REPORT OF PRESIDENT C. F. RAND FOR THE YEAR 1917 The noteworthy occurrences during 1917 were the creation of Engineering Council; the completion of the addition to the Engineering Societies Building. and the occupation by the American Society of Civil engineers of the space thus provided for it; the addition of 67,000 vol-

Jan 3, 1918

By J. F. Myers, F. M. Lewis

This second progress report of grinding presents comments regarding ball consumption and data pertaining to the hydroscillator, which is closed circuited with the tricone mill. A study and postulate of how balls function is presented. The paper summarizes cost reduction obtained by the method of "grinding for the tail race" rather than for "mesh tons."

Jan 11, 1950

By M. J. Miller

In modern mill design, a stockpile storage system for raw and/or semiprocessed ore has become almost indispensable. This paper discusses the benefits of such stockpile storage as well as the available types of belt conveyor stockpiling units. Alternative reclaiming arrangements for stockpiles are reviewed, and the advantages and disadvantages of each arrangement are discussed.

Jan 1, 1982

The ten-year "supply-demand relationship" tables in this chapter for various mineral and metal commodities have been adapted from Minerals in the U.S. Economy, compiled by the Bureau of Mines, U.S. Department of the Interior, published in 1975. Acknowledgment is made to the Bureau of Mines for compilation of the tables. [ ]

Jan 1, 1976

By Frederick F. Frick

SPONGE iron as produced at Anaconda is a fine, -35 mesh, impure product, about 50 pct metallic iron, obtained from the reduction of iron calcine at a temperature of 1850°F by use of coke resulting from slack coal. The metallic iron particles are bulky and spongey and precipitate copper readily and rapidly from a copper sulphate solution. Investigation of the treatment of Greater Butte Project, Kelley, ore at Anaconda early showed the desirability of using sponge iron as a precipitant for the copper in solution resulting from desliming of the ore in a dilute sulphuric acid solution. Anaconda had done considerable work on the production of sponge iron in 1914 for use as a precipitant of copper from leach solutions. Some success and considerable experilence were attained at the time. indicating that, sponge iron might be successfully made by a modification of the process used in 1914, a batch process in which an iron calcine was reduced by means of soft coke, resulting from noncoking coal, in a Bruckner-type revolving horizontal cylindrical furnace widely used 50 years ago. The coke and calcide formed the bed in the Bruckner furnace, which was rotated at about 1 rpm. The bed was brought to a temperature of about 1800°F by means of an oil flame over the surface. Although results were reasonably satisfactory, they did not warrant full development of the process at that time. A good deal of work has been done in the last 50 years on the production of sponge iron. The objective in some cases has been the production of a precipitant for copper from solution, but the bulk of the work has been done for the production of open-hearth steel furnace stock. The production of an open-hearth stock presents two problems rather than one: first, producticon of the sponge iron, and second, what is perhaps of equal difficulty and importance, conversion of the sponge iron into a form suitable for use in the open-hearth furnace. So far as is known to the writer, none of the sponge iron processes tried in the past have proved to be economically feasible. However, Anaconda had a combination of conditions appearing to justify an attempt to produce sponge iron which would serve for the leach-precipitation-float process. It was thought that the process used in 1914, if changed to a continuous one, might work out satisfactorily. The following favorable conditions at Anaconda justified the investigation: 1—A sufficient tonnage of good grade iron calcine resulting from the roasting of a pyrite concentrate in one of the acid plants, at substantially no cost. 2—Reasonably cheap natural gas. 3-—The fact that there was no need for production of a high grade product. 4— The fact that there was no need for obtaining a consistently high reduction of' the iron in calcine. A small revolving Bruckner-type furnace about 2 ft ID by 4 ft long was set up for early pilot work at the research building. This pilot furnace showed that a satisfactory product could be obtained at reasonable cost. It also indicated a marked advantage in preceding the reduction furnace with a furnace of similar size and capacity for preheating and roasting out any residual sulphur from the feed. The small furnace was operated for several months, various details of the process were worked out. and sponge iron was produced to supply a pilot LPF plant which treated 300 lb of Kelley ore pel- hr. Later a second pilot furnace 5 ft in diam and 12 ft long inside was set up at our reverberatory furnace building. This furnace confirmed the data of the small furnace and gave a basis for design of the final plant. At Anaconda a pyrite concentrate, running about 48 pct S, is recovered from copper concentrator tailings by flotation. This concentrate is roasted to sulphur of 3 pct or less at the Chamber acid plant. The iron calcine contains about 57 pct Fe and 18 pct insoluble. The iron calcine feed, as mentioned before, is re-roasted and preheated in a reroast furnace preceding the reduction furnace. Both are of the Bruckner type. The reroasted calcine is fed into the reduction furnace at 800" to 1000°F along with 30 pct slack coal. In the feed end of the furnace the volatile is burned from the slack, giving a soft coke which readily serves for reduction of the iron. Hard metallurgical coke will not serve the purpose. since it does not reduce CO readily at a temperature of 1850°F. All indications are that the actual reduction of the iron is accomplished by carbon monoxide below the surface of the bed, which is 30 in. deep at its center. Apparently there is a constant interchange: Fe²O³ + 3CO = 2Fe - 3CO², CO² + C = 2CO Actually iron oxide is reduced by CO at somewhat lower temperature than the 1850 °F used in the process. but this temperature is necessary to obtain a satisfactory rate of furnace production. The furnace atmosphere is generally reducing, and typical blue carbon monoxide flames satisfactorily cover the bed. Gas flames from four 3-in. Denver Fire Clay Inspirator burners are played directly on the bed, which is slowly cascaded by the 1 rpm of the furnace. An excess of coke is necessary to assure maintenance of good reducing conditions in the furnace bed. Part of this coke is recovered for re-use.

Jan 1, 1954

By D. S. Flett, D. W. West

The solvent extraction of chromium 111 has been studied for the system Cr 111, H,SO., H,O/RNH/RNH., xylene, where the primary amine used was Primene JMT. Rate studies have shown that extremely long equilibrium times are required, ranging from 1 hr at 80°C to 20 days at room temperature. Heating the solution prior to extraction increases the rate of extraction. The variation in the amount of Cr 111 extracted is an inverse function of the acidity of the aqueous phase. Thus, the slow rates of extraction appear to be connected with the hydrolysis of the Cr I11 species. Extraction isotherms for the extraction of Cr 111 have been obtained for two sets of experimental conditions, namely at 60°C and for a heat-treated solution cooled to room temperature. The separation of Fe 111 from Cr 111 and Cr 111 from Cu 11 in sulfate solution by extraction with Primene JMT has been studied and shown to be feasible. A survey of the literature relating to the solvent extraction of chromium showed that, although many systems exist for extraction of Cr VI, only a very few reagents have been found to extract Cr 111. The extraction of Cr III by di-(2-ethyl hexyl) phosphoric acid has been reported by Kimura.' A straight-line dependence of slope —2 was observed between log D,, and the log mineral acid concentration at constant extractant concentration. Since the slope of this plot reflects the charge on the ion extracted, it must be concluded that a hydrolyzed species of Cr III is being extracted. Carboxylic acids generally do not form extractable complexes with Cr III but di-isopropyl salicylic acie does extract Cr 111. Simple acid backwashing of the organic phase, however, failed to remove the chromium. Similar difficulty in backwashing was found by Hellwege and Schweitzer8 in the extraction of Cr I11 with acetyl-acetone in chloroform. The extraction of Cr 111 from chloride solutions by alkyl amines has been reported4-' but the maximum amount of extraction achieved in these studies did not exceed 10%: From sulfate solutions, however, Ishimori" has shown that appreciable amounts of Cr I11 were extracted by amines. The amines used were tri-iso-octyl amine, Amberlite LA-1 (a secondary amine, Rohm & Haas) and Primene JMT (primary amine, Rohm & Haas). The efficiency of extraction with regard to amine type was primary>secondary> tertiary. Appreciable extraction of Cr I11 was recorded for Primene JMT as the aqueous phase acidity tended to zero. The major difficulty with Cr I11 in solvent extraction systems stems from the nonlabile nature of the ion in complex formation. This accounts for the slow rate of extraction generally experienced and the difficulty encountered in backwashing the Cr I11 from the organic phase in the case of liquid cation exchangers. Consequently, the possibility of extraction of Cr I11 as a complex anion is attractive since the backwashing problems should be minimized in this way. From published data, it appeared that the extraction of chromium from sulfate solutions of low acidity by primary amines afforded the best chance of success for a useful solvent extraction system for Cr iii This paper presents the results of a study of the extraction of Cr I11 from sulfate solution by Primene JMT and examines the application of such an extraction procedure for the recovery of chromium from liquors containing iron and copper. Experimental Chromium solutions were prepared from chrome alum in sulfuric acid and sodium sulfate so as to maintain a constant concentration of sulfate ion of 1.5 molar. Solutions of Primene JMT were prepared in xylene and the amine equilibrated with sulfuric acid/sodium sul-fate solutions, of the same acidity as the chromium solution, until there was no change in acidity between the initial and final aqueous phases. The solutions of Primene JMT conditioned in this way were then used for the equilibration experiments. Equilibrations at 25°C were carried out in stoppered conical flasks shaken in a thermostat; equilibrations at all other temperatures were carried out in stirred flasks in a thermostat. After equilibration, the phases were separated and analyzed for chromium. In the tests on the rate of extraction, small samples of equal volume of both phases were withdrawn from time to time and the chromium distribution determined. The chromium analyses were carried out either coloi-imetrically using diphenyl carbazide, or volu-metrically using addition of excess standard ferrous ammonium sulfate and back titration of the excess iron with potassium dichromate. The oxidation of Cr 111 to Cr VI in the case of the raffinate solution was effected by boiling with potassium persulfate in the presence of silver nitrate and, for the backwash solution, by boiling with sodium hydroxide and hydrogen peroxide. Results Preliminary experiments indicated that extraction results were effected by the age of the chromium solution, higher distribution coefficients being obtained with solutions which had been allowed to stand for some time. Consequently a stock solution of chrome alum, 10 m moles per 1 Cr I11 in 1.4 M Na,SO,/O.l M &SO,,

