Search Documents

By H. Y. Yang, L. L. Tong

For gold recovery, a Chinese refractory, high-sulfur gold concentrate was subjected to biooxidation with high pulp density in a single stirred-tank reactor. The flotation concentrate contained 36.9 percent sulfur (S) and 33.9 percent iron (Fe). Different experimental regimes for biooxidation were applied. With a mixed culture and by controlling the amount of addition of the gold ores and the pH of the biooxidation system, maximum iron oxidation of 82.6 percent and sulfur oxidation of 79.3 percent were achieved. The experimental results indicate that the pH control was beneficial to the biooxidation of this concentrate. Approximately 28.4 percent of elemental sulfur (S8) was found in the oxidizing slags. Two dissolution mechanisms of elemental sulfur are proposed: (1) FeS2 → S80 → S2O32− → SO42− and (2) FeS2 → S80 → SO42−. The high pH had a positive effect on the reduction of the S8. The results of thermodynamic analysis indicate that as an oxidant the dissolved oxygen can effectively reduce the Gibbs free energy of the pyrite oxidation process and, compared with the reaction of ferric iron as the single oxidant, the oxidation of pyrite is easier. The efficiency of the gold recovery was related to the iron oxidation as well as the sulfur oxidation. Gold and silver recoveries of 92.4 percent and 66.4 percent, respectively, were achieved.

By A. Jafarnia

Aluminum alloys are frequently grain refined during solidification in order to promote the formation of an equiaxed grain structure in the casting. The application of Ti-based grain refiners and/or Ti containing master alloys for improving mechanical properties may result in formation of Al-Ti based intermetallics. Although the grain refinement produces many desirable qualities in aluminum castings such as improved castability and mechanical properties, the addition of Ti to Al-Si foundry alloys may lead to the formation of some undesirable intermetallic particles such as AlTiSi and cause a number of operational problems such as nozzle blockage due to segregation and agglomeration of aluminide particles within the nozzle. There are several questions to be clarified when minor amount of Ti is added to Al-Si alloys. They include nucleation and growth of AlTiSi particles, their morphologies and orientation relationships with aluminum matrix and the dissolution of these intermetallics during the course of solidification and/or post solidification treatments. The current study was initiated to study the process and possible mechanism of aluminide dissolution and the related phenomena such as segregation and agglomeration. It reports the results found during reheating of laboratory prepared Ti-added A356 alloy at three temperature ranges of below solidus, mushy zone and above liquidus.

Jan 1, 2004

By W. D. Cho

The slag chemistry in steel processing plays an important role in terms of the removal of impurities including alumina particles. In the present study, the dissolution of solid alumina particles in CaO-based fluxes at the temperatures between 1450 and 1550 °C has been investigated to determine dissolution kinetics and mechanism. Alumina particles were added directly in the slags and the size of alumina particles was measured as a function of time using optical and scaru;ling electron microscopes. The dissolution rate has also been obtained as a function of Si02, CaF2, MgO and MnO contents in the slags. The diffusion boundary layer between alumina and bulk slag phase has been observed and analyzed using SEM and EDX. In addition, some experiments have been performed for the dissolution of alumina in BaO-based fluxes.

Jan 1, 2003

By W. D. Cho

The slag chemistry in steel processing plays an important role in terms of the removal of impurities including alumina particles. In the present study, the dissolution of solid aluimina particles in CaO-based fluxes at the temperatures between 1450 and 1550 °C has been investigated to determine dissolution kinetics and mechanism. Alumina particles were added directly in the slags and the size of alumina particles was measured as a function of time using optical and scanning electron microscopes. The dissolution rate has also been obtained as a function of Si02, CaF2, MgO and MnO contents in the slags. The diffusion boundary layer between alumina and bulk slag phase has been observed and analyzed using SEM and EDX. In addition, some experiments have been performed for the dissolution of alumina in BaO-based fluxes.

