Search Documents

By Francis Vanbellen

Umicore Precious Metals Refining operates an integrated precious metals smelting and refining plant in Hoboken, Belgium. Once a smelter and refiner of complex concentrates, the plant today?s feed consists exclusively of industrial and consumer recycled products, making it the world?s largest recycling facility for precious metals. Unlike the fairy tale of the Frog Prince, it took much more than a princess? kiss to successfully realize this makeover. A completely renewed plant has been built over the past decade. The most visible technological innovation was the commissioning of the Pb-Cu smelter. Its flexibility towards very different types of feed makes it perfectly suited as main entry to the Hoboken flow sheet. A new Cu-leaching & electro winning plant and precious metals refinery make up the Precious Metals Operations (PMO) whose targets are fast throughput and maximized yields for gold, silver and the platinum group metals. The Base Metals Operations (BMO), flexibly process the by-products from the PMO, valorizing ?impurities? like indium, tellurium, selenium and others. Off gas and waste water treatments ensure compliance with strict environmental standards. Precious metals recycling is an art that goes beyond mastering a unique flow sheet. Umicore Precious Metals Refining offers a complete recycling service, taking care of sampling and assaying, metals management and logistics. The quality of this integral service is recognized through the attribution of ISO certifications for our operational activities, sampling and the environmental care. And it?s an art that follows Michelangelo?s experience: ?Art is 5% of inspiration and 95% of transpiration.?

Jan 1, 2006

By Francis Vanbellen

Umicore Precious Metals Refining operates an integrated precious metals smelting and refining plant in Hoboken, Belgium. Once a smelter and refiner of complex concentrates, the plant today?s feed consists exclusively of industrial and consumer recycled products, making it the world?s largest recycling facility for precious metals. Unlike the fairy tale of the Frog Prince, it took much more than a princess? kiss to successfully realize this makeover. A completely renewed plant has been built over the past decade. The most visible technological innovation was the commissioning of the Pb-Cu smelter. Its flexibility towards very different types of feed makes it perfectly suited as main entry to the Hoboken flow sheet. A new Cu-leaching & electro winning plant and precious metals refinery make up the Precious Metals Operations (PMO) whose targets are fast throughput and maximized yields for gold, silver and the platinum group metals. The Base Metals Operations (BMO), flexibly process the by-products from the PMO, valorizing ?impurities? like indium, tellurium, selenium and others. Off gas and waste water treatments ensure compliance with strict environmental standards. Precious metals recycling is an art that goes beyond mastering a unique flow sheet. Umicore Precious Metals Refining offers a complete recycling service, taking care of sampling and assaying, metals management and logistics. The quality of this integral service is recognized through the attribution of ISO certifications for our operational activities, sampling and the environmental care. And it?s an art that follows Michelangelo?s experience: ?Art is 5% of inspiration and 95% of transpiration.?

Jan 1, 2006

By Shuqiang Guo, Gonghui Yang, Xingxing Zhang, Yuyang Bian, Song Chen, Weizhong Ding, Yinhe Liu, Lan Jiang

One of the most promising refractory materials for application is zirconia in melting superalloy. In this work, the properties and phase composition of magnesia partially stabilized zirconia ceramics (MgO-PSZ) under different sintering temperatures were systematically investigated. Commercial magnesia partially stabilized zirconia (MgO-PSZ) powders were selected as the starting materials. The magnesia partially stabilized zirconia phase composition was measured by X-ray diffraction (XRD), the density of sintered samples was tested by vacuum density instrument, the thermal expansion were obtained by thermal dilatometer from ambient temperature up to 1450°C, and the microstructures of MgO-PSZ were characterised by scanning electron microscope (SEM). The results indicated that the properties of thermal expansion, densification, microstructures and phase composition were significantly affected by sintering temperature. Densification was consistent with SEM micrographs of MgO-PSZ at different sintering temperatures.

