Search Documents

By Huimin Lu, Min Li, Jinghua Zou

"Zeolitic imidazolate frameworks (ZIFs) are new type of porous materials, form inerratic polyhedral in three-dimensional with large cages and small apertures, and appear structural diversity. Their hole size can be adjusted. These materials have high selective adsorption capacity to carbon dioxide. In this paper, zeolitic imidazolate frameworks were synthesized by solvothermal synthesis method with dimethylformamide (DMF) as solvent and structuredirecting agent, divalent metallic ions as cation, and imidazole as ligand. The crystals were characterized with XRD, SEM for their crystal structures and physical properties, the adsorption of the crystals for carbon dioxide was also tested, and the result suggests that these porous materials have a capacity of 1.35ml/g for storing carbon dioxide at 273 Kelvin under ambient pressure.IntroductionGlobal warming caused by the increase of carbon dioxide in the atmosphere has become one of the main environment problems, contemporary research has focused on ways to slow or stop this trend. CO2 capture has attracted attention due to the potential to trap and sequester large amounts of CO2 from concentrated sources such as power plants [1]. Traditional technologies in capturing CO2 include absorption by aqueous amines [2]. However, utilization of this process is energy intensive and expensive. Carbon dioxide storage materials investigated so far can be divided into two categories: chemical storage adsorbents and physical storage media [3]. The first kind of materials can chemically adsorb carbon dioxide within their structures and need thermal energy to release the adsorbed carbon dioxide. The examples of the chemical adsorbents include aqueous amines, gas-hyperbranched aminosilicas [4]. The physical adsorbents store carbon dioxide by physical adsorption of carbon dioxide at elevated pressure and release the adsorbed carbon dioxide at low pressure. The physical adsorbents that have been investigated for carbon dioxide storage include zeolites, carbonaceous materials and other porous materials. Until recently, a new type of microporous material, known as zeolitic imidazolate frameworks (ZIFs), has been reported as promising adsorbents for carbon dioxide storage [5 ~ 10]."

Jan 1, 2010

By D. M. Dabbs

A static dew point technique has been used to evaluate the solubility of arsenic in ?slag and its dependency on P02 at temperatures of 1458 and 1523K. The ferrous-ferric ion ratio of the slags ranged from 3.9 to 23.8. These values correspond to partial pressures of 02 ranging from 10-8 to 10-12 atm. The solubility of arsenic in slag was found to be independent of? P02? The data indicate that elemental arsenic exists in silicate ?slags. This result was further substantiated by mass .spectrometric analysis of doped slag specimens.

Jan 1, 1983

By Zhang Hanbo, Niu Liping, Zhang Zhiqi, He Jicheng, Dou Zhihe

"Rutile, ilmenite and Al-Ca complex reducer were used to prepare high titanium ferrous alloy by enhanced reduction-SHS method. The effects of the complex reducer compositions and slag types on the enhanced reduction-SHS process were investigated. The high titanium ferrous alloys were characterized by XRD and SEM. The results indicate that the high titanium ferrous alloys consist mainly of TiFe2, AlTi3 and Al2O3. The oxide inclusions exist resulting in directly the high oxygen content and micro-structural defects in the alloys. The titanium and oxygen contents decrease, but the aluminum content in the alloy increases while the mass ratio of calcium in the Al-Ca complex reducers increases. When the mass ratio of Al/Ca in the Al-Ca complex reducer is 6:1, titanium, oxygen and aluminum contents are 63.75%, 3.01% and 10.72% respectively. When the mass ratio of Al/Ca is 5:1 titanium content is 55.00% nearly and aluminum content is higher than 14.00%, but oxygen content is lower than 2.0%.1. IntroductionThe high titanium ferroalloys with 65%~75% titanium have the advantages of low melting point and high titanium content. They are widely used in special steel refining, while they are also a kind of very important quality orientation alloys in the rage of aviation and aerospace. At present, the methods of preparing high titanium ferroalloy include vacuum remelting and thermit reduction. The alloys prepared by the vacuum remelting method have good qualities and low oxygen content, so it is widely used in Russia, Western Europe and other developed countries. In China, there are abundant rutile resources, but waste titanium is lack, therefore, the preparation method is the thermit reduction. But there are many quality defects in the high ferrotitanium alloy, including high oxygen content, unstable quality and so on. In order to improve the qualities of the high titanium ferroalloy, especially to reduce oxygen content, the domestic and overseas have done a lot of further researches. For example, Sichuan E-mei ferroalloy plant and Beijing Nonferrous Metal Research Institute have prepared high titanium ferrous with 73.77% titanium with natural rutile, but the oxygen content is high. Through controlling the quality of raw material, they obtained the better qualities, but the oxygen content is still very high. South Africa Mintek company have prepared high titanium ferrous alloy with low nitrate by plasma heating under the isolation air conditions, but they couldn’t also remove effectively oxygen in the alloy. The oxygen exists in the form of Al2O3 and titanium protoxide. So it can be speculated that except TiO2 not being fully reduced, the no-sufficient alloy-slag separation is the direct reason resulting in high oxygen and poor microstructure. In view of present technical difficulties during preparing high titanium ferroalloy by thermit reduction, this paper proposed a new method of preparing high titanium ferrous with low oxygen by enhanced reduction-SHS with Al-Ca complex reducer. Ca in Al-Ca complex reducer has stronger reductive ability, it can effectively strengthen the reductive degree of TiO2. The slagging agent CaO CaF2 and MgO can effectively reduce the viscosity of Al2O3 slag to improve its liquidities to strengthen alloy-slag separation effects so that to remove inclusions and oxygen. In this paper, effects of slagging agent type on the reduction and the qualities of high-titanium ferroalloy were studied."

