Search Documents

By R. G. Aspden

Crystals with an (001) [loo] initial orientation of an iron-base alloy containing 3 pct Si were cold rolled with and without the use of constraints. A major difference in the rolling and annealing textures was observed between crystals rolled with and without constraints. These data show that the contribution of constraints at grain boundaries in a poly crystalline sheet should be considered in applying textural data on single crystals to grains in an aggregate. SILICON-iron alloys with a cube texture have been recently developed and their magnetic characteristics reported.1-4 Of interest in the development of this texture were the textural changes of single crystals accompanying rolling and annealing and the influence of constraints at grain boundaries in an aggregate on the behavior of individual grains. The present study was primarily concerned with the effect of constraints during rolling on the textures of 3 pct Si-Fe crystals initially (001)[100]. Barrett and Levenson5 were among the first to observe an influence of constraints at grain boundaries on the textural changes of individual grains during deformation. They tested Taylor's6 theory of plastic deformation of face-centered-cubic metals in which deformation textures were predicted. About one-third of the grains in poly crystalline aluminum did not rotate as predicted. Grains of the same initial orientation were observed to rotate in different directions under the influence of applied stress and anisotropic flow of neighboring grains. Recently, the various inhomogeneities of flow of crystals in an aggregate have been studied7'8 and reviewed.9-11 Barrett and Levenson" rolled (001) [loo] iron single crystals inserted in close-fitting holes in copper to limit lateral flow and to simulate rolling of grains in an aggregate. Deformation bands were formed after a 90 pct reduction in thickness, and the cold-rolling texture contained two components described by rotating the (001)[100] about 35 deg in both directions around the normal of the rolling plane. No annealing textures were reported. Chen and Maddin13 rolled molybdenum single crystals initially (001) [loo]. The crystals were mounted between two hardened silicon-iron plates and 96 pct reduced in thickness by rolling at a low rate of reduction, about 0.0001 in. per pass. The deformation texture had the mean orientation of (001) [loo], and the azimuthal spread included orientations described by rotating (001) [loo] about 35 deg in both directions about the pole of the rolling plane. The presence of deformation bands were not reported by Chen and Maddin or detected in subsequent work of Ujiiye and Maddin.14 The ideal orientation of the annealing texture was (001) [loo]. Recently, Walter and Hibbard 15 reported on the textures of 3 pct Si-Fe alloy crystals initially near (001) [loo]. Each crystal was in an aggregate cut from a columnar ingot. After 66 pct reduction by rolling, the texture consisted of two symmetrical components which had the orientations described by rotating (001) [loo] about 30 deg in both directions about the pole of the rolling plane. Annealing texture was near (001) [loo]. In the above work, the textures of body-centered-cubic crystals were studied after rolling under the influence of constraints. The deformation textures varied from (001) [loo] to near the (001) [110] type and appeared sensitive to the manner in which the crystals were rolled. No textural data were available on the effect of rolling (001) [loo] crystals with and without constraints. The purpose of the present work was to evaluate the influence of constraints during rolling on the textures of 3 pct Si-Fe crystals initially (001) [loo]. Rolling and annealing textures were studied for a) crystals rolled with no constraints at different rates of reduction, and b) crystals rolled with constraints imposed by neighboring grains and by plates between which a crystal was "sandwiched". PROCEDURES AND EXPERIMENTAL TECHNIQUES Data are presented on four crystals which are representative of several crystals studied. The orientation of each crystal prior to rolling was (001) [loo] as determined by the Laue X-ray back-reflection method," i.e., each crystal had an (001) within 3 deg of the rolling plane and [100] within 3 deg of the rolling direction. These crystals were obtained from two iron-base alloys containing 3 pct Si by weight which were prepared by vacuum melting electrolytic iron and a commercial grade of silicon. Crystals 1, 2, and S-1 were cut from a large single crystal grown from the melt of one alloy by the Bridgman technique17 in an apparatus described by

Jan 1, 1960

By J. A. Coll, R. W. Cahn, A. Lawley

WHILE the creep properties of pure face-centered-cubic and close-packed-hexagonal metals have been thoroughly investigated and are well established, body-centered-cubic metals have been studied less extensively. Moreover, very few fundamental studies on the creep of solid solutions, irrespective of crystal structure, have been reported. The present study is concerned with the creep of a series of body-centered-cubic solid solutions. The present position concerning creep of pure metals is, briefly, as follows.1"3 Creep at first takes place at a steadily decreasing rate; this is the stage termed primary or transient creep. Except at the lowest temperatures this is succeeded by a stage of secondary or steady-state creep. At high temperatures and stresses, this may be succeeded by an accelerating stage, termed tertiary creep, with which we shall not here be concerned. There is no well-defined physical model at present for the transient stage; in general terms, transient creep is best regarded simply as a manifestation of work-harden ing. Steady-stage creep can certainly take place by several different mechanisms: the choice of dominant mechanism depends primarily on temperature. We shall here be concerned only with high-temperature steady-state creep, a term usually reserved for creep at absolute temperatures higher than 0.5 Tm, where T, is the melting point. In this range, the activation energy for creep is, for many metals, equal to the activation energy for self-diffusion, and this is generally interpreted in terms of a "climb mechanism.1-4 The creep rate is determined by the speed at which dislocations, impeded by obstacles the nature of which is disputed but which are probably established during transient creep, can climb by means of a diffusion process, until they are able to by-pass the obstacle. In solid solutions, the intrinsic resistance to the slip motion of dislocations may be much larger than in the solvent, to the extent that the motion of dislocations in the glide plane, rather than their escape by climb out of this plane, may become the rate-controlling factor. weertman5 has considered this possibility from a theoretical point of view, and concluded that some form of "viscous slip" is likely to be rate-controlling at comparatively low stresses. The resistance to slip may arise from "atmospheres" of impurities forming around dislocations; a high Peierls force in materials of high cohesion; or some structural peculiarity such as clustering or ordering of solute atoms.= We shall be concerned here with the case of ordering. The only published investigations concerned explicitly with the effect of order on creep refer to creep in ß-brass by Herman and Brown,7 and in Ni-Fe alloys, by Kornilov and panasyuk8 and by Suzuki and Yamamoto.9 Recently, Herman and Brown's paper has been supplemented by a determination of the tensile yield point of ß-brass as a function of temperature.10 Both studies showed a sharp drop in resistance to deformation of ß-brass over a range of a few degrees just above the critical temperature Tc at which order finally disappears. These observations are especially noteworthy, because in ß brass the degree of order diminishes steadzly to zero as the temperature approaches Tc. It is, therefore, the disappearance of the last traces of long-range order which has the largest effect on the resistance of the alloy to plastic deformation. In the Ni/Fe alloys of various compositions, resistance to creep at a given temperature and stress is maximum at the stoichiometric composition, both below Tc, (long-range order), and above T,. (short-range order).' Near Tc, the creep resistance of an ordered alloy is much higher than that of the same alloy in the disordered condition.9 The aim of the present investigation was to study the creep behavior in the neighborhood of Tc, of another system of ordering alloys. The iron-aluminum alloys were considered the most suitable. because: i) The order again diminishes steadily to zero as the temperature approaches Tc; there is no sudden drop in order at Tc, and it therefore is

