By Chen Song

Cobalt basic carbonate particles were precipitated from 1.0mol cobalt nitrate or cobalt sulfate solution with ammonia carbonate. By controlling the zeta-potential of the particles and the ionic strength of the solution, the uniform particles with ellipsoid or rod shapes were obtained. During the precipitation process, the interface tension was diminished to the minimum and therefore the Ostwald ripening and secondary nucleation were both inhibited. The morphology and the size control by zeta-potential seem to be the result of thermodynamics rather than classical crystalline kinetics. The particle sizes were in the range of 0.4-0.6, 0.3-0.4 micrometer. After thermolysis, the spinel-type C0304 particles were produced. The morphologies of C0304 particles were similar to that of their precursors.

Jan 1, 2003

By Jing Zhan, Tian-zu Yang, Wei-feng Li, Li-Hua Jiang, Shi-yan Xu, Jian-yang Huang, Chuan-fu Zhang, Yan-qing Fan

The amount and activity of coal, reduction temperature and other parameters of the process of bottom-blown reduction of liquid high lead slag were investigated in laboratory. Methods to strengthen the bottom-blown reduction process were studied by industrial production. The results were in the follows: the reduction temperature was 1150℃; reduction time was 1.5h; the reductant was anthracite; lead content in slag was controlled to 2%; the rate of coal was 7% and gasification loss of coal in high temperature was severe; liquid lead slag reduction rate was faster with coal; prolonging the reaction size had little effect on reducing lead in slag; the size of the reactor can be further reduced.

Jan 1, 2015

By E. Fockedey

he destruction of free cyanide on a Co3O4 doped carbon felt was studied. The experiments were done with an eiectrochemical filter press cell on dilute alkaline solutions containing 250 mg/l NaCN. No chloride ions were added to the solutions. The cobalt oxide protects the felt against corrosion and has a catalytic effect on the degradation of the cyanide. This kind of electrode allows working with current density as high as 1200 Aim without any visible degradation of the felt. The most interesting results were obtained with a current density of 400 Aim' at which the cyanide concentration can be lowered to 5 mg/l with a current efficiency of more than 70 % and a specific energy consumption of about 10 kWh/ kg CN.

Jan 1, 1998

By Yufeng Guo, Tao Jiang, Jianjun Fan, Haizheng Hao

"Function of High Pressure Roll Grinding (HPRG) in production of oxidized pellets from magnetite concentrate as raw material was systematically studied. It was found that bentonite dosage decreased from 1.3% to 0.8% if specific surface area of magnetite concentrate pretreated by HPRG was up to 2553.41cm2.g-1. The green ball quality improved obviously due to the increase of specific surface area and fine particles content, and the improvements of size distribution and the ballability of pretreated materials. However, the decrease of pellet porosity accelerated the primary solid phase reaction and oxidation reaction, which made the pellets surface form compacted layer that handicapped the diffusion and migration of oxygen, promoting the formation of double layer structure of finished pellet. Consequently, the compression strength of preheated and roasted pellets was not markedly improved by HPRG.IntroductionWith the increase of proportion of pellets in the BF recently, the technical-economic index of BF has obviously been improved. Consequently, the production and the quality of BF pellet are given more attention [1]. However, with the decrease of the quality of iron ore concentrate, the problems such as poor ballability, high bentonite dosage, high preheating and roasting temperature are becoming the great challenges to not only the quality of finished pellets, but also the energy consumption [2, 3]. In order to overcome these problems, mechanical pretreating technologies such as the High Pressure Roll Grinding (HPRG) and Damp-grinding are widely applied. HPRG has a number of advantages such as low energy consumption, high productivity and easy-maintaining. It is more economic and environmentally friendly than the Damp-grinding technology [4, 5]. A great number of experiments have revealed that HPRG can improve the quality of hematite pellets. Although there are some studies of function of HPRG in the magnetite oxidized pellet production, they are not comprehensive and systematic, especially to the preheating and roasting system [1, 2, 6, 7]. Accordingly, the influence of HPRG on the pelletizing system and the preheating and roasting system are systematically studied in production of magnetite oxidized pellets in this article."