Jan 1, 2012

By Varadarajan Seshadri

A physical model based on similarity principles was constructed for simulating the RH degasser of CST (Companhia Siderurgica Tubarao, Vitoria, ES, Brazil) to evaluate the circulation rate of the metal which essentially defines the degree of exposure of the metal to vacuum in the chamber and thus of the refining rate. The circulation rate on the other hand will influence the decarburization rate and removal of dissolved gases like nitrogen and hence it is essential to optimise this parameter to get maximum refining efficiency with minimum refming times, thus improving the productivity of the secondary refining process. Mixing characteristics in the ladle is evaluated by pulse tracer addition using conductivity-meters located at the down leg as well as at several locations in the ladle. The influence of gas injection through nozzles in the upleg with simultaneous bottom injection of gas as well as nozzle blockage on the circulation rates were investigated. Also simulation experiments of kinetics of decarburization were carried out using C02 adsorption-desorption process in sodium hydroxide solution as circulating fluid and the effect of, bottom gas flow rate in this case was also evaluated. The results were carried over to prototype and to optimize the process.

Jan 1, 2003

By Jun Li, Lin Chen, Tian-zu Yang, Wei-feng Liu, Wan-da Bin

"The Chinese bismuth production accounts for more than 80% all over the world in 2011. The main raw materials of bismuth smelting are bismuth concentrate and by-products of Cu or Pb smelting process. Many traditional methods of bismuth smelting in china was reviewed in this paper, such as reverberating furnace smelting, blast furnace smelting, fire-refining, ferric chloride leaching-hydrolysis, slurry electrolysis, and so on. But all the traditional pyrometallurgy or hydrometallurgy process have such shortages of low recovery, poor environment, and high cost. Therefore new technologies are introduced into the smelting process of bismuth concentrate, such as low-temperature alkaline smelting and side-blown bath smelting with oxygen-enrichment. These technologies have got great progress on energy saving, emission reduction, and friendly environment. Finally the development direction of new technology on bismuth smelting was prospected.IntroductionAs a green metal, bismuth has a wider applications, just extending from the traditional medicine, metallurgical-chemical engineering, low-melting alloys, solders, catalyst, and electronics to cosmetics, flame retardant, storage battery, semiconductor, supper conductor and nuclear energy etc[1,2,3,4,5,6,7]. This will increase the production of bismuth and promote the development and progress of bismuth smelting technology. At present, The major bismuth-product countries are China, Mexico, Peru, KZ, Bolivia and Canada etc, and China are dominating. A survey from the USGS[8] showed that Chinese bismuth production were 12,500 tonnes and got 80% of the world's in 2011. Thus the technology of Chinese bismuth smelting have a great representativeness."

Jan 1, 2013

By Ram V. Ramachandran

As an industry with major potential impacts (both good and bad) on water resources and due to the rising costs of process water, the mining and metallurgical processing industry has a key responsibility to contribute to the overall goal of preserving both the quantity and quality of water available within the watersheds they operate in. As we plan for new and existing mining and metallurgical projects, we need to consider a hierarchy of options to minimize our impact within the watersheds we operate; keeping clean water clean by diverting around our operations; reduction in the amount of water we use; reuse of water wherever possible, and improvements to water quality for recycling and/or release to environment. Technology is needed to treat water to improve its quality for reuse or release to the original watershed. While lime precipitation followed by sulfide polishing is effective for removal of most of the metals, it does little or nothing to remove ammonium ions and anions such as chloride, nitrate, molybdate, arsenate and selenite/selenite. Regulations on sulfate limits in treated discharge water has drawn close attention to the treatment of acid mine drainage (AMD). Management of brine and salt disposal is also posing a problem due to strict regulations and cost of disposal. This paper will: (a) address issues associated with managing water with the objective of maintaining water sheds—status quo-during and after operation (b) discuss potential technologies for advanced water treatment plants.