Jan 1, 1961

By R. H. Frazier, C. H. Lorig, F. W. Boulger

This investigation establishes the effect of ferrite grain size resulting from various heat treatments on the transition temperature of a semikilled steel plate. Different austenitizing temperatures and various cooling rates were used. The ductile-brittle transition temperatures were determined by the Navy tear test and the keyhole Charpy test. THE data presented in this paper deal with quality characteristics of ship-plate material which were investigated in a research project sponsored at Battelle by the Bureau of Ships, Dept. of the Navy. Specifically, the object of this investigation was to establish the effect of ferritic grain size (resulting from various heat treatments) on the so-called transition temperature of ship-plate steel. Transition temperature is not a fixed property of steel. It is derived from a series of static or dynamic tests made at various temperatures and is qualified by specifying the type of test employed as well as the testing criteria. Because in earlier investigations of ship-plate quality1,2 the so-called Navy tear test and standard notched-bar tests (keyhole Charpy) proved to be useful in interpreting instances of brittle behavior of ship plate in service, these tests were used in the investigation reported in this paper. By definition,' in the Navy tear tests the highest temperature at which one or more of four specimens breaks with a brittle fracture (that is, when less than 50 pct of the fracture area has a dull fibrous texture) is termed "transition" temperature. In the Charpy tests, the 12 ft-lb level of energy absorption was used as a criterion indicating the "transition" temperature, although other levels of energy absorption were also used for comparison. Earlier work" on ship-plate steels indicated that the temperature at which ship plate is finished has a very significant effect on its notched-bar properties. Plates rolled in the laboratory, where the finishing temperature can be carefully controlled, showed a 16°F decrease in tear test transition temperature when the finishing temperature was lowered 200°F (from X" to Y°F). The same plates showed a drop of 10°F in the keyhole Charpy transition temperature from the same decrease in finishing temperature. Commercially finished plates' exhibit a similar trend. When the ferrite grain size of the hot-rolled laboratory plates was determined, a close relationship was found between the ferrite grain size and the notched-bar transition temperature." " he indicated relationship between grain size and transition temperature was in agreement with the findings on low carbon steels of Hodge, Manning, and Reichhold' despite the differences in composition of the steels. The cooling rate after rolling varies from one steel plant to another. This variation changes the micro-structure" and appears very likely to affect the notched-bar properties of the steel plates. In the investigation summarized in the present paper, heat treatments simulating finishing practices in the hot rolling of ship plate were used in order to vary the ferritic grain size. It is believed that the indicated relationship between grain size and transition temperatures of the ship-plate material will prove useful in estimating the effect of rolling temperature and of cooling rates from rolling temperatures on the notched-bar properties of semikilled steel plate. Material The semikilled steel plate used in this investigation was a ¾ in. hot-rolled plate from an open hearth heat. Other plates from this heat have been used on many other studies performed for the Ship Structure Committee," "," and the heat has been identified as project steel "A". The chemical composition of the plate1 was 0.25 pct C, 0.49 pct Mn, 0.011 pct P, 0.045 pct S, 0.04 pct Si, and 0.004 pct N.

Jan 1, 1956

By Howard Reiss, C. S. Fuller

A theoretical and experimental study has been made of those interactions between holes and electrons which influence the solubilities of donors and acceptors in semiconductors. The major portion of the work concerns the solubility of lithium in silicon doped to varying degrees with boron. This solubility increases with increasing boron content in a manner predicted by theory and exhibits the expected temperature dependence. A qualitative experiment in germanium is described which demonstrates, in accordance with theory, that doping with a donor decreases the solubility of another donor. SEVERAL authors have discussed the possibility that holes and electrons behave like chemical entities and influence the solubilities of ionized impurities, Wagner was the first to invoke this concept in connection with his studies on nonstoichio-metric oxides. He used it again in explaining the solubility of hydrogen in molten binary alloys. In a theoretical paper,' Reiss drew attention to the fact that solutions of impurities in semiconductors

Jan 1, 1957

By S. F. Ramseyer, E. A. Steigerwald

INFILTRATED structures represent composite materials which are capable of combining high-temperature strength with adequate low-temperature toughness and thermal shock resistance. Although copper- and silver-infiltrated tungsten structures are actually being used in rocket nozzle hardware, adequate understanding of the fracture mechanics of these composite systems is not available. Specifically the relative importance of the strength, ductility, and modulus of the infiltrant in determining composite properties is not known to the extent that optimum composites can be selected. The major portion of experimental effort in the area of composite strength has been devoted to fiber-reinforced systems1 or to systems where a discontinuous phase is imbedded in a relatively ductile matrix.2'3 In the case of high-temperature systems, which are composed of a relatively brittle matrix, such as tungsten or an oxide, a continuous phase exists for the propagation of a crack. The method by which the presence of a conjugate ductile continuous phase influences the gross properties of the composite represents an area which requires further investigation. This technical note presents results which evaluate the effect of infiltrant strength on the strength of the tungsten-base composite. A tungsten matrix and copper-base infiltrant were selected for the initial studies because of the ease of fabrication. Tungsten structures with nominally 20 and 30 pct porosity were evaluated. The porosity was controlled by varying the initial powder size and a ratio of open-to-total porosity greater than 95 pct was obtained by selective sintering cycles. The processing sequence involved hydrostatic pressing followed by a 72-hr presinter in hydrogen at 2000° F and a final sinter at 4000°F for 4 hr in vacuum. The 20 pct porous structure was obtained