Jan 1, 2011

By I. M. Richardson, M. Janssen, W. Geerstma, I. J. Bennett, V. A. Popovich

Avoiding wafer breakage is a big challenge in the photovoltaic silicon industry, limiting production yield and further price reduction. Special fracture strength tests suitable for thin silicon solar wafers and solar cells, to be used in combination with Weibull statistics, finiteelement (FE) modelling and digital image correlation have been developed in order to study the mechanical stability of solar wafers. The results show that removal of the saw damage significantly increases the strength of crystalline silicon wafers. Furthermore, it was found that silicon crystallinity and the location where the wafer is extracted from the cast Si ingot have a significant effect on the strength, namely samples taken from the bottom of the ingot are 30% stronger than those taken from the top. The study also showed that there is a decrease in fracture strength when an anti-reflective SiNx coating is applied, which is caused by high thermal stresses.

Jan 1, 2015

By Jinjing Dua, Jun Zhua, Kuiren Liub, Bin Wang, Xiaolei Wua

V-Ti-Fe as hydrogen storage alloy was prepared by reducing metal oxides with a metallothermic reduction method. The deoxidation process of the V-Ti-Fe alloy was performed by electro-deoxidation and vacuum induction melting method, respectively. The results showed that the content of oxygen impurity can be controlled at about 0.2wt% after electrolyzing for 240min. Both the maximum values of hydrogen absorption capacity and the effective hydrogen desorption capacity are 2.65wt% and 1.01wt%, respectively. The deoxidization effect of vacuum induction melting process is more remarkable, with Ce as the reducing agent. It is found that Ce addition is beneficial for reducing the componential segregation, promoting the hydrogen absorption activation of V-Ti-Fe alloy. When m(Ce)/m(alloy) is up to 5%, the oxygen content has been reduced to 0.05wt% and the maximum hydrogen absorption capacity and the effective hydrogen desorption capacity are up to 3.36wt% and 1.85wt%, respectively.

Jan 1, 2015

By Xirneng Zhu

The electrochemical behavior of Pittsburgh and Illinois coal pyrite in basic and neutral borate/sulfate solutions was investigated. In the transpassive region, aggressive oxidation of pyrite occurred. The reaction products in this region were Fe(III) oxide, sulfate ion and partially oxidized sulfur intermediates. The formation of sulfur and polysulfides was identified by in-situ Raman spectroscopy. The growth kinetics of the reaction product film, resulting from transpassive oxidation of coal pyrites, were studied using chronoamperometry measurement with both stationary and rotating disk electrodes. The reaction rate was well correlated by a paralinear rate equation. The effects of electrode rotation speed, solution pH and temperature were examined. The kinetics were compared to those for mineral pyrite.

Jan 1, 1994

By R. Hurman Eric

The electrode in a slag-resistance electric furnace is the central factor in the design and operation of the furnace by its role of conveying the smelting power, i.e. heat needed for the operation. The control parameters are the size and positioning in the slag bath which are defined by slag resistivity, furnace resistance, cell constant and power input sequence all of which are closely interrelated. The flow of heat generated by the electrode current determines the energy distributions and thus the furnace dimensions. Heat flow models concerning vertical, horizontal and combined two-dimensional flows are discussed. All these considerations are based on the experimentally determined slag properties such as its resistivity.