Jan 1, 1971

By K. E. Barrett

Exxon owns a uranium mill and holds two mining leases in Live Oak County, Texas, about halfway between San Antonio and Corpus Christi. The properties make up the Felder Uranium Operations which was reopened earlier this year. Exxon held an oil, gas, and other minerals lease on the J. C. Felder tract, which was adjacent to a relatively shallow uranium discovery by Susquehanna-Western, Inc. on the Marrs-McLean lease immediately south of the Felder property. Drilling in 1967 and 1968 confirmed the presence of reduced uranium mineralization in the basal sand unit of the Oakville formation on the Felder tract, which formed the major part of the roll-front deposit. In 1969 Exxon and Susquehanna-Western, Inc. entered into a sale and purchase agreement which provided for Susquehanna to mine and process Felder ore and purchase recovered uranium. Susquehanna moved an alkaline-leach mill from Wyoming, erected it on the Ray Point property, and placed it into operation late in 1970. Susquehanna mined and processed ore from the Felder and McLean properties through March 1973. Susquehanna ceased operations in March 1973. Exxon then acquired the mill and mill property. Exxon also purchased the mineral rights to the McLean lease, re-negotiated a mining lease for that property, and carried out shut-down programs for the mining and mill areas in the fall of 1973. The project was put on a standby basis until late 1973, when Exxon initiated mine feasibility studies for the project. MINE PLANNING EVALUATION The feasibility study for reopening the Felder Project began in late 1975 and was not completed until late 1976. I will discuss several areas of the feasibility study that required additional work prior to making the decision to renew operations. Ore Reserves Preparations for estimating the ore reserves began with the re-evaluation of more than 1500 natural radioactivity logs from exploration and pre-development drilling that had been completed on the property. These gamma ray logs of non-core rotary drill holes were the principal source of data used in making the estimate. Chemical assays of cores from the deposit were also used in the reserve determination. Electric resistivity and self-potential logs were made along with the gamma ray log. In December 1975 an additional core drilling project was undertaken to confirm the in-place density and radiometric equilibrium characteristics of the ore deposits. Comparison of chemical assays of cores with the U308 values calculated from the logs showed that the unoxidized ores were in radiometric equilibrium. In contrast, cores from anomalies occurring in near surface, weathered, and oxidized zones were in radiometric disequilibrium. Several important decisions were made in developing a mine plan or schedule of production from the Felder and McLean ore bodies. Disposal of Produced Mine Water: The ore bodies of the Felder Uranium Project occur at a point below the ground water table. The ore zones to be mined must first be dewatered to allow removal of mineralized material. In the open pit operations, this is accomplished by maintaining a perimeter ditch around the periphery of the open pit, allowing the interior of the pit to drain and collect into a sump and be pumped from the mine. In addition to anticipated water production from future mining operations, approximately 200M gallons of water was contained in three open pits left from prior mining operations. In two of these existing pits, the water was to be removed and disposed to allow for planned backfilling of waste material into these pits. The third pit would also have to be drained to allow continued mining of an area left from the prior operations. Essentially no ground water information was available for this area. The only data available was water production history from Susquehanna's mining operation. Two water wells were drilled early in 1976 on the Felder lease for use in obtaining hydrological data. A long term draw-down test was performed by pumping one water well and measuring water level drawdown in both the pumped well and the observation well. From these data, values for permeability and storage coefficient were calculated. These data were then used in modeling the aquifer to allow calculation of water influx into the mining area versus time. Once a schedule of water production, including the stored volume in the existing pits was calculated, alternate solutions for disposal were evaluated. The first system evaluated was a series of deep injection wells. The wells were designed to inject at a depth of approximately 3500 feet. Again very little information concerning reservoir characteristics of the receiving sand units was known. Using assumed values for reservoir permeability and storage coefficients, an injection well system was designed to allow for disposal of produced mine water. The biggest

Jan 1, 1979

By G. P. Conard, R. C. Hall, J. F. Libsch

The 50 pct Fe-50 pct Co alloy undergoes a transformation from disorder to an ordered structure of the CsCl type reportedly in the vicinity of 732OC. During this process, the coercive force goes through a maximum, apparently as a result of strains associated with the coherent nucleation and growth reaction. This magnetic alloy also shows a marked increase in the ratio of residual to saturation induction, which is associated with annealing to a high degree of order with the continuous application of a magnetic field. The increase in ratio can be explained on the basis of a decrease in 90' domain boundaries and, perhaps, by an increase in anisotropy resulting from lattice distortion. THE 50 pct Fe-50 pct Co alloy undergoes a disorder-order transformation which has been reported to occur in the vicinity of 732°C1,2 The ordered structure is the CsCl type.' This magnetic alloy also shows a marked increase in the ratio of residual to saturation induction as a result of heat treatment in a magnetic field, sometimes called a response to magnetic anneal.'-' The purpose of this investigation was to study the course of the ordering reaction, the nature of the response to .heat treatment in a magnetic field, and the relation, if any, between ordering and the response. Procedure The method of approach in this investigation was to produce an initial structure as completely disordered as possible and then gradually to order the alloy by isothermal anneals at various temperatures under different conditions of the applied magnetic field. Magnetic, magnetostriction, and X-ray analyses were of primary importance in determining the property and structural changes resulting from the isothermal anneals. Rings of the 50 pct Fe-50 pct Co alloy were prepared from the elemental powders by a powder metallurgy technique, further details of which may be found in ref. 7. The initial structure was produced by annealing the specimens for ½ hr at 1000°C, cooling to and holding for ½ hr at 900°C (in the a range above the ordering temperature), and water quenching. Isothermal anneals were performed at 600°, 675°, 720°, and 740°C. For example, rings were heated to 600°C, held for a predetermined period of time, and cooled by natural cooling at a rate slightly slower than an air cool (average of 20" to 25°C per min). The tests (magnetic, etc.) were made after each heat treatment. All high temperature treatments were performed in a purified hydrogen atmosphere. The treatments at the various temperatures were carried out under one or more conditions of an applied field including 1—no field, 2—field of 20 oersteds applied on cooling only, and 3—field of 20 oersteds applied continuously during heating, holding, and cooling. Magnetic measurements were made using the standard Rowland ring technique8 with a maximum field strength of 100 oersteds. The magnetization curve, induction at 100 oersteds (B.), residual induction (Bt), and coercive force (Hc) were determined. All magnetic analysis data were based on an average of the results from three rings. A strain gage technique9 as used for the measurement of magnetostriction. The X-ray determination of the relative amount of ordered phase present was made on the ring specimen used for magnetic measurement. This was done by the back-reflection method using a rotating specimen (because of the large grain size) with unfiltered CoKa radiation and a 7 hr exposure time. Intensity measurements of the ordered line (300) were made by comparing visually the films so obtained with standard films prepared by exposing for different lengths of time a specimen given a long time anneal (high degree of order). Results In all instances the saturation induction (induction at 100 oersteds) was found to increase slightly with annealing time. This effect was small and appears to be the increase in saturation induction to be expected on ordering.10-13 The residual induction behavior was markedly influenced by the field condition during annealing, Figs. 1, 2. For the condition of no applied field, the ratio of residual to saturation induction remained essentially constant for short annealing times but showed a significant increase at longer times. With increasing annealing temperature, less time was required to produce this increase in the ratio. In the case of the 600°C anneals, the increase did not occur until approximately 20 hr, Fig. I, while on annealing at 740°C the increase was immediate, Fig. 2. Slight decreases in the ratio may be observed at 100 hr for specimens treated at 720°C and at 1 hr for those treated at 740°C. Specimens annealed in a field of 20 oersteds showed a residual to saturation induction ratio consistently higher than that for the specimens annealed without the field. The first anneal with the field (¼ hr) caused an abrupt increase in the ratio at all temperatures; thereafter, the increase in the ratio was generally similar for specimens annealed