Jan 1, 2003

By Mandira Madhuchhanda, N. B. Devi, P. C. Rath, R. K. Paramguru, K. Srinivasa Rao

An experimental investigation of the dissolution of three base-metal sulfide minerals, namely, CuFeS2, ZnS and PbS, in hydrochloric acid medium in the presence of manganese dioxide is reported. Polarization measurements and leaching studies were employed in the study. Dissolution occurred in the following three ways: by the cyclic action of the Fe3+/Fe2+ redox couple, by galvanic interaction between Mn02 and the sulfide minerals, and because of chlorine evolution from the system. The later two routes were found more effective at higher HCI levels. PbS appeared to be oxidized easily, whereas CuFeS2 was the most difficult to dissolve. ZnS dissolution fell in between PbS and CuFeS2.

Jan 1, 2002

By Jonkion M. Font

As a comprehensive contribution to the understanding of oxygen-blowing of matte smelting, the copper and nickel solubilities between the FeOx SiO2-MgO slag with saturated SiO2 and the Cu2S-Ni3S2 FeS matte with the NCu/(NcU+NNi) of 1, 0.75, 0.5, 0.25 and 0, in a MgO crucible were investigated at 1573 K under controlled partial pressures of SO2 at 0.1, 0.5 and 1 atm. The partial pressures of SO2, S2 and O2 were controlled by using an Ar-SO2-S2 gas mixture after passing through a sulfur reservoir. It was clarified that, at a given matte grade, the solubility of copper in the slag was independent of pso2 while that of nickel increased with increasing pso2. This notable difference was considered to be ascribable to the chemical formulas of the mono-metallic sulfides in which one copper atom combines with ½ sulfur atom while one nickel atom combines with 2/3 sulfur atom. It was also clarified that, at a given iron content in the matte, the pot and ps2 were independent of the matte species. This was ascribable to aFeS in the matte, which was independent of the matte composition, Ncu/(Ncu+NNi), at a given iron content in the matte.

Jan 1, 1999

By G. T. Lapidus, O. J. Solis-Marcial

Currently, ores with high-grades of copper oxides and secondary sulfides have become increasingly scarce, which has encouraged industry to look for alternative raw materials to obtain copper. The problem is that primary sulfides are difficult to dissolve at near ambient conditions. Proposed hydrometallurgical processes have not been implemented beyond a pilot or demonstration scale. One of the principal disadvantages is that the majority of these processes are not viable with ores that contain less than 4% copper. One of the more recently proposed techniques involves the use of organic solvents in the dissolution of copper concentrates with a chalcopyrite content of between 20 and 30%, which has shown high efficiency. The present research explores the ability of this process to leach copper from low grade chalcopyritic ores (<4% Cu) at different temperatures ranging from 20 to 50°C. It was found that depending on the temperature, high percentages of copper were extracted in 40 to 100 minutes, using different oxidants. Additionally, distinct leaching behavior was observed with each oxidizing agent. In some cases, the extraction kinetics adjusted to the diffusion controlled shrinking core model.

Jan 1, 2014

By Jimbo I, Ogawa O

A series of experiments was carried out to investigate the solubilities of copper, arsenic, antimony and bismuth in silica-saturated iron silicate slags under controlled oxygen partial pressures at 1200 and 1250¦C. Molten copper containing each of the above elements was kept in contact with a slag in a silica crucible for 24 or 48 hours to attain equilibrium. No me- chanical entrapment of metal into the slag was observed. The appearance of the magnetite phase in the slag was avoided by holding oxygen potentials at substantially lower values than that evaluated from available data on iron silicate slags. Solubilities of copper, arsenic, antimony and bismuth in slags were plotted against oxy- gen potentials and both oxidic and atomic types of dissolution were found, except in the case of arsenic, from the dependencies of the solubili- ties on the oxygen potential and from positive intercepts of regression lines when extra- polated to zero oxygen potential. The dissolu- tion of arsenic seemed mostly oxidic. Distri- bution coefficients of arseò,ic, antimony and bismuth between copper and slag are also Discussed.