Jan 1, 1995

By Oscar Perales Perez, Atsuo Kasuya, Kazuyuki Tohji, Yoshiaki Umetsu

"The removal of iron and various heavy-metal ions by their incorporation into stable ferrite-type precipitates at 25°C is a promising alternative to clean up large volumes of polluted aqueous effluents. Our research work investigated the conditions to produce magnetite and various M-bearing ferrites (where M: Zn, Cu, Co, Ni, Cd, etc.) directly from aqueous solutions at 25°C by simultaneous control of the oxidizing conditions and pH. The formation of the solids was followed by monit9ring the oxidation-reduction potential (ORP) and rate of proton release during the aerial oxidation of the suspensions at constant pH (contact stage). Only mildly oxidizing conditions, represented by ORP values between -110 mV and -150 mV and a moderate oxidation rate of Fe(II) species were conducive to well-crystallized ferrites at ambient temperature.' It was also found that increasing the Fe/M mole ratio in starting· solutions enhanced the stability ·of the M-bearing ferrites at ambient temperature. When the formation of the ferrite was incomplete, aging of the sludges in their mother liquors at 25°C promoted the crystallinity of the precipitates. The mentioned conditions ·favored the suitable progress of the ferrite-forming reaction involving the oxidation of Fe(II) entities, subsequent hydrolysis of produced Fe(III) species and dehydration of the intermediate:· Furthermore,· the ferrite formation at· low temperature permits the elimination of iron and co-existing heavy metal ions to sufficiently low concentration.In tum, the characterization of the precipitates evidenced their magnetic nature (room-temperature saturation magnetization above 60 emu/g) as well as the effective incorporation of target metal ions into the ferrite structure."

Jan 1, 2000

By Patricia A. Wells

In the remelting of scrap, the ultimate goal is to produce clean aluminum while minimizing metal losses. Recently, it has become more difficult to make significant recovery improvements in Reynolds' Reclamation Plants since metal recoveries were nearing the theoretical maximum. In an effort to gain a better understanding of the factors impacting Reynolds remelting process, a series of experiments using a Taguchi-type design was performed. Specifically, the critical variables and interactions affecting metal recovery of shredded, delacquered Used Beverage Containers (UBC) melted in a side-well reverbatory furnace were examined. This furnace was equipped with plunger-style puddlers and metal circulation. Both delacquecing and melting processes operated continuously with downtime only for necessary mechanical repairs. The experimental design consisted of an orthogonal array with eight trials, each using nominal 500;000 lb shred charge volumes. Final recovery results included molten output and metal easily recovered from dross generated during the test.

Jan 1, 1995

By Dong Liang, Qijie Zhai, Zhichen Zhang, Qixin Li, Zhishuai Xu

"The formation, distribution and survival of pure Al nuclei under surface pulsed magneto oscillation (SPMO) treatment were investigated with thecombination of experiments and numerical simulation. The results indicated that the nuclei originated from the whole top surface of melt owing to the oscillation of top surface induced by SPMO. The temperature field significantly affected the survival of the nuclei The electromagnetic force and flow field of the melt with SPMO treatment were simulated by finite element software ANSYS. The electromagnetic force mainly distributed below the top surface near the mould wall. The electromagnetic farce not only made the melt oscillate but also increased the convection of meh below the top surface vigorously. The oscillation near the top surface of the melt promoted the nucleation largely, and the convection increased the uniform of the temperature distribution in the whole meh which favored the survival of nucleiIntroductionAs we all know, fine equiaxed grains are beneficial fur the improvement of the mechanical property, process ability and the uniformity of metallic materials [1-2]. With the researches of recent decades, people discovered that the electromagnetic field is an efficient method to refine the solidified structure of metals [3-7]. Pulsed magnetic field technology obtains more and more attentions in recent years due to its smaller power consumption, bigger instantaneous magnetic field intensity, non-contacting with the meh and simple convenient equipment manufacturing [8-9]. However, the melts would splash fiercely when pulsed magnetic field is applied with a slightly higher power. Thus, based on the understanding of the solidification refinement mechanism of electric current pulse (ECP) [10], Gong et al [11] developed a novel technology called pulse magneto-oscillation (PMO) to refine the solidification structure. The technology can be easily applied in the solidification structure refinement of continuous casting slab. But fur aluminum continuous casting, the sump is very shallow, which greatly limits the application of pulse magneto-oscillation technology."

