By R. H. Doremus

From measurements of carbide precipitation rates in a iron it was concluded that the carbides nucleated on dislocations in both strained and unstrained samples, except for the latter at lower temperatures and higher carbon concentrations, where there were more muclei than could form on the dislocations. The equation of Cottrell and Bilby for the segregation of atoms to dislocations was found to be inapplicable to this system. No satisfactory theory for the growth process is available. A study of the rate at which a second phase separates from solid solution can frequently reveal much about the mechanism of separation. There are still many features of the precipitation of carbon from a iron that are not understood, although this system has been examined extensively. To provide more insight into the mechanism of carbide precipitation in a iron, rates of this process were measured at different temperatures, carbon concentrations, and densities of dislocations in the iron. The concentra- tion of carbon in solution was followed from the height of the internal-friction peak; this height is directly proportional to the amount of carbon in solution and is not affected by the growing carbide particles. In this paper these rates are compared with those found by earlier investigators, and the mechanism of precipitation is discussed in light of these results as well as two earlier studies1, 2 and the electron microscopic work reported in the preceding paper. EXPERIMENTAL The amount of carbon in solution was followed by

Jan 1, 1961

By C. G. Rhodes, D. Kramer

The kinetics of precipitation of transient a phase during the transformation in U-16 wt pct Mo between 400° and 550°C were studied using quantitative metallography and electrica1 resistiuity measurements. The volume percent of a phase goes through a maximum in time, corresponding to a critical degree of progress of y' formation. prior to its re-solution after prolonged annealing. The fastest rate of a precipitation oc-cuvs at 500°C with a concomittant lowest peak of 9.5 vol pct a. At 450°C, 14 vol pct a, greatest fov any temperature, was observed after 24 hr witlz an associated slowest rate of formation. a precipitation at 400°C ceases after approximately 160 hr and the amount of a present remains unchanged after long times at temperature; no y' was observed metallographically at this temperature. IN the U-Mo system at 16 wt pct Mo, an ordering reaction takes place below 600°C, see Fig. 1, whereupon the random bcc solid solution, y, transforms to the ordered bct phase, y'."2 The new unit cell is constructed of three old unit cells somewhat distorted. While attempting to study the kinetics of this transformation it was observed that an unexpected phase was precipitating out early during the transformation anneal reaching appreciable amounts before disappearing after long times. The y' appeared in the presence of this new phase and after long times constituted the whole sample. Owing to the high optical activity of this unexpected phase under polarized light, it was suspected to be the a phase. Subsequent X-ray powder pictures confirmed this belief. The kinetics of a phase formation and disappearance is the subject of this paper. EXPERIMENTAL PROCEDURE A) Alloy Preparation. Alloys for this study were prepared by vacuum induction melting normal reactor grade uranium and 99.5 wt pct Mo pellets in thoria crucibles. Two ingots were prepared, and sections of the top and bottom of each ingot were chemically analyzed for uranium and molybdenum content. The results of the analyses appear in Table I. B) Metallography. Samples of 16M were wrapped in tantalum foil, sealed in evacuated (5 X 10"6 mm of Hg) quartz capisules, and annealed at 1110"C prior to being transferred directly to the transformation temperature. They were examined metallographically after increasing times to determine the progress of the transformation at 400°, 450°, 500°, and 550°C. The samples were prepared for metallographic examination by mechanical polishing with diamond paste and electrolytic polishing with a solution of glacial acetic acid and chromic acid. Since the y' phase is tetragonal, its presence can be detected by viewing the sample in polarized light. To increase the contrast between y' plates, the samples were electro-etched in a 10 pct oxalic acid solution. To reveal a phase in bright field (it can be seen in polarized light in the "as-polished" state), the samples were electro-etched in a solution of citric acid and nitric acid. To determine the vol pct a phase, a variation of the one dimensional systematic point count method as described by Hilliard and cahn3 was used. The

Jan 1, 1962

By W. D. Potter, E. T. Peters

Single-crystal films of boron have been prepared by thermal reduction of purified BCl3 with subsequent deposition of boron onto oriented silicon substrates. The structural properties of films prepared under various experimental conditions have been determined by light microscopy and "grazing-" angle electron-diffraction analysis. An orientation relationship is proposed for silicon and a-rhombo-heclral boron which can be described as: (111)Si (112)B; [110]Si [110]B ElEMENTAL boron is known to have a high energy gap* and consequently has potential value as a high- *Energy gaps of 1.35 to 1.55 ev1-3 and 2.0 ev4 are reported for ß-rhombohedra1 and a-rhombohedra1 boron, respectively. temperature semiconductor.5 Exploitation of this property, however, has been hampered by the unavailability of pure, single-crystal boron. Two recent symposia6,7 have treated the subjects of purification, crystallization, crystal structure, and properties of boron and provide a foundation for further investigation in these areas. The structure, lattice constants, and observed ranges of stability for four reported polymorphs of boron8°12 are listed in Table I. The rhombohedral structures are generally accepted as true polymorphs whereas the tetragonal structures are believed to be transient. Most currently available single crystals of boron are grown by Czochralski and floating-zone methods. Unfortunately, these crystals generally contain numerous defects and are highly strained as a result of the polymorphic transformations and thermal contractions which accompany cooling. Recently, Armington, Potter, and Tanner13 have reported the formation of single-crystal films of boron on silicon single-crystal substrates through thermal reduction of BC13 by hydrogen. Boron E. T. PETERS, Junior Member AIME, is Senior Scientist, ManLabs, Inc., Cambridge, Mass., and W. D. POTTER is Research Chemist, Air Force Cambridge Research Loboratories, L. G. Hanscom Field, Bedford, Mass. formed at temperatures near 1000°C was identified as the a-rhombohedra1 form, consistent with expectation. The present paper describes a continuation of this work with specific reference to characterization of the structural features of the deposited boron films. The ultimate goal of this program is to produce large-area single-crystal films of a-rhombohedra1 boron to be used for electrical and optical studies by other workers. PREPARATION OF BORON FILMS The experimental procedure of preparing thin films is similar to that described by Theuerer14 for the epitaxial growth of silicon by thermal reduction of SiC14 and has already been described as applied to the preparation of boron thin films.13 Briefly, a mixture of BCl3 vapor and dry hydrogen is passed over a heated silicon substrate. Thermal reduction of the BC13 allows deposition of boron on the substrate. The substrates were {111}-oriented, single-crystal silicon. Square specimens 0.63 cm on an edge by 0.1 to 3.0 mm thickness were prepared by