Jan 1, 1965

By Craig R. Barrett, Alan J. Ardell, Oleg D. Sherby

It is shown that the apparent activation energy for creep of pure poly crystalline metals increases with increasing temperature in the temperature range 0.5 to 1.0 of the absolute melting temperature. This increase is probably associated with the influence 0-f the elastic modulus on the creep rate. By accounting for the variation of Young&apos;s nodulus with temperature, the true activation energies for creep of pure cadmium and aluminuvl are shown to be equal to the activation energies for self-diffusion in these metals, within experimental error, at all temperatures above 0.5T,. New creep parameters are proposed for cmrelation of steady-state creep rate and time-to-rupture data. These are respectively, where u is the creep stress, E is Young&apos;s rrodulus, i,is the steady-state creep mte, t, is the time -to-rupture, and D is the self-diffusion coefficient [equal to Do exp (-QSd/RT)] . It has been established experimentally1 and theoreticallyZm4 that high-temperature creep of poly-crystalline pure metals is a thermally activated process and may be represented by the general expression where <, is the steady-state creep rate, A is a constant dependent on the internal structure of the material, f is some function of the applied stress (0) and test temperature (T), and D is the self-diffusion coefficient. If D is separated into its temperature-dependent and independent portions, then it is possible to rewrite Eq. [I] as where Qsd is the activation energy for self-diffusion. Assuming a simple Arrhenius-type relationship between creep rate and temperature at a given constant stress, the apparent activation energy for creep, Q,, is given by the expression It is obvious that if is not a function of temperature It has been shown that the steady-state creep rate for pure polycrystalline metals1 can be represented by where S is a constant, L is the grain diameter, E is the isotropic polycrystalline (unrelaxed) elastic modulus, and n is a constant equal to approximately 5 over a wide range of stress. The apparent activation energy for creep calculated from this expression at constant grain size and stress is given by

Jan 1, 1964

By N. J. Grant, K. M. Zwilsky, J. T. Blucher

DISPERSION strengthening has been studied in a number of metal-metal oxide systems. To date those pure metals available as fine particles (less than about 5 p) have received most of the attention whereas solid solution alloys, generally unavailable as fine powders, have not been examined in detail. The present work was undertaken as a preliminary study to evaluate combined effects of solid solution and dispersion strengthening. The technique used was that of dry mixing of elemental powders with the oxide, followed by a diffusion treatment to obtain the solid solution. The average particle size of the powders used was: Ni, 3.2 p (1nco B); Mo, 1.3 p (Fansteel Metallurgical Corp.); and y alumina, 0.027 \i (G. L. Cabot, Inc.). The particle size of the metal powders was determined by Fisher subsieve measurements while the size of the alumina was calculated from a surface area determination. Prior diffusion studies on small compacts pressed from mixtures of nickel and molybdenum powders with and without 7.5 vol pct A1203 indicated that diffusion was complete after sintering for 100 hr at 1800" , or 50 hr at 2250", or 20 hr at 2550° F. The progress of diffusion was followed by microstructural examination and micro-hardness measurements. Two observations made during the diffusion experiments were: 1) That diffusion proceeded faster in the presence of alumina, confirming similar findings by Seith and Loepman on "SAP&apos;&apos;;4 2) That diffusion at temperatures above 1800°F resulted in coarsening of the alumina in agreement with results of other authors reporting on the growth of alumina in nickel above 1800"F. Similar experiments in the Ni-Cr system using 6 and 20 p Cr powders of 0.7 and 0.025 pct 0, respectively, did not result in significant solid solution formation even after long time exposures at 2550° F. It must be concluded that chromium oxide films around individual particles interfere with normal diffusion. A nickel alloy containing 5 wt pct Mo and 7.5 vol pct alumina was fabricated by dry mixing of powders, isostatically compacting at 30,000 psi, diffusing for 120 hr in dry hydrogen at 1800" F, and extruding at 1950"~ with a 30 to 1 reduction of area ratio. The resulting structure, presented in Fig. 1

Jan 1, 1963

By N. Brown, M. Herman

ORDERING&apos;S effect on the creep strength and other plastic properties of metals is unknown at the present time. Sachs and Weerts&apos; attempted to compare the mechanical properties of the ordered and disordered state by comparing a quenched specimen with one annealed for a long time at a low temperature. This experiment is unsatisfactory because it introduces a possible effect from quenching. Barrett&apos; used a hot impact test, but his method was not sufficiently sensitive to indicate any discontinuity in plastic behavior in the neighborhood of the critical temperature. On the theoretical side, Fisher9 as suggested that short range order would strengthen an alloy, but he gives no conclusions as to the effect of long range order. Cottrell" has discussed the interaction between long range order and dislocations, but does not indicate whether slip in a completely ordered alloy without domain boundaries is appreciably more difficult than slip in the disordered state. Because order exists in so many alloy systems, it is most important to prove experimentally whether long range order weakens or strengthens a metal. This investigation used -brass because: 1) it orders

