By J. P. Hirth, G. M. Pound

The flux of evaporation J from {loo) , {111), and (110) planes of silver single crystals and from poly crystalline specimens was measured at 744°C under a high vacuum using a time average weight loss method. The evaporation coefficient a was computed from the measured flux and vapor pressure data through the relationship J = aPe/21rmkT. The evaporation coefficients for the close packed planes and the poly crystalline specimens were found to be about 0.4 providing tentative confirmation of the theoretical limiting law for evaporation of metal crystals, a = 73(P/Pe) + % . The (110) planes faceted to form (111) planes, resulting in a greater evaporating area and larger a . The evaporation morphology of the plane surfaces and the surfaces of spherical single crystals is described in some detail. RECENTLY a detailed theoretical analysis of the mechanism and kinetics of metal crystal evaporation was made.1'2 A mechanism for vaporization involving the recession of monatomic ledges across a metal surface was deduced, and evaporation rate equations were derived by considering the dynamics of these ledges. In most metals, the process of evaporation is one of dissociation of atoms from ledges, surface diffusion, and desorption. The gross vaporization rate is controlled by the surface diffusion and desorption rates. It was shown that the monatomic ledges, under the action of surface diffusion gradients, tend to assume a terminal velocity and spacing. Further, it was shown that crystal edges and grain boundaries are a ready source for monatomic ledges. In the case of evaporation of large, perfect crystals with clean, low-index surfaces, the kinetic treatment1 leads to a limiting law for crystal evaporation: where J is the gross flux of vaporization, a is the evaporation coefficient, Pe the equilibrium vapor pressure, m the atomic mass, k Boltzmann's constant, T the absolute temperature, and P the actual pressure of vapor over the crystal surface. Imperfections such as grain boundaries, pores, cracks, and macroscopic steps should have the effect of causing positive departures from this limiting law. Such an imperfection is a source for monatomic ledges, which, near their origin, are closely spaced and thus give rise to higher evaporation rates there. However, under many experimental conditions,' this effect should be negligible due to the relatively low concentration of imperfections. In general, a more important cause of positive departure should be screw dislocations, and the effect of these has been considered in some detai1.2,3 Monatomic ledges emanate from points where the surface is intersected by a dislocation with a screw component normal to the surface. The dynamics of ledges arising from a screw dislocation are similar to those of ledges arising from a crystal edge. There is a perturbed region near the origin where the monatomic ledges are, under certain experimental conditions, closely spaced and the

Jan 1, 1960

By John R. Gould

A mathematical treatment of multiple-pass floating-zone refining of semiconductors, including the evaporation of solutes from the melt at reduced pressure, is presented. Vapor pressures and evaporation rate constants for phosphorus, arsenic, and antimony in germanium have been determined from floating-zone experiments conducted at 10 mm Hg. Rate sensi-tivity of arsenic in germanium has been examined over the range of 1 to 10 in. per hr growth rate. The equilibrium value of the segregation coefficient of arsenic in germanium, as determined by an extrapolation of these data, was found to be 0.09. PFANN has treated the segregation of nonvolatile solutes in the zone-melting process, Bradshaw and Mlavsky2 considered the evaporation of solutes in a vacuum during the growth of crystals by pulling from the melt, and van den Boomgaard3 has shown that it is possible to bring a volatile impurity element homogeneously into an ingot by means of zone-melting under a constant pressure of that element. This paper is concerned with the volatilization of solutes during zone - melting in a vacuum. The mathematical analysis by Lord4 of multiple-pass zone melting is extended to include evaporation of solutes. A method is presented in which evaluations of vapor pressures, evaporation rate constants, and distribution coefficients may be derived from the variation of solute concentration in the floating-zone refining of germanium at 105 mm Hg. EXPERIMENTAL Ingots of zone refined germanium, approximately 1/4 in. in diam and 10 to 12 in. in length, were subjected to several floating-zone passes at 105 mm Hg in order to provide intrinsic material for these studies. These ingots were then seeded in a [Ill] direction and solid-doped to a constant impurity concentration of approximately 1015 atoms per cmS in a forming gas ambient (10 pct H - 90 pct A) at 1/2 atm gage. The resulting crystals were subjected to repeated floating-zone passes at 105 mm Hg and a concentration profile along the length made after termination of each pass. Concentrations were determined from four-point probe resistivity measurements, and proper precautions were taken to prevent contamination during handling. A constant zone length, crystal cross section, and growth rate were maintained during zoning. A stationary coil and moving crystal system were employed for floating-zone growth with neither the section of crystal above nor below the melt rotated.

Jan 1, 1962

By W. H. Herrnstein, J. B. Clark, E. C. Utley, A. J. McEvily

The ratio of the endurance limit (10' cycles) to tensile strength of age-hardened aluminum alloys is approximately 0.3, whereas the ratio for annealed alloys is about 0.5. The lower value for the age-hardened alloys has been associated with the instability of coherent precipitate during cyclic loading, but it has not been definitely established whether this instability is due to overaging or reversion during cyclic loading. The results of the present investigatzon support the reversion viewpoint. In this work specimem of 2024-T4 aluminum alloy were aged for 16 hr at 150°C after cycling for 10 pct of the life at 25.000 psi. These specimens were then tested to failure and exhibzted a marked increase in fatigue life. It is proposed that during the early stages of fatigue in this alloy dislocations cut through the coherent precipitate and bring about the reversion of the precipitate. Subsequent aging at 150ºC induces reprecipitation in the precipitate-free zones so that the weakened regions are strengthened and the fatigue life is extended. It Is recognized that the fatigue strengths of precipitation hardened aluminum alloys are unusually low relative to their tensile strength.'-= This feature is illustrated in Fig. 1 where it can be seen that age-hardened alloys have lower fatigue ratios (the ratio of the fatigue strength to the tensile strength) than those in the annealed or cold worked state. Further, as shown in Fig. 2, the more an alloy is dependent upon precipitation hardening for its total strength, the lower is the ratio of the fatigue strength to the tensile strength. This state of affairs has been associated with an instability of the metastable metallurgical structure of precipitation hardened aluminum alloys during cyclic loading. Evidence2 in support of this view is that the fatigue ratio increases in these alloys as the test temperature is lowered, thereby indicating that thermo-mechanical instability, rather than some other factor such as a non-uniform distribution of precipitate, is the factor responsible for the low fatigue ratio at room temperature. Two mutually exclusive proposals have been ad- vanced to account for this instability. Hanstock has proposed that overaging takes place during cyclic loading, and in support of this view, Broom et a1.2 have indicated that an overaging process might be promoted by the large numbers of vacancies which are created during cyclic loading. The creation of vacancies by radiation4 has been shown to lead to rapid overaging. Hanstockl obtained visual evidence of overaging in an aluminum alloy after cyclic loading, but in this instance it has been pointed ou? that because of the high frequency used (60,000 cpm) the observed effect may have been due to normal high temperature precipitation around energy dissipating cracks. Efforts to discern visual evidence of overaging in this alloy at lower test frequencies were not successful.3 The alternative postulate3 is that reversion takes place during cyclic loading and leads to localized soft spots at which fatigue cracks are readily initiated. Evidence for this process has recently been provided by Polmear and Bainbridge5 who demonstrated metallographically that regions depleted of precipitate were created during cyclic loading of an aluminum alloy. Inasmuch as precipitate particles bordering the depleted region had not grown in size, it was concluded that the solute atoms which had constituted the missing particles had gone back into solution. No mechanism for the reversion process was presented. The present study was undertaken to investigate further the conditions leading to instability during cyclic loading, and to determine whether reversion or overaging had taken place as a result of cyclic loading. BACKGROUND AND TEST PROCEDURE In order to differentiate between the processes of reversion and overaging, rest periods at an elevated temperature, which ordinarily would insure additional precipitation, were used in this investigation. It was expected that after a period of cyclic loading an elevated temperature rest period would result in a decrease in the remaining life of the specimen if overaging were occurring during cyclic loading, whereas in the case of reversion, reprecipitation would occur and the fatigue life would be extended. Such an expectation is based on the assumption that the crack-nucleation phase is a significant portion of the total fatigue life, and that such a treatment is of influence in the crack-nucleation stage and is relatively unimportant thereafter.