Jan 1, 2014

By Du Sichen, S. Seetharaman, Wei Liu

"The viscosities of two-phase mixtures are of great importance in the modelling of the fluid flow in metallurgical processes. For example, in steel making and refining, the intimate mixing of metal droplets in the slag phase requires a consideration of the effective viscosities for the mixture. The present work was aimed at an understanding the phenomena underlying the viscous flow in a two-phase mixture with widely differing viscosities.Emulsions of silicone oils of known viscosities (345mPa.S and 1010mPa.S at 293K) with small amounts of water evenly distributed in the same were prepared by subjecting the mixture to uniform stirring using a magnetic stirrer. The viscosities of these emulsions were measured at constant temperature by rotating cylinder method using Brookfield Digital Rheometer. The uniformity of the preparation of the emulsions was confirmed by the reproducibility of the results. Th7 measured viscosities were generally found to be independent of the torque under the experimental conditions so that the two-phase mixture could be considered as a Newtonian liquid. The variation of viscosities with temperature and the effect of addition of a surface-active substance were also studied in this work.The measured viscosities were found to be· higher than those of both pure water and silicone oil. The experimental viscosities were found to increase with increasing concentration of water. The influence of surface tension on the viscosities was examined by adding surfaceactive agent to the mixtures. The result is discussed and compared with theoretical models developed by Einstein, Taylor and Oldroyd."

Jan 1, 2000

By Neale R. Neelameggham

"Ferrous and non-ferrous metal industries are used to handling several billion tons a year of ore bodies, fuel and fluxing agents by mineral processing techniques and varieties of extractive metallurgy ""Reduction"" processes. Metal industry know-how can be applied to meet the challenge of Reducing CO2 in the atmosphere. Processes for generating alloys of carbon and hydrogen by Reducing the CO2 and water mixture, [carbonated water or water vapor] called Soda, to easily stored fuels are normally endothermic. The processes are similar to generation of hydrogen alone from water which is also endothermic. But hydrogen is more difficult to store than compounds [or alloys] of carbon and hydrogen. This recycling of CO2 and water are possible by using other forms of energy by innovative carbon capture methods.Thermodynamic Diagrams developed for Soda [CO2 and H2O] - metal reactions provide hints for using low cost unused stored energy in un-recycled metallic waste for thermal conversion. Choices for conditions for the electrochemical approaches [using solar - wind - hydropower] are also discussed.INTRODUCTIONIn 2006, I was reading some of the arguments put forth by learned scientists on the benefits and lack of benefits of bio-fuels. I found that the arguments rose partly from the differing system boundaries that were chosen by one versus the other. Some part of the argument may have been based on political climate or atmosphere rather than the analytical science. This situation is seen when scientists discuss which came first - the chicken or the egg, the fuel or biological matter, the oxide or the element, and so on.Then I thought –[just like many of the learned persons participating in this symposium] that common fuels - regardless of them being simple hydrocarbons or oxygenated hydrocarbons or carbohydrates - can all be made from the respective oxides of carbon and hydrogen by simple chemical reductions efficiently carried out in an economical fashion. This is the systematic approach we take when designing a chemical or metallurgical process facility."

Jan 1, 2008

By Z. Smieszek, J. Botor, Z. Miczkowski, S. Sobierajski

"From 1978, the direct process for the smelting of chalcocite concentrates in a flash furnace by the Outokumpu method has been applied at the Glogów II copper smelter. The chemical composition of these concentrates make it necessary to control the process very strictly. In this paper, the method for controlling and measuring the main technological parameters of the copper production by flash smelting is being presented. It includes the determination of the chemical composition of the concentrate, its grain structure, the temperature of liquid products of the process, oxygen content in process gases, as well as lead concentration in copper and copper concentration in slag.The main process parameters are determined from the mass and energy balances. The relations between parameters, such as an effect of grain structure of a concentrate on oxygen and oil consumption, and dependence of chemical composition of a concentrate on capacity and products quality are discussed. 1. IntroductionThe Polish copper concentrates, as most concentrates occurring worldwide, contain from 18% to 30% Cu, and less sulphur (7-11%) and iron (2-5%). The main copper-bearing mineral contained in the concentrates is chalcocite, while bornite and chalcopyrite are present in smaller quantities. Moreover, the organic carbon (5-7.5%), arsenic (0.05-0.3%) and lead (1.2-3.0%) are also contained in the concentrates. The gangue consists mainly of silica, aluminosilicates, calcium carbonate and magnesium carbonate. Their proportions make the addition of slag-forming agents unnecessary.The composition of Polish concentrates, especially their low iron content, allows their application in the direct flash smelting process for blister copper production. Low sulphur content is the factor which determines the necessity of oxygen application in this process."

