By P. Marier, T. R. lngraham

The kinetics of the sulfation of MnO,, MnzO3, and Mn3O4 in SO,, SO3, and O, mixtures was examined and the descending order of sulfation rates at temperatures near 400°C was found to be Mn,O3 > MnO, > Mn3O4. The respective activation energies for the thermal decomposition of MnO, and Mn,O, are 39 and 47 kcal. At 900°C, the thernzal decomposition of MnSO, to MnzO3 is slower than that to Mn3O4. The respective activation energies are 62 and 51 kcal, respectitely. MANGANESE is used to improve the hot workability of steel in the proportions of approximately 13.5 Ib of ferromanganese per ton of steel produced. This requirement accounts for about 95 pct of its large industrial market in North America. The remaining 5 pct is used in the battery and chemical industries. In most North American ores, the percentage of manganese and the manganese-to-iron ratio are not suitable for the direct production of ferromanganese. Hence, most of the North American requirements for manganese are satisfied by importing ore. Typically, many of the studies done on native low-grade manganese resources have been directed toward the production of ore substittes" and the recovery of manganese from open-hearth slags.3 Of the wide variety of processes which have been proposed, the most popular involve compounds in the Mn-S-O system. The thermodynamic properties of manganese and its compounds were reviewed by ah' in 1960 and, more recently, lngrahams discussed the thermodynamics of some of the reactions involved in the Mn-S-O system at normal roasting temperatures. The conditions for producing manganese sulfide during the reduction roasting of manganese sulfate are discussed by Fuller and Edlund.9 A novel scheme was proposed recently by zimmerley7 for utilizing waste sulfur dioxide from stack gases to recover the manganese from ocean-mined manganese nodules. Very little of the work published on manganese compounds has been related to reaction rates. Singleton et 1.' studied the rates of reaction on the MnO-C and Mn7C3-3MnO systems and observed linear and parabolic kinetics respectively in the systems. Tatievskaya et a1.' studied the low-temperature reduction of Mn&, MnO,, and Mn& in HZ and CO, and reported activation energies in the range 1628 kcal. In this paper, the rates of some of the decomposition and formation reactions involving MnSO4, MnOz, MnzO3, and Mn3O4 will be examined after the conditions for the thermodynamic stability of the individual compounds have been designated. CONDITIONS FOR STABILITY OF MnSO4, MnOz, MnZO3, AND Mn3O4 The areas of stability for h'hSO4, MnOz, MnzO3, and h3O4 were established from the data of Mah4 and Ingrahams and are shown in the predominance area diagram,10 logpq- logpsq, in Fig. 1. The diagram is drawn for two temperatures, 700°K, solid lines, and 1100°K, dotted lines. The sketch for the lower temperature includes the conditions likely to prevail in the Zimmerley patent7 when manganese nodules react with sulfur dioxide and that for the higher temperature indicates the conditions for recovering MnzO3 or Mn3O4 from MnSO4 during a roasting reaction. From the fact that the boundary between the areas of stability of MnOz and hSO4 at 700°K is parallel to the abscissa, it is evident that MnOz and SO2 should react together to produce MnSO4, irrespective of the oxygen pressure in the system. If the source of sulfur for sulfation were from waste flue gases, it is likely that the oxygen content of the gas stream would be more than sufficient to oxidize any MnsO4 to MnzO3, 107 atm of O2 required, or even to convert any Mnz03 to MnOz, 0.02 atm OZ required, prior to sulfation. At 1100°K, the diagram indicates that MnSO4 may be converted directly to either MnzO3 of Mn3O4, depending upon the prevailing partial pressure of oxygen. When the gas stream contains more than 1 pct Oz, logpq = -2, only MnzO3 would be recovered from an experiment done under equilibrium conditions. At oxygen partial pressures of less than 1 pct, one would expect to bring about a reversible exchange between MnSO4 and Mn3O4 by appropriate adjustment of the partial pressure of SOZ. These various reactions will be described in the subsequent kinetic experiments.

Jan 1, 1969

By Anton Sawatzky, Erich Vogt

By means of mathematical solutions to the appropriate diffusion equations, we describe the kinetics of the thermal diffusion of hydrogen in Zircaloy-2 for the various temperatures and concentrations encountered in a heavy water moderated reactor. When the hydrogen concentration is below terminal solid solubility only the a Phase is present. Redistributions are then described in terms of the characteristic functions of the difhsion equation. For higher concentrations both the a and 6 phases are present. We assume the two phases to be always in equilibrium. For moderately small hydrogen concentrations exact solutions of the two-phase equation approach the the approximate solutions derived by Sawatzky and for all concentrations the exact solutions exhibit the qualitative features of his result: the two-phase concentration increases with time, everywhere; in the absence of a hydrogen current at the hot end of the sample an a-phase region always exists there; the interface of the a + 6 , a-phase boundary moves toward the cold md of the sample and the hydrogen concentration is discontinuous at the interface. Simultaneous solulions of the a and a + 6 hydrogen distributims and of the concomitant interface motion are obtained and compared to the observations of Sawatzky and Markowitz. The kinetics of the hydrogen diffusion process are shown to lead to m apparent heat of transport of the a phase which is lower than the actual value (even for samples with long anneals) thus resolving at least partially the disparity between experimental measurements of this quantity. A number of recent papers1"4 have reported measurements on the diffusion and redistribution of hydrogen in Zircaloy-2 under temperature and concentration gradients. These studies were instigated by problems arising from increasing use of Zircaloy-2 as a fuel element cladding material in pressurized-water power-reactors. The Zircaloy-2 picks up hydrogen during the operation of the reactor: the consequent precipitation of zirconium hydride in the Zircaloy-2 has pronounced effects on its mechanical properties. The Purpose of the present Paper is to describe the kinetics of the thermal diffusion of hydrogen in Zircaloy-2 for the various hydrogen concentrations and temperatures likely to be encountered in reactors. When the hydrogen in the Zircaloy-2 is entirely in the solid solution phase (a phase), the differential equation for thermal diffusion is well known and the redistribution can be described by standard mathematical methods some of which are given in Section 11 below. The treatment of the a + 6 (hydride) region differs from the earlier treatment of sawatzky3 by taking into account several modifications of the two-phase diffusion equations as suggested to us by Markowitz4 and Kidson.5 Even with the modifications the results obtained in our more complete treatment are substantially the same as those found by Sawatzky. As we show, the difference between the results of sawatzky3 and kIarkowitz4 is largely due to the difference in the geometry of their experiments. In the next section we derive the modified two-phase equation for arbitrary geometry. The exact solution of this equation is given in Section III for linear and cylindrical geometry. It is shown that Sawatzky's approximate solution is quite accurate for almost all the temperatures and hydrogen concentrations which are actually encountered. In Sawatzky's approximate theory the hydrogen concentration everywhere in the two-phase region increases continuously. As his paper pointed out, this result, together with hydrogen conservation, implies that in a sample with no hydrogen current flowing into the hot end a two-phase region is always accompanied by a single-phase region at the hot end of the sample. The net hydrogen gain in the two-phase region is supplied by the decrease of hydrogen in the single-phase region and by the movement of the (a, a + 6) boundary toward the cold end of the sample. Hydrogen conservation at the (a, a + 6) boundary leads to a discontinuity in the concentration and its derivative there. In Section IV it is shown how these qualitative features of the thermal diffusion kinetics arise from the simultaneous solution of the a-phase differential equation and a + 6 phase equation. Methods derived by us previously for the solution of the redistribution in both phases and the accompanying motion of the boundary are used to obtain approximate solutions valid for large times. The solutions account well for the observed redistributions of Sawatzky and Markowitz. It is shown how the continuing motion of the (a, a + 6) boundary leads to measured values of the heat of transport lower than the actual value, even for specimens with relatively long anneals.

