By Yutaka Shiraishi

Two methods were developed to measure the viscosity of the slag from the glassy to the liquid states in an ascending temperature process. The first method employs rotating parallel plates within which is placed a solid cylindrical sample in line with a sphere. The second method uses a tube which is pushed into a sample held in a rotating crucible. Both methods were tested using standard glasses, including boron trioxide and NBS standard glass #711. The main difference between these two methods is in sample preparation. Comparative measurements between two methods were performed using a sodium boro-disilicate glass containing 5%mol of alumina. The results showed good agreement in the mid-range of glassy viscosities, 105 to to7 Pa.s. In the liquid state, there were no significant differences between the two methods.

Jan 1, 2003

By S. A. Platias

Large amounts of dunile tailings can be recycled for olivine produdion from the existing beneficiation adivity of chromite ore in northern Greece. This olivine production aims at the preparation of a material suitable for the substitution of the environmental hazardous quartz sand in the foundries of Europe In smelting of chromite ore the losses that occur ore usually of the order of 6-8% Cr that report in the slag. Most of this is in the form of oxides that cannot be recovered, but usually 30-35% is in the form of FeCr alloy that can be recovered by gravity methods. About 90% of the produced slag is sold for road construdion after crushing to a desired grain size. Finally, recycling of chromites sludges from the ferrochrome produdion plant, through the preparation of pellets, improved the total chromite yield by 2%.

Jan 1, 1996

By Halvor Dalaker, Alain Marc Ferber, Thor Anders Aarhaug, Pål Tetlie

Off-gas monitoring of experimental reactors give little information about intermediate reaction products and reflect chemical equilibria at reduced gas temperatures. A reactor design with optical access was designed and tested in order to be able to qualify and quantify gaseous species from their emission spectra. By use of a sequence of sapphire, UV fused silica and IR transparent sapphire and CaF2 windows and lenses optical access to a hot, maximum 1800 °C, reaction zone was gained. A cooled area behind the reaction zone was used as a background in order to avoid signal saturation from reactor walls. In addition to molecular emission spectra, atomic emission lines are used to characterize stable gas constituents and radicals. The setup has been designed for the study of methane dehydrogenation experiments in order to investigate the carbon activity of reduction of oxide with methane, but has also been used to monitor gaseous silicon suboxide.

Jan 1, 2015

By Shengli Wu, Mingyin Kou, Laixin Wang, Zhe Wang, Xinliang Liu

The sticking behavior of iron ores in the shaft furnace is one of the most important problems in the COREX melting progress, which directly influence the smooth operation and productivity of shaft furnace. Therefore, it is of great importance to study the sticking behavior of pellets in COREX shaft furnace. The results showed that porous metallic iron produced at the interface of pellets samples was the main reason for the sticking of pellets in the COREX shaft furnace. The SI (sticking index) and metallization rate increased with the reduction temperature and gas flow, and decreased with melting rate. However, the SI of pellets in the COREX shaft furnace could be decreased by the proper match of melting rate and reduction temperature, reduction temperature and gas flow, while the metallization rate of pellets were kept at a certain level. Furthermore, the matching of melting rate and reduction temperature was more effective than the matching of reduction temperature and gas flow.