By M. Oliazadeh

Spodumene [LiAl(Si2O6)] is the most common and desirable economic lithium-bearing mineral due to its high lithium content. In Canada, there are several spodumene deposits at the development stage that have the potential to help narrow the forecast lithium supply gap stemming from the widespread acceptance and increasing use of electric vehicles. Spodumene processing can be conducted using Dense Media Separation (DMS), flotation or combination of both. If spodumene liberation is sufficient at coarse particle sizes, DMS can be used for primary lithium concentrate production and silicate gangue minerals rejection. If liberation is not sufficient, flotation is then the main processing route for spodumene concentration. Even in cases where DMS is a viable beneficiation option, flotation may still be required to process the DMS middlings and/or the undersize fraction which is outside the particle size range for DMS. Considering flotation as a technique for spodumene beneficiation, there are several alternatives including the use of mechanical flotation cells, column flotation cells, coarse particle flotation cells, and/or Staged Flotation Reactors (SFR), either alone or in combination. Ore sorting can be incorporated at the start of the spodumene flowsheet to remove gangue minerals, particularly amphibole and pyroxene in the early stages. The main objective of flowsheet development for hard rock lithium deposits is to evaluate the ability of these options to produce a spodumene concentrate with a concentrate grade above 6% Li2O, lithium recovery of above 80%, and with the minimum operating and capital cost. This paper aims to describe the various processing options available for the beneficiation of spodumene from hard rock deposits and compare the associated operating and capital costs for each.

By D. Papazoglou

This work was undertaken to investigate the thermodynamic and kinetic feasibility of using hot sulfur dioxide bearing gases from smelting processes to selectively sulfate the nickel in nickel laterite ores for subsequent extraction in water. The environmental benefits of this approach, as opposed to releasing the gas to the atmosphere, and the economic benefit of directly utilizing the SO2 rather than converting it to sulfuric acid are strong drivers for such a process. A thermodynamic analysis indicated that selective sulfation of the nickel could be feasible under appropriate conditions and these were explored through a series of laboratory scale experiments. Laterite samples were reacted at temperatures between 500 and 800°C with an equilibrated mixture of sulfur dioxide, oxygen and nitrogen in a fixed bed reactor. Tests were conducted on saprolitic ore from Bulong, Western Australia:, limonitic ore from New Caledonia and gamieritic ore from Indonesia. Nickel extractions were highest from the limonite and relatively low from the other ores. The maximum selective extraction of nickel from the limonite in a single stage sulfation was 73%. Sulfation of other elements present in the laterites was also examined. A two-stage process was also identified which involved sulfation using a strong sulfation potenrial followed by weaker sulfation potential to attempt to convert ferric sulfate formed in the first stage to ferric oxide. This increased the extraction for the limonite ore to around 84% Ni, 95% Co and 2% Fe. Direct sulfation of laterite could be feasible in locations where sulfide smelting or roasting operations are relatively close to laterite deposits.

Jan 1, 2003

By Torn H. Okabe

A fundamental study was conducted with the purpose of establishing an environmentally sound recovery process for recycling of valuable metals, by combining scraps containing such metals. As an example, direct extraction and recovery of neodymium (Nd) in magnet scraps was investigated by utilizing liquid metal as an extraction medium. It was found that liquid magnesium (Mg) is a suitable extraction medium and can extract Nd from iron alloys with high efficiency at around I 100 K. The newly developed extraction apparatus for Nd is a mechanically simple and static device without moving parts, where the Mg extraction medium circulates due to differences in the temperature inside the reaction vessel. This developed device can simultaneously accomplish continuous extraction of metal Nd from scraps, re-extraction of Mg from Mg-Nd alloy and the eventual recovery of pure Mg. As a result, metal Nd with 98 % purity was directly recovered from magnet scraps under certain conditions. It was also shown that the extraction agent Mg could be reused. The results of this investigation show the possibility of establishing a new process for the direct extraction of Nd in pure metal form without oxidization.

