By R. I. Jaffee, J. G. Dunleavy, W. Hodge, H. R. Ogden

Jan 1, 1949

By J. W. Craig, H. L. Walker

Industry has for many years recognized the dependence of certain mechanical and physical properties. as well as workability, upon grain size variations in brass. Although the dependence of properties upon grain size has been recognized there are not many instances where a planned program of testing has been conducted and where the only intentional variable has been grain size. In particular the literature is limited with respect to the effect of grain size on the endurance limit, though there are many industrial applications where the brasses are subjected to cycles of repetitive stresses. Literature A number of the physical and mechanical properties of a given brass sheet, in the annealed condition, will depend upon: (I) The ready-to-finish grain size before final rolling, (2) the percentage deformation by cold working, and (3) the time and temperature of annealing. The first and second variables affect the recrystallized grain size, and the third variable affects the coalesced grain size. Gibbsl has shown the effect of two different ready-to-finish grain sizes upon the tensile strength and hardness of deep drawing brass strip after a definite amount of cold rolling. The smaller the ready-to-finish grain size, the higher the tensile strength and hardness, but with lowered ductility, Gibbs also demonstrated, for a given time and temperature of anneal, that the tensile strength, hardness, and elastic limit are higher for the smaller ready-to-finish grain size, but the elongation is lowered. Townsend and Greena112 have reported data which show that cold working increases the tensile strength, hardness, and load carrying ability of deep drawing brass sheet under reversed stress. Greenall and Gohn3 have reported data which show that the smaller grain sizes have higher tensile strength and hardness properties, and the data also show that increased cold working increases the tensile strength and hardness properties of deep drawing brass sheet. Kommers4 has reported data for tests of brass of known ready-to-finish grain size, a specific amount of cold reduction, and annealed at different temperatures above and below the recrystallization temperature. Kommers' results indicate that annealing below the recrystallization temperature does not change the tensile strength and hardness properties, but the endurance limit may be increased from 22,000 to 28,000 psi. The increased endurance limit is explained as resulting from the reduction of internal stresses by a stress-relief anneal. Burghoff5 and associates have reported data on creep tests, over

Jan 1, 1949

By J. B. Newkirk, A. H. Geisler

Certain of the permanent magnet alloys provide ideal systems for the study of the kinetics of the precipitation reaction and the correlation of structure with properties. One such system, Cu-Ni-Fe, was found by Bradley1,2 to exhibit a coherent transition state in the precipitation process analogous to that reported for Al-Cu alloys somewhat earlier.3 The attractiveness of some perrnanent magnet alloys for study lies in the fact that vertical sections of the ternary phase diagram in certain regions of composition (Fig I) have as their prototype the binary Ni-Au diagram. Alloys of this type decompose into products that have the same crystal lattice type but only slightly different lattice parameters. The advantages that such alloy systems oA&apos;er for study over the usual in which an intermetallic compound is formed are many: 1. Since the precipitate has the same crystal strutture as the matrix, complex atomic movements are not required to form the new lattice. 2. Similarly, complex orientation relationships are not involved for both the matrix and the precipitate would be ex. petted to have the same orientation. 3, Small &,registry of the decomposition products at equilibrium (in contrast with Cu-Ag alloys) is conducive to extensive coherent growth in the transient state and thus the transition lattice can be detected by the usual X ray diffraction methods. 4. Finally, the relative quantities of precipitate and depleted matrix can be varied from 0 to 100 pet* thus permitting wide freedom for the study of the effect of cornposition on coherent growth and properties. In the Cu-Ni-Fe alloys of appropriate composition, the face-centered cubic precipitate and also the depleted matrix when first formed are coherent with the parent matrix.1&apos;2 The two have the same <Jo parameter as the original matrix but they are both tetragonal; the precipitate has an axial ratio c/a < I while that of the depleted matrix is c/a > I. When coherency is lost they assume the normal face-centered cubic structure with the depleted matrix having a lattice parameter greater than the original matrix and that of the precipitate less. Such a mechanism would also be expected for CU-Ni-CO alloys because of the similarity in constitution but this had not been demonstrated. The Present investigation was conducted on a CU-Ni-CO alloy. The constitution diagram and magnetic properties of these alloys have been fairly well established, however, no previous determinations of mechanism of precipitation and no correlation of structure with properties had been made. Thus, an alloy of this system Was chosen for a comprehensive investiga-

