of the cobalt-platinum system contained questionable features, in the region of 40 to 60 atomic pct Co, which were considered in another publication by the authors.4 That portion of the research reported elsewhere on the equilibrium states of cobalt-platinum alloys does not confirm the presence of a previously reported, high temperature disordered tetragonal phase and a low temperature body-centered cubic phase. On the other hand, the structure of the ordered phase is face-centered tetragonal with an atomic distribution analogous to that of CuAu.4 This lattice forms from the disordered face-centered cubic phase in such an orientation that the <100> directions are parallel to the <100> direc-tions of the disordered phase. At compositions other than the ideal 50 atomic pct the ordered phase can exist in equilibrium at high temperatures with the disordered phase. A Widmanstatten pattern of plate-like particles of the ordered phase parallel to (110) planes of the disordered matrix is observed when an initially disordered alloy is held at these temperatures. The temperature range of the two-phase region has been determined for three alloys by X-ray diffraction analyses, microscopic examination, and electrical resistivity measurements, and these results are incorporated with some of those of Gebhardt and Köster in the revised phase diagram of fig. 1. The purpose of the investigation reported here was to examine the mechanism of ordering in co-balt-platinum alloys by X-ray diffraction and metal-

Jan 1, 1951

By J. B. Newkirk, A. H. Geisler

The alloy Cu4Pd has a disordered face-centered-cubic structure when quenched from temperatures between 478ºC and the melting point (about 1100°C). Below 478ºC an ordered phase is stable. The results of a Debye-Scherrer X-ray analysis indicate that the ordered phase has a tetragonal unit cell described by the space group C24h — P42/mt with 2 Cu in 2a, 2 Cu in 2f, 4 Cu in 4j (x = 0.2, y = 0.6), 4Pd in 4j (x = 0.4, y = 0.2), and 8 Cu in 8k (x = 0.1, y = 0.3). The orientation relationship between the face-centered-cubic phase and the ordered tetragonal phase is given by: [100],,. // [130]al,. COO1Ia.d.//COO1I,,.. • The behavior of Cu,Pd is typical of ordering alloys except that the transformation is very sluggish. The increase in hardness and the microstructural and X-ray diffraction effects are interpreted in terms of coherency strains caused by the ordering. AN anomalous construction in the Cu-Pd phase diagram (Fig. 1) was reported in 1939 and has been allowed to stand without further published attention since that time. The odd figuration about the composition 10 to 27 atomic pct Pd is derived mostly from the work of Jones and Sykes.1 Evidently several features of this binary system require further study if the constitutional forms are to be well understood. The present paper includes a study of one of these features, that is, the crystal structure of a single ordered alloy containing nominally 20 atomic pct Pd. This choice of composition was suggested by the work of Harker and associates who determined the structure of Ni4Mo2 and Ni4W.3 The nature of the ordering process in Cu4Pd was studied also by observing the hardness, microstructure, and Debye-Scherrer patterns of specimens which had been aged at various temperatures after quenching from an initial disordering treatment. Experimental Methods A 20 gram ingot of Cu4Pd was made by melting spectrographically standardized copper from Johnson, Matthey, and Co., and commercially pure (99.5 + ) palladium in an argon-filled quartz tube. Chemical analysis showed that the ingot contained 80.0 atomic pct Cu. The ingot was rolled about 60 pct to a strip 0.060 in. thick and was homogenized for 16 hr at 950°C in low pressure argon. Rods cut from the rolled strip were worked into wire 0.015 in. in diameter, and specimens for hardness and microscopic examination were cut from the remaining strip. All specimens, with the exception of some of the wire, were given an initial disordering treatment by heating for 16 hr at 950°C, followed by water quenching. A 10 cm length of as-drawn wire was water quenched after being held in a temperature-gradient furnace4 for 89 days. Room-temperature Debye-Scherrer photograms were then made at points along the wire to determine the temperature below which the ordered phase was stable. Although the accuracy of temperature determination in the gradient was only about ±10 °C, the temperature gradient was sufficiently gradual that the sensitivity was much better and locations which had differed by as little as 1°C could be distinguished. An analysis of the crystal structure of the well ordered alloy was made by X-ray diffraction using a specimen cut from this wire. The change of Debye-Scherrer pattern as ordering progressed was studied by using isothermally aged samples of initially disordered wires. The wires were sealed under low-pressure argon in small quartz tubes for heat treatment. After the aging treatment, the tubes were quenched in water and photograms were made at room temperature in a 10 cm diam camera using filtered Cu kX. (A = 1.540511) Hardness was measured on a Vickers hardness tester using a 10 kg load and 2/3 in. objective lens. Reported values are the average of at least three impressions made on flat specimens 0.060 in. thick. After the hardness of a heat-treated sample had been measured, it was resealed in low-pressure argon and returned to the furnace for continued aging at the same temperature. In this way, two samples served for all aging times at each temperature. Hardness specimens which had been aged 500 hr or more were used for metallographic examination after the final aging treatment. A dilute potassium-dichromate etching solution was used.