Jan 1, 2016

By Jie Ma, Bo Wang, Jieyu Zhang, Jian Zhao, Zheng Chen

"In this paper, solidification process of steel ingot was simulated by ProCAST software, based on cellular automaton-finite element (CAFE) model. A 22 t steel ingot was divided into continuous small zones (100x150x180 mm) in radial direction, then the temperature field, shrinkage cavity and porosity, particularly, the microstructure were simulated. The results show that: there was a columnar-to-equiaxed transition in microstructure on radial direction. Zones, closing to the center of the ingot, had a more developed and fined equiaxed zone, while zones closing to the periphery of the ingot had a more developed columnar zone. It indicated that temperature gradient has a great influence on microstructural morphology. Thus, the simulation results were highly agree with the experimental results, verifying the feasibility of this simulation method. It significantly reduces the time of simulation, and has important significance for predicting the microstructure of large steel ingot.IntroductionSolidification microstructure of steel ingot have a significant effect on the quality of the final steel products. Although many experimental works have been carried out in order to obtain the optimum condition for solidification process of continuous casting, it is also very desirable to establish mathematical models to simulate the evolution of solidification structure. The simulation methods can be divided into deterministic models and stochastic models, which have been developed rapidly over the last couple of decades. Cellular automaton method is one of the stochastic models. Rappaz and Gandin [1, 2], Nasatac and Stefanescu [3, 4] are the earliest researchers engaged in the this field. Moreover, Rappaz and Gandin simulated the solidification structure and CET (columnar grain to equiaxed grain transition) of metals using the CAFE method (cellular automaton-finite element method) for the first time [1, 2]. Recently, the CA (cellular automaton) model also considered the effects of fluid flow on the solidification process. Zhu, et al. [5-11] improved method of CA , they used the KGT model to describe the undercooling needed during the growth of the dendrite tip."

Jan 1, 2014

By Katsukiyo Marukawa, Manabu Iguchi, Sigeta Hara, Shinichiro Yokoya, Sigeo Takagi

"A numerical analysis and water model study of the mold region of a continuous casting apparatus was performed with a novel injection concept using swirling flow in the pouring tube, to control the heat and mass transfer in the continuous casting mold.As a result, the following results were found:1) By changing swirl strength, it is easy to control the flow pattern as well as the direction of the flow.2) Uniform velocity distribution can be obtained within a very short distance from the outlet of the nozzle.3) Heat and mass transfer near the meniscus can be remarkably activated compared with a conventional straight type immersion nozzle without swirl.4) Swirl helps the superheat in the melt dissipate.S) Penetration depth of nozzle outlet flow is decreased remarkably by the application of swirling.6) For the case without swirl, the peak of the flow moves near the mold-wall with flowing down from the outlet of the nozzle due to the Coanda-effect. On the other hand, peak of the flow moves near the mold axis with flowing down from the nozzle-outlet within considerable short distance, namely axi-symmetric velocity distribution can be obtained within very short distance from the nozzle-outlet.Those findings mentioned above are very useful to control the flow pattern in the billet and bloom continuous casters."

Jan 1, 2001

By C. E. Dodson

Conventionally hydrometallurgical recovery processes from sulphide concentrates include roasting, leaching, precipitation, impurity removal and zinc electrowinning. The use of the novel (yet commercially proven in other mineral and metallurgical industries) TORBED process reactor for the flash roasting of sulphides will be proposed. The potential advantages in its application will be discussed including very fine particle processing capability, lower cost smaller roasters, waste minimization, improved leaching efficiency and overall process simplification.

Jan 1, 1999

By Hsin H. Huang

Equilibrium calculational software programs can be effectively utilized to model the importance of activity or concentration, solubility, temperature, solution pH, solution potential, and ligand complexation on extraction and recovery processes. Illustrative examples using the calculational program ST ABCAL for the creation of diagrams such as EwpH, activity or concentration-pH, and activity or concentration-EH are presented to demonstrate the fundamental characteristics of real hydrometallurgical mercury dissolution and recovery processes. An industrial application will include leaching of mercury from K 106 mercury sulfide waste and solution purification by iron cementation.

Jan 1, 2003

By Louis J. Cabri

The ion microprobe (dynamic SIMS technique) is a very sensitive instrument for the quantitative determination of trace concentrations of precious metals (often at the ppb level) occurring in common sulfide minerals, either chemically-bound or as discrete particles too small for resolution by SEM. The technique involves sputtering a 250 x 250 Jim area of the grains to a depth of about one ILm and analysing the secondary ions emitted from a circular central region in the sputter crater with a 62.5 I'm diameter. The combination of quantitative mineral-specific sub-ppm analyses together with depth-profiling and the ability to produce secondary ion maps of trace precious metals makes this a very powerful technique in quantifying the precious metal distribution in refractory and other sulfide ores and process products. The technique is particularly well-established for analysis of gold-and platinum-bearing ores and process products.