Jan 1, 1949

By R. P. Carreker, J. G. Leschen, J. H. Hollomon

The external appearance of a crystal which has undergone plastic flow suggests that adjacent blocks of the crystal have glided bodily past one another along the slip planes. However, the great discrepancy between the shear stresses calculated to effect such a movement and those actually observed has for many years stimulated searches for more satisfactory interpretations of the slip process. Appreciable success in these efforts has been realized by assuming the presence in the crystal of various sorts of imperfections and by considering the consequences of the presence of these flaws when stress is externally applied. The theory that has received the most attention recently—that of dislocations—postulates the occurrence of small, mobile imperfections or dislocations which move through the crystal along the slip direction, each dislocation being attended by a local shear displacement of one interatomic distance. Thus only that portion of the crystal through which the dislocation has passed may be said to have slipped. Since each dislocation produces a displacement of only one interatomic distance, an avalanche or train of many dislocations would be necessary to account for the observed displacements of several hundred or thousand interatomic distances. The salient point of the theory of dislocations is the concept that a slip band does not suddenly appear in its entirety. On the contrary, it grows progressively across the slip plane as the individual dislocations successively appear and advance in a train through the crystal. However, the concept of growth is not intrinsic only to the theory of dislocations, since atomistic mechanisms other than that postulated by the dislocation theory can quite probably also describe the growth of a slip band. For instance, a slip band might resemble a disc-like interface that appeared and then grew continuously from a small size, producing a displacement that increased with the size of the disc. Whatever the precise mechanism, the concept of growth is in itself consistent both with the observed low values of critical shear stress and with the experimental observation that slip bands frequently do not traverse the entire crystal. The likelihood that slip bands grow implies that they must first be nucleated and that the initiation of slip can therefore be analyzed in terms of the general concepts of nucleation. Indeed, this suggestion was advanced1 several years ago, but the matter does not appear to have been further pursued. Recent advances in the theory of nucleation 2,3,4 have encouraged such a treatment of the slip process. As will presently be demonstrated, this approach to the problem not only accounts successfully for the incubation periods that have been observed 5,6 to precede slip but also predicts certain transient effects in the deformation process. The existence of these transients apparently has not hitherto

Jan 1, 1949

By W. R. Hibbard

The increased strength of a polycrystal-line metallic aggregate compared with that of its individual crystals generally has been associated with complex stress distributions at the grain boundaries resulting from atomic irregularity between grains. This disregistry, together with the necessity for adjacent crystals to deform compatibly regardless of the single crystal crystallo-graphic strain mechanism, complicates this mechanism so as to increase the metal&apos;s resistance to deformation. Although Taylor1 has shown from purely mechanical considerations the requirement for at least five active slip systems to absorb the complexities during the homogeneous deformation of polycrystalline face-centered cubic metals, experimental studies by Barrett and Levenson2 indicate that this is feasible only in a qualitative sense because of deviations from homogeneous deformation. Seitz and Read in their review3 state: " Unfortunately . . . present knowledge of the grain boundary influence is not sufficient to complement the work in single crystals and provide us with a good foundation for treating polycrystals." The purpose of this investigation was to attempt to clarify the gap between single crystals and crystalline aggregates by an analysis of the effects of dcformational stresses. Some of the results were described by C. H. Mathewson in his 1943 Campbell Memorial Lecture.zl Previous Investigations Since the performance of single crystals deformed under pure stresses has been relatively thoroughly investigated, the most significant researches are concerned primarily with deviations from single crystal behavior of large grained specimens. Qualitative grain boundary effects involving the observed amount of slip werc reported by Carpenter and Elam5 in 1921. Individual crystals in a two or three grained aluminum specimen deformed by tension acted in the normal manner described by Taylor and Elarn4 except for marked modifications at the grain boundaries. There the power to withstand deformation was considerably increased, leaving a ridge on the specimen where decreased slip occurred, often noticeable yi in. from the boundary. Adcock,6 Yamaguchi,&apos; Seumel, Hirstg and others have also reported this phenomenon as a qualitative trend. Yet attempts by O&apos;Neill&apos;o and Ljunggrenll to measure a difference in hardness at grain boundaries in undeformed specimens were unsuccessful. Miller12 measured quantitatively the reduction in slip near the boundary between the single crystal and polycrystalline areas of zinc specimens. These effects consisted of two parts: I. Next to the polycrystalline interface thc distribution of stresses was so altered