Jan 1, 1955

By P. G. Shewmon, F. R. Winslow

An experimental method is describedfor Ihe determination of the derivative of the surface free energy (y,) with surface orientation using symmetric bicrystals. The method measures the equilibrium root-angle of grain boundary grooves for the same grain boundary on two different surfaces. In contrast to previous methods, the presence of annealing twins is not necessary. Results on silver at 900°C indicate that ??s/?3 is 0.014y, on the (loo), 0.075y, on the (111), and < 0.004?s on the (110). DURING an investigation of the kinetics of grain-boundary grooving on silver&apos; values of the derivative of the surface free energy ?s with respect to orientation were needed. Previous investigations of these so-called torque terms show that, for low-index planes in copper2 and nickel,&apos; a finite derivative exists even near the melting point. These two studies give the only previously published values of the torque on low-index metal surfaces. These investigators measured the equilibrium root angles, both greater than and less than 180 deg, along the lines where a twin boundary intersects a free surface. The technique described here is suitable for materials which do not have annealing twins, and enables the surface for study to be chosen instead of having to work in a direction normal to the twin trace on the surface. The purpose of this paper is to describe this new technique and to report the values found for the (111): (100), and (110) surfaces of silver. To check the technique proposed above, a series of 99.99 pct Ag bicrystals were used. These bicrystals were grown from the melt by a modified Bridge-man technique so that a low-index direction was parallel to the growth direction. Two orthogonal faces were studied on each bicrystal. One of these contained the low index or simple plane normal to

Jan 1, 1963

By F. R. Brotzen, D. L. Davidson

ALTHOUGH much effort has been devoted to the problem, the nature of plastic flow in bcc metals is still not fully understood. Some of the difficulties encountered stem from the scarcity of information on orientation effects and the uncertainty as to the glide system in these metals. In an attempt to provide some of this information, the present investigation was carried out, using zone-refined molybdenum single crystals deformed in tension and in direct shear. Considerable evidence exists to indicate that the primary slip system for molybdenum is (110) <111>.1,2 Figs. 1 and 2 indicate that this is, indeed, the case for direct shear at room temperature (see Ref. 3 for a description of the shear-testing equipment and procedure). Moreover, from Fig. 2, the shear stress on the (123) is lower than that on the (112). This would be the case if, as has been suggested,4,5 slip on these two planes is in reality com-

Jan 1, 1965

By A. G. Metcalfe, R. P. Elliott, F. A. Crossley

THE texture method (utilizing monochromatic copper radiation) was applied to determine the orientation of the columnar grains of two vacuum cast beryllium ingots of 3 in. diam. Samples were mounted in a fixture as illustrated in Fig. 1, which permitted rotation and translation in order to approximate the method used for wires. The specimens were aligned so that the major axes of the columnar grains were parallel. Rotation was around the growth direction. After each translation the specimen holder was rotated 2 deg (1 deg for the samples from the second ingot) until a range of 30 deg on either side of the vertical was covered. The speed of translation was 1 mm per sec. A representative Debye pattern is shown in Fig. 2. The pattern was compared with theoretical patterns for various orientations. Also shown in Fig. 2 is the disposition of reflections on the (10i0), (0002), and (1011) Debye rings for the two possibilities that growth is either in the <10i0> or <ll30> direction. It is apparent that no significant preference for the direction of columnar growth is indicated. It is considered that the lack of a preferred orientation is due to the occurrence of the phase transformation (reported by Martin and oore&apos; to occur above 1250 "C) which masked the original solidification orientation. This research was supported by the United States Air Force under Contract No. AF 33(616)-5911, monitored by the Materials Central, WADD, Wright-Patterson Air Force Base.

