By E. F. Koch, J. L. Walter

oriented crystals of iron and iron with 3, 5, and 6.25 pct Si were rolled to reductions of 10 and 70 to 97 pct at room temperature. Similarly oriented crystals were deformed in tension. Dislocation substructures of the deformed crystals were observed by transmission electron microscopy to determine the effect of silicon on the formation of substructures. Pole figures were obtained to relate orientation changes to substructure. When rolled 10 pct, the iron crystals and the 3 pct Si-Fe crystals formed cells, 1 and 0.2 u in diameter, respecliuely. Cells were absent in the higher-silicon crystals. Extended dislocations and possible stacking faults were observed in the 6.25 pct Si-Fe crystal rolled 10 pct and annealed at 650°C. The stacking-fault energy was estimated to be 20 ergs per sq cm. Rolling to 70 pct resulted in the formation of sub-bands (0.9 µ wide) ill the iron crystals and transition bands (containing 0.2-µ-wide subbands) in the 3 pct Si crystals. No subbands formed in the 5 pct Si-Fe crystal until it was ankzealed. SliP occurred on (112) planes ill tension. The slip traces on the 3 pct Si crystal were wary while those on the 5 pct Si crystal wvere straight. The strain-hardening coefficient for the 5 pct Si crystal was nearly zero. Cells did not form, at least at elongations up to 10 pet. The results suggest that cross slip of iron is restricted by additions of silicon beyond about 3 pct possibly by formation of immobile extended dislocations. IN a previous paper' the authors described the substructures developed in (100)[001]-oriented crystals of 3 pct Si-Fe which were rolled to reductions of 10 to 90 pct at room temperature. At low reductions (10 to 20 pct) cells, approximately 0.2 to 0.3 ja in diameter, were formed. The cell walls consisted mainly of edge dislocations. With increasing reduction (up to 50 pct) the cells were seen to elongate in the rolling direction. In certain regions of the crystal there were significant reorientations which were characterized as rotations about an axis normal to the (100) or rolling plane. These regions were called "transition bands". The regions in which there were no reorientations were called ('deformation bands". At reductions of 60 to 70 pct the elongated cells in the transition bands became sub-bands separated by low-angle tilt boundaries with angles of disorientation of about 2 deg. The elongated cell structure in the deformation band was replaced by a general distribution of dislocations. It was noted that the width of the subbands in the transition bands remained 0.2 to 0.3 µ; i .e., the width of the subbands was the same as the initial cell diameter for reductions up to at least 70 pct. From this, and from considerations of the mechanism of formation of the transition bands,' it was concluded that the subbands evolved directly from the initial cells. In order to check this conclusion, it was decided to examine the relationship between initial cell diameter and width of subbands produced by large rolling reductions. Cell size is known to be dependent upon the temperature of deformation.2,3 However, preliminary experiments with 3 pct Si-Fe crystals indicated that the change in cell size with increasing temperature of deform,ation was not sufficient for the present purpose. On the other hand, cell diameters generally reported for iron deformed at room temperature2'3 range from 1 to 2 p, a factor of 3 to 10 larger than the cells in 3 pct Si-Fe rolled to 10 pct reduction,' indicating the possibility of a marked dependence of substructure (at least in terms of cell size) on the amount of silicon in iron. Thus, the investigation was enlarged to include the study of the effects of varying silicon content on substructure in lightly rolled as well as in heavily rolled crystals of iron and iron with 3, 5, and 6.25 pct Si. The crystals used in this study all had the same orientation, (100)[001], with respect to rolling plane and rolling direction. These were rolled to reductions of from 10 to 97 pct and the substructures determined by electron transmission microscopy in both the rolled state and after annealing. In addition, stress-strain curves were obtained from (100)[001]-oriented crystals of iron and 3 and 5 pct Si-Fe to determine the effect of silicon on tensile properties. The dislocation substructure of the tensile specimens was also determined for Samples pulled to 2 and 10 pct elongation at room temperature for comparison with the substructures produced by rolling. 1) EXPERIMENTAL PROCEDURE Crystals with 3, 5, and 6.25 pct Si were prepared by annealing 0.012-in.-thick sheets of high-purity Si-Fe in purified argon at 1200°C to effect growth

Jan 1, 1965

By J. H. Jackson, P. D. Frost, C. H. Lorig, A. C. Loonam

THIS paper describes (1) the effect of sodium on the tensile ductility of magnesium-lithium base alloys, and (2) the precautions necessary to avoid sodium contamination. Effect of Sodium on Properties The harmful effect of sodium in magnesium-lithium base alloys has been recognized by other investigators.1,2 However, quantitative data on its effect have not hitherto been published. The effect of sodium on the ductility of an 87 pct Mg-9 pct Li-4 pct Zn alloy is shown in fig. 1. The sodium was introduced by adding sodium chloride to the flux, which consisted of 50 pct LiC1-50 pct KC1. Moderately high ductility was obtained at an indicated sodium content of about 0.05 pct. Actually, the value probably was less than 0.05 pct, be-cause analyses of the lithium, which were more accurate than those of the alloy, indicated that the highest ductility was obtained when its sodium content was 0.02 pct or less. In fact, in alloys having somewhat greater strength than this particular composition, the sodium content of the lithium must be under 0.01 pct to avoid embrittlement. The effect of sodium on the ductility of several alloys having fairly low strength levels is shown in fig. 2. These alloys were melted with a flux containing 75 pct LiC1-25 pct LiF, to which various quantities of sodium chloride had been added. Sodium had no significant effect in pure magnesium but markedly decreased the ductility of the magnesium-lithium-zinc alloy, even though the alloy contained only 3 pct Li. As the lithium content of the binary alloys was increased, the ductility of the sodium-free alloys also increased. However, the effect of sodium on ductility became progressively more pronounced. Sodium raised the minimum hot-rolling temperatures, particularly those of the high-strength alloys, but its effect, in this respect, was less critical than its effect on tensile ductility. For optimum cold roll-ability, a low-sodium content was required. No deleterious effect of sodium on the stability of properties at slightly elevated temperatures was found. Control of Sodium in the Alloys Optimum ductility is obtained in the magnesium-lithium base alloys when sodium-free materials are used. Commercial lithium was formerly the chief source of contamination. Now purified lithium is usually available. When lithium of ordinary purity is used, the effects of sodium can be minimized by using a flux consisting of 75 pct LiC1-25 pct LiF. Bubbling nitrogen through the melt also helps remove sodium. The damaging influence of sodium on the ductility of the magnesium-lithium base alloys was observed very early in the alloy development program. The discovery came about as a result of chemical analyses made on the lithium used in the alloys. Ductile alloys had been made from lithium containing about 0.2 pct Na, whereas the lithium used in the brittle alloys contained about 0.9 pct Na. The first magnesium-lithium alloys were melted under commercial fluxes ordinarily used in melting magnesium alloys. These fluxes were unsuited for scavenging the contaminating sodium, and the resulting alloys were not ductile. Next, a flux containing 50 pct KC1-50 pct LiCl was tried. This was somewhat more effective but still was not satisfactory. After a number of different experimental fluxes had been investigated, one containing 75 pct LiC1-25 pct LiF was adopted. This flux made it possible to obtain good ductility in the alloys. The