Jan 1, 1963

By R. E. Cech

Particles -3 to 30 µ diam of a 29.5 pet Ni, 70.5 pet Fe alloy after being melted and solidified while falling through a hydrogen atmosphere were found to contain a distortion-free body-centered-cubic phase. In most particles, the amount of body-centered-cubic phase approaches or equals 100 pet. It was shown by a series of experiments that this phase forms directly from the liquid. It is pointed out that a mechanism previously suggested in recent papers on the theory of the liquid-solid transformation can account for the solidification of body-centered-cubic phase in a temperature range where face-centered-cubic is the stable phase. IN the course of an operation to produce powders for a study of the martensitic transformation in Fe-Ni alloys, an unexpected phenomenon was observed. Powders of a 29.5 pet Ni alloy, which has a subzero M, temperature, were found to contain considerable amounts of a body-centered-cubic phase at room temperature. The experiments to be described were designed to elucidate the mode of formation of this unexpected phase. Experiments and Discussion An alloy containing 29.5 wt pet Ni, balance iron, was vacuum melted from high purity electrolytic iron and carbonyl nickel shot and solidified in the crucible. The metal was converted to oxide, ground to 100 pet <37µ, pressed to a cake, and homogenized 20 hr at 1350°C. To insure homogeneity the grinding, pressing, and homogenizing heat treatment was repeated a second time. The oxide was then ground to 100 pct <37µ and hydrogen reduced at 500°C. The reduced powder was given a spheroidizing treatment to produce spherical cast particles. The treatment consisted of dispersing the particles in hydrogen and allowing them to drop through a vertical hydrogen furnace set to a temperature higher than the liquidus of the alloy. This operation, commonly known as shotting, has been described more fully elsewhere.&apos; The powder produced by this method was found to contain approximately equal parts of body-centered-cubic and face-centered-cubic phases. A magnetic separation technique, previously described,&apos; was applied, and it was found that particles were either completely face-centered-cubic or nearly completely body-centered-cubic. The microstruc-

Jan 1, 1957

By T. S. Plaskett

A striated structure perpendicular to the growth axis was observed by the copper-decoration tech-nique in dislocation-free, .float-zoned silicon crystals. The striations, which were spaced about 100 p apart, fitted the relationship d = f/u , where d is the spacing, f is the growth rate, and u is the crystal rotation rate. Each stria was resolved into an UNDOPED silicon crystals pulled from quartz crucibles by the Czochralski technique usually exhibit a striated structure perpendicular to the growth axis.&apos;-&apos; This structure has been attributed to oxygen segregation, with the oxygen being introduced from the quartz crucible. If the crucible is rotated, the level of oxygen contamination has been reported as high as 10° atoms per cu cm.10 These striations are similar to solute striations commonly observed in doped Czochralski-grown crystals. The periodic nature of the striations is caused by a periodic variation in the growth rate",12 which is attributed mainly to thermal gradients in the melt.13 A finer striated structure14 attributed to constitutional supercooling is sometimes observed between the coarse striae. The oxygen striations have been observed by infrared transmission techniques,&apos; by the copper-decoration technique,&apos; by X-ray diffraction microscopy,6-8 and by 9 p absorption measurements3 on crystals pulled from the melt both with and without dislocations. In this investigation float-zoned dislocation-free crystals were examined by the copper-decoration technique. The level of oxygen for float-zone material is less than 1016 atoms per cu cm the lower limit of detection by 9 p absorption measurement. EXPERIMENTAL TECHNIQUE The crystals were grown by the float-zone process with the rf heating coil outside of the quartz envelope containing the silicon. All float zoning was done under an atmosphere of purified helium. The Dash technique15 was used to grow the crystal dislocation-free. This involves growing the crystal initially with a diameter between 2 and 3 mm and at array of starlike precipitates of copper. The strucLure was not .found at the surface tor a depth of about 1.5 mm, or in a region of similar width ahead of a dislocation network. The structure is postulated to consist of vacancy clusterings or dislocation loops. very rapid rates, about 20 mm per min, for a distance of about 3 cm. The diameter of the crystal is then increased to the diameter of the source of silicon, which in this case was about 19 mm. Because of the arrangement of the apparatus, the zone was passed downward rather than upward, contrary to the standard float-zoning practice. Also, the source was rotated rather than the seed. ziegler17 has made dislocation-free crystals by a similar technique but has passed the zone upwards. The starting material was zone-refined and had a p-type resistivity of 150 ohm-cm. The major impurity was boron; the total impurity excluding the boron was reported by the supplier (Dow-Corning) to be typically less than 2 x 1013 atoms per cu cm. The crystals were examined by the Dash copper-decoration technique18&apos;19—a method in which about 10" atoms per cu cm of copper are diffused at a temperature between 900" and 1000°C into silicon which is then quenched to room temperature. On quenching, the copper precipitates on crystalline defects which are then visible when viewed by transmission infrared microscopy. The photomicrographs shown were taken either of the infrared image tube screen or directly on infrared film. All sections prior to decorating were chemically polished and, for some sections, given a sirtlZ0 dislocation etch-pit examination. After decorating, the samples were mechanically polished. RESULTS A photomicrograph, taken in transmission of a decorated cross section, is shown in Fig. 1. The portion of the section shown is near the surface of the crystal. The entire cross section showed no dislocation etch pits after being given a Sirtl etch treatment. It is seen that the copper precipitated randomly. Each precipitate, as has been reported by others, was found to have a starlike structure.