Jan 1, 1957

By H. D. Kessler, R. J. Van Thyne

Phase diagrams of the titanium-rich portion of the ternary systems from 0 to 10 wt pct Al and 0 to 1 wt pct 0, N, and C were determined. Micrographic analysis of annealed high purity arc melted alloys was the principal method of investigation and was supplemented by X-ray diffraction. TITANIUM-ALUMINUM alloys exhibit excellent properties, particularly for elevated temperature use. For this reason, the Materials Laboratory, Wright Air Development Center, sponsored an investigation of the effect of the interstitially soluble contaminants, oxygen! nitrogen, and carbon, on the Ti-A1 system. Using high purity arc melted alloys and micrographic analysis of annealed samples as the chief method of investigation, titanium-rich partial phase diagrams were determined for the ternary systems. Experimental Procedure Materials: The titanium used in the preparation of the alloys was iodide crystal bar (99.9+ pct pure) produced by the New Jersey Zinc Co. and Foote Mineral Co. The aluminum was obtained from the Aluminum Co. of America in the form of sheet. The given analysis was: Si, 0.0006 pct; Fe, 0.0005; Cu, 0.0022; Mg, 0.0003; Ca, <0.0006; Na, <0.0005; and Al, 99.99. High purity titanium dioxide purchased from the National Lead Co. was used in the preparation of the oxygen-bearing alloys. The spectrographic analysis of this material was as follows: SiO,, 0.07 pct; Fe,O,,, 0.002; A1,0,, <0.001; Sb,O,, <0.002; SnO,,, <0.001; Mg, <::0.001; Cb, <0.01; Cu, 0.0004; Pb, 0.002; Mn, <0.00005; W, <0.01; V, <0.002; Cr, <0.002; Ni, <0.001; and Mo, <0.002. Special spectroscopic graphite rod purchased from the National Carbon Co. was used in the preparation of the Ti-A1-C alloys. Alloy Preparation: Alloy ingots weighing 10 grams were melted in a nonconsumable tungsten electrode arc melting furnace using water-cooled copper hearths and a helium atmosphere. The arc was struck on a tungsten stud in the copper block to minimize contamination from the electrode. Details of the techniques have been reported.&apos;, &apos; Each ingot was inverted and remelted a minimum of four times to insure homogeneity, without opening the furnace. Remelting small control ingots of iodide titanium under similar conditions resulted in no measurable hardness increase, indicating contamination-free melting conditions were used. The alloy charges and resultant ingots were weighed to the nearest milligram. Only small weight losses were obtained upon melting, indicating that the actual compositions were very close to the nominal compositions. Check analyses substantiated this. Oxygen and nitrogen were added during ingot preparation as master alloys. An oxygen master alloy containing 25 wt pct 0 was prepared by melting iodide titanium and pressed titanium dioxide (40 pct 0) powder. The Ti-25 pct 0 alloy is more easily handled during weighing and charging than the pressed TiO, powder. Chemical analysis indicated that titanium-nitride received from an outside source contained large amounts of impurities (2.7 pct Ca). Therefore, a master alloy containing approximately 12 pct N was prepared by melting nitrided sponge titanium. As the sponge melted with difficulty, the alloy was diluted by addition of titanium to lower the melting point. The chemical analysis of the final alloy was 6.69 pct N. Both master alloys are friable and were used as —8 +16 mesh lumps resulting from crushing the ingots. NIelting the Ti-A1-0 and Ti-A1-N compositions five times produced homogeneous ingots. The preparation of homogeneous carbon-bearing alloys caused considerable difficulty. Alloys containing less than 1 pct C were prepared using spectrographic graphite rod, 1/8 in. diameter by 1/8 in. long. However, the graphite did not dissolve even with long melting times and many remelts. The ?/s in. pieces of graphite were used rather than powder because the low density powder is troublesome in arc melting.

Jan 1, 1955

Using 5-p Ni powder and 0.018 ,u A1203, oxide dispersion strengthened nickel alloys were prepared by mechanical mixing of powders, followed by compaction, sintering and extrusion. Processing variables such as cooling of the powder during mixing, electrostatic discharging, mixing time, amount of oxide, and so forth, were studied to determine the effects on room-temperature tensile and high-temperature creep-rupture properties and on the reproducibility of alloys. MECHANICAL mixing of metal and metal oxide powders provides one of the simplest and most inexpensive methods for preparing dispersion strengthened metal-metal oxide alloys;" however, because of large differences in specific gravity, powder particle diameters and other variables, difficulties have been encountered in reproducing alloys and alloy properties. Using 5-p Ni powder and 0.018 p A1203, the following variables were investigated: a) Blending techniques b) Blending time c) Volume fraction of oxide for the selected pow- ders d) Sintering of compacts before extrusion Cooling of Powders During Blending— Cremens and Grant had indicated that dry ball milling of the powder mixture gave superior results over other procedures. When ultra-fine metal and oxide powders became available and comminution was unnecessary or offered little gain, the use of dry mixing in a Waring Blendor gave optimum results.&apos; In the current study, observations of the powder mixtures indicated that considerable heat was generated due to the high speed of the Waring Blendor (15,000 rpm). This heating appeared to produce some degree of clustering and pelletizing. To minimize such agglomeration, a Pyrex cooling coil was installed in the mixing vessel. A double coil, water cooled, proved to be quite satisfactory, providing a fair degree of cooling along with good erosion resistance. Discharge of Electrostatic Charge—Electron-microscopy showed that agglomeration was minimized by the cooling procedure but was not entirely eliminated. It appeared that some of the ag- glomeration had to be explained on the basis of an electrostatic attraction due to the high-speed blending operation. These charges had the effect of promoting the growth of alumina clusters. At the end of the blending procedure such clusters had an effective size which was as much as 50 times that of the individual powder particles and were very tightly bunched. Several methods were utilized to try to discharge the electrostatic forces to minimize the clustering. One successful method, utilized in alloy 17, involved continuous exposure during blending to a radium source of 50 millicuries at a distance of 1.5 ft from the container. A number of other methods were noted to work equally well. Fig. 1 shows the more open oxide structure which results from such a treatment, permitting the matrix metal to penetrate into the cluster more effectively. The combination of powder cooling and discharging led to noticeably improved structures. Fig. 2 shows a cross and a longitudinal section in alloy M-17, one of the best alloys, illustrating the marked decrease

