By Qingyu Deng, Shiwei Ma, Guibao Qiu, Hua Wang

"The flow behavior of the blast furnace slag bearing titanium, like viscosity, play an importance role during the iron-making process with the vanadium-titanium magnetite, which is a very special minerals in Panzhihua, China. The dependency of the viscosity on the chemical composition like TiO2, Al2O3, MgO, binary basicity (CaO/SiO2), temperature, reaction time were studied. The experiments showed that the viscosity decreased with the increase of TiO2, MgO content and binary basicity, and it increased with the increase of Al2O3 content and temperature. The viscosity showed a slight decrease within 60mins’ reaction with graphite crucible, however, it increased rapidly afterwards with the formation of Ti(C, N).IntroductionThe ordinary iron ore has been an essential part of raw materials for vanadium-titanium magnetite smelting in Panzhihua to avoid a series of problems, such as slag thickening, adhesive bond of slag and hot metal, etc. The ratio of vanadium-titanium magnetite has been decreased gradually since 1970s, and has down to about 65% now. However, with the substantial appreciation of price of imported ordinary iron ore, Panzhihua Iron and Steel Group aims to increase the ratio of vanadium-titanium magnetite and decrease the dependence on ordinary iron ore in order to lower the cost of smelting process."

Jan 1, 2012

By F. D. S. Marquis

An investigation of the mechanisms of formation of two types of porosity-primary and secondary-their characterization, evolution during processing, and effects on the mechanical behavior (fracture, fatigue, and failure) of 7X50 and 2X24 alloys has been conducted. The mechanisms of formation of three forms of primary or cast porosity were investigated, and each form was characterized: (a) macroscopic shrinkage porosity-MSP); (b) microscopic interdendritic porosity (MIP); and (c) hydrogen gas porosity (HGP) or primary hydrogen porosity (PHP). The mechanisms of formation of four forms of secondary or thermal/thermomechanical porosity were investigated, and each form of porosity was characterized: (a) high temperature oxidation (HTO). internal hydrogen precipitation (IHP), or secondary hydrogen precipitation (SHP); (b) preheating blistering porosity (PBP); (c) eutectic melting porosity (EMP);and, (d) dissolution micro void formation (DMF). The evolution and interactions of the primary and secondary types of porosity (w.ith special emphasis on PHP and SHP) during industrial and laboratory processing and their effects on the fracture and failure behavior of both types of alloys (with special focus on fatigue crack initiation and propagation) were investigated.

Jan 1, 1996

By Y. Ono

In lightweight metal processing such as aluminum (AI) and magnesium (Mg), metal cleanliness is a crucial process parameter for refining, part manufacturing and recycling in order to obtain high quality parts and products. In this paper, techniques for cleanliness evaluation of molten AI and Mg using ultrasonic probes with clad steel buffer rods having high signal-to-noise ratio (SNR) are presented. Due to the high SNR of the ultrasonic probes used, backscattered ultrasonic signals from inclusions, which may be oxide films and/or particles, in molten Mg and those from silicon carbide particles, having an average size of 50f.Ull, added in molten AI are successfully detected with reflection configurations of pulse-echo and/or pitch-catch modes at an ultrasonic frequency of 10 MHz. In addition, relative cleanliness evaluation of molten Al and Mg is demonstrated. In order to establish the procedure and to investigate the optimum system configurations for cleanliness evaluation of molten metals, particle flow simulation system using water and polyvinyl chloride (PVC) particles has been constructed. Counting the number and measuring the size distribution of the PVC particles, having an average diameter of 128um, suspended in water with the PVC volume concentrations of 5ppm and 10ppm are performed with ultrasonic pitch-catch mode. The counted numbers of particles by the presented method and system have good agreement with the calculated results with a count error of less than 10% or two counts. Based on the results obtained with water simulation experiments, the prototype system for cleanliness evaluation of molten Mg by counting and sizing inclusions has been developed. Keywords: Ultrasound, Clad buffer rod, Molten metal, Aluminum, Magnesium, Inclusion detection, Cleanliness measurement, Counting, Sizing

