By Wang Yun-yan

In order to examine the adaptability and the kinetics of leaching different gold ores in alkaline thiourea system, six kinds of gold concentrate and/or calcine with different physical and chemical properties were chosen as objects. The leaching behaviors in alkaline thiourea system with high stability, acidic thiourea system and alkaline cyanide system were compared. Changes of phase, surface appearance, particle distribution and specific surface area of six kinds of gold ores before and after leaching were studied in virtue of modern analytic techniques, e.g., XRD, SEM, and so on. The results indicate that alkaline thiourea solution can be used to leach gold ore, for oxidized gold concentrate removed arsenic by microbe pretreatment(4#) the leaching rate of gold is up to 82.68%, such conclusion overthrows the parlance reported that pH value must be less than 1.78, or gold can not dissolve in thiourea solution. Chemical components and phase are related to gold leaching rate, different gold ores are fit for different leaching system, and alkaline thiourea solution is suitable for the pretreated oxidized gold ores with low content of sulfur and in which the main phase was SiO2, phase almost does not change after leaching basically. Generally speaking, when leaching in alkaline thiourea solution, surfaces of gold ores with glaze change greatly to ones with coarseness, distinct trace and holes of corrosion. Particle size decrease and specific surface area increase of gold ores after leaching in alkaline thiourea solution with high stability except gold concentrate of Zhongyuan gold smelter(5#).

Jan 1, 2006

By C. J. Boreiko

Traditional patterns of lead and zinc utilization are being evaluated in accordance with new paradigms that seek to ensure the long-term compatibility of global industrial activity with precepts of sustainable development and sustainable consumption. As a consequence, both industry sectors are experiencing intense scrutiny from the international community, and numerous regulatory options are being considered that may impact upon international industry practice. This paper reviews the growing expectations being placed upon industry, and highlights some of the common regulatory concerns being expressed regarding both metals despite their differing toxicological profiles.

Jan 1, 2000

By N. M. S. Balbinot, A. L. Rodríguez, C. M. Mahlmann, R. de C. de S. Schneider

The use of sunflower oil co-products it was studied for production thermoplastic composites. Thermoplastic composites have been processed in polyethylene matrices of virgin linear low density polyethylene (LLDP) or recycled. Samples have been formulated with 10% mass fraction of sunflower bran, seed coat and mixture of bran and seed coat. The material characterization has been achieved by mechanical tensile test and Shore D hardness and by density physical testing. The results have demonstrated better properties to thermoplastic composites with sunflower seed coat.

Jan 1, 2008

By Sheng-hai Yang

The ultrafine, monodispersed, spherical cobalt powder has been fabricated by reducing cobalt hydroxide with glycol. It were investigated that the effect of NaOH concentration on the reaction rate and the effects of the concentration of cobalt hydroxide and surfactant on the morphology and particle size. The particles were characterized by the X-ray diffraction(XRD), scanning electron microscope(SEM), laser diffraction particle size analyzer and BET specific surface analyzer respectively. The XRD shows that the cobalt powders exist mostly in face centered cubic (fcc) structure, a little in simple hexagonal. The cobalt powders prepared at Co(OH)2150g/L, NaOH 40 g/L and surfactant 30g/L, its average particle size, specific surface area and cobalt content, were 0.88µm, 2.705m2/g. and more than 99.5% respectively.

Jan 1, 2006

By Peter Kong

This paper provides a general discussion of atmospheric-pressure plasma generation, processes, and applications. There are two distinct categories of atmospheric-pressure plasmas: thermal and nonthermal. Thermal atmospheric-pressure plasmas include those produced in high intensity arcs, plasma torches, or in high intensity, high frequency discharges. Although nonthermal plasmas are at room temperatures, they are extremely effective in producing activated species, e.g., free radicals and excited state atoms. Thus, both thermal and nonthermal atmospheric-pressure plasmas are finding applications in a wide variety of industrial processes, e.g. waste destruction, material recovery, extractive metallurgy, powder synthesis, and energy conversion. A brief discussion of recent plasma technology research and development activities at the Idaho National Laboratory is included.