Jan 1, 1951

By W. C. Winegard, A. Galibois, C. J. Beingessner

The effects of solutes on the distribution of two-dimensional configurations of grains in zone-refined tin have been studied. When solutes with partition coefficients (ko) greater than unity are added, three-sided pains become more prevalent and the growth law changes. It is shown by electron-Probe micro-analysis that a solute buildup occurs ahead of a moving grain boundary when ko > 1. It has been found recently1, 2 that solutes with partition coefficients greater than unity have a larger retarding effect on grain growth than solutes with k, less than unity. ko is defined as the ratio of the concentration of solute in the solid to the concentration of solute in the liquid with which the solid is in equilibrium. Niessen and winegard2 have suggested that this effect is probably due to the complex shape changes which occur during the process of grain growth and that no theory based on single boundary motion3-5 can explain the results. They suggested that the dissociation of the unstable fourfold junction was delayed in alloys where ko was greater than 1 because the boundaries at the junction had to move into a region of high solute concentration. If indeed this mechanism were correct, it was felt that not only would the dissociation of fourfold junctions be affected by the solute buildup ahead of the boundaries, but the collapse of three-sided grains would be impaired. These combined effects would naturally lead to a modification in the distribution of the number of sides per grain seen on a two-dimensional section. The present investigation was undertaken to test these hypotheses by examining the grain-growth process in detail. EXPERIMENTS The Distribution of Grain Configurations in Zone-Refined Tin as Seen on a Two-Dimensional Section. Following the method of Bolling and Winegard,6 zone-refined tin was cast into button-shaped specimens and, subsequently, plastically deformed under a drop hammer at room temperature. The resulting flat coin-shaped samples were annealed at 200°C, some for 50 sec and others for 100 sec. The specimens were then examined to determine the distribution of the number of sides per grain, i.e., the num- ber of crystals adjacent to any particular grain in the section. For simplicity, the grains were classified as three-sided, four-sided, and so forth; this concept is schematically illustrated in Fig. 1. As indicated by smith,' it was necessary to examine every grain within an enclosed area to obtain a proper distribution of the relative frequency of each type. The distributions for the two annealing times are illustrated in Fig. 2. The total number of grains examined is also indicated on the figure. It is evi-

Jan 1, 1965

By G. Sachs, E. J. Riping

All ferrous alloys can be made brittle by straining at sufficiently low temperatures. However, the changes in mechanical properties for different ferrous materials with decreasing testing temperature do not appear to follow any universal law. In particular, complex effects of testing temperature have been observed if cold worked steels were subjected to tensile tests at low temperatures. EFFECTS OF PRESTRAINING AT A TEMPERATURE ABOVE THE TESTING TEMPERATURE ON THE FRACTURE CHARACTERISTICS‡ A considerable amount of data has been presented by a number of investigators on the fracture characteristics of various cold worked steels.' These data usually relate to a two-step procedure first used by Davidenkov,² consisting of stretching by tension to a certain strain or " prestraining" at room temperature and then completing the tensile test, or "testing" at the temperature of liquid air. On the basis of data of this type made available to date, ferrous alloys can be classified into two groups with respect to their fracture characteristics observed on testing at a low temperature after prestraining at room temperature. Very complex phenomena have been observed for all annealed steels. On the other hand, some observations indicate that steels in certain other conditions represent a fundamentally simpler relation. In considering the effect of prestraining at one temperature on the properties obtained at some lower temperature, it should be expected that any cold work reduces the ductility retained in proportion to the magnitude of the cold work. However, the test data presented to date indicate that only heat treated (quenched and tempered) steels appear to conform to this expectation, according to the very limited test data in Fig 1, presented by McAdam, Geil and Mebs. This series of tests, Fig 1, shows that the retained ductility became smaller the larger the prestrain. However, this decrease is less than the amount of prestrain or, in other words, less than the decrease in ductility at the prestraining temperature. These effects of prestraining are fundamentally identical with those observed by Bridgman3 when a steel was prestrained (in tension) under hydrostatic pressure and then subjected to a regular tension test. It appears, therefore, that the basic effect of prestraining under conditions which yield a higher ductility than the (subsequent) testing procedure, consists of gradually increasing the total ductility of the metal from the initial low value of testing to the higher value of prestraining. On the other hand, all annealed steels, if cold worked by tension at room temperature and then tested at a lower temperature, provided that some ductility is retained, showed a far more complex behavior than that discussed above. This relationship is exemplified by Fig 2, for three pearlitic steels.4,5 These particular steels were selected because of the various shapes of their ductility-prestrain curves. All three steels, and any other investigated so far, suffered a rapid decrease in retained (and consequently also in total) ductility when subjected to small pre-strains. Then, after exceeding a certain prestrain it was generally observed that the ductility recovered.* This rather complex behavior of annealed steels may be tentatively correlated with the presence of stretcher strains at small restrains. Heat treated steels do not exhibit stretcher strains. This fact might possibly explain their simpler prestrain-retained ductility relationship. The destructive effect of these stretcher strains may possibly be associated with the presence of triaxiality, which may occur in any highly non-uniform stress and strain state (and which is retained as residual stress after unloading). Even a small degree of triaxiality may then cause a reduction in ductility, or even embrittlement at a sufficiently low testing temperature. The discussion presented above deals with the effects of cold working at a high temperature on the fracturing

