Search Documents

Using 5-p Ni powder and 0.018 ,u A1203, oxide dispersion strengthened nickel alloys were prepared by mechanical mixing of powders, followed by compaction, sintering and extrusion. Processing variables such as cooling of the powder during mixing, electrostatic discharging, mixing time, amount of oxide, and so forth, were studied to determine the effects on room-temperature tensile and high-temperature creep-rupture properties and on the reproducibility of alloys. MECHANICAL mixing of metal and metal oxide powders provides one of the simplest and most inexpensive methods for preparing dispersion strengthened metal-metal oxide alloys;" however, because of large differences in specific gravity, powder particle diameters and other variables, difficulties have been encountered in reproducing alloys and alloy properties. Using 5-p Ni powder and 0.018 p A1203, the following variables were investigated: a) Blending techniques b) Blending time c) Volume fraction of oxide for the selected pow- ders d) Sintering of compacts before extrusion Cooling of Powders During Blending— Cremens and Grant had indicated that dry ball milling of the powder mixture gave superior results over other procedures. When ultra-fine metal and oxide powders became available and comminution was unnecessary or offered little gain, the use of dry mixing in a Waring Blendor gave optimum results.' In the current study, observations of the powder mixtures indicated that considerable heat was generated due to the high speed of the Waring Blendor (15,000 rpm). This heating appeared to produce some degree of clustering and pelletizing. To minimize such agglomeration, a Pyrex cooling coil was installed in the mixing vessel. A double coil, water cooled, proved to be quite satisfactory, providing a fair degree of cooling along with good erosion resistance. Discharge of Electrostatic Charge—Electron-microscopy showed that agglomeration was minimized by the cooling procedure but was not entirely eliminated. It appeared that some of the ag- glomeration had to be explained on the basis of an electrostatic attraction due to the high-speed blending operation. These charges had the effect of promoting the growth of alumina clusters. At the end of the blending procedure such clusters had an effective size which was as much as 50 times that of the individual powder particles and were very tightly bunched. Several methods were utilized to try to discharge the electrostatic forces to minimize the clustering. One successful method, utilized in alloy 17, involved continuous exposure during blending to a radium source of 50 millicuries at a distance of 1.5 ft from the container. A number of other methods were noted to work equally well. Fig. 1 shows the more open oxide structure which results from such a treatment, permitting the matrix metal to penetrate into the cluster more effectively. The combination of powder cooling and discharging led to noticeably improved structures. Fig. 2 shows a cross and a longitudinal section in alloy M-17, one of the best alloys, illustrating the marked decrease

Jan 1, 1961

By J. K. Elliott, P. H. Kelly

Many engineering functions such as surface metering work and laboratory compressibility check points involve the use of liquid densities of light hydrocarbon mixtures at various pressures and temperatures. However, at the present time, no simple reliable method exists for determining density variation, particularly if the composition of the liquid is unknown. Consequently, a study was undertaken to develop and present a simple and accurate method of predicting density variation of a light hydrocarbon liquid with pressure and temperature, knowing only the density of the liquid at some condition. The experimental liquid compressibility data from API Project 37 by Sage and Lacey' have been considered to be accurate within 0.5 per cent and cover a wide range of pressure (14.7 to 10,000 psia), temperature (100" to 400°F) and molecular weight (up to 150). From these data, a set of liquid density curves, which relate density to pressure, temperature and molecular weight, was developed. These curves make it possible to predict density variation with pressure and temperature. Compared to extensive laboratory compressibility data on a complex, light hydrocarbon liquid, the use of the liquid density curves resulted in an average error of less than 0.5 per cent. Based on the results of this analysis, it is concluded that the set of liquid density curves developed from the data of Sage and Lacey provides an accurate and simple method for predicting the density variation of light hydrocarbon liquids when the density at some condition is known. These curves should be very helpful in many engineering calculations, particularly in the surface metering of light hydrocarbon liquids. INTRODUCTION Many situations arise in field and engineering laboratory work, such as reservoir engineering studies, check of experimentally determined laboratory data and orifice flow-meter formulas, where liquid density factors at various pressure-temperature conditions are required. Also, the need for accurate light hydrocarbon liquid information has become more important with the advent of miscible-type displacements for secondary recovery purposes in oilfield operations. Several reliable methods are available1 - "or determining the density of liquid hydrocarbons if the composition of the liquid is known. However, there is a definite lack of methods for accurately determining the variation of density when the composition of the liquid is unknown. The purpose of this study is to review the various methods for determining hydrocarbon liquid densities and to develop a simple and reliable method of determining variation in density of light hydrocarbon liquids with pressure and temperature when the compositio~n of the liquid is unknown. METHODS FOR DETERMINING DENSITY OF LIQUIDS OF KNOWN COMPOSITION Sage, Lacey and Hicks' have proposed a method to predict the density of light liquid hydrocarbons by using partial molal volumes. Data are available on experimentally developed partial liquid volumes of hydrocarbons over a rather limited range of temperature, pressure and composition. The partial mold volume method has proved satisfactory for determining the density of some hydrocarbon liquids when the composition is known. Within the range covered in the Sage, Lacey and Hicks1 data, the results agree within about 3 per cent of the experimental values. Hanson mentions the limitation of this method to a composition range of approximately 10 per cent by weight of methane, which will not allow this correction to cover most low molecular weight-light hydrocarbon liquids. Standing and Katz2 studied data on light hydrocarbon-liquid systems containing methane and ethane at high temperature and pressure and have presented a method for determining liquid densities, assuming additive volumes for all components less volatile than ethane and using apparent densities for methane and ethane. The compressibility and thermal-expansion curves used by Standing are based on assumptions that compressibility of a hydrocarbon liquid at temperatures below 300°F is a function of the liquid density at 60°F and that thermal expansion of the liquid is affected little by pressure. The information required to use this technique with an example problem is furnished by Standing.' Hanson eports an average error of - 0.5 per cent using the method of apparent densities in calculating liquid densities of several volatile hydrocarbon mixtures. However, as implied, the apparent density method is not applicable for liquid density calculations when the composition of the liquid is unknown. Watson- as presented a method