Jan 1, 2006

By John Fallavollita

Conventional gas atomization produces powders that vary widely in size distributions and microstructures, thus making it very costly to produce powders tailor made in a narrow size distribution and microstructure. Furthermore, it is difficult to determine the relationships between atomizer operating conditions and resulting powder characteristics. The Impulse Atomization Process (IAP) was developed at the Advanced Materials and Processing Laboratory to produce powders with narrow size distributions. Powders produced by the IAP were reproducible and their sizes could be easily controlled by adjusting experimental conditions. Characteristics of Zn, Sn-Pb, AI-Cu, and Cu powders will be described to illustrate the flexibility of the process to tailor-make powders.

Jan 1, 1994

By Nagy El-Kaddah, T. T. Natarajan

This paper describes a novel approach for modeling three-dimensional electromagnetically driven flow in inductively stirred systems, and its application to modeling electromagnetic and flow phenomena in sub-mold rotary stirring of billets. It is based on a new T-\jf potential formulation of electromagnetic field, which does not require the calculation of the field in free space. A finite element algorithm has been developed for solving the electromagnetic field and Navier-Stokes equations in the fluid flow domain. The computed results have shown that the electromagnetic force field generates a strong rotational flow within the vertical section covered by the stirrer, and a relatively strong secondary flow beyond the stirrer. It has also been shown that the rotational and secondary flows were driven primarily by the vorticity of the force field at the billet corners. The induced flow in the molten pool was found to be turbulent and the effective mixing region in the molten pool was about three times the length of the stirrer. The mathematical approach presented in this paper provides the theoretical framework for quantifying these effects for any given stirrer configuration and operating parameters.

Jan 1, 1999

By Hans Jürgen Maier, Gregory Gerstein, Florian Nürnberger

Microstructural analysis to support the development of material models provides valuable information to design complex forming operations. Damage models such as e.g. by Gurson consider spherical voids only. However, investigations of bcc steels by scanning electron microscopy reveal that voids exhibit an ellipsoidal shape with progressing deformation. The material’s weakening in the Gurson model is taken into account by the void volume fraction. Therefore, a three-dimensional characterization of the void shape offers important data for modelling. Thus, information on the anisotropy of the process of void evolution and accordingly, about the anisotropy of the deformation process is provided. Application of the information regarding the void shape anisotropy within the Gurson model is discussed.

Jan 1, 2016

By E. V. Redin, B. A. Dubrovsky, E. V. Knyazev, A. I. Starikov

"Ti-V magnetite is one of the most abundant composite ore resources in the world. This ore cannot be fully processed via blast furnace technology because of high content of Ti02. According to the investigations carried out in the USA and Japan ITmk3 RHF (Rotary Hearth Furnace) technology is a breakthrough in Ironmaking. Reduction, melting and slag removal can be achieved in just 10 min. The main objective of the investigation is to establish optimum operation conditions for the production of iron nuggets from Ti-V magnetite ore via the ITmk3 by means of the lab scale testing. Samples of ore from the Maly Kuybas deposit (Southern Ural), carbon reductant and fluxes were chemically analyzed. Green pellets were processed via a lab chamber furnace to simulate RHF conditions. The nuggets and slag were chemically analyzed. This preliminary test work provides valuable information which may be used for large-scale testing in a commercially sized RHF.IntroductionThe ITmk3 process upon which this paper focuses was developed by Kobe Steel in its research facilities [l]. After pilot testing at Kobe Steel's Kakogava Works in 1999-2004 the pilot demonstration plant was built and operations were successfully carried out by Mesabi Nugget joint venture in 2002-2004. Steel Dynamics put into operation the commercial plant at the Mesabi Nugget site in Hoyt Lakes (Minnesota) in 2010. Results were consistent with nugget characteristics confirming ITmk3' s flexibility with respect to raw material inputs. At the same time, no research in the field of nugget from the Ti-V magnetite bearing ore with high content of Ti02 and Alz03 has been done. It is well known, if a lot of Ti02 and Alz03 enter the blast furnace, slag becomes viscous. The viscous slag is obstacle for stable operation of the blast furnace. Besides, high content of Alz03 raises the melting temperature of gangue minerals disturbing the coalescence of reduced iron to the nuggets."

