Search Documents

By D. F. Toner

THE decomposition of the ß phase in the copper-aluminum system has recently been subjected to considerable investigation1-4 As a result of this work, principally by Haynes, much additional interest has been aroused concerning the various transitional or metastable phases in the Cu-A1 system. No attempt has been made to resolve the question of whether the PI and ß" phases of Klier and Grymko5 are the same as the rosette-shaped phase first observed by Smith and Lindlief6 in 1933 during an isothermal transformation study of an eutectoid alloy. It is the purpose of this study, however, to obtain

Jan 1, 1960

By E. Buehler, H. J. Levinstein

The temperature ranges in which the three inter-metallic phases in the Nb-Sn system form have been determined and the composition and structure of two of the three phases has been established. The kinetics of the formation of Nb3Sn in cored wire samples has been studied in the temperature range of 800° to 1050°C. From 800°to 950°C the rate of formation increases by four orders of magnitude. The rate-controlling step for the formation process in this temperature range appears to be the diffilsion of tin through NbSn. At higher temperatu~es a change occurs in the mechanism of the formation process such that up to a temperature of 1050°C the rate of formation of Nb3Sn does not increase above the rate observed at 950°C. For temperatures helow 950°C the current-carrying capacity of the wire increases with increased percent reaction reaching a maximum value when the formation process is 90 to 95 pct complete. The maximum current-carrying capacity obtainable in this temperature range is independent of the temperature. Above 950°C tlze current-carrying capacity obtainable in the wire decreases with increasing temperature of formation. A model is proposed which accounts for the ohserved behavior. RECENTLY, Buehler et a1.l reported the results of an investigation of the process variables which influence the superconducting properties of Nb3Sn-cored wire. These results indicated that at least four variables affect the properties of the manufactured wire. These include composition, particle size of the starting powder mix, temperature of heat treatment, and time of heat treatment. In order to understand completely the role of these variables, it is necessary to have an accurate knowledge of the phase equilibria in the Nb-Sn system. At the present time, phase-equilibrium diagrams for the Nb-Sn system have been published by a number of investigators.2-5 The diagrams differ as to the number of phases present, the composition of the phases, and the temperature range of stability of the phases. The present investigation was undertaken in order to resolve these differences. Since the investigation of Buehler et al. demon- strated that the length of time at the temperature of heat treatment affected the superconducting properties of Nb3Sn, it is apparent that it is necessary to understand the kinetics of the formation process as well as the equilibrium conditions before a complete understanding of the system is possible. As a result, the kinetics of formation of the various phases in the system were also studied in this investigation. EXPEFUMENTAL PROCEDURE Diffusion couples and sintered powdered compacts were employed in the phase-diagram investigation. The diffusion couples were made by filling 1/8-in.-ID monel-sheathed niobium tubes with tin. The monel sheath was employed to facilitate drawing.' The tubes were then drawn to a tin-core diameter of 32 mils. Samples approximately 3 in. long were then cut from the drawn composite. The tin was drilled out of the ends to a depth of 1/4 in. and niobium-wire plugs were inserted into the ends and peened over. The monel was removed by etching in concentrated nitric acid, after which the samples were sealed in evacuated quartz bulbs and heat-treated in a resistance-wound tube furnace. The samples were quenched into ice water upon removal from the furnace. The diffusion couple samples were examined metallographically employing a chemical etching solution consisting of 10 ml of saturated chromic acid per g of NaF. In addition, two anodizing solutions were used for phase-identification purposes. The first was the picklesimer7 solution; the second consisted of equal parts by volume of 30 pct H2O2 and concentrated NH4OH to which 1 g of NaF was added per 25 ml of solution. The anodizing conditions for the second solution were 2 v and 100 ma with a tin cathode. The powdered compacts were made by pressing previously mixed powders of 99.9 pct pure Sn and 99.6 pct pure Nb supplied by the United Mineral Co. into cylinders 3/8 in. in diameter by 1/2 in. long. The cylinders were then sealed in quartz tubes and heat-treated in the same manner as the diffusion couples. The samples were examined metallographically and by X-ray diffraction techniques. Since it was desirable to be able to correlate the kinetic data with current-carrying capacity, the type of specimen chosen for this part of the investigation had to be a compromise between the optimum system for studying kinetics and one which was suitable for making current-carrying capacity

Jan 1, 1964

By David J. Mack, Chin Bea Kim

The decomposition of the Ni-Zn eutectoid at 56 wt pct Zn was studied by isothermal transformation. Its progress was followed by metallographic, hardness, and X-ray diffraction methods. Three transformation products were found: lamellar pearlite at high temperatures; an intermediate temperature structure; and martensite at the lower temperaCures. No transition structu,ves were found. THE decomposition of the Ni-Zn eutectoid at 56 wt pct Zn was stuadied as part of a long-range program of study on the eutectoid transformation in alloy systems which do not have one or more components which exhibit allotropy. Available information on the Ni-Zn eutectoid transformation is limited to that presented in connection with the determination of the phase dilagram. No systematic studies of the eutectoid were found in the literature, alkhough the microstructures of the Ni-Zn eutectoid were reported by Tamuru.3 X-ray diffraction data exist for the ß, ß1, y , and y1 phases.' EXPERIMENTAL PROCEDURE The eutectoid alloy was prepared from "A" nickel shot and Bunker Hill super-purity zinc (99.998 pct).