Jan 1, 1963

By Peter R. Morris

The effecl of preferred orienlation on X-vay dzffvaction measurements of retained austenzte was investigated for four precipitation-hardening staznless steels in sheet form. A method is preserzted for estimating the ervor in measurement associated with a given samplirig direction. The method was used to select an "optimum" sampling direclion in order to minimize errors in measurement due to preferred orientation. hleasuremenls of retained austenite content employing lhe proposed sampling direction are conzpaved to measuretnents enzploying the more commonly used normal direclion for a series of sawzples. THE first application of X-ray diffraction to the measurement of retained austenite in steels is due to Sekito, 1 who employed a photographic technique in which the (111) reflection from a thin strip of gold affixed to a cylindrical sample was employed as a standard. Averbach 2 introduced the "direct comparison" method in which the ratios of observed to calculated random intensity are assumed proportional to the austenite and/or martensite contents. Averbach's work forms the basis of most subsequent X-ray diffraction methods for the determination of retained austenite. Subsequent improvements are due to: Averbach and Cohen,3 who employed a sodium chloride crystal to monochromate cobalt radiation; Averbach et a1.,4 who introduced a bent sodium chloride monochromator; Mager,' who used a bent quartz crystal to monochromate chromium radiation ; Littmam, who first used a geiger counter diffractometer for this purpose; Beu and Beu and Koistinen, 11,12 who studied effects of absorption factor, surface preparation, sample geometry, integrated intensity vs peak height, choice of radiation, monochromator, and filter. The possibility of errors in measured values due to orientation effects was noted by Miller,13 who suggested examination of a surface other than the plane of rolling. Lopata and Kula 14 have developed an experimental technique in which the preferred orientation is measured in each sample. They illustrated the method for a sample containing 42 pct retained austenite. Application of their technique to the 1 to 15 pct range typical for the precipitation-hardening stainless steels does not appear feasible. EXPERIMENTAL PROCEDURE The nominal compositions of the precipitation-hardening stainless steels investigated are listed in Table I. Ingots were solution-treated, hot-rolled to approximately 0.2 in., and reduced to 0.050 in. by a suc- cession of cold rolling and annealing operations. After this treatment the 17-4PH sample was in the marten-sitic condition, while the 17-7PH, PH 14-8Mo, and PH 15-7Mo samples were in the austenitic condition. Samples of 17-7PH and PH 15-7Mo steels in the mar-tensitic condition were obtained by heating to 1750'F for 10 min and holding at -100°F for 8 hr. A sample of PH 14-8Mo steel in the martensitic condition was obtained by heating to 1700°F for 1 hr and holding at -100°F for 8 hr, followed by aging at 950" for 1 hr. POLE FIGURE DETERMINATIONS Samples were thinned to 0.003 to 0.005 in. by etching in a solution containing 250 ml reagent-grade phosphoric acid (85 to 87 pct H3PO4), 250 ml technical-grade hydrogen peroxide (30 to 35 pct H 2 O 2), and 50 to 100 ml reagent-grade hydrochloric acid (37 to 38 pct HCl). The specimens were placed in an "integrating" sample holder which provided a 1-in. oscillation in the plane of the sample. The diffractometer was aligned to measure the intensity diffracted by planes of the particular {hkl} type being studied. The sample was Set for a given latitude angle, a, measured from the plane of the sheet, and diffracted intensity recorded as the longitude angle, 0, measured in the plane of the sheet from the rolling direction, was increased from 0 to 360 deg. After a 360-deg scan of B, a was incremented by 5 deg, and the process repeated. Random standards obtained by spraying suspensions of powdered iron (bcc structure) and nickel (fcc structure) in lacquer were used to correct observed intensities for absorption and geometrical effects. Zirconium-filtered molybdenum radiation was used to determine the transmission regions of the (111) (0to 45 deg), (200) (0 to 60 deg), and (220) (0 to 45 deg) austenite and (110) (0 to 45 deg), (200) (0 to 50 deg), and (211) (0 to 35 deg) martensite pole figures. Vanadium-filtered chromium radiation was used to