Jan 1, 1980

By Jogre A. S Tenório

he aim of the present investigation was to investigate technological features of the Fe-NbC dissolution in liquid Fe-C alloys. Fe-NbC is a Ferro-niobium alloy with 7%C, has a particle size smaller than 150 pm and its micro constituents are polygonal niobium carbides and an iron matrix. The obtained dissolution time was less than one-minute and the yields were in the range of 80-90% at 1873 K. In the Fe-NbC dissolution process, the dissolution occurs at first, and as a consequence the niobium carbides become free to dissolve. These carbides will dissolve until the melt reaches a saturation point. The non-dissolved carbides remain trapped in the liquid or will form a dross. The addition yields decreases when the niobium concentration reaches this limit value, that depends on the carbon concentration. These define a saturation curve.

Jan 1, 1994

By Batric Pesic

Recovery of gold from refractory ores was studied by pressure oxidation as the method of ore pretreatment followed by bromination of oxidized residues. Three different ores were examined, Au-Ag, Au-Ag-Te, and Au-silver free ore. Pyrite was the major host mineral for gold in these ores. The effect of pressure oxidation parameters (temperature, pressure of oxygen, time, and pulp density) on subsequent bromination under standard conditions was examined. Bromination of residues produced under standard pressure oxidation conditions was examined as a function of: temperature, bromine and sodium bromide concentration, and time. Recovery of gold on activated carbon, from the pulp after bromination, was studied too. Recovery of gold from silver containing ores was lower (87-91%) than the recovery of gold from silver free gold ore (97%). In each studied case, the presence of activated carbon in the pulp further increased the recovery of gold.

Jan 1, 1992

By H. Kaffash

Ferromanganese is a ferroalloy with high manganese content which finds many uses for example as deoxidizer in steelmaking industry. However, there is very little data on the dissolution rate of carbonaceous materials in Mn containing metals. In this paper, the kinetic analysis of carburization reactions is investigated for Mn–Fe alloys. Dissolution rate of graphite in pure iron and four different alloys with 10 wt%, 40 wt%, 60 wt% and 85 wt% manganese at 1823 K was studied. Results showed that the dissolution rate of carbon from graphite increased with increasing time for all alloys. The dissolution rate constant increased with the increasing manganese content from 6.5 × 10−3 cm/s for 0%Mn to 23.6 × 10−3 cm/s for 85%Mn.

By M. Clotilde Apua, A. F. Mulaba-Bafubiandi

"The efficiency of hydrochloric acid (HCl) leaching of gold from low grade gold-bearing material has been investigated in the presence of sodium hypochlorite (NaOCl) to produce in situ chlorine gas which is an oxidizing agent able to oxidize gold metal to its soluble forms. The effect of concentrations of HCl, NaOCl, and mixtures of HCl + NaOCl was sought. Iron and potassium present in the feed were leached and consumed all the HCl. Gold found as inclusion in pyrite was not exposed to the lixiviant. Therefore, leaching of gold from low grade gold-bearing material in aqueous chlorine solution is not an effective process for now.INTRODUCTIONHydrometallurgy of gold is commonly based on cyanide leaching solution. Due to the environmental concerns related to cyanidation and mercury processes, and inefficiency of cyanide gold leaching to dissolve refractory ores, sustainable alternative lixiviant systems, capable of generating gold (I) and gold (III) complexes must be studied. Amongst non-cyanide gold lixiviants there is the chloride/chlorine system (Hilson and Monhemius, 2006; Senanayake, 2004; Pilsniak and Trochimczuck, 2007; Wang et al., 2007; Reeves et al., 1999; Khodadad et al., 2008).In practice, the most oxidizing agents utilized for the leaching of gold as chloride, are chlorine (Cl2) or hypochlorite (HOCl) which are either generated in situ by suitable reaction or added in solution (Adamson, 1972). The dissolution of gold concentrate using hydrochloric acid, sodium chloride and sodium hypochlorite (Cl-/HOCl system) were studied (Puvada and Murthy, 2006). The effect of NaOCl and NaCl concentrations were also investigated. The leaching was performed under the following conditions; time: 4h, solid–liquid ratio = 1:4, at room temperature. It was found that the increase of the NaOCl concentration from 25 to 75 g/L did not have any meaningful effect on the recovery of gold which was about 30% (experimental conditions; S/L ratio = 1:4, NaCl concentration: 25 g/L, HCl concentration: 0.35 M). It was also found that from 25 g/L to 200 g/L NaCl, the recovery of gold rose from 30% to 40% (experimental conditions; S/L ratio: 1:4, NaOCl concentration: 25 g/L, HCl concentration: 0.35 M)."