Jan 1, 1961

By R. H. Frazier, C. H. Lorig, F. W. Boulger

THERE are both advantages and disadvantages in using semikilled steels in place of killed steels. One advantage of semikilled steels is they provide a higher ingot-to-product yield. This is especially important to shipbuilders in the time of national emergency. By using semikilled steel for hull plates, a greater number of ships can be built from the same ingot tonnage. Consequently, if semikilled steel plates are adequate for the service, the advantage of the higher product yield is of considerable importance. The performance of hull plates is closely associated with the ductile-to-brittle transition temperature, and this, in turn, is strongly dependent on the composition of the steel. A low transition temperature is desirable because it indicates that the steel is less likely to fail at low ambient temperatures. Killed steels are known to have lower transition temperatures than semikilled steels. It is believed that the better qualities of killed steels in this respect are due mainly to the low oxygen contents of the steel. The principal deoxidizers, aluminum, silicon, and manganese, lower the oxygen content. Fundamental studies1-0 have shown that the oxygen content remaining after the addition of one of these three elements is influenced by the residual amounts of the other two present. In the current study, therefore, various amounts of silicon and aluminum were added to steels containing different manganese contents for the purpose of studying the influence of silicon and aluminum on the notched-bar properties of hot-rolled steels. Eleven types of steels were studied. The temperature at which the plates were finish-rolled was care- fully controlled at 1850°F. All plates were rolled to ¾-in. thickness, and tested in the as-rolled condition. The total number of steels prepared in the laboratory for this study was 95. The charge consisting of ingot iron and ferrosilicon equivalent to 0.10 pct Si was melted in a 200-lb induction furnace under an atmosphere of argon to insure low, uniform nitrogen contents. After the charge was melted and the desired temperature was obtained, the melt was partly deoxidized with either silicomanganese or aluminum. Aluminum was used for this purpose in only those steels with very low silicon contents, where the finished steel was to contain some aluminum. This initial deoxidizing addition was made to obtain consistent recoveries of subsequent additions of ferro-manganese, ferrosilicon, and aluminum. Carbon, in the form of graphite, was added, either just prior to tap or to the final aluminum addition. The entire heat of 200 lb was poured directly into a 6x6-in. big-end-up mold. The ingots of semikilled steel were capped with a steel plate. The killed steels, on the other hand, were poured with a hot-top containing 14 pct of the total volume of the ingot. The ingots were processed by heating to 2250°F, followed by forging to slabs 1¾ in. thick and 6 in. wide. After reheating to 2250°F, the slabs were rolled to 0.9-in. gage, using reductions of approximately 1/6 in. per pass. The 0.9-in. thick plates were immediately recharged in a furnace held at 1850°F. After 30 min in the furnace at 1850°F, the plates were rolled to ¾ in. in one pass. Following the final pass, the plates were stacked on edge on a brick floor, with a brick separating one from another, where they were allowed to cool in air. Drillings for chemical analysis were taken from the plates at locations corresponding to the top and bottom of each ingot. Carbon, manganese, silicon, phosphorus, sulfur, and nitrogen contents of each sample were determined. The analysis of each steel was carefully controlled so that the contents of

Jan 1, 1957

By F. Bonaccorso, G. Venturello, C. Antonione

A study of the effect of small amounts of interstitial impurities on recovery and re crystallization in high-purity iron (99.995 pct) has been undertaken. This paper gives results on the effect of carbon, introduced in small-dosed amounts @om 0.0005 to 0.0086 wt pct) by heating iron specimens of high purity m a static atmosphere of CO + ,. The materials prepared in this way, cold-worked 80 pct and subjected to a series of isochronal and isothermal annealings, were submitted to examinations by X-rays, micrographs, and hardness tests. It was observed that effect of carbon is remarkable in the sense of blocking recovery of mechanical properties up to the temperature at which re crystallization begins. On the contrary, carbon has a negligible effect on primary re crystallization temperature, when compared with the known effect of substitutional impurities. This is in agreement with the high mobility of interstitials. In effect, only a slight decrease, -20 pct, of the grain-boundary motion rate was noted, due to the interaction between the grain boundary and the carbon atoms. On the other hand, in the samples in which the carbon content is above the solubility limit at the temperature at which re crystallization occurs, a slight increase of nucleation frequency is noted due to the presence of precipitated carbides. ThE effect of purity on recovery and recrystalli-zation phenomena has been known for a long time; however, recently, new attention has been given to the problem since new methods for obtaining metals with extremely low impurity contents have become available. Most of this research work essentially concerns the effects of impurities which cause precipitates or give rise to substitutional solid solutions. The works of Bolling and winegard1 and Aust and utter&apos; on lead, and Vandermeer and orddon&apos; on aluminum, 01sen4 on nickel, and Abrahamson and Blakeney on iron should in particular be referred to. On the effect of this type of impurities a quantitative theory has been formulated by Detert and Lucke6 and has lately been discussed critically by Cahn7 and Gordon and vandermeer.&apos; Interstitial solid solutions in iron have not as yet been studied. As the study of the effect of interstitials is of great interest both from a theoretical and practical standpoint, it was deemed useful to examine the effects of carbon, nitrogen, and boron on recovery and primary recrystallization of iron. There already is some work by Chaudron et al.,1-" on the effect of interstitials on iron; their work, however, mainly concerns secondary recrystallization. The present paper refers in particular to the effect of carbon. EXPERIMENTAL PART Preparation of Materials. The pure iron used for this research was obtained from FeCIS recrystal-lized and purified by extraction with isopropylic ether. From the ferric chloride purified in this manner, hydroxide was precipitated with a solution of very pure ammonia, and, by calcination in pure sintered alumina crucibles, oxide was obtained. Reduction of the oxide to iron sponge was performed in sintered alumina tubes with very pure hydrogen at 650°C; at the end of the operation temperature was increased to 900°C. Specimens for the experiments were obtained by sintering the sponge at 1480°C in pure Hz after a pre sinter ing treatment at 900° C. It is important to note that the treatment at 1480°C in Ha produces a further purification from more volatile elements such as zinc, cadmium, arsenic, lead, and tin. Details on the preparation and characteristics of this type of very pure iron are given in a previous work.&apos;&apos; Only the complete analysis performed by neutron-activation methodsz3 is given here, Table I. Some of the specimens prepared in this way were carburized in the 0 region with very low amounts of carbon by treating them at 700°C in a static atmosphere of Ha containing a definite amount of CO. The set-up used is described in Fig. 1. A gas-tight quartz tube containing the specimen to be carburized and an internal friction control specimen, after being evacuated, was filled with Hz