Jan 1, 1965

By Jack Washburn

The c axis indentations in zinc crystals were shown to undergo 100 pct strain recovery on heating. The mode of deformation and the details of the polygonization and collapse of indentations were found to be consistent with a number of predictions of dislocation theory. IT has been observed that indentations of the type made by Jillson in zinc crystals can, under certain conditions, be macle to shrink in size and even completely disappear on heating the crystal, Fig. 1. The details of the process are interesting in that they afford a simple experimental illustration of several predictions of dislocation theory. The indentations were made as shown in Fig. 2 by dropping a 0.2 g indenter with a hemispherical point on a cleavage face of a. zinc crystal. Such indentations can be made through relatively great thicknesses in the c-axis direction. The material close to the struck surface, where mechanical twinning and complex distortion occurred, was removed by cleavage. The remaining crystal, which was about 1 cm thick, contained a dent that was accurately round and almost the same size on both top and bottom surfaces. The indentation had the form of a flat cone of half angle approximately 89°, having a rounded apex and a rounded intersection with the unde-formed part of the crystal. The mode of deformation was primarily slip on the three equivalent systems in the basal plane. Six types of dislocation loop (plus and minus in each of the three directions) as shown in Fig. 3 are required by the geometry of the indentation. The maximum shear strain in the radial direction amounted to approximately 2.5 pct. Slip was distributed in the usual, microscopically nonuniform, manner among the possible parallel slip planes. When an indentation was made close to a (2110) surface, three separate sets of interpenetrating slip bands appeared as shown schematically in Fig. 3. A small biaxial tension strain in the plane of (0001) is also a geometrical necessity for the formation of an indentation. If the sides of the dent are tilted l° with respect to the undeformed surrounding crystal, and the surround-

Jan 1, 1957

By L. E. Murr, P. J. Smith

A study has been made by transmission electron microscopy of thin foils of 304 stainless steel fatigued external to the electron microscope in reversed bending, and of thin foils fatigued directly within the microscope in alternating tension. The build-up of stacking faults in the thin foils during fatigue zoas correlated with the dislocatirm structures found in thin films prepared fror fatigued bulk specimens. The performance of the special devices designed for fatigue of thin foils so outlined and the importance of alternative methods of preparation of more uniform fatigue specimens bY vapor deposition are emphasized. INVESTIGATIONS on fatigued bulk aluminum1,&apos; and stainless stee13j4 have revealed the existence of dislocation substructure on examination by transmission electron microscopy of electrolytically thinned foils representative of these bulk specimens. While this technique has proved extremely valuable, it has several shortcomings. First, the method of fatiguing bulk specimens and then thinning to foil for electron-transmission observation allows only one observation of internal structure at any one portion of the fatigue life. Second, thinning the bulk fatigued specimens to foil results in the loss of at least one original surface. Thus, what one sees in the remaining electron-transparent sections is an internal dislocation or fault structure which in many cases cannot be correlated with the original surface markings. This is an undesirable feature, since it is well-known that metal surfaces play an important part in the fatigue process.5 An obvious third undesirable feature of the thinning-from-bulk technique is the fact that static observations have difficulty (in the case of fatigue) explaining the mechanism of a dynamic process. What is required then is a method whereby a selected thin area can be continuously observed either while undergoing cyclic deformation or at various fixed stages of fatigue deformation. While Murr and wilkov6 have reported some success with an apparatus designed to fatigue thin metal foils directly within the electron microscope, the nature of the specimen-mounting procedure and the mechanical features involved in the adaptation of the fatigue device to the electron microscope make this method difficult to operate. It was not possible, for example, to make frequent observations of a selected area because of difficulty in maintaining a chosen area in a stable viewing position inside the electron microscope. Except for the build-up of a dislocation substructure and what are commonly referred to as "slip striations", little else has been reported from observations on thin-foil sections prepared from bulk fatigue specimens. segal17 has found "slip striations" in stainless-steel fatigued specimens which were electropolished from both sides, but gave no explanation as to their origin or identity in terms of lattice imperfections. The research to be reported in this paper was undertaken with the following objectives in mind. First, an attempt was made to devise a technique or techniques whereby thin metal foils could be fatigued and repeatedly observed by transmission electron microscopy. Second, it was hoped that some correlation could be made between deformation striations found in fatigued thin transmission specimens and thin foils prepared from bulk fatigued specimens. These investigations illustrate quite convincingly that a feasible method is available for the direct study of the fatigue mechanism and similar dynamic phenomena in thin transmission specimens inside the electron microscope. I) EXPERIMENTAL METHODS Three modes of specimen fatigue and observation of fatigue damage were used. These involved fatigue of thin-foil specimens in a special arrangement external to the electron microscope and observation of a selected area at various stages in the fatigue life, the fatigue of thin-foil transmission specimens inside the electron microscope, and the fatigue of bulk specimens external to the electron microscope followed by thin-foil preparation for direct observation at predetermined stages. Design of the External Fatigue Clip and Specimen Holder for the Hitachi H.U.11 Electron Micro-scope. The purpose of the fatigue clip was to provide a reversed bending fatigue stress to a thin-foil transmission specimen outside the electron microscope. In order to accomplish this, a flat-bottomed, U-shaped brass clip was made as shown

Jan 1, 1965

By Larry Kaufman, Martin Schatz

The effect of pressure on the extension of the ? loop in the FeSi system has been determined by means of metallogvaphic studies and hardness measurements performed on a series of high-purity Fe-Si alloys containing 7.5, 11.0, and 13.9 at. pct Si, respectively. These mensurements, performed at 42 kbar and temperatures up to 1200oC, indicate that the ? loop is expanded to about 10 at. pct Si at 42 kbar as opposed to a maximum extension of 4 at. pct Si at 1 atm. Comparison of the experimental results with thermodynamic predictions of the pressure shifts yields satisfnctory results. DURING the past few years, several studies have been performed in our laboratory1-&apos; in order to determine the effect of high pressure on phase equilibrium in pure iron and iron-base alloys. The purpose of these studies has been to elucidate the effects of high pressure experimentally and to compare the observed results with predicted pressure effects derived on the basis of known thermody-namic and volumetric data at 1 atm. These studies have included work on pure iron2,5,7 as well as Fe-Ni,1,5 Fe-cr,l,5 and Fe-c4-6 alloys. In addition, Tanner and Kulin3 have reported results of pressure studies on two Fe-Si alloys containing 2.0 and 6.25 at. pct Si. At the time of this latter study, no detailed information was available concerning the difference in volume between the a (bcc) and ? (fcc) phases in the Fe-Si system as a function of silicon content. In order to compare their observations with calculated pressure shifts, Tanner and Kulin were forced to assume that silicon had no effect on the difference in volume between a and ? iron. The resulting discrepancy between their calculation of the a/? phase boundary at 42 kbar and the observed results led them to the conclusion that silicon additions probably decrease the difference in volume between a and ? iron. Recently: Cockett and Davis8,9 have reported de- tailed studies of the lattice parameters of a series of Fe-Si alloys at temperatures ranging from 20" to 1150°C. These measurements, performed on alloys in the bcc and fcc range, show that silicon does indeed decrease the difference in volume between a and ? iron. By correcting the calculations of Tanner and Kulin in line with the observed effect of silicon they were able to show improved agreement between computed and observed pressure shifts.&apos; The present measurements were undertaken to provide additional corroboration of this effect, by extending the range of composition, in addition to exploring a situation where large extensions of a ? loop could result in impingement of the ? field with an ordered bcc phase (based on Feo.75Sio.25). I) EXPERIMENTAL PROCEDURES AND RESULTS The alloys investigated were obtained from Dr. F. Kayser of M.I.T. They were prepared at the Ford Scientific Laboratory by vacuum melting electrolytic iron and high-purity silicon. The melts were poured under an argon atmosphere into hot-topped steel molds. Subsequently the ingots were hot-worked down to 1/2-in.-diam rods. Three alloys containing 7.5, 11.0, and 13.9 pct Si were studied. Carbon, regarded as the principal impurity, analyzed at, or below, 0.001 wt pct for all of the alloys. Prior to pressure-temperature treatment, the rod was annealed for 24 hr in vacuum at 1000°C, water-quenched, and subsequently machined into 0.100-in.-diam by 0.100-in.-long specimens. Subsequent to machining, the specimens were again annealed and then examined metallographically. They were found to exhibit a clear coarse-grained ferrite similar to Figs. 10 and 110 of Ref. 1 and Fig. 2 of Ref. 3. Subsequently, specimens of each alloy were equilibrated at 42 kbar at various temperatures in supported piston apparatus.1,3,4,6 Three specimens, one of each alloy, were wrapped in platinum and exposed simultaneously. The pressure-temperature cycle consisted of increasing the pressure from ambient to 42 kbar at 25oC, heating rapidly to the desired temperature, holding for 15 min, and quenching to 100°C, followed by slower cooling to 25°C and pressure release. The temperature was measured with a Pt/Pt-13 pct Rh thermocouple which was not corrected for pressure effects. Subsequently, specimens were examined metallographically and by