Jan 1, 1962

By H. M. Strong

Nickel and carbon form a metastable nickel-nickel carbide eutectic system which was ohsen)able by freezing latent-heat arvests at pressures 210 khars. The eutectic freezing temperature Is pressure had a slope of -0.9°Cper kbar. At 50 khars, the nickel-nickel carbide eutectic was at 1297° * 5°C and 0.34 mole fraction Ni3C. The composition of the eutectic increased at an initial rate of 0.004 mol fraction per kbar. The carbon content of the a phase also increased with pressure. Seveval illustrations of nickel carbide microstruc-tures are given and data on the lattice expansion of nickel in terms of carbon content are included. IRON, cobalt, and nickel form a variety of carbides with compositions varying between MeC and MC. Of the three, the carbides of iron are most easily recovered. The nickel carbides are so unstable at temperatures above 900°C that their occurrence in Ni-C alloys is unusual. Under sufficient pressure, however, the temperature range for the stability of the ferrous metal carbides is likely to be increased, or their decomposition suppressed (e.g., see Hilliard' on FesC), providing an opportunity to study the unstable carbides more closely. This was found to be true for nickel carbide which, under pressure, formed a eutectic with nickel. This paper describes the conditions of formation of nickel-nickel carbide eutectic compositions and their subsequent recovery. Despite the comparative instability of the nickel carbides, something is already known about them through various chemical reactions at temperatures not exceeding a few hundred degrees, and from their recovery by the very rapid quenching of molten Ni-C alloys from temperatures of about 1450°C or above. At least four carbides of nickel have been reported: A discussion of the state of knowledge about Ni3C is given by ansen.' The studies of Morrogh and williams7 who obtained Widmanstatten nickel carbide structures and of sidorenko8 who first obtained nickel carbide eutectic structures are also of interest. Sidorenko used short heating times for molten nickel in a graphite crucible followed by very rapid quenching to obtain the eutectic structures. Long heating times produced only the nickel-graphite eutectic probably due to the presence of graphite crystals in the melt which nucleated graphite crystallization. According to the early work summarized by anssen,' nickel carbide may form at temperatures far above the melting point and may be recovered by very rapid quenching. More recently, Giardini and Tydings, working on diamond synthesis, found evidence for "free nickel carbide'' in high-pressure reactions carried to temperatures far in excess of the limit for diamond growth, followed by rapid thermal quench. They stated that nickel carbide was not found in association with diamond growth. In the present work, observations were made on the melting and solidification temperatures of Ni-C alloys as a function of composition, temperature, and pressure. The nickel-nickel carbide eutectic was found at pressures above 10 kbar and its variation with pressure followed up to 60 kbar. Nickel-nickel carbide microstructures were recovered by quenching under pressure from temperatures of about 1400°C and higher. The formation of nickel carbide structures under ordinary diamond-growing conditions was usually observed but the role of carbide formation as an intermediate step in diamond growth needs more study. EXPERIMENTAL METHODS The melting and solidification temperatures of various nickel-graphite compositions were observed by latent-heat arrests in the sample holder illustrated in Fig. 1. The samples were composed of mixtures of carbonyl nickel powder and National Carbon Co.'s SP-1 graphite packed to densities of about 6.4 g per cu cm. They were contained within

Jan 1, 1965

By E. R. Stover, J. Wulff

A tentative 870°C isothermal section, the solidus equilibria, and the solubility of Tic and graphite in the nickel solid solution have been determined with arc-cast specimens. Each of the Ni-Ti intermetallics forms two-phase fields with Tic; only Ti,Ni has a measurable solubility for carbon. A quasi-binary eutectic exists between Tic: and a titanium-rich nickel solid solution; ternary eutectics occur on either side, with TiNis or with graphite. Graphite is in equilibrium with a nickel solid solution containing a ratio of Ti/C which increases below the solidus. DURING the past decade, titanium-carbide cermets containing nickel or cobalt alloy binders have been widely studied for high-temperature and wear-resistant applications. Recent work has emphasized control of the carbide grain size and distribution2's and the thermal exparision match between the phases/ The present study was initiated to determine the phase compositions during the sintering or infiltration process, and during subsequent heating. Although the effects of additives and impurities in commercial compositions are important, it was necessary to consider first the pure ternary, Ni-Ti-C. Emphasis was placed on the nickel corner, since the nickel solid solution is the continuous phase in compositions having highest strength. Early metallographic work by Zarubin and Molkov- showed that solid solubility at either end of the section Ni-Tic is small. Edwards and Raine reported that nickel dissolves between 3 and 5 wt pct Tic at 1250° C, on the basis of microstructures of annealed, vacuum-melted powder mixtures. Although the solubility of nickel in Tic has not been measured, Tic formed by the menstruum process in liuid-iron solution contains as little as 0.06 wt pct Fe. BINARY SYSTEMS The most recent determinations of the three binary systems are summarized in Fig. 1. Titanium carbide (6) is predominant among the binary phases, and it melts above the boiling point of nickel. The Ni-C binary is based on separate liquid solubility' ) and solid solubilitylo measurements. The eutectic temperature, 1328OC, is taken from the solidus determination described below. However thermal analysis data by Morrogh and williams also show eutectic arrests in this vicinity in the absence of supercooling. The Ni-Ti binary is taken from the work of Poole