Jan 1, 2003

By B. Mishra

Several reactive metal purification processes using molten salts generate effluent from which significant quantities of metal can be recovered prior to discardinglrecycling the salt. A Salt-scrub [SS] process has been applied where the reactive metals are recovered as a metal-gallium alloy by calciothermic reduction of the metal compounds. The SS alloy compositions were produced by mixing, pressing and sintering the metal-powders. Measurement of metal recovery has been studied for cerium, silver, tin and lead. The process has been optimized for variables such as the metal quantity per kg of effluent salt, amount of excess calcium over stoichiometry, stirring rate and time and holding time at reduction temperature. Over ninety-seven percent metal recovery has been obtained under optimized conditions. The development of an alloy for efficient Salt Scrub processing reduces a major contaminated waste disposal problem as well as recovering the valuable reactive metal. Surrogate metals have been used in this work to study the behavior of plutonium.

Jan 1, 1994

By M. Waladan

The top submerged lancing Sirosmelt system has been developed through laborator.y scale testwork and pilot plant trials for recovery of zinc from ISF slag. The effects of the process variables of gas injection rate, method of coal feeding, and temperature on zinc fuming rates were studied in the laboratory. It was found that the rate of zinc elimination was dependent on all of these variabl.es. The rate of zinc removal from slag was independent of zinc content of slag down to approximately 1.5% Zn, below which the rate was proportional to zinc content in slag. Pilot plant trials were carried out to evaluate a proposed process and results followed predictions from the laboratory scale tests. A comparison of the proposed process with conventional slag fuming operations is made and it is shown that the process has a number of advantages which have a significant impact on the economics of zinc slag fuming.

Jan 1, 1990

By J. E. Dutrizac

A mineralogical study of a weak acid leach residue from the Clarksville zinc plant of Savage Zinc Inc. was carried out. The study focused on Pb and Cd as these elements most significantly impact on the environmentally acceptable disposal of the residue. The residue consists of major amounts of bassanite, zinc ferrite and various Zn-Pb-Fe-Cd silicate species. Also present are lesser quantities of PbSO4, sphalerite, Fe2O3 quartz, Mn-Pb-Fe oxides, SrS04, (Pb,Sr)SO4 iron gel-silica gel, jarosite and Ti oxide. The principal Cd carriers are the zinc ferrite, which contains up to 9.00% Cd and likely accounts for -45% of the total Cd content of the residue, and the various silicate species which contain up to 6.97% Cd and account for about 45 % of the total Cd. The sphalerite is a minor Cd carrier containing an average of 0.35 % Cd and accounting for -5 % of the total Cd; the other carriers contribute only trace amounts to the total Cd content. The major Pb carriers are PbS04, Pb-bearing silicates and Mn-Pb-Fe oxides. Minor proportions of the total 1.09% Pb content of the residue are carried by SrS04 and (pb,Sr)S04' Trace Ph carriers include the iron gel-silica gel, Fe-Zn-AI oxide and bassanite. The residue after the toxicity characteristic leaching procedure (TCLP) is mineralogically very similar to the initial weak acid leach residue; the amounts of calcium sulphate are approximately the same in the two products. The principal Cd and Pb carriers are also the same as those noted in the initial residue, except that some dissolution and reprecipitation of Pb-Sr sulphate takes place. That the residue fails the TCLP test is likely a consequence of the superficial dissolution of Pb and Cd from species such as PbS04 or Zn-Pb-Fe-Cd silicate.

Jan 1, 1995

By J. M. Skeaff

As much as 100% of the gold and 67% of the silver in a sulphur-bearing hydrometallurgical leach residue have been transferred to copper metal at copper smelting temperatures by dissolving the partially calcined residue in an iron-bearing slag maintained in equilibrium with the liquid copper metal and matte phases. The precious metals can then be recovered by conventional refining techniques. Copper can be recycled at least four times without any detrimental effects on gold and silver transfers and recoveries. Apparent copper recovery in the .process can be over 100% because of the copper content of the residue. Based on slag analys.es, the overal1 recovery of gold in the copper metal and matte phases varies from 94% to 100% under all conditions investigated. On the? same basis, silver recovery varies .from 9S% ?to 99% under optimum conditions, but is only 4S% to 73% under other, less attractive conditions. Unaccounted for silver losses of' about 30% make it difficult to determine the major factors affecting ?silver transfer and recovery. A method for implementing the technology on a commercial scale at a Canadian copper/zinc smelter has been proposed. A preliminary economic assessment and comparison of the proposed pyrometallurgical process with conventional cyanidation indicates that either process is economically attractive for recovering gold and silver from leach residues. Although the capital costs are higher, the pyrometallurgical process is simpler, has higher recoveries, lower operating costs and no .potential environmental problems related to cyanide disposal.

