Search Documents

By E. Buehler, J. E. Kunzler

High-pu.1-ity molybdenum has been heat treated, melted, and zone refined and the physical and chemical changes that are produced by these processes have been studied by making resistance ratio measurements. Pronounced effects are observed that are associated with recrystalliza-tion at about 1200°C and with melting. Melting alone is found to result in a substantial purification by the evaporation of impurities such as iron. Zone refining is found to be reasonably effective with four passes producing a three-fold decrease in resistance ratio and a minimum ratio of 0.0003. With the aid of low temperature measurenzents, it has been shown that the build-up of a deposit of the material being zone refined on the radio frequency coil used for heating can lead to contamination of the sample. CONSIDERABLE interest in high-purity refractory metals for the study of mechanical properties has developed during recent years. Also the need for highly pure metals in certain fundamental studies, such as electronic band structure, has become quite widely appreciated. Molybdenum can now be produced with sufficiently high purity to make it attractive for such investigations. The most suitable measure of chemical purity of metals used for many of these studies is its resistance ratio, R,.,o,/Ro, During the purification of molybdenum by zone refining and its subsequent evaluation by this technique, a number of informative observations were made. These observations concern the effectiveness of zone refining, the volatilization of impurities at the melting point, and the recrystallization of molybdenum and appear to be pertinent to other refractory metals. Also, the usefulness of low-temperature resistance measurements as an analytical tool for evaluating the presence of chemical impurities and physical defects in metals is again illustrated. Samples of high-purity molybdenum of known mechanical history were heated to various temperatures between 800°c and their melting point. Resistance ratios of the samples were measured after they had been given a specified treatment. The data were used, along with mass spectrographic analysis, as an aid in interpreting the nature of the processes that occurred in conjunction with each treatment. Changes in the concentrations of chemical impurities and physical defects are typical of things that effect the low-temperature resistivity. SAMPLES The starting material was obtained from Westing-house Corp., Bloomfield, N.J. It was in the form of molybdenum rods, usually 1/8 or 3/16 in. in diameter. These had been previously processed from bars, 5/8 in, in diameter, originally reduced from 4 in. diam arc-cast ingots, by hot swaging at about 1300°c. In the final step, the temperature was lowered to about l lOO°C which resulted in the production of elongated grains. Typical grains were about 0.03 mm thick and 0.6 mm long. The molybdenum was quite pure as is indicated by the results of mass spectro-scopic analysis1 given in Column 2 of Table I. Other nongaseous elements not listed in the table were not detected. ZONE REFINING AND THERMAL TREATMENT OF SAMPLES Several sample rods, 8 to 10 in. long, were zone refined or were heat treated at several temperatures. Both types of operations were performed using 3 me-

Jan 1, 1962

By H. C. Chang, N. J. Grant

REEP studies and measurements in most in-V> stances are based on a relatively gross gage length. Even in some recent theoretical studies on the mechanism of creep, changes were followed by means of X-rays and metallography without regard for the behavior of the individual grains and grain boundaries.'" Analytical studies of creep have frequently indicated that more than one competing process is operative and that the ultimate creep performance depends on the effects of temperature, time, and strain rate as well as grain size.'-" he grains and grain boundaries are known to respond differently to these variables but the extent of the response is still little known, especially in poly-crystalline materials where the relative orientations of grains and grain boundaries are important. This paper reports some experimental observations of the behavior of the grain boundaries and their effect on the deformation in the grains. High purity aluminum was used to avoid complications of aging reactions, second phase, inclusions, etc. Experimental Procedure A small vertical nichrome wound furnace was built to permit direct loading on the test specimen. This furnace is capable of operating up to about 1300°F with reasonable temperature distribution. A ground rectangular quartz window, 1.25x0.5 in., is imbedded in the external stainless steel tube to permit observations of the creep process with a microscope. An argon atmosphere ,was provided to prevent oxidation. The quartz window caused a temperature gradient between the back and front surfaces of the specimen of 15" at 700°F. The temperature gradient could be cut down to 3°F along the length of the specimen by adjusting shunts across the furnace windings. An ordinary metallurgical microscope with a working distance of 14 mm was rebuilt so that it could be moved in three mutual perpendicular directions. Visual examination could be made with either a 30X eyepiece or a 15X filar eyepiece. Using an objective of focal length 24.3 mm and a numerical aperture 0.20 a total magnification of 120X or 240X could be obtained. High purity aluminum rated at 99.995 pct was supplied by the Aluminum Co. of America as % in. then the gage portion was further machined to 3/16 in. diam. The ends were Y4 in. diam and threaded to fit available specimen holders. Two opposite flat surfaces of the gage portion were obtained by milling, giving final dimensions of the gage portion of 3/4x3/16x3/32 in. Machined specimens were first electropolished in Jacquet's solution.' Reference marks were produced by pressing a thin sewing needle into the surface of the specimen. The specimen was then annealed at 900°F for 24 hr and at 1150°F for 12 hr. Typical macrostructures of specimens treated in this manner are shown in Fig. 1. The range of the grain size was 1 to 5.5 mm (see Fig. l), but most of the grains were of 2.5 mm and went through the whole thickness of the specimen. The specimen was re-electropolished and etched electrolytically to reveal the grain boundaries. In order to reveal the orientation difference of the grains, etch pits were produced on the surface of the grains by etching in a mixture of hydrochloric and nitric acids (HC1, 45 pct; HNO,, 10 pct; H,O, 45 , by volume). The specimens were very carefully put into the holders and furnace; yet even with this care, fine slip lines were developed on the specimen surface.