Jan 1, 1960

By N. J. Grant, B. C. Giessen, R. Koch

The system Nh-Ir was investigated over the complete concentration range by metallography and X-my techniques, using forty one alloys. The solubility limits of terminal and intermediate phases and the solidus temperatures were determined. Five intermediate phases were found: a Nb3Ir, cubic, Cr3O type; tetragonal, ofecr thorhomhic, isostruc-turn1 with (ta-Rh); and a Nhlr3. cubic, AuCu, type. a Nb3lr and a Nbfr3 melt congruently; three eutectic and three pentectic reactions occur. The phase diagram of the Nb-Ir system had not been fully treated in the literature; only surveys of intermediate phases were found.1"5 In this study, the details of the phase boundaries were investigated as well as the crystallography of the intermediate phases. EXPERIMENTAL METHODS The experimental procedures such as arc melting of powder compacts, heat treatments, solidus measurements, X-ray, and metallographic observation were identical with those used in the work on the Nb-Rh phase diagram.&apos; They will therefore not be repeated here except where the conditions differed. The purity of the niobium powder was as stated in Ref. 6; the iridium powder of 99.9+ pct purity from J. Bishop and Co., Malvern, Penn., did not contain impurities exceeding 100 ppm, except rhodium (200 ppm). The melting points and vapor pressures of both elements are very similar. This fact contributed to a very small weight loss on melting and facilitated preparation of homogeneous alloys. As shown in Ref. 6 for Nb-Rh, no oxygen pick-up exceeding 200 ppm had to be considered; this was regarded as valid also for Nb-Ir. A total of forty one alloys were used in the determination of the phase diagram; their concentrations are shown in Fig. l, which presents the phase diagram. The concentration limits as determined by the weight-loss method averaged <0.2 at. pct, and never exceeded 0.5 at. pct. Heat treatments were carried out as described in Ref. 6. Depending on the concentration, only tantalum, tungsten, or iridium containers were employed, avoiding oxide crucibles altogether. Alloys from 0 to 25 and from 65 to 100 at. pct Ir were homogenized at 2095°C for 15 hr, intermediate compositions from 25 to 65 at. pct Ir for 65 hr at 1780°C. A typical annealing-time schedule is presented in Table I. Solidus points were measured as described in Ref. 6 with the modification that samples rich in niobium were held between pieces of tantalum foil and samples of high iridium concentrations were held between rhenium platelets or in iridium wire. After each run it was ascertained metallographically that no reaction with the holder had occurred. Rhenium was selected as holder material after it had been shown in separate tests that the melting points of Re-Ir alloys rise continuously from 2440°C. Metallographic examination was carried out as described in Ref. 6, and the same procedure and etchants were used successfully. While metallographic discrimination between a Nb3lr and o was easily possible, X-ray diffraction was necessary to separate al and ct2. X-ray powder patterns were taken and evaluated as for Nb-Rh6 yielding the error limits indicated in Table 111, to be introduced later. For the determination of the invariant reactions and phase boundaries, the same techniques as for Nb-Rh6 applied. The general accuracy of invariant concentrations is regarded as somewhat higher than for Nb-Rh due to the small slope of most solvus lines.

Jan 1, 1964

By D. L. Ritter, N. J. Grant, B. C. Giessen

Forty-six alloys covering the complete concentration range of the Nb-Rh system were examined by metallographic and X-ray methods; solubility limits of terminal ad intermediate phases and transformation and solidus temperatures were determined. There are nine intermediate phases; two eutectic, five peritectic, two eutectoid, and three peritectnid reactions were encountered. The experimental methods and the constitution diagram are described in Part I. Part 11 deals with the crys -tallography and relation of the intermediate phases. The Nb-Rh system was selected for study for three reasons: first, it was hoped that the anticipated similarity of the Nb-Rh phase diagram to the Ta-Rh1 and Ta-Ir2 diagrams treated earlier (see also Ref. 3) and to the Nb-1r4 diagram treated simultaneously would allow a crystallographic and comparative evaluation of the intermediate phases in these related systems; second, it was likely that the previous experimental methods could be carried over without significant change; and third, it was expected that the interesting mechanical properties of the a1 phase of the Ta-Rh and Ta-Ir systems would also be encountered in similar phases of the new systems, and that these phases could be investigated more closely. The phase diagram had not been treated fully in the literature; only brief surveys of some intermediate phases were found.5-7 It was attempted to cover the details of the phase boundaries, Part I, as well as to present the crystallography of the intermediate phases, Part 11. EXPERIMENTAL METHODS Specimen Preparation and Treatment. The following high-purity starting materials were used. 1) Niobium powder, 99.8 pct pure, mesh size -60 +200, from Wah Chang Corp., Albany, Ore. The analysis furnished by the supplier showed the following major impurities: Ta, <500 ppm; Zr, <500 ppm; 0, 300 ppm; Fe, 280 ppm; Ti, <I50 ppm; W, Si, <100 ppm; C, N, 30 ppm; all other impurities, <30 ppm. 2) Rhodium powder, ground sponge, 99.9+ pct pure, mesh size -80, from J. Bishop Co., Malvern,

Jan 1, 1964

By D. L. Ritter, N. J. Grant, B. C. Giessen

The crystal structures of eight of the nine intermediate phases in the Nb-Rh system were investigated by X-ray techniques. The following structures occur: a,Nb3Rh (Cr3O type);o(ofe - cr type) (H.T. phase, structure unknown); Q2 (AuCU type); a, (orthorhombic, analogous to a,, (Ta-Rh)); a (AuCd type); a,, (monoclinic, related to samarium type); a-8 (VCo3 type); a, NbRh, (AuCu, type). Structural relationships between the six close-packed intermediate phases are discussed and a comparison with the Nb-Ir, Ta-Rh, and Ta-Ir systems is made. In the Nb-Rh phase diagram,&apos; nine intermediate phases were encountered. In order to understand the phase sequence in the diagram and to be able to plot atomic volumes, several unknown crystal structures had to be worked out. These and the evi-

Jan 1, 1964

By R. A. Meussner, R. J. Goode

Six intermediate phases occur in the Nb-Zn sysThese phases form by peritectic reactions at 1120°, spectively. The Nb Zn 15 phase appears as the minor phase in the eutectic structure, and the terminal phases remain nearly pure niobium and zinc even at high temperature. Vapor -pressure measurements on the four high-temperature phases (Nb Zn to Nb Zn 3) permitted estimates of the composition limits of these phases and the calculation of approximate values of AFO, AH°, and AS°. 1 HE present study of the constitution of the binary Nb-Zn system was a part of an analysis of the mechanism by which coatings of the Nb-Zn intermediate phases protect niobium against oxidation at high temperature.&apos; Since the primary interest in these phases was in coating service, attention in this study was given principally to the four phases stable at high temperature with only cursory attention to the two low-temperature phases. The solubility studies of niobium in zinc by Martin, Knighton, and Feder2 and the reports from the present study of the Nb-Zn coating represent the only published data pertaining to this system. Previously Hodge, Evans, and Hoskins, in an experimental survey, had noted that niobium was not resistant to attack by molten zinc, but no further observations were reported. EXPERIMENTAL PROCEDURES a) General. The nature of the binary Nb-Zn system precluded the use of more conventional methods of determining the phase equilibria such as thermal analyses of a series of cast alloys. An extrapolation of the liquidus data of Martin, Knighton, and Feder2 to higher temperatures suggested that the solubility of niobium in zinc would remain low in the entire temperature range of interest. The preliminary results of the present studies showed that all of the high-temperature intermediate phases form by peritectic reactions. Thus the sluggish nature of this type of reaction and the steepness of the liquidus indicated that thermal analyses would not yield reliable data. The peritectic reactions, of course, precluded the direct formation of samples of the individual phases from the melt. b) Materials. The niobium and zinc used in the present studies were of high purity. The niobium, in the form of 0.1-in.-diameter rods, contained 30 ppm 0, 30 ppm N, and 15 ppm C. Aside from 0.05 pct Ta, the metallic impurities (iron, titanium,