Jan 1, 1989

By Mark H. Hashiguchi

Examination of tensile bar surfaces shortly after destructive testing was conducted to search for clues that would aid in optimization of mechanical properties, especially tensile strength, yield strength and elongation to fracture. Cu-Ni-Si-Cr alloy bars in the as-cast, forged, rolled and extruded conditions were examined. Low ductility bars (<4% Elongation) showed dramatically different features than the fracture surfaces of high strength - high ductility bars (7 to 10% Elongation). Analysis of the fracture surfaces at 15X to 2000X and use of Energy-Dispersive X-Ray Spectroscopy (EDS) identified Ni-Si and Ni-Si-Cr precipitates of varying sizes and morphologies. Thermo-mechanical processing techniques to control the size and distribution of these precipitates show promise in improving the properties and performance of this alloy system and appear to correlate with improvements in the fracture surface morphology.

Jan 1, 2008

By J. J. Kim

In a study of buildup in a green-feed reverberatory furnace, it was determined that approximately half of the crucible area has a moderate buildup of 25 in. or less, and that the area extending 45 f t from the burner end of the furnace has only a slight buildup. The false bottom, averaging 6 in. in thickness, was found to cover the entire crucible area. The stratification of Cr2O3, A12O3, and SiO2 occurs throughout the slag layer; this phenomenon is the principal reason for the formation of the false bottom in the green-feed reverberatory furnace. The false bottom is caused primarily by the settling of FeO*(A1,Cr),03 aggregates, which are derived mainly from returned converter slag. The false bottom can be transformed to a solid permanent buildup in the furnace, particularly when the matte is completely withdrawn. From the material balance of Al2O3 and Cr2O3 around the furnace, It is estimated that the average rate of aluminum chromite accumulation is approximately 0.3 ton per day or less.

Jan 1, 1976

By T. T. Chen

Raw anode slimes consisting primarily of PbSO4, AgCuSe, Cu3Se2, Cu2-x Se, Cu2O, CuSO4.5H2O, Sn arsenate and Sb-Bi-As oxide are batch-leached with electrolyte-O2 to dissolve Cu. During this process, Cu2O and CuSO4.5H2O are solubilized and the Cu in the selenides is leached with the formation of Ag2Se and Se. A small amount of Cu remains in the Ag2Se, Sn arsenate and Sb-Bi-As oxide. The decopperized slimes are repulped in Na2CO3 solution to convert most of the PbSO4 to NaPb2(CO3)2(OH). The Sn arsenate and Sb-Bi-As oxide partly react, but the Ag2Se is not significantly affected by the Na2CO3 solution. The NaPb2(CO3)2(OH) intermediate phase is dissolved in acetic acid to leave a final product consisting of Ag2Se, Se, Sn arsenate and Sb-Bi-As oxide, together with small amounts of PbSO4, NaPb2(CO3)2(OH) and various gangue constituents.

Jan 1, 1993

By William Petruk

The mineralogy of the primary and oxidized ores from the Malanjkhand porphyry copper deposit in India was studied to determine ore characteristics that affect metallurgy, and to assess applicable processes for recovering the copper. Three mineral assemblages were found. One occurs in primary ore, another in moderately oxidized ore, and a thir:d in intensely oxidized ore. Chalcopyrite, the main mineral in the primary ore, is relatively coarse-grained, with grain size increasing as the ore grade increases. High chalcopyrite liberations should be achieved at a relatively coarse grind, and good chalcopyrite recoveries should be obtained. The chalcopyrite, however, tarnishes readily and oXidizes to chalcocite in a relatively short time (several months). The presence of both the tarnished chalcopyrite and chalcocite may affect chalcopyrite flotation and reduce copper recoveries, The moderately oxidized ore occurs in an oxidized cap immediately above the primary ore, and stockpiled primary ore alters quickly to a moderately oxidized ore. Chalcocite is a major copper-bearing mineral in moderately OXidized ore. The concentrator processing this ore should be capable of handling a chalcocite-rich ore. The intensely OXidized ore contains a wide variety of acid-soluble copper-bearing minerals. Leaching may be required to recover the copper from them.