Jan 1, 1989

By Masayoshi Matswnoto

The Kosaka Smelter and Refinery produces copper and lead, and has a history of more than 100 years as a metallurgical department of Dowa?s Kosaka Mine. The Smelter treats complex sulfide concentrates which are difficult to smelt. Valuable metals are recovered using various processes developed by Kosaka Smelter and Refinery. Effluent waters from the smelter contain large quantities of heavy metals. This paper describes how Kosaka Smelter and Refinery recovers valuable metals from various effluent waters and handles overall waste waters in order to meet strict environmental standards.

Jan 1, 1993

By Wiraseranee. Chompunoot, Kazuki Morita, Toru H. Okabe

"Aiming at the development of more effective recycling processes, dissolution behavior of rhodium into molten slag was investigated. Using a pure rhodium crucible and Na2O-SiO2 slag system, equilibration experiments were carried out for 18 h at 1423-1623 K under various oxygen partial pressures of 0.005-1 atm with varied slag basicity. Rhodium solubility increased with increasing oxygen potential, slag basicity, and temperature. Rhodium dissolved into slag as rhodate ion ([RhO2]-) by the endothermic reaction: Rh(s) + 3/4O2(g) + 1/2O2-(in slag) = [RhO2]-(in slag). In the dissolution reaction, the “rhodate capacity” of slag is newly-defined. The correlation between rhodate capacity and optical basicity is reported.IntroductionDue to its high chemical resistance and outstanding catalytic properties, rhodium (Rh), one of the platinum group metals (PGMs), is utilized in various applications such as catalysts, molten glass vessels and containers, and electronic devices. Owing to the rarity of Rh resources in nature, recycled Rh from scraps such as spent automobile catalytic converters is currently considered as an important source of Rh supply [1]. According to the recycling practices, Rh is currently mainly recovered from scraps along with other PGMs such as platinum (Pt) and palladium (Pd) by a dry process (e.g., smelting), a wet process (e.g., leaching and subsequent separation of PGMs from aqueous solution), or a combination of both processes [2]-[4]. Among these processes, smelting is commonly applied because PGMs can be effectively separated from a relatively large amount of various impurities coexisting in scraps. In the smelting process, Rh and other PGMs are collected in the collector metal (e.g., iron and copper), and impurities in scraps are removed into slag [4]-[6]. The process may be carried out at a temperature range of 1573-1973 K, in either an oxidizing or reducing atmosphere. Due to the high oxidation resistance at high temperatures, Rh is expected to be collected efficiently in the metal collector rather than being oxidized and forming RhOx in a molten slag. However, Rh loss into slag does occur in this process [7]."

Jan 1, 2011

By I. G. L. Sinclair

The Selbaie deposit is located in northern Quebec. It is comprised of three distinct, but genetically related, Cu-Zn-Ag ore bodies which also contain economically significant amounts of Au. The deposits are Archean in age and volcanogenic in origin. At Selbaie, ore microscopy has been employed to aid in planning of ore beneficiation methods and to monitor the ongoing performance of the concentrator. Examples of both types of study are described. Early in the life of the mine, excessive amounts of Zn appearing were found to be appearing in the Cu concentrate. Microscopic examination of concentrates showed that this was being caused by the presence of coatings of supergene chalcocite on sphalerite grains. Fine coatings of supergene galena and chalcopyrite were also observed on some sphalerite grains. The presence of Ag and Au in the ores makes an important contribution to the revenue of the mine. The various modes of occurrence and mineralogical relationship of these two metals are described and discussed. Monitoring of the ongoing concentrating process at selbaie is done by qua-litative and quantitative examination of products collected at various points along the circuit. Causes of such problems as excessive loss of metals to the tailings or inefficient recovery of individual metals, can often be identified and possible solutions proposed.