Jan 1, 1956

By Carrol M. Beeson

Reasons are given for using a Boyle's-law porosimeter in conducting core analysis for either routine or research purposes. Among other things, it is pointed out that such a porosimeter permits the measurement of all basic properties on the same sample, thereby eliminating the sources of error inherent in the use of adjacent samples. References are made to investigations of gas adsorption on various porous materials, to show that the use of helium in Boyle's-law porosimeters reduces to negligible proportions the error due to the adsorption or desorption of the operating gas. Two Boyle's-law instruments are described. which permit accurate and rapid measurements of porosity. Schematic sketches and explanation:; are included, along with derivations of equations required in performing precise determinations. Summaries of data obtained during calibration are tabulated and analyses of the data are resented as indications of the precision and accuracy of each device. Comparisons are also shown for measurements made with each of the instruments on the same test pieces and cores. INTRODUCTION An accurate porosimeter, operating on the principle of Boyle's law. is of considerable value in the analysis of cores for either routine or research purposes. This is due primarily to the fact that the measurement of porosity with such an instrument leaves the sample free of contamination by any liquid. When used in conjunction with an extraction apparatus' for determining oil and water saturations, a Boyle's-law porosimeter permits the measurement of all basic properties on the same sample. This eliminates the sources of error inherent in the use of adjacent samples, or the necessity of determining porosity after all other properties have been obtained. Large errors may result from combining measurements made on adjacent samples in order to obtain a single property. This type of error is definitely involved when oil and water are measured with one sample, and the pore vo1ume is measured with an adjacent one. Furthermore, the source of error would be present to some extent, even if the analyst could choose the samples so they were truly adjacent from a geological standpoint. The use of adjacent samples in routine core analysis also necessarily decreases the probability of correlating core properties. For example, the chance of correlating the "irreducible" interstitial-water saturation with permeability, is bound to be greatly reduced by measuring these properties on "adjacent" samples. For research purposes, amplification is scarcely required concerning the greater flexibility of a method for measuring porosity which leaves the core free of contamination by any liquid. Even under those circumstances which require that the core be saturated with a liquid, a previous measurement of porosity with a gas is useful in determining the degree of saturation that has been attained in the process. Furthermore, for comparable accuracy, porosity usually may be determined more rapidly with a gas than with a liquid. This advantage of the Boyle's-law instrument is most outstanding when the determination time is compared with that required in obtaining porosity by evacuation of the core followed by saturation with a liquid of known density. Several porosimeters which operate on the principle of Boyle's law have been described2,3,4,5,6,7 in the literature. No comparison will be attempted between those instruments and the ones described herein. Before helium gas became readily available, Boyle's-law porosimeters were subject to an appreciable error due to the adsorption of the operating gas on the surface of the core solids. There is considerable direct and indirect evidence in the literature to support the contention that the adsorption of helium on porous solids is negligible at room temperature. In discussing the use of Boyle's-law porosimeters, Washburn and Bunting2 stated that "for most ceramic bodies dry air is a satisfactory gas, but hydrogen will be required in some instances. Helium could, of course, be employed for all types of porous materials at room temperatures or above." Howard and Hulett8 obtained evidence that the adsorption of helium was negligible at room temperatures, even on activated carbon ; for the density measured with this gas was unaffected by changes in pressure or by changes in temperature from 25 °C to 75 °C. For oil-well cores, Taliaferro, Johnson, and Dewees" obtained lower porosities with helium than with air, but apparently did not study helium adsorption. From the work of these investigators, it follows that the use of helium in Boyle's-law porosimeters reduces the error due to gas adsorption to negligible proportions. This makes it possible to construct instruments which permit the determination of porosity with (1) a high degree of accuracy, (2) with great rapidity, and (3) without contamination. THE KOBE POROSIMETER The fundamental design of the Kobe Porosimeter was developed by Kobe, Inc., which firm built about 12 of the instruments during 1936 and 1937. Since that time, seven or eight more have been constructed with their permission, making a total of about 20 that have been put into operation.

Jan 1, 1950

By D. E. Coates, G. R. Purdy, S. V. Subramanian

The morphological stability of the planar solid-liquid interface in dilute ternary alloys, undergoing steady-state unidirectional solidification, is analyzed in terms of both the constitutional supercooling principle and the perturbation methods recently developed by Mullins and Sekerka. First, various steady-state solutions for the two solute distributions ahead of a planar interface are examined. The nature of the solutions depends on the size and concentration dependence of the off-diagonal diffusion coefficients. W~thin the framework of the constitutional supercooling principle, a cumulative contribution to instability frorn the two solutes is found to exist in the absence of diffusional interaction. It is shown that the latter can produce a further enhancement of instability or can have a stabilizing influence, depending on the form of the liquidus surface and on the sign of the solute-solute interaction. A perturbation analysis, which ignores diffusional interaction, verifies the cumulative influence of lhe solute fields and demonstrates that the Mullins-Sekerka stability criterion for binary systems (with capillarity accounted for) can be readily extended for application to ternary systems. SOME time ago, Tiller et al.' calculated the solute concentration distribution ahead of the planar solid-liquid interface of binary alloys undergoing steady-state unidirectional solidification. An earlier qualitative proposal that the transition from planar to nonplanar growth morphologies is associated solely with the onset of constitutional supercooling in the liquid layer ahead of the moving interface2 was used in conjunction with this calculation to put the now well-known constitutional supercooling (C-S) stability criterion into quantitative terms. Mullins and Sekerka,3 in a recent and very elegant analysis, established a more complete criterion (hereafter referred to as the M-S criterion). Interfacial stability was investigated by determining the time derivative of the amplitude of a sinusoidal perturbation of infinitesimal amplitude which had been introduced into the originally planar shape of the moving interface. Of particular importance is the fact that capillarity was included in the boundary conditions of their calculation. The purpose of the present paper is to extend all of this earlier work on dilute binary systems for application to dilute ternary alloy solidification. The analysis is divided into three sections. In the first the two solute distributions ahead of a moving planar interface are considered. Mathematical solutions are de- termined for situations in which: a) diffusional interaction is negligible, 6) diffusional interaction must be considered but circumstances permit use of constant diffusion coefficients, and c) the concentration dependence of off-diagonal diffusion coefficients can be described by first-order dilute solution approximations. In the next section, a stability criterion analogous to the C-S criterion is developed and the influence of diffusional interaction on interface stability is analyzed. Finally, the perturbation formalism of Mullins and Sekerka, with capillarity included in the boundary conditions, is extended for analysis of ternary systems in which diffusional interaction is negligible. The study of interface stability in binary systems usually commences with the assumption that the equilibrium distribution coefficient and the slope of the liquidus line are constant at values corresponding to infinite dilution. Similar assumptions have not been introduced into the present treatment; that is, we do not assume planar solidus and liquidus surfaces joined by tie lines which yield constant distribution coefficients. The latter involves the assumption of no ther-modynamic interaction between solute species in both the solid and liquid. We consider a ternary phase diagram for which the solidus and liquidus surfaces are, in general, nonplanar and of course pass through the corresponding binary solidus and liquidus lines. These lines are not assumed to have constant slope. In the dilute regions we are concerned with, the following assumptions are made: i) The solidus and liquidus surfaces are of a form such that both the solidus and liquidus temperatures are monotonically varying functions of each solute concentration. ii) The tie lines are such that the equilibrium distribution coefficient of a given solute is greater than unity for every point on the solidus (or liquidus) surface or it is less than unity for every point. STEADY-STATE SOLUTE DISTRIBUTIONS IN THE LIQUID As will be demonstrated in the next section, a knowledge of the steady-state solute profiles is not a necessary prerequisite for the formulation of a ternary C-S stability criterion. However, in that details, such as the complete description of the equilibrium liquidus temperature profile, require an evaluation of the solute distributions, the overall treatment is enhanced if these distributions are determined. Consider a ternary system (solvent plus solutes 1 and 2) for which a planar solid-liquid interface is in unidirectional motion at constant velocity V. At this stage it is unnecessary to limit ourselves to dilute solutions. For a stationary frame of reference the generalized forms of Fick's equations are:

Jan 1, 1969

By A. S. Nowick, C. Y. Li

It is deMonstrated that quenching from an elevated temperataupe accelerates the grain boundary relaxation in two solid solutions (aAg-Zn and a Cu-Al). This result is consistent with the proposal that, in solid solutions, grain boundary relaxation occurs by a mechanism of' self diffusion. Nevertheless, an alternative possibilitg, that quenching introduces vacancies into the boundary itself, must also be considered. THE phcnomenon of grain boundary relaxation has been well known for many years,1,2 yet the mechanism of this process is very poorly understood. One of the most interesting suggestions which relates to the mechanism of grain boundary relaxation was that of Ke,3 who claimed that the activation energy for grain boundary relaxation and for lattice self diffusion were essentially the same. The implication is therefore that the elementary step in the two processes is the same. This suggestion is particularly startling in view of the fact that activation energy for self diffusion along a grain boundary is very significantly lower than that for volume self-diffusion. Later evidence5-7 showed that there really are two grain boundary peaks, one which appears in high-purity metals, and the other (which develops at a higher temperature than the first) which appears in solid solutions beginning at solute concentrations in the range of 0.1 pct. Data for silver6 show that Kg's hypothesis is surely incorrect for the grain boundary peak in the high-purity metal, since it has an activation energy of only 22 kcal per mole, but that the hypothesis may still be correct for the grain boundary peak in various silver solid solutions, for which activation energies in the range 40 to 50 kcal per mole are observed. If the elementary step in the grain boundary relaxation process were the same as that for self-diffusion, it would be expected that the relaxation process could be hastened by quenching, 2.c. by introducing a non-equilibrium excess of lattice vacancies. Such a quenching effect has already been demonstrated in the case of another anelastic relaxation process, viz., the Zener relaxation effect. The Zener effect, which occurs in essentially all solid solutions, may be attributed to the reorientation of pairs of solute atoms in the presence of an applied shear stress,' and therefore must take place by means of a volume diffusion mechanism. The hastening of this process through quenching9 has been one way of demonstrating that atom movements in the lattice take place through a defect mechanism, presumably single vacancies. In order to see if the grain boundary relaxation is affected by quenching, it is particularly convenient to compare the grain boundary relaxation with the Zener effect, by choosing a specimen for which both relaxation effects appear. Specifically, a fine-grained sample of a solid solution shows in the curve of internal friction vs temperature, first a peak due to the Zener effect, then a second rise (and eventually a peak at substantially higher temperatures) due to the grain boundary relaxation. The same phenomena are also observable in static anelastic measurements, such as creep at very low stress levels. Thus, for the same fine-grained solid solution, the creepstrain, when plotted against log time, falls on a sigmodial curve with a sharp inflection point, due to the Zener effect, which is followed by a second rise and inflection resulting from the grain boundary relaxation. To look for a quenching effect, static measurements are preferable to the dynamic internal friction measurements, due to the fact that quenching effects tend to anneal out too rapidly at the temperatures at which the internal friction is measured.9 RESULTS AND DISCUSSION Creep experiments in torsion were carried out in an apparatus similar to that described by Ke1, whereby a wire is held under constant torque and its angular displacement is observed as a function of time. The alloy Ag-30 at. pct Znwas selected because of the large Zener relaxation that it displays. The two samples used were a "coarse grained" wire with a mean grain size about twice the diameter of the wire (diam = 0.032 in.), and a "fine-grained" wire which had several grains across the diameter. In Fig. 1 a comparison is made of the creep curves at 160°C of these two samples after they had been cooled slowly from 400°C. Curve A, which represents the coarsegrained sample, shows a unique relaxation process due to the Zener relaxation, with a relaxation time, T , in the vicinity of 100 sec. Curve B, which represents the behavior of the fine-grained sample, on the other hand, shows first the same relaxation process as that in A, followed by a turning up of the curve which corresponds to the onset of a second overlap-

Jan 1, 1962

By C. E. Armantrout, J. A. Rowland, D. F. Walsh

THE close-packed-hexagonal structure of mag-J- nesium is converted to a ductile and malleable body-centered-cubic lattice by the addition of lithium in excess of 10 pct. Further, the density of magnesium or magnesium-base alloys is decreased by additions of lithium. The practical possibilities of such alloys as a basis for uniquely light, malleable, and ductile structural materials were pointed out by Dean in 1944' and by Hume-Rothery in 1945.2 It was apparent to these investigators, however, that more complex compositions would be required if strengths sufficient for structural applications were to be developed in these alloys. In a search for strengthening additions, various investigators w have examined a number of the ternary and more complex alloys containing magnesium and lithium. An investigation of the fundamental characteristics of these alloys was undertaken by the Bureau of Mines. The investigation was initiated with a study of the magnesium-rich corner of the equilibrium diagram for the ternary system, Mg-Li-Al. The following data from published investigations of Mg-Li-A1 alloys were available: 1—a description of isothermal sections at 20" and 400°C through the Mg-Li-A1 constitution diagram by F. I. Shamrai;' 2—a diagram by P. D. Frost et al." showing approximate phase relationships at 700°F for a number of the Mg-Li-A1 alloys; and 3—diagrams showing the constitution at 500" and 700°F for the Mg-Li-A1 alloy system published by A. Jones et al.' Where compositions and temperatures permit comparison, these diagrams show disagreement. The 700°F isotherms of Frost and Jones differ only in the placement of the phase boundaries. But Sham-rai's 400°C (752°F) isotherm shows a variation in phases as well as in phase boundaries. Although rigid comparison of these different isothermal sections might not be justifiable, it seems impossible to reconcile Shamrai's construction with the isotherms of Frost or Jones. The isothermal sections presented in this paper were prepared to determine compositions which might be suitable for age hardening and to develop the general slope and placement of the various phase boundaries in the magnesium-rich corner of the diagram. Sections at 375", 200°, and 100°C were selected for investigation. In constructing these sections, the solubility of aluminum in magnesium, as reported by W. L. Fink and L. A. Willey Vn 1948, was used at the binary Mg-A1 boundary and the solubility of lithium in magnesium was obtained from the equilibrium diagram for that system as reported by G. F. Sager and B. J. Nelson" in the same year. The solubility of magnesium in lithium was determined experimentally and conforms in general to data reported by P. Saldau and F. Shamrai." Parameters for AlLi and MgI7A1, were taken from American Society for Testing Materials X-ray diffraction data cards. Experimental Procedures Although the isothermal sections presented in this paper are not unusually complex, the experimental techniques involved in their construction are made extremely difficult by the relatively high vapor pressure of lithium and the great chemical activity of both magnesium and lithium. Because of these characteristics, which make precise control of the composition of equilibrium-treated filings practically impossible, the disappearing phase method was used in preference to the parametric method in conjunction with metallographic studies. The alloys used in this investigation were melted and cast in an atmosphere of helium using a tilting-type furnace which enclosed a steel crucible and mold in a single unit. Each portion of the charge (500 to 600 g) was cleaned carefully just before placing it in the crucible; and the charge, crucible, and entire melting apparatus were evacuated and then washed with grade A helium while preheating to approximately 100°C. The alloys were melted and chill cast in an atmosphere of helium. Alloys prepared in this way were relatively free from inclusions and a fluxing treatment was considered unnecessary. The cylindrical ingots obtained were scalped and then reduced 96 pct in area by direct extrusion, yielding % in. diam rod. Sections of the rod, approximately 3 in. long, were given equilibrium heat treatments and then sampled for metallographic examination, X-ray diffraction study, and chemical analysis. The surface of each equilibrium-treated rod was machined to a depth sufficient to insure removal of contaminated material before samples for chemical analysis or X-ray diffraction study were obtained, and all decisions on microstructure were based on the examination of the central portion of the metallographic specimen. All specimens homogenized at 375°C were analyzed after this equilibrium heat treatment. When the composition of an alloy placed it in a critical area of the 200" or 100°C isothermal section, a check chemical analysis was made on a sample taken from the alloy specimen as-heat-treated at the particular temperature. Standard chemical procedures of gravimetric analysis were used in the determination of magnesium and aluminum; lithium, potassium, and sodium were determined by flame photometer methods