Jan 1, 1950

By J. O. Nelson, C. J. Altstetter

Single crystals of hcp cobalt, 3 mm in diameter and up to 35 cm long, were grown using an electron-beam, zone-melting technique. The martensitic-phase transformation was studied in single-crystalline and polycrystalline specimens by making length-change measurements as a function of temperature under various elastic compressive stresses. Upon thermal cycling, single-crystalline or polycrystalline specimens repeatedly transformed almost entirely on the same variant of close-packed plane provided the maximum temperature did not exceed 600°C. Cycling to 1000°C resulted in transformation on more than one {111} variant. This behavior is termed multivariance. The multivariant transformation occurred very rapidly at an M, temperature 2° to 6°C lower than the M, of a transformation which would result in a single-crystal product. Elastic compressive stresses (up to 253 g per sq mm) tended to lower the A, and raise the M, temperatures, decreasing the width of the temperature vs dilatation hysteresis loop. The transformation habit plane and transformation shear direction of an as-grown single crystal were not grossly affected by elastic compressi?ie stress. This was evidenced by similar dilatations on the temperature us dilatation loops joy specimens with and without compressive stress. A dislocation mechanism is proposed to explain the observed results. IT has been shown that, on heating, cobalt transforms martensitically from the hcp to the fcc phase.' The transformation habit plane is (0001)hcp || (lll)fcc and the transformation shear direction is (1010)hcp || (112)fcc. The transformation involves a shear of 1g°28', which may be achieved by a shearing of a/6(112) of every two planes with respect to the plane beneath, thus changing the ABABAB stacking of hcp to the ABCABC stacking of fcc. Associated with the phase change is a 0.3 x 10"3 contraction in the habit plane and a 4.2 X 10"3 expansion perpendicular to the habit plane resulting in a 3.6 x X volume increase on heating.' On cooling, an identical volume decrease takes place. The temperature at which the fcc phase begins to form on heating (A,) is reported as 430°C, and the temperature at which the hcp phase begins to form on cooling from an elevated temperature (A&) is reported as 390oC1,3 Consequently, temperature vs dilatation plots have the form of a hysteresis loop. If heating or cooling is reversed during a transformation, a smaller hysteresis loop results. Upon heating, the transformation is always complete; whereas, fcc is often retained at room temperature as a metastable phase entrapped in the polycrystal-line hexagonal matrix.1,4,5 Two obstacles in the theory of the allotropic-phase transformation of cobalt have been: 1) a detailed knowledge of the product nucleus, and 2) a plausible method of propagation of the transformation. Bilby,8 christian, 7 and seeger 8,9 have suggested a "pole mechanism" as a means of propagation of partiai dislocations from plane to plane. A pole dislocation and a Shockley partial come together at a node. The a/6(112) Shockley partial rotates about the pole dislocation effecting the transformation shear. The pole dislocation must have a 2a/3(111) screw component which causes extension of the transformed region by two atomic planes with each full rotation of the Shockley partial. Bollmannl0 suggested, on the other hand, that transformation propagation occurs due to the stress fields of intersecting (111)-type stacking faults. As faults intersect, a stress distribution is set up about their intersection which is in turn reduced by the emergence of another fault on the second nearest plane. This process continues with the final result of a complete phase transformation. In view of the similarities between deformation and transformation in cobalt, the effect of stress on the transformation would, hopefully, yield valuable information concerning nucleation and propagation. In the present work single-crystalline and polycrystalline specimen length changes were measured as a function of temperature at various compressive loads. PROCEDURE Several orientations of single crystals of hcp cobalt in lengths up to 25 cm were grown by electron-beam floating zone melting from 99.95 and 99.999 pct, 3-mm-diam cobalt rod as supplied by Johnson

Jan 1, 1964

By R. I. Garrod, R. A. Coyle

The shapes and positions of X-ray reflections from specimens of copper, steel, and aluminum alloy haue been examined in the elastic and plastic ranges both while the specimen was under stress and in the unloaded condition. For the aluminum alloy the shape was unaltered by the application of stress either within the elastic limit or in the plastic range provided that no additional plastic strain was induced. In copper the broadening accompanying plastic deformation was very slightly reduced when the specimen was unloaded. A similay but more marked elastic component of broadening was also found for steel, but in this case below the yield stress. Line profiles corrected for instrumental and particle-size broadening indicate very large internal stresses in local regions of the plastically deformed metals. The results are discussed in terms of a recent suggestion that the heterogeneous dislocation distribution between the cells and their boundary walls plays a major role in the peak shifts and broadening of the X-ray reflections. STUDIES of the X-ray line profiles from strained polycrystalline aggregates concentrate usually on one or the other of two main parameters: a) the displacement of the peak of the intensity contour from its position for a strain-free aggregate, or b) the shape of the profile. From peak shifts data can be obtained either on the relation in both the elastic and plastic ranges between applied external stress and average lattice strains in a given (hkl) direction, or, alternatively, on the residual lattice strains which are present after a plastically deformed specimen is unloaded.' On the other hand, the shapes of the broadened profiles from cold-worked metals can be analyzed to separate the broadening produced by small particle size and by heterogeneous lattice strains.' In this paper the terms "size broadening" and "strain broadening'' are used in the general sense adopted by warren.' In the past, apart from two early qualitative observation, it has been customary to examine only the movements of the peaks of the profiles while the specimen is actually under load, since the line broadening induced by plastic strain remains after removal of the external stress. Consideration of the implications of existing data of this type suggests, however, that fruitful additional information on a number of fundamental aspects might be gained by careful examination of whether the X-ray line profile is in fact different in the loaded and unloaded states of the specimen. By taking advantage of the sensitivity and convenience of modern diffractometer techniques it is possible to explore with relative ease the magnitude and importance of any elastic effects which may be superimposed upon the well-known permanent changes in profile. The main aim of the work to be described was thus to investigate this point for typical metals and alloys. For this purpose annealed specimens were extended first elastically and then plastically and the positions and shapes of X-ray reflections were recorded. Initially it was anticipated that prime interest would center on observations within the plastic range; it has been found, however, that small changes in profile sometimes occur both before and after the nominal elastic limit of the material is reached. It is shown that the results obtained have important implications in relation to the structural changes and processes associated with deformation. I) EXPERIMENTAL To enable the diffraction lines to be recorded while the specimen was under uniaxial-tensile stress, a small hydraulic testing machine was designed and constructed for direct attachment to the goniometer of a Philips diffractometer. The specimens, which were machined from 1/2-in.-diam rod and had a central rectangular section 3/8 by 1/16 in. over a gage length of 1 in., were held in the machine by split collets mounted in grooves in the cylindrical ends of each specimen. No special precautions were taken to ensure precise axiality of loading. Constant oil pressure was maintained by a lever and weights system and transmitted to the loading rig by flexible pipe. The actual load on the specimen was measured by a load cell in the machine to an accuracy of * 1 pct. To enable smooth X-ray profiles to be obtained the specimen and machine were oscillated continuously during recording through *7-1/2 deg about the normal half-angle position of the goniometer. The three materials chosen for the investigations were high-purity copper as representative of a ductile fcc metal, a low-carbon steel for a bcc metal, and an aluminum alloy as a material in which the proof stress/ultimate strength ratio is high. Details are as follows. a) Copper. 99.999 pct purity. After machining the specimen surface was polished mechanically and

Jan 1, 1964

By G. B. Craig, J. Rezek

The critical resolved shear stress of zone-refined zinc single crystals deformed in tension is found to increase with increasing amount of striation substructure. The increase in strength with numbers of striations can be accounted for by a dislocation pile-up mechanism. A somewhat different means of plotting stress-strain data is introduced which allows a more unambiguous choice of yield stress to be made. FEW systematic studies of the role played by mac-romosaic or striation-type substructure in the de- formation of high-purity metal single crystals grown from the melt have been reported. McGrath and Craig' found that striations increased the critical resolved shear stress of zone-refined aluminum crystals, postulating a dislocation blockage by the striations as the strengthening mechanism. Lauri-ente and Pond2 found that, as the etch pit density increased in aluminum crystals grown from the melt, the critical resolved shear stress also increased. Fleischer and Chalmers3 also found changes in the critical resolved shear stress of aluminum crystals grown from the melt at varying rates, but could not be certain whether an increase of strength with rate was due to a higher concentration of impurity in the gage length or to an increase in the number of small-angled boundaries. An early work by Hibbard4 indicated that copper crystals containing lineage boundaries were stronger than those free from this type of imperfection.