Jan 1, 1968

By P. Douglas, G. M. Leak, B. Mills

The sinusoidal surface relaxation technique has been used to measure the surface self-diffusion coefficient of spectroscopically pure nickel over a wide temperature range under a hydrogen atmosphere. A kink in the Arrhenius plot has been observed. In the temperature range T/T 0.98 to 0.80 (T in O K and T, is the melting temperature) the average self diffusion coefficient is given by Below the temperature T/T,- 0.80a decrease in the slope of the log Ds us 1/T plot is observed. This is associated with a diffusion process characterized by a lower activation energy (-20,000 cal mole'') and smaller preexponential term (-10- sq cm sec"). A series of experiments were carried out at T/Tm = 0.61 under a hydrogen atmosphere of higher oxygen partial pressure than for the rest of the experiments. It was found that Ds was significantly depressed due to oxygen adsorption. This evidence supports the opinion that the low temperature process (activation energy -20,000 cal mole-') is unlikely to be due to oxygen adsorption. An interesting feature of the present data is that the transition temperature (T/Tm - 0.80) is a function of orientation. For a small number of crystals of measured orientation the transition temperature was observed to be higher towards the low index (100) pole. Theories of surface diffusion are briefly reviewed and it is concluded that the present reszuts are best explained by invoking a surface roughening process. GJOSTEIN has recently analyzed available surface diffusion data for a wide range of metals. He suggested that two mechanisms were operative for fcc metals, an adatom process at high temperatures and a vacancy process at low temperatures. Results for nickel can be summarized as follows. At low temperatures (T/T, - 0.3 to 0.44) under ultra high vacuum conditions, Melmed2 measured an activation energy Q of 21 kcal mole-' using field electron emission microscopy. At higher temperatures (T/T - 0.7 to 0.9) under a vacuum of 10- ' torr, Maiya and lakel measured y as 39 kcal mole-' using the multiple scratch smoothing technique. The present work was undertaken to try to find out if two distinct processes could be observed. High temperature results give Q about 47 kcal mole-': there is evidence also for a low temperature value of about 20 kcal mole-'. These measurements were all made under a hydrogen atmosphere, in the temperature range 860" to 1412°C. Concurrent with the present study Bonze1 and jostein> have also observed a break in the Arrhenius plot for the (110) surface of nickel. These measure- ments under ultrahigh vacuum conditions using the laser diffraction technique are in excellent agreement with the work reported here under hydrogen annealing conditions. THEORY The available surface relaxation techniques include single and multiple scratch smoothing and grain boundary grooving. The processes have been compared in detail by Gjostein for conditions where surface diffusion dominates6 and Mills et al? where volume diffusion dominates. In summary the relevant points are as follows. Grain boundary grooving gives an average Ds for the two surfaces adjacent to the boundary and this can, to some extent, be simplified by using symmetrical bicrystals. This technique has been used to study the effect of environment on Ds for silver and copper.'-'' Scratch techniques yield Ds values for the small orientation range exposed by the scratches (-2 deg). The multiple scratch process is preferable because the profile rapidly becomes sinusoidal and can then be interpreted theoretically in a relatively simple way. Also corrections for mass transport processes other than surface diffusion can be introduced easily. Mullins" considered a sinusoidal profile described the wavelength of the profile. After time t the profile can be described by the equation The terms A, A', C, and B which account, respectively, for contributions due to evaporation-condensation, diffusion through the gas phase, volume diffusion through the lattice, and surface diffusion are defined as: where Ds = the surface self diffusion coefficient ys = the surface energy per unit area p = the equilibrium vapor pressure over a flat surface pa = the equilibrium vapor density over a flat surface DG= the diffusion coefficient of vapor molecules in the inert gas DM = the mass transfer diffusion coefficient which for a pure cubic metal is Dv/f where Dv is the radiotracer diffusion coefficient and f is the correlation factor H = the molecular volume V = the surface density of atoms, il2'3 M = mass of an evaporating molecule

Jan 1, 1970

By R. L. Fleischer, W. F. Hosford

Tensile data for coarse grained aluminum Polycrystals suggest that the "grain size" effect is not due to dislocations piled up at grain boundaries but rather is primarily a relative size effect due to surface crystals being weaker and less confined. STUDIES directed at interpreting hardening of poly-crystalline metals normally identify their strain hardening properties with those in some particular type of single crystal.1"4 The recent recognition in face centered-cubic metals of a nearly linear stage with rapid hardening occuring at comparable rates for both polycrystals and single crystals, suggested that the same process or processes determine both cases and hence that there exists some justification for the use of single crystals to understand polycrystals. Further evidence for the above view may be found by an approach initiated by Chalmers:5 By using bicrystals of controlled orientation it is possible to begin to assemble a polycrystal and also to study grain boundary effects in detail. In this way it has been found that a single grain boundary affects easy glide but not the subsequent stage II hardening.6 This result suggests that a sensitive way to observe grain boundary effects in polycrystals would be to vary grain size and measure easy glide. As will be seen, easy glide is only possible for coarse-grained samples, and hence the results will serve to fill in the gap in measurements between single crystals and bicrystals on one hand and fine-grained polycrystals on the other. One problem inherent in comparing single crystals with polycrystals is the uncertainty as to what slip systems are acting in a polycrystal. To compare the two types of samples, rates of shear hardeninn---L. on the acting -planes are needed. and these may be computed only if it is known what particular systems are active. The acting systems were examined for a coarse-grained polycrystal and it will be shown that the systems supplying the preponderance of slip can be determined with little ambiguity. EXPERIMENTAL PROCEDURE Twelve samples of aluminum were prepared by chill casting into a heated graphite mold, followed by annealing at 635° ± 5°C for 24 hr with an 8-hr fur- nace cool, and finally either etching7 or electropol-ishing.' The samples, with a 7 to 10 cm length between grips and 4.4 by 6.6 mm in cross section, were deformed at a strain rate of about 3 10 -3 . per min in a tensile device which has been described elsewhere.5 The composition was reported by Alcoa as 99.992 pct Al, 0.004 pct Zn, 0.002 pct Cu, 0.001 pct Fe, and 0.001 pct Si; nine samples were deformed while immersed in liquid helium and three in air at room temperature. The stress-strain curve for one of the samples (P-1) deformed at 4.2 "K has been reported previ~usl~.~ This sample was selected for determination of active slip systems. Eighteen of the crystals were examined by optical microscopy to determine the angles of slip line traces and by X-ray back reflection to determine orientation. By this means the slip planes were determined and the resolved shear stress factors for possible slip systems could be computed. Finally each sample was sectioned so that after etching, the number of crystals could be counted for each of ten newly exposed surfaces. The average of these ten values will be termed n, the number of crystals per cross section. Values of 11, varied from 1.9 (nearly bamboo structure) to 12.7. Sketches of typical cross sections appear in Fig. 1. RESULTS AND DISCUSSION: SLIP SYSTEMS 1) Determination of Acting Slip Planes—The stress axis orientation and operative slip planes in eighteen crystals of sample P-1, as determined by slip line traces and crystal orientation, are summarized in Fig. 2. For one of the crystals two planes had a common trace. so that the traces alone did not distinguish which plane or planes were slipping. However it was found that the stress resolving factor for the primary system was 0.386, .while that for the most stressed system in the other plane (indicated bv the dotted arrow) is 0.138. It will be assumed tgerefore that only the primary plane acted. Since the orientations were determined after extending the samples 4 pct, the stress axes may be rotated from their original value by as much as 2 deg in some cases. It is interesting to note that in five crystals only one slip plane acted, in eight two acted, and in five three planes were observed—an average of two slip