Jan 1, 1965

By C. H. Li, R. J. Stokes

This paper compares the fracture behavior of tungsten rods in three conditions: recrystallized. recovered, and wrought. Notched specimens suhjected to a 50 in.-lb impact load showed ductile-brittle transitions at 700, 4.90°, and 440°C, respectinely. The recrystallized material had an equiaxed pain structure and jracbred by simple cleavage from a grain boundary source at all temperatures up to 700°C. The wrought and recovered material had an elongated fibrous structure and at low temperatures fractured by cleavage originating from the notch. As the transition temperature was approached cleavage was preceeded by more and more intergvanular splitting which deflected the crack front into planes parallel to the tensile axis. The enhanced toughness of wrought and recovered tungsten was attributed both to its inability to initiate cleavage because no pain boundaries were suitably oriented perpendicular to the tensile stress and to its inability to maintain cleavage because of intergranular splitting ahead of the crack. It has been appreciated for a long time in a qualitative manner that the room-temperature brittleness of fully recrystallized tungsten may be alleviated by working the material at relatively low temperatures.&apos; More recently this difference in mechanical behavior between wrought and recrystallized tungsten has been examined quantitatively by measurement of the tensile properties as a function of temperature. In these experiments brittleness has been expressed in terms of ductility or reduction in cross-sectional area upon tensile fracture or in terms of the bend radius before fracture under bending.&apos; This work has shown the existence of a fairly sharp transition from brittle to ductile behavior with an increase in temperature. The ductile-brittle transition temperature for recrystallized material is approximately 200°C higher than for wrought material. An increase in strain rate, small additions of impurity,&apos; or an increase in grain size4 shift the respective transition temperatures to higher values, but the difference between them remains approximately the same at 200°C. A number of explanations for this embrittlement by recrystallization have been given. It has been blamed either on the concentration of impurity at the grain boundaries, the increase in grain size, or the change in texture which occurs upon recrystallization. The present paper examines the effect of different heat treatments on the notch-impact behavior of commercial powder-metallurgy tungsten rods. The change in the ductile-brittle transition temperature for this method of loading and the fracture mode has been related to the different mi-crostructures produced by heat treatment. EXPERIMENTAL PROCEDURE Commercial swaged powder-metallurgy tungsten rods 1-3/8 in. in length and 1/8 in. in diameter were machined to introduce a sharp V notch 0.030 in. deep. To change the microstructure from that of the as-received wrought material some of the specimens were subjected to an anneal in nitrogen either at 1300° or 1400°C for 8 hr or at 1600° or 2000°C for 1/2 hr. The notched rods were then placed in a miniature Charpy-type impact machine and struck at their midpoint (opposite the notch) with a hammer designed to deliver 50 in.-lbs of energy. The strain rate at the base of the notch was estimated to be approximately 100 sec-1 at the instant of impact. The specimens were heated in situ to the desired impact temperature. The microstructures produced by the various anneals were studied by both X-ray diffraction and metallographic techniques. Fig. 1 reproduces the microstructures observed metallographically following a 10-sec electroetch in a 10 pct KOH solution. Fig. l(a) shows the elongated fibrous grain structure of the as-received material. Following the anneal at 1300" or 1400°C the grain structure was still elongated as shown in Fig. l(b) but the etch pits delineated dense polygonized dislocation arrays within many of the grains. Occasionally a relatively dislocation-free recrystallized grain was found growing into the matrix. The anneals at 1600° and 2000°C resulted in complete recrystallization and some grain growth. The grains produced at 1600°C were still slightly elongated as shown in Fig. l(c) whereas the anneal at 2000°C produced equiaxed grains. The changes in grain size produced the expected changes in the X-ray back-reflection patterns; there was no indication either in the as-received material or the annealed material of any preferred orientation. RESULTS a) Impact Behavior. Fig. 2 reproduces the ductile-brittle transition curves measured in the manner described in the previous section. It can be seen that under these testing conditions the as-received