Jan 1, 1964

By M. J. Spendlove, H. W. St. Clair

An automatic surface-follower mechanism was used to measure the surface temperature and the rate of evaporation of molten zinc while undergoing distillation at low pressure. At pressures of 50 to 100 microns Hg, the rate of evaporation may be 60 to 80 pct of the theoretical maximum corresponding to the measured temperature. The rate decreases rapidly at pressures above 100 microns Hg, to only 7 pct of the theoretical maximum at 2000 microns Hg. Measured temperature gradients at the surface are in agreement with theoretical gradients calculated from the heat of vaporization, rate of evaporation, and thermal conductivity of molten zinc. THIS paper covers a series of careful measurements of the rate of evaporation of molten zinc at low pressures, undertaken as a part of a general investigation on the separation of metals by distillation.&apos; Preliminary results on the rate of evaporation of zinc were described in a previous publication.&apos; The results of the preliminary study are as follows: 1—The observed rates of evaporation of zinc were as high as 0.60 g per sq cm per min, corresponding to 75 pct of the maximum rate as determined by the temperature of the metal. 2—The evaporation rate was decreased from 0.30 g per sq cm per min at a pressure of 25 microns to only 0.09 g per sq cm per min when the pressure was increased to 5 mm. 3—The temperature of the surface during rapid evaporation may be 35" to 100°C less than the main mass of metal. Observed temperature gradients at the surface are consistent with those calculated from the heat of vaporization and the thermal conductivity of liquid zinc. In the preliminary experiments, the rate of evaporation was determined from the loss in weight of the metal in the crucible during the test. This was compared with the weight of the condensate. Obviously, this method was subject to error because of some uncertainty as to the period of evaporation that should correspond to the loss in weight. Furthermore, this method did not permit taking into account probable variations in the rate of evaporation during the test. A more serious shortcoming was that the temperature at the evaporating surface was not known, so the maximum theoretical rate of evaporation could not be calculated accurately. To improve the precision of rate measurements and to allow accurate measurements of the surface temperature, a refined experimental technique was developed whereby the temperature and position of the surface could be measured accurately. This was done by an automatic surface-follower mechanism that gave a continuous record of the surface temperature and the amount of zinc evaporated. These data permitted an instantaneous determination of the actual rate of evaporation and the surface temperature throughout the test. Pure zinc (99.99 pct Zn) was used in all experiments. Description of Distillation Furnace The details of construction of the distillation furnace are shown in Fig. l. The furnace is enclosed in a large quartz tube open at one end. The open end of the quartz tube is sealed by means of a water-cooled head. The entire enclosure is vacuum tight. The connection between the water-cooled head and the quartz tube is sealed by means of a rubber gasket which fits tightly against the smooth end of the tube. The metal is heated by induced current set up in the molten zinc and the walls of the graphite crucible by means of a water-cooled induction coil outside the quartz tube. High frequency current is passed through the induction coil from a 6 kw mer-

Jan 1, 1952

By W. A. Krivsky, R. Schumann

Relaxation calculations were made to find the temperature distribution in the refractory wall surrounding a tuyere pipe. One set of boundary conditions approxiwated those of a standard copper converter while a second set represented a hypothetical,thermally insulated tuyere pipe. The pvonounced cooling effect of the tuyere is related to the problem of tuyere accretions and tuyere bunching. PARTICULARLY severe service conditions are encountered in the tuyere zone of a basic copper converter during the matte blow. High-temperature gradients result from the juxtaposition of the hot charge and the tuyere pipe carrying cold air. Refractory temperatures near the tuyere mouth vary rapidly with time when the blast is turned on or off. One of the most serious problems is the formation of magnetite accretions around the tuyere mouth, which occurs very rapidly under some operating conditions. As a result, continual punching of the tuyeres is necessary to maintain a satisfactory rate of converting. Thus, if some means could be devised for keeping the tuyere pipes fully open without necessity for punching, a considerable saving should result from reduction in labor cost, maintenance of full capacity operation, and reduction in refractory costs. Recent quantitative studies of the FeO-Fe,O,-SiO, system1 have shown that the solubility of magnetite in iron-silicate slags decreases rapidly with de- creasing temperature in the range of copper converting temperatures. Data taken from the previous work are shown in Fig. 1. Thus the formation of "horns" and accretions around the tuyere mouth can result simply from the freezing out of magnetite on the cooler areas of refractory immediately adjacent to the tuyere pipes. One might expect to find a correlation between the severity of magnetite formation and the area of refractory surface which is cooled below the freezing point of the slag (corresponding to magnetite precipitation). Magnetite itself has a very high melting point (1597°C) so that the accretions are for all practical purposes infusible. The accretions might be dissolved by increasing the silica content of the slag and at the same time raising the temperature, but this approach is not feasible because it results in rapid corrosion of the basic refractory lining of the converter as a whole. In order to understand better the problems involved in tuyere design and operation, it seems essential to have at least a semiquantitative idea of the thermal conditions in the tuyere zone. Accordingly, this paper presents results of thermal calculations for an idealized copper converter tuyere. These calculations follow the so-called relaxation

