By Satu Strömberg

Four different nickel concentrates were oxidized in a laboratory scale laminar flow furnace in simulated flash smelting conditions. The major nickel- and iron-bearing minerals in the con- centrates were pentlandite, violarite, gersdorffite, and pyrite and pyrrhotite, respectively. Thermal decomposition, ignition and oxidation behavior of nickel and iron sulfides were examined by using optical and scanning electron microscopy. General reactivity of the concentrates was monitored with sulfur removal which was most effective in violarite-based concentrate. Pentlandite-concentrates needed higher experimental temperatures for complete desulfurization and gersdorffite-based concentrate contained 5 - 10 % of the original sulfur even in the most oxidizing conditions studied (1 100°C, 50 vol-% 02). The reactivity of the iron minerals was found to depend on the other minerals present in the concentrate. In this paper, the observed re- action products and mineralogical changes are presented and preliminary conclusions of possible reaction mechanisms of nickel-bearing minerals are discussed.

Jan 1, 1997

By Mukesh Jain

The liquor from potroom wet scrubbers is treated with lime to precipitate the soluble fluorides. The solids after filtration, referred to as scrubber mud, contain in addition to calcium fluoride, alumina, carbon, tars including polyaromatic hydrocarbons (PAH), cryolite and pachnolite and are considered hazardous. This communication deals with the pilot plant scale calcination of scrubber mud with a rotary kiln to obtain non-hazardous fluoride raw materials. Air classification was performed to separate the mudinto aluminarich andcalcium fluoride rich fractions which were then calcined. With proper control of calcination parameters and addition of lime, the carbon and tars were destroyed and hydrogen fluoride emissions were controlled. The calcined products could be used in the steel indusny as a fluxing agent or as a substitute for fluorspar in the production of aluminum fluoride.

Jan 1, 1994

By Daniel Adolfsson, Ryan Robinson, Fenwei Su, Jelena Blagojevic

"Cold bonded briquetting of steel plant by-products has proven to be a viable recycling alternative concerning technology, economy and environment in both the traditional blast furnace route and the direct reduction process. A critical parameter in cold bonded briquettes is the type and amount of binder used during production. The binder material must meet certain quality requirements concerning low and high temperature strength, chemistry and economy. Currently, SSAB Tunnplåt uses ordinary Portland cement (OPC) as binder in their cold bonded briquettes. In order to improve binder quality and possibly decrease OPC dependency, a binder feasibility study has been conducted concerning an internal by-product, ladle slag, as a supplement and/or partial substitute for OPC. Several characterization techniques have been used to study the behaviour of ladle slag, these include: XRD, XRF, SEM, glass content analysis, calorimetric analysis, particle size distribution and thermochemical stability considerations concerning the CaO-Al2O3-SiO2 system.IntroductionRecently, a project was initiated at SSAB Tunnplåt AB, in Sweden, which aimed at reducing the amount of ordinary Portland cement (OPC) as hydraulic binder in cold bonded briquettes by partly replacing it with ladle slag. OPC is traditionally used within civil engineering, and widely accepted as a hydraulic binder in a number of different applications. OPC consists of four major crystalline phases, i.e. C3S, C2S, C3A and C4AF. Tricalcium aluminate as well as the ferrite phase in OPC reacts very quickly with water, for this reason gypsum is added to the clinker in order to retard these reactions. The fact that gypsum is present in the system limits the recycling of briquettes to the BOF, since the presence of gypsum during steelmaking results in a significant amount of sulphur emissions. The latter along with the expense that follows, makes it worthwhile to consider alternatives for OPC as binder in cold bonded briquettes."

Jan 1, 2008

By V. Madhusudhan Rao

Fly ash is a finely divide non ? combustible material obtained as a by ? product of coal combustion. It is a major by ? product of coal based thermal power stations. Until recent past it was considered as a waste and highly polluting material. However its formation can only be minimized by using suitable technology in the boilers. In recent past it is found that Fly ash has many end uses and it has proven itself to be a potential construction material. But the suitability of fly ash for various applications largely depends on the amount of unburned carbon, which is turn depends on the firing method. Fly ash samples from various power plants existing in India using a fluidized bed method and pulverized bed were analyzed and a comparison of these two firing methods was carried. This paper deals with the compositional requirements for fly ash used for the fabrication of insulating doors using AAC (Aerated Autoclave Concrete) and the methods employed to make fly ash suitable for this purpose. It also includes the latest ?U? beam technology for effective fly ash recycle. If the by products of coal combustion from power plants like fly ash as the paper stresses are utilized properly, it is not an exaggeration to say that power generation is possible with absolutely zero cost.