Jan 1, 1987

By A. H. Rhoades

The modern polarizing microscope with such accessories as cameras, infrared devices, reflectance and/or transmission photometers, indention hardness, and heating stage is used to characterize coal, coke, and other carbon forms. It allows characterization of coke by-products, such as tars and pitches and their insoluble residues. A useful product of the microscopic approach is the coal petrographic analysis which permits the prediction of coke strength carbonization pressure and volume change. Carbonization tests are expensive, time-consuming and require large amounts of coal. Tests on the coke show it to be strong or weak but give no indication of why. Petrographic analysis requires grams of coal and yields data that indicates why the coal produces coke of a given quality. Small samples from drill cores are sufficient for petrographic analysis. These data are also used to optimize blends for coke production. When coke-plant problems occur, ~he microscope can be used to check the coal blend proportions, as well as for weathered coal. Microscopy is useful in spore correlation work which may be a prerequisite to sound coal reserve estimates. Dispersed vitrinoid reflectance studies are used to determine the degree of organic metamorphism which serves to establish oil and gas deadlines. Tars and pitches are examined microscopically for the amount of normal solids as well as the size of undesirable carry-over solids resulting from pollution abatement practices in coke works. The microscope is also used to study coals for gasification and liquefaction.

Jan 1, 1981

By Batric Pesic

The interactions of mineral-pyrite with T. ferrooxidans were studied by using a cyclic voltametry technique. The interactions with bacteria were carefully examined during the entire growth stage of bacteria (fermentation). Several very important discoveries were made. For example, the pyrite surface invariably drastically changed its properties at the second day of fermentation. Beyond two days of fermentation, the cyclic voltamograms were insensitive to convective diffusion produced by stirring. The SEM study revealed that bacteria populated the pyrite surface at an extremely high density levels. The high density of bacteria, and the solid reaction products formed on the pyrite surface created conditions for pore diffusion which explained why the CVs became insensitive to convective diffusion in solution (stirring).

Jan 1, 1990

By Saeid Pournaderi, Ahmet Geveci, Ender Keskinkilic, Yavuz A. Topkaya

There are mainly three commercial nickel laterites in Turkey: Gordes, Caldag and Sivrihisar. The first two appear in Western Anatolia. The third one, Sivrihisar (Yunusemre) laterites have been found in the first decade of the millennium, in the Central Anatolia region of Turkey. Since then, mining facilities have been continued in Yunusemre. Calcination, prereduction and smelting of Sivrihisar laterites have been extensively studied and published. In the current work, some results of the studies related to characterization of Sivrihisar laterites will be presented.

Jan 1, 2016

By Chunyang Guan, Jilai Xue, Jun Zhu, Qiaochu Liu

"Al-Sc Alloys have showed many advanced properties for a wide range of industrial application, which is usually produced using thermal reduction process. This work is aimed to develop an electrochemical process to make Al-Sc alloy using industrial Hall aluminum reduction cells. The experiments have been carried out in a lab cell where NaF/AlF3-Al2O3-LiF as electrolyte, Sc2O3 as raw material, and liquid aluminum as cathode were used at operating temperature of 950 °C. The resulting Al contained 0.2 - 0.5 wt.% Sc that is the common range in its content for advanced applications. However, a small fraction of Sc was found from thermal reduction at Al melts interface. SEM-EDS and ICP-AES analysis showed a uniformed distribution of Sc at varying locations of the Al-Sc alloy sample. In addition, a higher Sc content in Al-Sc alloy can be obtained with introducing ultrasound through the cathode than that without it.IntroductionIn recent years, scandium has been investigated as an alloying element for aluminum alloys. With addition of a small amount of Sc, Al alloys can improve the strength, weld ability, resistance to re-crystallization and corrosion resistance [1-3]. Due to their advanced properties and potential applications, the demand for Al-Sc alloys will increase in the future. However, the difficulties in reduction technologies and the high costs in production process may limit their expansion in application areas.The current major method of producing Al-Sc alloys is to mix Sc into Al by melting Al-Sc master alloy. This alloying process has several technical problems, such as easy segregating and heavy burning loss, etc. The price of Sc metal or starting material is also high, so the mixing process is an expensive alloying method. Molten salt electrolysis is alternative method to prepare RE metal and RE alloys [4, 5]. It also can reduce the segregation of alloying elements. Sc2O3 is an ideal material as raw material with low price and decomposition voltage. Some work has proved that Al-Sc alloys can be obtained by electrolysis Sc2O3 directly in cryolite [6-8], or CaCl2 molten salt [9]."