Jan 1, 1962

By J. T. McGrath, G. B. Craig

Tensile tests on aluminum single crystals, grown from the melt, revealed that the yield stress of these crystals was raised as the amount of striation substructure was increased. The number of striation-type boundaries was varied by changing the rate of growth of the crystals. The results are interpreted in terns of a blockage of dislocation movement by striation boundaries. IMPERFECTIONS are known to have a large effect on the mechanical properties of metals. Teghtsoonian and Chalmers 1 studied a block or striation-type substructure in tin and found that the formation of the striations depended upon rate of crystal growth and orientation. They found that the angular misorienta-tion between neighboring striations varied between 15 min and 5 deg. Atwater and chalmers2 investigated striations in tin and lead, and found that purity was another factor which influenced their formation. There was a limiting purity above which the striations were straight and regular. There is little information in the literature concerning how substructures in melt-grown crystals affect strength. washburn3 introduced small-angle boundaries into zinc by a shear process and found a subsequent increase in yield stress which he attributed to the presence of these boundaries. Lauriente and pond4 found the critical resolved shear stress in aluminium crystals grown from the melt, to increase with etch pit density. The etch pits were used as an indication of growth imperfections. In Hibbard's5 work on lineage structure in copper crystals grown from the melt, he tested one crystal containing interlineage boundaries, and found a 50 pct increase in the critical resolved shear stress. Fleischer and Chalmers6, in a recent paper, mention briefly that, in the production of aluminium crystals from the melt when the growth rate was raised from 1.2 to 18 cm per hr, the yield stress increased 50 pct. They felt that the increase in yield stress with rate of growth might be attributed to a higher concentration of impurities in the gage length and also might be affected by the increased number of small-angle boundaries (striations). The present investigation was undertaken to determine the effect of the striation substructure on the strength of aluminum single crystals. EXPERIMENTAL PROCEDURE Aluminum single crystals of 99.9992 purity were grown from the melt using a technique described by Chalmers.7 The growth rate was varied from 0.6 to 20 mm per min, thus producing crystals with varying numbers of striation boundaries. To avoid prior deformation, the crystals were chemically cut to the desired length with a saturated solution of cupric chloride. They were then annealed at 580°C for 24 hr and allowed to cool slowly in the furnace. Finally, the specimens were electropolished using an electrolyte of 5 parts ethyl alcohol and 1 part perchloric acid. Each specimen was approximately 5 in. in length and 0.125 sq in. in cross section. The average orientations of the 5 series of crystals studied are shown on the stereographic projection of Fig. 1. The crystals were strained approximately 2 pct in a soft tensile machine. The strain sensitivity was 3.6 x 10-4 cm over a 5-cm gage length.

Jan 1, 1960

By H. W. Fox, M. R. Achter

IN a previous study of the effect of atmosphere on creep-rupture properties,' it was shown that the relative strength of nickel in air and in vacuum may be reversed by a change in either stress or temperature, Fig. 1. At low stresses and high temperatures the metal is stronger in air but stronger in vacuum at high stresses and low temperatures. A mechanism to explain this reversal was proposed involving two competing processes; oxidation strengthens the metal while adsorption of gas lowers the surface energy, relative to that in vacuum, and reduces the work required to propagate a crack. The process which controls is determined by stress and temperature. In a number of private communications, however, the objection has been made that even in the vacuum of objection mm of Hg used in this study, the surface of a

Jan 1, 1960

By C. H. Li, J. A. Sarteli, W. Bonfield

The stress to cause a permanent micros train of 2 x 10-6 in. per in. (defined as the microscopic yield stress) in beryllium is found to be very sensitive to surface condition. The initiation of plastic flow in as-machined specimens, which contain a high density of twins and large residual compressive stresses to a depth of about 0.010 in. from the surface, occurs by the nucleation of slip from high stress fields around twin tips in the surface layers. Removal of the damaged surface layers by chemical polishing results in an appreciable increase in the microscopic yield stress, which is attributed to the remoual of stress raising twins rather than to the release of residual stresses. IT is well known that the macroscopic mechanical properties of beryllium are very sensitive to the nature of its surface finish. Matthews and coworkers1 have shown that the tensile strength of rolled beryllium sheet can be considerably enhanced by chemical polishing, presumably due to the removal of the high concentration of notches, twins, and large residual compressive stresses normally found in the surface layers of ground specimens. There was no similar effect of surface condition on the macroscopic yield stress (the stress to produce 0.2 pct strain), a point to which we shall return. To date there have been no extensive studies on the effect of surface condition on the microstrain region of beryllium. Recent measurements2 of the stress to cause a permanent microstrain of the order of 10-6 in. per in. on machined hot pressed QMV beryllium, gave values ranging from about 600 to 3500 psi. Reasons for the considerable scatter in the results were not discussed. In this paper, we wish to show that the microstrain region of polycrystalline beryllium is, in fact, very sensitive to surface condition. The stress to cause a permanent strain of 2 x 10-6 in. per in. which for convenience we will refer to as the microscopic yield stress, can be increased by almost a factor of 2 by minimizing the amount of surface damage. The variation of microscopic yield stress is attributed to the presence of twins in the surface layers, rather than to residual compressive stresses. EXPERIMENTAL PROCEDURE The starting material for this investigation was commercial purity hot pressed QMV beryllium, with an average grain size of about 20 . The effects of surface treatment were assessed by comparing the microstructure with residual stress measurements and microstrain properties. Specimens were prepared for metallographic examination by wet grinding with 240, 400, and 600 papers, followed by polishing with a suspension of fine alumina in warm 20 pct oxalic acid. After this treatment, the surface could be examined, either in the unetched condition with polarized light, or after etching in 2 pct hydrofluoric or boiling 20 pct oxalic acid with normal light. Thin films of beryllium suitable for electron transmission study were prepared from bulk specimens by chemical polishing with hydrofluoric and phosphoric acids, and were examined in an RCA-EMU-3 electron microscope. Residual stress measurements were made by a procedure similar to that of Treuting and Read.3 Specimens 4.0 in. by 0.625 in. by 0.080 in. were prepared by three different machining procedures, namely: turning, grinding, and sawing, in order to introduce different levels of residual stresses. An electrical resistance strain gage was attached to one side of the specimen, and that surface was then protected by an acid-resistant enamel, while the opposite surface was removed by etching approximately one thousandth of an inch at a time. The change in specimen curvature in the longitudinal direction was noted and the residual stress was calculated by the following formula:

Jan 1, 1963

By I. R. Kramer, L. J. Demer

Aluminum single crystals were pulled in an electrolytic cell allowing surface removal during the deformation. The extent of Stages I and 11 of the stress-st-aitz curve was increased and the slope decreased as the rate of metal removed from the surface was increased. An increase of the strain rate caused a decrease in the effectiveness of the metal removal. The data indicate that the work-hardening coefficient in Stage I is determined primarily by the conditions which exist on the surface of the crystal. In Stages 11 and 111, both surface effects and internal barriers are important. ALTHOUGH numerous investigations have been conducted on the plastic flow characteristics of metals in an attempt to explain the mechanism of work-hardening, relatively few studies have taken into account the influence of the surface. In all current theories of work-hardening it is assumed that the impediments to the movement of dislocations are within the crystal. The barriers due to the surface and the existence of solid and liquid films have been neglected even though it has been demonstrated that the surface exerts a large effect. A number of investigators1-l8 have shown that solid films on the surface of single crystals markedly affect their mechanical behavior. In general, the presence of a solid film tends to increase the yield stress and increase the work-hardening rate. Often, on single crystals, Stage I and, at times, Stage II regions are completely suppressed. Various mechanisms have been offered for the effects of oxide and metal films as well as the influence of electrolytes. Of these, concepts concerned with the locking of surface dislocation sources and the blocking of dislocations at the surface resulting in pileups appear to be actively considered at present. Barrett,11 Takamura,6 Gilman,19 Lipsett and King,20 Shapiro and Read,10 and Weiner and Gensamer21 are among those who have interpreted their results in terms of piled-up dislocations at the surface, while Adams.22 and Chalmers and Davis23 have explained their experimental observations in terms of locking of surface dislocation sources. In general, the change in plastic flow properties due to electrolytes has been explained in terms of the unblocking or unlocking of dislocations by the removal of the oxide films. In considering the two proposed mechanisms, it appears that the locking of sources of surface dislocations by a solid film should exert a primary influence only on the critical resolved shear stress for flow and not on the slopes of Stages I and 11. However, the blocking at the surface of dislocations from internal sources may also affect the critical resolved stress and furthermore exert an influence throughout the whole plastic range. In certain cases it does not seem feasible to explain the results of experimental observations in terms of locking of surface dislocation sources. The abnormal aftereffects found by Barrettll,12 by removing the oxide by an acid treatment are excellent evidence of the blocking of dislocations at the surface. Additional evidence in favor of a blocking due to a pileup of dislocations at the surface may be found from the observations that the critical resolved shear strength continues to increase with the thickness of the oxide layer until very heavy oxide layers are formed. If the locking of surface dislocations sources were the dominant factor, the critical resolved shear stress would not be expected to increase after all of the surface sources were locked by the formation of the oxide. This may be expected to happen after a few atomic layers of the oxide are formed. In spite of the above evidence on the strong influence of the surface on the plastic flow characteristic, this has been ignored in current theories of work-hardening. Seeger24,25 suggested that most of the dislocations may slip out of the crystal only when the specimen axis is within certain areas of the orientation triangle. In other areas the resolved shear stress in other glide systems is large enough to generate dislocations which can form Lomer-Cottrell locks, thereby decreasing the average slip distance in some directions and causing a larger hardening rate. Friede126 assumed that at the beginning of Stage 11, a large number of Lomer-Cottrell dislocations are formed by a catastrophic process which used up all the Frank-Read sources on the secondary slip-planes. In this manner a fixed number of Lomer-Cottrell locks is formed which act as barriers against which the dislocations can pile up. In Stage 111, Seeger24 and Diehl, Mader, and Seeger25 proposed that Lomer-Cottrell barriers are circumvented by the cross slip of extended screw dislocations. Cottrell and Stokes,27 Friedel,26 Cottrell,26 and stroh29 suggest that the Lomer-Cottrell dislocations collapse under the stress field of the dislocation pileup. It is the purpose of this paper to report the changes in Stages I, II,and III of the deformation process in

Jan 1, 1962

By I. R. Kramer, L. J. Demer

T. H. Alden and R. L. Fleischer (General Electric Research Laboratory)— The authors' results indicate clearly and, we believe, significantly that during tensile deformation the surface layers of an aluminum crystal are hardened more severely than the interior of the crystal. A probable explanation of this effect, as the authors indicate, is that dislocations in the primary slip system may be obstructed at the surface or, it should be added, near the surface. The intent of this discussion is to show that the oxide film on aluminum is not likely to be responsible for this effect, but that the results can be understood if it is assumed the secondary slip is more active in the surface layers than in the interior. Prior study has shown that the principal mechanical effect of an oxide film on a single crystal is to raise the yield stress while leaving the rate of strain hardening during the initial deformation relatively unaffected.33 Since the yield stress is unchanged during polishing in the present case, we conclude that continual removal of the oxide film exerts a small effect on the plastic hardening.* It appears that the hardening interactions are occurring not only at the immediate surface, but to an appreciable depth below it, although with decreasing severity. For example, Kramer and Demer found that with removal of 0.004 in. from a specimen, the easy glide region was extended somewhat; but the yield stress did not decrease. The initial yield stress was recovered only after 0.041 in. was removed. Since a very brief polish would permit dislocations trapped behind a surface film to run out,34 extra dislocations must, instead, be trapped to a considerable depth below the surface. The same conclusion is drawn from the observation of decreasing hardening slope with increasing surface removal rates. If the hardening interactions were only at the immediate surface, a full softening effect would be observed at some small removal rate. The view is taken here that strain hardening is principally caused by small amounts of secondary slip.35 The secondary dislocations will interact in various ways with the primaries, interfering with their motion and causing them to accumulate in the crystal. Prior studies of easy glide have shown Diehl's model of hardening to be qualitatively consistent with the effects of impurities,36 of temperature,36 and of crystal size.37 On this basis the enhanced hardening of the surface layers in aluminum arises from increased secondary slip at and to some depth below the surface. Selective removal of this hardened layer is expected to decrease the measurable "bulk" hardening, the effect increasing with the removal rate and decreasing with the applied strain rate. We suggest that the stress on secondary systems is raised by the bending moments arising from interactions with the grips during the deformation. This stress from the grips has been shown to be a maximum37 near the surface, and hence, increased secondary slip should result. Prior investigations of grip effect:; indicate that as the grip stresses are raised by changing the crystal shape, the easy glide slope increases while the extent of easy glide decreases.38-40 It has been shown also that bending moments superimposed during tensile testing may either decrease easy glide, when supporting the moments caused by gripping, or increase it, when cancelling the gripping moments.38 This interpretation of the authors' results, emphasizing the special importance of secondary slip near the surface, is also consistent with the earlier results of Rosi.41 Copper crystals alloyed with silver in the surface layer show greatly increased easy glide compared with pure copper. In addition, the easy glide slope is reduced. The effect of bulk alloying in extending easy glide has been well established and has been interpreted as indicating the relative difficulty of secondary slip in alloy crystals. Since non-basal glide is difficult in zinc crystals, the effects of surface removal during deformation may be less important. Experiments to test this idea are in progress. I. R. Kramer and L. J. Demer (authors' reply)—The authors wish to thank Dr. Alden and Dr. Fleischer for their discussion. Our interpretation of the data in the paper is that dislocation motion is obstructed by "debris" which starts to form at the surface and extends towards the interior of the crystal with further plastic deformation. The fact that we did not find a reversion from Stage II to Stage I by surface removal shows that in Stage II the "debris" fills the entire cross-section of the specimen. Drs. Alden and Fleischer take the view that bending stresses due to the grips are responsible for the