By N. Standish

Heat transfer coefficients have been measured in beds of various packings irrigated with mercury and molten fusible alloy countercurrent to hot gases. The measured coefficients for both systems were found to increase with gas velocities and liquid rates. Correlations were determined which show this dependence and also indicate that heat transfer in these systems is influenced by the liquid flow characteristics and the thermal conductivity of the gas and the solid packings. A heat transfer model has beer2 proposed which explains the various features of the experimental results. On the basis of this study, which gives an insight into the heat exchange in the melting zone of the blast furnace, it was concluded that by comparison with the furnace stack heat transfer coefficients are about 1.5 times higher in the melting zone. EACH year large tonnages of metal are produced in operations which, in part, involve liquid metal irrigation of "packings" countercurrent to hot gases. The melting zone in blast furnaces and in cupolas is a good example of packings irrigated with a liquid melt countercurrent to gases. In all instances of this kind large amounts of heat are exchanged and it is desirable to have some knowledge of heat transfer phenomena involved in these systems. So far the most common method of analyzing furnace efficiencies, fuel requirements, and the general thermal state of the furnace has been through the use of heat balances. As heat balances are essentially statements of the first law of thermodynamics they give no real indication of the factors which govern heat transfer between phases in the various zones of blast furnaces. Hence, rational improvement in production efficiency and the development of theoretical models is only possible if the heat transfer characteristics are known at every stage of the process and related to the important variables involved. This has been generally recognized for some time but it was only recently that Kitaev et al.' have produced a comprehensive treatment of heat transfer in solid-gas countercurrent systems such as the blast furnace stack and the packed bed regenerator. Using their treatment it is now possible to predict the effect of particle size, thermal conductivity, bed porosity, and the flow rates of both the gas and the solid material on the heat transfer in the blast furnace stack. However, the stack of a blast furnace is only one part of an integral unit for which the heat transfer analysis cannot be complete without also considering the heat exchange in the melting zone. The complexity of heat transfer processes in this region of the furnace has so far escaped quantitative description. Yet, the melting zone accounts for a greater amount of heat exchange than all the other zones of the furnace put together. Moreover, if the reduction of oxides in the melting zone proceeds in part in the liquid state the importance of heat transfer on furnace productivity and on the metal and slag temperatures is obvious. THEORY Heat transfer for two-phase flow in packed beds is a complex problem involving a number of heat exchange paths for which interphase areas are not known with any degree of certainty. Analytical solution is, therefore, difficult. This difficulty is emphasized by noting that Rabinovich~ and Luck have only recently solved the steady-state heat transfer for simplified two-phase heat exchangers of known area. However, useful progress can be made for the system considered by making a not unreasonable assumption that the usual heat transfer considerations apply and restricting treatment to the steady state. For these conditions the rate of heat transfer dq in a height dz of a packed bed of unit area is: dq = UaATdz [I.] Integration of Eq. [I] then gives the total heat transferred: assuming both U, the overall heat transfer coefficient, and a, the interphase area, to be independent of bed height. Since a, in these systems, is unknown it is convenient to combine this term with U. The group U, then represents the overall heat transfer coefficient on a volumetric basis. If AT is linear with q, then for a bed of unit volume Eq. [Z] can be integrated to give: is the log mean of terminal temperature differences. From Eq. [3] U, can be readily calculated as q and {AT)im are experimentally obtained quantities, but a difficulty arises in interpreting its meaning. Two approaches are possible depending on whether the effect of packing in the transfer of heat is neglected or not. If the packing is thermally decoupled then the resistance concept gives the relationship: which states that the overall resistance is the sum of the gas phase and the liquid phase resistances (assuming areas are equal throughout). Because the resistance to heat transfer in liquid metals is negligible by comparison with that of the gas,4 Eq. [4] can be simplified, i.e.:

Jan 1, 1969

By D. V. Edmonds, C. J. Beevers

Tensile tests were carried out on a! titanium containing 850, 1250, and 2700 ppm 0, and up to -500 ppm H. The tests were performed at -196", -78", 20°, 150°, and 300°C at a strain rate of -1.0 x 10??3 sec-1. Increasing oxygen content, increasing grain size, and decreasing test temperature resulted in enhanced embrittlement of the a titanium by the hydrogen additions. Metallographic observations showed that this can be correlated with the influence of these parameters on the introduction of cracks into the a! titanium by fracture of titanium hydride precipitates. CRAIGHEAD et al.1 reported that the hydrogen content normally found in commercial-purity a! titanium (60 to 100 ppm) was sufficient to cause a substantial lowering of the impact strength, and they attributed this embrittling effect of hydrogen to the precipitation of titanium hydride. Lenning et al.&apos; found that in commercial-purity a titanium there is an almost complete loss of impact strength at about 200 pprn H, which is approximately half the value needed to eliminate the impact strength of high-purity a titanium. They also showed that the presence of 3000 ppm hydrogen reduces the room-temperature tensile ductility of commercial-purity material to a value of the order of 10 pct; the corresponding hydrogen concentration for high-purity titanium is over 9000 ppm. It thus appears that the detrimental effect of hydrogen on the mechanical properties of commercial-purity titanium becomes evident at much lower hydrogen contents than for high-purity titanium. The main difference between the two types of a titanium might be expected to be the higher level of interstitial impurity in the commercial-purity grade. Jaffee et a1.3 studied the influence of temperature and strain rate on the hydrogen embrittlement of high-purity and commercial-purity ! titanium. In general, the behavior was the same for both materials; embrittlement was enhanced by decreasing temperature and increasing strain rate. Recent results from tests on commercial-purity a titanium containing 850 ppm O and varying amounts of hydrogen up to -500 ppm showed that the degree of embrittlement by hydrogen is intimately related to the fracture characteristics of titanium hydride precipitates.4 The present paper considers the interrelationship between the mechanical properties and micro-structural features of commercial-purity a! titanium containing 850, 1250, and 2700 ppm 0 and varying amounts of hydrogen up to -500 ppm. 1. EXPERIMENTAL PROCEDURE Three types of commercial-purity titanium supplied by IMI* were used in the investigation, and for the *Address: Witton, Birmingham 6, United Kingdom. purpose of this paper are designated Ti 115, Ti 130, and Ti 160. The principal impurity elements are given in Table I. The material was received in the form of 12.7 mm diam bars having a fully recrystallized structure. Tensile specimens with a round cross-section of 4.5 mm diam and a gage length of 15.2 mm were machined from the bars. In order to develop the same grain size (mean linear intercept of grain boundaries) in each of the three types the specimens were annealed under a dynamic vacuum of <10?5 mm Hg, Table 11. Specimen hydriding was carried out in a modified Sieverts apparatus;&apos; hydrogen was taken into solution at 450°C and after holding the specimens at this temperature for 24 hr they were furnace-cooled to room temperature at an average rate of -100 C deg per hr. By this method nominal hydrogen contents of 0, 50, 100, 250, and 500 ppm were introduced into specimens of Ti 115, Ti 130, and Ti 160 (100 ppm (wt) -0.5 at. pct). The actual hydrogen contents were calculated from the weight differences obtained by weighing the specimens before and after the hydriding treatment. Tensile tests were carried out at temperatures of -196", -78", 20°, 150°, and 300°C on a 10,000 kg In-stron machine at a nominal strain rate of -1.0 x 10-3 sec-1. Fractured specimens were sectioned in planes parallel to the tensile axis, mechanically polished to 0.25 µm grade of diamond paste, and then attack polished using a solution containing by volume 99 parts H2O, 1 part HF, and 1 part HNO3. Although the latter treatment unavoidably opened out cracks and voids visible after mechanical polishing, it did reveal the grain structure, titanium hydride morphology, and deformation twinning structure.

Jan 1, 1970

By E. J. KENNEDY

FEBRUARY 15-18 will be the outstanding dates of the month for members of the A. I. M. E., for then the 141st Meeting of the Institute is to be held in the Engineering Societies Building, at New York. What with 41 technical sessions, the Annual Business Meeting at 4 o&apos;clock Tuesday afternoon,, two sessions of the Section and Division delegates, minor committee meetings, and the many luncheons and dinners, the Dinner-Smoker, Informal Dance, President&apos;s Reception and the Dinner-Dance, the opportunity will be limited to do- more-than cast sheep&apos;s eyes at New York&apos;s other multitudinous attrac¬tions until the meeting is over. The technical program is diverse but well organized. The sessions are almost equally divided among the four days, with ten on Monday, Tuesday, and Wednesday, and 11 on Thursday. The meeting opens Monday morning with registration. Be sure to attend to this detail. Failure to do so may have its repercussions at the meeting and throughout the year.

Jan 1, 1932

By James Aston

A PROPER consideration of this subject is not confined to the technical channels of production and metallurgy. It concerns an industry, and should cover economic aspects which are of material importance in any program of development. The discussion may logically be treated under three subdivisions, as follows: (1) manufacture, (2) characteristics related to quality of material; (3) adaptability and exploitation of product. MANUFACTURE OF WROUGHT IRON The manufacture of wrought iron is the most ancient art of the ferrous metal industry. The eighty years or less of existence of processes identified with our modern "Age of Steel" is a relatively brief interval compared with the several thousand years associated with the production of wrought iron by man. From the primitive early methods of production, manufacture for many centuries followed the line of direct reduction. There were developments as experience was gained through the years; but man&apos;s needs for a strong, ductile, forgeable product were met by reducing the ore to metallic iron in a single-stage operation. Following the development several centuries ago of what has become our modern blast-furnace operation, manufacture of wrought iron was gradually transformed into a two-stage method of first producing cast iron and then refining this to the desired degree of forgeability; the forerunner in principle of today&apos;s scheme of manufacture of steel. The product retained the essential characteristics of highly refined base metal with iron-silicate slag incorporation, which were associated with the material resulting from direct reduction methods. Cort&apos;s invention of the puddling process in 1784 is a landmark in wrought-iron manufacture. It consisted essentially in adapting a coal-fired reverberatory furnace to the refining operation; thus lifting the industry out of the slough of

