By C. R. Schumacher, W. H. Moyer

Cornwall, Pa. magnetite ore, containing recoverable sulfides in the form of chalcopyrite and pyrite, has been mined continuously since 1742 1 Beneficiation of the ore was begun in 1905, at the Lebanon concentrator located six miles from the mine. At first, only magnetite was recovered, using Grondal magnetic separators. In 1907, copper minerals were recovered by means of Wilfley tables. Copper flotation, attempted as early as 1912, was finally successful in 1919. In 1940, flotation of the cobalt- bearing pyrite was begun, and Cornwall ore became the major domestic source of cobait for many years. In 1916, the Bethlehem Steel Corp. began to purchase interests in the Cornwall mine and Lebanon concentrator properties, and by 1926 had acquired complete ownership. Metallurgical practice at the old Lebanon concentrator was good, but by today's standards the plant was outdated. The flowsheet was complex, due both to the mineral content of the ore and to the low capacities of much of the equipment. As the flowsheet developed, buildings were added and the plant was spread over a relatively large area, with resulting high manpower requirements. Another disadvantage was the six-mile rail haul from the mine to the Lebanon concentrator.

Jan 3, 1966

By Sabert Oglesby, Albert L. Thomas

Until recently, probably the best means of sampling airborne dusts has been the impinger method. Dust-laden air is drawn into a sampling tube, and the particulate matters separated from the air and collected in the liquid in the impinger. A sample of the suspension is prepared on a slide and counted through a projection microscope. This method is simple and reliable, but it does suffer drawbacks. Since the collected particles must be counted visually, results of the dust count are taken. This seriously impedes studying the effectiveness of dust inhibitors, such as water sprays, or making adjustments in equipment. Greatest disadvantage of all, however, is the tedious task of counting particles in the sample. With the growing desirability of taking more samples, the effort involved in making these counts is a real factor in the cost of dust control. Finally, it is generally recognized that impinger dust counts can be related to health hazard only for specific kinds of dust and under similar conditions. This is because the rather complex mechanism of dust damage depends so much on size distribution of the dust. Counts determined by impinger samples cover a limited size range that does not necessarily correlate with retention by the lungs and upper respiratory tract.

Jan 3, 1959

By C. E. Webber

THE economical recovery of the valuable constituents from the effluent of gas-con-densate wells has developed into a problem of balancing the cost of recovery against the cost of compressing the residual gas back into the formation. A possible method of extracting the gasoline and distillate from the natural gas is by oil absorption at high pressures. In order to design and evaluate an absorption plant, fundamental data on the composition of the coexisting hydro-carbon vapor and liquid phases at various temperatures and pressures are essential. A review of the literature indicated that the necessary data for the design of such plants are lacking. The nearest approach to desired published data is that of Katz and Hackmuth,5 who experimentally deter-mined the composition of the coexisting vapor and liquid phases in a natural gas-crude oil system at pressures up to 3000 lb. per sq. in. and at temperatures from 40° to 200°F. This paper presents the results of the experimental determination of the equilib-rium distribution of the hydrocarbons methane through hexane between natural gas and a typical absorber oil. The ranges of temperature and pressure chosen were from 33° to 180°F. and from 100 to 5000 lb. per sq. inch.

Jan 1, 1940

By W. W. Harvey, F. O. Dudas

Toward hot hydrochloric acid, the usual order of reactivities of the common copper sulfide and associated minerals is reversed, and the rates of H2S formation vary as [ ]. The iron component of chalcopyrite and bornite reports to the solution as ferrous chloride, while pyrite remains essentially unreacted. If a pressure of H2S is maintained in the reactor, copper solubilization is suppressed, and the primary copper sulfides are converted to finely divided secondary sulfides (principally covellite). The HCl leach reside then consists mainly of covellite, pyrite and acid-insoluble gangue. Copper can be selectively leached from this upgraded concentrate to yield a clean, strong copper sulfate solution for direct electrowinning. Preliminary analysis indicates competitive economics with respect to established hydrometallurgical processes. Other concentrate treatments based on an initial HC1 leach are proposed and relative advantages compared. The common denominator of the major process routes considered is the requirement to regenerate HC1 from an FeC12 solution. Five distinct concentrate compositions were employed in the experimental study, which included some attention to the fates of selected minor constituents of the copper concentrate, especially gold, silver, molybdenum, arsenic and selenium. Significant mineralogical features of reactants and products are described.