Jan 1, 1949

By J. E. Burke

Recent investigations have elucidated many of the phenomena of the grain growth process, but have also revealed some conflicting and unexplained results. Beck and his co-workers 1,2,3 have shown that grain growth continues with continued heating at one temperature until the average grain size approaches the thickness of the specimen. Plotting the logarithm of the average grain diameter, D, against the logarithm of the annealing time, t, they find the straight line relationship given by the equation: D = Ktm [,] with possible small deviations at short annealing times. K and n are constants at constant temperature. On the other hand, Wa1ker4 finds that, in alpha brass) the rate of growth falls off more rapidly than indicated by Eq i after long annealing, so that an equilibrium grain size is approached. Burke5 showed, using Walker&apos;s data, that time and temperature for grain growth are apparently related through an activation energy, H, according to the relationship: ] where h and tz are the annealing times necessary for the average grain size to increase from Do to D at temperatures T1 and T2 and R is the gas laws constant. In the case quoted, H had the value 60,000 cal per mol. The apparent validity of this relationship, at least up to 700°C, and the approximate value of H were later confirmed by Beck3 The results obtained by Beck Kremer, Demer and Holzworth2 for aluminum and aluminum-magnesium alloys could not be satisfied by such a relationship, since the slope of the isothermal curves increased with increasing temperature. These data indicate and Beck, Holzworth and HuV ater demonstrated expcrimentally that the only apparent factor controlling the rate of grain growth at constant temperature is the grain size. While many of the phenomena have been elucidated, a reasonably quantitative explanation of the process is lacking. There exists uncertainty even as to the primary driving force for grain growth, although there is a considerable body of indirect evidence that the interfacial energy of the grain boundary is responsible.7,8,io Making implicit use of this assumption, several authors14,16 have pointed out that grain boundaries should migrate toward their center of curvature. Harker and Parkerg have advanced this concept furthest, and show that one can expect grain boundary migration to occur only when the grain faces are curved, or when they meet at non-equilibrium angles. When the face is curved toward a grain A, for example, the atoms in the surface of grain B, on the other side of the boundary7 are on the average more surromded by the atoms of their lattice than the atoms on the surface of grain A. Because of thermal motion, the atoms at the interface will sometimes be attached to grain A and

Jan 1, 1949

By J. N. Hobstetter

It is widely believed that the nucleation of phase transformations in solid metals is accomplished by some type of local atomic fluctuations in the parent phase which arise from spoutaneous difiusion in the metal or alloy system. Under appropriate conditions, these fluctuations are believed to be stable in the sense that the free energy of the entire system is lowered if the fluctuations, or nuclei, grow. Under other conditions they are thought to be unstable in the sense that the free energy is lowered if they redissolve. The criterion for stability is usually taken as the size of the fluctuation. This view has been rationalized by Beckerl in terms of the free energy released by the volume of the nucleus and the free energy associated with the formation of a new surface surrounding the nucleus. The qualitative result of this reasoning is shown in Fig I where the changes in free energy for the surface and volume effects are plotted together with their sum against the radius of the nucleus. There is evidently always a critical size r, beyond which the release of free energy which is proportional to the volume always dominates the increase of free energy which is proportional to the surface area. Borelius2 has also attempted to rationalize the stability criterion for binary alloys, but in terms of the internal concentration of the fluctuations. He has found that, if surface energies are entirely ignored, the fluctuation must still reach a critical concentration if it is to become stable and avoid subsequent dilution. Although the Borelius theory fails to predict many observed nucleation phenomena such as the vanishing of the nucleation rate at the critical temperature, the major premise must certainly be valid. In this paper a reconciliation of the Becker and Borelius views is made by means of a search for nuclei which are at once stable with respect to both size and internal concentration. The increase in free energy per mole accompanying the formation of a nucleus which is just stable, AF., is independent of the path whereby the nucleus is brought into being. It is thus appropriate to seek critical nuclear attributes without reference to the fluctuation mechanism. The rate of nucleation, however, cannot be treated without a detailed understanding of the exact fluctuation process which produces stable nuclei. In this and succeeding papers the purpose will be to find the size, shape and internal concentration of the stable nucleus which is formed with a minimum increase in free energy in a wide variety of systems. The Nature of the Nucleus It is necessary ti have rather detailed knowledge of the nature of a nucleus if AF, is to be computed. Fortunately, enough facts are known or suspected about the nucleus to make possible a detailed analysis. X ray diffraction studies have shown

