By Guo-Sen Zhu

Research on the formation mechanism and control of corner transverse cracks was carried out. The optical microscope and SEM were applied to analyze the characteristics of cracks. It is found that the cracks occur at the relatively lower temperature due to unbending strain and have almost nothing to do with the mold cooling and powder. The keys to prevent corner transverse cracks are to optimize the corner temperature of slab and maintain the good state of casting machine. Increasing casting speed and decreasing the cooling water flux at the corner in the unbending segments, resulting in mild cooling, were applied during investigation to control corner temperature above the upper limit temperature of the No.3 brittle zone of Nb-contained steel tested by Gleeble-1500 system. As a result, corner transverse cracks were minimized, but centerline segregation got worse. And then increasing the cooling water flux at the corner (intensive cooling) was applied to make corner temperature below the lower limit temperature of the No.3 brittle zone. Great diminution of both corner transverse cracks and centerline segregation was achieved finally.

Jan 1, 2006

By Junto Nishiwaki, Shinji Kumai

"Mechanical and physical properties of the impact welded dissimilar metal joints are controlled by joint interface morphology. An intermediate layer (IML) is often formed at the joint interface and this deteriorates the interface quality in some metal combinations. Numerical and experimental studies were performed in order to examine the formation mechanism of the wavy interface and intermediate layer for explosive welded Al/Cu dissimilar metal joints. The impact welding process consists of (1) high-speed oblique collision of metal plates, (2) metal jet emission and large deformation and temperature increase at collision point and (3) rapid cooling at the joint interface. Euler-Lagrange coupling method, smooth particle hydrodynamic (SPH) method and modified laplacianFoam (LF) method were linked together to simulate a series of processes from (1) to (3), and the final interface morphology including the formation of IML was reproduced. The wavy morphology (wave-height, wavelength) and the position and composition of IML formed at the joint interface of Al/Cu joints were quantitatively in good agreement with those reproduced by numerical analysis. Our simulation results are useful for the control of the interface morphology, reduction of the amount of IML, and improvement of the mechanical properties of the impact welded dissimilar metal joints.INTRODUCTIONImpact welding is a kind of solid state joining method providing extremely high joint strength for both similar-and dissimilar metal combinations. Explosive welding and magnetic pulse welding are representative methods to achieve the impact welding. By a high-speed oblique collision between two metal plates, a metal jet is emitted from the collision point. The metal jet can remove any oxide films and contaminations on the plates and produce an active refreshed surface. Consequently, good metallurgical bonding can be achieved even for dissimilar metals (Crossland, 1982). Solid metals deform like fluids under the high pressure condition at the collision point and characteristic wavy interface is formed. In addition to the wavy interface, an intermediate layer (IML) is often formed at the joint interface in some metal combinations. Elimination or reduction of the amount of IML at the joint interface is desired since the excessive IML formation along the joint interface causes a large reduction in physical and mechanical properties. Formation of IML is considered to result from characteristic thermal history at the joint interface including partial melting due to the local temperature increase and successive rapid cooling behavior at the joint interface. In order to control the IML formation at the joint interface, it is necessary to reveal both heating and cooling processes at the joint interface. However, it is impossible to observe the phenomenon occurring at the joint interface and also difficult to investigate the temperature change at the joint interface directly during the impact welding. Therefore, simulation or numerical analysis is indispensable to overcome this problem. In the present study, the explosive welded Al/Cu joint, which is prone to form IML at the joint interface, was selected for the research. By using a newly developed numerical analysis method, not only the formation process of wavy interface, but also the local temperature increase and successive temperature decrease at the joint interface were reproduced. The formation process of IML was investigated by using both numerical analytic and experimental results."