Jan 1, 2015

By Toshia Ishii, Jun Kubota, Noriko Kubo

"For steel continuous castings, it is essential to control molten steel velocity at the meniscus, since the velocity is closely related to surface defects on the resultant products. Argon gas is supplied with molten steel into the mold through the submerged entry nozzle to prevent nozzle clogging. In this study, to investigate the influence of argon gas on molten steel flow, a numerical simulation was carried out by a two-phase model. Simulation results indicate that as argon gas bubbles ascend near the nozzle by their buoyancy, they induce the molten steel flow with them and resulted a meniscus molten steel flow from the nozzle to the narrow face of the mold. This flow direction is opposite to the case without argon gas. The calculated data are compared with the experimental data. The comparison shows generally good agreement between the measured and the calculated data. IntroductionIn a steelmaking process, molten steel carried by a ladle is first fed into a buffer vessel called tundish. From the tundish, it is then fed into a continuous casting mold. Molten steel solidifies gradually in the mold (the primary cooling zone) forming a solidified shell. As the solidified shell is just thick enough to support the molten steel at the mold exit, it is withdrawn through the mold by pinch rolls. It is progressively thicken as it is further cooled with water sprays in the secondary cooling zone. At the end of guide roll zone, completely solidified steel is cut into desirable lengths. Schematic view of a typical continuous casting is shown in Figure 1."

Jan 1, 1999

By Kiyoshi Takai

The Para-Eco Incinerator Ash Processing System for cleaning slag has been developed after a seven-year pilot plant study. The major part of the system is an electric furnace heated to 1773 K. The feed material consists of a municipal solid waste incinerator ash mixture containing a reducing agent of a coke and an inorganic flux of calcium and magnesium. With this furnace system, three kinds of products are produced. They are an inorganic molten salt that is slag, molten iron alloy absorbing non-ferrous metals, and fly ash. Due to the reducing atmosphere in the furnace, the slag does not contain any metal components as well as chlorine components just like natural rock and/or aggregate. A retreatment plant modifies this slag into a practically useful aggregate. The plant consists of a slow cooling step for crystallizing the slag as well as a water granulation step. The iron components in the ash are reduced to molten iron droplets, which concentrate at the furnace bottom. The non-ferrous metal components such as copper, chromium, and others are absorbed into the molten iron but not into the molten slag. Volatile metals such as lead, zinc, cadmium and others as well as sodium, potassium, and chlorine go back into the fly ash. A solvent extraction method and/or other appropriate procedures can be used to extract the metal components from this fly ash.

Jan 1, 2003

By Norbert Steiner

For the desulfurization of weak SO2 gas streams, Degussa developed a process using dilute H2SO4 solution containing H2O, instead of conventional gas scrubbing with all solid absorbent medium (limestone, MgO). The process is based on fast reaction of H2O, with SO2 yielding H2SO4 up to 70% strength, depending on off-gas temperature. Compared to the conventional systems with typically < 95% efficiency, independent on the raw gas SO2 concentration, residual SO2 concentrations of less than 20 mg/Nm3 can be easily achieved, corresponding to nearly 100% removal. These features render the H2O, process a very attractive, low capital cost technology to retrofit existing conventional desulfurization plants.

Jan 1, 1996

By J. W. Tsai

Both diamond crystals and diamond films were grown on silicon and copper substrates using a methane/hydrogen gas mixture as a precursor with thermal CVD techniques at low pressure environment. In addition to diamond particles, other crystalline phases including graphite and aluminum silicon carbide were observed on the substrate surface. ?The grown materials were analyzed with X-ray diffraction, electron microscopy, Auger electron spectroscopy and optical microscopy. Most synthesized diamond crystals were twinned. The flow rate of reactant gases, substrate nature, substrate temperature, decomposition temperature of the precursors, total pressure of reaction chamber, methane/hydrogen ratios and other possible parameters were varied during the growth processes, and the significant effects of these factors on nucleation and growth rate were evaluated.

Jan 1, 1989

By Takaaki Ishikawa

The distribution equilibria of lead, zinc and copper between CaO-Si02-Ah03 melts and liquid copper were measured at 1623K under a controlled H2-C02 atmosphere. The distribution ratios were plotted against the oxygen partial pressure, and reasonable oxide forms dissolved in the melts were estimated from the slopes of the plots. The activity coefficients of zinc oxide (ZnO), lead oxide (PbO) and cuprous oxide (CuO0.5) increased with increasing slag basicity, defined by XCao/Xsio2 The temperature dependence of the activity coefficients was also measured.