Jan 1, 2006

By James C. Sever

Two green field magnesium reduction plants are under consideration using dolomite as the raw material. The Calix calciner was independently selected for both plants. The unique design of this calciner is detailed and the advantages defined for the specific application. The low carbon foot print of this unit combined with the ability to capture food grade carbon dioxide makes this an environmentally proactive approach to carboniferous ore calcination.

Jan 1, 2015

By Kenneth N. Han

Ammonia has been found to be an effective leaching reagent for gold, silver and platinum group metals in the presence of appropriate oxidants. Electrochemical and kinetic aspects of the dissolution of elemental gold in ammoniacal solutions have been investigated. The cathodic reaction of aurous di-ammine on the gold cathode has been investigated first. From this investigation, the standard electro-potential of the cathodic reaction .and hence. the Gibbs free energy of formation of the aurous di-ammine were established. The solubility of gold in ammoniacal solutions was also examined in relation to ammonia concentration, temperature and concentration of various oxidants. The anodic reaction of the gold disk in ammonia? in the presence? of various oxidants including oxygen, ozon, hypochlorite, hydrogen peroxide, cupric and cobaltic ammine, and iodine was also examined and the results have been discussed. Excellent dissolution yielding of gold and many other metals, typically better than 95% recovery in 1'-2 'hours of leaching at a temperature ranging 80°C to 190°C has been observed. Test results of the dissolution of gold from elemental state as well as other sources including sulfidic ores and scrap are presented.

Jan 1, 1998

By F. J. Arriagada

Where gold is present in a finely disseminated form within sulfide particles, the porosity and surface area of the calcined material strongly influence leaching since they control the penetration of solution inside the gold-bearing grains. On the basis of a stability diagram for the Fe-O-S in the temperature range of 400 to 750aC, the expected sequence chemical transformations associated with the oxidation of pyrite is discus-sed. By using analytical techniques which include scanning electron microscopy, X-ray diffraction and BET gas adsorption, the chemical and structural changes experienced by auriferous pyrite-arsenopyrite concentrates and pure pyrite samples are studied under an oxidizing roasting atmosphere of com-position 80% N + 20% O2 in the temperature range of 450 to 750°C. The results indicate that as the roasting temperature increases, the surface area of the calcines decreases sharply after a maximum value attained at about 450-500°C. SEM micrographs show that the needle-shaped tips which characterize the surface of the oxide product become wider and the size of the pores between them is decreased when the roasting temperature is in-creased from 550 to 750°C. This effect suggests that the formation of a more "closed" hematite product at higher temperatures is due to sintering associated with a faster growth and crystallization of the oxide. A strong correlation is shown between increasing roasting temperature and increase in gold lost in cyanidation tailings, an effect which may be partly attributed to the loss in surface area of the calcines.

Jan 1, 1982

By Carlos Antonio da Silva

Steel refining reactors based on chemical heating are being used as an alternative to ladle furnaces, They show a high degree of flexibility in respect to heating rate in addition to carrying out refining reactions such as de-S, inclusion removal, alloying etc. IR-UT and CAS-OB are examples of such reactors. Their performance is dependent upon geometrical characteristics as well as operational conditions which determine the flow field inside the vessel. A physical model of the IR-UT process of the Companhia Siderúrgica de Tubarão, steel plant located in Serra, Espirito Santo, Brazil, was developed to assess the features of the flow field and its influence on the metallurgical behavior. Results of the physical model were used to optimize the process parameters in the industrial unit.

Jan 1, 2003

By Carlos Antonio da Silva

Steel refining reactors based on chemical heating are being used as an alternative to ladle furnaces. They show a high degree of flexibility in respect to heating rate in addition to carrying out refining reactions such as de-S, inclusion removal, alloying etc. IR-UT and CAS-DB are examples of such reactors. Their performance is dependent upon geometrical characteristics as well as operational conditions which determine the flow field inside the vessel. A physical model of the IR-UT process of the Companhia Siderurgica de Tubarao, steel plant located in Serra, Espirito Santo, Brazil, was developed to assess the features of the flow field and its influence on the metallurgical behavior. Results of the physical model were used to optimize the process parameters in the industrial unit.