Jan 1, 1935

By J. W. Halley

THE effects of tin on steel have become increasingly important because of the necessity of using poorly detinned scrap, tin cans, and terne plate, in the open hearth. Since a tin can contains about 1.5 per cent tin, it would be possible to have up to 0.75 per cent tin in steel made with a 50 per cent scrap charge. In order to use tin-containing scrap, it is necessary to know the effect of tin on various grades of steel. The following investigation is by no means comprehensive but covers a number of steels in which tin content is important. PUBLISHED WORK A number of investigations of the effects of tin on rolling quality and physical properties have been published. It has been found that tin increases strength and hardness and reduces ductility and notched impact resistance. The decrease in ductility and notched impact resistance becomes more marked as the carbon decreases. McKimm1 found no change in Olsen ductility, Rockwell hardness, yield strength, tensile strength or elongation in cold-reduced strip containing up to 0.124 per cent tin. A tin content of 0.15 per cent gave difficulties in rolling and increased the hardness but 0.21 per cent tin showed no change in properties from material containing very little tin. No explanation of this contradiction is offered. Andrew and Peile2 investigated steels containing 0.10 to 0.25 per cent carbon and up to 0.63 per cent tin. They found an increase in tensile strength 0f from 100 t0 200 lb. per sq. in. for each 0.01 per cent tin on normalized samples. The elongation and reduction of area were decreased and the notched impact resistance was reduced markedly. Quenched and drawn samples did not show embrittling if water-quenched from the draw temperature of 1148°F. (620°C.). They could find no evidence of tin under the microscope. Whitely and Braithwaite3 investigated the effect of tin on rail steel containing 0.55 to 0.60 per cent carbon. They found that 0.08 per cent tin caused a marked decrease in elongation, notched impact resistance and the degree of bend. The tensile strength was increased in some tests and not in others. Bolsover and Barraclough4 investigated the effect of tin up to 0.50 per cent on a 0.35 per cent carbon steel and on several alloy steels with from 0.30 to 0.40 per cent carbon. They found a comparatively uniform decrease in notched impact resistance with increasing tin on quenched and drawn samples. If the samples were quenched from the drawing temperature or reheated to the drawing temperature and quenched, the embrittling was much less severe. Steels containing molybdenum suffered much less embrittlement than other steels. EXPERIMENTAL WORK Effect of Tin on Low-carbon Rimmed Steel Increasing quantities of tin were added to four ingots of a heat of the following ladle analysis: carbon, 0.08 per cent; manganese, 0.39; phosphorus, 0.009; sulphur, 0.025.

Jan 1, 1942

By H. A. Bedworth

ALLOYS of copper and silicon have been known for one hundred years or more but the commercial development of this type of alloy has taken place during the past few years. In 1905, Sperry1 proposed the use of copper-silicon alloys for springs and other purposes for which copper-tin bronzes were used. Some attention was given to this proposal at the time but no one succeeded in producing a practical alloy containing more than a fraction of a per cent. of silicon. The equilibrium relations of the copper-silicon system were studied first by Rudolfi2 and later by Sanfourche3 and Corson.4 The constitution of the system has also been recently investigated by Matuyama,5 and in the laboratories of the American Brass Co. by Smith.6 Some of the physical properties of the copper-silicon alloys have been investigated by Norbury7 and by Geiss and Van Liempt.8 Summarizing the results of various investigators of, the constitution of copper-silicon alloys, the solubility reaches its maximum value, 6.7 per cent. silicon, between 721° and 782° C. At 852° C. the solubility is 5.25 per cent., while at 400° C. it is only 4.1 percent. silicon. The copper-silicon alloy begins to get so hard at about 3 per cent. silicon that it is difficult to manage. It was found by Jacobs that the addition of manganese to this alloy considerably improved the working

Jan 1, 1929

By L. C. Uren

Field studies and laboratory research have established the fact that the expulsive force which drives petroleum into wells, from the reservoir sands in which it is stored by nature, is primarly an expression of the energy latent within compressed natural gas dissolved or occluded in, or otherwise associated with the oil. Each barrel of oil produced is forced into the recovery well by the expansive energy of a certain volume of compressed gas, originally stored with the oil in the pores of the reservoir rock; and each cubic foot of gas so produced with the oil and expanded to atmospheric pressure reduces by so much the total natural energy available for oil expulsion. This relationship between the volumes of gas and oil produced has seemed so important that petroleum production technolo-gists have come to regard the "gas-oil ratio," or the "gas factor" as it has been more conveniently termed, as a measure of oil-production efficiency. Different methods of oil recovery and production devices are now Com pared on this basis and estimates of ultimate recovery obtainable through their use are considered by many to be inversely proportional to the values of their respective gas factors. The writer has been among those who have given support to a widcspread movement toward a proper recognition of the significance of the gas factor as a guide in the control of producing oil wells, and does not wish to oppose its more extended application. It seems necessary, how-cvcr, in view of the almost elemental faith with which the principle of the gas factor has been received in many quarters, to point out that it is a most complex factor, and one which cannot be regarded as an absolute index of production efficiency without due regard to other contributing factors by which it is influenced to an important degree. Variables Influencing Gas Factor The mere recording of a low gas factor, obtained through the use of some method or device, does not necessarily imply efficient oil production; and conversely, a high gas factor does not always signify inefficient recov-

