By Chunyang Guan, Jilai Xue, Zengjie Wang, Qiaochu Liu

Molten salts electrolysis method to prepare Al-RE alloys has attracted increasing attention recently. CaCl2 and Na3AlF6 were the most often used melts for this purpose. In this work, Al-Sc alloys prepared by electrolytic deposition process in both CaCl2 and Na3AlF6 melts were investigated, respectively. It was found that Sc distributes almost uniformly and Sc contents increase with increasing current intensity in both melts. Current efficiency was measured for comparison among various current densities applied. The alloy products were analyzed using XRD and SEM, where the formation behaviors of Al-Sc intermetallics were investigated in details. The experimental and theoretical results demonstrate that Al3Sc and Al0.968Sc0.032 are the major precipitates in the Al-Sc alloys prepared by molten electrolysis. The results are useful for selection and optimization of the molten salts compositions and the parameters of electrolysis operation.

Jan 1, 2015

By Akira Kaneda, Nozomu Hasegawa

"In the Mitsubishi Continuous Copper Smelting and Converting Process, slag/matte mixture overflowed from the smelting furnace is separated continuously in an electric furnace (slag cleaning furnace, CL-furnace). In order to improve the separation efficiency of slag and matte and to minimize power consumption, the design and the operating conditions of the CL-fumace should be optimized. In the previous study, the authors developed a mathematical model for simulating phenomena in the CL-furnace. The model consisted of 3 modules, electric field analysis, heat and fluid flow analysis and the particle tracking method. In this study, the model was partially modified: k -E. model was adopted, and the effects of various conditions, such as furnace shape (including accretion) and scale, electrodes configuration, immersion depth of electrodes, and thickness of slag layer, were evaluated. And the optimum design and operating conditions were discussed.IntroductionUnder the recent environmental restriction, advantageous features of the Mitsubishi process have attracted much attention. The process uses 3 furnaces connected by launders. Mixture of matte and slag formed in a smelting furnace flows continuously to a slag cleaning furnace (CL-furnace), where the matte is separated from the slag. The matte is continuously siphoned out to a converting furnace and converted to blister copper. The slag overflowed from the CL-furnace is discarded. Because the slag contains about 0.6 % copper, improving slag/matte separation efficiency and decreasing copper loss make a great profit. Moreover the process requires a large amount of electric energy, so reduction of electric power consumption brings in enormous benefit.The objective of this study is to optimize the design and the operating conditions of the process, especially the CL-furnace. This will be achieved by developing the mathematical model and clarifying relations between the design or the operating conditions and various phenomena in the furnace. Fig. 1 shows an outline of the CL-furnace. The mixture entering through an inlet is separated to slag layer and matte layer . In order to maintain the temperature of the melt at a predetermined level, 6 electrodes are immersed into the lag and Joule's heat is generated by 3-phase alternating current flowing."

Jan 1, 2000

By R. C. Hubli

A panial equilibrium model? to simulate the dissolution of millerite (NiS) in aqueous solutions containing copper(II) chloride as the oxidizing species has been developed. The predominant copper(I) and copper(II) species are CuQ3 and CUO2 respectively. The model computes the initial concentrations of the species present in the aqueous phase under the specified input conditions, prior to the simulation of dissolution. During the dissolution of millerite, nickel enters the leach liquor as NiH and it has been found that the H+ decreases as a function of NiS dissolution. The simulation has been accomplished under conditions prevailing during actual dissolution, with only one mineral undergoing dissolution. The model can be applied for the simulation of co-dissolution of two or more sulfides. Under the given conditions, the precipitation of Cu1(OH»)O is negligible but loss of Cu(1l) could be significant if the initial H+ is lower than 0.03 M. The results of the simulation compare favorably with experimental observations.