Jan 1, 1953

By D. L. Creighton, S. A. Hoenig

The field-emission microscope has been adapted for the study of microcrack growth during the early stages of fracture in metal wires. Cracks as small as 6 1 in length can be detected and their growth can be followed to specimen failure. The system is quite useful in searching for microcracks since only sharp-edged surface defects will emit electrons under the experimental conditions. THE conditions leading to brittle fracture were discussed a number of years ago by Griffith1 and the term Griffith Cracks is often used for the small surface cracks which are responsible for brittle fracture. Griffith's theory has been modified by stroh2 and more recent results on metals are discussed by Allen,3 pp. 123-40. At present the phenomenon is not completely understood but there is general agreement that at least in certain materials the sequence leading to brittle fracture involves several stages. The initial microcracks are present because of cooling or working stresses, Hahn et al.,3 p. 95. When a stress is applied to the specimen the cracks grow slowly until the release of stored elastic energy is large enough to accelerate the crack and provide the necessary surface energy for crack growth. At this point the growth rate appears to increase rapidly to some new equilibrium velocity, and failure occurs. Since the microcracks are usually about the size of a single metallic grain (Ref. 3, p. 99) it is not easy to find them and it is very difficult to follow their growth under stress. This paper will report on the use of a cylindrical field-emission microscope for observation of the formation and growth of microcracks. I) THE FIELD-EMISSION MICROSCOPE The field-emission microscope (FEM) has a high magnification and resolution and is almost uniquely suited for observations of microcracks. Since the FEM is relatively new as a metallurgical instrument, a short description will be given here. Normally metals at room temperature do not emit electrons; however in the presence of a strong electric-field gradient, electrons can tunnel out through the reduced potential barrier. Since this tunneling is a function of the local field gradient and the local work function, the emitted electrons can be used to produce a highly magnified image of the surface by allowing them to strike a phosphor screen. Because the electron emission is dependent upon the local field gradient, smooth surfaces emit few electrons except at very high fields. On the other hand cracks, extrusions, or other surface defects, having sharp edges, emit strongly since the field gradient is very high in the vicinity of these defects. This indicates that the FEM should be most useful for detection of microcracks on otherwise smooth surfaces. A field-emission microscope was first used by Muller4 in 1936 for observation of metal surfaces, and recent reviews have been given by Muller5 and Gomer.6 The instrument has been used for metallurgical studies in the area of surface diffusion,= recrystallization,7 and grain growth 8 (Ref. 8 is directed specifically at metallurgists). In the work of Muller4,5 and Gomer 6 the specimen was in the form of a sharp metal point at the center of a phosphor-coated glais sphere. The impact of the emitted electrons on the phosphor produced a highly magnified image of the specimens. Such a system is not practical for applying a controlled stress to the specimen and a cylindrical geometry has been used in this investigation. This allowed the application of a controlled tensile stress to the wire specimen. Normally a cylindrical FEM geometry produces magnification only in the radial direction. This is the case because a smooth wire at the center of a cylinder produces a purely radial electrical field. However, if there is a break in the smooth surface of the inner cylinder, the field near the break becomes three-dimensional and the area of the break is highly magnified. The reason for this is clear if it is recalled that the field gradient depends on the relative radii of the inner and outer cylinders; if a crack forms, its edge radii are of atomic dimensions and a very high field gradient is formed near these crack edges. Since the electrons receive most of their acceleration near the crack edge and are always traveling perpendicular to the field lines, they tend to spread out and produce the magnified image observed in the cylindrical field-emission microscope. 11) BRITTLE-FRACTURE STUDIES A) Experimental Apparatus. The geometrical arrangement chosen was that used earlier by Gifford

Jan 1, 1965

By P. E. Doherty, R. S. Davis

Sub boundaries and micropores, as well as certain other imperfections, may be revealed in aluminum by the formation of pits on the surface during cooling from elevated temperatures. The pits are attributed to the condensation of vacancies from supersaturated solution. This "vacancy pit" phenomenon has been used as an etching technique for studying the structure of aluminum specimens grown from the melt. Three fundamental structures were studied: stria-tions, cells, and dendrites. Two types of striations, as well as a crosswise structure are reported. Mic-roporosity is observed to occur in the cell walls on freezing. Subboundaries between primary, secondary, and tertiary branches are observed in dendritic growth. A special case is cited in which cellular growth suppresses the formation of striations. SMALL, well-defined pits have been observed to form on the surfaces of electropolished aluminum specimens during cooling from elevated temperatures.' This phenomenon was attributed to the condensation, from supersaturated solution, of vacancies at particular points on the surface. It was shown that the amount of cooling required for the formation of pits increased exponentially with decreasing holding temperatures in a way that was consistent with the thesis that a critical supersaturation of vacancies was required for the pits to form. Pits do not form in the vicinity of certain imperfections, namely, subgrain or normal graind boundaries, phase boundaries, certain surface irregularities, and pores. The width of the pit-free region increases with decreasing cooling rate. This observation suggests that the imperfections in question are effective sinks for vacancies and that the pit-free region around them is material that is not sufficiently supersaturated with respect to vacancies to nucleate the surface pits during cooling.