Jan 1, 2018

By Bin Zhu, Mingmei Zhu, Hong Zhou, Xiaofei Dou, Bin Xie, Yu Wang, Tiancheng Lin

In this study, the formation of 2CaO·SiO2 and 3CaO·P2O5 solid solution (nC2S-C3P) in hot metal dephosphorization process is discussed. The variations of CaO and SiO2 mass, both in nC2S-C3P solid solution phase and liquid slag phase with increasing P2O5 mass in CaO-SiO2-FetO-P2O5 slags were calculated using Factsage software. CaO-SiO2-FeOt-P2O5 slag containing up to 18 % P2O5 was melted at 1823 K then cooled to 1673 K. The contents of CaO and SiO2 both in the solid solution phase and liquid slag phase of quenched samples were observed and analyzed by SEM/EDS. Both the calculated and experimental results show that the contents of CaO and SiO2 in the solid solution phase decreased, just opposite in the liquid slag phase, with increasing P2O5 content in the slags. Formation mechanism of nC2S-C3P solid solution in the slags was derived based on the ionic structure theory of molten slag. The SiO4 4- in the nC2S-C3P solid solution can be replaced by PO4 3- in the liquid phase resulting in the increasing of free Ca2+ and SiO4 4- in liquid phase.

Jan 1, 2015

By Feng Liu

A thermal upgrading process by which nickel value can be concentrated in a ferronickel alloy is a possible alternative to treat Sudbury pyrrhotite (Po) tailings with nickel content of 0.5–1.5 wt%. The basis of this process is precipitation of Ni from Po at high temperature once Fe/S ratio in the iron-deficient Po is shifted towards stoichiometric or near stoichiometric FeS (troilite) either by the addition of iron and/or the removal of sulfur. For the iron addition route, the reaction between elemental iron and nickeliferous pyrrhotite to produce ferronickel alloy and Ni-depleted iron sulfide phase plays a critical rule. In this paper, the formation mechanism of ferronickel alloy was investigated using the diffusion couple technique to better understand the nickel diffusion behavior in the iron and sulfide phases.

By Zenjiro Asaki, Teruo Tanabe

"To clarify the formation of light rare earth (R =Ce, Pr, Nd or Sm) -Fe compounds in the reduction-diffusion (RD) process, two kinds of experiments were carried out: (a) RD experiment in which briquettes composed of R oxide powder, Fe (particles or wire) and CaH2 were reacted, and (b) immersion experiment, where an Fe plate was immersed into R-Fe melt having the composition of Fe-side liquidus line in Fe crucible. The compound formation was examined by using XRD, SEM and EPMA. The formation rates of RzFe17 measured by the RD experiment were compared with those obtained by the immersion experiment. The growth rates of compounds obtained in the RD experiment for Pr-Fe and Nd-Fe systems were much lower than those obtained in the immersion experiment. This result was explained by the difference of the reduction rates of R oxides by Ca. The parabolic rate constants for the formation of RzFe17 were separated in two groups of (a) Pr-Fe and Nd-Fe systems and (b) Ce-Fe and Sm-Fe systems. This was discussed in connection with the difference of their crystal structures and the driving force of diffusion. The parabolic rate constants for the formation of compounds in Ce-Fe and Sm-Fe systems decreased in the order of RFez, RFe3 and RzFe17.IntroductionTo understand reaction behaviors in the production of rare earth (R) -iron intermetallic compounds, which have excellent magnetic properties, is very important from engineering point of view. And the reduction-diffusion (RD) process<O has recently attracted attention as one of the promising processes to economically produce R-related materials. A few fundamental studies on the compounds formation in the RD process have previously been reported. Qi, Hino and Yazawa(2) observed the formation of R(Nd, Sm)-Fe and R-Co compounds in the process from various view points. Song and Ogawa(3) measured the growth rates of Nd-Fe and Sm-Fe compounds by using Nd or Sm vapor supplied from Nd-Ca or Sm-Ca melts. The authors have also carried out fundamental studies (4)-(8) to clarify the rate and mechanism in the production of R-Fe intermetallic compounds."