Jan 1, 1996

By Yafei Xiong, Yue Wang, Guotao Xu, Shuzhong Li, Huaiyuan Li

"The composition, properties and structure of taphole clay with high strength and friendly surrounding used in a new blast furnace with 3800 M3 volume was studied. The developed taphole clay had been applied in the blast furnace for four months, pouring times were 11-13 every day, flowing rate of hot iron was 7.5 t/min and the consumption of taphole clay was 0.49Kg per ton iron, which can make the new blast furnace attach the designed production quickly and decrease the cost of hot iron. The taphole clay is easy to be opened in the channel of hot iron which can be remained in stable shape under the corrosion of slag or hot iron, and it dose not produce poisonous smoke in yellow or dark color in the use process. The development of new taphole clay is useful to improve the work surrounding of the blast furnace.IntroductionIn the iron-making process, the taphole clay's function is filling up the taphole and protecting the formation as well as the growth of the clay in the blast furnace, maintaining the enough taphole depth; simultaneously it is easily to open a hole and knock out the clay. The taphole clay has a good performance of molten slag and hot iron resistance. The traditional taphole clay uses coal tar or carbolineum as a binder, and the performance of taphole clay is good, but it has the black and yellow poisonous smoke, which is harmful for work condition. Through the investigation on the binder's composition and poisonous performance of taphole clay, the environmental taphole clay is developed by some foreign companies, which is named the third generation product with benzene is less than 300ppm, and it has been used in European steel companies. This application of the taphole clay with high strength and environment-friendly using in 3800m3 blast furnace is introduced and the performance is discussed and analyzed in this paper."

Jan 1, 2012

By José Luiz Rodrigues Bravo

The production of electrolytic copper with assured quality corresponding to international standards, in a conventional electrorefkery of a custom smelter, is a hard and cautious task, if no advanced technologies for selective control of electrolyte impurities are available. The improper control of the amount of As , Sb and Bi in the anode that enter the tankhouse , attributable either to a bad schedule of concentrate input or to the unavailability of clean concentrates in the international market , as well as the lack of means to maintain the suitable level of these elements in the electrolyte together with other operational circumstances, can result in off-grade copper, as well as affect the starting sheet chemically and physically. This paper presents in a practical way the relationship between the operational conditions and the cathode and starting sheet quality produced at CMSA, covering the period of the last five years of operation, discusses the technologies available in the market for antimony and bismuth removal and compare the results of testwork, achieved in the laboratories of CMSA, using two resins not associated with patented technologies.

Jan 1, 1997

By Motohiro Horiguchi, Kazuo Ichii, Toshio Oishi

"As a fundamental study to prepare copper-based alloys with rare earths (RE: La, Gd, Nd, Ce and Y) without any inclusions, the solubility of rare earth in liquid copper was experimentally determined. Liquid copper alloys were equilibrated with carbon and rare earth carbide in a graphite crucible in an argon atmosphere at 1523-1873 K.Solubilities of rare earth in liquid copper were determined by approaching the equilibrium values from both the lower and the ·higher concentrations than those expected· in the preliminary experiments. They were expressed as a function of temperature. Carbon in Cu-RE alloy was also analyzed and thermodynamically discussed.IntroductionOver the past several years, the demand for highly conductive and high strength copper-based alloys, such as Cu-Cr, Cu-Zr and Cu-Cr-Zr for use in electronic materials has increased.1 -7 These alloying elements are very reactive and easily oxidized to form oxide inclusions during melting. To avoid the oxide inclusions, it may be effective to utilize the strong reducing power of carbon in conditions under which no carbides form.In this study, to provide fundamental data for producing Cu-RE( rare earth) alloys without any inclusions, the solubility of rare earth in liquid copper in equilibrium with .carbon .was determined and discussed on the basis of the experimental results and the thermodynamic data.ExperimentalSample preparation for equilibrium experimentsOxygen-free copper (99.99%), lanthanum (99.9%), gadolinium (99.9%), neodymium (99.9%), cerium (99.9%) and yttrium (99.9%), and their oxides were used as starting materials.Each rare earth carbide was prepared by mixing rare earth oxide with carbon, which is a little more than the stoichiometric composition, pressing it into a tablet form and sintering at about 2000.K for 20 ks in a vacuum furnace using a graphite crucible. Powder X-ray analysis showed that only the carbon and rare earth carbide (REC2) was present in each sample.Cu-RE mother alloys (5-20 mass % RE) were prepared beforehand by mixing metallic rare earth with oxygen-free copper, and melting in an electric arc furnace."

Jan 1, 2000

By Katsunori Yamaguchi

Secondary materials, that contain relatively high concentrations of platinum group metals, (PGMs) are treated in copper smelting process. The PGMs lost in the slag is increasing with increasing quantities of scrap treated amount. To determine the portion of the PGMs chemically dissolved and that associated with the mechanically trapped matte in the slag will be a key factor to improve the recovery of those metals. An experimental study was carried out to determine the distribution of palladium between the FeOx–SiO2 slag and the liquid Cu2S–FeS matte at 1573 K and a fixed partial pressure of SO2 of 0.1 atm. It was found that the distribution ratios are around 10−3 for platinum and palladium. The distribution ratios show a tendency to increase when the grade of matte is increased above 60 mass% Cu. In addition, the solubility of platinum in FeOx–SiO2 slag equilibrated with a pure palladium and the Pd-Cu alloy was determined at 1573 K and the range of oxygen partial pressure from 10−9 to 10−7 atm. The solubility of palladium in the slag tends to increase with increasing oxygen partial pressure and activity of CuO0.5 in the slag.