Jan 1, 1960

By Don M. Jackson, Robert W. Howard

Techniques for the epilaxial growth of single -crystal silicon carbide films on silicon were developed. The vapor-phase decomposition and bydrogen reduction of silicon tetrachloride (SiC14) and Propane (C3H8) resulted in clear films of silicon carbide, lip to seveval microns in thickness. The growth took place in a horizontal . silicon epilaxial reactor at 1100°C (pyrometer) at a rate of- 3000Å per minute. Electron diffraction and X-ray diffraction studies demonstrated that the films were single-cyrstal, ß -phase, or cubic silicon carbide. SiO2 film were used to mask areas of the silicon sur-lace in order that the silicon carbide might be grown in controlled geometries. Both n- and p-type films were grown on p-type silicon waters.. Heavily doped silicon films of the same conductivity type as the silicon carbide films were deposited over the silicon carbide in order to affect better probe contact to the structures. when n-type silicon carbide mesas were grown on p-type silicon substrates the de vollage-current relationships between films and substrates were that of junction diodes. These diodes showed a sensitivity to while light ill that the incident light increased forward- and reverse-satro,ation currents, P-type silicon carbide mesas grown on p-type silicon were ohmic rather than rectifying in their voltage -current relationship. No conclusions could he reached concerning heterojunc-tiou rectification in the structure. SILICON carbide is a semiconductor with many interesting properties. It decomposes at temperatures above 2200°C.1 It occurs in two general crys-tallographic forms—hexagonal (a Sic) and cubic (ß Sic)—with the cubic form having a forbidden-gap energy of 2.32 ev and the hexagonal form (specifically the 6H polytype) a gap energy of 2.86 ev.3 It behaves as an extrinsic semiconductor at temperatures approaching 5003C. It has been shown to have a high resistance to radiation damage4 and p-n junctions formed in Sic have been shown to radiate visible light under forward- or reverse-bias conditions. Epitaxial silicon carbide on silicon carbide has been successfully grown through the use of a variety of techniques, such as gaseous cracking of SiCL4 and CC4, nearly all of which require a deposition temperature above 1500°C.6 This paper will cover very recent work on the gas-phase deposition of highly ordered films of silicon carbide on high-quality silicon single-crystal substrates. The films have been shown to ex- hibit junction-rectification properties when geometrically isolated regions are electrically biased with reference to the silicon substrate. There will be no discussion of the mechanism of heterojunction rectification, but the methods of film fabrication, geometry control, and structural evaluations will be covered in detail. Electron diffraction, X-ray diffraction, and diode electrical properties were used to characterize the films and the junctions. GAS-PHASE DEPOSITION OF Sic The techniques for the deposition of silicon carbide films were a logical outgrowth of the standard silicon epitaxial process. The major premise followed was that, for any film to nucleate in an ordered fashion where there is considerable mismatch in lattice parameters (in this case 22 pct), an extremely clean, damage-free substrate surface must be presented to the gas stream. Thus a standard gas-phase HCl etching step was used to prepare the substrates for growth. A minimum of 5 µ of substrate-surface material was removed prior to the deposition of Sic overgrowth films. The techniques used for growing silicon carbide films were those of growing silicon alone, with the added injection of a hydrocarbon gas into the hydrogen and silicon tetrachloride gas stream. The hydrocarbon gases used thus far have been research-grade (99.99 pct) methane (CH4) and propane (C3H8). Propane ultimately gave the best results. The gas flows were controlled through a panel shown schematically in Fig. 1. A hydrogen main stream of 30 liters per min passed through the horizontal quartz-tube epitaxial reactor, while SiC14, C3H8, HC1, and doping gases were injected as side streams. The

Jan 1, 1965

By R. E. Tate, L. J. Herman

We have had occasion to produce wire of Np-237 in small diameters for use in some chemical experiments. Since the mechanical metallurgy of neptunium has not been investigated extensively, it seems desirable to report our successful extrusion technique. Because of the neptunium activity and its attendant health hazard the experimental work was done in glove boxes and related equipment also used for Pu-239. At room temperature a phase neptunium&apos; is a hard (Dph -355) orthorhombic metal of high density (p = 20.45 g per cu cm). a neptunium transforms2 to tetragonal ß neptunium at about 280°C and this in turn transforms to bcc y neptunium at about 577°C. The y phase melts at about 637°C. A temperature of 340° to 345°C was selected for the extrusion, this temperature being a compromise be- tween a possible advantage of working with the presumably more plastic cubic y phase above 577°C and the risk of having the neptunium react with the alloy steel die to form the low-melting Fe-Np eutectic. A 0.75-in.-long, 0.26-in.-diameter ingot of good-purity* Np-237 was extruded by the direct *C = 230 ppm, Pu = 200 ppm, thirty-five metallic elements below limit of detection by spectrographic methods. process through flat-face orifices to form several sizes of wire ranging from 0.010 to 0.030 in. in diameter. Molybdenum disulfide was used as the die lubricant. The extrusion was done in a vacuum of about 10-4 torr to reduce reaction of the neptunium with atmospheric gases. British workers3 at Harwell have extruded neptunium under similar conditions. The force required to extrude 0.010-in.-diameter wire at the rate of 4 in. per min was 6000 lb, as measured with an electrical load cell. Wire 0.020 in. in diameter was extruded with a force of 4700 lb at a rate of 2 in. per min, and wire 0.030 in. in diameter was extruded with a force of 4000 lb at a rate of 1.3 in. per min. An extrusion constant, c, can be computed from the measured forces, P, for the equation4 P = c log-A/a where A/a is the extrusion ratio or the ratio of the cross-sectional areas of the container and the

Jan 1, 1965

By K. G. Wikle, J. G. Klein, W. W. Beaver

Consolidation of hydride process, electrolytic, calcium reduced, and comminuted thorium powder, as well as saw chips and lathe turnings, by vacuum hot pressing and by cold pressing-vacuum sintering was studied. The mechanical properties of the consolidated material in the extruded form are compared with those of wrought castings. AT present there little little industrial use for thorium metal, although it has some important though small scale applications in electronic equipment. Despite its high inelting point—about 1750°C —a low modulus of elasticity, 11.4xl0 si at 20°C;&apos; relatively low mechanical properties coupled with a high density, 11.7 g per cu cm; and an unusually high chemical activity with normal atmospheres limit any structural applications. The metal is utilized as an alloying element principally in magnesium. Pure thorium finds utility as electrodes in gaseous discharge lamps such as the high intensity mercury lamp&apos; because its low work function and high electron emissivity provide lower starting potentials and more uniform operating characteristics than other available materials. The metal is also found in photoelectric tubes used for the measurement of the ultraviolet spectrum." Thorium metal has been used in germicidal lamps of the cold cathode type as sputtered coatings on nickel in order to provide a low work function surface and a low starting voltage. Other applications have involved the radioactive properties of thorium for the production of ionized particles." The potential value of thorium is much greater than its present use pattern because of possible utility in the field of nuclear power. Th may be converted through nuclear reaction to a fissionable element U which should be capable of acting similarly to U in the g&apos;eneration of atomic power. Thorium has been reported to be about three times as plentiful as uranium in the earth&apos;s crust, placing it in the order of abundance of lead and molybdenum." Thus, it is of interest in augmenting the potential supply of fissionable material for nuclear power. Because of its high melting point, thorium is usually produced as a powder through the calcium reduction of its oxide or thermal reduction of halides by sodium, magnesium, and calcium. It may also be produced in flake form by electrolysis of fused alkali or alkaline earth chloricles and fluorides. Therefore, powder metallurgy assumes importance in the fab- rication of thorium metal shapes. Furthermore, it is rather difficult to obtain pure thorium by melting, as the molten metal reacts readily with graphite as well as oxide, carbide, and nitride refractories. These contaminate the melt with oxides, carbides, and metallic impurities." The current investigation was undertaken to examine the fabrication of thorium by powder metallurgy methods which have been used for the commercial production of beryllium and other metals.&apos; A sparcity of data concerning the comparative cold and hot compaction of thorium powders of different derivation existed. Therefore, all commercially available types were examined along with other experimentally produced thorium powders in order to round out the comparison of consolidated thorium powders with melted reguline metal. Review of the Literature By heating a mixture of ThC1, with potassium, Berzelius made the first thorium metal as an impure powder in 1828. Improvements in the basic process, increasing thorium assay to 99 pct, were made by several investigators including Arsem," Lely and Hamberger10 and Von Bolton." Calcium reduction of Tho, to make powders was investigated by Berger," Huppertz,&apos;" Kroll," and Kuzel and Wedekind.&apos;" A thorium powder produced by this method using a CaC1, fluxing agent assayed 99.7 pct, as reported by Marden and Rentschler.&apos;" Compacted and sintered, this product was found to be ductile, and could be fabricated into wire and sheet. Improvements of the calcium reduction process were made later" wherein CaCl, was eliminated from the reaction, producing metal assaying 99.8 pct Th. Further work by Lilliendah118 howed that a coarser metal could be obtained by the substitution of ThC1, or ThOC1, for oxide with consequent advantage of stability to atmospheric reaction. Reports on the technology of thorium developed in Germany during World War II have been made by Espe."&apos; Thorium powder of 99.5 pct Th was obtained by reduction of the oxide by calcium. Screening to —200 mesh, compacting with about 20 tsi, and sintering in vacuo at 1320" to 1360°C for 3 hr resulted in a porous sinter cake. The sinter cake was sufficiently ductile to be worked into bar, wire, and sheet which could be employed as electrode materials.

