Search Documents

By L. Gasser, N. Bellinger, H. Awatta, A. Merati

As aircraft age, the extent of interactions between fatigue and other damage mechanisms, such as corrosion and fretting, increases. At present, however, there is no generally accepted methodology within the Aircraft Structural Integrity Program (ASIP) framework to account for the effects of these interactions on life and the residual strength of aging aircraft components. A comprehensive program is being carried out by the National Research Council Canada in collaboration with Analytical Processes/Engineered Solutions, using the Holistic Structural Integrity Process (HOLSIP) to address time and cyclic load issues. This approach predicts the evolution of a discontinuity state in a material from production to retirement. This paper summarizes the results of a study on the 2024-T3 aluminium alloy in different forms (clad and unclad), thickness, and specimen geometry. This study consisted of identifying the microstructural features associated with crack nucleation sites and relating them to the testing parameters and fatigue life. Several coupons were fabricated and fatigue-tested. The fracture surfaces were carefully examined, and the physical characteristics of the microstructural features found near the crack nucleation sites were analyzed. Effect of stress level, loading direction, coupon geometry and surface condition on the number of crack nucleation sites, and fracture origin size has been discussed. Four distinctive mechanisms were found to be responsible for crack nucleation: for unclad materials constituent particles, oxide residue, surface irregularities and for clad samples the clad layer was the sole fracture origin.

Jan 1, 2006

By M. Imamura

Sumitomo Metal Mining Co., Ltd. has developed a novel hydrometallurgical process for producing not only copper metal but also iron metal from copper concentrates. Because copper concentrates generally contains the same amount of iron as copper, cost-effective rejection of the iron is a key issue for the development of the process. Conventional hydrometallurgical processes produce a large volume of goethite or hematite for disposal and the residues are not environmentally friendly. In the novel Sumitomo hydrometallurgical process, copper is leached effectively from chalcopyrite concentrates using chlorine gas, followed by purification through solvent extraction and electrowinning for copper and iron recovery. This process has many advantages such as the minimization of the volume of solid waste by the recovery of metallic iron and the production of high purity copper. Iron metal with a purity of more than 98% can be recovered from the purified raffinate. This paper presents the results of the batch and continuous tests of the process flowsheet.

Jan 1, 2006

By S. Foged

Umicore and MWH jointly demonstrated that mechanical dewatering of goethite and neutralised tailings significantly increased the life of a 30 ha tailings pond and improved the operation of the pond. Umicore operates one of its zinc production plants in Balen, Belgium. As part of its production process, an excess of neutralised and goethite¬containing tailings is generated. These have historically been stored inside large lined ponds. As the storage area of the current goethite pond was nearing its capacity, Umicore studied the potential for an extension to the existing embankment. However, this extension would face intense regulatory scrutiny, because the environmental and safety impacts were considered important. Together with Umicore, MWH suggested and investigated an alternative treatment approach consisting of mechanical dewatering prior to storage. A feasibility study was prepared where wet storage was compared to dry storage. Differences in safety risks, environmental impacts and economic costs were outlined. The study demonstrated that the life of the tailings pond could be increased from 6 to 22 years, seriously reducing the environmental impacts and safety risks at no significantly higher cost than would have been incurred with the continued operation of the existing pond. The results of the study are presented in this paper.

Jan 1, 2006

By H. Al-Kazzaz

The effects of laser power and joint gap on the welding quality of 2-mm butt joints of ZE41A-T5 sand castings were investigated using a continuous wave 4 kW Nd:YAG laser system and 1.6-mm EZ33A-T5 filler wire at a welding speed of 6 m/min and surface defocusing. The smooth weld profiles with the minor welding defects were obtained at a laser power of 4 kW and joint gap of 0.3-0.4 mm. The hardness values in the fusion zone are similar to those of the base metal but there is a drop in the heat-affected zone after a natural aging of 18 months.

Jan 1, 2006

This paper focuses on the dissolution of various Manganese based compact additions into liquid Magnesium. The experimental procedure employed cylindrical compacts with various Manganese compositions. The various temperatures of the additions and the Magnesium bath were measured simultaneously during the immersion of the additions into Magnesium bath. The exothermicity level of these additions during their dissolution into liquid Magnesium was determined. The relation of the exothermicity level with the dissolution kinetics was also examined. In addition, SEM and EDX work was conducted for additions, which were withdrawn from the Magnesium bath. Finally, the recovery of these additions was estimated by taking samples from the Magnesium bath and conducting ICP analyses.