Jan 1, 1962

By I. R. Kramer

Studies of the effect of size of the specimen on the change of slopes of Stages I and 11 by surface removal showed that the change of Stage I was independent of size with respect to the polishing rate; however, the change in the slope of Stage 11 with polishing rate increased directly in proportion to the surface area. The removal of the surface during the test affected the plastic deformation characteristics of gold, aluminum, and zinc single crystals and polycrystalline aluminum. The apparent activation energy of aluminum was found to be decreased markedly by removing the surface during the deformation process. In previous papers1-3 it was shown that the surface played an important role in the plastic deformation of metals. By removing the surface layers of a crystal of aluminum by electrolytic polishing during tensile deformation, it was found that the slopes of Stages I, II, and III were decreased and the extents of Stages I and II were increased when the rate of metal removal was increased. By removing a sufficient amount of the surface layer after a specimen had been deformed into the Stage I region, upon reloading, the flow stress was the same as the original critical resolved shear stress and the extent of Stage I was the same as if the specimen had not been deformed previously. The slope of Stage I was decreased 50 pct and that of Stage 11 decreased 25 pct when the rate of metal removal was 50 X 10"5 ipm. These data show that in Stage I the work hardening is controlled almost entirely by the surface conditions, while in Stages 11 and III both surface conditions and internal obstacles to dislocation motion are important. It appears that during the egress of dislocations from the crystal, a fraction of them becomes stuck or trapped in the surface regions and a layer of a high dislocation concentration is formed. This layer would not only impede the motion of dislocations, but would provide a barrier against which dislocations may pile up. In this case, there will be a stress, opposite to that of the applied stress, imposed on the dislocation source and dislocations moving in the region beyond this layer. It has been found convenient to refer to this layer as a "debris" layer. The "debris" layer may be similar to the dislocation tangle observed by thin-film electron microscope techniques.4 Reported in this paper are the results of studies on the effects of removing the surface during plastic deformation on aluminum crystals of various sizes. The effects of the surface on the yield point behavior of gold and high-purity aluminum crystals as well as the creep behavior were also determined. The effects of surface removal on polycrystalline aluminum (1100-0 and 7075-T6) are also reported. EXPERIMENTAL PROCEDURE For those portions of the investigation involving creep and tensile specimens, single crystals, having a 3-in. gage length and a nominal 1/8-in. sq cross section, were prepared by a modified Bridgman technique using a multiple-cavity graphite mold. The single crystals were prepared from materials which had initial purities of 99.997, 99.999, 99.999, and 99.999 pct for Al, Cu, Zn, and Au, respectively. The aluminum specimens for the size effect studies were prepared through the use of a three-tier mold in which crystals having a cross section of 1/8, 1/4, and 1/2 in. were grown from a common seed. The mold design was arranged so that one 1/2-in. crystal, two 1/4-in. crystals, and four 1/8-in, crystals of the same orientation could be cast. With this technique, it was possible to obtain only one set of crystals with the same orientation. Because of this limitation, it was not possible to determine both the changes of extent and slope of the various stages since a large number of crystals of the same orientation would have been required. Instead, only the change of slope as a function of the rate of metal removal was studied by abruptly altering the current density of the electrolytic polishing bath at various strains within the regions of Stages I and 11. The experimental techniques used for the tensile studies were essentially the same as those used previously.1,3 The specimens were deformed in a 200-lb Instron tensile machine, usually at a rate of 10-5 sec-5. A methyl alcohol-nitric acid solution was used as the polishing bath for aluminum. The temperature was maintained constant within ±0.l°C by means of a water bath. The tensile machine was

Jan 1, 1963

By C. Feng, I. R. Kramer

A study was conducted to determine the influence of the surface on the yield point of fcc metals and high-purity iron. For the high-purity fcc metals, the yield Point produced by restraining a specimen may be eliminated by removing a sufficient amount of the layer. A yield point similar to that in fcc metals was found when iron specimens were pre-strained after a prior deformation. This yield point is not due to an aging effect but is associated with the surface layer. The yield points in age-hardenable aluminum alloy and those connected with "work softening" are not affected by a surface-removal treatment and are, therefore, caused by bulk-type dislocation reactions. The yield point which appears in previously strained fcc metals has been the subject of numerous studies. Several theories have been advanced to explain this "unloading-reloading" yield point. Cottrell and stokes,' from their study on the effect of temperature on plastic properties of high-purity aluminum, considered that it was the result of an avalanche "breakdown" of Lomer-Cottrell sessile dislocations. Haasen and Kelly2 extended this concept of dislocation-dislocation interaction to account for the yield point when unloading and reloading was carried out at the same temperature. On the other hand, strain aging was found to be responsible for the yield point in A1-Mg alloy by Westwood and Broom,3 and in aluminum alloys containing various amounts of alloying elements by Smallman, Williamson, and Ardley.4 In these cases, the yield point is considered to be associated with the locking of dislocations by impurity atoms. Birn-baum and filer5,6 and Takamura and muira7 reported that, when a high-purity copper specimen was prestrained, then held at a lower stress, and finally reloaded at the prestrain temperature, a larger yield point was observed. Such an increase was attributed to the locking of dislocations by point defects. In addition, Bolling8 suggested that both mechanisms, i.e., dislocation-dislocation interaction and strain aging, are responsible for the yield phenomenon, at least in a brass. Thus, there appears to be experimental evidence for both the strain aging and dislocation-dislocation interaction theories to explain the yield point in the fcc metals and alloys. In a previous article,9 one of the authors observed that, if sufficient amounts of metal were electrolti-cally removed after deformation of a high-purity aluminum single crystal, the yield point did not appear upon reloading. Continued pursuit in this area revealed that the effect of the surface on the yield-point phenomenon is not limited to one metal but affects a variety of metals of different lattice structures. Nor is the effect limited to the yield points produced by simple unloading-reloading at constant temperature; the surface exerts an important role on the yield point even when the temperature is changed at some stage during the test. It is the intent of the present article to give additional information regarding the effect of the surface on the yield-point phenomenon and to show the association between the yield point in both fcc and bcc metals and the existence of a heavy concentration of dislocation in the region near the surface of a deformed specimen.10 EXPERIMENTAL Materials. The single crystals used in this study had a nominal cross section of 0.125 by 0.125 in. and a 3-in. gage length and were prepared by a modified Bridgman technique. The initial purity for the metals was 99.997, 99.999, and 99.999 pct for aluminum, copper, and gold, respectively. Bar stock of these same materials was used in the preparation of the polycrystalline specimens of aluminum and copper. The iron specimens were machined from rods of "ferrovac", reported to have a purity of 99.98 pct. In addition, a precipitation-hardening aluminum alloy, containing 1.5 pct Cu, 2.5 pct Mg, and 5.5 pct Zn, was used. The polycrystalline specimens of iron, copper, and the aluminum alloy had a diameter of 0.17 in. and a gage length of 2 in. while the high-purity aluminum specimen had a nominal rec-