Jan 1, 1928

By A. G. Raine

For the technological age in which we live, with the constant goal of further improvement in the efficiency of mechanized systems, the need for a replacement of the antiquated drill and blast method of shaft construction has been recognized. For over a decade now; the trend in shaft construction has been toward large diameter bored shafts using either raise boring methods or more flexible, rodless "down the hole" boring machine. The limits of conventional shaft sinking have been reached, the mining regulations are more stringent, and the environmental agencies more aggressive, all contributing to the growing need for development of the rodless shaft boring machine. In the last three years in the United States, world shaft construction records have been achieved using a V-Mole machine, designed by Mirth GmbH of West Germany, using American electrics and hydraulics. Shafts of 7.0 meters (23 feet) diameter, totaling 2,255 meters (7,400 feet) in depth have been constructed at high advance rates, yet with unusually low accident rates. Bearing in mind the high cost of today&apos;s mining labor and the inherent danger associated with conventional shaft sinking, this alternative method of shaft construction achieves a fast, competitive, low manpower requirement, whilst enhancing a safer environment for the labor force. Recent results have proven that program time savings of 50 percent over conventional shaft sinking can be achieved which can be directly translated into improved client cash flow projections and more accurate project budgeting.

Jan 1, 1984

By M. G. Jones

AT the Edwards mine a 4 by 81/2-ft two-compartment shaft is used for men and supplies in the older workings down to the 900-ft level. All ore is hoisted through a 5 by 15-ft three-compartment vertical shaft which extends to the 1500-ft level. Ore pockets are on the 1300- and 1500-ft levels. The two-compartment countershaft used below the latter level is 6 by 12 ft inclined at 42°. Ore from the countershaft is hoisted to the 1350-ft level where it flows by gravity to the 1500-ft level ore pocket. One-ton skips are used in balance in the countershaft and two-ton skips, also in balance, from the 1500-It level to the surface. These skips are slung under the man cages. Each level has an ore pocket of 200 tons&apos; capacity. Development at Edwards is similar to that at Balmat except that haulage drifts are only 7 by 7 ft. They are mucked with Eimco-Finlay No. 12 loaders. A drill carriage similar to that used at Balmat is being tried out on the new 2300-ft level, the present bottom of the mine. Drifts are driven below grade and later raised 6 in. and ballasted with waste leaving a ditch 6 by 12 in. at one side for drainage. All development is done on an incentive bonus system, the miner paying for his explosives.

Jan 1, 1947

By John E. O’Rourke, Kevin M. O’Connor, Pamela H. Rey

INTRODUCTION The resurgence of coal mining activity in the United States, brought on by the spiraling costs of fossil fw1 energy in the Seventies, has come at a time of intense public concern for the quality of the environment. Notwithstanding pressure on our economy to develop alternate sources of fue1 energy to the import of oil, the legislatures of several states have reacted to public concern over the environment by passing strict regulations aimed at con- trolling the subsidence effect s of underground mining. Agencies of the federal government charged with assistance to the mining industry, including the Department of Energy and the Bureau of Mines, have sponsored a number of instrumentation and field measurement projects aimed at the development of subsidence prediction models that can aid the mine operator&apos;s task of subsidence control. There are good empirical models developed in Europe for subsidence prediction, but they were made possible by a large body of mining-induced subsidence data collected there over a long period of time. No com- parable subsidence data base exists in the United States, and consequently empirical modeling of subsidence is not a realistic approach for our near term needs. Moreover, the geologic and topographic diversity of the several coal regions in the United States is expected to necessitate the development of several empirical models, each one expected to be relevant to its own region. Because of the time and costs that are likely to be involved in an empirical modeling approach, it is considered more expedient and cost effective to develop a general, mechanistic model for subsidence prediction purposes. In order to develop such a model, it is necessary to investigate and quantify the mechanics of the subsidence process from the mine level up to the ground surface. The series of projects discussed in this paper are designed to achieve this objective and include the following work: (1) the identification of geotechnical instrumentation that will pro- vide mine level overburden and surface subsidence data. (2) a field demonstration of selected instruments, and (3) documentation of case histories for complete subsidence mechanics, using the demonstrated and preferred instruments. An identification of feasible instrumentation and monitoring techniques was completed by Woodward-Clyde Consultants (WCC) in 1977 (O&apos;Rourke and others). This paper discusses a demonstration of those instruments at a mine in Utah, and at two subsequent projects, currently underway at longwall mines in Colorado and West Virginia. &apos;he latter two projects when complete will provide documented case histories of subsidence mechanics. The process of optimizing subsidence instrumentation and monitoring techniques to the conditions encountered during installation and monitoring for these underground mines is shown to be an evolving one, and one which has had some notable successes to date. INITIAL DEMONSTRATION The initial design and demonstration of selected monitoring systems was carried out at the SUFCO No. 1 mine, near Salina, Utah. The instrumented panel was approximately 152 m wide. 640 m long. and was 290 m to 320 m deep. The mined height of coal. seam averaged 2.4 m. The mining method was room and pillar using continuous mining machines. This method allowed some monitoring of the supported condition during development, and eventually allowed monitoring of a caved system when both chain pillars and room pillars were extracted on retreat. The two instrument systems shown on Table 1 were selected from the earlier feasibility report for demonstration at SUFCO No. 1. Collectively, the two systems, one for a fully-supported mining method and the other for a fully-caved method, incorporate most of the instrumentation to be found within all five systems listed in the earlier feasibility report. The instrumentation includes surface, subsurface and mine monitoring installations. All of the SUFCO instruments selected to meet the specifications of the general instrument types listed on Table 1 were manually operated. That is, data from the installed system could only be obtained while a person was there to physically observe or operate the system readout. Automatic data recording equipment was available for some installations, but the objectives were to keep the systems as simple as possible for the demonstration project. A complete description of the surface, sub- surface and mine level instruments, and the demonstration project results are given in WCC (1982), and selected features are discussed in this paper.