Jan 1, 1965

By R. F. Mitchell, G. F. Dillon, A. F. Armington

In this paper the present methods of boron preparation are discussed with emphasis on the iodide intermediate. Several methods of boron triiodide preparation were investigated, the most satisfactory method being the preparation from the elements. A yield of 60 pct based on iodine is found for this method. Zone-refining, sublinzation, distillation, and fractional-recrystallization results are given for the boron triiodide, with distillation producing the best results. Several methods of decomposition are also discussed. The purity of the resulting iodide boron approximates the puritjl of the best available bromide boron, ELEMENTAL boron has been suggested as a possible high-temperature semiconductor by several workers,' but has never been exploited as a device material. The principal difficulty with boron is the unavailability of pure crystalline material from which accurate information on electrical properties could be obtained. Most boron crystals presently produced are very imperfect in structure and of questionable purity, particularly in relation to carbon content. Several methods of boron purification have been reported in the past few years, all of which produce material with a purity better than 99.0 pct. Most of these methods have been the subject of a recent review by Starks' and will not be elaborated upon in this report. However, of all the purification methods reported, only those using halide intermediates produce a purity approaching that usually required for electronic applications. The bromide intermediate has been most used for the preparation of high-purity boron.'y3 This material is easily prepared from the elements and can be effectively purified by distillation and decomposed by hydrogen reduction. The resulting product contains a trace of silicon, and an uncertain amount of carbon, believed to be approximately 100 ppm. It has been recently reported by Russian workers that high-purity boron can be produced using an iodide intermediate.' In the work cited, boron is reported free of spectro-scopically determined impurities, but the reported detection limits are quite high (- 100 ppm). In addition, no data is given on the carbon content of the product. In the present paper, boron triiodide was chosen as the intermediate for several reasons. First, carbon tetraiodide, which could be a major impurity, is reported to be unstable above 200" and hence could be easily separated from the boron triiodide by its decomposition, since temperatures greater than this are attained during the purification process. The low melting point (45°C) and boiling point (20B°C) and the relatively high vapor pressure of boron triiodide should allow the application of any physical purification technique to the material. The possibility of a lower decomposition temperature than that used for the bromide process is another advantage which might cut down extraneous contamination. The iodide, however, does have certain disadvantages when compared with the bromide, the production cost being the most significant. This is the result of a higher halide-to-boron weight ratio, which means more intermediate must be employed. The cost of the starting material is also greater for the iodide. This cost could be considerably reduced however, by recycling the iodine byproduct. Epitaxial growth of boron, which is probably the best method of producing junctions, should be possible with either the bromide or the iodide as the intermediate. However, this has been attempted only on a limited scale up to the present time because of the unavailability of good crystals. The authors have been relatively successful in laying down a heterotaxy of boron on silicon, however. This will be reported at a later date. Several crystalline modifications have been reported for boron, four of which are now believed to be real.' These are the a! and 0 rhombohedral and the a, and 0 tetragonal. In general, the a! rhombohedral is the low-temperature form and the B rhombohedral is the high-temperature form. The tetragonal structures are detected between 1000"

Jan 1, 1964

By George C. Fryburg

The oxidation of platinum at high temperatures (above 800°C) is controlled by boundary-layer diffusion, except at the lowest pressures. The rate of oxidation is determined by the rate of diffusion of oxide through the boundary layer away from the platinum. This is in contrast to the situation in tungsten and molybdenum oxidation, where the rate is controlled largely by the diffusion of oxygen through the boundary layer towards the metal. The difference in mechanism is a consequence of the much lower rate of oxidation of platinum. Evidence is presented that supports this mechanism for the oxidation of platinum. SOME years ago we reported1 a study of the oxidation of platinum in ordinary oxygen in the temperature region above 800°C, where the oxide is volatile. All the data available up to that time had been obtained with platinum crucibles or plates heated in tube furnaces. The results were widely variant and highly dependent on the flow rate of gas through the furnace: the faster the gas flow rate, the higher the measured oxidation rate. These results indicated to us2 that reaction equilibrium was being approached in the furnace and that the rate was diffusion limited. To minimize these effects, we employed1 electrically heated ribbons placed in a cooled bulb. We were primarily interested in the low-pressure region, but some experiments were performed at pressures up to 1 atm. We found a peculiar pressure dependency which was explained on the basis that the rate of oxidation was proportional to the pressure at all pressures, but that with increasing pressure an increasing fraction of the volatilizing oxide was back-reflected to the ribbon by the surrounding gas molecules. The oxide molecules are not stable at the temperature of the platinum and are decomposed on impact, the platinum being re-deposited on the specimen. Because of the limitations of space, this explanation was offered summarily without detailed support. Recently, Jaffee and associates3, 4 have suggested that the pressure dependency of our data up to 0.5 torr could be explained on the basis of a Langmuir-type adsorption of molecular oxygen followed by dissociation. Since the correct explanation of the effect of pressure on the oxidation rate is a necessary requirement to the development of the basic mechanism of the oxidation reaction, we felt that the back-reflection theory should be presented in more detail. This is the object of the present paper. RESULTS AND DISCUSSION A typical set of results showing the pressure dependency of the oxidation reaction is presented in Fig. 1, where we have plotted, on logarithmic scales, the rate of oxidation, R, vs the pressure, p. For comparison some results of Krier and Jaffee4 and of Raub and plate5 are also shown. These data were taken at atmospheric pressure using furnaces. The effect of reaction equilibrium within the furnace is apparent from the much smaller values that these observers obtained: Raub and Plate In O2 found a rate of 3.1 µg cm-2 hr-1 compared to our value of