Jan 1, 1963

By G. Venturello, C. Antonione, G. Della Gatta

Results from work on the effect of inferstitials on recovery and recrystallization of&apos; very pure iron (99.995 pet) doped with nilrogen up to 400 ppm are reported. Nitrided specimens were obtained by heating the iron in a static atmosphere of NH3 + H2. The samples were cold-rolled 80 pet, subjected to a series of isochronal and isothermal anneals, and submitted to examination by X-rays, micrographs, and hardness tests. Small additions of nitrogen show a strong effect in reducing recovery of&apos; the mechanical properties of high-purity iron. At the temperatures of. the experiments, this effect proved greater than in the case of carbon. At 400°C pure iron recovers more than 50 pet of the total hardness increase, carburized iron vecovers 25 pet, and nitrided iron only 10 pet. On the other hand. the addition of nitrogen has, similarly to carbon, a very small effect on recrystallization; the effect is, however, slightly higher than that of carbon. When the concentration Of nitrogen is above the solubility limit in a iron at the temperattue of the experiments, an increase in the frequency of nu -cleation is also observed. THE object of the present work is to improve knowledge on the effect of interstitials both on recovery and on primary recrystallization of pure iron. In fact. at present there are no available data on the effect of nitrogen on high-purity iron. The only work which at present can be somewhat related to this problem is a work of Leak et al.1 in which grain boundary internal friction at high temperature in the presence of increasing amounts of nitrogen is studied by a torsion pendulum. The present work is a continuation of a previous one2 on the effects of carbon. EXPERIMENTAL PART Preparation of the Material. Pure iron was prepared following the same methods used in the pre- vious work2 and was nitrided using controlled quantities of ammonia in an apparatus similar to that used for carburizing. The apparatus consists essentially of a gas-tight quartz tube containing the specimens. The tube, maintained at constant pressure by means of a mercury seal, is placed in a resistance furnace. For nitriding, the NH3 + H2 atmosphere with a suitable concentration of NH3 was introduced into the tube, which had been previously carefully evacuated and degassed by heating at 600°C. The hydrogen used was carefully purified by passing it through a palladium filter. The ammonia required was prepared with the following reaction: CaO + 2NH4CI —CaCl2 + H2O + 2NH3 by heating the mixture of CaO and NH4C1 in a glass flask and then collecting the ammonia in a graduated Hempel burette. For each nitriding program a given amount of NH3 prepared by this method was introduced together with the H2 into the tube previously evacuated. Nitriding of the sample was then performed at 570°C for 48 hr. After this, to ensure a homogeneous distribution of nitrogen, the samples were further heated for 72 hr at 800°C. With this method which uses a static nitriding atmosphere, carefully controlled conditions of purity are obtained. Contrarily, with the conventional continuous-flow methods, using large quantities of circulating gas, there is a greater risk of introducing impurities into the samples. Furthermore, the required nitrogen concentration in the specimen is easily predetermined and obtained. A plot of the relation observed between the initial concentration of NH3 in the gas and the quantity of nitrogen introduced into the iron samples is given in Fig. 1. The data refer to samples of 1.2-mm thickness and to the nitriding conditions previously described. Furthermore, as a comparison, the data relative to two 0.5-mm-thick samples are reported. The presence of a reservoir in the cold zone of the reaction bulb made possible the gradual dissociation of ammonia on the sample in the hot zone. Internal-friction methods were used to determine the content of nitrogen dissolved in the iron samples. Some analyses were also carried out with chemical methods. The following table, Table I, shows a comparison of data obtained with chemical and internal-friction methods. The correspondence between chemical methods and internal-friction

Jan 1, 1964

By Craig R. Barrett, Oleg D. Sherby

The creep characteristics of four pure metals with widely Varying stacking-fault energies (silver, copper, nickel, and aluminum) were evaluated above 0.5Tm. Creep tests were performed under conditions of constant atomic diffusivity and constant stress over the elaslic modulus. The sleady-state creep rate, Es, was found to he a funclion of the THE most common empirical representation of the steady-state creep rate, Es, at high temperatures and intermediate stresses is of the form where a is the applied stress, E is an elastic constant, A and n are constants (n is typically stacking-fault energ, y, such that Es is proportional to y3,5. In addition, it was uncovered that the primary creep strain and the strain to fracture increased with increasing y, and that the ratio of initial to steady-state creep rate decreased with increasing y. about 5), Q is the activation energy for creep (usually equal to that for self-diffusion), and kT has its usual meaning. sherbyl and McLean and ale&apos; have used this expression to correlate creep data for a number of pure metals. An interesting aspect of Eq. [I] is the absence of any dependence on the stacking-fault energy. While most creep data seem to obey the stress and temperature dependence predicted by Eq. [I], when data for several metals are put on a master plot they do not fall on a common line but form a band. The width of this band corresponds to a variation in Es of 102 to l03. sherbyl attempted to explain this band by assuming that a grain-size effect was present which led to the observed variation. On the other hand, Felt-

Jan 1, 1965

By D. J. McAdam

In a series of papers the author and associates have discussed the influence of temperature on the tensile properties of metals.11-18 These papers present much information about the influence of temperature and the stress system on the conventional indices of mechanical properties, with special attention to the fracture stress. A recent study of the data, however, has revealed much additional information about the influence of temperature on the fundamental factors involved in the flow of metals. The present paper presents results of this study. Attention will be confined almost entirely to results derived from tension tests of unnotched cylindrical specimens at strain rates a little slower than those used in ordinary tension tests. According to a concept first presented by Ludwik and elaborated in recent papers by others,8,9,22,23 the mechanical state of a metal depends on the total plastic strain, but not on the temperature during straining, provided that the only structural changes are those essential to plastic deformation. In the summer of 1948, however, the author made the previously mentioned study of results of a general investigation by the author and associates and reached the conclusion that the mechanical state depends not only on the total strain, but also on the temperature during the straining. A number of diagrams were then prepared. These conclusions were presented without diagrams in a discussion last October of a paper by Dorn, Goldberg and Tietz.2 The metals used in the investigation on which this paper is based were Monel and oxygen-free copper. The Monel was supplied by the International Nickel Co. through the courtesy of Dr. W. A. Mudge. The copper was supplied by the Scomet Engineering Co. through the courtesy of Dr. Sidney Rolle. The data to be presented are based on results of tests at temperatures ranging between 165 and — 188°C. Description of the apparatus and methods of test are given in previous papers.1011&apos;1"2 The present paper is the first part of the general discussion of the influence to temperature on the stress-strain-energy relationship for metals. The next paper will deal with metals that are subject to structural changes other than those induced solely by plastic deformation. Influence of Temperature and Plastic Strain on the Flow Stress of Monel and Copper For a study of the influence of temperature on the stress-strain relationship, flow-stress curves obtained with annealed metals at various temperatures will be compared with curves obtained with the same metals after cold drawing or cold rolling at room temperature. Diagrams thus obtained with Monel and copper are shown in Fig 1 to 8. Fig 1 to 7 show the variation of the flow stress with temperature and plastic strain; Fig 8 is a diagram of a different type, derived from Fig 4 to 7. In Fig 1 to 7 strain is expressed in terms of A0/A, in which A0, and A represent the initial and current areas of cross-section. Since values of Ao/A are represented on a logarithmic scale, abscissas are proportional to true strains; moreover, the true strains representing prior plastic deformation and those representing subsequent strain during a tension test are directly additive. Fig 1 shows flow-stress curves obtained with annealed Monel. Five of the curves are based on results of tension tests. Between yield and the maximum load, the flow was under longitudinal tensile stress; between the maximum load and fracture, the local contraction induced transverse radial tensile stress. The portions of curves designated F, therefore, represent flow with increasing radial stress ratio, the ratio of the transverse stress S3 to the longitudinal stress Si. Curve Fo is based on the ultimate stresses of specimens taken from bars that had been cold drawn various amounts.17 Since the tensile stress at the maximum load is unidirectional, curve Fo represents the course that a flow-stress curve would take if the stress during an entire tension test could be kept unidirectional. The flow-stress curve F obtained at room temperature (Fig 1) has been established accurately by numerous measurements of the diameter of the specimen during the extension from yield to fracture.17 At the time of the experiments, however, no apparatus was available for measuring the diameter during tension tests at low temperatures. Nevertheless, curves have been established to represent with sufficient accuracy the flow at low temperatures. Each flow-stress curve must be tangent to a curve U, which starts at a point representing the ultimate stress of annealed metal. Since the ultimate stress is based on the area of