Jan 1, 1949

By W. P. Saunders, W. R. Hibbard, G. H. Eichelman

Interest in the various products of the austenite eutectoid transformation in iron-carbon alloys, particularly as produced by the isothermal sub-critical techniques introduced by Davenport and Bain,&apos; has resulted in the application of similar heat treatments to other eutectoid transformations. Studies o f the beta copper-aluminum alloy eutectoid transformation revealed microstructures very similar to those found in iron-carbon alloys. Investigations5t6 of the kappa phase in the copper-silicon alloy system have established the eutectoid type transformation of this phase into terminal alpha and intermediate gamma phases. This transformation has been reported5 as forming a eutectoid type structure in a very sluggish manner by a long time isothermal treatment. The purpose of the present investigation is to study the products of the kappa eutectoid transformation as affected by transformation temperatures by means of microscopic and hardness methods. Preparation of Alloys The copper-silicon alloy equilibrium diagram is shown in Fig 1. The kappa field converges to a minimum silicon solubility at the eutectoid composition and all other completely kappa alloys are hypereutec-toid. Thus, kappa decomposition involves first the proeutectoid precipitation of gamma, followed by the eutectoid transformation of a lower silicon content kappa (5.2 pct) Smith6 has indicated that alloys containing between 5.4 and 5.7 pct silicon could be hot rolled, but that the latter composition was desirable in order to permit a wider kappa temperature range. The alloy was prepared by adding Baker&apos;s commercially pure silicon to an ingot of copper-silicon alloy containing 2.34 pct silicon remaining from the investigation of Brick, Martin and Angier.&apos; Following the casting techniques of Krynitsky, Saunders and Stern,s the ingot was melted under a heavy layer of dried charcoal in a clay-graphite crucible in a gas-fired pot furnace. Small lumps of silicon were held under thc melt surface with a graphite rod. After the silicon had dissolved, the alloy was chill-cast and then remelted without a cover, stirred thoroughly, skimmed and poured into a preheated cast iron mold. The cast microstructure is shown in Fig 2. The casting, 10 X 4 X K in., was annealed at 750°C for 21 hr and furnace cooled, About }{& in. was milled from all surfaces. The plate was cut in half longitudinally and the bottom half analyzed by A.S.T.M. and The composition by weight was as follows: copper 94.24 pct, silicon 5.56 pct, iron 0.11 pct.

Jan 1, 1949

By J. D. Lubahn, R. P. Carreker, J. G. Leschen

The formation of slip bands in crystalline solids undergoing plastic deformation has recently been treated as a problem of nu-cleation and growth.&apos; A simplified theory was developed and shown to be qualitatively consistent with certain experimental observations reported in the literature, such as the frequent failure of slip bands to traverse the entire crystal, the effect of specimen diameter and temperature on the yield stress, and the occurrence of incubation periods in the deformation of suddenly loaded crystals. The theory further predicts the appearance of transients in the rate of strain of a crystal when the applied stress is suddenly changed from one constant value to another. A transient consists of a discontinuous change in the strain rate followed by a gradual approach to a steady-state value. Such transient behavior apparently has not been recognized in previous experimental work. The preliminary experiments reported in the present paper were undertaken to confirm the existence of the predicted transients and thus to determine whether a more detailed treatment of the nucleation theory of slip might be theoretically and experimentally fruitful. Experimental Procedure A simple creep apparatus was assembled as shown in Fig I. Very little insulation was used on the furnace in order to facilitate rapid changes of temperature. Temperature was measured with a thermometer placed in the center of the furnace and was controlled by adjusting the Variac setting. The specimens were cold-headed in split-cylinder grips. The strain was measured as total elongation by a dial gauge sensitive to I/I0,000-in movement of the weight pan. Since the specimen gauge lengths were