By Ole Rud Bendixen

Topsoe has developed a Wet gas Sulphuric Acid (WSA) process which effectively recovers SO2 in off-gases from non-ferrous smelters and roosters. The product is concentrated sulphuric acid of typically more than 96 wt% irrespective of SO, concentration in off-gas. The process does not generate any waste products or waste water and does not use any absorbents or other chemicals. In the process, up to 99.3% of the SO2 is converted catalytically into SO3, which reacts with water in the gas, hereby forming gaseous sulphuric acid. The acid is condensed in a WSA condenser of proprietary design. Excellent heat economy and practically no sensitivity to the water balance mean that no extra sulphur burning is required at any S02 concentration, The process is especially well suited for treating off-gases where the SO2 content is lower than approx. 5-6%, and it is a good alternative to a complete renovation of a smelter. However, also off-gas from flash smelter may be treated. The process has found good use in both molybdenum and lead roosters. An example from a molybdenum roaster in Chile shows that 97-98wt% acid is produced from a 2.3 % S02 gas. This plant is situated in the outskirts of Santiago and represented a major local source of SO2. The plan was started in May 1993.

Jan 1, 1996

By M. Misra, J. Nanor

The precipitation and removal of arsenic from process waters can be accomplished with addition of lanthanum chloride alone or in conjunction with ferric sulfate. The long term stability of these corresponding precipitated compounds is critical from the disposal stand-point. In this paper the characterization of ferric, lanthanum and lanthanum-ferric arsenate compounds formed at room temperature in acidic and alkaline pH is presented. The characterization techniques used included zeta potential, XRD and SEM. Zeta potential measurements of ferric and lanthanum hydroxides in the presence of arsenate indicate that oxyanions of arsenate are chemically adsorbed onto the positively charged surfaces of these hydroxides. In alkaline pH there is desorption of arsenate species from the ferric hydroxide surface, hence the product is thought to be unstable. On the contrary, lanthanum arsenate is stable in alkaline pH. XRD patterns show that the ferric arsenate formed in acidic and alkaline pH is amorphous, whereas lanthanum arsenate and lanthanum-ferric arsenate formed in acidic and alkaline pH are crystalline.

Jan 1, 1999

By Sheng Dai, Yuan Lee, Haiming Xiao, J. P. Young

"There are numerous analytical applications of scatter-emission and/or absorption spectroscopy applied to liquids and solids in the temperature range of 0 to 350°C. In this paper an all-silica fiberoptic probe is described which is useful for spectral analyses from 0 to 1600 K and can be used in harsh chemical environments. The probe has been used for Raman spectral analyses of many molten salt and solid material systems to 1000°C. It has applications for such studies at higher temperature ranges. The instrumentation required along with the demonstrated and proposed applications of the all-silica probe are presented and discussed.IntroductionThere are many kinds of scatter-emission spectroscopies that are of value for analytical measurements. Fluorescence, reflectance, arc or spark emission are descriptors for some of these. Raman scatter spectroscopy is also quite a useful technique for analytical measurements.In Figure 1, we give a simplified explanation of the Raman effect. If one shines monochromatic light into a sample, light may be absorbed, exciting the sample to some virtual state. We know from experience that almost all of the light is re-emitted in the same wavelength range. This is called Rayleigh or Mei scattering and is designated in the figure by the arrows in both examples that point up and down from the same lower energy state. A very small percentage (the order of 10-4%) of the monochromatic light is re-emitted leaving the sample at a vibrationally-excited state. Thus, this light is at a distinctly lower energy compared to the exciting radiation. This is called a Stokes shift and is represented in the left-hand example by an arrow descending to a more energetic vibrational state. If the sample is not at a temperature of absolute zero, some of this vibrationally excited state will be thermally populated. That portion of the sample still absorbs and re-emits exciting radiation as Rayleigh scattered light, but a small percentage of the exciting light is re-emitted as the sample relaxes to the lower vibrational state. The energy of this light is of higher energy and is called an anti-Stokes shift, depicted in the example to the right. Notice that the energy separation of the Stokes or anti-Stokes shifted emission from that of the exciting radiation is the same, and expressed in ~cm-I. The intensity of either shifted emission is a function of the population of the vibrational energy states; therefore, the ratio of the intensity of Stokes to anti-Stokes signal varies with absolute temperature. We will come back to this point later."