Jan 1, 2003

By Donghai Li, Cheng Pan, Xuewei Lv, Mei Liu, Enguang Guo

"Phosphorite is the main raw material for the production of phosphorus in chemical industry. More attentions have been drawn to the phosphorite concentrate beneficiated from low-grade phosphorite due to the decrease of high-grade phosphorite. For another, the agglomeration process is necessary for the phosphorite concentrate after beneficiation process. The mineralogy and sintering process of the phosphorite from Leshan, China were studied in this work. The result shows that the main phases in the phosphorite are fluorapatite (Ca3(P04)3F), hydroxylapatite (Cas(P04)3(0H)), quartz (Si02) and dolomite (CaMg(C03)2). The yield of the sinter increases with increasing the carbon dosage to 7%, and then decreases when it continuously increases. Similar regularities were found for the strength and the content of P20s of the sinter. The best strength of the sinter as well as its P205 content were discovered when the carbon dosage is 7%. Fluorapatite ((Ca5(P04)3)F) is the main phase in the sinter while fuggerite (Ca2MgSiz01) is the main binder phase.IntroductionPhosphorus is an important foundation industrial raw material of national defense industry, food industry and chemical industry, where it is used to produce red phosphorus, phosphonium hydroxide, phosphorus pentasulfide and phosphoric anhydride[l-2]."

Jan 1, 2013

By D. A. Horne, V. R. Daiga

Certain steel mill wastes contain significant amounts of zinc oxide due to the use of galvanized scrap during the steel making process. Typically electric arc furnace (EAF), and basic oxygen process (BOP) flue dusts contain 20 to 30% zinc oxide and 40 to 50% iron oxides, along with smaller quantities of lead and cadmium. These materials can be recovered from the flue dusts by using a proven rotary hearth furnace (RHF) process. By-products of the recycling operation include a crude zinc oxide fume, which is captured in a baghouse filtering system, and sponge iron that may be recycled into the steel making operation. Crude zinc oxide properties plus the operating experience from two commercial RHF installations utilizing MR&E's DRyIron™ Process will be presented.

Jan 1, 2000

By Aiyuan Ma, Tu Hu, Chenyu Sun, Yonggang Zuo, Hongying Xia, Jinhui Peng, Libo Zhang, Yongguang Luo

"In this study, the adsorption characteristics of tannin acid in aqueous solution were investigated using regenerated activated carbon (AC), with the aim to remove the tannin acid organic matter from the solution after zinc hydrometallurgy and Ge precipitation. Results showed the temperature has little effect on the adsorption ability (q.) of the regenerated activated carbon. The experimental equilibrium data were tested for the Langmuir and Freundlich isotherms. The adsorption equilibrium was better described by the Langmuir isotherm (R2 > 0.99). Pseudo first- and second-order kinetic models were used for describing kinetic data. It was determined that the kinetics of tannin acid removal was well fitted by second-order reaction.IntroductionGermanium recovery is a complex processes [1]. Hydrometallurgical processes are favoured and these are based on the precipitation of germanium as hydroxide or sulphide or alternately with tannic acid [2]. However, in the germanium recovery process, too much tannin is consumed by the germanium-tannins complexation process, and results in a high content of tannic acid remaining in solution, which is harmful to the valuable metal recovery [3]."

Jan 1, 2014

By T. Ranki-Kilpinen

In the flash smelting technique, developed by Outokumpu Oyj, off-gases with dust load are directed into the heat recovery boiler (HRB). As the temperature decreases, metallic sulphates become thermodynamically stable. Sulphation of oxidic particles initiates. The release of heat causes an increase in particle temperatures, and soft sulphated particles can stick to the heat transfer surfaces. Dust accretion may form and cause operational problems. The objectives of the project are to study sulphation reaction mechanisms and kinetics of flue- dust particles under HRB conditions, and get more information for the flue-dust treatment possibilities. The sulphation behaviour of synthetic Cu2O particles (37-53 pm) was studied using a fluid-bed reactor of laboratory scale. The experimental parameters in the latest campaign were oxygen and sulphur dioxide contents of 2.5-10 vol-% 02 and 40-60 vol-% SO2 respectively and temperatures of 600-660°C. Samples were examined microscopically (SEM+EDS) and chemical analysis were conducted. The sulphation rate was found to have a maximum at the certain temperature, which was dependent on the gas SO2 content. Regardless of the level of SO2, a rise in oxygen content promoted sulphate formation.