Jan 1, 1956

By Robert D. Pehlke, Robert G. Blossey

The solubility of nitrogen in liquid binary and ternary Fe-Ni-Co alloys has been measured by the Sieverts' method between 1550°and 1700°C. Solubility data and standard free energzes and enthalpies of solution for nitrogen in the alloys are presented. Interaction parameters are discussed and presented for binary and ternary alloys. MOST of the studies of nitrogen solubility in liquid metals have been directed toward the dilute alloys of iron. Several of these investigations have included measurements of the nitrogen solubility in Fe-Ni al10s'- and in Fe-Co alloys.435 There has been some work, however, that has extended across the e-i-" and F-CO" binaries. This investigation was undertaken to determine the nitrogen solubility in both binary and ternary alloys of the Fe-Ni-Co system. It was also hoped that the differences between earlier studies might be resolved. EXPERIMENTAL METHOD This investigation was made using a Sieverts' apparatus described previously." The nickel (99.85 pct) and cobalt (99.9 pct) were obtained from Sherritt-Gordon Mines, Ltd., and the iron (99.95 pct) was Fer-rovac-E obtained from Crucible Steel Co. Recrystal-lized alumina crucibles were used throughout the entire investigation with no evidence of crucible-melt reaction. Melt temperatures were measured with an optical pyrometer and the temperature scale calibrated against the melting points of the three pure metals. The emissivity of the melt was assumed to be a linear function of composition for all alloys, as has been shown for Fe-Ni alloys.lZ The emissivity of the pure metals at 1600°C were taken as 0.43 for iron, 0.44 for cobalt, and 0.45 for nickel. Using these emissivities, the trans mis sivity of the system was found to be 0.51 i 0.01. The Sieverts' method was used for this study and followed the procedures outlined previously.l' The individual metals were weighed to give about 100 g of alloy. The alloys were melted in the crucible under a partial pressure of argon. The system was evacuated, and the "hot volume" was measured with argon. To avoid the errors caused by vaporization, the melt was held under vacuum only long enough to ensure that all of the gas in the system had been removed. The influence of any small amount of vaporization on the "hot volume" was shown to be negligible by measuring the "hot volume" after a run. This measurement agreed with that made at the start of the run within the implicit error, 0.2 cc, caused by the limitations in accurately reading the buret. The solubility-pressure relationship was measured in the pure metals and in several alloy compositions throughout the ternary system. These measurements were made by admitting measured amounts of nitrogen to the system, and then determining the equilibrium nitrogen pressure above the melt. This method has the distinct advantage of higher accuracy, particularly at lower pressures, than measurements made by withdrawing gas from the system to reduce the pressure after determining the solubility at 1 atm nitrogen pressure. This latter method has a practical lower limit of about 0.4 atm where an increased error is encountered because the buret must be emptied to permit further measurements at lower pressures. By determining the relation between apparent solubility and pressure, it was possible to make a good estimate of the initial nitrogen content of the metal from the intercept of the solubility curve extrapolated to zero pressure.11 DISCUSSION The solubility data corrected to 1 atm nitrogen pressure are summarized in Table I. The reported solubility has been corrected for the initial nitrogen content of the alloys. The initial nitrogen contents fell between 0.0002 and 0.0010 wt pct, and were lower in the iron and nickel than in the cobalt. Sieverts' law was obeyed in all alloys at pressures up to 1 atm. Examples of this behavior are shown in Fig. 1. The reaction for solution of nitrogen is Taking the standard state as 1 wt pct N in the alloy and the reference state as nitrogen at infinite dilution in the alloy, and noting the adherence to Sieverts' law, K becomes the solubility of nitrogen in the alloy at 1 atm pressure. Thus the solubility data of Table I were used directly to calculate the standard free energy for the solution reaction. These results are also presented in Table I. The enthalpy of solution is also summarized in Table I as calculated from a form of the van't Hoff relation: Iron-Nickel System. The data for the solubility of nitrogen in liquid Fe-Ni binary alloys is presented in Fig. 2 along the with data of aito, Schenck et al.,' and Humbert and 1liott.l' The data for studies of nitrogen solubility in Fe-Ni alloys containing less than 20 pc t i'- are not presented in Fig. 2, although they are in good agreement with the present work. The results of this study are in good agreement with Schenck

Jan 1, 1967

By D. T. Peterson, T. Carnahan

The diffusion coejTicients of carbon, nitrogen, and oxyget were determined in $ thorium over the tempernilcre range 1440" io 1715°C. The diffusion coyfiicir?zls are given by: D = 0.022 exp (-27,000/RT) jor carbo)~, D = 0,0032 exp(-l7,00Q/RTj for nitrogen, and D = u.0013 expt(-11,UOU/RT) for oxygen. Cavl~orz was found to increase the hardness of thoriunz nearly linearly with concentration over the range 100 to 1000Ppm carbon. ThORIUM has a fcc structure up to 1365°C and a bcc structure from this temperature to its melting point at 1740°C. Diffusion of carbon, oxygen, and nitrogen in bcc thorium was of interest in connection with the purification of thorium by electrotransport.' In addition, it was possible to measure the diffusion of all three of these interstitial solutes in the same bcc metal. Only in niobium, tantalum, vanadium, and a iron have all three interstitial diffusion coefficients been measured in a given bcc metal. Diffusion coefficients have been measured for carbon and oxygen in a thorium by Peterson2, 3 and for nitrogen by Gerds and Mallett.4 Activation energies for diffusion are reported by the above authors to be 38 kcal per mole for carbon, 22.5 kcal per mole for nitrogen, and 49 kcal per mole for oxygen. Values of the diffusion coefficients of carbon and nitrogen in 3 thorium have been reported by Peterson et al.' However, these were secondary results of their investigation of electrotransport phenomena in thorium and it was hoped that the present study could provide more precise data. EXPERIMENTAL PROCEDURE The specimens used in this study were the well-known pair of semi-infinite bar type. The couple was formed by resistance butt welding two 0.54-cm-diam by 3.0-cm-long bars of thorium together under pure helium, the concentration of the solute being greater in one cylinder than that in the other. The finished couple then contained a concentration step at the weld interface and diffusion proceeded only along the axis of the rod. The thorium used in this study was prepared by the magnesium intermediate alloy method.5 The total impurity content was less than 400 ppm. The major impurities were: carbon, 100 ppm: nitrogen, 50 ppm; and oxygen. 85 ppm. The total metallic impurity content was less than 150 ppm. The high solute concentration portions of the diffusion couples were prepared by adding the solute to the high-purity thorium in a non-consumable electrode arc melting procedure. Carbon and nitrogen were added in the form of spectroscopic graphite and nitrogen gas while a Tho2 layer was dissolved by arc melting to add oxygen. High-purity thorium formed the low concentration portions in the carbon and nitrogen couples. The low oxygen portions were obtained by deoxidizing high-purity thorium with calcium for 3 weeks at 1000°C according to a method reported by Peterson.3 The high C-Th contained 400 ppm C, the high N-Th contained 400 ppm N, the high 0-Th contained 220 ppm 0, and the low 0-Th contained 25 ppm O. The high O-Th was brine-quenched from 1500°C to retain most of the oxygen in solution at room temperature. These concentration levels were all below the solubility limits in 0 thorium at 1400°C. A resistance-heated high-vacuum furnace was used to heat the couples. The samples were mounted horizontally on a tantalum support which had small grooves near each end. Spacer rods of thorium, 0.4 cm in diam, were placed in these grooves to prevent contact between the sample and the tantalum support. This arrangement should have prevented contamination of the sample by contact with the support. In further effort to reduce contamination, the oxygen diffusion couples were sealed inside evacuated outgassed tantalum cylinders lined with thorium foil. Thorium rings around each end of the samples acted as spacers in this case. Pressure during diffusion runs was about 10-6 torr after an initial outgassing stage. Temperature measurements were made by sighting on black body holes in the sample support adjacent to the samples with a Leeds and Northrup disappearing-filament optical pyrometer. Temperatures were constant during a diffusion anneal to ±5C. The observed temperatures were corrected for sight glass absorption after each diffusion run. The pyrometer was checked against a calibrated electronic optical pyrometer and a calibrated tungsten strip lamp with the electronic pyrometer being taken as the standard. All temperature readings agreed to within ±3C over the temperature range 1450" to 1690°C. Time corrections due to diffusion during heating and cooling were necessary because of the short diffusion times. The diffusion times ranged from 6 min for the oxygen sample run at 1690°C to 90 min for the carbon sample run at 1500°C. A series of temperature vs time plots were made for heating and cooling of the samples to the various diffusion temperatures. This data was then used in a method according to shewmon6 to determine the time corrections. The corrections amounted to