Jan 1, 1965

By T. Vasilos, J. T. Smith

THE mechanism of pressure sintering, or hot pressing, for ceramic materials, has been investigated by several researchers.1-8 Plastic flow has been suggested as the rate-determining mech-anism1,2 while grain boundary sliding3,4 and fragmentation processess have been found controlling in other studies. Vasilos and Spriggs5,6 have reported that pressure sintering occurs by a diffusion-controlled mechanism. For the pressure sintering of metals, investigations with lead7 and with tin6 have not identified the operative mechanism during consolidation of these powders. This note reports the results of a pressure sintering study initiated to determine the mechanism controlling the densification of spherical copper powder. Temperatures of 300°, 400°, 500°, and 600°C at 2500, 5000, 7500, and 10,000 psi pressures were investigated. The copper powder for this study was obtained from Metals Disintegrating Co., Elizabeth, N.J. The minimum purity was reported to be 99.9 pct. The powder size was -325 mesh and a lineal analysis showed the average size to be less than 1 p. An alumina die body and punches were employed. Graphite spacers were placed between the copper powder and the punches before pressing. It was expected that the graphite would form carbon monoxide with any entrapped air and form a reducing atmosphere within the die cavity. This condition was generally realized during pressing although a minor amount of oxidation occurred at 500" and 600°C. The oxide particles were located randomly in the pressed samples and were not considered to influence the densification process. Calibration tests showed the temperature of the copper pellet to be about 20°C less than the die wall temperature, probably resulting from heat losses through the punches. This difference was compensated during the experimental pressing operations. The hot pressing equipment employed for this work has been described by Spriggs et a1.9 and was calibrated with a Baldwin-Lima-Hamilton load cell. Travel of the punches was monitored with a dial indicator showing increments of travel to 0.0005 in. Relative density was calculated at selected time intervals for a known copper weight, punch travel, and die diameter. The accuracy of this calculation was *1 pct. Average grain size after hot pressing was obtained by lineal analysis. Typical densification curves are presented in Fig. 1 and Fig. 2 where relative density is plotted vs log time as a function of applied pressure for the 300" and 600°C pressure sintering temperatures, respectively. The curves for 400" and 500°C were similar to those at 300°C and consequently are not shown. The curves at 300°C as well as 400" and 500°C do not show an end-point or limiting density for a particular applied pressure. At 600°C, a density in excess of 95 pct of theoretical has been reached such that further densification is extremely slow for the 5000, 7500, and 10,000 psi pressures. It is suggested that further densification at these pressure levels may be retarded or prevented by discontinuous grain growth, by entrapped gases, and by other microstructural limitations as described by Cob1e.10 The curve for 2500 psi hot pressing pressure is a straight line over the time interval although a slight change in slope may be occurring at the last time intervals. The plastic flow models,1,2 derived for hot pressing, predict the existence of an end-point (or limiting) density dependent on the yield point of the material at the temperature of interest. The yield stress of copper at a 0.005 strain level has been

Jan 1, 1965

By Philip N. Adler, Harold Margolin

Univariant equilibria between the Ibcc, IIhcp, and UIfee phases of thallium have been determined and indicate a triple point at 110°C and 37 kbars. Calculated II —I transformation curves are compared with the experimental. Transformation volumes and/or enthalpies are calculated and enthalpies are compared with available data. ThE triple point of solid thallium has been reported by Bridgman as 153°C and 38 kbar.' More recently, Jayaraman et at.2 have reported the triple point as near 115°C and 39 kbars. Meyerhoff and Smith,3 assuming the elevated-pressure modification of thallium is fcc, as Kaufman suggested,4 and that it is continuous with the room-temperature fcc phase in the Tl-In system, have used pressure data up to 5 kbars to predict the triple point at 162°C and 35.8 kbars. Piermarini and weir5 have indeed found the elevated-pressure phase to be fcc. The effect of variations of pressure and temperature in the IIhCp — Ibcc transformation in thallium have also been reported by werner6 and more recently by Ponyatovskii.7 The work reported here is part of an investigation of the effects of temperature and pressure on the Tl-In system. I) EXPERIMENTAL PROCEDURE The onset and progress of transformation were determined by changes in resistance. A commercially available tetrahedral-type pressure apparatus was used. Specimens of 0.060 in. diam, representing 0.63 pct of the cell volume, were encased in AgCl and mounted in pyrophyllite, as shown schematically in Fig. 1. It can be seen that the specimen is in series with the graphite furnace. Resistance changes of 0.1 pct could be detected with a Kelvin bridge. Resistance of the sample was of the order of 1 milliohm. Other pertinent details in regard to calibration and cell-assembly design are given elsewhere.' Temperature calibration of the cell was carried out in two ways as a function of input wattage. Through a hole drilled in the graphite furnace, a chromel-alumel thermocouple was inserted into the AgCl to a point 0.010 in. from the sample, with the

Jan 1, 1964

By J. W. Rutter, K. T. Aust

In previous studies of grain boundary migration in zone-refined lead, the authors used bicrystal specimens consisting of a striated crystal which was grown from the melt, and an adjacent striation-free crystal, introduced by artificial nucleation and growth.1 While this method permits the study of the motion of individual grain boundaries, it does not provide control of the relative orientations of the grains. The present note will describe a technique for controlling the orientations of the two crystals in this type of specimen. The technique consists essentially of placing a striated crystal and a striation-free crystal of controlled orientations end-to-end in a graphite trough, then melting a short zone at the junction of the two crystals and allowing it to freeze to form the desired grain boundary. The apparatus used to carry out this process is illustrated in Fig. 1. It consists of a trough milled from high-purity graphite,with grooves in the underside for the placement of thermocouples. The graphite piece fans out on one end at the level of the bottom of the trough; the sides of the trough are completed in this region by the attachment of a mating plate with a slot cut at any desired angle to permit reorientation of the crystal placed at this end of the assembly. The joint between the crystals is made at or near the point where the slotted plate joins the rest of the trough. The thermocouple slots are deepened in this region so that the thermocouples are separated from the melt by only 1/32 in. of graphite. An induction heater, with suitable temperature control, is used to obtain the molten zone. The two single crystals used are first chemically polished in a solution consisting of eight parts glacial acetic acid and two parts 30 pct hydrogen peroxide. They are then placed in the trough with the ends to be joined at the position of the thermocouples. Next, cooling is applied to the two crystals by means of air