Jan 1, 2002

By I. Ohnaka

Although many works have been reported on the semisolid casting, the mold filling behavior of semi-solid alloys has not been so well understood. This paper compares the physical and numerical simulation results on the mold filling behavior. Physical simulation was performed by using solid-water mixture. The numerical simulation was made under the assumption of one phase flow with an effective viscosity. It was found that the solid particles stabilize the flow greatly if the kaction solid exceeds about 0.4, because viscosity increases greatly. The overall flow behavior can be estimated by the numerical simulation. Interesting flow behavior was also found which can not be observed in the case of one phase flow and which is difficult to simulate by the one phase flow assumption.

Jan 1, 1997

By Guiming Yang, Xiaoxian Huang, Zhiyun Ji, Min Gan, Lishun Yuan, Xiaohui Fan, Zhiyuan Yu

"The roasting characteristics of hematite pellets containing MgO were studied where magnesia powder, serpentine and magnesite were used as magnesium-additives respectively. The mechanical strength of both preheated and roasted pellets decreased when MgO content increased, which implied the addition of MgO had an adverse effect on pellet consolidation. By adding flux containing CaO, the mechanical strength of both preheated and roasted pellets were improved. The addition of calcium flux facilitated the formation of calcium ferrite and provided a certain amount of liquid phase, resulting in faster diffusion ofMg2+ and Fe3+. The result showed that diffusing speed of Mg2+ was enhanced by 1.48 times, and rate constant of Fe203 crystalline growth was enhanced by 62% when basicity was around 0.4. Improvement of mineralization degree and recrystallization of Fe203 assisted in consolidation of hematite pellets containing MgO.IntroductionOxidized pellets are ideal iron-bearing burdens in blast furnace. At present, magnetite is the main raw material for oxidized pellet production in China. However, as the rapid development of iron and steel industry, resources of magnetite have been depleted and cannot satisfy the requirement of pellet production. Using hematite concentrates to produce oxidized pellets has become a trend [1, 2]. Many pellet enterprises abroad nowadays have adopted high proportions of hematite concentrates when producing oxidized pellets, e.g. the percentage is 100% in a lot of Brazilian factories [3, 4]. But high proportion of hematite concentrates will lead to low mechanical strength and high reduction swelling index of pellets. Some studies show that Mg-bearing pellets have excellent metallurgical properties, and the reduction swelling phenomenon can be solved by adding fluxes containing MgO [5, 7]. However, there are problems such as low pellet strength and bad roasting characteristics for MgO-bearing pellets, which remains an obstacle in pellet industry. Hence, it's vital to undertake the study on strengthening measures for indurations of Mg-bearing hematite pellets."

Jan 1, 2013

By Wei Yu, Tiejun Chun, Jian Pan, Deqing Zhu

In this paper, improving the pelletization of Brazilian hematite by adding a boron bearing additive was carried out, and the pelletization parameters were also optimized. The mechanism of boron bearing additive was revealed in the kinetics of crystal grain growth by using LEICA microscopy and its software to measure hematite grain growth. Good qualities of green balls are manufactured with drop numbers above 5.7 times/0.5m, compressive strength higher than 13 N/pellet and thermal shock temperature over 620? under the following conditions: 1.2wt% bentonite, 0.4wt% boron bearing additive, 7wt% moisture and pelletizing in disc for 15 min. When the green balls were preheated at 1000? for 8 min and fired at 1280? for 15 min, the compressive strength of the fired pellets containing boron bearing additive is about 3096 N/pellet, which is far beyond the standard requirement for good quality pellets. Compared to the fired pellets without adding any boron bearing additives, the compressive strength of fired pellets containing boron bearing additive is increased by 1225 N/pellet. It is revealed that adding boron additive into the hematite pellets help to form more liquid phases, lower the activation energy of the hematite grain growth by 135.2 kJ/mol and increase grain growth rate by 33.6%, leading to higher strength of fired pellets due to forming more coarse and dense recrystallized hematite and energy saving by firing at lower temperatures for shorten time.