Jan 1, 2003

By Deepak Gupta, R. Kageyamat, J. W. Evans

"In electromagnetic casting, a liquid metal pool is partly supported by electromagnetic forces resulting from the interaction between induced currents and an alternating magnetic field. Stability of the metal surface is of paramount importance if the cast ingot is to be free from surface defects. Prior work by Garnier and Moreau had suggested that the magnetic field has no influence on the surface stability, but a more complete analysis at Berkeley suggested that surface perturbations are destabilized by the magnetic field once a critical magnetic field is exceeded. More recently we have employed a modified version of the software SOLA to compute the behaviour of a melt surface in the presence of an alternating field. The computed results support the theoretical analysis in predicting an unstable surface. Experimental work is now in progress to examine the stability of a mercury pool in the presence of an alternating field. Introduction and Previous InvestigationsElectromagnetic casting (EMC) is a technique widely employed in the aluminum industry to produce ingot for subsequent rolling. It is a ""continuous"" casting technique (illustrated in Fig. 1) producing ingots several meters high (and perhaps 1m by 2m in horizontal dimensions) at a casting speed of one or two mm. per second. The technology has gained acceptance because the metal is solidified without contact with a mold. Consequently the surface finish of the ingot is usually smooth and the ingot can be fed directly to rolling without machining, the surface (""scalping""). Scalping is necessary with alternative technologies (e.g., DC casting) where a mold is used. Consequently any disturbances that result in surface imperfections of EMC ingot are a serious matter. One type of imperfection is waviness on the surface of the ingot; a line drawn along the crest of a wave would run horizontally around the ingot. This imperfection may be caused by waves on the surface of the metal pool. As the waves reach the solidification line at the periphery of the metal they cause alternate outward and inward bowing of the meniscus at that point with attendant small (but significant) changes in ingot width. Elimination of building vibrations and similar disturbances minimize the occurrence of these surface waves but it is interesting to speculate whether there are disturbances of the metal pool that arise from the electromagnetic forces supporting the liquid metal. These forces are generated by the interaction of currents induced in the melt and the magnetic field produced by the current imposed on the inductor surrounding the melt. The present investigation has been concerned with whether the alternating magnetic field destabilizes the melt surface."

Jan 1, 1994

By Arpad E. Torma

The identification and characterization of lithographic iron and sulfur oxidizing bacteria in the 1940&apos; s. opened up new possibilities and challenges for the mining and metallurgical industries. These were exploited during the 1950&apos;s and&apos; 1960&apos;s, when it was demonstrated&apos; that mining wastes and complex unused mineral resources could be economically treated by bacterially assisted heap and dump leaching processes?. During the 1970&apos;s this technology grew into a more structured discipline called "biohydrometallurgy". In the l980&apos;s efforts were devoted to the identification of a variety of organisms involved in naturally occurring leaching processes. Further efforts dealt with the elucidation, of leaching mechanisms; the leach ability of nickel, coban, zinc, and precious metals; the desulfurization of coal; and diverse biosorpion phenomena. The application of genetic engineering techniques for the improvement of microbial performance was also initiated?. Current trends in biohydrometallurgy include improvement of many of the techniques noted above, as well as application of leaching. technolog.ies to. environmental remediation scenarios. These activities afford considerable opportunities for research in the 1990&apos;s. For example, bioremectiation of abandoned mining and processing sites requires development of new and economically viable technologies capable of removing low concentrations of toxic metals from high volumes of solid and/or liquid wastes.

Jan 1, 1991

By Y. Wang, L. Liu, G. Xu, Y. Lv J. Sheng H. Zhang

In order to increase the service life of large scale coke dry quenching furnaces, the damage mechanism of lining was investigated, and the structure and properties of lining refractories used in cooling section were researched. The results showed that the abrasive wear volume of lining bricks at one fourth height section under skew tunnel was smaller than other sections. The wear loss of mullite brick and dense clay brick used in the lining of cooling section were respectively 8.02 cm3 and 11.65 cm3 in fifteen minutes. The mullite brick was laid with clay brick alternatively. By the different wear rate, the surface of lining was rough and uneven in the later service life, and short brick was easily dropped from lining. During the service, the basis wore off more easily than the aggregate. It is necessary to improve the wear resistance property, which will increase the service life of cooling section’s lining for coke dry quenching furnaces.