Jan 1, 1962

By Robert Maddin, Neng-Kuan Chen

THE (001) planes have been reported as the cleavage planes in body-centered cubic metals such as alpha-iron and tungsten.' However, in molybdenum, which is also body-centered cubic, experimental X-ray evidence indicating a similar cleavage plane still seems lacking. Tsien and Chow" observed microscopically in the extension at around 1000°C of molybdenum single crystalline wires 0.25 mm in diam that the fracture plane seemed to be parallel to the operative slip plane, which appeared to be (110) at that temperature. Zapffe' pointed out from fractographic study of polycrystalline molybdenum that "although the transgranular pattern is characteristically non-crystallographic, patterns occasionally reveal {100} cleavage." This has been generally assumed to be the case at ordinary temperatures. In the present experiments, a single crystal of Fansteel molybdenum, Vs in. diam x 2 in. long, prepared by the methods described by Chen, Maddin, and Pond" was fractured at room temperature by bending. The fracture surface appeared to be quite similar to the cleavage surface of zinc and was crys-tallographic. A back-reflection Laue photogram was made using 35 kv copper white radiation; the X-ray

Jan 1, 1952

By R. J. Wasilewski

The resistivity of single crystal and of polycrystalline metal has been determined between 77° and 1500°K. At comparable purity, the resistivity of the poly crystalline metal differs from that calculated from the axial resistivity values. The observed anisotropy is briefly discussed. A zone refined titanium rod was obtained from F. J. Darnell.1 The hardness of this material varied between 52 and 64 Bhn, indicative of its high purity. Single-crystal specimens were cut out from a few large grains, elongated predominantly along <1120>. Resistance measurements were taken with specimens immersed in liquid nitrogen, solid CO,, and acetone, and at ice point, and then recorded continuously between room temperature and 1200" to 1250°C, throughout at least one full heating and cooling cycle at a rate of l° to 3°C per min. Four probe measurements were taken using spot-welded Pt wire 0.003 in. in diam as potential terminals, and the electromotive force drop was determined poten-tiometrically. A standard resistance, in series with the specimen, served to determine the dc current (generally about 80 ma) in the circuit. In order to eliminate spurious thermal electromotive forces, the circuit polarity was automatically reversed at 5-min intervals, and the mean of the two adjacent readings taken as the true electromotive force value. The discrepancy between the readings at reversed polarities was generally of the order of a few µ v, as all the spot-welded joints were contained within a volume of some 5 mm cube. The relative resistance (R T/R 273o) variation with temperature is tabulated below, and shown in Fig. 1, as measured during the first heating run. The discontinuous drop in resistance, corresponding to the a — ß transformation, started for both initial orientations at 1170°K; i.e., some 15°K above the accepted value of 882°C (1155°K). Judging by the temperature ranse of transformation—some 30°K for the single crystal and 20°K for the polycrystal-line specimen—this difference is believed caused by the solution of the oxygen present initially on the surface of the specimens. The general trend of the resistance vs temperature shown in Fi,;. 1 is in qualitative agreement with that previously reported for polycrystalline titanium metal. 2,3 Significant anisotropy is, however, indicated by the crossing over of the curves for <1120> and <0001> orientations at 273°, 650°, and 1000°K. This difference is most startlingly shown in Fig. 2, where instantaneous temperature coefficients (l/R273 x dR /dT) are plotted for both the first heat-

Jan 1, 1962

By H. C. Rogers, B. W. Roberts

Vanadium foils and wires, either cold-worked or recrystallized, show a ductile-brittle-ductile fracture sequence with temperature. At about 150°C the hydrogenated vanadium wires are found to be ductile. At room temperature the wires show brittle fracture, and at liquid nitrogen temperature the wires are again ductile, although to a lesser extent than found at 150°C. Hydrogenated cold-rolled vanadium foils have been found to fracture in unusually straight lines along the [100] texture directions. The hydrogen content required to show this [loo] texture fracture is limited to a few atomic percent in range. Hydrogen content above this range causes fracture to occur in random directions. PRELIMINARY experiments with hydrogenated vanadium foils indicated that the embrittling effect of the hydrogen on the vanadium, which was severe at room temperature, was reduced at both lower and higher temperatures. In order to investigate more quantitatively the ductility changes with temperature, vanadium wires were tested in tension at three temperatures. The reduction of area was measured and the fractures examined. Specimen Preparation—The material used was kindly supplied by A. U. Seyboltl in the form of M-in. rod. The nominal analysis was: 99.2 pct V assay, 0.2 pct C, 0.01 pct Si, 0.01 pct Fe, 0.015 pct Ca, 0.02 pct O,, 0.01 pct N2, and 0.003 pct H,. The specimens were 0.035-in. diam wires. These were prepared by cold-swaging the supplied rod to the final diameter without intermediate anneal. They were finished with long-bearing dies. The surface was then given a light polishing with 0 emery paper and degreased in trichlorethylene. An X-ray check indicated that the cold-swaged wire had a fairly strong [110] fiber texture. The wires were then recrystallized in vacuum in continuously pumped quartz tubes at two temperatures to give two different grain sizes. One group of wires was given 45 min at 800°C; another, 60 min at 1000°C. The microstructures in Fig. 1 show the wires after they have been electropolished and elec-troetched in 10 pct HCI. After the 800°C anneal, the vanadium grains had a diameter of 1 to 2p and there appeared to be a tendency to elongation in the longitudinal direction. However, the latter may be an etching effect. After the 1000°C anneal, the grains appeared to be equi-axed, but there was a very large spread in grain size, probably due to some impurity segregation in the wire, Fig. 1, right. The grain diameters varied between the limits of 1 to 150p. The small particles shown particularly clearly in Fig. 1, left, are also visible on the polished surface of all samples before etching and are undoubtedly carbides and nitrides of vanadium. An X-ray check indicated these annealed wires had a strong [110} recrystallization fiber texture. The hydrogenation was carried out in an iron retort with dry hydrogen flowing through it, the retort and contents being heated in a tube furnace with a hydrogen atmosphere. The hydrogenation temperature was approximately 500°C. The hydro-genation times chosen were approximately those which would be just enough to cause the vanadium to be brittle at room temperature and thus allow the greatest chance for ductility to occur at the other two temperatures. Part of the fine grained specimens were hydrogenated for 21/2 min at 490°C. Part of the coarse grained specimens were hydro-genated for 11/2 min at 515°C.