Jan 1, 1964

By J. B. Newkirk

ABOUT twenty-seven years ago W. bergl discovered that interesting detail could be seen in an X-ray diffraction spot made with a rock-salt crystal if the recording photographic film were held very close to the reflecting crystal. He also showed that much of this detail could be explained in terms of the deformation structure of the specimen. In the same year, 1931, Fox and parr2 reported that X-ray reflections from a quartz crystal were much more intense while the crystal was undergoing piezoelectric oscillation than when it was at rest. This observation was soon confirmed (and explained in terms of X-ray extinction) by Barrett3 in the United States and by Nishikawa et a1.,4 in Japan. During the next few years Barrett refined Berg&apos;s method for making X-ray diffraction micrographs and applied it to the study of metallic crystals. He reported this work in the 1945 annual lecture of the AIME.5 Since 1945 relatively little use has been made of the Berg-Barrett (B-B) method for making diffraction micrographs, though considerable interest in investigating subcrystal structures by other methods has developed. Some of these methods depend upon evaporation6 or chemical etching7 and, therefore, suffer from the occasional intrusion of subtle artifacts such as those recently reported by Hooker for leada and Welsh for aluminum.9 Other methods require the introduction of foreign elements which "decorate" the substructure in some way, thereby rendering it detectable by direct" or indirect1&apos;. visual examination. Still others depend upon complex and often highly questionable analyses of X-ray diffraction line profiles. There have also been a number of related X-ray techniques, such as the Lambot,12 Schulz13 and Merlini and Guinier,14 which have proved to be quite useful for specific applications. Some of these methods give a picture of the substructure which is more or less directly related to the shape and the topography of the specimen. The Berg-Barrett method carries this desirable feature to the limit. Closely related to the B-B method are three photographic X-ray techniques recently described by Lang.15 These methods give beautiful pictures of the internal structure of crystals but are limited by the facts that the required apparatus is rather complex, exposure times are long, and the specimen crystals must be thin. An experimental appraisal which I have recently made of the original B-B method has shown that this simple technique is not only inexpensive and convenient, but can give more information than was apparently realized by its inventors. For example, first-order subgrains in iron-silicon crystals were clearly delineated and their relative orientation subject to description. Also defect structures could be seen within the subgrains and in some materials slip bands could be clearly seen with respect to the topography of the rest of the specimen. This much had already been described by Barrett. However, in the present study it was found that the actual sites of individual dislocations which emerge upon the crystal surface could be located. Furthermore, by a simple procedure, the direction (but not sign) of the dislocation Burgers&apos; vector could be defined as well.

Jan 1, 1960

By A. E. Gorum, I. Cornet

Fatigrle of ionic crystals has been studied primarily in magnesinm oxide. under cyclic stress dislocations move irrreversibly; they multiply; slip bands form and grow; cracks mucleate and propagnte, and failure occurs. The use of ionic crystals such as MgO is advantageorus in such investigations because they are optically transparent. Individual dislocation Intersections with {100} surfaces may be observed with a standard microscope, using etch-pit techniques. Slip, deformation, crack .formation, and fracture in MgO crystals under cyclic stress are compared with cotrresponditzg processes in metals. ThE effect of cyclic loading in metals has been studied for many years. The appearance of slip lines is readily observed and the ensuing fracture may also be seen. From these observations it is possible to predict the behavior of a material and make an educated guess as to what is happening internally, but the actual changes taking place within the structure are not readily apparent. If one could obtain a material in which the individual glide components could be observed, it would be invaluable in determining the actual slip distribution resulting from cyclic loading as well as the distribution of slip in the neighborhood of a growing crack. Such a material is magnesium oxide. Dislocation arrays may be observed by means of etch pits

Jan 1, 1961

By R. E. Hook, H. J. Garrett, A. M. Adair

X-ray diffraction and metallographic techniques were employed to examine the impurity phases occurring in as-swaged and recrystallized chromium produced fvom high-purity iodide chromium crystals. Chromium oxides are found to form in a consistent manner associated with the temperature of recrystallization. Microscopically observable second phase particles of Cr203 are observed to form intergranulurly beginning at 1300T. Beginning at 1500°C. Cr30, is formed intergvanulurly, atzd at 1600°C and above Cr30, is also formed in association with migrating grain boundaries. Geometrical traces formed by particles of this high temperature oxide uithin the grains rez)eal the histmy of grain boundary motion. X-ray evidence is presented which suggests the existence of a high temperature form of Cr203. Other impurity phases in addition to the oxides of chromium are also present. THE partitioning Of impurity elements between grain boundary aid lattice sires, either as solutes in solution or as second phases, may exercise an important influence on the mechanical behavior of metals and alloy systems. This partitioning of impurities could have a direct bearing on the iecrys-

Jan 1, 1963

By A. S. Koster, G. D. Rieck

X-ray experiments were carried out to show the occurrence of cylindrical texture in drawn tungsten wire. Only a small amount of (110) (110) cylindrical texture could he found in wires of intermediate thickness, i.e., of about 1.5 mm diameter. DRAWN wires of tungsten and other bcc metals like iron and molybdenum show a well-established (110) fiber texture. Now it might be conceivable that in drawing radial stresses remove the randomness of the crystallites around the [110} axis, thus giving a fiber texture of higher symmetry. In the resulting so-called cylindrical textures a specified plane normal coincides with the radius of the wire. Several authors discuss the occurrence of cylindrical textures in bcc metals. ~ieck&apos; found no cylindrical texture in drawn tungsten wires of 165 n diameter. Leber~ states that in tungsten wires of 3 mm diameter a cylindrical {100)(110) texture is developed, which is gradually converted to a normal fiber texture by subsequent drawing. He also reported a definite cylindrical texture at the surface of iron wires. Peck and Thomas3 observed a nonuniform mode of deformation of the grains in transverse sections of heavily drawn tungsten and iron wires. According to Bhandary and cullity4 a swaged iron wire has neither a perfect (110) fiber texture nor a perfect {100}(110) cylindrical texture. It is clear that the concept of cylindrical texture in bcc metals still lacks a firm experimental basis. Leber&apos;s eviden~e,~ which seems to be the strongest, rests upon qualitative interpretation of photographs. The appearance of the 110 and 200 lines on the photograph of 3-mm wire, however, can be very well attributed5 to a normal ( 110) fiber texture superimposed on random background; our Fig. 1, giving a Debye-Scherrer diagram of etched tungsten wire of 180 p, is free of cylindrical texture according to all authors, but is quite similar to Leber&apos;s diagram. It was therefore decided to use a different method of X-ray texture determination on tungsten wires of diameters where cylindrical textures may be expected.