Jan 1, 1978

By Richard A. Busch, Roy L. Soderberg

Large, high, open stopes resulting from vertical crater retreat (VCR) and similar methods are usually filled with sand tailings to support the stope walls and make it possible to mine the pillars. The hydrostatic head resulting from these high stope fills demands extremely heavy bulkheads in the crosscuts to withstand the pres- sure. Occasionally, these bulkheads fail because there are no drains or the installed drains are inadequate. Costly flooding of the mine and loss of life result from these failures. With proper design of blanket drains and filters, the fill can be made failure-proof, requiring only a minimum bulkhead, designed specifically for zero water retention. The effectiveness of the blanket drains can be increased by laying perforated pipes on the bottom of the crosscut within the blanket drain. These drains can have a safety factor of 10 with minimal expense. When the water is properly drained, the hydrostatic pressure on the bulkhead is reduced to zero, leaving only the lateral pressure of the sand. This lateral pressure is partially dissipated by arching and shear against the crosscut walls and consolidation of the tailings as the water is drained. The bulkhead should be placed at least one cross-cut diameter back from the collar of the drawpoint.

Jan 1, 1983

By Hans Lundberg

IN ORDER to comprehend the help and information that may be expected from electrical prospecting, it is necessary to have at least a general knowledge of the methods and principles involved in preparing and interpreting results obtained in the field. Electrical prospecting is rather complicated, both in theory and practice, and in order to make a brief description clear to the practical mining man it has been necessary to idealize and generalize the problems, at the risk of having such simplification criticized by the theoretical man. This simplification must not be misinterpreted as showing a lack of theoretical knowledge. FIG. 1.-FLOW OF CURRENT IN AND AROUND A CONDUCTING BODY. For its operation, electrical prospecting mainly depends on the fact that most metallic ores conduct an electric current much more readily than barren rocks. If an electric current flows through a block of ground within which a body of chalcopyrite is enclosed in country rock of schist, the current will find less resistance to its passage through the chalcopyrite than through the schist, even though the passage through the latter be much shorter. This is because the longer path through the chalcopyrite offers less resistance, owing to the superior electrical conductivity of the chalcopyrite (Fig. 1).

Jan 1, 1928

By Edward Perry

IN the exploration of a copper deposit by drilling, obvious advantages are to be gained from a distinction between primary and secondary ore.1 Perhaps the chief of these is the aid which such a distinction renders in determining where a given hole should stop. The copper assay, often a sufficient guide, cannot always be exclusively relied upon. Primary ores may extend downward indefinitely and may fluctuate in value independently of depth: if primary ores are consistently lean for a considerable vertical distance, there is little reason to expect that, still deeper, they will increase to the commercial grade; on the other hand, rich primary ores may persist uninterruptedly downward or may come in again below a lean interval. Secondary ores, however, have a comparatively limited vertical extent; in a large way enrichment decreases with depth and finally gives out. It follows then, that when a hole descends from profitable ore into ore of less than the commercial minimum, the practical significance of the situation depends upon whether this decrease results from a decrease in secondary enrichment or is a variation in primary content: if the copper of the ore passed through has been chiefly secondary, little is gained in the average case by extending the hole much below the point at which the commercial limit is reached; but, when copper is chiefly primary, due weight must be given to the possibility that, still deeper, the ore may again improve.