Jan 1, 2012

By S. Ozbilen

"Al-Li binary alloys with nominal Li contents of0.15, 1.1and2.8 (in wt%) were aged naturally at room temperature for two months, aged at low temperatures ( 65 and 1 OOEC) for up to 2 months and aged artificially at 190EC for 4 days after water quenching to 25EC following solutionizing at 530EC for 20 minutes. Ageing behavior of these binary alloys were studied by Vicker's Hardness measurements and DSC thermal analysis. Thermal analysis results indicate the formation of GP zones of Al-Li system in Al-2.8wt%Li binary alloy. In the same alloy, rapid quenching from one phase region (a) gives rise to precipitation of small o' particles in a matrix (a) with still high supersaturation. During ageing of this alloy below lOOEC an additional transformation, i.e., GP zone formation occurs proceeding at a very high rate which is described on the basis of the theoretical analysis for the quenched Al-Li system proposed by Khachaturyan et al [6]. Ageing at temperatures below 11 OEC takes place slowly by the formation of small d' particles of lower thermal stability than the quenched-in d precipitates in addition to GP zones resulting in an increase in hardness compared to water quenched samples. During artificial ageing, GP zones transform by dissolution to d' precipitates while d' particles already in the microstructure coarsen during under aged condition at which hardness increases with time till peak aged condition.IntroductionIn binary Al-Li alloys the d' (Al3Li) fully coherent internally ordered inetastable phase of Li2 structure with a=0.4038d [1-5] forms homogeneously between 120 and 190EC before the formation of stable d' (A!Li) phase and cause the superior mechanical properties. This is due to an appreciable age hardening effect resulting because of the d' precipitation during ageing [1]. The response of d' to decomposition and its formation kinetics have been studied previously and it is believed that the decomposition of the a-supersaturated solid solution occurs in a two stage process; i.e., a 6 d' (Al3Li) 6 d(A!Li). Khachturyan et al [6] theoretically investigated precipitation of the d' phase and gave an interpretation of the transformation paths of the quenched Al-Li alloys. They predict that the disordered supersaturated solid solution congruently orders, and then the uniformly ordered solution decomposes into ordered regions that differ in Li-content. Finally, ordered d' phase forms in the disordered matrix."

Jan 1, 1998

By U. Lauwers

The influence of different waste materials in sinter blends on the quality and mineralogical composition of a sinter is described. As a result of partial preservation of the original textures of waste materials in the final product the degree of assimilation of the original material in the sinter product can be ascertained. Recycling of waste materials such as dolo char , arc-furnace slag, scrap fmes, mill scale and BOF-mud via the sintering process a saving on costs of raw materials such as flux and fuels, and a reduction on pollution can be achieved. A comparison of a typical sinter with a sinter produced through the utilization of waste materials showed a distinct correlation between certain types of waste material and some metallurgical properties. Dolochar in a sinter blend acts as part of the fuel and flux that are normally added to a sinter mix. Generally dolochar improves the quality of the sinter and decreases the consumption of coke. Other waste materials adversely influence the quality of the sinter. The glass and calcium ferrite content of a sinter when dolochar is used in the blend is similar to that of a sinter produced with only coke as a fuel in the sinter mix. The glass content is lower and the calcium ferrite content is higher, in a sinter produced from dolo char in the blend compared to a sinter produced with additions of other waste materials. Changes in the mineralogical composition are related directly to the metallurgical properties of the sinter product.

Jan 1, 1991

By Guy Deschênes

Thiourea solutions can be used as leach liquors to treat gold ores or slimes. It is also efficient to elute resins or strip solvents that were loaded in cyanides solutions. The hydrogen pressure reduction is a practical step to recover gold and silver from leach solutions, and strips and eluates without any destruction of thiourea. It is a critical point because these processes have to consider the recycling of the liquors to be irore economical. The effect of temperature, pressure, acidity, compotation of the solution and the nature of catalysts on pressure reduction by hydrogen were investigated. An electranetallurgical study was? carried out to investigate the mechanism. The composition of the products was studied by different analytical methods. The process shows a good selectivity to precipitate gold and silver in a thiourea solution containing iron and copper. Gold and silver concentrations can be decreased to 0.2 ppm and 0.1 ppm at respectively 70 KPa H2 and 28°C. No decomposition of thiourea was evident during the tests. Metals such as nickel powder or platinum activate the reaction and improve the reduction.