Jan 1, 1957

By F. W. C. Boswell, R. L. Cunningham, H. M. Weld

Chemical analysis shows the partition of the magnesium addition between the metal and the graphite is independent of whether the graphite is in the form of nodules or flakes. The bright central spot observed in nodular graphite polished sections is shown to be due to the structure of the nodules. DURING the past few years numerous papers have been published on the production1-7 and heat treatment" of nodular cast irons. However, very little information is available on the structure of the nodules and the reason for their formation. It would appear that an explanation of the phenomenon of nodulation must await a detailed knowledge of the nature of the nodule. Disagreement exists among various workers on such a fundamental point as to whether or not a nodule actually contains a microscopically visible, nongraphitic nucleus.9-11 Work was initiated with a view to obtaining definite information on this and other aspects of the problem. Chemical Separation and Analysis Microscopic appearance had indicated9-11 that a nongraphitic core might exist in nodules (Fig. 1). It appeared that a chemical comparison of separated nodules and flake graphite would be profitable, for if the core is nongraphitic a relatively large amount of certain elements would be found in the nodules as compared to the flake. This comparison could best be made by obtaining nodules and flake from the same melt of cast iron, part of which had been in-noculated with a suitable addition reagent for the formation of nodules. A 300 lb melt was produced. About half of this was innoculated in the ladle with an Fe-Si-Mg alloy to produce nodules and cast into keel blocks; the remaining half of the melt had silicon added in an effort to compensate for the silicon in the innoculant used in the other half of the melt and this was cast into similar keel blocks. The analyses of the resultant irons are given in Table I. Nodules and flake were chemically extracted from 2 kg samples of metal as described in the appendix. While this method dissolved the iron and chromium carbides, it did not dissolve the titanium, vanadium, and molybdenum carbides. These latter carbides could have been removed by nitric acid, but in other experiments it was found that it attacked pools of metallic iron entrapped in the nodules which had, until the nitric acid treatment, been protected from the attack of the sulphuric, hydrochloric, and hydrofluoric acids. It will be shown in the next section that entrapped iron exists in nodules but not in flake. On microscopic examination many tiny irregular particles were observed to accompany both the nodules and the flake. These were identified by tabling a sample of nodules from which a sufficient fraction was obtained for X-ray analysis. A good pattern of titanium carbide was obtained indicating that this was the predominant compound present. Since it was not possible to determine how completely the carbides could be removed mechanically and since their removal from flake is much more difficult, it was decided not to resort to any separation as this would render further comparisons more difficult. The samples were ashed in a combustion

Jan 1, 1953

By J. R. Low

The brittle fracture of a Tic-lnconel cermet at room temperature is shown to occur primarily as a result of the cracking of the larger carbide particles (at a tensile strain of approximately 0.3 pct), followed by cracking of adjacent, smaller carbides and, finally, by the rupture of the lnconel matrix between cracked carbides (at a strain of-1.2 pct). No evidence was found for separation at the interface between carbide and matrix at any point in the fracture process. MATERIAL used in this study was a Tic-Inconel cermet prepared by infiltration (50 pct Tic, 50 pct Inconel: designated as TC66-I). A thin section of this material was brazed to a piece of low carbon steel and then mounted in lucite for metal-lographic preparation." After grinding, polishing, Deformation and fracture of the specimen was accomplished by bending the specimen as a simply supported, centrally loaded beam, in a bending fixture which could be placed in the stage of a microscope, with the tension side of the bend specimen under the microscope objective.? This method of deformation and observation has the advantage that the surface under examination is the most severely deformed portion of the specimen. The procedure followed was to deform the specimen a small amount, scan the surface at Xl OOO for any evidence of deformation or cracking, deform another small increment, scan the surface again, and so on until a