Jan 1, 1957

By H. H. Klepfer, M. E. Snyder

UNTIL very recently, the commercial availability of the rare earths as metals has been very limited. Fabrication of mill products from these metals has not been studied in most cases. This note reports the results of the development of fabrication techniques for thulium. Thulium has a melting point of about 1550°C and a hexagonal close-packed crystal structure. It oxidizes in air to give a black oxide (TmzO,). The procedures for producing thin thulium foil were developed on one ingot weighing about 220 g and were subsequently applied in processing about a pound of metal to foil. Several alternates for the various fabrication steps were investigated and will be discussed. The metal fabricated was in the form of commercial chill-cast ingots 1 in. in diam and 2 in. long weighing approximately 220 g. Impurities in the ingots were reported by the vendor to be 4000 ppni tantalum, 2000 ppm calcium, 200 ppm nickel, 100 to 200 ppm iron, 100 ppm europium, and less than 100 ppm copper, lutetium, and ytterbium. In addition to these impurities, several salt-like inclusions as large as l/8 in. in diam were revealed along the center line of the one ingot sectioned. Preliminary tests indicated that small wafers cut from the as-cast ingot would not fabricate readily by rolling. Forging of copper-jacketed wafers was therefore attempted. At 1550"F forging was satisfactory but an apparent reaction of copper with thulium demanded investigation of lower temperatures. Therefore, the remainder of the test ingot was forged at 1450°F—with only minor cracking. All ingots forged were inserted into copper tubes of 1 in. 1D and 0.125-in. wall thickness. The jackets were sealed by flattening the ends of the tubes and welding under helium. Heating time at 1450°F was 30 min. Press forgings of 1/8 in. per pass were used, followed by 10 min reheats. When the ingots had been squared and reduced to 0.250 in. in thickness, the original copper jacket was stripped off and replaced by a new jacket in preparation for hot rolling. Hot rolling at 1450" F without edge cracking was readily accomplished after forging. Excellent results were obtained with 10 pct reductions of thickness followed by 5 to 10 min reheats. After reduction of thickness from 0.250 to 0.100 in. the copper jacket was removed. It was found, in fact, that hot rolling in air was possible. A tenacious black oxide similar to that seen on zirconium was formed during 3 min reheats at 1450°F. Reduction in air to 0.010 in. foil was possible taking 10 pct reductions per pass. The oxide coat formed during hot rolling in air could best be removed by sand blasting and pickling. Common pickling solutions containing polar solvents were found to attack the metal too rapidly and a concentrated nitric-hydrofluoric acid mixture attacked neither the oxide nor the metal. The most satisfactory pickling solution was 52 vol pct concentrated nitric acid-48 vol pct glacial acetic acid. After forging to 0.250 in., vacuum annealing and cold rolling was found to be another satisfactory alternate to hot rolling in copper jackets. After forging. a hardness of Rockwell B76 was found. Annealing in vacuum (2 X l0-5 mm of Hg) for 1 hr at 1200"F did not alter this value. Annealing at 1470"F for 1 hr brought the hardness down to R;]63. With cold rolling (5 pct per pass) the hardness returned to about R,1:76 after 20 pct reduction and edge cracking became noticeable. However, cold rolling to a total of 40 pct reduction in thickness (RI,,83) was possible before edge crack propagation became serious. Good surface finish was obtained, and the metal loss due to oxidation was minimized by cold rolling and vacuum annealing. Using this procedure the yield of 1.25 in. wide by 0.010 in. thick foil from a 1-in. diam ingot was about 40 pct.

Jan 1, 1961

By H. W. Weart, S. Sarian

The effect of temperature, impurities, and capillarity on the morphology of solid particles in a liquid matrix is investigated. For the NbC-liquid iron system, at least, it is found that those particles which are dissolving will assume a spherical shape; all others will take the equilibrium shape. An aniso-tropic-isotropic transition in the interfacial tension is observed at about 1725°C and is believed to be due to cooperative roughening of the interface on an atomic scale. The presence of boron as an impurity lowers the transition temperature. It is the purpose of this paper to present some observations on the shape of particles in a system consisting of solid particles of nonuniform size in a liquid matrix and to propose an explanation for these observations. Although qualitative only, these observations, which were made largely in the course of a study of particle-growth kinetics,&apos; are presented separately to draw attention to them. They reveal the effect of particle size, temperature, and surface-active impurities on particle shape in the solid NbC-liquid iron system, and are unique in demonstrating for the first time the reversible effect of temperature and impurity concentration on the anisotropy of the energy of the solid-liquid interfaces involved. Some of the changes are readily demonstrated with the few particles whose shapes can be clearly shown in a single photomicrograph, but others are more subtle, and their recognition depends upon some experience and the study of a much larger sample. For this reason, a certain amount of judgment must be acknowledged to underlie their detection, but every effort was made to maintain proper scientific objectivity in evaluating the observations. The observations will be presented first, and then an explanation rationalizing them will be offered. Brief reminders of the relevant theories will be inserted into the discussion at the appropriate points. EXPERIMENTAL The observations were made of the shape of NbC particles dispersed in liquid iron. All specimens were prepared by pressing NbC powder and car- bony1 iron powder treated according to standard powder-metallurgical procedures. Except as noted, all specimens were heated to 1900°C for 1/2 hr. In investigating the effect of temperature, specimens were quenched from 1900°C to various lower temperatures, and held long enough (48 hr) to allow shape changes to be completed. Boron, in the form of amorphous powder, and oxygen, in the form of niobium oxide powder, were added as impurities to some specimens. Nitrogen was introduced into some specimens as an impurity by heat treating the samples under a partial pressure of nitrogen gas. Effect of Temperature. It was first observed that increasing temperature had a marked effect in rounding the corners and edges of the particles. At 1900°C the particles are all very nearly spherical and remain so even when the holding time is extended to 48 hr. As can be seen from Fig. 1, there is virtually no evidence of the presence of low-index planes. At 1300°C, however, most of the particles are prismatic with very slightly rounded edges and corners, Fig. 2. (In making these shape comparisons, attention should be focused on the larger particles, even though the smaller ones would be expected to be the first to change shape, owing to the shorter diffusion distances involved. The cause of the mixed particle shape will be explored later.) It was established that these structures are re-