Jan 1, 1962

By T. E. Leontis

Several publications1-7 during the past few years have demonstrated the markedly greater effect of cerium, as compared to all other alloying elements, in enhancing the strength and creep resistance of magnesium at elevated temperature either with or without the presence of other elements. In the work reported in Ref. 1-6, the cerium was added in the form of Mischmetal, which contains all the rare earth elements in essentially the same proportions as they occur in monazite sand, the principal ore of these metals. Mellor and Ridley7 have presented the creep characteristics at 200°C of magnesium alloys prepared both with pure cerium and with Mischmetal. Up to the present time, however, no comprehensive study of the effect of the various component elements of Mischmetal on the properties of sand-cast magnesium has been made. This hiatus in magnesium technology undoubtedly is associated with the difficulty in obtaining the rare earth metals separately. This investigation provides such a survey, the object of which was to determine which of the elements present in Mischmetal contributes the greatest effect in developing high strength and high resistance to creep at elevated temperatures. Toward this end the compositional variation of these properties has been determined as a function of temperature in the following alloy systems: 1. Magnesium-Mischmetal 2. Magnesium-cerium-free Misch- metal 3. Magnesium-didymiuin 4. Magnesium-praseodymium- lanthanum 5. Magnesium-cerium 6. Magnesium-lanthanum This designation, based on the names of the metals as furnished by the producer, is used throughout the paper in order to avoid the complicated system of listing all the elements present in the more complex alloys. The composition of the metals and the alloys is discussed in detail below. Preparation of Alloys ALLOYING INGREDIENTS The chemical composition of each of the six alloying ingredients used to prepare the alloys reported in this paper is given in Table 1. In each case, the percent total rare earths, percent cerium, percent neodymium, percent praseodymium, and percent thorium were determined in addition to the listed impurities. The percent lanthanum was determined by difference from the total rare earth content and consequently includes the other elements (samarium, terbium, yttrium, etc.) present in Mischmetal. These additional elements, however, seldom amount to more than 1 to 2 pet of the total rare earth content of Mischmetal. The iron content of the Mischmetal is considerably lower than that of the other metals. This grade of Mischmetal is now readily available. The metals are listed in the order of decreasing complexity. Elimination of the cerium from Mischmetal results in what the trade calls "Cerium-free Mischmetal." Carrying the separation a step further by eliminating the lantha-

Jan 1, 1950

By K. E. Nelson

The effect of thorium and zinc variations on the strength and 100-hr creep characteristics of Mg-Th-Zn-Zr alloys was investigated. Optimum resistance to creep at 650° and 700°F are attainable within a certain range of thorium and zinc contents. This range does not conform to that which develops maximum tensile properties. RAPID advances have been made during the last few years in the development of magnesium alloys for elevated temperature applications demanding high resistance to creep. The beneficial effect of rare-earth metals on the creep resistance of magnesium alloys has been emphasized by a number of publications1-13 and such alloys are now in commercial production. The use of thorium as an alloying ingredient in magnesium was mentioned by McDonald and also in two Alien Property Custodian patent applications.10,17 The initial observation of Sauerwald that thorium contributes still higher creep resistance to magnesium than is attainable with rare-earth metals has recently been substantiated.'" " In fact, it has been demonstrated that the useful temperature range of magnesium alloys is appreciably extended by the use of thorium. In all cases, it was observed that zirconium must be included in the alloys in order to render them fine grained and more readily castable. Several recent publications:2-27 indicate that a still further improvement in creep resistance and a further extension of the useful temperature range can be realized by the addition of zinc to alloys. The primary purpose of this paper is to present the results of a comprehensive study of the effect of zinc on the strength and creep characteristics of Mg-Th-Zr alloys. Compositions covering the range of thorium content from M to 6 pct and zinc content from 0 to 5 pct have been investigated. The creep characteristics at 650" and 700°F reported in this paper are based on results of tests of 100-hr duration. It is appreciated that creep tests of 100-hr duration might not yield adequate data for design purposes for parts with much longer expected life. However, for the purposes of the present discussion, it is felt that the combination of stresses and temperatures used in the 100-hr creep tests have yielded a clear representation of the compositional variation of creep resistance at the temperatures investigated. Creep tests of 1000-hr duration are now in progress on a few of the most promising alloys. Preparation and Testing of Alloys The alloys studied in this intensive investigation were prepared in 25 lb capacity mild steel crucibles. The thorium, zinc, and zirconium were alloyed and poured as described in earlier publications The thorium was introduced into the melt in the form of a Mg-Th hardener," the zinc added in the metallic form, and the zirconium alloyed in the form of the commercial hardener containing magnesium and 30 to 50 pct Zr.10, 26 Fluxing practices for melting and refining were the same as for magnesium-rare-earth metal-zirconium alloys. The melts were sampled for analytical determinations and poured into separately cast 1/2 in. diameter standard tensile bars. The test bars were given a precipitation treatment of 16 hr at 600°F in laboratory furnaces. It has been shown by other tests that a high temperature solution treatment followed by an aging treatment is unnecessary for the development of optimum properties in Mg-Th-Zn-Zr alloys. The selection of 600°F as the aging temperature was based on an attempt to achieve metallurgical stability without coalescence of the undissolved phases and the attendant loss in strength. The thorium, zinc, and zirconium contents of each melt were determined chemically. The zirconium contents are reported in two parts, "soluble" and "insoluble," referring, respectively, to the portions present in the alloy which are soluble and insoluble in dilute HCl acid. Distinction is being made between these two components of the zirconium content in the alloys because it has been found that only that portion of the zirconium content which is soluble in dilute inorganic acids affects the structure and properties of the alloys. The usual impurities consisting of copper, iron, manganese, and nickel were determined spectroscopically. The analysis for each melt is listed in Table I. A description of the methods of tension and creep testing has been detailed in earlier papers. The tests were performed with the cast skin re-