Jan 1, 1965

By I. R. Kramer

Single crystals of aluminum were pulled in tension in a solution of paraffin oil and stearic acid. The critical resolved shear stress did not change with the concentration of the stearic acid solution; however, the extents and slopes of Stages I and II were affected greatly. The observations lend evidence that the weakening effect of surface-active agents is controlled by the rate of desorption of the metal soap formed by the reaction of the surface-active agent and the metal surface. IT has been shown by various investigators1-" that surface-active agents markedly affect the mechanical properties of single crystals. (A surface-active agent, for the purpose of this report, is defined as a long-chain organic molecule which contains one or more polar groups. Usually, however, investigations have considered only molecules having one polar group.) In general, when single crystals are deformed in some solutions containing surface-active agents, the creep rate, Fig. 1, is increased and the yield strength is decreased. The fatigue strength has been reported to be affected also.ll Rehbinder and his asociatesl' explained the "weakening" effect of surface-active agents in terms of physical adsorption. They assumed that a large pressure was created in microcracks which existed on the surface of the crystal." Harper and Cottrell,' from their study of the effects of surface conditions, found that the deformation characteristics of zinc single crystals were not altered by a solution containing a surface-active agent unless the surface of the specimen had an oxidized surface. They concluded that the role of the polar molecule was to remove the strengthening effect of the oxide coating. Later, And-radeetBpresented additional evidence which appeared to agree with this conclusion. In contrast, Klinken-berg et al.7 reported data which confirmed the results of Rehbinder. Using zinc and cadmium crystals which had been cleaned by electrolytic polishing, a large increase in the creep rate was observed when Lle specimens were tested in a 1 pct oleic acid-paraffin oil solution. They also reported that the creep rate

Jan 1, 1962

By I. R. Kramer

A study was made of the effect of surface-active agents an copper, gold, and zinc single crystals as well as polycrystalline aluminum. The study on coppw showed that the maximum effect of the surface -active agent occurred at the same concentration of the solution as that at which the rate of solution of the copper soap was the greatest. Surface -active agents did not affect the creep behavior of gold or freshly polished zinc specimens. The creel-, rate of zinc specimens in a solution containing a surface-active agent zoas always lower than that of freshly polished specimens. In previous papers1'2 it was reported that the surface played an important role in the plastic deformation of metals. By removing the surface layers of a crystal of aluminum by electrolytic polishing dur- ing tensile deformation, it was found that the slopes of Stages I, 11, and In were decreased and the extent of Stages I and I1 were increased when the rate of metal removal was increased. The results of the investigation of surface-active agents showed that changes in the slopes and extents of Stages I and II occurred when single crystals of aluminum were deformed in tension in a bath containing solutions of paraffin oil and stearic acid. The amount of change was a function of the concentration of stearic acid and the maximum effect occurred at a concentration of 0.002 mole per liter. These results were interpreted2 in terms of the rate of solution of metal soaps which form as a result of the chemical reaction between the surface-active agent and the metal. According to this interpretation, the "weakening" effect is controlled by the rate of solution of the soaps which depends upon the concentration of surface-active agents. At low concentrations, the number of metal soap molecules formed is low; at high concentrations, the rate of solubility is low, because of the high degree of saturation.

Jan 1, 1963

By A. Rosen, P. Wynblatt, J. E. Dorn

The temperature, strain rate, and structure dependence of the flow stress in a poly crystalline Fe-2 pct Mn alloy was investigated between 77" and 370°K. It was possible to identify the low-temperature data from 77° to 160°K with Dorn and Rajnak's theory of the Peierls mechanism of plastic deformation. Above 160°K one or more thermally activated mechanisms must he operative; however, these were not identified in this investigation. The mechanistic basis for the rapid decrease in the flow stress of bcc metals with an increase in temperature over the low-temperature range is yet being debated. Various dislocation mechanisms have been suggested in the past but the agreement between the various proposed theories and the experimental results have not been definitive. In the present paper, the authors will demonstrate that the plastic behavior of polycrystalline iron containing 2 wt pct Mn plus interstitials agrees excellently with predictions based on the Peierls mechanism from 77" to 160°K whereas from 160" to about 370°K other as yet unidentified thermally activated mechanisms take over. Undoubtedly, the overlap of these mechanisms with the Peierls mechanism contributed to the difficulties of rationalizing the low-temperature behavior of iron and its alloys. I) EXPERIMENTAL TECHNIQUES AND RESULTS Although extensive data are now available on the effect of temperature and strain rate on the flow stress of various bcc metals and alloys, it was, nevertheless, deemed necessary for the objectives of the present study to obtain highly accurate data of the type most pertinent for checking the theories on a series of well-documented work-hardened states. Iron containing 2 wt pct Mn was used in this investigation in order to obtain a lower ductile to brittle transition temperature than that for iron.' The additional elements present were 0.004 pct C, 0.05 pct 0, 0.004 pct S, 0.003 pct P, 0.006 pct N, and 0.001 pct Si. The as-received 3/8 by 3/4 in. bars were cold-rolled to 0.100-in. thickness, recrystallized under argon for 30 min at 1073"~, further cold-rolled to 0.063-in. thickness, and finally recrystallized under argon for 30 min at 1000°K. This treatment gave a stable reproducible equiaxed grain structure having an average grain diameter of about 90 p. Prior to the final recrystallization treatment, the sheet was machined into tensile specimens 1/4 in. wide having a 1.625-in.-long gage section. All specimens were tested in controlled-temperature baths on an Instron Testing Machine. For convenience in the theoretical analyses the data will be given in terms of the shear stress for flow, 7, the shear strain rate, f, and the shear strain, y. A series of three standard strain-hardened states were obtained by prestraining specimens at 300°K and at a shear strain rate of 7.68 x lo-' per sec to three stress levels of 6.89 X l08, 10.3 X lo8, and 14.5 x 10' dynes per sq cm, respectively. Immediately following this prestrain the temperature bath was changed and each specimen was pulled in tension at either f = 7.68 X lo-' or f = 3.06 X 10"3 per sec. In terms of the accuracy that was achieved, the values obtained did not deviate more than *0.1 X 10' dynes per sq cm and * 1°K from the reported values of stress and temperature and not more than *5 pct in the reported values of the strain rate. The tensile stresses were converted to shear stresses using a factor of 1/2. The shear stress for the initiation of flow at the test temperature was determined by taking a y = 6.16 x 10'3 offset. from the modulus line at which point good accuracy could be achieved in determining y and the associated flow stress 7, with only a negligible increase in the pre-