Jan 1, 1962

By G. W. Nabor, A. S. Odeh

The effect of production history of a well on the results of two-rate flow tests, and conventional build-up analyses was investigated. The effect was examined by means of digital computers and an R-C network model, respectively, for wells with infinite and finite radii of drainage. For systems which behave as infinite, it was found that production history and the duration of production at constant rate prior to the initiation of the test have important effects on the results. During build-up time equal to about one-fourth of the stabilized time, correct permeability-thickness product calculations can be made. For wells with finite radii of drainage, the time was determined during which the straight line can be satisfactorily used for permeability-thickness product calculations in case of drawdowns and build-ups. On build-ups, the dimensionless time (based on the external radius) during which the straight line gives reliable results was detertriined to be about 1/12. This is one-fourth as long as that of the drawdown. The investigation was done theoretically, and subsequently was verified by R-C network model runs. General interpretive rules were formulated which, if not followed, could lead to serious errors. Moreover, a recommended testing procedure is reported. INTRODUCTION The method used by most reservoir engineers for estimating formation characteristics in a producing well is the analysis of pressure build-up data. The method originally devised by Horner' makes use of the point source solution to the diffusion equation. This solution is approximated by a logarithmic function and the superposition principle is employed to arrive at the well known pressure build-up equation:where q, the flow rate, is in reservoir B/D; ft is in cp; kh is in md-ft; At is the shut-in time; and t is the producing time. At and t are in any consistent time units. Ey. 1 is applicable to a well of unlimited drainage radius which produces at a constant rate q from zero to time t and is then shut in. Such a constant production rate seldom obtains in practice. Therefore. a correction term must be applied to Eq. I to account for the varying rate. Two theoretically accurate methods are available for treating the variable rate case. The first, originally derived by Horner,' is based on the application of the superposition theorem. It requires knowlege of production history of the well as a function of time and results in lengthy and laborious calculations. The second t*q* niethod is suited for short production tests and requires that the shut-in time be at least one and one-half times the production time. A third method which is not based on any theoretical justification and which was suggested by Horner as a "good working approximation" is the one used by the majority of reservoir analysts. especially when the well has been producing for a long time and the t*q* method is not practicable. The key to this method is in choosing or determining the t that appears in Eq. 1. Horner suggested using a corrected time t, in place of t. t, is calculated by dividing the total cumulative production by the last established rate. Therefore, a normal procedure of pressure build-up testing is to stabilize the well at a constant rate for at least 24 hours before shut in and to use the stabilized rate to calculate t,. The analysis is then made by plotting either or P. and examining the resulting plot for the expected straight line to calculate kh and the original reservoir pressure. Recently, Russell" proposed a method for determining formation characteristics from two-rate flow tests. His method reduces to pressure build-up if the second flow rate is zero. Russell uses the Horner simplified procedure for calculating a corrected t,. His method also requires the stabilization of the well at a constant rate q which is used to calculate t,. Theoretically, the above procedure is valid for a well with an unlimited radius of drainage or with a limited radius as long as the boundary effect has not been felt by the well. Several authors'' derived formulas which allow the estimation of time during which limited reservoirs behave as infinite ones and, thus, can be treated by unsteady-state mechanics. One equation derived by Swift and Kiel' terminates the application of unsteady-state theory when the drainage radius reaches one-half the reservoir radius. Thereafter, steady-state behavior obtains. Another equation derived by Jones'" initiates steady-state

Jan 1, 1967

By A. W. Adamson

A model for transport processes in liquid mixtures is discussed which supposes that the elementary act involves a position exchange between two species and that the exchange is so confined by the solvent cage as to occur nearly isosterically. The rate-determining step, thus, is likened to a bi-molecular reaction and is so treated, using absolute rate theory. The cage model has been applied to diffusion, thermal diffusion, sedimentation and viscosity, but only the first and last of these phenomena are emphasized in the present paper. The model leads to semi-empirical relationships between the absolute value for a digusion coefficient and the activation energy for diffusion, between mutual and self-diffusion coefficients and for the variation of the viscosity of a binary mixture with composition. These are discussed in relation to experimental data for various systems, including hydrocarbon mixtures. It is shown that the proposed viscosity equation and seven other commonly used ones all may be regarded as special cases of a single general relationship; a brief critical analysis is made of the basis of selection of one or the other for data fitting or interpolation. INTRODUCTION AND GENERAL THEORY The present paper covers a brief discussion of a cage model for transport processes in liquid mixtures and how this model may be useful in treating the diffusional behavior and the viscosity of such systems. Since diffusion requires the more detailed treatment, it will be taken up first, and the model then applied to viscosity. There are two types of diffusion coefficients that may be measured experimentally, apart from thermal diffusion quantities. The first is the mutual or binary diffusion coefficient, D which may be defined in terms of Fick's first law. This states that the permeation, or flux P, is proportional to the concentration gradient. In the usual experiment, P is measured relative to a frame of reference fixed with respect to the medium (e.g., the diaphragm in a diffusion cell); as a consequence, the same value of D is obtained regardless of whether P and C refer to Component 1 or to Component 2; i.e., there is only one independent mutual diffusion coefficient for a binary system. In addition to D there will be various self-diffusion coefficients. defined in terms of the gradient in labelled species i and its permeation in an otherwise uniform medium. The thermodynamic approach to mutual diffusion supposes that the actual driving force is the gradient of the chemical potential, i.e., that In the case of a dilute solution of solute, Eqs. 1 and 3 lead to the Einstein equation, If the solution is ideal and the friction coefficient is taken to be then the familiar Stokes- Einstein equation results. Mutual and self-diffusion coefficients can not be related on general thermodynamic grounds; it is necessary to invoke some additional assumptions, i.e., a model; several such have been proposed. Hartley and Crank' supposed the existence of separate, intrinsic diffusion coefficients (Dl and D2) for each component, essentially corresponding to the two self-diffusion coefficients. The two flows can not be independent, however, but must be coupled through the usual restriction that there be no net volume flow. For an ideal solution. one then obtains' Glasstone, et al' treated diffusion in terms of absolute rate theory, but their approach otherwise resembled the previously mentioned one in that each species was considered to move with respect to the general medium in a manner determined by its individual jump distance and specific rate constant. For other than dilute solutions, a coupling of flows leading to an equation such as Eq. 6 would again be present. However, as required by Eq. 6, one does expect that the self-diffusion coefficient for the solute and the mutual-diffusion coefficient for the system become identical at infinite dilution. Lamm4 recognized that there should be three distinctive interactions in a two-component system-1-1, 1-2 and 2-2 — and, therefore, proposed three rather than two fundamental friction coefficients. Mutual diffusion resulted from 1-2 interactions only, and self-diffusion resulted from 1-2 plus either 1-1 or 2-2 interactions. Again, a collective coupling between all motions was imposed to meet the condition of no net volume flow. Laity' has shown how to convert the Onsager equations to a form very similar to Lamm's. Cage Model For Diffusion Work in this laboratory on diffusion in aqueous sucrose solutions made it apparent that three, rather than two, interactions were indeed needed," but considera-