Jan 1, 1998

By O N. Antzutkin, W Forsling, K J. Pike an

The adsorption mechanism of three different O,OÆ-di-alkyl-dithiophosphate (dtp) collectors, K[S2P(OR)2] with R = Et, i-Bu and i-Amyl, on the surface of synthetic chalcocite (Cu2S) was studied by means of solid-state 31P CP/MAS NMR spectroscopy. The morphology changes on the conditioned Cu2S surfaces, in the collector concentration range 0.1 - 10 mM, were also monitored with scanning electron microscope (SEM). In order to assign Cu(I)-dtp species on the surface of Cu2S, the corresponding bulk Cu(I)-dtp compounds, which are clusters of the monovalent copper containing either Cu6(antiprismatic) or Cu8(cubic) cores, were synthesised, and characterised by means of solid-state 31P CP/MAS and static 65Cu NMR. Further investigations on the crystal habits of the bulk systems were carried out by powder x-ray diffraction and SEM. A comparative analysis of the 31P chemical shift and chemical shift anisotropy (CSA) data estimated from the experimental NMR spectra of the polycrystalline bulk Cu(I) dialkyldithiophosphate complexes was used for assigning the 31P resonance lines in the NMR spectra of the collector treated Cu2S powder samples. The species formed on the synthetic Cu2S surfaces were assigned to polycrystalline phases of: Cu6L6 with L = Et2dtpû, Cu6L6 and Cu8L6(S) with L = i-Bu2dtpû, and Cu8L6(S) with L = i-Amyl2dtpû. A heterophase autocatalytic step process of both formation and growth of solid CuxLy (L = R2dtp, x = 6 or 8 and y = 6) complexes on the collector treated Cu2S surface is proposed. A possible role of the oxidised form of dithiophosphate collectors, bis[di-alkyl-thiophosphoryl]-disulfane (disulfide), is discussed in terms of a specific self-redox reaction. The second order quadrupolar lineshapes in 65Cu NMR spectra were simulated and the interaction parameters, CQ and hQ, for the bulk dialkyldithiophosphato-copper(I) complexes were obtained.

Jan 1, 2005

By Y. Ide, K. Kishitake

It is expected that an Al-Cr-N composite nitride film may have a higher resistance to oxidation at elevated temperatures than the well-known Ti-Al-N films. The formation conditions of Al-Cr-N films by a de reactive sputtering method and their properties were studied in this study. The films characterized with respect to their high temperature properties such as chemical composition, crystal structure, microhardness, wear and· friction. The crystal structure of the Al-Cr-N films changed from hexagonal phase to cubic phase with an increase in Cr content in the films. The resistivity to thermal oxidation of the Al-Cr-N films is superior to that of usual TI-Al-N films. A half of the friction coefficient in the Al-Cr-N film was obtained comparing with that in the ordinary TI-Al-N film at room temperature and the wear rate of Al-Cr-N film was 2 order smaller than that of TI-Al-N film. The Al-Cr-N films show a small friction coefficient at 500°C and then they are recognized to have good tribological characteristics.

Jan 1, 2000

By M. L. Mahlatji

Mechanical alloying of an equiatomic mixture of crystalline Ti and Pt elemental powders in a high-energy ball mill formed an amorphous alloy by solid-state reactions. Mechanical alloying was carried out in an argon atmosphere at a rotation speed of 1200 r/min and a 20:1 ball-to-powder weight ratio, for time intervals of 4 to 40 hours. At an intermediate stage of mechanical alloying, scanning electron microscopy showed the formation of characteristic layered structures of inhomogeneous composition within the powder particles. X-ray diffraction analysis showed the gradual disappearance of crystalline Bragg peaks and the emergence of broad amorphous maxima as milling progressed. The amorphization process was completed after 8?12 hours. The amorphous state of the product indicated that temperatures during processing did not exceed the crystallization temperature of the alloy.

Jan 1, 2014

By J. D. Budai, D. H. Lowndes, D. P. Norton, D. K. Christen, B. C. Chakoumakos, J. R. Thompson, B. C. Sales