Jan 1, 1949

By J. R. Long, T. R. Graham, C. W. Matthews, R. S. Dean

In a previous paper! the authors reported on the mechanical properties of a 65 per cent copper, 10 per cent manganese, 25 per cent zinc alloy as compared with, similarly processed cartridge brass. Additional investigations by these laboratories, on higher copper alloys, have demonstrated that at lower zinc concentrations even larger amounts of pure manganese may be added to copper-zinc alloys without exceeding the single-phase solid solution limits, and that similar increases in tensile strength, yield strength, and hardness may be obtained without excessive decreases in ductility. Several compositions in this range showed also a decided color change with increasing manganese. The normal "brassy" color was considerably lightcncd and reduced to a faint yellow cast at 15 per cent manganese. With higher manganese contents the alloys were essentially white and similar in appearance to the nickel-silver alloys. From this work it appeared that it would be desirable to determine more completely the properties of the wrought and annealed white alloys. Accordingly, a more detailed study was planned of an alloy having the composition 70 per cent copper, 20 per cent manganese, and 10 per cent zinc. This alloy remained single-phase throughout the working and annealing cycles of the preliminary tests and appeared to be&apos; about the strongest of the white single-phase alloys. The project included also an investigation of additional alloys, deviating from this composition by 5 per cent of each of the three components to evaluate the effects of variation in composition and a study of the propertics of the central alloy made with silicothermic manganese. Material Preparation Electrolytic manganese, wirebar copper, and electrolytic zinc were used for the preparation of the alloys. Representative analysis of the electrolytic manganese seldom exceeds 0.01 per cent iron, 0.02 per cent sulphur and 0.02 per cent lead, with no silicon or aluminum. A typical sample of the silicothermic manganese metal contained 2 per cent iron, 0.81 per cent silicon, 0.16 per cent carbon, and 0.36 per cent aluminum. Melting and alloying were performed in a high-frequency furnace with magnesia crucibles. Melts were deoxidized with small aluminum additions and cast into 25-lb. slab ingots. Care was exercised in deoxidation to avoid excessive amounts of residual aluminum, which has been found to have significant effects on alloys in this system. All ingots were hot-rolled at 1200&apos; to I300°F. and then cold-rolled with intermediate anneal-

Jan 1, 1945

By E. P. Polushkin, Henry L. Shuldener

This paper describes the results of microscopic examination of a series of brass pipes removed from apartment and office buildings in New York City, adjacent localities on Long Island, and Philadelphia. They were selected as typical of approximately four hundred pipe specimens obtained over a period of five years during an investigation of corrosion in hot-water installations. A part of the investigation is reported in this paper and includes a brief history of the pipes, a description of their inside surface and microstructure, and a study of the effects of corrosion, with particular reference to the structural aspects of local and selective dezincification. Although the bibliography on the corrosion of brass pipes is quite extensive, it refers almost entirely to corrosion in sea water. The authors believe that their examination of this series of pipes, which had been subjected to the corrosive action of fresh water for various lengths of time, may throw some additional light on the problem of corrosion. Pipes Examined The pipes were made by different manufacturers and their sizes range from 3/4 in. to 4 in. nominal inside diameter, the majority being within I to 2 in. They can be divided into two groups according to chemical composition: (I) with a copper content of 60 to 62 per cent and (2) with a copper content of 65 to 68 per cent. The first group (pipes made of Muntz metal) comprises 22 pipes and the second (pipes made of high brass) comprises 18 pipes. The pipes had been in service in various locations in the hot-water systems of the buildings involved. Some were taken from horizontal lines in the basement, some from overhead distributors and some from vertical risers. The distance, in terms of feet of pipe, of the specimens from the hot-water generator was no less than 75 ft. and often IOO to 300 ft. In the majority of cases the water-heating equipment was provided with a regulator to limit the temperature of the hot water supply. The normal range of temperature in pipe systems of this kind is Ioo° to 160°F. Water Supples The average chemical composition of the water supplies carried by the pipes is shown in Table I. In evaluating the corrosiveness of a natural water, four factors are considered of prime importance: namely, hardness, alkalinity, pH and silica content. The waters listed in Table 1 are characterized by relatively low hardness, 10, alkalinity, low pH and low silica content. The waters of lower pH and higher CO2 content are more corrosive. A characteristic of all of these waters is that they do not deposit a protective mineral coating as do waters with high bicarbonate of lime content, which would be reflected