By Walter Showak

The published phase diagrams for the copper-zirconium system1,2 indicate that the solid solubility of zirconium in copper is not accurately known. Studies made on relatively impure alloys by Pogodin, Shumova, and Kugucheva3 yielded a maximum solubility value of 1 wt pct Zr at the eutectic temperature. Allibone and sykes5 reported that an as-cast 0.2 wt pct Zr alloy is single phase at room temperature. Limited results obtained by Raub and Enge14 indicated that zirconium solubility in copper is less than 0.13 wt pct Zr at 940°C. Tn 1960, on the basis of a microstructural examination of several copper-rich Cu-Zr alloys, saarivirta6 placed the maximum solubility of zirconium in copper at 0.15 wt pct at the eutectic temperature, 980°C. The present note describes results obtained during a re-investigation of the Cu-Zr system for the purpose of accurately establishing the solidus and solvus curves and the eutectic temperature in copper-rich alloys. High-purity copper (99.99 pet) and zirconium (99.64 pet) consolidated reactor grade sponge were used to prepare several alloys, containing up to 2 wt pct Zr, by induction melting in graphite crucibles in vacuum and chill casting into a split steel mold. The melting procedure consisted of first melting the copper charge and then adding the bulk zirconium wrapped in pure copper foil. Chemical analyses were made of both the cold-rolled alloy ingots after homogenization at 925°C for 450 hr in evacuated quartz capsules and of small specimens which had been used in the phase diagram studies. 'The carbon content of each alloy was also determined and was found to be less than 0.001 wt pct in every case. Metallographic and electrical resistivity measurements were used as the primary methods for this investigation, although some thermal analysis studies were also performed. Heat treatments of all the alloys were carried out with the specimens wrapped in molybdenum or alloy foil (of the same composition as the specimen) and sealed in quartz tubes either in vacuum or under a purified helium atmosphere. Following high-temperature anneals for long periods of time, slight depletion of zirconium from the specimen surface was observed. Therefore, careful preparation of samples for microscopic examination and chemical analysis of the samples themselves was necessary to check the composition of samples used in determining phase boundaries. Points on the solvus curve were determined on quenched specimens by both isothermal reaction after solution heat treatment at 950°C for 8 hr and by isothermal annealing of alloy specimens at successively higher temperatures for times ranging from 24 to 500 hr. Liquation studies for positioning of the solidus and eutectic temperatures were performed by holding a pre-

Jan 1, 1962

By Ralph Hultgren, David W. Mitchell

MAGNESIUM alloys usually are superheated before casting in order to ensure fineness of grain. Superheat temperatures in common use range from 1600° to 1700°F while the casting temperature, which depends upon the mold shape, is usually 200° to 300°F lower. The process of superheating requires considerable time and seriously shortens the life of the iron pots used. Recently it has been reported' that if acetylene, carbon dioxide or natural gas is bubbled through molten electrolytic A.S.T.M. No. 4 alloy at 1400°F. for 5 min., grain refinement equivalent to that of superheating will take place. Addition of certain solids such as graphite or aluminum carbide accomplishes the same results.2 As will be shown in this paper, it is possible to achieve grain refinement in magnesium casting alloys at low temperatures by mechanical stirring of the molten metal for a short time. This process was developed in the course of research work, supervised by the War Metallurgy Committee under the "Restricted" Project NRC-550, for the Office of Production Research and Development of the War Production Board. This paper, based on that work, has been released for publication by the O.P.R.D. MATERIALS AND METHODS The alloys studied were the most common American sand-casting alloys designated as No. 4 and No. 17 by the American Society for Testing Materials. The magnesium used in these alloys was of both carbothermic3 and electrolytic4 origin. Chemical analyses supplied by the producers are shown in Table I. Each heat consisted of approximately 5 lb. of alloy melted in a Tercod crucible. It was refined by fluxing with Permanente No. 7* refining flux at 1300° to 1350°F. After cooling to 1200' to 1250°F., portions of approximately one pound each were ladled into iron crucibles contained in an electric furnace at about 1250°F. The molten metal was covered with Permanente No. 21† covering flux and then heated to the temperature to be investigated. Normally each of the four portions was given a different treatment. In a typical case one portion was stirred vigorously for 5 min., acetylene gas was passed through a second portion for 5 min., a third portion was superheated to 1600°F for 15 min., then cooled to casting temperature, and the fourth was held for 5 min. at the temperature of stirring or gassing without other treatment. Each portion was then cast into one-inch diameter cylinders in three "nonturbulent" molds of identical shape. One mold was made of cast iron and the other two of baked sand. The cast-iron mold and one of the baked sand molds were heated to 360°F., the other baked sand mold was at room temperature. The freezing times in these molds were

Jan 1, 1945

By Ralph Hultgren, David W. Mitchell

Magnesium alloys usually are superheated before casting in order to ensure fineness of grain. Superheat temperatures in common use range from 1600" to r 7o0°F.; the casting temperature, which depends upon the mold shape, is usually 200° to 300°F. lower. The process of superhcating requires considerable time and seriously shortens the life of the iron pots used. Recently it has been reported1 that if acetylene, carbon dioxide or natural gas is bubbled through molten electrolytic A.S.T.M. No. 4 alloy at 1400°F. for 5 min., grain refinement equivalent to that of superheating will take place. Addition of certain solids such as graphite or aluminum carbide accomplishes the same results? As will be shown in this paper, it is possible to achieve grain refinement in magnesium casting alloys at low temperatures by mechanical stirring of the molten metal for a short time. This process was developed in the course of research work, supervised by the War Metallurgy Committee under the "Restricted' project NRC-550, for the Office of Production Research and Development of the War Production Board. This paper, based on that work, has been released for publication by the O.P.R.D. Materials and Methods The alloys studied were the most common American sand-casting alloys designated as No. 4 and No. 17 by the American Society for Testing Materials. The magnesiun used in these alloys was of both carbothermic3 and electrolytic' origin. Chemical analyses supplied by the producers are shown in Table I. Each heat consisted of approximately 5 lb. of alloy melted in a Tercod crucible. It was refined by fluxing with Permanente No. 7* refining flux at 1300° to 1350°F. After cooling to 1200° to 1250°F., portions of approximately one pound each, were ladled into iron crucibles contained in an electric furnace at about 1250°F. The molten metal was covered with Permanente No. 21 † covering flux and then heated to the temperature to be investigated. Normally each of the four portions was given a different treatment. In a typical case one portion was stirred vigorously for 5 min., acetylene gas was passed through a second portion for 5 min., a third portion was superheated to 1600°F. for 15 min., then . cooled to casting temperature, and the fourth was held for 5 min. at the temperature of stirring or gassing without other treatment. Each portion was then cast into one-inch diameter cylinders in three "nonturbulent" molds of identical shape. One mold was made of cast iron and the other two of baked sand. The cast-iron mold and one of the baked sand molds were heated to 360°F., the other baked sand mold was at room temperature. The freezing times in these molds were