Jan 1, 1965

By R. F. Hehemann, D. J. Cometto, G. L. Houze

The w transformation in the Zr-Nb system was studied using X-ray diffraction, dilatometric, re-sistornetric, hardness, and metallographic techniques. w forms in a diffusionless, completely reaersible manner on quenching and in a diffusion-controlled manner- on aging. The temperature at which w begins to form on quenching was determined as a Junction of composition and was found to decrease with increasing solute content. w formed bv aging establishes a metastable equilibrium with an enriched ß phase. The ß/w + ß transus has been determined for this metastable equilibrium and employed to rationalize retrogression and reversion phenomena observed in these alloys. The decomposition mechanism is discussed in terms of a gradual or continuous transformation from ß to the w state. BETA- stabilizing alloying elements lower the MS temperature of the martensitic bcc (ß) to hcp (a&apos;) transformation in zirconium and titanium alloys. In certain titanium alloys, a lower symmetry modification of the martensitic structure, termed (a"), also has been reported.1,2 These martensitic transformations are suppressed when the amount of the ß-stabilizing element exceeds a critical level. However, the high-temperature ß phase cannot be quenched to room temperature without change. At alloy contents just above the critical level, |ß trans-forms to the w phase when cooled rapidly.3-6 The amount of w in quenched alloys is reduced by increasing alloy content, and this phase virtually disappears above a critical composition.5 In addition to the transformation during cooling, w also can be formed by aging ß at temperatures below approximately 500°C, and significant alloy enrichment of retained 13 accompanies the isothermal transformation.1-8 The structure of LC is closely related to that of the ß from which it forms.9-15 The bcc (ß) lattice can be generated using a hexagonal cell with three atoms located at (000) and ±(2/3, 1/3, 1/3). This cell has an axial ratio of 0.612 and is oriented with respect to the cubic cell such that (0001)H (111)C and [1120]H [101]C. Consequently, there are four possible orientations of the hexagonal cell, associated with the four (111) planes of the bee lattice. Formally w can be obtained from 0 by allowing the two atoms at the ±(2/3, 1/3, 1/3) positions to approach the coordinates ±(2/3, 1/3, 1/2) and there are four equally probable orientations of w for each 0 grain. In titanium alloys w retains the cubic axial ratio of 0.612" and hence also can be indexed as triply cubic, but this is not the case for aged Zr-Nb alloys where w is clearly hexagonal with an axial ratio of 0.622." The lattice parameters and atomic positions of w depend on thermal history and alloy content. The atomic positions (000), ±(2/3, 1/3, 1/2) provide reasonable agreement between calculated and observed diffracted intensities for w in the fully aged condition.10,14 In the quenched condition, on the other hand, the atoms appear to be displaced from the central plane12,13,15 and assume positions ±(2/3, 1/3, Z = 0.42-0.48) rather than ±(2/3, 1/3, 1/2). This results in a structure with trigonal rather than hexagonal symmetry. The readily detectable parameter and axial-ratio changes of w in Zr-Nb alloys make this system especially attractive for studying the structural changes that occur in the formation and aging of w. Particular attention in this investigation has been directed to the relationship between the structure of w in the quenched and aged conditions, and to certain aspects of the reaction kinetics. MATERIALS AND PROCEDURE Zr-5, 12, 17.5, and 25 pct Nb alloys were prepared by a double arc-melting practice, encased in stainless-steel cans and hot-rolled to 1/8-in.-thick sheet.* Charged weights have been employed for the niobium contents and interstitial analyses are reported in Table I. Dilatometric, X-ray diffraction (filtered CuK, and MoK, radiation), metallographic, and hardness techniques have been employed to follow the transformations during isothermal and quench-aging heat treatments. In quenched specimens, the electrical resistivity also was studied. Betatizing was conducted for 1 hr at 900°C. With the exception of the isothermal dilatometric studies, samples were

Jan 1, 1965

By Paul A. Beck, M. N. Parthasarathi

The vecrystallization texture. formed by selective growth of random nuclei in an 80 pct volled 99.997 pct A1 crystal of initial orientation mear (123) (41.21 was found to consist of components related to the single-component rolling texture by 40 deg. rota-tiows around [111]axes. The relative-volume fractiovz of the various recrystallization-texture componezts may be accouzted for 012 the basis of the Lou) mobility of twist boundaries, if it is assumed that the mobility of the tilt boundaries also varies with their orientation. Similar results with a, aluminum-alloy cystal of the (110) [112] orientation, containing iron, silicon, and zinc, show that these solute contents do not impair the effectivezess of the oriented growth mechanism of re cry s-tallization- texture formation. In a previous investigation1,2 it was found that a sharp recrystallization texture is formed as a result of the oriented growth of random artificial nuclei in an aluminum crystal rolled to 80 pct RA, on the (110) plane in the [ 112] direction. Four recrystallization-texture components were found to occur, with orientations corresponding to 40-deg rotations around [111 1 axes of the deformation texture. Reorientations of this type were already found in earlier work,3,4 where the presence of random nuclei could be reasonably assumed, but was not rigorously documented. The same orientation relationship was found also by Lucke and Liebmann, who actually measured the orientation dependence of boundary-migration rates in the recrystallization of A1 crystals slightly deformed in tension.5,6 The occurrence in the recrystallization texture of only four of the eight crystallographically equivalent orientations of the type referred to above remained unexplained,1,2 although it was clearly not a result of the absence of suitable nuclei. Recently Burgers7 suggested that this effect may be due to the aniso-tropy of boundary mobility observed2&apos;6; it was found that the recrystallized grains of the 40-deg [111]-rotated type grow much faster in directions perpendicular to the [ 111] they have in common with the matrix than parallel to this direction, i.e., the tilt boundaries have much higher mobility than the twist boundaries. The four orientations corresponding to