Jan 1, 1965

By M. Semchyshen, A. P. Coldren, W. G. Scholz

A survey of the Fe-Mo-B system was made to determine the extent to which boron might affect the microstructure and strength properties of iron-rich Fe-Mo alloys. Seventeen vacuum-induc tion melted ingots were prepared with approximate mo-lybednum contents 01 2, 4, 9, and 19 wt pct and approximate boron contents of 5, 14,50, and 630 ppm by weight. Phases extracted from annealed specimens and identified by X-ray diffraction analysis included E Fe3MO2, Mo2FeB2, and an oxide hazling a diffraction pattern practically identical to that of MnFez04. Three types of alloy strengthening were observed: a) Fe-2 pct Mo-B alloys were hardenable by a bainitic-type transformtion of austenite to ferrile; b) Fe-4 pct Mo-B alloys were hardened by the solid-solution mechanism; and C) Fe-9 pct Mo-B and Fe-19 pct Mo-B alloys were hardened by precipitation of the E Fe3Moz phase. Boron was observed to have a very strong hardening effect in the Fe-2 pct Mo alloys and a mild strengthening effect on the 1200°F properties of the Fe-4 pct Mo alloys. In the Fe-9 pct Mo alloys there was no consistent effect of boron on strength at either room temperature or 1200° F. The Fe-19 pct Mo alloys were so brittle that meaningful tensile or creep-rupture data could not he obtained. No dispersion hardening from borides was recognized in any of the alloys. THE high-temperature properties of iron-rich Fe-Mo alloys were studied by Reiter and Hibbard.&apos; They found that the strength of the alloys increased markedly as the molybdenum content was raised from 0 to 15.9 pct by weight. The authors explained the various degrees of strengthening in terms of a) solid-solution strengthening, b) strengthening from a martensitic-type transformation, and C) precipitation strengthening. The objective of the present investigation was to conduct a survey of the iron-rich portion of the Fe-Mo-B system to determine whether the beneficial effects of molybdenum on the strength of iron can be enhanced by the presence of boron. It was thought that perhaps fine dispersions of molybdenum- rich borides would be found which could improve the high-temperature strength of ferritic alloys beyond the strengths attainable by molybdenum additions alone. Also, it was considered worthwhile to study the effects of boron in alloys which are essentially free of carbon. Most, if not all, of our present knowledge about boron in high-temperature alloys pertains to alloys containing carbon and carbides. EXPERIMENTAL PROCEDURES Alloy Preparation. Seventeen 8-lb ingots were prepared from electrolytic Plastiron, unalloyed molybdenum chips, and boron powder by a vacuum-induction melting procedure employing hydrogen as the main deoxidizer. The alloys were melted in alumina crucibles using 35-lb melts, with each melt being split four ways to achieve varying boron contents within four Fe-Mo base compositions. The results of chemical analyses conducted on chips machined from the chilled ends of the ingots are presented in Table I. The boron analyses were performed by a spectrographic method utilizing primary standards prepared from boric acid. They indicated that in ingots to which no boron was

Jan 1, 1964

By A. Yoshikawa, T. Sugeno

To detenmine the origin of the sharp fatigue limit in many ferrous metals, S-N curvces were determined in push-pull fatigue at 18.6 kc per sec at room temperature and - 67°C for various kinds of iron. These differed in carbon and nitrogen content and grain size (25 and 2500 grains per sq mm). Sharp knees appeared in the S-N curves of fine-grained specimens with high interstitial content at both temperatures. In coarse-gruined specimens, knees were not sharp .regardless of the interstitial content and the testing temperature. It is concluded from these results that the controlling factov for the appeavance of the sharp fatigue limit is not strain aging but grain size. It has already been mentioned that iron and some iron alloys show fatigue curves characterized by a more or less sharp knee and a fatigue limit.&apos; Explanations of the origin of this characteristic behavior of fatigue in iron appear to fall into two broad classes. One is concerned with interstitial impurities through the aging or locking effect and the other is based on intrinsic plastic properties of iron. Levy and sinclair2 and Lipsit and Horne3 have suggested that the fatigue limit observed generally in iron and steel is due to interstitial solute aging during the course of fatigue. On the other hand, Thompson and wadsworthl have suggested that the fatigue limit may be analogous to the sharp yield point, in the sense that alternating stresses above the fatigue limit are necessary to break down the dislocation locking. However, there are some experimental results which cast doubt on the general validity of these suppositions.4-8 Ferro and Montalenti&apos; have recently suggested that the typical form of the fatigue curve of iron seems to come from an intrinsic plastic characteristic of the iron structure. This suggestion is based on the experimental result that pure iron containing an insufficient amount of interstitial solute to alldw appreciable strain-aging effects still showed a fatigue limit at room temperature. Although systematic investigations on the effect of grain size are scarce, it is thought that this effect is important in relation to the sharp fatigue limit. In fact, sensible differences were observed by Oates and Wilson4 in fatigue behaviors of a low-carbon steel depending on grain size. Ideally, the fatigue limit will be defined as the upper limit of stress amplitudes at which the life is infinite. This ideal fatigue limit can never be determined because of the limited time available for experiments, and moreover scattered data points often leave the construction of S-N curves somewhat arbitrary. And, it is usually stated that a material has a fatigue limit when its statistical S-N curve becomes apparently parallel to the N axis with a more or less sharp knee. The meaning of the fatigue limit and the sharp knee will be discussed in detail in relation to the construction of S-N curves. The origin of this sharp knee was investigated by determining S-N curves of iron for various interstitial contents, testing temperatures, and grain sizes. EXPERTMENTAL PROCEDURE The material as received was a commercial-grade low-carbon steel in the form of 4-mm-diameter rods with the following composition in weight percent: C, 0.09; Si, 0.017; Mn, 0.43; P, 0.006; S, 0.012; Cu, 0.11. Five different groups of specimens were tested. The grain sizes and interstitial contents in each group are given in Table I. The specimens of group C-02 were decarburized by annealing for 100 hr at 700°C, followed by an additional 100 hr at 850°C in wet hydrogen. Specimens of groups N-2 and N-9 nitrided in a mixed atmosphere of ammonia and hydrogen after an initial treatment identical to group C-02. The specimens of group C-9 were prepared in a manner similar to those of group C-02, except heat treatment was carried out in a vacuum. After polishing their surface with emery paper, the specimens of all groups were given a final anneal for 30 min at 930°C and air-cooled in an evacuated quartz tube. For group C*-9 this