Jan 1, 1945

by their overdogmatic picture of geology and their resulting drastic oversimplification and idealization of geologic features. I am in hearty disagreement with the recommendation that geophysics should be done by cooperative work between a geologist and a geophysi-cist. That arrangement would be comparable to doing petrography by having a physicist at the microscope and a geologist sitting by his side. The interpretation of the geological significance of geophysical data can be done efficiently only by a physicist who has become also a good geologist or by a geologist who is also a good geophysicist. Less Well-trained Men The rank and file, composing perhaps two-thirds of the personnel of exploratory geophysics, is not, and should not be, composed of highly trained men. The routine, stereotyped character of the work and the impossibility of promotion of more than a few from these lower ranks even under the best circumstances justify companies in filling the bulk of these rank and file positions with men having only a bachelor's degree at the most. There can be a wide range of training for such positions, although certain lines of study are preferred for certain kinds of work, and different employers have different preferences. For work in gravitational and magnetic prospecting, first preference will be for men having geological training and second for men with civil engineering training. In seismic work, men with geological training are preferred by some employers for computers; physicists, electrical engineers and all whose technical education has covered radio circuits are preferred for the other technical positions. Collegiate training in geophysical prospecting brings no preference and by many employers is given a slightly inferior rating. One large company seldom hires men who have just graduated with a major in geophysical prospecting. This prejudice is based on the reasoning that much of what is learned in college is obsolete or obsolescent, that most of the techniques learned in college will have to be unlearned, because different from those used by the employing company, and that in the long run additional courses in basic physics, mathematics and geology are of more value to a man than the courses on geophysical prospecting. DISCUSSION [This discussion refers to the five papers beginning on page 23 and ending on page 74.1 L. W. Blau,* Houston, Texas.—I have had some rather sad experiences with forecasting. For example, I could not foresee 10 years ago my present occupation, and I do not profess to be able to look ahead 10 years and tell anyone what he will be doing then. Referring to the point raised in the discussion, I do not know, for example, what the price of oil will be 10 years from now. If an appreciable number of

Jan 1, 1940

By W. A. West

ONE who attempts to collect and classify equilibrium data from various iron-alloy systems is soon struck with the absence of any quantitative theory that can serve as a general background against which to compare and contrast results from different systems, at different temperatures, and with different concentrations. It is not necessary to wait for a perfect theory; investigation of divergences of theory from observation may prove of great value in acquiring understanding of the subject. For example, one has only to think of Raoult's law as applied to aqueous solutions. The equations developed by Zener1 represent an effort to provide such a quantitative theoretical background, and it is therefore desirable to subject this theory to such tests as can be applied. The present article is intended to be an application of available tests, and may thus be considered as a supplement to Zener's paper. It is assumed that this paper is available to the reader. The equations make it possible to calculate the effect on the equilibrium concentration of one alloying element due to the presence of one or more other elements. In particular they are intended to give, for alloy steels, the carbon concentrations in alpha and gamma phases in equilibrium with each other, and in gamma in equilibrium with cementite. They may, however, be modified for use for carbon-free alloys. A summary is given later of the equations used in analyzing the data in this paper, and the symbols are there defined. About 125 papers have been examined for experimental data suitable for this investigation. An effort was made to look up all available reports of ternary systems including iron and carbon, as well as similar systems of higher order. Supplementary material was also obtained from a number of binary systems. A few noncarbon ternary systems were also found to which these methods could be applied. A comparatively small proportion of the papers read provided usable material. In many systems the number of quantitative observations made in the iron-rich region is extremely small, and the smoothed curves to be found in most published phase diagrams are entirely useless for quantitative treatment. This opinion is confirmed by the authors of the series on Alloys of Iron Research, whose remarks show clearly that they have no illusions as to the accuracy of many diagrams that they present. A further difficulty arises from the fact that these equations apply only to rather low percentages of alloying elements. The result is that at the lowest concentrations, where the best agreement might be hoped for, the errors of observation become relatively very large. The experimental difficulties in measurements of this kind of equilibrium are, of course, an old story.

Jan 1, 1946

By J. E. Gould, H. J. Hand

MANY independent studies are being made on slag-metal relationships in the open-hearth furnace, and these studies cannot help but result in an ultimate improvement in the quality of open-hearth steel of both the open and killed types In maintaining quality control at the National Tube Company's plant, emphasis has been placed on an evaluation of the iron oxide content of the steel in as quantitative a manner as possible, in order that the most desirable level of oxidation might be obtained for a given type of steel, and to secure a more precise basis for final deoxidation In the past, various methods were used for estimating FeO content of the metal at tap to ensure uniform and thorough deoxidation of killed steel, avoiding over-deoxidation to minimize the amount of inclusions present and to make as sound a steel as possible For the open-type steels, such control involves obtaining the necessary level of oxidation for the most suitable action of the steel in the molds to provide good surface quality and cross section for the specific grade involved While rapid analytical methods are available for determination of FeO in the liquid metal, such methods are still not sufficiently rapid for routine control on the open-hearth floor, nor do such analyses provide information as to what causes high or long FeO values The method of sampling can still be considered a problem in view of the variability encountered in taking simultaneous duplicate tests With the accurate rapid methods now available for determining carbon in the metal, estimating slag basicity and obtaining temperatures of liquid metal, it was believed possible to determine the influence of the various furnace reactions in establishing the state of oxidation at a given time Simultaneous slag and metal tests were used in this analysis, aided by statistical methods, to determine the factors that affect the metal FeO, and also to make a quantitative evaluation of these factors Data obtained are from actual furnace operations, the metal test being of the spoon, Herty type, and taken in duplicate. Metal temperatures were taken with the open-tube bath pyrometer developed by the Research Laboratory of the United States Steel Corporation This method of taking open-hearth metal temperature was invented by Collins and Oseland,1 and was developed into its present form by L 0 Sordahl,2 of the Research Laboratory The instrument and its mode of operation have been fully described by Sordahl and Sosman in three publications 3,4,5 Slag components were obtained by chemical analysis Data were taken from four 165-net-ton furnaces during the working period of the heat Recognizing that additions of ore affect the

Jan 1, 1942

The object of crushing and grinding for leaching is obviously to permit contact of the solvent and mineral and subsequent removal of pregnant solution in a reasonable time. Heap leaching is the leaching of ores that have been mined and transported to prepared, relatively impervious pads for leaching by sprinkling or ponding, and percolation of the lixiviate through the ore. Dump leaching is the leaching of dumps or low-grade ore or overburden without the use of prepared pads under them. Run-of-mine material, e. g., low -grade ore from open pit stripping operations, may be leached without crushing, and a fairly high recovery made by heap leaching. An alternate method for better grade gold/silver ores is to crush to 9 to 13 mm (318 to112 in. ) size for pad heap leaching, as used by Smoky Valley Mining Company at Round Mountain, Nevada, on gold ore, and to 38 rnrn (1 -1 12 in.), which will be done by Candelaria Partners, at Candelaria, Nevada, on silver ore. Heap leaching of copper probably began at Rio Tinto, Spain, about the year 1752. This was done by the leaching of weathering piles of ore in the open air followed by iron cementation of the liquor that drained off the heaps. Its application to the low -grade southwestern United States copper ores was overlooked for many years, and low- grade ores from Sacramento Hill at Bisbee, Arizona, were the first to be heap leached in 1923. Site preparation used a half century ago is the same today. "The need for some form of waterproofing of the pad was evident. Before leaching ore was piled, the site was cleared of cactus and brush. After clearing a gentle sloping area, it was then covered with a blanket of rolled and tamped clay or slime tailing. When heaps are built, a layer of coarse fragments may be put down first to assist drainage. A second method of leaching without grinding, usually for higher grade ores, is by vat or tank leaching of material crushed to 9 to 13 mm (318 to 112 in.) size. Such a plant is considerably more expensive than a heap leaching installation but much less costly than grinding for agitation leaching, and a recovery higher than that obtained by heap leaching is to be expected. Vat leaching has been widely used by the copper industry on higher grade copper ores but has been used in only a few small operations on that size gold or silver ores. However, such a plant should be considered for a modest tonnage of a few million tons, 3 to 7 g per mt (0.10 to 0.20 oz per st), of Carlin-type leachable ores crushed to 9 mm (318 in.).