Jan 1, 1945

By H. F. Silliman, Daniel R. Hull, John R. Freeman

In the normal operation of a brass-rolling mill, sheet and strip has, for the most part, been finished in comparatively thin gauges, involving a substantial amount of cold-work and a considerable number of anneals. This condition has been disturbed by the preponderance of cartridge brass, which is not rolled to thin gauges, and particularly by brass for artillery cartridge cases, on which the mill may finish its work at a thickness between 0.400 and 0.900 in. Obviously, the amount of rolling and the number of anneals to which such a product can be subjected are small compared with strip that is carried to a thickness of a few hundredths of an inch. As a result, critical examination into the internal condition of metal has been made on an extensive scale at a stage of manufacture that would not, in normal times, have been chosen for complete inspection. Under these conditions, a type of defect has been recognized that is not seen at thinner gauges. It might be more accurate to call it the appearance of a defect, since it refers to an apparently laminated, discontinuous structure, which, in fact, does not exist as such, and disappears after suitable treatment. For this reason it has been called a phantom lamination, which the authors consider an appropriate term. It is the purpose of this paper to describe the phenomenon and the conditions of its occurrence and, at least tentatively, to discuss its nature and cause. Great numbers of phantoms may be found in 2:r brass, either hot-rolled or cold-rolled. They are also found in 70-30 brass, sometimes when hot-rolled and generally when cold-rolled. It is not believed that phantoms are confined to these alloys but this paper is limited to them for the purpose of description. Hot-rolled 2:1 Brass For illustration, therefore, a typical cake of hot-rolled 2:I brass has been chosen. This was rolled to a slab 36 in. thick, from a casting 5 in. thick by 24 in. wide by 18 in. high, which was believed to have been sound. After hot-rolling and cooling, the slab was sheared and a portion of such a shear cut is shown in Fig. I. It would be difficult to convince anyone viewing this specimen that the metal was not unsound. The impression would be confirmed by the appearance of a tensile break, as shown in Fig. 2. This is an ordinary tensile-test piece from metal just described. Although there was nothing in its tensile strength or elongation that suggested unsoundness, it appeared run through with pipes and laminations. To question the reality of such a condition would imply questioning the obvious. But, considering the history of the metal, it would be difficult to believe that it could be so bad as it appeared. It seemed reasonable, though, that if the defects were what they appeared to be, they could be traced back from the sheared or broken face.

Jan 1, 1945

By F. H. Wilson, R. M. Brick

With the papers of Palmer and Smith1 and of Burghoff and Bohlen,2 published in 1942, understanding of the problem of the development of ears on deep-drawn brass cups was brought to the point where, from a practical standpoint, producers of brass sheet could keep earing under control. However, these very practical results raised questions concerning the reasons for the observed behavior. Since plastic deformation is fundamentally a function of crystallographic slip, these reasons must be considered in the light of the textures to be found in the annealed sheet. Various attempts have been made. to interpret the mechanism of ear formation by correlation with the preferred orientation and the anisotropy of the sheet. However, none of these has satisfactorily explained why ears are usually found in the rolling and transverse directions for copper but at 45&apos; to these directions for brass. This paper offers additional data on these two related subjects and has been divided into two sections The first section provides a survey of the recrystallization textures of brass as affected by annealing temperatures and prior reductions, and an account of the caring behavior which accompanies these textures. The second section reports new data on the anisotropy that accompanies a characteristic texture for brass and endeavors with partial success to establish the factors that account for the difference in earing behavior between copper and brass Earing BehavioR oF Brass Review of Textures The recrystallization texture of severely rolled brass was first reported by Bass and Glocker.3 The preferred orientation to which this texture, obtained from metal annealed at 500°C., was most akin was (II3)[I12] This texture has been confirmed by Bauer, von Göler and Sachs;4 Brick;&apos; Brick, Martin and Angier;6 and Cook and Richards7 who, in general, used annealing temperatures under 500°C. Bass and Glocker3 also reported the recrystallization texture at 850°C. to be the same as at 500°C. They analyzed their textures by means of single photograms obtained with white radiation. The photo-grams for both temperatures are reproduced in their paper, and there is a strong similarity between the two. However, for the latter temperature, the number of spots registered on the film was remarkably large for the grain size to be expected, and the authors made no mention of using a technique that would integrate a large enough area of the specimen to produce so many spots. The only other attempt to determine textures resulting from high temperature