Jan 1, 2013

By Margarete Kalin

Mine abandonment is associated with the securing of access to underground workings, shafts, raises and adits. Waste rock piles and tailings are generally contoured and revegetated. When the waste materials contain pyritic material seepages can often emerge long after the physical reclamation work has been carried out. Their extent and origin has to be delineated to facilitate remedial measures. The depth to which the seepages extended can be determined with an electromagnetic (EM) survey. This paper reports on the experience gained using a winter and a summer EM survey correlated with measurements of specific conductivity at the sediment water interface. Lake sediments and ponds which represent a homogenous background material are good media, where specific conductivity and electromagnetic conductivity can be correlated. The origin of the seepage within the recontoured mine site requires detailed site knowledge, as many anomalies in heterogenous materials such as represented by a mine site are evident.

Jan 1, 1994

By Toshiyuki Kozuka

CdTe metal composite semi-conducting material has high potential in good performance of energy conversion efficiency for solar cell and there is much room for improvement of the performance by developing a process of making a thin CdTe film. In this paper, the imposition of intense magnetic field on CdTe electro-depositing surface is proposed, which is one of the possibilities for improving the energy conversion efficiency. In the experiment, cryogen-free super-conducting magnet up to 5T was used and CdTe film was deposited electrically in -o.nv vs. SHE The electrolyte was Cd and Te ammonia alkali solution with controlled temperature in the acrylic cell of 70mm diameter. Electro-deposition behavior of CdTe has affected by the imposition of the intense magnetic field due to microscopic convection in the vicinity of the depositing surface. Electro-deposited surface of CdTe becomes smooth due to microscopic convection around the surface, and the crystallization behavior is also affected, where crystallization temperature and the grain size is changed by the imposition of intense magnetic field.

Jan 1, 2003

By Dilek Kirgöz, Onuralp Yücel, Murat Alkan

"In this study, Mo containing Fe-based alloys, such as Fe-Ni-Cr-Mo, were synthesized using a mixture of Fe203-NiO-Cr203-Mo03 powders reducing with Al powders by metallothermic process which is a high energy efficient, fast and low-cost production technique for synthesis of cast alloys and advanced ceramics. Detailed thermochemical studies were simulated by using FactSage 6.2 Thermochemical software in order to calculate adiabatic temperature of the reactions and effects of initial molar composition on the final products. In the metallothermic processes, effects of stoichiometric Al addition and addition of the oxide powders (Alz03, Si02, CaO, MgO) on the metal recovery and compositions of final alloys were carried out. Final products were characterized by using chemical analysis (AAS), XRD, XRF and SEM/EDS techniques.IntroductionSelf Propagating High Temperature Synthesis (SHS) has significant advantages compared to the high technology furnace applications, such as very short processing time, simple operation, low energy requirement and low cost [l, 2]. In a SHS process, the ignition starts the combustion and propagates throughout the reactant mixture yielding the desired product. However, the disadvantages of the process such as inhomogeneous or unreacted products due to undesirable reaction rates needs to be overcome by changing some parameters such as ignition temperature, particle size, additive, atmosphere etc. [3, 4]. This work aims to establish a scientific and engineering background in the production of some cast Fe based alloys (Fe-Ni-Cr-Mo) which are used as surface coatings, wear-corrosion-oxidation resistive applications via SHS (Self Propagating High Temperature Synthesis) metallurgy which is attractive process technique regarding fast and low-cost production ability of cast alloys."