Jan 1, 2006

By M. Fujikawa

The Kamioka Zinc Smelter was converted from the jarosite process to the goethite process in the year 2000. The reasons for the conversion of the process were that the silica content of the raw material increased and the iron content decreased. The silica easily turns to a gel in sulfuric acid solutions and this causes the solid-liquid separation characteristics to deteriorate. The basic behavior of silica in sulfuric acid solution was investigated and it was found that the goethite process is the most suitable to effectively separate and remove silica from solution. Furthermore, Fe has the capability to remove elements such as Ge that have an adverse effect on zinc electrolysis. This means that, when the Fe content of the raw material decreased, the impurity removal capability also decreased and there was a risk of a build-up of impurities in the process. Iron precipitates in many forms in sulfuric acid solutions. The capability to remove elements such as Ge differs depending on the compound precipitated. Goethite has a higher capability than jarosite to remove elements such as Ge. In this report, the results of applying the process established by investigations of the basic behavior of Fe, silica and Ge in the zinc refining plant are presented.

Jan 1, 2006

By P. Su

Friction stir spot welding of a range of Mg-alloys is investigated (AZ91, AZ31, AM50 and AM60). The peak temperatures during friction stir spot welding of all Mg-alloys are close to their solidus temperatures. Also, the apparent material viscosity of Mg-alloy sheet is lower than that when Al-alloy sheet material is spot welded. This is important since it means that the widths of the stir zones forming during spot welding of Mg-alloy sheet are smaller than those when Al-alloy sheet is welded (when identical welding parameter settings are applied). These lower apparent viscosity values must be taken into account during numerical modeling of the Mg-alloy spot welding process. The efficiency of energy utilization is very low when Mg-alloy sheet is spot welded and is of the same order as that when fabricating Al-alloy sheet. The energy generation contributions of the rotating pin and the tool shoulder are investigated. When the spot welding operation is carried out without the application of a dwell period, the contribution made by the rotating pin vis-à-vis energy generation is around 66%. The contribution made by the tool shoulder increases to about 65% when a dwell period of four seconds is incorporated during the spot welding operation. This increase results from a longer contact time between the tool shoulder and material within the stir zone, The failure load during overlap shear testing increases when the bonded area and the energy input increase during spot welding. Sample failure initiates from unbonded regions and from discontinuities at the edge of the stir zone. The formation tendency of discontinuities is increased when Mg-Alloy sheet is spot welded because of the limited deformation characteristics of the base material at lower temperatures.

Jan 1, 2006

By A. Kraly, M. Complojer, P. Paschen, K. Gamweger, H. Antrekowitsch

Increasing quality of aluminium alloys and continuous optimization of the production process leads to an improvement of the gas purging systems. The application of porous plugs for the treatment of liquid aluminum is nowadays not widely used in the aluminium industry especially in Europe. The Department of Nonferrous Metallurgy and the Christian Doppler Laboratory of Secondary Metallurgy of Nonferrous Metals intensified the research and development of refining and alloying processes by gas treatment during the last years. CFD-modeling supports these experiments, which should lead to lower hydrogen content, lower suspended particles and a better distribution of alloying elements in the melt. Different parameters such as temperature, bubble size, gas amount and which kind of gas is used influence the quality of the products.

Jan 1, 2006

By G. Diaz

Técnicas Reunidas (TR) has been involved for over 30 years in the development of process technologies for the recovery of zinc from different primary and secondary feed materials, such as the ZINCEXTM process. Because of the complexity of the feed mineral resources, solvent extraction (SX) is an invaluable technique to concentrate and purify zinc solutions. When applied to a pregnant leach solution, solvent extraction can produce an extremely high quality zinc electrolyte, suitable for obtaining SHG zinc ingots, after electrowinning and melting and casting processes. However, the high affinity of most organic extractants for Fe(III) poses a serious problem, which may adversely affect the zinc extraction process. Different methods may be applied to deal with the negative effect caused by Fe(III). An acid regeneration step and electro-reduction stripping have been considered as the most viable techniques to remove the iron from the organic phase. This paper describes some findings of Técnicas Reunidas in the area of zinc solvent extraction, especially on removing Fe(III) from the organic phase.

Jan 1, 2006

By S. Malkin, Z. Shi, H. Attia, D. Chellan

An experimental investigation is reported on creep-feed grinding of a nickelbased alloy (IN718) using conventional aluminum oxide grinding wheels. Straight surface grinding expe.riments were conducted on nickel-based alloy blocks over a wide range of grinding conditions with straight oil as- grinding fluid applied at high pressure. Grinding power, forces, workpiece surface roughness, and radial wheel wear were measured. Specific material removal rate as high as 64 mm2/s was Used without burning the workpiece, which can be attributed to the extremely low specific energy of 12.6 J/mm3. It was found that the grinding wheel under the present test conditions had a strong capability of self-sharpening as indicated by the stabilized power, forces, and surface roughness after an initial short transient.