Jan 1, 1957

By J. L. Walter

Extra-low carbon iron sheet, when deformed and annealed, undergoes exaggerated or abnormal grain growth in the critically deformed regions of the sheet. This exaggerated pmth occurs, for low strains (3 to 6 pct), only in sheet which has a fine dispersion of precipitates in the subsurface region of the sheet and fewer and coarser precipitates in the sheet interior. These particles have been identified as manganese sulfides. Wing the anneal, grains near the surface are gvowth-inhibited by the fine particles but the grains in the interior are free to grow normally. With the additional driving force provided by the strain energy, the interior grains first grow into the small subsurface pains. Eventually, these growing grains grow completely through the sheet. Calculations of limiting grain sizes at various values of strain indicate that a volume fraction of precipitates in excess of 10-&apos; would be required to eliminate exaggerated growth in material strained to 10 pct. OPEN-COIL annealing has made decarburization of sheet steel both efficient and economically practical. Use of such material for porcelain-enameling stock is one of many possible applications of low-carbon iron since carbon in steel is deleterious to porcelain-enameling properties.&apos; However, the extra-low carbon iron presently available presents another problem, that of exaggerated grain growth in regions where the sheet has been deformed as by bending or stretching. In exaggerated grain growth a few grains start to absorb their neighbors and these may become very much larger than the average grains of the sheet. Other names for exaggerated grain growth are coarsening, critical grain growth, secondary recrystallization, abnormal grain growth, or discontinuous grain growth. While this grain growth does not affect the enameling qualities of the low-carbon iron sheet, their presence results in a marked reduction of tensile-yield strength in the region of the sheet containing the large grains. The loss of tensile yield strength may render the material unsuitable for many applications . This report describes the results of a study undertaken to determine the cause of the exaggerated grab growth in extra-1ow carbon iron and, if possi- ble, to prescribe practical procedures for its prevention. GENERAL THEORY The driving force for exaggerated grain growth is the grain boundary free energy. This driving force is proportional to (l/rl + l/r2) where rl and r2 are the mutually perpendicular radii of curvature of the boundary between the growing grain and the grain being consumed. Thus, the greater the difference in size between the growing grain and the matrix grains, the higher the driving force for grain growth. If, however, the matrix grains are free to grow simultaneously, the driving force for exaggerated growth will be diminished. Stability toward growth of the matrix grains may be caused by a) a strong single orientation texture (texture inhibition),&apos; b) a dispersed second phase,3"5 c) the thickness effect,&apos; or d) intergranular segregation.7"9 As exaggerated growth occurs when growth of the matrix grains has been slowed by the stabilizing processes mentioned above, there must be an additional factor acting to promote growth of a few of the grains to the point where they are enough larger than the matrix grains that boundary energy driving forces are sufficient to cause continued growth. For instance, at the annealing temperature, growth-inhibiting inclusions may slowly dissolve and coalesce. Eventually, a grain boundary becomes unlocked and migration occurs at the expense of neighboring grains. Or, an additional driving force may be supplied to some of the grains if the material is strained. Then, since some grains will be strained less than others, the difference in strain energy between adjacent grains may be sufficient to overcome boundary locking and allow growth of the grains with lower strain energies. In the present study, therefore, such factors as the presence or absence of dispersed phases, the nature of the exaggerated growth, and the effect of strain have been considered. EXPERIMENTAL PROCEDURE I) Material and Processing. Three types of low-carbon iron were used in this study; types A and B were commercial grades, each from a different supplier.* The precise details of the processing of

Jan 1, 1963

By R. D. Nelson, D. H. Polonis

ThE eutectoid decomposition of 6 phase in the Cu-Sn system (32.53 wt pct Sn) has been studied by several investigators.1-6 On the basis of X-ray work, Iball and 0wen1 reported complete decomposition of 6 in powder specimens after 7 days at 300°C. Wang and Hansen followed the micro-structural changes during heat treatment of lump specimens and estimated 5 pct decomposition after 63 days at 300°C. Wang and Hansen suggested that the discrepancy between the decomposition rates of powder and lump specimens might be due to the excess surface free energy of powders. The present work involved 6 decomposition in copper-tin alloy powders containing 32.6 wt pct Sn. Alloy lump specimens exhibited entirely 6 phase after fairly slow cooling (air cooling) from above 350°C and were so brittle that they could be easily crushed to-200 mesh in a percussion mortar. X-ray diffraction study of the as-crushed powders (-200 mesh) revealed 100 pct 6 phase with very slight line broadening effects due to strain introduced by crushing. Only 6 phase was detected by X-ray diffraction in powders which were heat treated 4 hr at 450°C and air cooled to room tem-