Jan 1, 2011

By Qiang Zhong, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

Viscosity of slag determines the production efficiency, energy consumption and distribution of elements between metal and slag, which is very important for pyrometallurgy. Slag of goldantimony ore blast furnace smelting has seldom been studied. In this paper, the viscosities of gold-antimony ore smelting slags of different composition have been studied by the rotating cylinder method. The results showed that, for a slag of 38.95% SiO2, 16.17% CaO, 25.97% FeO, 10.25% Al2O3, 5.17% MgO, the viscosity can be decreased by reducing 3.24%-8.5% SiO2 or increasing 3.31%-9.56% CaO content. Complex SixOy z- from SiO2 acts as the main cause for the high viscosity in a slag of high SiO2. The increasing of CaO causes the decreasing of the amount of SixOy z- and the O2- dissociated from CaO breaks the complex SixOy z-, which can decrease the viscosity. Viscosity of different composition slag in the appropriate range temperature can be calculated from the Arrhenius equation.

Jan 1, 2015

By Filipe de Menezes Torres, Augusto Pereira de Sa, Itavahn Alves da Silva, Eliana Ferreira Rodrigues, Carlos Antonio da Silva, Varadarajan Seshadri

Top slag eye opening which happens as a result of gas injection is a function of the gas flow rate in addition to other factors such as ladle geometry, porous plug location as well as slag properties. Slag eye opening leads to entrapment of atmospheric nitrogen, oxygen by the steel melt affecting adversely the steel quality. In this work aspects of mixing and eye formation in steel making ladles with inert gas injection have been analyzed through physical and mathematical modeling techniques. Influence of ladle, gas flow rate and distribution and slag properties has been assessed. A correlation for estimating eye opening has been developed. Results from PIV measurements and images of eye opening obtained using a camera have been utilized to validate results from CFD simulation.

Jan 1, 2015

By Sang-Beom Lee

For thermodynamic prediction, the deoxidation equilibrium of aluminum in Fe-36%Ni alloy was studied with a cold crucible under Ar gas atmosphere at 1773K. For the deoxidation reaction in liquid Fe-36%Ni base, i.e.: A12O3(s) = 2A1 + 3O The interaction parameters and the equilibrium constant between aluminum and oxygen in liquid Fe-36%Ni alloy are given in the following: eo Al = -3.8, roA1=0.9, eAl° = -6.4, rAl° = 700, rAIAIo = 3.1, roA1o = 833 within the composition range of [Al] < 1 mass%. The temperature dependence of the equilibrium constant was obtained in the range of 1773K < T < 1973K by using reported data and present results as follows: log KAo= 0.58-24463.7 / T The deoxidation equilibrium with aluminum in Fe-36%Ni could be thermodynamically well described in the range up [Al] < 1 mass% with first and second order interaction parameters as well as the equilibrium constant determined in this study.

Jan 1, 2002

By Jilai Xue, Jun Zhu, Baisong Li

"TiB2-C/C Function Gradient Materials (FGM) is used in cathode materials to improve aluminum wettability and melt penetration in aluminum electrolysis. In this investigation, FGM was tested for use as part of the cathode materials, where a 10 mm thick TiB2-rich layer was on the top as an Al-wettable surface, the TiB2-C layers in the middle as a gradient layer and the carbon on the bottom as a base. Electrical resistances ofFGM were determined in the temperature range of25- 9600C in argon atmosphere. The results show that the present of TiB2-C gradient layer can reduce the open porosity and the electrical resistance of the cathodes materials at elevated temperatures. The cathode samples after aluminum electrolysis usually demonstrates an increase in electrical resistance, but the application of FGM layer can compensate such an increase for certain extend due to less variation in porosity and lower the level of melts penetration.IntroductionCarbon is still used for aluminum reduction cathodes dominantly, but it has a poor wetting properties by liquid aluminum and the anode-cathode distance has to be kept about 4-5cm with an additional 1.3-2.0 V voltage drop [l]. TiB2 has better wettability by liquid aluminum with higher electrical conductivity and stronger chemical resistance to the electrolyte attack. And the wettability ofTiB2-C composites cathode on liquid aluminum can be also improved, while liquid aluminum can completely wet the cathode surface ifTiB2 content exceeds 27% [2-4]. However, during the process of TiB2-C composites cathodes preparation and aluminum electrolysis, the deformation by temperature variation or sodium penetration are great disparity between TiB2 and carbon due to their physical properties difference. This will accelerate the cathodes cracking and deterioration."

Jan 1, 2013