Jan 1, 2003

By Torn H. Okabe

A fundamental study was conducted with the purpose of establishing an environmentally sound recovery process for recycling of valuable metals, by combining scraps containing such metals. As an example, direct extraction and recovery of neodymium (Nd) in magnet scraps was investigated by utilizing liquid metal as an extraction medium. It was found that liquid magnesium (Mg) is a suitable extraction medium and can extract Nd from iron alloys with high efficiency at around 1100 K. The newly developed extraction apparatus for Nd is a mechanically simple and static device without moving parts, where the Mg extraction medium circulates due to differences in the temperature inside the reaction vessel. This developed device can simultaneously accomplish continuous extraction of metal Nd from scraps, re-extraction of Mg from Mg-Nd alloy and the eventual recovery of pure Mg. As a result, metal Nd with 98 % purity was directly recovered from magnet scraps under certain conditions. It was also shown that the extraction agent Mg could be reused. The results of this investigation show the possibility of establishing a new process for the direct extraction of Nd in pure metal form without oxidization.

Jan 1, 2003

By F. H. A. Abdalla

A process is described for the recovery of valuable nonferrous metals from steelmaking dust by suiphatizing roasting using ammonium sulphate. Maximum recoveries of soluble metal sulphates achieved at optimum conditions were> 99.0 %. Selective metal separation of the soluble sulphates in the leached liquors were performed either by controlling the roasting temperature or by adjustment the pH values of the leached liquor ranging from 3.6-6.2. Either pure zinc oxide orland tin oxide could be obtained at optimum conditions, and the products were evaluated chemically and by X-ray analyses. The residues rich in iron oxide can be removed and recycled. The mechanism of sulphatizing roasting process was considered. A general flow-sheet for the overall process of treatment the steel making dust to recover its valuable nonferrous metals was suggested, which ca be applied for other nonferrous bearing materials.

Jan 1, 1996

By G. S. Victorovich

Technical progress in primary smelting has changed the face of the copper industry in the years since the Second World War. Much of this change has resulted from a wide acceptance of flash smelting technology. In addition, research has been directed toward devising converting processes to replace conventional Peirce-Smith converting technology. One major thrust has involved a revival of the old " ", idea of oxygen flash converting of comminuted mattes. This paper reviews the 60-year history of flash converting. Particular attention is paid to Inco's investigations into the processing of white metal containing significant amounts of nickel and, in some cases, iron. Thermodynamic analysis and laboratory experimental results are presented which throw light on the behaviour of nickel and other salient features of flash converting. The possible role of oxygen flash converting in the copper pyrometallurgy of the future is briefly discussed vis-a-vis direct production of copper.

Jan 1, 1993

By John R. Goode

The fist part of this paper comprises a general discussion on refractory gold ores and their mineralogy. Processing methods now in use are reviewed and test procedures for the important methods are discussed. Factors determining the selection of a process are outlined. The paper includes a survey of production plants using pressure oxidation, roasting and biological oxidation to process refractory ore. The status of processes under development is briefly reviewed.

Jan 1, 1993

By Muammer Kaya, Sait Kursunoglu

"The aim of this study was to investigate the effectiveness of ascorbic (C6H8O6) / oxalic (C2H2O4) acid as a reductant for the simultaneous recovery of zinc and manganese from a spent and mixed zinc-carbon and alkaline battery powder in sulphuric acid leaching. The effects of sulfuric acid concentration, ascorbic/oxalic acid dosages, reaction temperature and leaching time on the zinc and manganese dissolutions were investigated according to 2k full factorial experimental design; then, a simple optimization study was carried out for the best reductant. The optimum reductive acid leaching conditions were determined at 3 hours leaching time, 70°C leaching temperature, 0.5M sulfuric acid concentration, 13 g/L ascorbic acid dosage, 1/20 g/mL solid/liquid ratio and 200 rpm stirring speed. Under these conditions, the dissolution efficiencies were 99.9% for Zn and 99.3% for Mn. When our results were compared with the previous results, our findings were better than previous studies.In addition, the manganese dissolution kinetics was undertaken, and the activation energy was found to be 7.04 kJ/mol. Selective precipitations of Zn and Mn from acid solutions were carried out using NaOH and KOH. Using 3M NaOH as precipitating agent at room temperature and at pH 8; 95.4% of Zn and at pH 10; 93.7% of Mn were precipitated from the leaching solution. Under the same conditions, using 3 M KOH at pH 8; 91.6% of Zn and at pH 10, 96.4% of Mn were precipitated. Based on the experimental results obtained, an appropriate flow sheet was proposed to recover zinc and manganese."