Jan 1, 1954

By J. J. Casey, R. S. Busk, D. L. Leman

The mechanical properties and the phase-temperature relationships of magnesium-lithium-aluminum, magnesium-lithium-zinc, and magnesium-lithium-aluminum-zinc alloys are presented. It is shown that the strengths of some of these alloys can be tripled by heat treating and aging but that the high strength is accompanied by brittleness and lack of stability. MAGNESIUM-LITHIUM alloys are interesting because the hexagonal structure of magnesium can be changed into the more ductile and workable body-centered cubic structure by the addition of only 10 pct lithium.1 After Loonam2 determined that the ductility of the magnesium-lithium alloys is destroyed by even trace quantities of sodium, it was possible to prepare ductile alioys and study their mechanical properties. Jackson3 and coworkers have ably described their results with both the binary and polynary magnesium-lithium alloys. The present paper is a report of the mechanical properties of wrought magnesium-lithium-aluminurn, magnesium-lithium-zinc, and magnesium-lithium-aluminum-zinc alloys. Experimental Procedure The alloys were made by melting 7 lb of magnesium in a steel crucible under a molten flux of 75 pct LiCl + 25 pct LiF3 previously dried at 1600°F. The metal was heated to 1300°F for alloying aluminum and zinc and then cooled to 1250°F for adding lithium (sodium content: 0.01 to 0.04 pct). After the lithium had been alloyed, dry LiF powder was sprinkled on the melt to thicken the excess flux. After a 15 min holding period, the flux was skimmed off. Paraffin vapors were used to protect the metal as it was poured into 3 in. diam by 11 in. long magnesium molds. Billets were extruded into 3/8-in. diam rod and 1/16 x 3/4-in. strip; sheet was prepared from 1/8x 7/8-in. extruded strip, first by hot rolling and then by cold rolling 2 pct per pass. Hot rollability, or the temperature range through which the alloys could be rolled, was determined by rolling the strip two passes at 30 pct reduction per pass. Cold rollability, or the percentage of cold reduction to cause detrimental cracking, was determined on 0.064-in. hot-rolled sheet. Standard ASTM procedures were followed to obtain the mechanical properties, using 0.2 pct offset for the yield strengths. The level of properties produced with commercial magnesium alloys using the procedure described is given in a previous publication." Results Magnesium - Lithium - Aluminum System: The good workability of magnesium-lithium alloys is illustrated by the data in table I, which shows approximately how the extrusion pressure decreases as the amount of cubic phase increases. Binary magnesium-lithium alloys are soft and weak, but aluminum raises their strengths con-

Jan 1, 1951

By R. J. Allio, C. H. Randall

An automatic system for the quantitative analysis of microstrulcture has been developed. The method is based upon a statistical model of microstructure and employs phase intercept fractions as fundamental random variables. Structure-sensitive properties can be related explicitly to parameters derived from the distribution of phase intercept fractions in a matevial. THE properties of mechanical dispersions and of multiphase alloys art: intimately related to the amount, distribution, and intrinsic properties of the dispersed material. In many instances, the amount and distribution of the dispersed substances have greater influence on the over-all system properties than do the properties of the dispersed substance-Such properties as average particle size, particle size distribution, homogeneity of dispersion, volume per cent of dispersed phase, and mean free path between dispersed particles thus become critical in any evaluation of the properties of a dispersion. Unfortunately, techniques for evaluating quantitatively the microstructural characteristics of dis~ersions rapidly and accurately have not been available. If necessary, qualitative or semiquantitative devices can be utilized. Some such devices are based merely upon comparison of the specimens in question with arbitrary standards. Other techniques involve superposition of grids and tabulation of particles observed in different portions of the grid. Still other methods based upon lineal analysis entail counting lines or points at random upon the specimen to be examined; the number of intersections of the line with a given phase, the proportion of line or number of points which are covered by given phase are variously recorded. The mathematical basis for most of the techniques of quantitative metallography have been amply reviewed in the literature.'l2 without exctption, however, the standard techniques for quantitative metallography are either imprecise or are exceedingly tedious to apply. For example, tranverse integrating stage for rapid manual areal fraction measurement has been designed by Smith.3 Howerer, as in the case of any device based upon visual eslimation, operator bias may cause appreciable error. Various flying spot devices, on the other hand register particle size distributions in 2-dimensions, from which it is difficult to derive other properties of the dispersion. Thus, e.g., the 3-dimensional distribution cannot be inferred unless certain rather broad assumptions are made concerning the randomness of distribution and geometrical configuration of dispersed phase. Many limitations to the application of quantitative structural analysis can be overcome by the use of the microdensitometer, which is essentially an automated areal analysis device. Data obtained in the form of a distribution of phase intercept values are

Jan 1, 1962

By R. P. O’Shea

AS part of a program to investigate phase relationships in ternary systems containing semiconducting elements and compounds, an X-ray survey of alloys in the system Pb-Te-Bi was carried out which revealed that the pair PbTe-Bi probably formed a quasibinary system. This portion of the ternary was examined fully by thermal analysis, X-ray, and microscopic procedures. More than twenty-five alloys were made by melting together the proper combinations of the elements in quartz tubes at a temperature of 1000o C. The compositions which were high in PbTe content were prepared in evacuated, sealed, quartz tubes, allowed to freeze in vacuum, and then transferred to Crucibles for thermal analysis. The bismuth-rich alloys were made directly in the crucibles under a protective gas cover. The starting elements were obtained from the American Smelting and Refining Co. and had a purity greater than 99.99 pct. Cooling curves were made with about 50 g of alloy in graphite crucibles which were placed in a covered quartz container in which a protective atmosphere of helium or nitrogen was maintained. The thermocouple protection tube was made of mul-lite and served as a stirring rod when connected to a reciprocating stirring motor. Temperatures were