Jan 1, 1982

By L. D. Jaffe

From data found in the literature, a method has been derived for calculating hardenability of titanium alloys from their composition. A single graph gives the contributions of each alloying element. These are simply added to a base hardenability for unalloyed titanium. Results agree satisfactorily with measured harden-abilities. RECENTLY the importance of hardenability of titanium alloys in permitting attainment of high strength and hardness has become apparent. If a titanium-base alloy has adequate hardenability for the section size and quenching practice used, it can generally be heat treated to high strength and hardness either by simple quenching or cooling from temperatures near the ß transus, by quenching and tempering (aging), or perhaps by direct isothermal transformation of ß1,2 If the hardenability is inadequate, high strength cannot be attained. Preliminary charts translating hardenability requirements for shapes quenched in various media into terms of Jominy end quenched hardenability specimens or ideal round sizes are now available for titanium alloys." The method proposed in 1942 by M. A. Grossmann for calculating hardenability of steels from composition has proved to be of great practical value.&apos; It appeared worthwhile to see whether, using information available in the literature, a corresponding method for calculating hardenability of titanium-base alloys could be derived. Data No systematic experimental study of the hardenability of titanium-base alloys has yet been made. There is available, however, a considerable quantity of scattered data bearing on hardenability. Some investigators determined Jominy curves on one or several alloys. Others reported as-quenched hardness for specimens of a few alloys cooled at various rates or in various media. Still others gave the as-quenched hardness for systematically varied composition, using one or several cooling mediums. The measurements utilized in this work were limited to hardness. Strength measurements were not used because a low strength may reflect high hardness combined with brittleness. Since, in general, the hardness of titanium alloys goes through a peak as the cooling rate is varied from extremely fast to extremely slow, the cooling conditions at which peak hardness was found were taken as the measure of hardenability.1,2 When as-quenched hardness was found to drop as the content of an alloying element (believed to increase hardenability) was raised, this was taken as an indication that the cooling rate was faster than that giving peak hardness; otherwise, the hardness should go up because of solid solution hardening. Also, if the hardness increased on tempering at low temperatures, this was again taken to indicate that the cooling rate had been faster than that giving peak hardness. Many of the data did not indicate precisely the cooling conditions for peak hardness but merely set a maximum or a minimum bound, or a bracket. Since the sizes of specimens quenched and the location of the hardness readings were not always given, it was occasionally necessary to estimate reasonable limits for them. Only the nominal compositions were available in some cases. As quenching from below the ß transus is equivalent to starting with a mixture of a and ß phases, whose individual composition would differ from the overall composition of the alloy, only measurements after quenches from above the ß transus were used. Hardness measurements on samples heated during metal-lographic mounting were also discarded. Because of their bulk, the data used will not be reproduced. They have been or will be published elsewhere.5-22 Approach All data were first translated into terms of ideal round size. For conversion from Jominy or quenched round or sheet, the author&apos;s graphs were used." For a few furnace cools or helium quenches where cooling rates were given, conversion was made on the basis of equal cooling coefficient.23 Plots of ideal round size for peak hardness against percentage of alloying element were next made for

Jan 1, 1956

By Lennart Bergstedt, Olov Fägremo

Boliden Metall Aktiebolag, the prime base metal mining company of Sweden, treats some 10-10.9 t/y (11-12 stpy) of sulphide ore in nine concentrators. During the years considerable effort has been devoted to the development of all phases of the technology of ore prospecting, mining, milling, smelting and refining. This has been necessary due to the complex and low grade ores. The autogenous grinding technique was first studied within the company as early as 1945. Basic test work commenced during the early fifties, whereby the merits of pebble grinding could be evaluated. In parallel with the converting of the rod mill/ball mill grinding systems to rod mill/pebble mill systems, the development work concerning the feasibility of autogenous grinding went on resulting in the installation of a 8 6.7 x 2.1 m (8 22 x 7 ft.) cascade mill at the Vassbo lead mine in 1959. Long term tests at the Vassbo plant together with a number of pilot plant test involving low grade silicious ores and pyritic comples base metal ores successive led to a better understanding of the process of autogenous grinding. Before a two stage autogenous grinding system could be chosen for the expansion of the Aitik copper mine, a carefully planned survey concerning grinding characteristics and variances in the ore and flowsheet was undertaken. The expanded plant went on stream in 1972 and in the beginning of 1973 and since then has performed excellently.