Jan 1, 1970

By Michael Epstein, Daniel E. Rosner

Fume nucleation sufficiently close to vaporizing suvfaces can augment net vaporization rates into cooler environments. Environmental conditions favoring large vaporization rate enhancements are briefly discussed and a previous theoretical treatment of this nucleation phenomenon is generalized to account for the self-regulating effect of condensalion-heat release within the boundary layer. Despite kinetic limitations on homogeneous nucleation, and latent heat release, non-diffusive condensate removal processes appear to make possible large enhancements in steady-state vaporization rates, provided surface temperatures are well below the boiling point. When condensed phases vaporize (or dissolve) into cooler media, the diffusion-limited mass loss rate can be strongly influenced by the process of nucleation/con-densation (or precipitation) within the thermal boundary layer. This condensation process (which typically leads to mists or fumes in the case of evaporation into cooler gases) has the effect of steepening the vapor pressure profiles near the evaporating surface, since the condensation zone acts as a vapor sink. However. the resulting enhancement in the diffusion-limited evaporation rate can be estimated (as first done by Turkdogan1 for the case of molten iron/nickel alloys evaporating into helium) only if one has independent knowledge of the critical supersaturation, sCrit(T), required to homogeneously nucleate the vapor.* In a recent reformulation and generalization of the theoretical model of Ref. 1 it has been shown that, when log sCrit is approximately linear in reciprocal temperature, rather simple expressions can be derived4 for the ratio of the actual rate of vaporization j" to either the minimum (no condensation) rate j"min, or the maximum (equilibrium condensation) rate j"max In the present communication we wish to briefly report on further developments and implications of the formulation of Ref. 4, with emphasis on i) environmental conditions favoring large enhancements in vaporization rate, and ii) the self-regulatory influence of condensation heat release (neglected in Refs. 1 to 4) on predicted vaporization rates. Additionally, we take this opportunity to correct several misprints appear- ing in Ref. 4, and comment on Elenbaas's recent criticism5 of Ref. 1. MAXIMUM POSSIBLE VAPORIZATION RATE IN PRESENCE OF CONDENSATION A nonequilibrium theory is of interest because of the very large difference between the minimum (no condensation) and maximum (equilibrium condensation) vaporization rate. The magnitude of this maximum possible enhancement can be shown quite clearly by combining a result of Refs. 3 and 4 with the fact that for most liquids there is a simple relationship between the molar heat of evaporation, A, and its boiling point, i.e., A/(RTBp) = C, where the constant C, often called the Trouton ratio, takes on values not very different from 11.* More generally, for any substance (including The Trouton ratio (which for water is 13, for methane, 10, and so forth) will be recognized as the ratio of the molar entropy change upon vaporization (at TBP or Ttransf) to the unlversal gas constant R. Its near constancy reflects the fact that the change in atomic order upon vaporization depends only weakly on the kinds of molecules involved. those that sublime under ordinary conditions) we can define a characteristic transformation temperature. Ttransf, by a relation of the form Ttransf =A/(CR), and then examine the maximum possible evaporation rates as a function of how far removed from Ttransf are the surface temperature, Tw, and ambient temperature, T. Subject to the assumptions: 1) equilibrium vapor pressure, pv,eq, everywhere small compared to prevailing total pressure, p, and 2) negligible effect of condensation heat on temperature profile, the maximum enhancement ratio was found (Eq. [17], Ref. 4) to be: where, for most vapors, Nu/NuD (the ratio of heat transfer coefficient to mass transfer coefficient for the same configuration) is a number near unity.* Ex- *An alternative derivation of the Nu = NuD special case of this equation. revealing its validity for arbitrary velocity/temperature profiles in a laminar boundary layer, is given in Ref. 3. amining this result for a "Trouton substance", one obtains the results shown in Fig. 1, constructed for C = 11. Since we are concerned with vaporization enhancements (j'max/J"min > 1) at surface temperatures below Ttransf, this area of interest is shown unshaded. One notes that at a fixed ambient temperature (hence, T/TtranSf) there is a unique surface temperature, 2T , at which j"max/j"min attains its peak value; moreover, the peak enhancement ratio, see dashed locus. Fig. 1, is: (NuA/NuD)(C/4)(Ttransf/T,). Hence, if Nu = NuD, when the ambient temperature is less than 1/4 of TtranSf the peak enhancement exceeds the Trouton

Jan 1, 1969

By E. W. Filer, L. S. Darker

ONE of the primary purposes of this investigation was to determine how far blast-furnace metal and slag depart from equilibrium, particularly with respect to sulphur distribution. In studying the equilibrium between blast-furnace metal and slag, there are two approaches that can be used. One method is to use synthetic slags, as was done by Hatch and Chipman;' the other is to equilibrate the metal and slag from the blast furnace by remelting in the laboratory. In the set of experiments here reported, metal and slag tapped simultaneously from the same blast furnace were used for all the runs. The experiments were divided into two groups: 1—a time series at each of three different temperatures to determine the t.ime required for metal and slag to equilibrate in various respects under the experimental conditions of remelting, and 2—an addition series to determine the effect of additions to the slag on the equilibrium between the metal and slag. An atmosphere of carbon monoxide was used to simulate blastfurnace conditions. The furnace used for this investigation was a vertically mounted tubular Globar type with two concentric porcelain tubes inside the heating element. The control couple was located between the two porcelain tubes. The carbon monoxide atmosphere was introduced through a mercury seal at the bottom of the inner tube. On top, a glass head (with ground joint) provided access for samples and a long outlet tube prevented air from sucking back into the furnace. The charge used was iron 6 g, slag 5 g for the time series, or iron 9 g, slag 7 % g for the addition series. This slag-to-metal ratio of 0.83 approximates the average for blast-furnace practice, which commonly ranges from about 0.6 to 1.1. A crucible of AUC graphite containing the above charge was suspended by a molybdenum wire in the head and, after flush, was lowered to the center of the furnace as shown in Fig. 1. The cylindrical crucible was 2 in. long x % in. OD. The furnace was held within &3"C of the desired temperature for all the runs. The temperature was checked after the end of each run by flushing the inner tube with air and placing a platinum-platinum-10 pct rhodium thermocouple in the position previously occupied by the crucible; the temperature of the majority of the runs was much closer than the deviation specified above. The couple was checked against a standard couple which had been calibrated at the gold and palladium points, and against a Bureau of Standards couple. The carbon monoxide atmosphere was prepared by passing COz over granular graphite at about 1200°C. It was purified by bubbling through a 30 pct aqueous solution of potassium hydroxide and passing through ascarite and phosphorus pentoxide. The train and connections were all glass except for a few butt joints where rubber tubing was used for flexibility. The rate of gas flow was 25 to 40 cc per min. As atmospheric pressure prevailed in the furnace, the pressure of carbon monoxide was only slightly higher than the partial pressure thereof in the bosh and hearth zones of a blast furnace—by virtue of the elevated total pressure therein. Simultaneous samples of blast-furnace metal and slag were taken for these remelting experiments. The composition of each is given in the first line of Table I. There is considerable uncertainty as to the significant temperature in a blast furnace at which to compare experimental results. This uncertainty arises not only from lack of temperature measurements in the furnace, but also from lack of knowledge of the zone where the slag-metal reactions occur. (Do they occur principally at the slag-metal interface in the crucible, or as the metal is descending through the slag, or even higher as slag and metal are splashing over the coke?) The known temperatures are those of the metal at cast, which averages about 2600°F, and of the cast or flush slag, which is usually about 100°F hotter. To bridge this uncertainty, remelting temperatures were chosen as 1400°, 1500" (2732°F), and 1600°C. For the time series the duration of remelt was 1, 2, 4, 8, 17, or 66 hr; crucible and contents were quenched in brine. The addition series were quenched by rapidly transferring the crucible and contents from the furnace to a close-fitting copper "mold." Of incidental interest here is the fact that the slag wet the crucible