Jan 1, 1950

By W. A. Backofen, G. Y. Chin, W. F. Hosford

The effect of machine stiffness on discontinuous flow and fracture of the 2024 aluminum alloy was studied in tension at 4.2OK. An increase of machine stiffness was found to decrease the amount of elongation and drop in load during discontinuous flow, thereby postponing fracture to larger strains and higher stresses. The possibility of utilizing stiffened tools in deformation processing to suppress shear fracture originating from unstable flow was indicated. The problem of nucleating discontinuous flow and the role of the effective mass of the system in discontinuous flow were also considered. AT low temperatures the plastic flow of metals is often discontinuous, with sudden load drops and elongations.1,3 Basinski1,4 has presented strong evidence that discontinuous flow, at least in aluminum alloys, occurs under nearly adiabatic conditions. During testing the load may drop suddenly and flow become localized when the thermal softening, due to heat generated in plastic straining, is greater than the strain and strain-rate hardening. This instability criterion is more easily satisfied at low temperatures because 1) the volume specific heat is reduced so that relatively large temperature increases are possible in straining, and 2) the flow stress is relatively temperature-dependent. The important role of adiabatic shear in ductile fracture processes has been emphasized,5-1 and consideration has already been given to the influences of thermal and mechanical properties on the tendency of a material to undergo adiabatic shear.17677 By focusing attention on how the mechanical loading system influences low-temperature discontinuous flow, additional insight into adiabatic shear and its effect on fracture may be gained. EXPERIMENTAL PROCEDURE Because of its low thermal conductivity, the 2024 aluminum alloy exhibits a highly consistent discon- tinuous-flow behavior at 4.2°K and was therefore chosen as the material for study. Machined specimens of 0.113 in. diam and 1.125 in. gage length were solution heat-treated at 490°C for 3 hr, quenched into cold water, and immediately immersed in liquid nitrogen until just before testing. Testing was done at 4.2°K by immersion in liquid helium at a crosshead drive rate of 0.03 in. per min. As normally used (hard-machine basis), the spring constant of the testing machine was k = 25,000 lb per in. By inserting beam springs in series with the specimen, this value could be lowered by a factor of about 100. Details can be found elsewhere.? As a result of variable machine stiffness, the actual strain rate ranged from about 3 x 10 5 to 3 x 10-4 per sec from one test to another, as well as within any one test. However, preliminary tests had established that the tensile curves were not altered significantly by this strain-rate variation. Fig. 1 shows a typical load vs plastic-elongation curve for a solution heat-treated 2024 aluminum alloy specimen pulled in the standard hard machine (k = 25,000 lb per in.) at 4.2"K. The elastic extension has been subtracted. Plastic flow proceeded smoothly from yielding at approximately 22,000 psi (load = 220 lb) to a strain of about 4 pct at which point the flow became discontinuous. The magnitude of the load drops as well as the plastic elongation per drop increased with increasing strain until the specimen finally broke abruptly. The load-elongation behavior of a sample tested with a relatively soft machine under otherwise identical conditions is given in Fig. 2. In general, there

Jan 1, 1964

By I. R. Kramer

The stress associated with the high-dislocation layer at the surface of deformed aluminum crystals was measured by progressively polishing the specimen and determining the change in the initial flow stress when the specimen was reloaded. This surface stress increased linearly with strain in the Stage II and Stage III region. The depth to which the high-dislocation layer extends was found to be 0.0025 in. The influence of the surface layer on Stage I is discussed and it is shown that Stage I ends when, on the secondary slip system, the difference between the applied stress and the opposing stress due to the surface layer is equal to the critical resolved shear stress. In previous papers&apos;-3 it was shown that the surface exerts a pronounced effect on the plastic-flow characteristics of metals. For fcc metals it was possible to increase the extent and decrease the slope of Stages I and II and decrease the work-hardening coefficient of Stage II by removing the surface of the specimen continuously during the deformation process.2,3 More recently,L it was shown that the activation energy for plastic deformation and the activated volume were also influenced by the surface. These changes were related to the existence of a high concentration of dislocations in the region near the surface of the deformed specimen and it was concluded&apos; that the effective stress, T, acting on a dislocation was T = Ta-Ti-Ts [1] where 7, is the applied shear stress, Tj is the internal stress, and TS is the stress associated with the surface region containing the high concentration of dislocations. From Eq. [I] it is seen that the effective stress, 7, acting on a dislocation is a function of 7,. Therefore 7, becomes important in any description of the work-hardened state. In this paper the value of 7, as a function of strain and its variation with depth are reported for aluminum single crystals. In particular, it will be shown that the end of Stage I occurs when the net stress, 7, on the secondary slip system is equal to the critical resolved shear stress. To measure Ts, single crystals of aluminum were deformed in tension to various strains, whereupon the load was removed and a known amount of metal was removed by electrolytic polishing. The differ- ence between the final flow stress before the specimen was unloaded and the initial flow stress upon reloading is designated as ?Tp and is the decrease in the stress due to the removal of the surface layer in whole or in part. The value for Tp is taken equal to -Ts. EXPERIMENT PROCEDURE The details of the tensile apparatus, method of electrolytic polishing, and crystal preparation were the same as those used previously,1"3 The single crystals were 1/8 by 1/8 in. in cross section with a 3-in. gage length. The initial purity of the aluminum was 99.997 pet. The specimens were held in vacuo at temperatures 50°C below their melting points for 16 hr and furnace-cooled. Just prior to the application of the tensile stress the specimens were electrolytically polished to remove 0.004 in. from the thickness. This latter operation was conducted after the specimen was placed in the tensile apparatus. The tensile tests were conducted at a strain rate, i, of 10"5 sec-&apos; and a temperature of 3°C. The aluminum crystals used for the determination of 7, are designated A1-3-12 and A1-116. The orientation of the various crystals used throughout the investigation is shown in Fig. 1. The ?Tp values for specimens A1-3-12 as a function of Ax were determined mainly at four strain levels, i.e., ? = 0.0217, 0.0381, 0.0593, and 0.075, where Ax is one half of the total reduction of the thickness after polishing and ? is the re-