Jan 1, 1979

By H. R. Thresh, A. F. Crawley, D. W. G. White

The densities of liquid tin, lead, and Sn-Pb alloys have been measured over a range of temperature above the liquidus. In all cases, data can be adequately represented by an equation of the type p = a + bT. For pure tin, the values of a and b are, respectively, 7.139 and 7.125 x 10-4, and for pure lead, 11.060 and 12.220 x 10-4. At constant temperature, molar volumes in the Sn-Pb system vary linearly with composition. DURING the course of a long-term program at the Department of Energy, Mines and Resources, Ottawa, Canada, the densities of liquid tin, lead, and Pb-Sn alloys were studied. The work reported herein draws on two sets of results independently achieved by Thresh, on the one hand, and by Crawley and White, on the other. EXPERIMENT The method and apparatus were originated by Thresh and have been described in detail in Mines Branch reports.172 In operation, the 14 cu cm graphite pycnometer is put in the furnace as shown in Fig. 1 after a machined charge has been placed inside the pycnometer and the lid screwed down. The dimensions of the charge are such that, upon melting, a small excess of liquid metal is discharged through the capillary hole to displace the weighted float above. When the pycnometer has been equilibrated at the experimental temperature, the

Jan 1, 1969

By G. Borelius

ABOUT the turn of the century, Gibbs&apos; thermo-dynamic theory of heterogeneous equilibrium, on the one hand, and the experimental methods of thermal and microscopic analysis, on the other, gave to the physical metallurgist his first scientific tool, the equilibrium diagram. The classical equilibrium diagram of a binary alloy system shows the boundaries between ranges of homogeneous and heterogeneous equilibrium in their dependence of concentration and temperature. A homogeneous solid sohtion which on cooling passes such a boundary is assumed to precipitate, forming a mixture of two phases with different concentrations. The equilibriunl diagram and the equilibrium theory, however, give no information about the time scheme of the process or the intermediate states passed during precipitation. For this reason it satisfies neither the practical need of the metallurgist nor the curiosity of the physicist. As a matter of fact, in the heat treatment of alloys for technical use the objective very seldom is the equilibrium state. Thus good mechanical properties of construction material are connected, for the most part, with some intermediate state. As these intermediate states are thermodynamically unstable, there is, from a theoretical point of view, always to be expected a decay of the good properties with time; and it is a matter also of practical interest to know whether this natural life time of a material is of the order of, say, ten or thousands of years. Thus, for many reasons, there is a current demand to complete our knowledge of equilibrium through knowledge of the kinetics of the precipitation phenomena. From the point of view of the physicist, the most interesting question in this case is whether there are any general laws governing the kinetics. According to a generally accepted view, precipitation is ruled by two more or less independent phenomena, the formation of nuclei of a new phase and the growth of these nuclei. It is also commonly accepted that there is a tendency for the velocity of growth to increase with increasing temperature because of the increasing mobility of the atoms. There is also a tendency for the velocity of growth to decrease in the neighborhood of the two-phase boundaries. So far, however, very little is known quantitatively about this fundamental phenomenon in the case of solid metallic systems. In our laboratory attention has been directed especially toward the nucleation phenomena, and a series of measurements have been carried out with the guidance of a work- ing hypothesis (based on experiences from previous work on order-disorder transformations in alloys) about the influence on the nucleation of thermo-dynamic potential barriers. However, before discussing the experiments, the theoretical ideas will be considered. In a binary solid solution the arrangement of atoms on the lattice points approaches with increasing temperature a state of full randomness, as illustrated by the ball model of Fig. 1, that might represent a [111] plane of a face-centered alloy with 30 pct "black" and 70 pct "white" atoms. In reality the atoms are changing places continually with their neighbors so that the picture should rightly have been a moving one. On account of this thermal motion the concentration of black atoms within a certain group of, say, a hundred or a thousand lattice points fluctuates with time around the bulk concentration of 30 pct in a manner governed by statistical laws. With decreasing temperature two independent changes in this state grow more and more important. First, the mobility of the atoms decreases, and second, the forces between the atoms will have an increased influence on the fluctuations. In alloys with a tendency for precipitation, which are the concern of this lecture, the distribution function of concentration fluctuations will broaden, so that the relative probability of great local variations from the bulk concentration increases. Fig. 2 gives an example of such a fluctuation. When the alloy is supercooled below the solubility limit into the range of two-phase equilibrium, the fluctuations will now and then at some point give rise to a state that resembles the equilibrium state and thus will form a stable nucleus that is capable of growing by diffusion processes. In discussions with colleagues and in the literature, I have often encountered the idea that three or four atoms of the dissolved metal could form a nucleus of the new phase. A look at the ball model might be enough to indicate that this cannot be true. If it were true, there should be nothing but nuclei, whereas we know from experiment that nucleation must be a rather rare occurrence. In fact we have, as will be mentioned later, certain reasons to believe that the nuclei are formed by fluctuations containing some hundreds of atoms, which should be the order of the number of black balls in the fluctuating group of the figure, if it were extended into three dimensions. As a working hypothesis we have assumed that the fluctuations producing nuclei, though large and rare, still are ruled by the distribution laws of fluctuations of the supercooled solid solution in its initial state. Thus the probability of nucleation will be connected to the thermodynamic properties of the solid

Jan 1, 1952

By F. W. DeVries

The subject article is an excellent comparison between two potential oxidants, molecular oxygen and hydrogen peroxide, as used in the Palangana field at the time of the trials. The tests showed no advantage to using hydrogen peroxide; however, it would be unwise to generalize that the experience in these trials was universally true. During the time of the work cited, extremely high levels of an unusual impurity were recycling in the lixiviant, which substance was a catastrophically destructive catalyst for peroxide. Since this material was not removed before recycle, it was not surprising that much of the peroxide fed was decomposing in the feed piping and never made contact with the uranium mineralization. Under these conditions, indeed, peroxide showed no improvement over oxygen. This is, however, perhaps the most adverse environment encountered to date in US in-situ uranium leaching. In other operations, peroxide has proved advantageous where two factors have been exploited: 1.Despite the tendency for Hz02 to decompose to water and oxygen in the in-situ leach environment, its higher redox potential before decomposition has provided higher leach rates. In some formulations, overloading beyond the O2 saturation equivalent with peroxide has allowed higher oxidant levels, and higher leaching rates, when overloading with molecular O2, led to vapor-locking.