"Artificially-layered structures, consisting of (Sr,Ba,Ca)CuO2 layers in the tetragonal, ""infinite layer"" crystal structure, have been grown by pulsed-laser deposition. Superlattice chemical modulation is observed for structures with SrCuO2 and (Sr,Ca)CuO2 layers as thin as a single unit cell (~3.4 Å). In addition, novel thin film superconductors were formed by using the constraint of epitaxy to stabilize SrCuO2/BaCuO2 superlattices in the infinite layer structure. Using this approach, two new structural families, Ba2Srn-1CUn+l O2n+2+ d) and Ba4Srn-1CUn+3O2n+6+ d, have been synthesized which superconduct at temperatures as high as 70 K. These results represent not only the synthesis of new structural families of superconductors, but also demonstrate that pulsed-laser deposition and epitaxial stabilization can be effectively used to engineer artificially-layered thin-film materials.Advances in the understanding of epitaxial thin-film growth of the cuprates have heightened interest in creating artificially layered superconductors.(1-3) The layered structure of the copper oxide superconductors opens the possibility of forming novel materials by carefully controlling the epitaxial growth of sub-units of the crystal structures. Thin-film growth methods offer unique opportunities for the atomic engineering of new high-temperature superconducting (HTSc) materials through the ability to form artificially layered crystal structures.(4,S) Moreover, the surfaces of single-crystal substrates provide an ""atomic template"" that can be used to stabilize epitaxial films in metastable crystal structures.An important development in forming new HTSc compounds by artificially-layered epitaxy has been the epitaxial growth of (Sr,Ca)CuO2 films in the so-called infinite layer structure.(6-17) This material, which can be considered the parent compound of all of the copper oxide superconductors, has a relatively simple, layered structure consisting of CUO2 planes separated by planes of alkaline earth elements.(18) Bulk synthesis of (Sr,Ca)CuO2 with the tetragonal, infinite layer structure generally requires the use of high pressure and high temperature bulk processing techniques.(19-24) However, recent experiments show that this metastable compound can be epitaxially stabilized at less than atmospheric pressure, resulting in the growth of tetragonal (Sr,Ca)CuO2 single crystal thin films of the infinite layer defect perovskite structure by pulsed-laser deposition (PLD) over a wide range of growth conditions.(6-17)"

Jan 1, 1994

By Masayuki Kudoh, Tohru Maruyama, Yohichi. Ito

When hypo-peritectic carbon steel is quenched during unidirectional solidification, the region of fine columnar grain is observed. It is classified into two coexisting phases. One is coexisting phases of liquid, delta and gamma in the upper part of the region, and the other is coexisting phases of delta and gamma in the lower part of the region. To form the coexisting part of the three phases means that solidification in this experiment proceeds in non-equilibrium state. The size of the narrow side of one fine columnar grain coincides with the arm spacing of a primary dendrite and this result is the same as the hyper-peritectic carbon steel. However, the boundary of the fine grain in the hypo-peritectic carbon steel is formed in different location from that of the hyper-peritectic carbon steel. The former is formed in the skeleton of the dendrite, while the latter is formed in the interspacing of the dendrite. The region of the fine grain changes suddenly to that of the coarse grain when the delta phase in the coexisting part of two phases disappears completely. Therefore, the delta phase in the hypo-peritectic carbon steel might prevent the growth of gamma grain. In order to recognize it, ferrite formers such as Mo, V and Ni are added in the sample. Then, the longitudinal length of the fine columnar grain extends in the sequence of the no addition, Mo, V and Nb.

Jan 1, 2000

By John Cassie

The condition of roadways in the Deep Main seam at Asfordby mine, operated by RJB Mining (UK) Ltd, is strongly dependant on drivage direction relative to the maximum horizontal stress. The mine is laid out with gate roads driven approximately parallel to the maximum horizontal stress giving favourable drivage conditions. This has led to particulary difficult conditions for face installation headings which have to be driven to an increased width and at a high angle to the horizontal stress. A solution to the formation of face headings is described making use of stress relief with the face heading being driven in the zone of reduced stress surrounding a previous heading. In implementing this solution use was made of results from computer modelling and detailed monitoring of roadway behaviour. High reinforcement densities including cable bolts were used in supporting the headings. The experience provides an example of a traditional technique being applied more scientifically. The results obtained demonstrate the effect of stress relief and reinforcement methods in altering drivage conditions and suggest possible alternative strategies for the formation of future face headings in these conditions.