Jan 1, 1953

By D. Atkinson, C. Bodsworth, I. M. Davidson

A geometric model of interstitial solid solutions, which has been used previously as a basis for the prediction of carbon activities in Fe-C austenite, is shown to serve also for the calculation of nitrogen activities in Fe-N austenite. The model has been developed to enable predictions to be made of the activities of an interstitial element in the presence of two host atom species. The activities calculated via the model are shown to be in satisfactory agreement with the measured values in the austenite phase for carbon in Fe-C-Co, Fe-C-Cr, Fe-C-Ni, Fe-C-~n, Fe-C-Si, and Fe-C-V alloys and for nitrogen in Fe-N-Ni alloys. The effect of the second substitu-tional solute on the logarithm of the activity of the interstitial element is expressed as the product of a constant mad the atomic concentration of that solute. The constants so derived we related to the thermo-dynamic interaction coefficients which describe the effect on the activity coefficient of carbon of an added solute element. In recent years the thermodynamic activities of carbon and nitrogen in the single-phase austenite field have been determined for iron binary alloys and for several iron-base ternary alloys. In order to extend the use of these measurements, it is desirable to be able to predict with reasonable accuracy the activities of the interstitials at compositions and temperatures other than those which have been measured experimentally. In all the systems studied to date, the interstitial elements do not conform to ideal behavior. Hence, the available data cannot be extrapolated or interpolated using the simple thermodynamic concepts of solutions. Several models have, therefore, been formulated for the purpose of predicting the activity of an interstitial element in the presence of one species of host atom. These models can be divided into the geometric1"5 and energetic6-' types. The former group is based on the assumption that at low concentrations the activity of the interstitial species is determined by a composition-dependent configurational entropy term and an excess free-energy term which is temperature-dependent but independent of composition. The purpose of this paper is to show that the treatment, based on a geometric model, can be extended to enable predictions to be made of interstitial activities in the presence of two substitutional host atom species. THE CONFIGURATIONAL ENTROPY OF MIXING ICaufman5 has shown that the configurational entropy, S,, for a binary solution comprising of a host atom species, A, and an interstitial species, I, can be expressed as: where NI is the atom fraction of the interstitial species, R is the gas constant, and (2 - 1) is the number of interstitial sites excluded from occupancy by the strain field around each added interstitial atom. The number of interstitial sites per host atom, p, is unityg for the fcc austenite solutions considered here. The configurational entropy of mixing for a ternary solution comprising two substitutional atom species, A and B, and one interstitial species, I, can be derived similarly. Let the number of atoms per mole of each of these species in the solution be represented by «a, ng, and nI. From geometric considerations, it is improbable that the addition of a few atom percent of a second host atom species will change the type of sites (i.e., octahedral) in which the interstitial atom can be accommodated in the austenite lattice. At higher concentrations (determined largely by the relative atomic radii of the atomic species present and any tendency to nonrandom occupancy of the host lattice sites) other types of interstitial sites may become energetically favorable. Restricting consideration to compositions below this limit, for 1 = 1 the number of suitable interstitial sites is given by (n + nB). However, if each interstitial atom excludes from occupancy (Z - 1) additional sites, the total number of sites available for occupation is reduced to (n + ng)/Z. The number of vacant interstitial sites is given by: The total number of recognizable permutations of the atoms must include the recognizable, different configurations of the A and B atoms on the host lattice. Assuming that these arrangements are purely random, and are not affected by the presence of the interstitial species, the total number of recognizable permutations in the ternary alloy is given by: The configurational entropy is obtained by expanding, using Stirling's approximation, and collecting like items, as:

Jan 1, 1969

By D. Mills, G. B. Craig

ZIRCONIUM has been float-zone-refined in an electron-beam furnace and the redistribution of oxygen, iron, and tungsten has been measured. The iodide zirconium used in the present experiments initially contained both oxygen and iron in the range 100 to 200 ppm by weight, and tungsten in amounts less than 10 ppm. Float-zone refining of zirconium, using induction heating, has previously been attempted by Kneip and Betterton1 and Langeron.2 Kneip and Betterton were primarily interested in the removal of iron and nickel. They achieved some purification, with respect to both these elements, in material given up to six passes at 150 mm per hr under an argon atmosphere. Langeron reported purification for a large number of elements after four completed passes in a static vacuum system operating at pressures less than 10-6 mm of Hg and with rates of zone travel between 30 and 40 mm per hr. He did not report oxygen concentrations, but stated that there was inverse segregation of this element. westlake5 has also used a minimum of four zone passes to remove iron from zirconium. No rates or conditions were given. Belk6 has shown that tungsten contamination can occur during electron-beam melting. He reported an increase from 0.01 to 0.05 pct by weight tungsten in molybdenum after four complete zone passes. The vacuum system for the electron-beam unit used in the present investigation consisted of a single-stage rotary pump backing a liquid-air-trapped oil-diffusion pump. A pressure of less than 10-8 mm of Hg was obtained with Dow-Corning 705 fluid in the diffusion pump. In order to avoid contamination of the zirconium by evaporation from the tungsten filament, a special focusing cage4 was employed. Three rates of zone travel, 114, 38, and 4 mm per hr, were investigated, with the liquid zone moving from the bottom to the top of the bar. The bars used were 3 mm diam and the total melted length was 130 mm. Oxygen was analyzed by neutron-activation analysis using a neutron flux of 10' neutrons per sq cm per sec to form the isotope N16 by the 016 (n,p) N16 reaction. The standard deviation is quoted for each oxygen determination. The iron and tungsten analyses were performed spectrographically, and the precision is estimated to be ±6 pct. Analyses for tungsten were all below the detectable limit of 10 ppm, confirming the protection given by the focusing cage. No significant redistribution of oxygen was found at the two higher rates of zone travel. The redistribution of oxygen and iron obtained after five passes at a rate of zone travel of 4 mm per hr (1.1 x 10-4 cm per sec) is recorded in Tables I and 11. Burris, Stockman, and Dillon3 have estimated the distribution of solutes during multipass zone refining. Using their curves for an effective distribution coefficient of Keff = 1.5 and 2 for oxygen and Keff = 0.3 for iron, the expected concentrations were estimated for the present material. These are shown in Tables I and 11, along with the experimentally measured values. The calculated concentrations are based on a molten-zone length of 10 pct of the total melted length, whereas in the present experiments the molten zone was approximately 5 pct of the total melted length. The effect of zone length on solute redistribution is most pronounced after a large number of zone passes. Comparison with Pfann's published data8 for solute redistribution for various Keff's and zone lengths indicates only small differences at low numbers of completed zone passes. It is evident that the expected distribution has not been realized in the case of iron. Scrapings of material deposited on the inner surfaces of the electron-focusing cage were found to be magnetic. It is, therefore, concluded that redistribution of iron is masked by evaporation. Deposition of iron inside the focusing cage was observed at all rates of zone travel. The results of the investigation may be summarized as follows: 1) Segregation of oxygen is typical for a solute with a distribution coefficient, Keff > 1. 2) No redistribution of oxygen takes place at high rates of zone travel. 3) The distribution coefficient for oxygen lies between 1.5 and 2.0. 4) Purification with respect to iron occurs mainly by evaporation. 5) The focusing cage is effective in preventing tungsten contamination.