Jan 1, 1981

By R. W. Fenn, H. A. Lepper, W. R. Hibbard

THIS paper reports the results of static tension and torsion tests made on single crystals of alpha brass for the purpose of determining its elastic coefficients. 70-30 alpha brass was chosen because it has been used extensively in the study of the plastic deformation and because it has the following desirable characteristics: (1) face-centered cubic structure, (2) marked elastic anistropy, (3) low elastic modulus. In 1928 Masima and Sachs' using static methods reported the following values for the elastic coefficients of 72-28 pct alpha brass: S11 = 19.4 X 10-13' cm2 per dyne S12 = —8.35 X 10"' cm2 per dyne S44 = 13.9 X 10-13= cm2 per dyne These values were obtained from the measurements shown in fig. 1. The experimental points for both tension and torsion lie consistently below the lines drawn to represent them. Fig. 2 shows the stress-strain curves for their specimens. Only a few points in the elastic range of these curves were available to obtain their values for Young's modulus. Therefore, it was considered that a re-evaluation of these data was desirable. In addition a variation of from 1.13 to 1.485 kg per mm2 was found in the values of the critical resolved shear stress for 70-30 alpha brass reported by Burghoff,² Treuting and Brick: Martin,4 Maddin, Mathewson and Hibbard5,6 and von Goler and Sachs.' Therefore, it was desired to evaluate the conclusion of Boas and Schmid8 that a constant resolved shear stress and not a constant elastic shear initiates plastic deformation. Theoretical Considerations*: The elastic deformation of cubic crystals may be defined by three elastic coefficients (S11, S12, S44,) or three elastic parameters (C,,, C,, C,,). These coefficients or parameters are sufficient to define the stress and strain relations for cubic crystals in the generalized form of Hooke's law referred to Cartesian coordinates. Elastic parameters and coefficients in the cubic system are related by the expressions: C11 —S11+S12/(S11-S12)(S11+2 S12) C12=-S12/(S11-S12)(S11+ 2 S12) (S11 — S12) (S11 + 2 S12) [2] C44 =1/S44 PI It is possible to determine all the elastic coefficients for a cubic metal by measuring two of the three elastic constants: Young's modulus (E), torsion modulus (G), or compressibility (S). The following relations exist between crystallographic orientation and E, G and S for cylindrical crystals of the cubic system: 1/E = S11 — 2 [(S11 - S12) — Su] (?1² ?2² + ?2²?83 + ?3² ?1²) [4]

Jan 1, 1951

By L. G. Jones

The objective of this paper is to present a better method for determining reservoir reserves of gas from extended drawdown test data. Means are proposed for conducting the test with or without the requirement of prior build-up to a static reservoir pressure. The test is based upon solutions to unsteady-state gas flow developed in an earlier paper and is believed to be superior to previous methods for determining reserves from flow-test data. The limitatiom of such tests are discussed, with emphasis on the subject of test duration. The test can supply useful information if the mechanics and limitations of it are understood. This type of information can be particularly valuable in deciding whether or not to drill offsets to producing wells. INTRODUCTION In the life of any gas or oil field, the engineer in charge must decide if certain wells need stimulation and whether or not to drill more wells in the field. Well production tests can aid in making these decisions. For instance, the value of stimulation can be estimated by determining formation permeability and the amount of well damage from drawdown or build-up tests. These tests are freely used in the oil industry. A less well-known type of analysis uses data from extended drawdown tests for determining reservoir reserves. Into this category fits the "reservoir limit test" of Jones,'-3 and the "reservoir reserve test" presented in this paper. The chief value of these tests is their ability to "see" reservoir boundaries and thus prevent costly dry holes. Methods for determining reserves of both gas and oil reservoirs were proposed in the work of Jones. His proposals appear sound for single-phase liquid flow. The generality of his work on gas flow is open to question, however, since the analysis is based upon solutions to liquid-flow equations. The test for gas reserves presented here is derived from unsteady-state gas-flow solutions presented in a previous paper.' In deriving this reservoir reserve test, it has been assumed that all of the reservoir energy is provided by expansion of the reservoir fluid and that the reservoir is radially symmetrical. No mention has been made of the effects of deviations from Darcy's law such as quadratic (turbulent) flow and well damage. Since the terms representing these effects are function of rate only, since the rate is constant and since the data are plotted in a differential form, it seems reasonable that these terms will not affect the test results in any way. No attempt has been made to estimate the effects of water drive, faults, or other departures from an idealized and isolated reservoir. For a qualitative discussion of some of these effects, the reader is referred to a paper by Jones3

by their overdogmatic picture of geology and their resulting drastic oversimplification and idealization of geologic features. I am in hearty disagreement with the recommendation that geophysics should be done by cooperative work between a geologist and a geophysi-cist. That arrangement would be comparable to doing petrography by having a physicist at the microscope and a geologist sitting by his side. The interpretation of the geological significance of geophysical data can be done efficiently only by a physicist who has become also a good geologist or by a geologist who is also a good geophysicist. Less Well-trained Men The rank and file, composing perhaps two-thirds of the personnel of exploratory geophysics, is not, and should not be, composed of highly trained men. The routine, stereotyped character of the work and the impossibility of promotion of more than a few from these lower ranks even under the best circumstances justify companies in filling the bulk of these rank and file positions with men having only a bachelor's degree at the most. There can be a wide range of training for such positions, although certain lines of study are preferred for certain kinds of work, and different employers have different preferences. For work in gravitational and magnetic prospecting, first preference will be for men having geological training and second for men with civil engineering training. In seismic work, men with geological training are preferred by some employers for computers; physicists, electrical engineers and all whose technical education has covered radio circuits are preferred for the other technical positions. Collegiate training in geophysical prospecting brings no preference and by many employers is given a slightly inferior rating. One large company seldom hires men who have just graduated with a major in geophysical prospecting. This prejudice is based on the reasoning that much of what is learned in college is obsolete or obsolescent, that most of the techniques learned in college will have to be unlearned, because different from those used by the employing company, and that in the long run additional courses in basic physics, mathematics and geology are of more value to a man than the courses on geophysical prospecting. DISCUSSION [This discussion refers to the five papers beginning on page 23 and ending on page 74.1 L. W. Blau,* Houston, Texas.—I have had some rather sad experiences with forecasting. For example, I could not foresee 10 years ago my present occupation, and I do not profess to be able to look ahead 10 years and tell anyone what he will be doing then. Referring to the point raised in the discussion, I do not know, for example, what the price of oil will be 10 years from now. If an appreciable number of