Jan 1, 1962

By Y. C. Liu

The orientation relationship between the dejormation and recrystallization textztres of binary Cu-P alloys of high phosphorus content was observed to he a ± 14-deg (110) rotation. According to the ori-ented-gvowth hypothesis, the same relationship should exist between a successfully flowing pain and the strained single-crystal matrix of alloys of corresponding composition. The orientations of thirty successfully growing grains were obtained in a Cu-1.0 at. pct P alloy. Both a conventional analysis and the more detailed analysis advanced in the present study demonstrate that the observed orientation relationship is not comparahle to that predicted by the oriented growth hypothesis. IT has been shown experimentally that the formation of recrystallization textures in metals may be explained on the basis of the oriented-growth hypothesis. This conclusion is based primarily on the results of cooperative experiments carried out by various investigators in aluminum. Beck and HU&apos; suggested that the orientation relationship between the recrystallization and deformation textures of aluminum is a 38-deg(111) rotation. A similar relationship, i.e., a 40-deg(111) rotation, was observed between the primary and secondary recrys-tallization textures.&apos; Since the secondary grains result from a process of selective growth, this naturally implies that the same mechanism is also responsible for the formation of the primary re-crystallization texture from the deformed matrix. Further evidence was provided by the experiments of Liebmann, Liicke, and Massing3 and Yoshida, Liebmann, and Lucke.4 They observed that grains which could successfully grow into strained aluminum single crystals invariably exhibited the same orientation relationships with their matrix. Thus, regardless of other opinions,5&apos;9 these results offered good evidence in favor of the oriented-growth hypothesis. In order to examine broader applications of this oriented-growth hypothesis, experiments should be carried out in metals other than aluminum. In a recent investigation on the recrystallization textures of binary copper alloys with phosphorus, arsenic, and antimony,7 it was found that the predominant recrystallization components were related to the deformation textures by a (110) rotation. The (110) rotational relationship is different from the (111) relationship generally proposed between the recrystallization and deformation components of other binary copper alloys. 1,8,9 Applying the observations made for aluminum, the oriented-growth hypothesis predicts that the orientation relationship of grains successfully growing into the strained single crystals of either one of these copper alloys should correspond to that observed in the textural study. Verification of this prediction would provide a critical test of general applicability of the oriented-growth hypothesis to the formation of recrystallization textures in fcc metals other than aluminum. The Cu-1.0 at. pct P alloy was selected in the

Jan 1, 1964

By J. Fageant, W. C. Ellis

All major regions in a progressively solidified germanium ingot were related through successive orders of octahedral twinning. The occurrence of lineage structure and the generation and survival of orientations are discussed. WHEN metals solidify in a temperature gradient a preferred orientation, or casting texture, usually develops. For example, in face-centered and body-centered cubic metals, most of the solidifying crystals have a cube axis, <loo>, aligned approximately in the freezing direction.&apos; In the solidification of diamond cubic metals this is not the case, since there is a natural tendency to form twin orientations.&apos; . In this paper, twinning relationships in cast germanium are described; some conclusions with respect to nucleation and survival of new orientations are discussed. In the first experiment, an ingot of high purity germanium, % in. in diameter and 1 % in. in length, was formed by progressive solidification4 from the bottom. The ingot was cut into 21 slices, each circular and about 0.030 in. thick. The top surface of each slice was polished and etched to reveal the regions of different orientations. Orientations were determined by the Laue X-ray back-reflection method. The uncertainty in the determined orientation relationships was l" or 2" when separate slices and films were involved. Frequently, however, advantage was taken of illuminating across a boundary when the patterns of the two orientations were recorded on the same film. The uncertainty then was less than 1". Often the twin relation was evident from common zones or individual reflections. Twin relationships were recognized through comparison of the values of the nine angles between cube poles of the two orientations with those calculated for successive orders of octahedral twinning. The birth and survival of each region can be reconstructed by visual examination of the etched slices shown in Fig. 1. In slice 21, where solidification began, many regions are present; these regions were found to be twin-related. Solidification appears to have started from one nucleus formed probably at the wall of the crucible.* Subsequent ori- entations were developed by nucleation on existing solid surfaces, and only in the twin relationship. This is an example of a general process of nucleation on a surface of existing solid and may be descriptively termed oriented nuc1eation.t In germanium, and other diamond cubic substances, the orienting habit is that of twinning on an octahedral plane.&apos; " The prevalence of straight traces in the polished surfaces of succeeding slices (Fig. 1) suggests that the twinning observed in the first slice persisted throughout solidification. This was confirmed by X-ray determinations. The schematic diagram of Fig. 2 shows the twinning relationships of the major regions throughout the ingot. Since all observed relationships are describable as twinning, it is reasonable to conclude that no random nucleation occurred in the freezing of the ingot. An alternative possibility would be that nucleation of a random nature occurred, but only those nuclei in twin orientations survived in subsequent growth. This is unlikely for there would be as good a reason for the growth of randomly oriented nuclei as for the growth of the many different orientations present after several orders of twinning. The many twin components contain a wide distribution of orientations, and did grow. In fact, they are the only ones found in the solid. The conditions of solidification of this ingot were such as to discourage nucleation of crystals wholly in the liquid. The rate of solidification was 0.125 in. per min. This slow rate of heat removal afforded but small opportunity for supercooling within the liquid —a condition needed to provide enough decrease in free energy for such nucleation. When nucleation occurs on an existing solid surface, the interfacial energy between the existing and forming regions is important in determining the new stable orientation. The new orientation is expected to be one which minimizes this energy. In the diamond cubic structure, the interface for the

Jan 1, 1955