Jan 1, 2013

By M. K. Alam

Chemical Vapor Deposition (CVD) processes are currently attracting special attention in materials processing. CVD processes are now used to produce special materials in the form of thin films, coatings, composites, and optical fibers. This process produces material of high purity, in complex shapes, and in a variety of microstructures. It is a capital intensive process, involving use of high cost raw materials. Modeling simulations have the potential of reducing the time for CVD . process design, and the need for experimentation. Modeling would, therefore, appear to be an attractive option for producing a product of acceptable quality. At Ohio University, progress has been made in modeling of CVD processes, specially in the areas of optical fiber preform fabrication, and fiber coating.

Jan 1, 1990

By Ker-Chang Hsieh

Four three-phase equilibria and one two-phase equilibrium in the FeNi- S-0 quaternary system in the vicinity of 1023 K and Pso2 = 1 atm were studied using the following emf cell 2 Pt,o2 (air)Zr02 .CaO/Pso2 = 1 atm, mixture of phases, Au The four three-phase equilibria are sp + (Fe,Ni )S + Ni 3s2, sp + Ni 3s2 + NiO, sp + NiO + N1S04 and Fe2 o3 + sp + (Fe,NOS04 -Y:he two-phase equilibrium is sp + (Fe,Ni)S. The two-.phase equilibrium was measured by using mixtures containing a major portion of one phase and a minor portion of the other. The results are presented in terms of oxygen potential as a function of YNi = nNi/(nN1+nFe) at constant temperature and pso2 = 1 atm. The stability diagram was also calculated using appropriate thermodynamic models for all the pertinent phases. The calculated diagram is in accord with the measured ones.

Jan 1, 1985

By C. E. M. Meskers, U. Boin

"The increasing use of coated magnesium in consumer products results in creation of coated Mg scrap during product manufacture and after End-of-Life product treatment. Currently this material is generally not recycled, leaving a material resource unused. Closure of the magnesium cycle in a sustainable manner is necessary. In order to do so, the effect of coatings on the recycling process has to be quantified, predicted and minimized. For this purpose metrics have been developed, based on first principles supported by detailed understanding of the recycling process. The developed 3D metric enables quantitative assessment of the recyclability and links coating design, product design and recycling to each other in a visual manner. The parameters that form the metric can be measured and predicted, hence an engineering basis for Design for Sustainability of coated magnesium is provided.IntroductionEvery product progresses through the four phases of the product life cycle depicted by figure 1. In each phase residues are created. Their amount and composition is largely determined by the complex material combinations created/invented during product design in the manufacture phase. Compared to the ideal cycle the magnesium cycle is far from closed (fig. 2). Most noticeable is absence of the link between the EoL phase and raw materials production. A closed cycle only exists for class 1 scrap, which goes from the product manufacture phase directly to production from industrial material and returns to the manufacture phase as magnesium alloys. The four problematic streams are marked by ???. Coated semi-products are present in two of the four residues, namely in rejects and collected scrap. When these semi-products are recycled the amount and composition of the dross and salt slag residue is affected as well.During product design selection of the coating takes place, fixing the coating character¬istics and properties from this moment on for the rest of its life cycle. The choices made in the manufacturing phase are therefore critically linked to the recyclability of coated semi-products as well as the sustainability of the magnesium cycle as a whole. Sustainable closed life cycles, in which the quality of materials is preserved and residue creation and resource depletion are minimized, can be attained by selecting the appropriate alternative during product design. To realize this the effect of design choices on the life cycle and more specific the recycling process has to be known and quantified."