Jan 1, 1997

By Katsunori Yamaguchi

A new technique for the removal of tramp-elements from steel scrap has been required from the viewpoint of saving energy and protection of environment. In order to obtain fundamental information on the removal of copper, tin and zinc from molten iron, the extraction method by using of phase separation in the liquid Fe-Pb-C system was investigated at 1453K. A mixture of iron, lead and carbon melted in a carbon crucible separates into two phases of lead and iron containing carbon. The compositions on the miscibility gap in the Fe-Pb-C system are 95.4%Fe-4.5%C-0.1 %Pb and 99.9%Pb-0.I%Fe. The distribution ratios of copper, tin and zinc between the lead and the iron phases, Lx [mass%X in molten Pb]/(mass%X in molten Fe), are 2.2, 2.2 and 1.4, respectively. Seventy percent of copper and tin from iron scrap can be eliminated with comparable lead addition. Gold, silver and palladium are enriched in the lead rich phase, on the contrary platinum and rhodium are more distributed to the iron rich phase than to the lead phase.

Jan 1, 2003

By G. A. Irons, D. Guo, D. Angheiina

To produce low-carbon (<30 ppm) steel in the tank degassing process, a ladle of steel with an oxidizing slag is placed in a vacuum tank equipped with bottom bubbling. The kinetics of this process are slow compared to the more prevalent RH degassing process, providing the impetus for the present work. There are several aspects to this work: water models of the fluid flow in the ladle; simulation of the decarburization (CO evolution) with C02 desorption in water; pilot-plant (60 kg) studies of the decarburization kinetics; mathematical modelling of the fluid flow in the ladle; mathematical models for each of the kinetic sites (plume, top slag and auto-nucleation); and full-scale trials. The results show that during the refining cycle the contribution from each reaction site changes, suggesting avenues for reducing cycling time and final carbon contents.

Jan 1, 2000

By L. J. Cabri

The level of mineral exploration activity for platinum in recent years, especially in North America, has ranged widely. Exploration programs have been based on a variety of ore deposit models and deposit types. These range from the classic magmatic model for sulfide/oxide deposits and their associated placers, through hydrothennal models for bonanza-type deposits, to low-grade mineralization potentially amenable to lower cost bulk mining methods. The platinum-group element (PGE) distribution in these different deposit types is not well-known however, and PGE determination is fraught with analytical difficulties. To properly assess a prospect or to achieve effective recovery by mineral processing, it is important to determine the mineralogical distribution of the PGE.

Jan 1, 1988

By Osamu Iida

Since &apos;start-up of the larger Mitsubishi Continuous Copper Smelting Process in 1991, furnace relining campaign was gradually prolonged to once every 2 years according to deregulation of governmental boiler inspection. On the other hand, in 1998 Naoshima smelter embarked on an intermediate strategic expansion plan to strengthell its international competitiveness. As part of this plan, modifications were implemented in the copper smelter designed to increase output of anodes from new charge source to 270,000 tpa. In May 1998, treatment of dried neutralized residue was started in C furnace, and during the shutdown for brick relining in April 1999, intensive modifications to the boilers as well as the installation of new spray coolers for furnace off gas treatment were implemented. Finally, the new larger oxygen plant was commenced its operation in May 2000 and the expansion was achieved around 30% increase of anode production from original design.

Jan 1, 2001

By S. Jolivet, A. Klöfverskjöld, P. Latostenmaa, B. P. Wilson, M. Lundström, P. Halli

Doré slag is secondary product of copper electrore fining anode slime treatment. The slag consists mainly of different slag formers, such as borax and silica based minerals together with soda and traces of sealing materials. However, Doré slag also contains metals present in the anode slime, such as Ag, Cu, Bi, Sb and Te. At some plants, slag cleaning has been conducted utilizing conventional grinding and flotation circuits in order to enrich the content of precious metals in the slag [1]. Nevertheless, the routine consideration of the slag as a secondary raw material has so far not been adopted on an industrial scale. The current study presents the preliminary results of the nitric acid and chloride leaching of antimony from Doré slag. Chemical and mineralogical analyses (SEM-EDS, AAS, XRD) were performed for the raw material, leaching residue, and leaching solution in order to ascertain the metal recovery and kinetics during leaching.