Jan 1, 1962

By C. G. Dunn, W. W. Martin

Various X ray diffraction techniques have been developed for determining orientations of crystals. Transmission and back-reflection Laue methods1,2,3 in particular have been found to be very useful. In many applications, however, a need still exists for a simplification of the details of analysis so that orientations can be determined more rapidly, and operators with little or no training in crystallography can be easily instructed in the necessary procedures. Filling this need in part is a system of analysis that has been in use for several years in the Metals Section of the Laboratory, General Electric Co., Pittsfield, Mass. This method is an extension of the one of Majima and Togino,4 which uses fifty-five indexed standard transmission Lauemams to cover the entire range of crystal orientations. Greater rapidity in determining the orientation of a crystal is achieved by using a slightly larger set of standard Lauegrams and by systematizing the steps followed. This system of analysis in its present form constitutes the subject matter of the present paper. Although the method uses transmission X ray Laue patterns, many of the operations are applicable to the analysis of back-reflection Lauegrams. Very briefly the method is based on the fact that Bragg and azimuthal angles for two or more identified Laue diffraction spots completely determine the orientation of a crystal, and standard Laue photographs of the Majima and Togino type provide a ready means for identifying Laue spots. After a preliminary analysis, which consists of identifying the pattern in terms of one of the standard patterns, a correctly marked Lauegram is selected to carry out the final analysis. From measured Bragg and azimuthal angles, the normals (poles) of the reflecting planes for the selected Laue spots are located on a stereographic projection and the orient.at.ion of the crystal determined (in terms of the positions of cube poles for example) by a few additional operations on a \I1ulff net. The actual procedure followed will be illustrated in detail after a brief treatment or X ray problems connected with orientation determinations and a discussion of useful principles and techniques. X Ray and Plotting Problems RELATIVE ADVANTAGES OF BACK-REFLECTION AND TRANSMISSION LAUE DIFFRACTION METHODS In the back-reflection Laue method it is easy to make a direct measurement of the tilt of a zone of Laue spots. Specimen thickness also is generally no problem. In the case of thin specimens, however, the time of exposure is less for the transmission Laue method. For example, with silicon ferrite this advantage holds up to a thickness of 0.6 mm if tungsten radiation at 40 kv peak voltage is used. Furthermore, the transmission photograph represents the entire thickness of the crystal whereas the back-reflection picture represents only a surface layer (a thickness of less than 0.05 mm for silicon ferrite), the deeper layers supplying a negligible amount to the diffraction pattern. If a crystal is distorted, the transmission Laue pattern gives more information particularly with regard to the orientation of the crystal and the overall amount of spread in orientation. Finally a 3 1/4 X 4 in. film suffices for transmission photograms; a 4 X 5 in. or 5 X 7 in. film with a central hole is needed for back-reflection patterns Not only is the manipulation of film easier because of the size of film, but

Jan 1, 1950

By G. R. Speich, R. A. Oriani

The rate of coarsening (Ostwald ripening) of copper precipitate Particles in an a-iron matrix has been studied in three Fe-Cu alloys containing 2.3, 4.0, and 5.4 wt pct Cu in the temperature range 730° to 830°C. The kinetics of Ostwald ripening ohevs the law as deduced by Lifshitz and Wagner so that matrix diffusion controls the process. The equilibrium shape of the particles is that of rods with hemispherical caps, and is due to the BOTH Lifshitz and slyozov and wagner3 have recently solved the complex problem of determining the rate of coarsening of an assembly of precipitate particles. Both workers, although using somewhat different mathematical approaches, arrive at the same equation for the relation between the mean radius 7 of a distribution of spherical particles and the bulk solubility co, diffusivity D in the matrix, large anisotropy in the copper/a iron interfacial free energy (y,/y, = 4). A Lifshitz -Wagner equation, modified for both the nonsphericity of the diffusion field and the reformulation of the Gibbs-Thomson equation for the case of nonsphencal particles, is derived. Using the modified equation, the calculated values of the mean radius are smaller than those observed by a factor of about one -half. absolute temperature T, gas constant R, surface free energy y of the precipitate/matrix interface, and the time t of aging: where V, is the molar volume of the precipitate and v is a stoichiometric factor. Wagner's treatment is restricted to the case of spherical particles growing in a liquid matrix where strain energy is not a factor. Lifshitz and slyozov have discussed the effect of anisotropic particle shapes and internal strains on the rate of coarsening. Oriani4

Jan 1, 1965

By R. M. Hudson

The removal of nitrogen from a nitrogenized low-carbon sheet steel that contained 0.011 wt pct N was determined during heat treatment in Hz-N, mixtures. TIze process followed a first-order rate law; that is, plots of the logarithm of nitrogen content in steel were linear with the time of treatment at a given temperature. The rate of removal increased with an increase in temperature from 900" to 1300°F. By 1400°F the rate in dry hydrogen had decreased to a value intermediate between the rates at 1200" and at 1300°F; in wet (2.47 vol pct water vapor) hydrogen the rate at 1400°F was less than the rate at 1300°F and nearly the same as the rate at 1200OF. The rate at a given temperature increased as the 3/2 power of hydrogen concentration in the atmosphere. While wet atmosplzeres were generally more effective than the corresponding dry atmosplzeres, the effect of water vapor was much less pronounced than the influence of hydrogen content. NITROGEN is the principal agent in the strain aging of ferrite, the effect of carbon being secondary.' To eliminate the return of the yield point after straining and aging, it is claimed2 that the amount of nitrogen in solution in steel must be reduced to 0.0002 wt pct. Strong nitride-forming elements (titanium, vanadium, zirconium, and aluminum) can act to eliminate strain aging by combining with nitrogen. It is extremely difficult to decrease the nitrogen content in commercial steels to the low level required by conventional coil annealing because of the poor contact between the strip surface and the reactive atmosphere. However, a variety of gas-metal reactions can be effected by use of the open-coil annealing method,3 in which the metal surface is fully exposed to the atmosphere. With this possibility in mind, the Applied Research Laboratory has studied the influence of time, temperature, and atmosphere composition on the removal of nitrogen from low-carbon sheet steel. MATERIALS AND EXPERIMENTAL WORK Samples from a commercial nitrogenized low-carbon steel (0.010 in. thick) in the cold-reduced condition were used. The chemical composition of this steel is given in Table I. The gas mixtures used are listed in Table 11. The moisture content in the "wet" annealing atmospheres was controlled at a +70°F dew point (2.47 vol pct water vapor) by passing the gas mixture through a glass tube packed with a solid mixture of 10 pct anhydrous oxalic acid and 90 pct oxalic acid dihydrate held at 127°F; this technique has been described previously.4 For "dry" atmospheres, the gas mixtures were passed through a cold trap immersed in liquid nitrogen. A hinged-top Hevi-Duty electric furnace was used with a Vycor-glass furnace tube. When the furnace was at the desired temperature, the gas mixture was passed through the furnace at a flow rate between 1.1 and 1.2 cfh; coupons (size 3 by 3/4 in.) of the steel were pulled into the center of the Vycor-glass