Jan 1, 1967

By David W. James, Howard Jones, George M. Leak

Conditions are described for producing, by primary recrystallization, a matrix suitable for the growth of large grains near (110)[001] orientation in silicon iron strip by secondary recrystallizaliun in a steep temperature gradient. The orientation distribution of these large grains is expressed in terms of rotational deviations about the cross-rolling direction, the rolling direction, and the normal to the sheet, the deviational spread increasing in that order. With the aid of cowplenientary published data on the orientation dependence of growth rate, it is shown that this observation is consistent with the oriented-growth theory of recrystallization lextures. It is conclutled that growth-rate and orientation-distribution data obtained in a steep thermal gradient should be used with caution to account for isothermally Produced recrystallization textures. SEVERAL authors have reported methods of growing large grains by re crystallization of a small-grained matrix in silicon iron 1- B and pure a cr The present study was a preliminary in the growth of single crystals and bicrystals for surface relaxation," grain boundary mobility, and grain boundary diffusion studies. The method was to control the growth of a seed crystal into a suitable primary re crystallized matrix by feeding through a steep temperature gradient. The driving energy for growth derived from the grain boundary energy released as the seed crystals grew into the matrix. Thus, stability of the matrix against normal grain growth was considered to be essential for success. It was known that the manganese sulfide dispersion present in commercial silicon iron performs this function during secondary recrystallization to the (110)[001.] texture.12 Hence commercial, rather than high-purity, material was used throughout. The paper describes the growth conditions for grains large enough to be used as seed crystals for further growth into single crystals. The orientation distribution of the seed crystals is analyzed and its significance for the theory of recrystallization textures is discussed. EXPERIMENTAL PROCEDURE Strip material was supplied by the Steel Co. of Wales, Ltd. The chemical analysis in weight percent was Si, 2.90; C, 0.015; Mn, 0.059; P, 0.011; S, 0.027; Ni, 0.032; 0, 0.009; Fe, balance. A gradient furnace of similar design to one described previously4 was loaned from B.I.S.R.A. It consisted essentially of a vertical water-cooled copper slot projecting downwards into the hot zone of a molybdenum furnace. Hydrogen was passed through the furnace to protect both heating element and specimen from oxidation. Strip specimens up to 8 cm wide and 0.2 cm thick were sealed into the furnace at the mouth of the copper slot. A coating of light oil on the strip surface maintained the seal during translation of a specimen. The maximum temperature gradient in the region just below the copper slot was 500°C per cm over 1 cm, with the hottest point controlled at 1175°C. Several large grains would usually grow by secondary recrystallization from the primary matrix when a specimen was immersed in the hot zone for about 30 min. A back-reflection X-ray camera was constructed to facilitate rapid and accurate orientation determinations of the large grains produced. It was possible to reproduce a standard geometry, with regard to strip and camera, without the tedium of careful alignment on each occasion. Specimens, typically 4 cm wide and 75 cm long, were cut with the longitudinal axis parallel to the rolling direction of the original strip. The surfaces were cleaned by immersion alternately in a hot aqueous solution containing 2 pct hydrofluoric acid plus 10 pct sulfuric acid and in cold 10 pct nitric acid. The nitric acid etch was just sufficient to reveal the grain structure. Rolling and annealing treatments to prepare the matrix (discussed below) were followed by growth of seed crystals in the gradient furnace. The matrix was transformed to a single crystal by growth of a selected seed crystal connected to the matrix by a thin neck. 4,5 Growth was promoted by controlled feeding into the gradient furnace. Several single crystals of controlled orientation were grown successfully from seed crystals by twisting the interconnecting neck in a reorien-tation jig.4 EXPERIMENTAL RESULTS AND DISCUSSION Growth Conditions. A suitable matrix for growth of large grains was prepared starting from primary re-crystallized strip 1.9 mm thick. This was cold-rolled in two stages each being followed by a recrystallization anneal at 800°C for a few minutes. Such treatment gave the required growth matrix only if the two cold-reduction stages were each performed in several passes and in the following ranges: the first, 30 to 70 pct; the second, 10 to 50 pct. Immersion in the temperature gradient otherwise resulted in an equiaxed

Jan 1, 1967

By A. H. Larson, L. G. Twidwell

The influence which Au, Ag, Sb, Bi, Sn, and Cu have, both individually and collectively, on the activity coefficient of sulfur in liquid lead at 600"C zuas studied by circulating a H2S-Hz gas wlixture over a specific lead alloy until equilibrium was attained. Subsequently, the H2S concentration in the equilibrium gas mixture and sulfur concentration in the condensed phase were deterruined. The elements gold, silver, and antinzony (above 8 at. pct) increased the activity coefficient of sulfur. Bismuth had no apparent effect. Tin (above 3 at. pct) and copper decreased the coefficient. The influence of an individual element, i, on sulfur is best reported as the interaction parameter, riS, which is defined as The values o these first-order interaction zus are: ESzu = —55.0. These interaction parameters are used to predict the activity coefficient of sulfur in six fouv-component alloys and one seven-component alloy. Comparisons are made with direct experimental determinations. INTERACTIONS in dilute solution have been studied by many investigators. Most of the experimental work has been confined to solute-solvent interactions in simple binary systems and solute-solute interactions in ternary systems. Dealy and pehlke"~ have summarized the available literature on activity coefficients at infinite dilution in nonferrous binary alloys and have calculated from published data the values for interaction parameters in dilute nonferrous alloys. Interaction parameters are a convenient means of summarizing the effect of one solute species on another in a given solvent. Only a few investigators have studied interactions of the nonmetallic element sulfur in a metallic solvent. They are as follows: Rosenqvist,~ sulfur in silver; Rosenqvist and Cox,4 sulfur in steel; chipman, sulfur in alloy steels; Alcock and Richardson,% ulfur in copper alloys; Cheng and Alcock,' sulfur in iron, cobalt, and nickel; Cheng and ~lcock,' sulfur in lead and tin. The only reported work on the Pb-S system in the dilute-solution region is that of Cheng and Alcock.' Their investigation involved a study of the solubility of sulfur in liquid lead over the temperature range 500" to 680°C. The results may be summarized by the following relationship: S (dissolved in lead) + Pb(1) = PbS(s) log at. %S = -3388/T + 3.511 Experimentally, it was found that Henry's law was valid up to the solubility limit of sulfur in lead, i.e., at 600°C up to 0.43 pct. Their investigation did not include the study of sulfur in lead alloys. More accurate calculations could be made in smelting and refining systems if activity coefficients of solute species could be accurately predicted in complex solutions. One of the objectives of this study was to compare the experimental data with the values calculated from the equations derived from models for dilute solutions proposed by wagner9 and Alcock and Richardson. A temperature of 600°C was chosen as the experimental temperature to attain reasonable reaction rates and to minimize volatilization of the condensed phase. EXPERIMENTAL Materials. The Pb, Au, Ag, Sb, Bi, Sn, and Cu used for preparation of the alloys were American Smelting and Refining Co. research-grade materials. All were 99.999+ pct purity except the antimony and tin which were 99.99+ pct. The initial alloys prepared for this study consisted of twenty-one binary alloys, eleven ternary alloys, and one six-component alloy. The constituent elements were mixed for each desired alloy and were placed in a crucible machined from spectrographically pure graphite. The crucible was placed in a vycor tube which was evacuated with a vacuum pump and gettered by titanium sponge at 800°C for 8 to 12 hr. After the gettering was completed, the chamber containing the titanium was sealed and removed. The remaining sample chamber was placed in a tube furnace at 800°C for 2 hr and quenched in cold water. The final operation consisted of homogenization of the alloy for 1 to 2 weeks at a temperature just below the solidus for the individual system. The resulting master alloys were sectioned into small pieces and a random choice made for individual equilibrations. Cobalt sulfide (Cogs8) used to control the gas atmosphere in the circulation system was prepared by passing dried HzS for 24 hr over a Co-S mixture heated to 700°C in a tube furnace. This material was then mixed with cobalt metal to give a two-phase mixture which, when heated in hydrogen to a particular temperature, produced a desired H2S/H2 gas atmosphere in the circulation system. A Cu2S-Cu mixture also used in this study was prepared in a comparable manner. Apparatus for Equilibrium Measurements. The experimental technique of this study required apparatus

Jan 1, 1967