Jan 1, 2006

By P. Wanjara, M. Xiao, M. Jahazi, C. Poon

Using a robotic 4kW Nd:YAG-laser system, Inconel 718 (1 mm sheet) was welded with and without filler wire to investigate the effect of processing parameters, including power input and welding speed, on the weld geometry, microstructure and mechanical properties. By means of both nondestructive testing and microscopic examination, the weld quality was studied to determine the nature of the welding defects (porosity, cracking and bead shape) over the processing range of 3-3.5 kW for the power input and 4.5-6 m-min-1 for the welding speed. Application of the design of experiment methodology permitted the examination of the relationship between the process parameters and mechanical properties, from which the optimized laser welding conditions could be determined for joining Inconel 718. In particular, the research results indicate that Nd:YAG-laser welding technology can achieve defects free, mechanically sound welds with narrow fusion and heat effected zones.

Jan 1, 2006

By I. M. Masters

Iron removal and control in processes employing pressure leaching technologies developed at Dynatec Corporation are reviewed. Discussions are focused on recent developments in the processing of nickel-copper matte and copper concentrates, and on the Ambatovy laterite project in Madagascar. Iron control and its implications on flowsheet design in the pressure acid leaching (PAL) treatment of laterite ores and in the oxidative pressure leaching of mixed nickel-cobalt sulphide intermediates are also discussed.

Jan 1, 2006

By S. Shrestha

Magnesium-based alloys are of growing interest for many industrial applications due to their favourable strength-to-weight ratio and excellent castability. Mass reduction has advantages in many industrial sectors for example, in automotive, a reduction in mass improves fuel economy and can lead to more efficient mechanical systems by reducing the weight of moving parts like wheels, gears, pistons. However, the relatively poor corrosion and wear resistance limits the use of magnesium and its alloys in many potential applications. The patented Keronite® plasma electrolytic oxidation (PEO) process enables manufacturers to overcome such problems and, in its latest generation equipment has been developed to industrial realisation for high volume production. This paper presents microstructural characteristics and corrosion performance of two most widely used high pressure die-cast magnesium alloys AZ91D and AM6OB with a duplex corrosion protection coating system that comprised a thin Keronite pre-treatment followed by a subsequent automotive grade final powder coat.

Jan 1, 2006

By P. Personnet, D. Wheaton, E. Couzinie, V. Demetriou, Brooks. W., G. Girault, M. Meyer, L. Charbonnel

A common problem in Gas Treatment Centers (GTC) from primary aluminium smelters is the temperature of the gas to be treated : above a threshold, filtering media are irreversibly damaged. The traditional way of dealing with high gas temperature is to dilute with fresh air, which implies over sizing - and therefore higher cost for - the GTC in order to have the capacity to treat this dilution air without compromising on pot suction. A system was developed which decreases gas temperature without having to use dilution air. This system is based on water pulverization in gas collectors. The water vaporization leads to a temperature decrease of the gas. A pilot system was trialed in our R&D unit. Satisfactory results led to the development of an industrial system based on Envirocare equipment (partnership), which was trialed in our production plant in Tomago (NSW, Australia). This patented system was then generalized in this plant, which is now using it with success during austral summer.

Jan 1, 2006

By W. Beres, M. Bielawski

Recent research on the development of erosion resistant coatings has been directed to the finite element modelling of the behavior of coating and substrate, and their interface under the impact of eroding particles. The approach presented in this paper is based on advanced computer simulation techniques using ABAQUS/Explicit to investigate stress and strain at the surface and at the coating/substrate interface of multilayer coatings under single particle impact. It was found previously that solid particle erosion mechanisms are predominantly governed by the kinetic energy of the impacting particles. However, recent modelling efforts revealed that effects of various material models could be also significant. Therefore, different material models representing relevant coating and substrate properties were investigated and the effects of these models on the coating/substrate response were studied. Particularly, differences between elastic, elastic-plastic and brittle cracking model responses were assessed.

Jan 1, 2006

By M. H. Attia

The concept of sustainable development has been evolved into a working framework for sustainable manufacturing, in which the environmental requirements are introduced into product development at the design stage. This keynote paper is discussing a number of issues pertaining to the impact of manufacturing on the environment. The conflicting requirements of sustainable development, sustainable manufacturing (SM) and economical growth are presented in the light of successful case studies that were able to convert conflicts into opportunities. Integration of SM into the product life cycle is also presented. A number of concepts that are related to Ecoefficiency, e.g., inverse manufacturing, demanufacturing and re-manufacturing are also discussed. The paper underlines the fact that the positive impact of this new philosophy is equally applicable and beneficial to both; developed and developing countries. The paper concludes with an overview of Global trends in environmentally benign manufacturing (EBM); e.g., product-take back and emerging material and processing technologies. The state-of-the-art approach to Life Cycle Impact Assessment and integration of design for the environment DfE principles are demonstrated through some case study.