Jan 1, 1996

By K. G. F. Janssens

In the process of annealing a deformed metal the microstructure changes due to concurrent recrystallization, grain growth and precipitation. It is common knowledge that all three of these microstructural transformations show a strong dependence on each other, and that an overall model must take the relevant interactions into account. Aiming at the development of an approach which is useful in the more general case, a computational model is being developed which allows the prediction of the three dimensional grain topology and orientation distribution function of any metal submitted to subsequent deformation and annealing, taking into account concurrent recrystallization, grain growth and precipitation and starting from a statistical representation of the deformed microstructure. In this contribution a case study is presented which illustrates the potential and limits of the state of the art in the field. Keywords: Microstructure Evolution Modeling, Irregular Cellular Automata, Deformation, Precipitation, Recrystallization, Grain Growth

Jan 1, 2003

By J. A. Eisele

There is currently much interest in how extraction of gold and silver from ores with acidic thiourea solution compares with extraction using alkaline cyanide solution. Agitation leaching tests were performed by the Bureau of Mines on 14 precious metal ores using sodium cyanide (?NaCN) and thiourea [(NH2)2CS) as extractants. The objective was to compare the results of the two extractants. NaCN was used at a concentration of 2 g/L with and without H202 as an oxidant. (NH2)2CS was used at concentrations of 2 and 20 gjL, and the solution potential was controlled at 390 to 420 mV standard hydrogen electrode (Eh) with Fe2(S04)3. With both reagents a.t 2 g/L extractant levels, NaCN extracted more gold and silver than (NH2liCS from all of the ores. At 20 g/L (NH2)2CS compared with 2 g/L NaCN, (NH2)2CS extracted more gold than NaCN from two ores, the same amount from one ore, and more silver from one ore. NaCN extracted more gold than (NH2 )2CS from 10 ores and more silver from 4 ores.

Jan 1, 1989

By Shenghui Guo, Jianbo Lan, Hongying Xia, Jinhui Peng, Lihua Zhang, Libo Zhang

Spent Hawaii nut shell was converted into a high-quality activated carbon via steam physical activation. Analysis of the experiment including activation temperature, activation duration, steam flow rate on the adsorption capability and yield of activated carbon were identified. Response surface methodology showed that the activation temperature was identified as 866 , an activation duration of 36 min and a steam flow rate of 2.5mL/min with the methylene blue adsorption number of 195 mg/g and yield of 77.75%. The key parameters that characterize quality of the activated carbon such as the BET surface area, total pore volume and average pore diameter were estimated to be 1125m2 /g, 0.94mL/g and 5.21 nm, respectively. Additionally, by the SEM analyses of char and activated carbon, the surface of activated carbon has large number of pores of irregular and heterogeneous morphology.

Jan 1, 2016

By Katsukiyo Marukawa, Mashamichi Sano, Shigeta Hara

"Various subject of studies are discussed to develop ·innovative refining processes in the 21st century for cost reduction, production of high quality steel and environmental conservation. The future refining reactor should have abilities of highly efficient mixing and separation of different phases. It is stressed ·that applications of electromagnetic and ultrasound energies, and control of flow fields rate required to create the highly efficient mixing I separation reactor.IntroductionIn recent years, it seems that the research and development in the field of steelmaking has shifted its emphasis to the solidification I ingot-making process in which continuous casting plays the leading role. From a long-range point of view, however, the need for continual development of the refining process will probably increase but is very unlikely to decrease. In order to meet such demands, it is required that problems and issues of the present process should be clearly grasped and that there must be rapid progress in process elements, such as highly efficient mixing and separation of different phases.Applications of electromagnetic and ultrasound energies and flow field control will become important options for resolving the above-mentioned problems. By efficiently and skillfully incorporating these new technologies into high-efficiency mixing/separation reactors, the innovative refining process will be established in the early 21st century."