Jan 1, 1965

By H. Yoshida, B. G. Liebmann, R. E. Green

In recent years considerable work has been undertaken in order to gain an understanding of the mechanisms responsible for the generation of recrystal- lization textures in face-centered-cubic metals. Two theories have been proposed, that of oriented growth1 and that of oriented nucleation,&apos; and several attempts have been made to check these theories directly by recrystallizing deformed single crystals.3-5 Two groups, Graham-Cahn and Liebmann-Liicke-Masing, studied the orientation of recrystallized grains and their rate of growth, both using strained aluminum single crystals of commercial purity (Graham et al., 99.6 pct, Liebmann et al., 99.8 pct). Surprisingly, the results obtained by the two groups were completely

Jan 1, 1960

By H. I. Aaronson

Isothermally formed plates of proeutectoid a, lengthen at approximately the rates predicted by the Zener-Hillert equation, indicating that their lengthening kinetics are controlled by the volume diffusion of chromium in the ß matrix. Solution annealing treatments in the vicinity of the transus introduce a second mode of transformation, in which the lengthening rate is at least 1.8 x 104 faster than predicted by this equation. Little or no volume diffusion appears to accompany the latter transformation. The Presence of oxygen is evidently a Prerequisite for the occurrence of this reaction. X HE effects of thermal history prior to the initiation of transformations which proceed by nucleation and diffusional growth are currently evoking considerable interest. The rate of nucleation (but not the rates of growth) of pearlitel and of bainite,2 and the over-all rates of aging reactions in Al-cu3 and Al-si4 alloys have been shown to be appreciably dependent upon thermal history in the solid-solution region"&apos; or in the two-phase region prior to the onset of pre~ipitation.3,4 In none of these reactions, however, was the transformation mechanism changed by variations in the temperature-time path used to reach the reaction temperature. Preliminary experiments reported by M. K. McQuillan5,8 and a systematic investigation by Farrar and Margolin7 have disclosed that the transformation behavior of hypoeutectoid Ti-Cr alloys is considerably more sensitive to thermal history. Qualitative evidence strongly suggests that not only the rate of nucleation but also the rate of growth and even the mechanism of the ß — a reaction can undergo remarkable changes when a solution annealing treatment in the vicinity of the ß/a +ß, or transus temperature, is interposed between a high-temperature solution anneal (conventionallq at 1000°C) and the isothermal reaction treatment. The present investigation was undertaken in an attempt to ascertain the nature and origin of these effects. Study of the changes in the kinetics and morphology of the ß - a, reaction produced by varialtions in thermal history was the primary means employed for this purpose. EXPERIMENTAL PROCEDURE The compositions of the alloys used in this in~esti~ation are given in Table I. These alloys were homogenized for 5 days at 1050° C in evacuated (2 x 10 -5 mm of Hg), zirconium-gettered fused quartz capsules. The capsules themselves were enclosed in a porcelain chamber evacuated with a mechanical pump during the homogenization anneals. Upon completion of homogenization, the alloys were cooled to room temperature and then reheated to 550°C for 3 1/2 days in order to transform the alloys to a finely divided mixture of a and TiCr2, and thus provide an approximately constant initial mi-crostructure. Individual specimens were sealed in evacuated and internally gettered Vycor capsules and heat treated as previously described.8,9 EXPERIMENTAL RESULTS Ti-10.64 Pet Cr. This investigation was largely performed on the 0.64 pet Cr alloy. The "base"

Jan 1, 1962

By W. Rostoker, H. Nichols

The embrittlement by mercury of aluminum alloys in various states of anneal, cold work, and aging has been studied. It is shown that single phase and non-precipitation hardened structures irrespective of de,pee of prior cold work demonstrate some small measure of yielding before fracture occurs. Sub-yield-stress failure is confined to the aged state, and embrittlement is accentuated by small plastic prestrains. With large plastic pyestrains, embrittle~nent is progressively reduced. In previous work&apos; it was shown that the propensity of commercial aluminum alloys for embrittlement when wetted with mercury seems to be related primarily to the intrinsic strength in the normal un-wetted condition. The data from a large number of commercial alloys in various states of anneal, cold work, and/or aging gave a generalized relationship. At low strength levels, the wetted fracture strength increases proportionately to the increase in tensile strength; but above 65,000 psi normal ultimate strength, the trend is abruptly reversed, and the wetted fracture stress decreases proportionately to the increase in tensile strength. This paper will demonstrate that the simple character of this relationship between normal tensile strength and wetted fracture strength is fortuitous. It will be shown that structure and thermal-mechanical history are clearly relevant factors. The term brittle fracture has been used to connote the geometry of the fracture surface (transverse vs shear plane) or the negligible extent of preceding plastic strain. At its maximum effectiveness, liquid metal embrittlement can satisfy both criteria—fracture transverse to the axis of tension and without observable plastic strain. In this paper, brittle fracture will signify failure at stresses below the engi-

Jan 1, 1962