Mar 1, 2017

By F. J. Tavera

The column flotation technology, at first developed for application in mineral dressing, has received special attention in processing of non-mineral dispersions as a result of its low cost, high efficiency and relatively simple operation. This paper presents the results from the operation of a laboratory flotation column for the separation of vegetable oil and soap from aqueous industrial effluents, The flotation system was operated under continuous countercurrent conditions without and with additions of a cationic collector. The experiments show that it is possible to separate about 80% of the organic phase in a rougher flotation stage. These results suggest that the recovery of the organic phase is highly dependant on the dispersion characteristics (i.e. bubble size, gas holdup and bubble surface area flux) and the existing an optimum bubble size from which either smaller or larger, the recovery of the organic decreases.

Jan 1, 2003

By Charles A. Sorrell

Two red muds, two fly ashes, and several aluminosilicate minerals were subjected to direct treatment with concentrated H2SO4 at temperatures of 175°C and below. X-ray analysis showed that virtually all the sulfate reaction products remained in the solid residue because of their low solubilities in x SO Substantial portions of the Al2O3 Fe2O3TiO2, Na2O, and K2O components of the materials reacted to form water soluble sulfates, which were then removed by H2O leaching at 55°C. The solid residue after water leaching consisted largely of amorphous silica and, in lime bearing compounds, CaSO4, The reaction and leaching processes were effective in removing all or nearly all the Al2O3. Fe2O3, TiO2, Na2O, and in lime components in the fly ashes, red muds, china clay, bentonites, the nephelioe fraction of nepheline syenite, and a plaster insulating brick composed of anorthite and mullite. Reaction with potassium feldspar and petalite took place, with formation of alkali aluminum sulfates, but the reaction rates and yields were extremely low. Potassium feldspar can be heated with Na2O and x O in air at 700°C for 24 hours, or with CaO at 1000°C for 24 hours, after which the reaction product kaliophilite, nepheline, and leucite-like phases, prove to be very susceptible to H2SO4, reaction and H2O leaching, providing yields near 100% of the Al2O2 content. An alternative method of H SO treatment consists of heating the sample in a silica tube and passing H2SO4 vapor over it. Preliminary results indicate that this method can be effective in enhancing the kinetics of reaction with the Al O component of potassium feldspar and offer the possibility that formation of Al2 (SO ) Fe2(SO4)3 and TiOSO4 can be accomplished selectively by taking advantage of the fact that the upper stability limits of the respective sulfates in the presence of H2SO4 vapor will be different.

Jan 1, 1982

By R. Padilla

The reaction of chalcopyrite with gaseous sulfur has been investigated in the range 350-450 °C in order to transform this mineral into a more acid soluble copper sulfide and insoluble iron sulfide. The results of thermodynamic analysis of this system as well as the X-ray diffraction analysis of the reaction products showed that in the temperature range 350 400°C the sulfidation reaction proceeded without formation of intermediate copper-iron sulfides according to: The effects of temperature and time on the conversion of chalcopyrite were studied. Conversion of chalcopyrite reached about 80% very rapidly with increase in temperature up to about 400°C. The recovery of copper from the sulfidized samples was determined by leaching in oxygenated 1.2M H2S04, 2M NaCI solution. Copper recoveries over 90 % were obtained from samples sulfidized for 30 min at temperatures lower than 400°C.

Jan 1, 2001

By L. Sh. Tsemekhman

A new technology for the treatment of copper nickel-containing concentrate after high-grade matte flotation to blister copper with the production of liquid silicate slags in a vertical autogenous unit with upper oxygen blow has been considered. The copper and nickel behavior in the process of sulphide copper concentrate interaction with silicate melt containing oxide copper has been studied. The general mechanisms of such interaction are found.

Jan 1, 2003

By Federico Chavez

The process for recovering lead from battery residues used in several Mexican Plants include lead blast furnace and rotary furnaces. The formers are basically fed with recycled batteries together with the necessary additives to produce metallic lead. One of the by-products generated in the blast furnace is a dust mainly formed by lead sulfide. The rotary furnace is used to recover lead .from lead batteries, dross from the refining-alloying process and the leady fines produced in the blast furnace. This paper describes thennodynamic analysis made to the rotary furnace process to understand the effect that each component of the system has upon the lead recovery. In order to enhance the process, the influence of iron chips composition and excess coke on slag viscosity is discussed. A computer optimization program . has been developed to design the furnace charge based on material and energy balances, .together with the thennodynamic equilibrium calculation.

Jan 1, 1995