Jan 1, 1965

By B. A. Wilcox

ThERE are several reports in the literature which indicate that both solid-solution hydrogen and hydride precipitates can promote low-temperature em-brittlement of tantalum.1-3 For example, Imgram et al.2 showed that hydrogen additions in the range of 140 to 580 ppm promoted a ductile-to-brittle transition at slightly above room temperature in both wrought and recrystallized tantalum. This contrasts with the observation that tantalum of norma1 purity is very ductile, even at liquid-nitrogen temperature. Imgram et al. also found that hydrogen additions caused a deterioration of notch tensile properties of tantalum. The purpose of this communication is to present some limited evidence that hydrogen can also cause fatigue embrittlement of tantalum. The material used in this investigation was wrought, stress-relieved (1000°C, 1 hr), are-melted tantalum rod (5/8-in. diameter) containing the following impurities in weight percent: 0.005 C, 0.007 02, 0.0005 H2, 0.003 N2, 0.08 Cb, 0.01 W, and 0.01 Fe. Hydrogen charging was done in an atmosphere of flowing dry hydrogen for 3 hr at 600°C, followed by an homogenizing anneal in purified argon for 15 min at 600°C, and cooling in an argon atmosphere. Typical micro-structures of the hydrogen-free and the hydrogen-charged materials are shown in Fig. 1(a) and Fig. 1(b), respectively. Fig. 1(b) shows the appearance of hydride precipitates which, in many cases, formed preferentially parallel to the rod axis. The hydride dispersion was uniform across the diameter of the specimen. The fact that the precipitate was a tantalum hydride was tentatively confirmed by X-ray diffraction on a metallographically prepared surface. After hydrogen charging, chemical analyses by vacuum fusion revealed the hydrogen content to be 0.0295 wt pct. In addition, the oxygen and nitrogen contents were slightly raised to 0.0095 O2 and 0.005 N2.

Jan 1, 1964

By W. A. Backofen, M. L. Ebner

SINCE the early work of Gough with Hanson and Wright,l-3 the study of fatigue has been characterized by experiments on single crystals only in recent times.9-10 Now, increasing attention is given to this aspect of fatigue research for the insight that it may provide into details of mechanism. The investigations have concentrated to a large extent on the development of deformation markings on fatigued crystals, and have shown the cracks to originate in slip bands possibly preceded or accompanied by slip-band extrusions. Experiments of special interest to the present work were conducted by paterson5 on copper crystals and involved both metallographic examination and measurement of change in flow stress. Crystals were cycled in alternating tens ion-compress ion with a constant plastic shear-strain amplitude of approximately 0.8 pct, and were particularly revealing for their demonstration of hardening with accumulated strain similar to that in unidirectional straining, through an easy-glide stage I followed by a stage II of rapid hardening; deformation was not continued beyond 40 cycles, however, so that the eventual course of the hardening curve could not be decided. For the conditions used by Paterson, surface slip markings were similar to those observed in unidirectional straining, but there were no X-ray asterisms and no deformation bands on the surface. In current thinking about the nature of fracture in fatigue, two views relative to mechanism are generally acknowledged, with the reservation that both could apply simultaneously in some measure. As one possibility, fracturing across a slip plane is regarded as a result of loss of cohesion from the creation of many point defects by dislocation movement under the cyclic loading.&apos;&apos; On the other hand, fracture has also been taken to follow as a consequence only of the geometry of slip at a free surface, consisting of offsets and crevices which eventually become fatigue cracks.12, l3 The work of McCammon and Rosenbergl4 showing fatigue in polycrystals at 4.2oK makes clear that any long-range diffusion of point defects is unnecessary, yet studies such as those of Forsyth and stubington15 show that accelerated diffusion may be a characteristic of deformation under fatigue loading. Interest in obtaining data of possible use for resolving such questions led to the experiments described below. Copper crystals were conveniently loaded in alternating four-point bending at constant deflection, a test condition shown to approximate a constant plastic strain amplitude for a wide range of axial orientations. The method of testing was not readily adapted to extensive study of temperature effects, but an investigation of the geometry of crack formation could simply be made by orienting,the slip direction at different angles to the surface. EXPERIMENTAL PROCEDURES Single crystals were grown by a modified Bridgman method in a stationary gradient furnace under an atmosphere of purified dry nitrogen. Purity of as-grown crystals was 99.999 pct as determined by spectrographic analysis plus vacuum fusion and gravimetric analyses for oxygen and sulfur, respectively. Crystals were of reasonable perfection as evidenced by a critical resolved shear stress at 10 deg from (110) of 60 g per sq mm and half-width of a (400) X-ray diffraction line from one crystal of

Jan 1, 1960

By C. S. Barrett

THE crystal imperfections known as faults in stacking (stacking disorder) are of importance to both fundamental and applied science and are receiving increasing attention. On the theoretical side there have been recent advances in the analysis of diffraction patterns in terms of stacking faults, and on the experimental side it has been found that certain metals develop a faulted structure on cooling through a phase transformation. Beyond this, little is known of what may be called the physical and mechanical metallurgy of faulting, although there has been no lack of discussion and conjecture as to the presence of faults in metals and the effect of faults on mechanical properties and microstructures. In the close-packed metals the nature of faults can be described very simply. Face-centered cubic (FCC) crystals consist of close-packed layers of atoms, (111) planes, stacked above each other in a definite manner. If one layer is designated as the A layer, the next must be a B or a C layer; that is, every atom of the second layer lies not above the atoms of the A layer, but nestles in the hollows between these, using the hollows designated as the B positions, or the equivalent hollows designated as C. If the sequence of layers is ABCABC...., so that layers three spacings apart are directly over each other, the crystal is FCC; if CBACBA ... it is an FCC crystal that is a twin of the former; if ABAB........or BCBC..it is hexagonal close-packed (HCP). A fault is a break in the sequence, such as ABCABABC .. . which has the effect of inserting an HCP lamella into an FCC crystal. Regularly spaced faults spaced two layers apart would convert an FCC crystal entirely to HCP, or an HCP to FCC. A fault in an FCC crystal is also equivalent to creating an FCC twin of minimum thickness; in fact, the entire crystal would be converted to its twin if faults were introduced regularly. (In HCP crystals, however, twinning does not occur on the basal plane and a fault on this plane is not identical with a thin twin). Faults are one of the possible causes for annealing twins,&apos; for the strain markings that are brought out by etching deformed metal,&apos;," for the altered X ray reflecting power of metal at slip bands that is revealed in X ray reflection micrographs,&apos; for the extinction of Kikuchi lines in electron diffraction patterns, and for the hardening of latent slip planes.&apos; Since other explanations of these effects are also available," there has been no direct proof of faults from deformation; yet it has appeared likely that they would occur. Faults resulting from phase transformations in metals, however, have been clearly revealed by diffraction in cobalt" and lithium. It is to be expected that the faulting tendency is greatest

Jan 1, 1951