Jan 2, 1916

By Leonard Larson

DURING several years immediately preceding the adoption of wet-charge smelting at McGill, various necessary conditions affecting this procedure, such as plant rearrangement and the metallurgical nature of the concentrate produced at the concentrator, were fully considered. Wet-charge smelting is not altogether novel to the recently recon-structed smelter at McGill. A number of years prior to this improve-ment, when flotation methods were initiated at the concentrator, large tonnages of wet and (at that time) sticky flotation concentrate were charged directly into the reverberatory furnaces, because of the difficulty in handling the entire tonnage in the roasters. The plant had excess reverberatory units and this surplus furnace capacity was utilized to smelt raw flotation concentrate. During the years 1927 and 1928, a number of actual operating furnace test runs were made to determine in principle the feasibility of wet-smelt-ing operation. Results were encouraging, and in November 1932 the roasting plant was shut clown. For some time thereafter the wet feed was delivered directly to the reverberatory side-charging calcine hoppers already in place. Feeding the wet material through the old calcine hoppers and charge holes into the furnace involved considerable labor, but under the conditions existing at that time it was desirable to continue wet smelting even under the handicap of this laborious procedure. The smelting plant during this period was on a curtailed production basis, operating only about 15 days per month. The alternate starting up and shutting clown of the roasting plant presented a difficult problem and charging the wet material directly to the furnace entirely eliminated this difficulty. The roasting plant was never operated thereafter.

Jan 1, 1938

By N. E. Bonn

IT is well known that most of the materials entering into the manufacture of thermocouples are subject to variations in their thermoelectric characteristics, the chief causes of which are: differences in chemical composition; the previous .history, which includes mechanical working, ageing, oxidation, and contamination; and mode of use, such as depth of immersion, etc. In the case of a very extensively use thermoelement, the iron-constantan couple, neither iron nor constantan are absolutely uniform, and a number of checks are made during the process of manufacture. As both are subject to diversion from a standard value, neither, can be used for checking the other. It is, therefore, necessary to find a third metal against, which iron and constantan maybe checked. It was to find such a metal; that the present investigation was undertaken. To be a reliable, checking standard, the metal must possess a fairly high melting point? it must be obtainable in sufficient purity, and it must be uniform and constant with respect to its thermoelectric qualities. The choice is, as a result, limited to a few metals, such as copper, gold, and silver. Copper has the advantage of low cost, which makes it possible to use each wire only once and thus avoid any variations due to continued use, although previous investigators have found1 that continued use does not affect the calibration of a copper-constantan thermocouple. Copper also has the advantage of a large thermal electromotive force against constantan and would be desirable as a checking standard if it could be shown that it possessed the proper thermoelectric characteristics. The investigation, accordingly, resolved itself into three phases: the uniformity of commercial electrolytic copper, the effect of aging and method of annealing, and the calibration of the copper-constantan thermocouple.

Jan 9, 1919

J. S. UNGER,*Pittsburgh, Pit., (written discussion?).-From the subject of the paper it is natural to expect that the data presented must be results secured from an open-hearth furnace working under normal conditions, but such is not the case, as the conclusions are based on the results of laboratory tests, which do not approach service conditions. The early basic hearths were made of burnt lime, then followed burnt dolomite, bricks made of calcined dolomite and a 'binder, usually tar, and finally magnesite bricks covered with a layer of sintered magnesite. When this material became scarce, special dolomitic refractories were used. In the summary, it is claimed that magnesite low in lime, or of greatest purity, ranks first in the resistance to slaking and to corrosive slags. It is well known that neither pure lime nor magnesia has much value as a refractory. By the addition f fluxes, such as silica and iron oxide, lime is rendered inert to slaking in the same way as are the special dolomitic refractories. An example on a large scale is the ordinary basic open-hearth cinder, produced every clay, which does not slake. Pure magnesia, regardless of the lime content, is not any better fitted for a refractory than pure lime. The pure natural varieties, such as Grecian or Washington magnesites, must be burnt with sufficient silica and oxide of iron to produce a satisfactory material. Grain magnesite, either artificial or natural, is, not used in burning in a hearth in the state in which it is received. To make a satisfactory hearth, it must be made more impure by adding about 20 per cent. of basic open-hearth cinder, otherwise it will-not remain in place.