Jan 1, 2012

By Mur D. M

Metal ferrites are formed by the high temperature reaction of various metal oxides with hematite and are commonly found in the calcines derived from the sulfation roasting of zinc, copper and nickel sulfide concentrates. The Jarosite Process is designed to treat such zinc ferrites by hot acid dissolution but little information is available on the basic reactivity of various ferrites and the effect of Eh. As part of an overall study of the reactivity of calcine products from copper and nickel sulfide concentrates it has been found that Eh plays an important role in the rate of dissolution of magnetite, hematite and nickel oxide by HC1 and H2SO4. Further studies on the reactivity of pure synthetic copper,zinc,and nickel ferrites also show a dependence on Eh. This paper discusses the relative reactivity of iron oxides and metal ferrites in 1 M HC1 and the results of electrochemical studies using cyclic voltammetry. A mechanism for the dissolution reaction is proposed as well as factors which determine their leaching. It is shown that the rate of leaching of metal ferrites with HC1 is enhanced in the presence of reducing agents such as Cu(I) and Sn(II). By contrast the leaching of NiO is enhanced by oxidising agents such as Cu(II).

Jan 1, 1987

By Kenneth N. Ham

Hydrometallurgy covers a wide spectrum of areas and its knowledge base is enlarged and enhanced by contributions from many other fields. Dissolution of metals and alloys in aqueous media will be used to illustrate how rich the field of metal extraction can be. Comprehensive understanding of the fundamentals of metal and alloy dissolution in aqueous systems requires creative application of thermodynamic principles, solutions chemistry, ligand complexation theory, electrochemistry, transport phenomena and heterogeneous kinetics. In addition, recent developments in instrumentation in the fields of interfacial phenomena and corrosion have tremendously advanced the field of metal extraction in aqueous system. The close relationship between metal extraction in aqueous systems and various physicochemical phenomena occurring in corrosion and interfacial systems will be discussed and illustrated with examples.

Jan 1, 2002

By R. C. Hubli

Copper (II) chloride has proven to be an efficient lixiviant for copper sulphide ores and secondary sources of copper such as scrap. Nickel sulphides are generally associated with copper ores and copper-nickel matte is an intermediate product of processing mixed sulphides. While the copper species in aqueous chloride media are present as chlorocomplexes, the presence of nickel as Ni++ offers effective separation between the two by solvent extraction techniques. Oxidation of millerite by cupric chloride in sodium chloride solutions has been studied as a function of rate of agitation, leaching time, temperature, acid concentration and total initial cupric concentration. The reaction has a 1/2 order of dependence on initial cupric concentration in the range of 0.0 to 0.5M. The activation energy for the temperature range 333 -363 K has been found to be 59.2 kJ/mol with chemical reaction at the unreacted mineral surface as the rate controlling step. The rate expression, according to the shrinking-core model, for initial cupric concentrations between 0.0 to O.5M, is evaluated as

Jan 1, 1996

By R. C. Hubli

A panial equilibrium model? to simulate the dissolution of millerite (NiS) in aqueous solutions containing copper(II) chloride as the oxidizing species has been developed. The predominant copper(I) and copper(II) species are CuQ3 and CUO2 respectively. The model computes the initial concentrations of the species present in the aqueous phase under the specified input conditions, prior to the simulation of dissolution. During the dissolution of millerite, nickel enters the leach liquor as NiH and it has been found that the H+ decreases as a function of NiS dissolution. The simulation has been accomplished under conditions prevailing during actual dissolution, with only one mineral undergoing dissolution. The model can be applied for the simulation of co-dissolution of two or more sulfides. Under the given conditions, the precipitation of Cu1(OH»)O is negligible but loss of Cu(1l) could be significant if the initial H+ is lower than 0.03 M. The results of the simulation compare favorably with experimental observations.