Jan 1, 2006

By J. W. Senn

A magnesium alloy modeled after commercial alloy WE54 was thermomechanically processed and characterized to understand the mechanisms by which its texture can be randomized, as reported by Ball and Prangnell [1]. Samples were deformed in plane strain compression to prescribed strain levels at temperatures high enough to prevent cracking and then recrystallized. The deformation texture is very similar to that observed after plane strain compression (e.g., rolling) of other Mg alloys, such as common AZ31. However, the texture can radically evolve during recrystallization. Annealing above the precipitate solvus temperature results in a nearly random recrystallization texture where the initially strong basal texture is completely eliminated. Annealing below the solvus temperature produces a recrystallized texture similar to conventional Mg alloys, i.e., a weakened basal texture. If this same material is then annealed above the solvus to promote grain growth, a randomized texture evolves, which is similar that of samples simply recrystallized above the solvus. It is hypothesized that a sort of preferred growth mechanism, whereby grains with random orientation grow faster than those with the original basal texture, contributes significantly to the texture randomization observed in wrought magnesium alloys containing rare earth elements.

Jan 1, 2006

By A. Bowles

The process of accumulative roll bonding (ARB) has been applied to wrought magnesium alloy AZ31. Accumulative roll bonding results in severe plastic deformation of sheet material. In AZ31, this process leads to the refinement of the microstructure by dynamic recrystallization. The refinement of the microstructure results in an improvement in mechanical properties with potential for producing materials for superplastic forming. In this work AZ31 was bonded with up to 64 layers and the potential of roll cladding with aluminium was also investigated. The development of microstructure and the mechanical properties are reported here.

Jan 1, 2006

By Claude Deveau

"Studies on the performance of Falcon batch type concentrators treating ultrafine tantalum at Tanco have revealed that very fine heavy minerals are concentrated within certain areas of the concentrate bed. This information led to the design of a bowl which would allow entrapped lighter low grade particles to escape while providing more space for heavier particles to be recovered in the bed.Numerous tests were then completed with a modified batch-type and non-fluidized Falcon bowl in which the diameter of the discharge lip was adjusted downward manually in steps. This allowed for the gradual building of a higher grade concentrate bed.This work ultimately led to the design of a new Falcon with an automated continuously variable lip. In April 2005, Tanco commissioned the first Falcon UF600.This paper will discuss laboratory scale results and also plant performance of the Falcon’s UF technology.INTRODUCTIONTantalum Mining Corporation of Canada, also known as Tanco, is a wholly owned subsidiary of Cabot Corporation based in Boston, Mass. Operating since 1969, the underground highly mechanized room and pillar operation produces tantalum, lithium and cesium minerals and is located a 2 hour drive east-northeast of Winnipeg Manitoba, Canada.At Tanco, tantalum is recovered using conventional gravity concentration, enhanced gravity concentration and flotation. This paper will discuss how the need for improved equipment to treat very fine tantalum particles was filled by a machine which was modified to the point of creating a completely new technology.In November 2003, Tanco began the investigation for the potential use of a high g-force smooth walled concentrator for treating ultra fine tantalum produced by its flotation circuit. Until then, the tantalum flotation concentrate had been treated by a circuit which consisted of a Mozley Multi-Gravity Separator 902 (MGS), a Mozley MGS 900 and a Bartles cross belt concentrator. Through QemScan analysis, it was found that the majority of the losses from this circuit were of an extremely fine nature which exceeded the recovery limits of equipment on hand. Mean particle size of the tantalum losses was less than 10 µm."

Jan 1, 2006

By R. Q. Honaker

A significant problem in ultrafine particle classification is the significant amount of submicron particle by-pass to the coarse particle stream. In classifying cyclones, submicron particle by-pass to the underflow stream can be reduced by decreasing water recovery. Past studies have shown that a reduction can be realized when the feed solids concentration is increased or the apex diameter is reduced. However, both adjustments tend to increase the particle size cut point and negatively affect classification efficiency due to the impact on slurry rheology. The addition of a viscosity modifier to the feed stream of a classifying cyclone improved the classification performance and decreased the particle size cut point over a range of feed solids concentrations. The detailed test program investigated the use of the modifier in conjunction with varying apex diameters to identify conditions that minimize ultrafine by-pass. With small apex sizes, roping conditions were readily eliminated by the addition of viscosity modifiers. The addition of the modifier had no deleterious effect on froth flotation performance, which commonly serves as a downstream separation process. The fundamental and practical benefits of viscosity modifiers in classification processes are discussed in this publication.

Jan 1, 2006