Jan 1, 1965

By H. G. Sell, G. W. King

An investigation was made of the lensile proper-ties of recrystallized high-purity tungsten and a W-1 pel ThO2 dispersed-phase alloy over the temperature region of 800° to 2400°C. The thoria addition resulted in a modest strengthening effect over the entire temperature region. A decrease in ductility of both materials occurred above 0.5 Tm which was caused by void formation. Current theories of IT has long been recognized that a second phase of hard particles has a strengthening effect on a pure metal. At low or intermediate temperatures (<0.5 Tm), the strengthening effect is thought to arise mainly from the interaction of dislocations with dispersed particles. Above 0.5 Tm, dynamic recovery processes greatly alter the deformation mechanisms from those simply involving glide, and grain bound- strengthening by a dispersed second phase do not adequately explain the tensile results. Melallographic examination suggests that the improved strength of tire alloy results from the effect of thoria on the mierostructure. Stress-dependent thermally activated processes were found to occur high temperatures. aries may act as sources of weakness rather than strength because of grain boundary sliding. Grain boundary sliding at high temperatures has been postulated to be the primary factor giving rise to the formation of voids or cavities at grain boundaries1-3 which in turn cause premature failure and poor ductility.4 Voids, once formed, can grow by the condensation of vacancies from the equilibrium concentration&apos; or from the excess vacancies produced by the deformation.4,5 The high-temperature tensile properties of unalloyed tungsten have previously been investigated by Sikora and Ha116 and also by Taylor and Boone.7 The purpose of the present work was to investigate

Jan 1, 1965

By E. C. Rudolphy, M. E. Potter, J. R. Mitchell

The effects of 0.006 to 0.20 pet Sn ml the hot workability and the annealed mechanical properties were investigated for Types 302, 410, and 430 stainless steel. The hot workability of these steels was not significantly affected by their tin content within the range studied, although some effects on mechanical properties were noted. Apart from the effect of tin, optimum hot-working temperatures and V-notch Charpy impact transition temperatures for these grades were determined. HIGH tin residuals in some heats of stainless steel have been blamed for the poor hot workability, particularly during secondary mill rolling. However, very little quantitative information has been available. Previous work1"6 with carbon steels indicates that tin increases tensile strength and hardness but de- creases tensile and impact ductility. Halley,7 in reviewing the sources and effects of residual elements in carbon and alloy steels, concluded that much of the surface checking (hot shortness) encountered in rolling was caused by copper, and that tin, arsenic, and antimony combined with copper to form low-melting constituents which further increase the steel&apos;s sensitivity to hot shortness. These elements had little effect in the absence of copper. A more recent paper by Langenberg and Johnson8 concluded that tin reduces hot workability but that researchers disagree concerning the amounts which will cause trouble. They state that laboratory investigations with small ingots seem to indicate a higher tolerable level of tin than do statistical studies of mill data, and also that statistical analysis of mill data indicate that small amounts of residual tin are detrimental to the surface quality of stainless sheet. The accumulative increase in the general level of tin and other tramp elements in steelmaking materials will present greater problems to steelmakers in the future. The purpose of the present study was to obtain quantitative information on the specific effects of tin on the hot workability and mechanical properties of such common stainless steels as Types 302, 410, and 430.

Jan 1, 1962

By C. H. Lee, R. Maddin

The diffusion rates of Ag110 in cylindrical single crystals of 99.99 pct pure silver, which were twisted to a total surface strain of 0.91 during the diffusion anneal at temperatures of 700°, 750°, and 800°C, were measured by sectioning and counting as a function of the strain rates. The ratio of the diffusivities while strain ing occurred (Ds) to those of the unstrained specimens varies linearly with the rate of twisting and attains values of near 100 for some of the rates used. The enhancement of diffusion by straining is inversely proportional to the temperature at which diffusion occurs. The activation energy for diffusion determined from the data plotted as a function of the rate of twisting decreases from 44,090 cal per mole for zero strain, to an asymptotic value of 21,000 cal per mole for the strain rates of 22 x it)"5 see-l. Qualitative explanation for the observations based on the generation of nonequilibrium number of defects by plastic deformation will be discussed. The initial research of Buffington and cohen1 on self-diffusion in a iron under compressive stresses contributed the first quantitative information concerning the effect of applied stresses on diffusion. These results were obtained from radioactive Fe55 plated on one of the horizontal surfaces and compressing the large-grained specimens while the diffusion-anneal was occurring. Enhancement of diffusion of a maximum of seventeen times was observed provided the strain was in the tertiary stage of creep and the rates of straining were at least as fast as rates used in the normal creep test. On the other hand, Darby, Tomizuka, and Balluffi,2 extending silver single crystals up to 30 pct elongation at rates of straining about equal to those used by Buffington and Cohen observed no effect. For the past two and a half years at the University of Pennsylvania, we have been investigating the effect or torsional strains on self-diffusion in silver single crystals. If enhancement is observed as has been reported1 a possible explanation may be based upon the generation of fairly large numbers of point defects and their role in the diffusion process. Hence, since torsion should produce an abundance3 of point defects, an increase in the diffusivity while the crystal is being twisted should easily be measured. EXPERIMENTAL PROCEDURE Our research uses single crystals of silver prepared from 99.99 Ag by the Bridgman method in a dynamic vacuum of less than 25 µ. As grown, they are about 25 cm long by 1.3 cm in diam. The crystals are cut into 7.5 cm lengths with a jeweler&apos;s saw and machined to the shape shown in Fig. 1. The test length of the crystal is machined to a 0.6 cm diam after which the ends are masked and the test section etched heavily in HNO3, and KCN:(NH4),S2Os , solution to remove the effects of machining. The specimen is then annealed in vacuum for 8 to 12 hr at 800°C to remove any residual stresses and also to recrystallize the end sections. The recrystallized ends are necessary since experiments showed that single-crystalline end sections are too soft to transmit the desired torque. Occasionally, recrystalliza-

Jan 1, 1960