Jan 1, 1997

By James R. Hein

Rodriguez Seamount, located 150 km off the central California coast at the base of the continental slope, was studied using the ROV Tiburon aboard MBARI?s R/V Western Flyer, October 13-16, 2003. Fe-Mn crust and rock samples were collected along the SW flank of the seamount at water depths from 700 to 2100 m; bottom-water dissolved oxygen content (O2) and temperature were determined at each sample site. Fifty-three samples of bulk crusts, crust layers, and surface scrapes (~0.5 mm) were analyzed for 59 elements. Data allow for the correlation of crust compositions with precisely known water depths and seawater O2 measured at the actual site of sample collection. This is the first detailed study of Fe-Mn crust compositions in a region of strong continental-margin upwelling. Compared to open-ocean seamount Fe-Mn crusts, Rodriguez crusts have significantly higher (2-6 fold) mean concentrations of Fe (26.9%), Al (1.65%), Si (13.0%), Cr (82 ppm), Th (64 ppm), and Ag (1.7 ppm); and significantly lower (2-8 fold) mean concentrations of Ca, P, Bi, Co, Cu, Ni, Tl, and especially Te (8.2 times lower). All but one Fe/Mn ratio are >1 compared to <1 ratios for open-ocean crusts. O2 contents (0.35-2.03 ml/L) are nearly perfectly corrected with water depth and elements correlated with one are correlated with the other. The Fe-Mn surface scrapes represent 60-450 ka (mean 150 ka) of growth, whereas the dissolved oxygen contents of seawater represent an instant in time. Assuming that the entire sample set was affected uniformly by oceanographic changes, we suggest that correlation of elements with O2 may reflect oceanographic processes. O2 has a negative correlation with P, V, As, Fe, U, Be, Pb, Cr, Mg, Y, Bi, Te, and REEs (except Ce) and a positive correlation with aluminosilicate-hosted elements (Al, K, Rb, Cs). This later relationship is related solely to water depth, indicating that detritus shed down the seamount slopes accumulates in greater abundances in deeper-water crusts. Si/Al ratios indicate that the detritus includes a large component of biosilica produced by upwelling-mediated high productivity. These observations are supported by positive correlations of aluminosilicate-hosted elements with crust growth rates (range 1.2-13.0 mm/Myr). In contrast, other elements (Sr, Co, Mn, Mg, Te, As, Mo, V, W, U, Ti, Ni, REEs, etc.) are negatively correlated with growth rates. Growth rate has a weak positive correlation with O2. These compositional characteristics indicate that even though low-O2 seawater acts as a reservoir for Mn and associated elements and produces slow growth rates, which would allow for the concentration of elements and surface oxidation processes to occur, the high rate of input of detritus and high bioproductivity ameliorate the strong concentration of most metals. This dilution is significantly enhanced by the doubling of FeOOH in the crusts--the main cause of the generally high growth rates compared to open-ocean crusts. The high growth rates limit the oxidation of Co, Tl, and especially Te on the crust surface, which is reflected by their relatively low concentrations. Within the range of oxygen contents measured, O2 has less of an influence on crust chemistry than does the availability and incorporation of FeOOH and detritus.

Jan 1, 2004

By S Kodate, Ö Aydan, Y Suda, J Tomiyama

Fracture zones are commonly found in the Earth’s crust. These zones may cause very severe engineering problems. Therefore, the formation and the assessment of the mechanical characteristics of these zones is of great concern for rock engineers. A new double shearing jig was used to study the formation of shear zones in rock under static and impact loading conditions using the device developed by the authors. A series of experiments were undertaken to investigate formation on the formation and characteristics of fracture zones in laboratory. Although actual fracture zones are more complicated, various tests give some insight view of the formation of fracture zones as well as some information on their mechanical behaviour under both dynamic conditions and static conditions. The authors report the outcomes of these experiments and discuss their implications in practice.

Nov 29, 2022

By K. Hanumantha Rao, A. Javadi

Our recent studies revealed that the sulfide minerals in contact with water during grinding produced hydrogen peroxide (H2O2) where the amount of H2O2 production by the minerals found to be in the order of pyrite > chalcopyrite > sphalerite > galena. The H2O2 effect on the oxidation of pulp components and its influence on the concentrate grade and recovery in flotation have been studied and the results have been presented and discussed in this paper. Studies have also been carried out to build correlation between percentage of pyrite in the concentrate, grinding conditions and concentration of OH•/H2O2 in the pulp and as well of controlling the formation of these species through known chemical means for depressing the generation of the oxidant. Flotation tests using a complex sulfide ore with the same reagent scheme that is being used at Boliden concentrator in Sweden but with the addition of i) collector and depressant, ii) Na2S reductant and iii) inorganic (EDTA) and organic (TETA) surface modifiers, during grinding stage have been performed to judge the beneficial or detrimental role of H2O2 on the selective flotation of sulfides. The results demonstrate that the selectivity of metal sulfides against pyrite increases with increasing generation of H2O2 in the pulp liquid. H2O2 is also found to be a better oxidant in chalcopyrite-galena flotation separation than the commonly used K2Cr2O7.