Jan 1, 1989

By Hong Yong Sohn, Miguel Olivas-Martinez

"Different approaches are used for calculating the ‘energy requirement’ of a process. The determination of energy requirement becomes confusing for a process in which a fuel is also a reactant. The key issue is which heat of chemical reaction should be included in the ‘energy requirement’ value. We will use the example of ironmaking processes to illustrate the problem. The different approaches essentially boil down to the question: does one include the combustion heat of the reductant used in the reduction reaction or just the heat of the reduction reaction? Depending on the viewpoint, either approach can be accepted; it is a matter of convention. There is a need, however, to select a standard approach because the absolute value of ‘energy requirement’ of a process depends on the choice. The energy requirement of a novel flash ironmaking process will be compared with that of an average blast furnace operation.IntroductionDifferent approaches are used for performing energy balance calculations and perhaps more significantly in presenting the ‘energy requirement’ of a process. The question becomes more involved for a process in which one or more reactants are also used to generate the process heat by combustion. Often the key issue is which heat of chemical reaction to include in presenting the ‘energy requirement’ of the process.It is worthwhile to note at the outset that the difference in energy requirements between different processes for converting similar raw materials to the same desired product is largely unaffected by the choice of chemical reactions to be included. However, the absolute value presented as the ‘energy requirement’ of a process can be different by a large amount depending on the approach. We use the example of ironmaking processes to illustrate the problem. In these processes, as currently practiced or under development, carbon and/or hydrocarbons (including hydrogen) are used as the fuel as well as the reactant for reducing the iron oxide mineral.The different approaches in this case essentially boil down to the following question: does one include the combustion heat of the reductant used in the reduction reaction or treat the reductant portion as just a reactant? Depending on the viewpoint, either approach can be considered acceptable. It is a matter of convention. There is a need, however, to select a standard approach because the absolute value of ‘energy requirement’ of an ironmaking process (e.g., the currently dominant blast furnace process) depends on such a choice. It is particularly important to clearly state the specific approach used when the energy requirement of ironmaking is compared with those of other industrial processes such as petrochemicals production."

Jan 1, 2014

By Wade L. Karlsen

"Revision surgery to replace joints in the human body requires materials that are strong, long-lasting, and biocompatible. Metallic implants made of cobalt-chromium-molybdenum alloys are already popular because of their proven corrosion and wear resistance properties, but there is an on-going effort to economically improve their performance. Alloying with inert nitrogen can enhance the mechanical properties of the alloy, enhance its corrosion resistance, and elevate the temperature at which the metallic implants can be thermally treated, without increasing the threat to the human body. The current work has produced a high-nitrogen Co-Cr-Mo alloy through HIP consolidation of metal powders that have undergone nitriding in a mechanically fluidized bed. The already fine microstructure of the powders combined with the increased nitrogen content resulted in significant property gains in the consolidated materials.IntroductionMetallic implants made of cobalt-chromium-molybdenum alloys are already popular because of their proven corrosion and wear resistance properties, but there is an ongoing effort to improve their performance. Research on a Stellite 21 cobalt-chromiummolybdenum alloy has shown that nitrogen alloying can be desirable from several standpoints [l]. Firstly, it has indicated that nitrogen can enhance the mechanical properties of the alloy, which could allow more demanding implant designs. The same work also demonstrated that nitrogen can elevate the temperature at which the metallic implants can be thermally treated, which is desirable in situations in which surface textures are to be sintered to the implant to enhance its fixation properties. Finally, that research work discovered that, not only does nitrogen not harm the corrosion resistance of the cobalt-chromium-molybdenum alloys, but it may in fact enhance it. Combining this with the fact that small amounts of nitrogen are not considered a threat to the human body, makes nitrogen alloying an attractive alternative for enhancing the properties of Co-Cr-Mo."

Jan 1, 2000