Jan 1, 2000

By G. Springer

The identification of lost mineral values in mill tailings frequently requires the inspection of hundreds of thousands to millions of particles. The search of these particles can be made automatic by using an electron microprobe. A standard instrument (Cambridge Mark V) was modified by the addition of stepping motors to advance the specimen stage in a controlled manner. The X-ray Signal is monitored continuously by a computer interfaced to the instrument with an analog-to-digital converter. 400,000 particles of a tailings sample can be scanned in about 3 hours. Particles as small as 2 um and containing as little as 3% of a particular element can be detected.

Jan 1, 1982

By R. J. Mitchell

Results from investigations into impurity distributions over cathodes are presented with implications for various sampling methods, Selection of an optimum treatment procedure for the test sample is outlined. The impact of both these studies on the development of an in-house method for sampling Isa Process cathode is discussed. The economic compromise actually undertaken, satifying wants and needs to sustain confidence in high grade cathode purity is detailed.

Jan 1, 1987

By R. W. Bartlett

A two step process for treating platinum group metal flotation concentrates Is described while experimental results. The process was designed to be simple and Inexpensive While yielding a high recovery and fast turnaround. Ii consists of electric furnace smelting of concentrate to remove gangue and produce a homogeneous sulfide matte containing all of the base metals and platinum group metals. Sulfide oxidation Is minimized during smelting to avoid Installing an acid plant In the second step, matte Is pressure-leached with oxygen In an acid sulfate system to dissolve Iron, nickel, ?and copper while leaving a residue highly concentrated In precious metals, and typically about 1% of the flotation concentrate mass, A batch process with oxygen titration against the base metal composition of the feed Is used to control the end point of the leach. Sulfides must be eliminated while minimizing the precipitation of hydrolysis products. The leach residue can be smelled to bullion to facilitate sampling accuracy.

Jan 1, 1989

By Evan O. Jones

Processes involving distillation under reduced pressure were developed at the Pacific Northwest Laboratory several years ago to recover spent acid solutions generated during the manufacture of nuclear fuel for the N-Reactor at the Hanford site. Following construction and testing of a pilot-plant, the technology was licensed to Viatec Recovery Systems, Inc. for commercialization. The technology developed included specialized distillation and rectification of volatile acids, removal of water and/or volatile acid from sulfuric acid, and precipitation of salts. A key feature of the Waste Acid Detoxification and Reclamation (WADR) technology is the development and use of advanced thermoplastic and fluoropolymer materials of construction in all critical process equipment. The technology was then expanded to include crystallization to recover metal salts for possible reuse. Economic and environmental advantages of the procedures include recovery of acids for reuse, simplification or elimination of the disposal of waste solutions, and possible recovery of metals. Industries expected to benefit from such applications include galvanizing, electroplating, sand leaching and any where metals are cleaned in acid solutions. Currently a modular system has been assembled for recovery of several different spent acid solutions.

Jan 1, 1995

By Seshadri Seetharuman

The present paper summarises a series of measurements of the interaction parameter of oxygen in liquid copper with respect to a third element, e(M)o, where M is Mn, Zn, As, Se or Te which are common impurities in the liquid metal. The technique employed was the solid electrolyte galvanic cell method. The cell used may be represented as Pt, W or cermet / Cu-O-M // ZrO2 - CaO // AO, A /PT where AO/A represents a suitable oxide/metal reference. The measurements indicate that Mn and Zn interact very strongly with oxygen in liquid copper while, in the case of arsenic the interaction parameter is nearly zero. The behaviour of the elements Se and Te is unique with respect to oxygen interactions in copper bath. At oxygen levels, xo= 10-4 ? 10-5, the apparent interaction parameters are negative, comparable to that for sulphur. On the other hand, at lower oxygen levels, the results indicate that the interaction parameter values are positive. The results are discussed in the light of some of the theoretical models for solute interactions in liquid metals.