Jan 1, 1960

By Harry A. Lipsitt, Rollins E. Hook, Attwell M. Adair

A necessary condition for a uniaxial stress distribution in compression testing is that the specimen end surfaces make full contact with the apparatus compression plates. In addition all compression surfaces must be machined perpendicularly to the loading axis. In general this condition is not sufficiently fulfilled in a simple apparatus. Therefore on application of the load the compression plate may first touch the specimen at one point only. This may cause crumbling of the specimen if the material under investigation is brittle (e.g., ionic crystals). It also precludes a precise study of the beginning of deformation as the effective cross sectional area is unknown. In addition a complex stress state is set up which renders quantitative work impossible, e.g., on dislocation density and arrangement as a function of stress. To overcome these difficulties a "self-adjusting" upper compression plate is required. A simple and reliable method of achieving this is shown in Fig. 1: A steel hemisphere is placed on the specimen. As soon as the compression plate (which no longer needs precise machining) makes contact with this hemisphere the load is uniformly distributed over the whole specimen surface, and a homogeneous uniaxial state of stress results. An advantage of the method is that the loading is always central, even when the specimen surface is not parallel to the compression plate (Fig. 1, dashed line). Therefore to a first approximation a uniaxial state of stress is maintained if the misorientation of the specimen end surface is small. Two typical stress strain curves of identically prepared sodium chloride crystals are shown in Fig. 2; curve 1 was taken without and curve II with the hemisphere under otherwise identical conditions. The improvement in the accuracy of defining the beginning of elastic and plastic deformation is clearly indicated. The writer wishes to thank the Deutsche Forschungsgemeinschaft for financial support, and Professor P. Haasen for providing facilities for this work.

Jan 1, 1962

By Ronald C. Koo

THE effect of grain size on the mechanical properties of the bcc metals has been a subject of intensive theoretical and experimental study.&apos;-l5 Quantitative relationships have been established experimentally between yield stress and grain size and between the ductile-brittle transition temperature and grain size in a number of metals.6"15 Much significance has therefore been attached theoretically to the grain size dependence. In all these experiments, different grain sizes were always achieved by annealing specimens at various temperatures. The implicit assumption was that any change in the dislocation substructure or in the distribution of impurities which might occur simultaneously with the production of various grain sizes had only a negligible effect on the mechanical properties. The validity of this assumption, however, is questionable. transformation in iron-nickel alloys is actually an extraneous phenomenon due to inadvertent compositional changes in the martensite if the heating rate is not sufficiently rapid. This complication can be avoided by up-quenching for the reversal treatment,5 and then the stabilization does not appear. Clearly, the lattice imperfections and strengthening produced by the reverse transformation are not responsible for the marked stabilization which has been observed by other investigators in these alloys. Data will be presented in this note to show that, at least in recrystallized tungsten of commercial purity, the difference in the ductile-brittle transition temperature of specimens annealed at various temperatures is more a result of a variation in the distribution of impurities rather than of the difference in grain size produced by the anneal. Ductile-brittle transition temperatures in tension were determined on powder-metallurgy tungsten specimens recrystallized at various temperatures. Tensile specimens having a gage length of 1.50 in. and gage diam of 0.18 in. were recrystallized at 1450°, 2000°, 2350°, 2550°, 2750°, or 2800" for 30 min in a vacuum furnace at a pressure of 1 x 10"5 mm of Hg and then tested at a constant extension rate of 8 x 10 per sec in an argon atmosphere from 100" to 800". Typical quantitative analyses of impurities are given in the Table. These results show that, within the precision of the analyses, see Table, annealing did not result in any detectable change in the impurity contents of the specimens, nor was there any detectable difference in purity between specimens having large differences in grain size annealed at the same temperatures . The results of the tensile tests yielded three distinct ductile-brittle transition curves approximately 225&apos; apart. As shown in Fig. 1, data of specimens annealed at 1450°C and those of specimens annealed at 2000°C (O) fell on Curve A. Data of specimens annealed at 2350" and 2550°C fell on Curve B, and those of specimens annealed at 2750" and 2800°C fell on Curve C. The decrease in ductility with increase in annealing temperature became so pronounced that one third of the specimens annealed at 2750" and two thirds of the specimens

Jan 1, 1963

By W. Rostoker

A STUDY of the titanium-oxygen system&apos; involved an associated series of measurements of the lattice parameters of the a and TiO phases. The results permit some interesting deductions which are herein reported. A comprehensive survey of the physical PI-operties of the phases in this alloy system has been made by Ehrlich.2 However, only impure titanium was available at that time, so that some revision of his measurements is to be expected. The lattice parameters were calculated from the high angle lines of Debye-Scherrer patterns taken in a 14 cm camera and using filtered CuKa radiation. The specimens were prepared largely by crushing and screening of lump samples which had been quenched from elevated temperatures. Only in the case of low oxygen contents was it necessary to resort to filing and annealing. The results of the lattice parameter studies are graphically presented in Figs. 1 and 2. It will be seen that oxygen produces a pronounced distortion of the c parameter of the a phase (hexagonal close-packed). The trend is in general agreement with Ehrlich&apos;s work, although the divergence of actual parameter values strongly suggests that his titanium was very impure. It will be noted that the a phase of titanium can tolerate the unusually high saturation solubility of about 34 atomic pct 0. By virtue of this unique effect, it is possible to make a calculation of the effective atomic diameter of oxygen when dissolved in a lattice with metallic bonding. This has not been possible before. Ehrlich&apos;s2 density measurements demonstrated that oxygen occupies interstitial positions in the a lattice and the trend of the lattice parameters would certainly support this. In a hexagonal close-packed unit cell the largest interstitial positions lie at (2/3, 1/3, 1/4) and (2/3, 1/3, 3/4). Accordingly, if both of these positions were occupied, the ratio of titanium to oxygen would be 1:1. The extrapolated c parameter may be taken as between 4.93 and 4.99?. The a parameter appears to reach a constant value of 2.955? at low oxygen contents. The distance of the center of a titanium atom site from the [vc2/16+a2/3-1.448] Then the atomic diameter of the oxygen atom is represented by the function: where the radius of the titanium atom is 1.448A,