Jan 1, 1945

By J. R. Long, A. H. Roberson, T. R. Graham, R. S. Dean

Experimental work on the properties of high-purity alloys of the copper-man-ganese-zinc system has necessarily required extensive metallographic work to determine the equilibrium conditions in this system. Previous work on these alloys is fragmentary and, unfortunately, based on alloys made with impure grades of manganese, thus introducing significant amounts of iron, silicon, aluminum and carbon. Since these elements are known to affect equilibrium conditions, it became desirable to re-examine these alloys made from the pure metals. The alpha solid solution field was of particular interest and, therefore, was chosen for the initial work, which was outlined to determine the composition limits of this field. Previous Work Heuslerl conducted an extensive survey of the liquid-solid regions of this system and also made an estimate of the solid-phase boundaries at 340°C. The pertinent part of his diagram is given in Fig. I, but it is of limited usefulness, since it applied to a single temperature only and is based on impure alloys under admittedly nonequilib- rium conditions. Bauer and Hansen,2 likewise working with impure alloys, have determined the phase boundaries for alpha-beta brasses containing small amounts of manganese and indicate an increase in the extent of the alpha field with increasing manganese. This is not in accordance with Heusler or with data obtained on pure alloys.3 They also described a third constituent precipitating in the alpha plus beta field below 350&apos; to 400°C. but did not identify this constituent. Guillet4 and Heike and Ledibur6 have also noted this precipitate. Each of these investigators recognized that impurities present in the manganese could and did have an effect on the structure and properties of their alloys. Corson6 in particular pointed out the hardening effects of silicon, aluminum, and carbon in copper-manganese alloys and Heusler reported that his alloys containing more than 25 per cent manganese were extremely brittle. In all probability this brittleness was due to the impurities present. This early work, therefore, should be taken as a general guide for preliminary studies only, and high-purity alloys may be expected to produce different results. The work of the Bureau of Mines laboratories with electrolytic manganese has been briefly summarized by Dean7 but includes only a short section on this system. Later work3 outlined a limited portion of the alpha field in the neighborhood of 65 per cent copper, 10 per cent manganese, and 25 per cent zinc. The present work was under-

Jan 1, 1945

By Svetlana Krashenina, Nebojsa Petrovic, Oscar Lopez

"As easily mined gold deposits are becoming increasingly rare, gold producers are turning to the processing of ores with polymetallic and copper mineralization. These base metals can create metallurgical and waste handling/disposal challenges, which can render the project uneconomic. Base metals such as copper compete for the cyanide reagent used to extract gold, necessitating the need to increase cyanide volumes and consequently, cyanide consumption costs. Copper will also stabilize in tailings water as weak acid dissociable cyanide, a form that is both difficult and costly to destruct. SART (sulphidization-acidification-recycling-thickening) process technology can be applied to remove base metal interferences in gold projects. SART breaks the copper-cyanide complex and precipitates the copper as a saleable copper sulphide concentrate. With the copper removed, the cyanide can be regenerated as free cyanide for recycle to the gold recovery process. This improves cyanide utilization efficiency and mitigates copper presence in tailings. Additionally, copper recovery generates an incremental revenue source to further improve project economics. Engineering Dobersek GmbH together with BioteQ developed a SART and AVR testing program to recover cyanide and maximize operational efficiencies at a gold processing plant in Kazakhstan with high cyanide consumption in the leach circuit. Results from on-site testing demonstrated that up to 99.98% of copper can be removed and precipitated as copper sulphide and 60-90% of cyanide can be recovered from the AVR and recycled for leaching, reducing total overall cyanide use. This paper provides an overview of the testing methodology and results together with a discussion on the potential of SART to improve gold production operations to deliver both environmental and economic benefits."