Jan 1, 1940

By E. W. McAllister

The decision of the California Oil Umpire's' office to accept well potentials established from subsurface-pressure data has brought to the attention of many operators for the first time the application of such data to production problems. This paper reviews the development and application of subsurface-pressure data in kettleman Hills, where these data have been used in production work since 1932. The Kettleman Hills field was discovered in October 1928. The first subsurface-pressure surveys were made early in 1932 and by the middle of 1933 the two major operators in the field were making routine pressure runs in thcir respective wells. Shortly therefter, these companies agreed to exchange pressure data, and later a third company entered into the agreement. This made it possible to analyze the effects upon the reservoir pressure of past production practices, which are discussed in the latter part of the report. It is interesting that many of the applications of subsurface-pressure data discussed herein were anticipated by C. L. Clark and C. B. Kimberlint in a report2 dated March 1933. PRODUCTIVITY Index In the majority of individual well problems involving the use of subsurface- pressure data, it is necessary to use a factor known as the "productivity index," which indicates the ability of a well to produce and represents the number of barrels of oil or oil and water per day that will enter the well bore for each pound per square inch pressure drop made opposite the producing interval of the well. The productivity index may be determined from pressure and production data for one or more rates of flow and a static or shut-in pressure survey or from production and pressure data for two or more rates of flow. Productivity indices may be based upon either net oil or total fluid production. All indices referred to in this report are based upon net oil. The value of the productivity index for Kettlcman Hills wells decreases generally with time and it is not uncommon for the index to vary in value at any specific time fur various rates of flow. The decline of the productivity index may be attributed partly to the loss of reservoir pressure. As the reservoir pressure decreases, gas originally in solution is released from the oil, congesting the flow of fluids through the formation and increasing the viscosity and surface tension of the oil; thus the flow resistance of the fluids through the formation is increased, resulting in a decrease of the productivity index. For convenient reference, the productivity indices for each well are plotted against time and a curve is drawn through the points showing the trend of the average index value. Plotted on Fig. I are index values for five

Jan 1, 1941

By M. R. Hatfield, F. J. Vosburgh

In a recent article, it was shown that in the blast furnaces in Germany that are lined with carbon blocks no cooling plates are used, and that shower cooling is employed on the hearth and bosh sections. While one of the authors was in Germany he was told that one furnace was being operated without even the shower cooling on the bosh section, though the hearth section was shower-cooled. In discussion of this interesting situation with a number of blast-furnace operators in this country, it was made clearly and promptly evident that shower cooling was very unpopular, probably because of its messiness and its ineffectiveness. Both of the causes for the dislike of shower coolings are reasonable ones. Shower cooling can be and frequently is messy, but the present cooling of blast furnaces leaves much to be desired on that score. Shower cooling is ineffective as compared with plate cooling, so far as its usefulness in keeping the bricks cool enough not to melt or fall to pieces is concerned. However, the introduction of carbon linings changes the situation. No one is concerned with keeping a carbon lining cool, for no temperature in the blast furnace has any effect on carbon, which is just as stable at 3000°F. as it is at 70°F. The only concern is for the shell—to keep it cool enough for safety and comfort— and for that shower cooling is sufficient. Of course, with only the shell to cool, instead of the shell plus all the refractory material, much less water would be required, and the necessity for constant attention to the flow would be lessened, as the hundreds of inlets and outlets would be eliminated. Probably half of the water used in cooling a blast furnace is used for cooling the shaft and tuyeres and the remainder for the bosh and hearth sections. However, in view of the dislike of shower cooling in the United States, and particularly because at least one German blast furnace is operated with no cooling of the bosh section, thought was given to the possibility that a carbon-lined blast furnace might be operated without any cooling of the entire carbon-lined portion. For that reason a series of experiments was performed to determine what might be the temperature of the shell of a blast furnace protected by a carbon lining and operated under varying conditions up to a maximum inside temperature of 3000°F. Experimental Procedure A schematic diagram of the experimental setup is shown in Fig. I and a photograph of the entire assembly in Fig. 2. The heating element was a a tubc nominally 25/8 in. 0.d. by 2 in. i.d. by 30 in., used as a resistor. Power was furnished by a I5-kva. transformer operating

Jan 1, 1942

By W. A. West

One who attempts to collect and classify equilibrium data from various iron-alloy systems is soon struck with the absence of any quantitative theory that can serve as a general background against which to compare and contrast results from different systems, at different temperatures, and with different concentrations. It is not necessary to wait for a perfect theory; investigation of divergences of theory from observation may prove of great value in acquiring understanding of the subject. For example, one has only to think of Raoult's law as applied to aqueous solutions. The equations developed by Zener1 represent an effort to provide such a quantitative theoretical background, and it is therefore desirable to subject this theory to such tests as can be applied. The present article is intended to be an application of available tests, and may thus be considered as a supplement to Zener's paper. It is assumed that this paper is available to the reader. The equations make it possible to calculate the effect on the equilibrium concentration of one alloying element due to the presence of one or more other elements. In particular. they are intended to give, for alloy steels, the carbon concentrations in alpha and gamma phases in equilibrium with each other, and in gamma in equilibrium with cementite. They may, however, be modified for use for carbon-free alloys. A summary is given later of the equations used in analyzing the data in this paper, and the symbols are there defined. About 125 papers have been examined for experimental data suitable for this investigation. An effort was made to look up all available reports of ternary systems including iron and carbon, as well as similar systems of higher order. Supplementary material was also obtained from a number of binary systems. A few noncarbon ternary systems were also found to which these methods could be applied. A comparatively small proportion oi the papers read provided usable material. In many systems the number of quantitative observations made in the iron-rich region is extremely small, and the smoothed curves to be found in most published phase diagrams are entirely useless for quantitative treatment. This opinion is confirmed by the authors of the series on Alloys of Iron Research, whose remarks show clearly that they have no illusions as to the accuracy of many diagrams that they present. A further difficulty arises from the fact that these equations apply only to rather low percentages of alloying elements. The result is that at the lowest concentrations, where the best agreement might be hoped for, the errors of observation become relatively very large. The experimental difficulties in measurements of this kind of equilibrium are, of course, an old story.

Jan 1, 1947