Jan 1, 1953

By W. J. Babyak, J. M. Sheehan, H. W. Paxton

THE- solubility of hydrogen and deuterium in solid niobium up to I-atm pressure has been established bv a number of workers.1-5 X-ray examination at room temperature of specimens reacted in hydrogen at high temperatures from 300° to 1000°C shows the presence of two phases—a bcc phase (a) based on the niobium lattice and with an u0, increasing from 3.30A for Nb to 3.32Afor NbHo.L, and an orthorhombic phase6n = 4.84A, h=4.90A, c =

Jan 1, 1960

By John D. Roach

DURING an investigation of the yttrium-hydrogen system aimed at producing solid yttrium hydride specimens containing various amounts of hydrogen, it was observed that yttrium containing approximately 2 wt pct H exhibited a tendency to crack and crumble to a powder on standing in air at room temperature. It was also observed that longer hydriding times, at a given temperature, increased this susceptibility to powdering without an increase in hydrogen content, also that moisture in the air is necessary for the observed effects to occur. Even if cracking did not occur, there was a continual formation of a light gray powder on the as-treated surface of the hydrided yttrium and this reaction continues until the entire hydrided piece has been reduced to a powder. Storing the hydrided specimens in the absence of air or removing the surface either by machining or grinding were effective means of preventing this disintegration of hydrided yttrium. In an attempt to determine the reason for this powdering phenomenon, the surfaces of a number of as-hydrided yttrium specimens were examined by X-ray techniques. In all cases the X-ray pattern obtained showed the major phase to be yttrium hydride (YH2) as would be expected since the specimens contained 2 to 2.2 wt pct H. In some cases a trace of yttrium oxide was observed. There was also a third phase present on the surface of these hydrided specimens which could not immediately be identified. This unknown phase was a face-centered cubic material, NaC1-type structure, with a lattice parameter of 4.855 and a calculated density of 5.914 g per cc. Very slight hand polishing of the surface of the hydrided yttrium specimens completely removed both the unknown phase and the traces of oxide so that only the yttrium hydride pattern remained. Based on the X-ray patterns the quantity of the unknown phase on the surface of the hydrided yttrium appeared to be directly related to the susceptibility of the material to powdering. Work at the Denver Research Institute on the yttrium-nitrogen binary system showed that yttrium nitride (YN) is a face-centered cubic material with a lattice parameter of 4.878A and a density of 5.890 g per cc. They also noted that this compound rapidly disintegrated to a powder on standing in air. The unknown pattern observed in the above specimens corresponds very closely to that of the nitride—fcc structure, 4.885 parameter, and density of 5.914 g per cc. The presence of this thin film of nitride on the surface of the hydrided specimens probably accounts for the observed powder formation and crumbling. The nitride reacts with the water vapor in the air (verified by private communication from Dr. C. Huffine, General Electric Co.) to yield yttrium oxide and ammonia. Ammonia is readily detected when hydrided yttrium specimens were allowed to stand in bottled moist air. The powder formed on the surface of the hydrided specimens was shown by X-ray analysis to be yttrium oxide. This reaction appears to occur primarily at the grain boundaries since discrete particles of yttrium hydride separate from the specimens during this powdering process. The reaction of yttrium nitride with water vapor is believed to be as follows: 2YN + 3H2O - Y203 + 2NH3. Despite the fact that this nitride is present only as an extremely thin surface film, if the above reaction is not prevented by removing this film from the surface either by machining or grinding, the reaction continues until the entire hydrided piece has been reduced to a powder. To account for this continuation of the reaction, it is believed that the following reactionalsooccurs: 2YH2 + 2NH3 -2YN + 5H2. The nitride produced by the latter reaction reacts in turn with water vapor. The reaction therefore becomes autocatalytic and continues until the hydride has been consumed and the entire piece reduced to oxide powder. The amount of nitride required to initiate this reaction is quite small and this nitrogen contamination can occur from a number of sources—hydrogen gas employed, minute leak in the hydriding apparatus or even from degassing of the reaction vessel itself. Longer hydriding times increase the possibility of nitrogen contamination and this is especially true when a dynamic gas system is employed in the hydriding process. The production of stable, solid hydrided yttrium is dependent on the complete absence of nitrogen contamination during processing. If such contamination does occur, powdering of the hydrided product can be prevented by removing the nitride from the surface e.g. grinding or by preventing access of air to the pieces e.g. sealing in wax or plastic. The author wishes to express his appreciation to General Electric Co. for sponsoring this research and for permission to publish the results of work under Subcontract AT-93.