Jan 1, 1989

By Xinlei Jia, Wenming Guo, Yanling Zhang

A large amount of stainless steel dust rich in Fe, Cr, and Ni has been being generated in China. Smelting treatment is accepted as a practical method for the recovery/reutilization of these second resources, during which Fe, Cr, and Ni is reduced into one metal phase and then separated from the residue slag. Based on the typical compositions of stainless steel dust, the residual slag can be termed as CaO-SiO2-MgO-Al2O3 system. In this paper, the activity coefficients of Cr in Fe-Cr-Ni-C (-Si/Al) melt and the properties of CaO-SiO2-MgO-Al2O3- 1%CrO system thermodynamically approached. Then, in laboratory experiments, the recovery ratios of Cr and its distribution behaviors between Fe-Cr-Ni-C melt and CaO-SiO2-MgO-Al2O3 slag system were examined.

Jan 1, 2015

By Gudrun A. Saevarsdotti

For decades tile aluminium industry has been practicing gas treatment of aluminium melts. This treatment is of great importance because of its influence on 'impurity" and inclusion removal from the melt. The gas-melt interaction is greatly influenced by the gas composition, melt temperature etc. This paper gives an overview of the interaction between argon-chlorine gas mixtures and the aluminium melt. It covers the thermodynamics of the reaction between the chlorine and a number of different elements commonly found in liquid aluminium, and discusses the behaviour of reaction products in the melt. The paper reports an experimental study of the behaviour of the chlorine-molten aluminium interface, using sodium contaminated aluminium melt with and without the addition of grain refiner.

Jan 1, 1996

By Takeshi Ohgai, Hisaaki Fukushima, Tetsuya Akiyama, Joon-Seo Ki

"Recently, an intensive attention has been paid to the electrodeposition of Zn-Cr alloy in the field of the production of super-highly corrosion-resistant alloy plated steel sheets for the next generation. In this study the electrodeposition of Zn-Cr alloys from the sulfate baths was conducted to investigate the codeposition mechanism of Cr with Zn. As a result, Cr was codeposited with Zn at higher current densities in both polyethyleneglycol(PEG)-free and PEG- containing baths. However, PEG made it possible to reduce Cr+ to the metallic state and Cr existed in the form of Cr(III) hydroxide in the deposits obtained from PEG-free bath. The measurements of the partial polarization curve of Zn and the pH in the cathode layer revealed that PEG acted as a polarizer to shift the cathode potential to the reduction potential of the composited hydroxides of Zn and Cr formed due to the pH rise in the cathode layer.1. IntroductionRecently, much attention has been paid to the electrodeposition of Zn-Cr alloys because of its application to the production of super-highly corrosion-resistant alloy plated steel sheets for the next generation1Hl_ Some researches have already tried to commercialize this type of steel sheet. High corrosion-resistance of this steel sheet is brought about by codeposited Cr in the alloys. According to Piontelli's classification5l concerned with metal deposition from aqueous solution, Cr belong; to an inert metal and its deposition is associated with a large amount of hydrogen evolution. Therefore the current efficiency for Cr deposition is extremely poor. It has been also reported that Cr is unable to codeposit in the electrodeposited Zn film in the absence of a certain additive in the solution. 0-compounds group colloids7l, ether group organic compounds8), 9>, peptide based compounds10l, etc., have been found to be effective additives to induce the codeposition of Cr with Zn. However, few studies have been made on the codeposition mechanism of Cr with Zn. In this research, the fundamental electrodeposition behavior of Zn-Cr alloys from sulfate baths was investigated to clarify the codeposition mechanism."

Jan 1, 1998