Jan 1, 2016

By Isrun Bohlinger

Resources recovery of brasses for semifinished products often results in the formation of hard spots impairing the quality of following abrasive and/or surface finishing processes. A short survey is given on the recycling processes, followed by the actual knowlegde of genesis, composition, and possibilities of avoidance of hard spots. Informations on genesis and composition of hard spots are completed by data from recent experiments.

Jan 1, 1998

By M. Okido, H. Yamamoto, T. Sakamoto, R. Ichino, K. Kuroda

"Hydrogen absorption alloy films have been produced by molten salt electrolysis. Lanthanum-Nickel alloy film can be formed on a nickel substrate in KCl-NaCl-LaCb molten salts by electrolysis diffusion process. LaNi5 alloy was formed by mutual diffusion between La ·and Ni after La deposition on Ni substrate. Though several kinds of La-Ni compound existed in deposits, the alloy compounds on Ni substrate changed by electrolysis condition. According to the open-circuit potential measurement in molten salts after La electrodeposition, the formed compounds had a relation to the potential. In the case of the substrate electroplated a cobalt thin film on nickel, LaNi4_5Co0.5 was formed by the electrolysis in the molten salts with lanthanum ions. This ternary alloy film showed better hydrogen absorption behavior in cyclic charge/discharge test in alkaline solution.IntroductionHydrogen storage alloys have attracted attention as the active materials for batteries with the charge/discharge property at ambient temperature. The alloy of nickel and misch metal, mainly consisting of La and Ce, has been commercially 'used as a metal hydride with rechargeable property. In recent years, researches have been developed many kind of new alloys with better hydrogen absorption properties. The hydrogen absorbing alloy ingots are commonly produced by melting method of both metals in furnace, otherwise, prepared by mechanical grinding and metallurgical sintering technique with metal powders. The film is also made by vapor-phase techniques such as sputtering method, ion plating method, etc. ·We have proposed a new method to produce hydrogen absorbing alloy films by molten salts electrolysis technique [1-3]. The hydrogen absorbing film, LaNi5, Mg2Ni and CaNi5, were obtained in this process through controlling the electrolytic condition. The active metals, La, Mg and Ca, are electrodeposited on Ni substrate, diffuse into the substrate and form various kinds of intermetallic compounds. This technique provides a direct process using metal chlorides as resources to produce functional films without using active metals such as La, Ca and Mg."

Jan 1, 2000

By K. Hanumantha Rao, A. Javadi Nooshabadi

"Formation of hydrogen peroxide (H2O2), an oxidizing agent stronger than oxygen, by chalcopyrite (CuFeS2), which is a copper iron sulfide mineral, during grinding, was investigated. It was observed that chalcopyrite generated H2O2 in pulp liquid during wet grinding and also in the solids when placed in water immediately after dry grinding. The generation of H2O2 during either wet or dry grinding was thought to be due to a reaction between chalcopyrite and water where the mineral surface is catalytically active in producing •OH free radicals by breaking down the water molecule. The effect of pH in the grinding medium or in the water in which solids are added immediately after dry grinding showed that the lower the pH value, the higher the H2O2 generation. When chalcopyrite and pyrite are mixed in different proportions, the formation of H2O2 was seen to increase with increasing pyrite fraction in the mixed composition. The results of H2O2 formation in pulp liquid of chalcopyrite and together with pyrite at different experimental conditions have been explained by Eh-pH diagrams of these minerals. This study highlights the necessity of revisiting the electrochemical and/or galvanic interaction mechanisms between the chalcopyrite and pyrite in terms of their flotation behavior.IntroductionHydrogen peroxide causes nonselective oxidation of sulfide minerals if present in pulp liquid. Oxidation of sulfide minerals takes place when they are exposed to atmosphere and during the grinding process when the particle size is reduced for flotation. The oxidation of chalcopyrite leads to iron dissolution from the particle surface and from a metal-deficient, sulfur-rich surface (Fairthorne et al., 1997). Other studies report the formation of iron hydroxide on the surface with the metal ion dislodged on the surface (Buckley and Woods, 1984; Chander, 1991). The chemical reactions for the oxidation of chalcopyrite in alkaline and in acidic solutions with the addition of oxidants, such as oxygen or hydrogen peroxide, are shown in Eqs. (1) and (2), respectively (Shi and Fornasiero, 2010)."