Jan 1, 1964

By A. K. Mukherjee, John E. Dorn

The effects of strain rate and temperature on the critical resolved shear stress for (321)[111] slip were determined for the silver-rich CsCl type of intermetallic compound AgMg. The flow stress increased only slightly as the test temperature was first decreased below room temperature; a rapid increase in the flow stress was obtained with yet further decrease in temperature from about 250' to 4OK. The effect of both the temperature and strain rate on the flow stress over the low-temperature range could be rationalized satisfactorily in terms of the Peiwls mechanism when the deformation was controlled by rate of nucleation of pairs of kinks. IN spite of the well-documented interest of metallurgists and engineers concerning the mechanical behavior of intermediate phases and intermetallic compounds, very little definitive information is available on this important subject. As recently summarized by westbrook,1 only limited and modest progress has been made thus far in elucidating the details of the mechanism of plastic deformation for the intermetallic compounds; the available information largely concerns phenom-enological descriptions of empirical observations and experimental facts, principally with reference to poly crystalline aggregates. The present report on the elucidation of the rate-controlling mechanism for slip in the bcc structure of AgMg is part of the comprehensive program of a systematic investigation on the mechanical behavior of intermetallic compounds. The intermetallic compound AgMg has a CsCl type of lattice structureZ and is completely ordered up to its melting point of 820c3 This material was selected for our present investigation because of its simple crystal structure, moderate and congruent melting point, ordered structure persisting up to the melting point, and some solubilities of the constituent elements, which could be expected to help in the growing of single-crystal specimens. Whereas previous investigations on the properties of AgMg include hardness,*"6 slip systems,7 tensile flow stress of polycrystalline specimens,' and electrical resistivity,4 the current investigation will be directed principally at elucidating the rate-controlling dislocation mechanism responsible for slip in single crystals at low temperatures. It will be shown that the strain rate is consistent with a model involving the rate of nucleation of pairs of kinks by the Peierls mechanism for plastic deformation. EXPERIMENTAL TECHNIQUES Single-crystal specimens of the AgMg intermetallic compound were prepared and tested as follows: 1) A master alloy ingot of AgMg was produced by melting and chill casting the high-purity silver (99.995 wt pct) and high-purity magnesium (99.997 wt pct) in an induction furnace under a helium atmosphere. 2) Sections of the above-mentioned ingot were placed in a graphite mold containing a spherical cavity in which a single-crystal sphere of 1 in. diam was grown under helium by the Bridgman technique. 3) The operative slip systems were investigated at room temperature on a singlecrystal of AgMg, from measurements of the angles made by the slip traces on the two surfaces of the specimen, which were at 90 deg to each other. The investigation confirmed that the AgMg compound undergoes slip primarily in the (321) plane and in the [Ill] direction, but a small amount of secondary slip was also noticed in the (112) (111) system. No slip was observed in the (110) planes. 4) The single-crystal sphere, mentioned earlier, was oriented in a graphite mold containing a cylindrical cavity of 3/8 in. diam above the spherical receptable to give the angle xo = 45 deg between the axis of the cylindrical bar and the normal to the slip plane (321), and the angle AO = 45 deg between the slip direction [Ill] and the axis of the bar. Oriented single-crystal bar seeds were produced by melting, under a helium atmosphere, a polycrystalline bar in the cylindrical cavity above the oriented spherical seed and by growing an oriented single-crystal bar from the seed. 5) Finally, oriented single-crystal specimens were grown from these cylindrical seeds. 6) The cylindrical specimens were machined in a High-Tension Spark Cutting unit to give a 2-in. gage length. The spark-machined gage section was elec-tropolished in a bath containing 200 ml of H3PO4,

Jan 1, 1964

By Allan T. Gwathmey, J. Bruce Wagner, Kenneth R. Lawless

Between 250°and 550°C in oxygen pressures of 10 to 760 mm Hg, the relative oxide thicknesses formed per unit time on the (100), (111), (110), and (320), decreased in this order. The predominant oxide orientation was (001)Fe3O4 and [110] Fe304 A small amount of a-Fe2O3 which exhibited a fiber pattern was observed in all oxides except those formed at 250°c in low oxygen pressures. IN order to understand the properties and behavior of thin films, particularly their role in oxidation reactions, there is needed more experimental information on their structure, composition, and kinetics of formation on clean surfaces of known geometry. The present study was undertaken to obtain such information for thin oxide films formed on single crystals of a body centered cubic metal, iron. Crystals in the form of spheres were used in order to expose all possible crystal planes to the reactant gases simultaneously. Using this procedure the relative rates of oxidation of all planes could be estimated, and those exhibiting, maximum or minimum oxidation rates could be selected for a more intensive study of composition and expitaxy. Since the three types of information were obtained from the same experiment using a single crystal substrate, any differences between rate, composition, and expitaxy on the several planes may be attributed to the influence of the substrate structure. EXPERIMENTAL The starting material for this study was Armco iron rods, 6 in. long and 3/8 or 1/2 in. in diam. The analysis was reported to be 99.8 pct Fe, with major impurities listed as carbon 0.018 pct, manganese 0.027 pct, phosphorous 0.005 pct, sulfur 0.029 pct, silicon 0.005 pct, and copper 0.11 pct. These rods were cleaned with ether and heated in an atmosphere of moist hydrogen at 950°C for three days. The purpose of this treatment was to decarburize the iron and to provide a consistent, uniform grain size for the growth of single crystals. Crystals in the form of rods, up to 1/2 in. in diam and 2 in. long, were prepared by a method similar to that reported by Leidheiser and Buck.2 Spherical crystals, 3/8 and 1/2 in. in diam and having a handle about 1/4 in. in diam by 112 in. long, were machined from the single-crystal rods. After machining, each crystal was etched in aqueous nitric acid to remove the cold-worked metal at the surface. Before each experiment, the crystal was polished mechanically with metallographic papers through number 4/0, and electropolished in a perchloric acid-acetic anhydride mixture by the method of Jacquet and Rocquet.3 The crystal was washed in running distilled water for at least 5 min. The excess water was blotted with a soft paper tissue, and the crystal was placed in an all-glass reaction vessel (See Fig. 1). The crystal was heated at 550°C in hydrogen for at least 8 hr prior to the oxidation in order to reduce any surface oxides and to help relieve any stresses in the metal. For the structure and composition studies, flat faces were cut parallel to (loo), (111), and (110) planes on the iron crystal spheres. The orientation of these faces was checked by a back-reflection X-ray diffraction technique. The faces were within 2 deg of the desired orientation. The flat faces were treated as described above except that prior to electropolishing they were given an additional polish on metallographic felt saturated with twenty-minute levigated alumina. After the crystal was heated in hydrogen for at least 8 hr, the temperature was adjusted to the desired value, and the hydrogen was evacuated. Commercial oxygen which had been purified by successively passing through tubes containing magnesium perchlorate, Ascarite and magnesium perchlorate was admitted to the desired pressure as measured by a mercury manometer. A resistance-wound furnace surrounded the oxidation chamber, and a temperature controller maintained the temperature within ±3°C. The furnace was provided with a small window for observing the crystal. The changes in thickness of the oxide films were followed by observing the interference colors. The oxidation was allowed to proceed until the desired oxide thickness was attained on a given crystal plane. The experiment was terminated by evacuating the oxidation