Jan 1, 1962

By H. Hu

Observations were made on the recrystallization of a 70 pct cdd-rolled silicon-iron crystal with an initial orientation of (113) [332]. Its polygonization and recrystallization characteristics were studied. Results indicated that re crystallization tendency of the deformed crystal is much weakened by the polygonization of the matrix. Complete recrystallization in such specimens is achieved by the growth of recrystallized grains of sufficient size and of the right orientations in relation to the matrix. Evidence was also furnished which suggests that the difference in the re-crystallization tendency is a result of the difference in the severity of lattice bending rather than the difference in orientation of the deformation texture. DUNN and Koh1,2 have made an extensive study on the rolling and annealing textures in silicon-iron crystals. Their results indicated that the recrystallization tendency can be widely different in crystals with different orientations. A particularly interesting example of their results was a crystal with an initial orientation of (113) [332], which developed a deformation texture of (001) [110] after 70 pct cold-rolling. Recrystallization in this crystal took long time anneals at high temperatures. Other crystals having different orientations recrystallized very rapidly. Wiener and corcoran3 have observed the retention of the (100) [011] deformation texture in a low-temperature annealed specimen of a commercial silicon-iron alloy, corresponding to areas of light-etching low-angle boundaries in the annealed struc-

Jan 1, 1960

By J. Gurland

THE microstructure of sintered carbides consists of particles of metal carbides, such as WC and TiC, embedded in a metallic binder which is usually a cobalt—or nickel-rich solid solution. One of the important factors influencing the strength of the alloys is the degree of dispersion of the carbide particles in the binder matrix. While it is generally accepted

Jan 1, 1960

By D. W. Levinson, L. E. Tanner

DURING the course of an investigation of the zirconium-iron-tin system the zirconium-iron system was reexamined up to 55 pct* Fe. The alloys pre- visible melting3 and X-ray diffraction studies were made of samples of the alloys. The ferromagnetic properties of ZrFe2were determined by Professor P. W. Selwood* using a modified Faraday balance.4 The zirconium-rich portion of the phase diagram is presented in Fig. 1 and compared with the work of Hayes et al.1 The maximum solubility of iron in ß is somewhat decreased while the eutectic temperature is raised. There seemed to be no change in the eutectic composition of 16 pct Fe. Since the base material was so low in iron content, it was possible to establish the maximum solubility in a between 0.017 and 0.025 pct Fe at the eutectoid temperature. The observation of fine ZrFe, particles in the micro structure of a specimen of 0.012 pct Fe alloy quenched from 700°C indicated that the solubility drops below this composition at 700° C and lower. Further study was made of the intermediate phase ZrFe2. wallbaum5 identified the compound initially as ZrFe2 with a C 15 (MgCu2) structure, placing it at 55 pct Fe stoichiometrically. Hayes et al.1 believed they found the phase at about 47.2 pct Fe and called it Zr2Fe3 but reverted to ZrFe, in the discussion of their paper.6 Jordan and Duwez7 confirmed Wallbaum&apos;s work as well as finding the same single-phase structure to about 62.3 pct Fe or Zr0-61 Fe2-18. In order to establish the ternary phase relations in the zirconium-iron-tin systema the exact position of this phase had to be known. This was accomplished by X-ray diffraction, visible melting, and metallographic techniques. Elliott8 obtained a single-phase ZrFe2 X-ray diffraction pattern from an alloy of about 55 pct Fe. This was confirmed in the present study with an alloy of 54.81 pct Fe. However, extra lines (attributable to a or ß zirconium) were found in diffraction patterns of the 47.42 and 49.83 pct Fe alloys. The melting characteristics of these same alloys were studied by suspending 47.42, 49.83, and 54.81 pct

Jan 1, 1960

By E. A. Calnan, B. E. Williams

IN the development of a new treatment for the prediction of deformation textures,&apos;-&apos; it was noted that for no metals are there experimentally determined tension textures with which the predictions may be compared. There is a considerable knowledge of drawing textures and previous workers have been content to consider these as equivalent to tension textures for the purposes of comparison. It is shown, however, in the new treatment that the tension and drawing textures are not necessarily identical, the radial compression exerted by the dies in the drawing operation producing some modification of the tension texture. In particular for the face-centered cubic metals it is predicted that for drawing the final texture should be [1ll] with a spread towards [211] (a more detailed derivation of this texture has been made by Calnan3). This has been amply confirmed by experiment, see Hibbard.6 For the pure tension case, however, the treatment predicts intermediate [1ll] and [loo] textures leading to a [211] end-point, while all previous treatments have predicted the final texture as [1ll] with in some cases an additional [loo] component. Thus evidence that the pure tension end-point is the [211], or at least that [1ll] and [l00] are not the final textures, should provide a valuable test of the new treatment. Accordingly some experiments were made on aluminum. Three aluminum specimens were examined in detail, one of cold-rolled high purity rod (99.99 pct), specimen A, and two of commercial extruded rod of purity 99.4 pct, specimens B and C. The initial annealing treatments were: A, 1½ hr at 400°C; B, 2 hr at 400°C; C, 1½ hr at 650°C. The principal difficulty is that of obtaining sufficient elongation before fracture occurs. This was overcome to some extent by giving a softening heat treatment, 1 hr at 300°C, after each 15 pct of extension. Vickers hardness measurements gave values before and after the softening treatment of about 30 and 28, respectively, in comparison with the initial value of about 19 corresponding to fully annealed material. From recent observations in this laboratory it is concluded that this small recovery corresponds to a polygonization process rather than recrystallization proper and consequently the preferred orientation is unaffected. At the higher extensions, however, some slight necking of the specimens took place and it was necessary to turn them down to a uniform cross-section before

Jan 1, 1953