Jan 1, 1962

By J. J. Kramer, K. Foster

The orientation distribution of surface-energy -induced secondary recrystallized grains was determined. This work was conducted on thin sheets of a 3 pct Si-Fe alloy annealed under environmental conditions that furor grouth of grains with a (100) plane in the surface of the sheet. The texture was found to be extremely sharp and almost independent of sheet thickness. The distribution varied exponentially with the angular deviation from the {100} plane. It was possible to relate the distribution to the nu-cleation rate of the secondary rains as influenced by the surface-energy difference. THE role of surface energy in the secondary grain growth of cube-oriented grains (grains with a (100) plane in the plane of the sheet) in thin Si-Fe sheets has been previously discussed.1-4 In high-purity sheet material normal grain growth usually occurs until the grains have extended through the sheet. Further grain growth is inhibited by the thermal grooving of the boundaries at the sheet surface. However, additional growth of cube grains can occur by a secondary grain growth process under conditions where the (100) plane has a lower surface energy than other orientations. Apparently for these alloys, cusps exist in the polar plot5 of surface free energy with the lowest cusp energy occurring at the (100) orientations. This has been reported to be the result of preferential adsorption of sulfur on the (100) planes.6 As a result of this process, a distribution of orientations could arise from two possible mechanisms. First, when a cusp is present in the polar plot of surface free energy, there are orientations inside the cusp that have a lower surface energy than elsewhere on the polar plot. Also, at sufficiently high temperatures, flat surfaces whose orientations are inside or just outside the cusp (depending on its shape) can often thermally etch, yielding a microscopically stepped surface of even lower surface energy. As a result, grains oriented close to cube would also have a lower surface free energy, either because of the cusp shape or by thermal etching, and could possibly grow as secondary grains by the surface-energy phenomenon. One should thus observe a distribution in the surface orientation of the cube grains comprising the secondary structure. It is the purpose of this paper to investigate this orientation distribution experimentally and to discuss the factors involved in its formation. For this purpose, the surface orientations of a large number of secondary grains in various sheet thickness were determined by means of the Laue back-reflection X-ray technique. PROCEDURE A vacuum-melted 3 pct Si-Fe alloy containing a nominal impurity content of 0.005 wt pct was processed into strip. A single cold-rolling step of 90 pct reduction was used for each strip regardless of the final sheet thickness. Final strip thicknesses of 0.60, 0.30, 0.15, and 0.075 mm were used. Care was taken to insure that the final strip surface was smooth and flat. All strips of a given thickness were annealed together at 1200°C in dry hydrogen (dew point -70°C) to develop the desired secondary structure and to insure identical environmental annealing conditions. The annealing time was selected to develop a complete secondary structure in the thinner sheets but to permit the thicker sheets (0.60 mm) to have residual primary grains remaining. This was necessary to determine whether growth impingement could lead to one secondary grain consuming another at a greater angular deviation. For the X-ray determination of the surface orientation of the secondary grains, a special specimen holder was used. The camera and holder arrangement could be aligned by X-raying a grain in three positions rotated 180 deg to each other. Thus, with a small beam X-ray focus (1 mm), the surface orientation of any grain could be determined to within one-half a degree. The surface orientations of one hundred cube secondary grains were determined for each sheet thickness. The criteria of a secondary grain were its size relative to the sheet thickness and the number of sides of the grain observed in the sheet surface. (A primary recrystallized grain extending through a sheet will generally have six edges visible in the plane of the sheet, whereas a secondary grain will have many more when growing entirely into primary grains.) Grains were selected as randomly as possible by X-raying every secondary grain found along a line drawn on the strip. No attempt was made to determine the exact orientation of the planes of the surface, as many strips from randomly selected sheets were used. On1y the angular deviation of the surface plane from {100} was measured. In order to assess the volume distribution in the

Jan 1, 1965

By R. Maddin, C. H. Mathewson, W. R. Hibbard

According to conventional crystal mechanics, a face-centered cubic single crystal slips on the system {111} <110> which receives the highest shear stress in terms of the stated orientation of the stress axis of the crystal.l However, in brass, the slip process is never as simple as this conventional analysis indicates. There is always a second cooperating plane which contains the same slip direction as the primary plane.2&apos;3 There is still another cooperating slip system commonly called the conjugate system3 previously observed to function with considerable lag only after the rotation due to the action of the first plane had produced a symmetrical condition of equal shear stress on the two systems. In the 1943 Campbell Lecture,4 a slip mechanism was outlined in which the {111) planes moved step-wise in two adjacent <112> directions integrating into the <110> slip direction. "... the slipping process would be visualized as a succession of steps 30" to the right and left of the resultant, microscopically observed, slip direction; a first step setting up the twinned configuration in the single spacing involved and an ensuing slip returning the atoms to the untwinned configuration while completing a fully integrated <110> movement."4 This process is shown diagrammatically in Fig 1 which shows two close packed layers of atoms at a slip site. A movement of the full circles through the "valleys" into the adjacent sites would produce a twin configuration with respect to the open circles. The term, "twin fault," seems most appropriate to define this faulted condition of the lattice. Annealing twins in face-centered cubic metals may arise from preformed nucleii which could be described as twin faults produced by the first movement of this two stage slip process. However, it is clear that this kind of slip does not take place so as to embrace a measurable number of adjacent planes because careful X ray examination has not conclusively shown the existence of ponderable twin lamellae (as in the case of Neumann bands in the body-centered ferrite). In view of the imponderable character of these hypothetical twin faults, the search for evidence of their existence seems restricted to indirect methods. The most obvious experimental technique serving this purpose is the determination by micrographic and X ray methods of the alignment of the composition planes of annealing twins with the former slip planes in axially strained and recrystallized single crystals. In previous attempts of this sort not all of the annealing twins could be traced to slip planes known to be operative in the conventional sense and hence evidence appeared negative or inconclusive. With the discovery of additional slip systems2&apos;3 operating in conjunction with&apos; the major system of highest resolved shear stress in axially strained brass it became apparent that the simple technique outlined above might be re-employed with more gratifying results. If, on annealing single crystals of alpha brass previously strained in tension, twins are found with their composition planes parallel to all three operative slip planes and with no participation of the fourth plane there is good evidence in favor of the existence of twin faults and of the two stage slip process. Experimental Procedure and Resuits Single crystals of alpha brass of the 70-30 composition were grown by solidification from the molten state.