Jan 1, 1996

By Muammer Kaya, Sait Kursunoglu

"The aim of this study was to investigate the effectiveness of ascorbic (C6H8O6) / oxalic (C2H2O4) acid as a reductant for the simultaneous recovery of zinc and manganese from a spent and mixed zinc-carbon and alkaline battery powder in sulphuric acid leaching. The effects of sulfuric acid concentration, ascorbic/oxalic acid dosages, reaction temperature and leaching time on the zinc and manganese dissolutions were investigated according to 2k full factorial experimental design; then, a simple optimization study was carried out for the best reductant. The optimum reductive acid leaching conditions were determined at 3 hours leaching time, 70°C leaching temperature, 0.5M sulfuric acid concentration, 13 g/L ascorbic acid dosage, 1/20 g/mL solid/liquid ratio and 200 rpm stirring speed. Under these conditions, the dissolution efficiencies were 99.9% for Zn and 99.3% for Mn. When our results were compared with the previous results, our findings were better than previous studies.In addition, the manganese dissolution kinetics was undertaken, and the activation energy was found to be 7.04 kJ/mol. Selective precipitations of Zn and Mn from acid solutions were carried out using NaOH and KOH. Using 3M NaOH as precipitating agent at room temperature and at pH 8; 95.4% of Zn and at pH 10; 93.7% of Mn were precipitated from the leaching solution. Under the same conditions, using 3 M KOH at pH 8; 91.6% of Zn and at pH 10, 96.4% of Mn were precipitated. Based on the experimental results obtained, an appropriate flow sheet was proposed to recover zinc and manganese."

Jan 1, 2012

By Toru Taniguchi

In the Mitsubishi smelting furnace, copper concentrate, silica sand and water granulated slag from the converting furnace are injected through the process lances, together with oxygen enriched air, into the melt. Because bath smelting is used, the rates of particles/melt and gas/melt reactions are high enough and therefore tine grinding of the solid materials is&apos; not necessary. Among these reactions, the dissolution rate of silica sand is the slowest and limits the overall reactions in the smelting furnace. Information on the dissolution rate of silica sand plays an important role for design of a new furnace. Theoretical calculations of the dissolution rate .of silica particles have been reported elsewhere. The authors conducted cold model experiments and could verify the calculation. In this paper, the dependence of dissolution rates of particles on the gas blowing rate, particle size and solid penetration depth in the bath is discussed.

Jan 1, 2002

By Denholm WT

The main objective of the experimental study was to investigate the dissolution kinetics of various forms of carbon under iron bath converting or smelting-reduction conditions, i.e., particulate, free moving carbon in contact with a turbulent iron melt. Iron/carbon melts were contained in cast magnesia-lined silicon carbide crucibles heated by a medium frequency induction furnace. The melts were stirred by injecting nitrogen through 2 mm I.D. alumina lances submerged to a depth of 50 mm in the 100 mm deep baths. Particulate carbon in the form of graphite, brown coal char and petroleum coke, were dropped directly onto the turbulent bath. The dissolution rates of the various carbon types were monitored by taking periodic bath samples for subsequent carbon analyses. The effect of carbon particle size (1-6.25 mm), the degree of bath turbulence (nitrogen stirring rates of 0-20 litres/min), and bath temperature (1300-1500¦C) were assessed. The analysis of the results was complicated by particle buoyancy effects, but it was established that the dissolution rates of the three carbon types investigated were similar, and increased linearly with increases in the gas stirring power inputs. Particle size had relatively little effect on the dissolution rates.

Jan 1, 1984

By Luiz A. Teixeira

A process is described whereby worn, deffective or crystallized photoconductive Se-As layers can be stripped off from aluminium photocopier drums, using hydrogen peroxide solutions in conditions such that the aluminium substrate is preserved from chemical attack. The process allows the stripped drum to be recoated with a new photoconductive layer, and to be put again in use.

Jan 1, 1990