Jan 1, 2015

By Walter Crafts

ALTHOUGH many elements reduce the tendency to porosity in steel castings, manganese, silicon, aluminum, calcium, titanium and zirconium appear to be most generally suitable for the purpose. The manganese and silicon contents are usually maintained in a fairly constant range. Sili-con-killed castings often are made to be sound with little or no addition of the stronger degasifiers. In many cases, however, it is more practical to utilize the stronger degasifying elements, aluminum, calcium, titanium and zirconium. Since they greatly modify the composition, shape, and distribution of the nonmetallic inclusions, and thereby the ductility, the strong deoxidizers must be used in such a way as to form the least harmful types of inclusions. As the reasons for failure always to obtain good results have not been obvious, an effort has been made to determine the mechanism of solidification of steels deoxidized to produce certain types of inclusions. Diagrams representing the mechanism of their formation have been constructed from the appearance of the nonmetallic con-stituents and have not only illustrated the limiting features of specific deoxidizing treatments with respect to inclusion formation and ductility, but have also indicated a relation between inclusions and resistance to hot tearing. Three different types of deoxidation treatment have been used for obtaining sound castings with relatively high ductility. The first method is to make and cast the steel under such conditions that deoxidation with silicon and a small addition of a strong deoxidizer assures soundness. The effective addition that will promote soundness without causing the formation of intergranular inclusions varies with the furnace practice and composition, but may be limited to about 0.025 per cent Al, Zr or Ti. Up to 0.10 per cent Ca and 0.15 per cent V are also used for this purpose. The inclusions in these steels are characteristically glassy silicates and round or irregular sulphides. As pointed out by Sims and Lillieqvist,1

Jan 1, 1940

By H. R. Hanley

IT is a well-known fact that the solubility of zinc compounds decreases when these compounds are roasted in contact with iron compounds, but descriptions of tests to quantitatively express the fact have not appeared in the literature. Possibly such an expression cannot be uniformly and exactly duplicated by different operators because of the variation in the personal equation. In a general way, however, the reactions between zinc compounds and iron compounds under roasting conditions will show a certain trend with changing conditions and the approximate quantitative expression of this trend appears reasonably well established by experimental work conducted for this purpose.

Jan 1, 1929

By Chu E. Ho

Jet grout column formation at large depths are prone to several uncertainties, such as inaccuracy in setting out boreholes, drilling deviation, soil variability and reduced jetting energy at the nozzle. This would result in shorter cutting distance of the jet, with potential lack of interlock between grouted columns. A design strategy for mitigating the risk should include a soil investigation program aimed at discovering potential variability in soil conditions at the locations of jetting. Determination of soil strength profiles with depth would be useful for evaluation of jetting parameters and prediction of the achievable cutting distance at any depth. Selection of design column spacing should include allowance for setting out accuracy, verticality of the boreholes and the achievable jet cutting distance. For deep jet grouting operations, it would be necessary to take into account the energy losses at the nozzle inlet; however the increase in the presiding pressure at the nozzle outlet at depth is small relative to the range of jetting pressures commonly employed and would not affect the cutting distance to any significant degree. Design column spacing should not be so close as to cause problems with ?masking? which may lead to localized ungrouted zones of soil. For effective field control, boreholes should be cased up to the top elevation of the grouted zone so that the orientation of the borehole can be measured prior to grout injection. An analytical equation for calculating the cutting distance is proposed for adjusting jetting parameters where necessary to compensate for drilling deviation and changes in soil conditions. It is preferable that jet grouting trials be executed at elevations that correspond to the actual production jet grouting depths for accurate evaluation of jet cutting performance.

Jan 1, 2008