Jan 1, 1950

By P. E. Doherty, B. Chalmers

Subboundaries may be revealed in aluminum by the formation of pits on the surface during cooling from elevated temperatures. The pits do not form in the vicinity of high- or low-angle boundaries. They are attributed to the condensation of vacancies from a super saturation produced during coolirzg. Using the vacancy pit and Schulz X-ray techniques for observing low-angle boundaries, a study was made of the transition from the nearly perfect seed to the striated structuke characterist-ic of aluminum crystals grown from the melt. It was found that the individual striation boundaries develop by the coalescence of very small-angle boundaries, as well as by the addition of individual dislocations. Several mechanisms for the formation of striations are discussed. Evidence was found suggesting that a super-saturation of vacancies exists near a growing interface, and it is proposed that the resulting climb of existing dislocalions produces "half&apos;-loops" at the interface, which combine to form the low-angle striation boundaries. LINEAGE, or "striation" boundaries, have been studied in detail by Teghtsoonian and Chalmers 1,2 in crystals of tin grown from the melt, and by Atwater and Chalmers3 in lead. They found that single crystals grown from the melt consist of regions which are separated by subboundaries that lie roughly parallel to the growth direction. A difference in orientation of 0.5 to 3 deg exists between the striated regions; the misorientation is such that the lattice of one region could be brought into coincidence with the lattice of its neighbor by a rotation about an axis approximately parallel to the direction of growth of the crystal. They observed an incubation distance for the formation of striations which increased with decreasing growth rate. They also found that in any crystal, the sum of all rotations of the lattice in one sense, in going from one striation to the next, is very nearly equal to the sum of all the rotations in the opposite sense. A striation boundary, which is a low-angle grain boundary, can be described as an array of dislocations. If it is assumed that suitable dislocations are introduced into the crystal during solidification, the formation of striation boundaries can be explained as a result of the migration of the disloca- tions into arrays. The formation of arrays is energetically favorable since the energy of an assembly of dislocations can be reduced by the interaction of the stress fields when a suitable array is formed. This investigation presents and interprets new information concerning the nature and origin of striation boundaries in aluminum. EXPERIMENTAL TECHNIQUE Single crystals of high-purity aluminum (Alcoa 99.992 pct) were prepared by horizontal growth from the melt.&apos;&apos; The specimens were subsequently electropolished in a solution of 5 parts methanol to 1 part perchloric acid kept between -10° and 0°C in a bath of dry ice and alcohol. The current density was approximately 6 amps per sq in. Doherty and Davis9 have shown that in aluminum sub-boundaries with misorientations of not less than several seconds of arc may be revealed by the vacancy pit technique. During cooling from elevated temperatures pits form on electropolished surfaces of aluminum crystals as a result of the condensation of vacancies.11 Pits do not form in the vicinity of small- or large-angle grain boundaries, presumably because such boundaries act as sinks for vacancies. Boundaries of misorientations down to 3 sec of arc are revealed as pit-free regions, see Fig. 1. The Schulz X-ray technique12 was used to determine the angular misorientations of subboundaries. In this method, white radiation from a micro-focus X-ray tube is used to produce an image of a fairly large area of a single crystal surface. Subboundaries cause splitting in the diffracted image, see Fig. 2. Misorientations down to about 15 sec of arc may be observed with this technique. OBSERVATIONS AND DISCUSSION Figure 1 shows a striated aluminum crystal grown at 10 cm per hr etched by the vacancy pit technique. An incubation distance of about 1 cm is observed before the initiation of striation boundaries. Fig. 2 is a Schulz X-ray photograph of a striated crystal similar to that shown in Fig. 1. A large area of the crystal was studied by means of a series of photographs. Fig. 2, which is a reflection from the (100) plane, included about the first 4 cm of crystal to freeze. There is an incubation distance of about 1 cm, and a distance of about 2 cm over which the angle of misorientation builds up to its final value of approximately one degree. Some twist component can be seen in Fig. 2 at the right side of the photograph. From Fig. 2 it can be seen that the sum of all rotations of the lattice in one

Jan 1, 1962

By D. Walton, B. Chalmers

A preferred orientation is known to occur frequently in the columnar zone of castings. This has been attributed to a preferred direction of growth. However, no satisfactory mechanism was proposed by which the preferred direction of growth led to the preferred orientation. The purpose of this work has been to establish this mechanism. It has been found that in general the observed preferred orientations only develop when the preferred directions of growth reveal themselves by dendritic growth. A mechanism based on this premise is found to be in agreement with the experimental data obtained in the course of this work. WHEN a liquid metal is allowed to solidify in a mold, it usually freezes in three stages, distinguished from each other by the size and shape of the grains. The first zone to freeze (the chill zone near the mold wall) consists of relatively fine grains that are equiaxed in shape and random in orientation. The next zone consists of crystals that are elongated in the direction of heat flow, i.e., normal to mold wall. These crystals are much larger in cross section than the crystals of the chill zone and have a very strongly preferred orientation. This is the columnar zone. The final zone, which is absent in very pure metals, is again equiaxed and randomly oriented, but usually has a much coarser grain size than the chill zone. The purpose of this study is to describe and account for the crystal size and orientation in the columnar zone. The occurrence of a preferred orientation in the columnar zone is well known, and in 1940, Greninger&apos; suggested that it is apparently related to dendritic growth although at that time the only data were for metals with the face-centered-cubic structure. Table I shows that the direction of dendritic growth and the crystal axis that follows the heat flow direction coincide in all cases so far studied. The term "dendritic growth" is used here to represent the branched type of morphology that is characteristic of growth into supercooled melts.&apos; In addition to the supercooling which is necessary before nucleation will occur at the mold wall, the necessary supercooling for continued dendritic growth can be provided in a mold by heat flow into the already formed solid at an interface whose Liquidus temperature is depressed by an accumula-

Jan 1, 1960