Jan 1, 2014

By Lj. Obradovic

The aim of this paper is to study the feasibility of copper and gold recovery from the old flotation tailing dam at Bor, Serbia. Laboratory leaching experiments were carried out using a composite sample taken by drilling from 16 - 40 m depth. Different oxidation agents as FeCl3, Fe2(SO4)3 and H2O2 were used. An H2SO4 solution with a pH less than 3 was used for leaching. The influence of a number of parameters on the recovery of both elements as temperature, pH, duration of leaching and concentration of oxidation agents was also studied.

Jan 1, 2006

By Patrick R. Taylor

This paper presents a fundamental study of the thermodynamic and kinetic effects of copper and iron on gold-cyanide leaching. It quantifies the solubilities of the impurities, complex formation, and kinetic effects. The necessity of solution recycle, to meet environmental standards, requires that fundamental information be generated to characterize behavior and allow the identification of treatment methods. Mathematical descriptions of both solubilities and kinetics will be presented

Jan 1, 1983

By M. Lonoff

Byproducts are more important to the copper mining companies than to the copper market. Copper ores frequently contain gold, silver, molybdenum, lead, zinc, and cobalt. With the increase in the prices of these metals copper mining has become more profitable. If byproduct prices remain high, additional firms will be attracted to the copper industry; the increased supply of copper will reduce the long-run copper price. However, this is unlikely to happen because the markets for the copper byproducts, especially molybdenum and cobalt, are small. Increased recovery from copper and other sources will depress the prices of these byproducts before the copper price is significantly affected. Should byproduct prices remain high, the copper market will both settle at a lower long-run price and be more unstable in the short run. Since changes in the copper price do not affect the entire earnings of a multi-metal mine, the copper price must fall further before such mines reduce output in the short run. Higher byproduct revenues will make copper supply less responsive to copper prices; shifts in copper demand will result in greater copper price fluctuations in the short run than they did before.

Jan 1, 1984

By Marc Lonoff

Byproducts are more important to the copper mining companies than to the copper market. Copper ores frequently contain gold, silver, molbydenum and cobalt. With the increase in the prices of these metals copper mining has become more profitable. If byproduct prices remain high, additional firms will be attracted to the copper industry; the increased supply of copper will reduce the long-run copper price. However, this is unlikely to happen because the markets for the copper byproducts, especially molybdenum and cobalt, are small. Increased recovery from copper and other sources will depress the prices of these byproducts before the copper price is significantly affected. Should byproduct prices remain high the copper market will both settle at a lower long-run price and be more unstable in the short run. Since changes in the copper price do not affect the entire earnings of a multi-metal mine, the copper price must fall further before such mines reduce output in the short run. Higher byproduct revenues will make copper supply less responsive to copper price; shifts in copper demand will result in greater copper price fluctuations in the short run than they did before.

Jan 1, 1980

By John G. Hall

Everyone forms his own mental picture when the subject of copper is mentioned. To an architect, copper is a warm, enduring metal with a quiet beauty; to the historian, man&apos;s first metal; to the product engineer, the best electrical and thermal conductor of all commercial metals; to the investor, a volatile stock; to the speculator, the daily price quotation; to those in the mining industry, the challenge of producing copper for rising needs in the face of rising costs and lower grades of ore. At this meeting, we will look upon copper as a key raw material in industry, in national defense, in technology, in world trade, and as a principal commodity in the economies of several developing countries. As miners, and most of us here are miners, we are prone to view our role as suppliers of copper. We locate, mine, smelt and refine the metal. In the complexities of today&apos;s world, however, following a period of the longest domestic copper strike in history which caused critical world-wide shortages and widely fluctuating prices; it becomes necessary for all of us to concern ourselves with the whole spectrum of copper affairs -"from mine to consumer " But first we need to look at the miner&apos;s side of the picture -- capacity and production. We will examine these functions in terms of the whole world -- not simply the free world. Nature did not endow all regions of the earth equally, and copper in world trade has a way of ignoring political boundaries. Science and technology, as well, know no national boundaries. It is said that the "Engineering & Mining Journal" has as many readers in the Communist World as in the Free World. Nor is this a one-way street. We presently have available to us in the. U.S., cover-to-cover translations of many Communist World mining and metallurgical journals.

Jan 1, 1968