Jan 1, 1993

By Z. Zhang, Cuihuan Huang, Zongshu Zou, Nan Wang, Xueqian Xin

"Vitrification is considered as an attractive procedure for municipal solid waste incineration ash, which can realize the volume reduction and innocent treatment of incineration ash, as well as reuse of bottom ash. The main oxide components of molten ash slag are CaO, Al2O3, SiO2, Fe2O3, MgO, and Na2O, accounting for more than 90% of the total mass. The phase relations and thermodynamic properties of the CaO-Al2O3-SiO2-FeOx-MgO-Na2O oxide system is highly required, and is of great scientific significance for optimization of vitrification processing and sustainable resource utilization of melting slag. A study on the equilibria phase relations of CaO-SiO2-MgO-FeOx system was done by using CALPHAD method based on FactSage in this paper. The modeling parameters for the thermodynamic properties of liquid phase in CaO-SiO2-MgO-FeOx system were established and the equilibrium phase relations of MgO-SiO2-FeOx and CaO-SiO2-FeOx-MgO systems were calculated for different temperatures and oxygen partial pressures.IntroductionThe main oxide components of vitrified bottom ash slag are CaO, Al2O3, SiO2, Fe2O3, MgO, and Na2O, accounting for more than 90% of the bottom ash by weight [1]. During slag processing and modification, the knowledge of thermodynamic properties and liquidus temperature in the related slag system is highly required [2-5], which is not yet available. Through literature survey [6-9], it is clear that the systematic information on the concerned complex slag system is scarce. Most binary subsystems except FeOx-Na2O have been investigated well. Among ternary subsystems, few phase relations of the Na2O-MgO-SiO2 ternary system are available. For the phase relations of the system Na2O-MgO-Al2O3, all the studies are focused on the Al2O3-rich region. Investigation on the CaO-Al2O3-FeOx system is limited to Fe2O3-containing system with relatively higher oxygen potential. Most quaternary systems are not studied well except the CaO-MgO-Al2O3-SiO2 system, mainly due to their metallurgical importance. Figure 1 demonstrates the research status of the vitrified bottom ash slag with almost zero effort [10]. The effort here is defined based on the published literature by considering the number of publications, the investigated composition ranges, and the research details. So far the engineers in the field have to make assumptions of the thermodynamic properties of the simplified oxide system, without taking into consideration the interactions of the different oxide components, which hinders the development of the slag valorization and utilization. In order to provide thermodynamic properties for the application of the vitrified bottom ash, the six-component oxide system (CaO-MgO-Al2O3-SiO2-FeOx-Na2O) will be investigated through both experimental approach and computer modeling."

Jan 1, 2011

Designing rigging systems for complex castings has been more of an art than a science. Foundrymen have used thumb rules based on past experience to develop working designs. Of late, attempts are being made to formalize the procedure through the use of rule based expert systems, process modeling and other tools. Designing risers is one of the challenges of the rigging system design. Once the riser location have been determined, an optimization technique coupled with a casting simulation code can be used to determine the optimum riser dimensions. The main drawback of using a finite element or a finite difference based process simulation code along with the optimization routine is that the computation time involved is too large. Such an approach, thus, is unrealistic for practical situations where different options have to be explored and conclusions drawn in a short period of time. This difficulty has been avoided in the present work. The optimization scheme has been coupled with a modulus based solution routine to optimize the riser dimensions. The modulus calculations provide a good and quick estimate of the freezing time at different points in the casting. A functional, obtained from these freezing time values, is minimized by altering the dimensions of the riser until an optimum shape is obtained. Some examples have been included to illustrate the utility of this technique.

Jan 1, 1994