Jan 5, 1919

By J. J. Bodmer

IN 1855, Franz Uchatius patented, in England, his process of manufacturing cast steel. The first experiments, on a practical scale, were made at the Ebbw Vale Iron Works, Monmouthshire. The charge consisted of a mixture of cast iron with about 20 per cent. of a pure iron ore, and with or without other ingredients. In order to obtain the cast iron in a subdivided condition, Uchatius granulated molten pig-metal by running it into water, which during the operation was kept well agitated, and found that "the finer the iron is granulated, the softer will be the resulting steel." The writer is not aware that granulated iron has been used practically, otherwise than in the above-named process ; and until 1866 no other process of subdividing iron than by granulation was known. In April, 1866, an English patent was obtained by the writer for subdividing blast-furnace and other slags and metals in a molten condition, by passing the same through one or more pairs of rolls. In reference to iron the idea was, in following up the direction pointed out by the Uchatius process, to obtain better results in the puddling process by means of a thorough amalgamation (not simply a mixture) of the iron with the oxides and other ingredients in the charge itself. Experiments were made. A quantity of iron direct from the blast-furnace was subdivided (or laminated) by passing it through a pair of plain rolls. The rolls were hollow, and water was made to pass through them to keep them sufficiently cool. Without giving differential speed to the rolls, sheets were obtained about one-sixteenth inches thick, and from about one hundred square inches surface, downwards. With differential speed, the iron falls from the rolls in

Jan 1, 1874

By C. P. Watson

It is perhaps significant that a few years ago the sessions held here were chiefly occupied with production. In the last two years these sessions have been concerned with production curtailment, unitization and conservation, notwithstanding that production in the United States in 1929 reached a total in excess of 1,000,000,000 barrels. A study of the leading producing units in the United States shows that Oklahoma, Texas and California in 1929 yielded 84 per cent. of the total production from 33.5 per cent. of the total number of producing wells. Production in the United States in 1929 showed an increase of 107,000,000 bbl. over the 1928 figures. This increase in itself perhaps is not enough to have caused the serious situation that is now confronting the industry. However, taking into account the gradual encroachment on the consumption of fuel oil through the greater utilization of natural gas, probably we have reached the point in the United States where prices will determine to a large extent,' in 1930, the amount that will be produced. In the states of Texas, Oklahoma and California, the most significant developmcnt of 1929 has been the desire of operators to reach some agreement to bring production more or less in control with the estimated demand. In November, production in California, particularly in the Santa Fe Springs field, was drastically cut to meet a certain requirement. Similarly, in Texas, the Yates field has been developed and has been producing under an agreement on the part of the operators; and more recently in Oklahoma City, serious efforts have been made to keep produetion in line with consumption. For the year 1930 we can see nothing in sight except drastic curtailment. This is a matter that I am sure is occupying the attention of all the leaders of the industry.

Jan 1, 1930

By Leonard Larson

DURING several years immediately preceding the adoption of wet-charge smelting at McGill, various necessary conditions affecting this procedure, such as plant rearrangement and the metallurgical nature of the concentrate produced at the concentrator, were fully considered. Wet-charge smelting is not altogether novel to the recently reconstructed smelter at McGill. A number of years prior to this improvement, when flotation methods were initiated at the concentrator, large tonnages of wet and (at that time) sticky flotation concentrate were charged directly into the reverberatory furnaces, because of the difficulty in handling the entire tonnage in the roasters. The plant had excess reverberatory units and this surplus furnace capacity was utilized to smelt raw flotation concentrate. During the years 1927 and 1928, a number of actual operating furnace test runs were made to determine in principle the feasibility of wet-smelting operation. Results were encouraging, and in November 1932 the roasting plant was shut down. For some time thereafter the wet feed was delivered directly to the reverberatory side-charging calcine hoppers already in place. Feeding the wet material through the old calcine hoppers and charge holes into the furnace involved considerable labor, but under the conditions existing at that time it was desirable to continue wet smelting even under the handicap of this laborious procedure. The smelting plant during this period was on a curtailed production basis, operating only about 15 days per month. The alternate starting up and shutting down of the roasting plant presented a difficult problem and charging the wet material directly to the furnace entirely eliminated this difficulty. The roasting plant was never operated thereafter. EARLY PROCEDURE Fig. 1 shows the general layout of the smelting plant before the smelter was remodeled. Under this arrangement, all concentrates and fluxes except converter flux were delivered in cars to wooden storage bins, which paralleled the roaster building. The material to be roasted was dis-