Jan 1, 2012

By P. D. Lee

The effect of strontium on porosity formation in aluminum-silicon alloys is not well understood and there is no consensus upon the cause of the effects observed. This paper describes a series of experiments where the effect of adding strontium on pore formation was observed directly with combination of a traditional temperature gradient stage and real time micro-focus radiography. These in situ observations provide a new insight into the effect of strontium on the nucleation and growth kinetics of porosity. The addition of strontium was found to have a minor effect on the growth of the pores in the mushy zone. However, strontium appeared to alter the nucleation and stability of hydrogen bubbles within the melt. The interaction of strontium with titanium-boride grain refiners produced an even stronger change in the nucleation and stability of the bubbles formed.

Jan 1, 2002

By John C. Taylor

With growing emphasis on energy conservation and increased concern over the presence of heavy metals in the environment, it is fortunate that most metals are readily recycled. In this respect, metals have a significant advantage over plastics and similar materials used as metal substitutes. For many years a secondary industry has processed scrap copper, nickel, lead and zinc to produce refined metal which has, to varying degrees, influenced the price and displaced the production of primary metal. This paper reviews some of the challenges the industry will face and the changes in process technology which will be required as pressure mounts to increase the amount of metal recycled. In the case of most base metals, this will have an impact on primary metal production; as the tonnage of metal recycled increases, the requirement for primary production, or new metal, will depend more and more on the growth in consumption.

Jan 1, 1993

By Eric Klaffenbach

Valorization of slag from metallurgical industrial processes becomes ever more important as this may help optimizing and reducing the use of natural resources such as rock and sand. In view of this objective, metallurgical processes have to be analyzed in order to modify the slag composition so that it will meet the expected requirements of potential users of these resources. This paper gives the results of a thermodynamic analysis of the flash smelting process to understand the impact of operational parameters on slag chemistry and elemental partitioning in the process. It is shown that an increase of the matte grade and temperature leads to higher deportment of Pb, Zn and As to the slag. With increasing matte grade the volatilization of these elements decreases. Furthermore, the results indicate an increasing solubility of Cu and S in slag at higher temperatures.

By Yasuhiro Konishi

Hydrolytic stripping is the process in which metal ions are simultaneously stripped from a loaded cation-exchange solvent extractant and precipitated as oxides or hydroxides. Hydrolytic stripping is usually effected by contacting the loaded organic phase with water at elevated temperatures. The possibility of using hydrolytic stripping to prepare ceramic powders with controlled size and morphology is now being evaluated for different systems, using carboxylic acid extractants. As part of this work, mathematical models were developed to describe the kinetics of nucleation and growth of nickel ferrite particles. This paper describes the development of the models, along with estimation of key parameters appearing in the rate equations from experimental data.

Jan 1, 1990

By V. I. Lakshmanan

The demand for elements such as nickel, cobalt, titanium and gold in various applications has increased significantly. Innovation to recover these elements now plays a major role in metallurgical processes as established technologies have challenges in treating the types of ores that are available while meeting the increasingly stricter environmental regulations. Alternative chloride based processes have been developed that can be used to recover the value elements from the available feed stocks with potentially lower environmental impact. Chloride-based hydrometallurgical processes have several advantages, including higher leachability of complex ores/tailings and relative stability of chloro-complexes of the metals. Process Research ORTECH Inc. (PRO) has developed mixed-chloride process flowsheets, where innovative solvent extraction process steps are used for the separation of nickel, cobalt, titanium and gold from their respective chloride solutions. This paper will discuss the potential aqueous chloro-chemistry of these metals and separation reaction mechanisms involved in the solvent extraction process.

By I. Gaballah

Jarosite contains up to 15 % of heavy metal compounds 'HMC'. The current waste disposal methods will not be allowed in the near future due to new environmental regulations and pollution risks. For these reasons, thermal treatments of raw or decomposed jarosite, in controlled atmospheres, were investigated. The aim of these treatments is to decontaminate the jarosite and/ or to recover the HMC for recycling. According to physico-chemical characteristics of the samples, the thermal treatments in controlled atmospheres N2, CO+N2 and C12+air lead to the extraction rate that vary from 93 to 98 %. Heavy metal compounds were separated by cooling the gaseous phase. The treatments' residue was almost free from HMC. Between 700 "C and 800 "C, the chlorinating treatment was successful of eliminating more than 97 % of HMC contained in four different samples.

Jan 1, 1999