Jan 1, 1962

By A. Bar-Or, G. Hirsch, P. Wynblatt

The rates of nucleation and growth at various temperatures in U-0.45, 1.1, and 1.35 at. pet Cr alloys were determined, providing a qliantitative proo-f that the transformation under study is controlled by nucleation and diffusional growth. The linear relationship, log NV US 1/T2, suggests that the nucleation of the alloys is probably controlled by the classical law of nuclei formation. The established linear relationship, log G us 1/T, in the three alloys suggests that growth in each alloy is controlled by bidimensional nuclei formation. It was established that both the rate of growth and the rale of nucleation are retarded by chromium. Using classical formulae, sApN and sApG (the ß/a apparent interphase energies) were calculated from the nucleation and growth results, respectively. It was found that their values are of the same order of magnitude. However, why sApN is unaffected by the addition of chromium, while sApG increases with it, needs further clarification. In the last few years, an appreciable amount of research has been conducted into the mechanism of the ß —a transformation in uranium and uranium alloys. Recently, Burke1 reviewed the published work concerned with this transformation. He concluded that in dilute uranium alloys it is firmly established that, at high temperatures in the a range, ß decomposes by a diffusional process. However, he based his conclusion either on experiments dealing with the over-all transformation,2 or on qualitative results.3 It was felt that a better insight into the mechanism of transformation could be gained from the quantitative measurements of growth and nucleation rates, which we aimed to carry out in the present work. In a previous work,4 we have shown that a rim of a grains is formed during isothermal transformation at the high a range. The thickening of this rim with time was used for measuring the rate of growth in U-0.45 at. pet Cr.5 This method was also used in the present work for two more alloys. For meas- uring the rate of nucleation, a method of quenching and macroetching was developed to allow differentiation between a grains formed during isothermal transformation at the upper a range and those formed after quenching, Fig. 1. EXPERIMENTAL WORK AND RESULTS The Rate of Nucleation. The measurement of the rate of nucleation was effected by counting the num-

Jan 1, 1965

By Klaus Detert, Joseph Ziebs

The progress of primary recrystallization has been studied in alloys of nickel with 0.01, 0.1, and 1.0 at. pct Ta. It can be shown that in one particular alloy containing 0.1 Ta and 0.02 02 a large grain structure (0.5 mm diameter) could he developed by primary recrystallization in thin sheetswhich were cold-worked to 97.5 pct reduction in thickness. Electron transmission microscopy demmstrates that this phenonmena was linked to the occurrence of fine precipitates at subboundaries. A discussion of how fine precipitates can exert under certain circumstances a rather distinct retarding effect on nucleation rate is included. IN a former investigation, the recrystallization and texture formation in a series of binary nickel alloys including pure nickel were studied.' Nickel alloys with some tantalum added displayed peculiarities during primary recrystallization which have been studied in more detail by the present investigation. The alloys were prepared by powder-metallurgy techniques similar to the previous investigations.' Pure metal powders were thoroughly mixed to obtain alloys with 0.01, 0.1, and 1.0 at. pct Ta, referred to as alloy A, B, or C, respectively. The metallic impurities were kept below 0.005 at. pct except iron and cobalt with slightly higher values, by using highly purified nickel and tantalum powders.' The mixtures were pressed into bars and sintered at a temperature of 1300°C. The sintering atmosphere was either high vacuum, dry hydrogen, or wet hydrogen. The sintered rectangular bars were rolled 60 pct to a thickness of 3 mm, then annealed under dry hydrogen at 1000°C and again cold-rolled to about 97.5 pct reduction of thickness. After this heavy deformation, the sheet thickness was 0.07 5 mm. In order to study primary recrystallization which occurred in measurable times between 400" and 600°C, samples of the rolled sheets were annealed in a salt bath at various temperatures for various times in order to study the progress of recrystallization by hardness measurements and microscopic examination. For optical observation, the samples were polished and etched in a solution of 65 cu cm HNO3, and 18 cu cm acetic acid in 20 to 100 cu cm H2O, depending of the particular sample and annealing treatment. For transmission electron microscopic observations, thin foils were prepared by the combined window and Bollmann techniques.273 The electrolyte consisted of 23 pct perchloric acid and 77 pct acetic acid held at 15°C. Polishing was performed at a current density of 0.4 amp per sq cm. The examination of the thin films was accomplished by a Siemens Elmiscope-type electron microscope operating with an accelerating voltage of 100 kv. RESULTS The progress of primary recrystallization was very accurately followed in these alloys in order to establish the time when recrystallization started and ended during an isothermal anneal. Table I gives some of the data obtained by these studies. The time for beginning is a mean value, where somewhat less than 5 pct of the matrix has recrys-tallized. The end of recrystallization is the time when at least 95 pct of the matrix has recrystal-lized. Listed are three different B alloys, with 0.1 Ta distinguished by different sintering atmospheres which influence the rate of primary recrystallization. By the above method, the state of the grain structure when primary recrystallization was completed, but grain coarsening had not started, could be clearly defined. The average grain diameter of the recrystallized matrix is also given in Table I. The grain size did not depend on the temperature of the isothermal anneal. With one exception the grain size of the primary recrystallized matrix was found to be rather fine

Jan 1, 1965