Jan 1, 1938

By Alfred E. Hunt

The technical papers of the last few years give numerous in stances of serious failures by cracking or rupture of soft steel boiler plates, marly of which have satisfactorily passed the rigid inspection and tests required by both Lloyds' Register and the Board of Trade in England. I speak of the inspecting department of Lloyds' and the Board of Trade, for we do not begin to have as systematic and intelligent work regularly done in this country as is done by these institutions in England. Tension-tests of this steel have given from 65,000 to 65,000 pounds per square inch tensile strength, with from 20 to 30 per cent. elongation in 8 inches. Chemical analyses have shown the steel to contain from 0.12 to 0.15 per cent. carbon, from 0.25 to 0.40 per cent. manganese, and from 0.03 to 0.05 per cent. phosphorus. All of these tests are considered normal, and, in the words of one of our members, " boiler-plates with these qualities ought not to fail." There are, however, several causes of failure in soft steel plates which, although the writer does not presume to ascribe to then], or either of them, any particular instance, are still dangerous, and ought to be guarded against much more carefully than in usual present practice. These causes are: 1. The hardening property of all steel. 2. Insufficient work from the ingot to the finished plates. 3. Temporary fiber in certain steels. 4. Internal strains caused by unequal work upon the material. Hardening.-The writer, in a paper read before the Institute in October, 1883," made the statement that soft .steel, no matter how low in carbon, would harden to a certain extent upon being heated red-hot and plunged into water, and that it hardened more when plunged into brine and less when quenched in oil, and gave the results of one experiment, merely as an illustration of many which had all confirmed the statement made. The illustration was a heat of open-hearth steel made by the . writer, of 0.15 per cent. carbon and 0.29 per cent. of manganese, which gave (he following results upon test-pieces from the same 1/4-thick plate.

Jan 1, 1886

By N. G. W. Cook

At present, tunnels can be driven in rock by either of two essentially different techniques, in one of which rock-breaking is accomplished by drilling and blasting and in the other by mechanical loading. The methods based on these techniques are comparable in terms of the rates at which tunnels may be advanced, although they differ widely in their range of applicability to different types of rock and lengths of tunnel. The method based on drilling and blasting has reached a high degree of development. It is applicable to even the hardest rocks and rates of advance in excess of 50 ft per day (fpd) are attainable. The main disadvantages of this method are that it involves a sequence of operations punctuated by blasting and that it is relatively uncontrolled, resulting in overbreaking the tunnel profile and damage to the surrounding rock. However, its flexibility, mobility, and low capital cost constitute real advantages in many situations, such as those involving short lengths of tunnel or low rates of advance. Tunneling machines based on mechanical breaking of the rock are a more recent development. They offer a continuous and controlled means of tunneling capable of rates of advance in excess of 100 fpd under favorable conditions. However, these machines weigh many tens of tons and consume several hundred horsepower, so that they are costly and lack mobility. At present, their applicability is limited to long tunnels in relatively soft rock where the high rates of advance and tunnel quality can offset their onerous capital cost. Many situations exist in which the superior quality of a machined tunnel and freedom from blasting would be real advantages, but where the rock is either too hard for existing machines or the length of the tunnel does not justify their capital cost: What are the possibilities of developing cheaper, more flexible, and mobile tunneling machines? Most existing tunneling machines fragment all the rock at the tunnel face to facilitate its disposal. If a machine were used to cut only the profile of a tunnel as one of a sequence of operations, it would be required to break

Jan 1, 1970

Jan 1, 1940

Jan 1, 1940

Jan 1, 1932

By A. Taylor, S. Leber

WHEN studies of deformation texture, lattice stress, and crystal orientation are made, it is frequently required to know the interplanar angles and subsequently to embody the results of the investigation in a stereographic projection. Tables of

Jan 1, 1955

By I. R. M. Chatson

Radial layout's guiding principle is the grouping under one roof of the operating processes which require continuous supervision. Separate treatment sections are isolated by outside stockpiles fed with radiating conveyors. Hence the name "radial" layout. Many plants are designed with "linear" layout where successive operating stages are dotted like beads along a string of conveyors.

Jan 11, 1978