Jan 1, 1983

By Nicholas Kowall, K. L. Clark

Maximum furnace efficiency and close control of final steel composition demand that the steel melter be able to follow closely the variations in the carbon content of the bath. For many years, the fracture test has been used by melters for estimating carbon, because it requires only a very short time to pour a sample into a chill mold, cool it in water, break it with a sledge hammer, and observe the fracture. After long experience gained from the observation of such fractures, most melters are able to estimate the carbon content of steel with amazing accuracy, particularly in the lower carbon ranges. Notwithstanding the utility of the fracture test, there has been widespread interest in other methods for rapid carbon determination to supplement it and to ensure against possible errors in human judgment. Several methods, based upon measurement of magnetic properties as functions of carbon content, have been described in the literature1-6 and have been found to give reasonably reliable results in plant practice when scrap composition is known and controlled. A difficulty encountered in the use of analyzers of the magnetic type is that alloying elements do change the relationship between carbon content and magnetic properties and it becomes necessary to establish calibration curves for all the expected combinations of alloy residuals that are not oxidized in the bath. The work reported here is of an investigation of a method that is independent of alloying elements normally present in constructional steels, being based upon the relatively well-known fact that in plain carbon and low-alloy steels martensitic hardness is a function of carbon content alone. Work oF Other Investigators In I938, Burns, Moore and Archer published & curve? that showed that the hardness of martensite is a function of carbon from 0.10 to 0.50 per cent and is independent of grain size or alloy content, at least within the rallge found in construc-tional S.A.E. compositions. Some of the deeper hardening types investigated, however, contained carbon to a maximum of only o.2o per cent. Using this principle, Kern8 developed a method of rapid carbon determination for S.A.E 43xx steels, His procedure consisted of chill-casting a test bar that was large enough to give a a that could be prepared for Brinell indentations. The test piece was quenched immediately after solidi fication was complete and hardness readings were taken, so that the carbon content could he read from an experimentally determined curve giving the relationship between as-quenched hardness and carbon. Experimental Work Although Kern&apos;s work had been done with a relatively deep-hardening steel, it

Jan 1, 1944

By K. L. Clark, Nicholas Kowall

Maximum furnace efficiency and close control of final steel composition demand that the steel melter be able to follow closely the variations in the carbon content of the bath. For many years, the fracture test has been used by melters for estimating carbon, because it requires only a very short time to pour a sample into a chill mold, cool it in water, break it with a sledge hammer, and observe the fracture. After long experience gained from the observation of such fractures, most melters are able to estimate the carbon content of steel with amazing accuracy, particularly in the lower carbon ranges. Notwithstanding the utility of the fracture test, there has been widespread interest in other methods for rapid carbon determination to supplement it and to ensure against possible errors in human judgment. Several methods, based upon measurement of magnetic properties as functions of carbon content, have been described in the literature1-6 and have been found to give reasonably reliable results in plant practice when scrap composition is known and controlled. A difficulty encountered in the use of analyzers of the magnetic type is that alloying elements do change the relationship between carbon content and magnetic properties and it becomes necessary to establish calibration curves for all the expected combinations of alloy residuals that are not oxidized in the bath. The work reported here is of an investigation of a method that is independent of alloying elements normally present in constructional steels, being based upon the relatively well-known fact that in plain carbon and low-alloy steels martensitic hardness is a function of carbon content alone. Work oF Other Investigators In I938, Burns, Moore and Archer published & curve? that showed that the hardness of martensite is a function of carbon from 0.10 to 0.50 per cent and is independent of grain size or alloy content, at least within the rallge found in construc-tional S.A.E. compositions. Some of the deeper hardening types investigated, however, contained carbon to a maximum of only o.2o per cent. Using this principle, Kern8 developed a method of rapid carbon determination for S.A.E 43xx steels, His procedure consisted of chill-casting a test bar that was large enough to give a a that could be prepared for Brinell indentations. The test piece was quenched immediately after solidi fication was complete and hardness readings were taken, so that the carbon content could he read from an experimentally determined curve giving the relationship between as-quenched hardness and carbon. Experimental Work Although Kern&apos;s work had been done with a relatively deep-hardening steel, it

Jan 1, 1944

By J. J. De Witte, J. G. Cazort

The Paranam plant in Surinam (formerly Dutch Guiana) was built during 1939-40 to supply crushed and dried bauxite for the growing U.S. aluminum industry, supplementing production from the Suriname Aluminum Co.&apos;s Moengo works, which began operation in 1922. A subsidiary of Aluminum Company of America, Suralco&apos;s total annual production from these two plants averages 2.55 million dry metric tons of various grades of bauxite. Starting in 1941 with bauxite from mines on the west side of the Suriname River, annual production at the Paranam plant has varied from a low of approximately 450,000 tons to more than 1 million tons in 1949. High production rates during World War II and the late 1940&apos;s rapidly depleted these reserves, and in 1950 plans were made to mine the known deposits on the east bank of the river, about five miles downstream from the original Paranam plant.

Jan 11, 1960