Jan 1, 2008

By M. H. Staia

A Venezuelan ilmenite concentrate has been chlorinated at a temperature of 700" C by carbon tetrachloride. In the experimental rig, built at laboratory level, the direct chlorination process yielded a TiCI, recovery of approximately 85% after 280 minutes processing. The partial pressure of carbon tetrachloride was nearly atmospheric (0.94 atm). Product vapors from the reactor were fractionally condensed in a condenser which was maintained at a temperature of 250°C meanwhile TiCl, vapors were condensed in refrigerated coils at a temperature of -20°C. The concentrate used in this investigation was obtained by applying gravitational and magnetic concentration methods to the black sands. The experimental results have shown the need to asses the influence of the weight ratio of ilmenite to carbon tetrachloride on the resultant products. The equilibrium of the heterogeneous system has been calculated taking into account the initial experimental conditions.

Jan 1, 1995

By Supachai Surapunt

The distribution behavior of V A minor elements (As, Sb and Bi) in the smelting stage of the Mitsubishi process were evaluated thermodynamically based on thermodynamic data and operating data. The fractional distributions between the gas, slag and matte phases considered as the degree of vapor saturation of 1.0 are as follows: 53.8, 27.2 and 19% for As, 23.6, 56.6 and 19.8% for Sb, and 91.3, 1.1 and 7.6% for Bi, respectively. Arsenic is mostly distributed to the gas and slag phases. It is effectively eliminated by volatilizing and slagging. Antimony is mainly in the slag phase, which is suitably removed by slagging. Bismuth is easily vaporized to gas phase. The degree of vapor saturation has a large effeet on the distribution behaviors of the three elements between the three phases. The amount of a minor element in the charge has an effect on the distribution of As but no effect on the distributions of Sb and Bi. Increasing matte grade and temperature results in the change of distributions for As and Sb, significantly. The change in the distribution ratio between slag and matte phases also considerably affects the distributions of As and Sb. The distribution behavior of Bi is not significantly changed by the change in matte grade, temperature and distribution ratio.

Jan 1, 2003

By Runsheng Xu, Haiyang Wang, Pengcheng Zhang, Tengfei Song

Semi coke, a byproduct in the chemical industry, is a new fuel for blast furnace injection in China. In this study, semi coke and bitumite were milled into different size, ranged from 0.147mm to under 0.074mm. The content of volatile matter and ash, which affect the combustibility of semi coke, were measured using muffle furnace. The mixture, in which the proportion of coal in different sizes changed, was blend by semi coke and bitumite with different size. Activation energy calculation and the comprehensive combustion characteristic index of all kinds of blends was also discussed. The result obtained by Thermogravimetry –Derivative Thermogravimetry curves indicates that the smaller the size of mixture is, the lower for the characteristic temperature, and the better for its combustibility, Semi coke can be a substitute for anthracite in blast furnace injection.

Jan 1, 2015

By O. P. Pandey, Rama Arora, Gurmel Singh, Suresh Kumar

The tribological behavior of Dual Particles Size (DPS) rutile reinforced LM13 alloy composite was investigated under varying applied pressure from 125 kPa to 625 kPa at a constant sliding speed of 1.6 m/s. In the present studies, 15 wt.% of rutile particles of different sizes (50-75 μm and 106-125 μm) are reinforced in the Al-12Si alloy (LM13) by liquid metallurgy route. Microhardness of the prepared samples was measured in different phases. Microstructure, wear mechanism and surface morphology of the wear surfaces and debris was observed under optical and scanning electron microscope. The change in wear behavior has been explained with reference to the observed EDS analysis of the wear track and debris. However, an interesting change in wear feature, mild to severe wear transition at critical pressure was noticed in wear behavior of the composite. The Al-DPS composite has immense potential to be used as a component material for tribological applications.

Jan 1, 2015

By Natasa Mitevska

The statistical analysis of the slag composition influence on copper losses to discard slag in the reverberatory furnaces No.1 and No.2 in the RTB BOR, Copper Smelter and Refinery (Yugoslavia) is presented in this paper. The model for the slag basicity calculation is determined, and connected to the copper distribution coefficients between the matte and slag phase. The influence of all components on the slag structure is also illustrated.

Jan 1, 2003