Jan 1, 2016

By W. Hoffelner

Plasma technology has become increasingly important for the treatment of several types of waste (toxic, nuclear, metal-bearing scrap). Plasma furnaces combine the advantages of a closed hearth process with a very versatile (several plasma gases can be employed) and effective heat source. It can be successfully used for recovery of metals with subsequent purification and/or vitrification of residuals from drosses or filter dusts.

Jan 1, 1994

By Steve Naruk

Microscopic point-count analyses, although time-consuming, provide detailed mineralogical information which is not obtainable by any other means. Such information can be invaluable for evaluating mill circuit behavior. In comparing two months of operation of a Cu-Pb-Zn sulfide flotation circuit, chemical analyses show that higher copper recoveries and concentrate grades were obtained from lower grade ore, but they provide no explanation of how the improvements were obtained. Quantitative micro-scopic analyses, on the other hand, show the following: 1. There was no change in the identity of the Cu-bearing minerals. 2. Increased copper recovery was achieved primarily by increased recovery of chalcopyrite middling particles. 3. The increased recovery of chalcopyrite middling particles also increased the amount of gangue entrained as locked particles. 4. Increased rejection of free gangue particles, particularly those finer than 25 microns in size, resulted in a net decrease in gangue content.

Jan 1, 1981

By C. Lupi

The electrorefining of primary copper is a well known technology: in this work copper scrap was directly processed in the same way. he copper and copper alloy scrap was previously pressed by means of a 20 tons apparatus in order to avoid pyrometallurgical operations. The samples obtained in this manner showed a good compactness so that they were used as anodes in the electrorefining tests. The tests were carried out on anodes made by copper scrap, copper alloy scrap and a mixture of the two. The electrorefining tests were performed at both 303 and 333 K, in a perspex cell having a volume of 500 ml using a current density of 250 A/m2. The cathode used was always a sheet of pure copper and the electrolyte composition was 40-50 g/l Cu as CuS04 and 150-200 g/l H2SO4. Current efficiency in the range of 92-97% and specific energy consumption ranging from 0.14- 0.20 kWg of copper were reached in all the tests. The refined copper deposits were analyzed by AAS to verify their purity and observed by SEM to highlight their morphology.

Jan 1, 1998

By Anne Kvithydl

Printed circuited boards contain considerable quantities of valuable metal, while also containing many environmental pollutants making them unsuitable for landfill. In this study the decomposition of common plastics used in printed circuit boards were studied. Polytetrafluoroethylene (PTFE), polyvinyl chloride (PVC) and polyethylene (PE) were heated in both CO, and argon atmospheres using a thermo-gravimetric furnace (TG) coupled to a mass spectrometer (MS). Soda ash Na,C03 and baking soda NaHC03 were used as reactants. The degradation temperatures and evolved gases are presented for single plastics and mixtures. Mixed plastics are shown to behave as a sum of the individual plastics. The mass loss temperature is the same in CO, and argon. However, less residue is formed when heated in CO,.

Jan 1, 2008

By Peter Bates

"HIsmelt has faced and overcome many challenges in the understanding and development of injection technologies that satisfy process and engineering requirements for further scale up to a commercial plant.An overview of the design basis of bottom and top injection systems with plant results are described in this paper.IntroductionAn appropriate way to introduce this paper is to initially reflect on the genesis of the HIsmelt Process.It is appropriate that Professor Womer is the one we are honouring as it can be claimed that by the involvement of CRA in the WORCRA process that the concepts for irijection systems in iron and steel pyrometallurgical processes achieved significant attention by the company. The development of water cooled injection lances and their application injecting solids and gases with success was certainly a pre-cursor to the development of other injection systems commonly used today in arc furnaces and for top injection at HIsmelt.HistOrically it was the work of Savard and Lee in Canada with shrouded tuyeres and the subsequent commercialisation of this technology at the Maxhiitte Steelworks spawning the suite of bottom oxygen blown process as known as QBOP; OBM and the subsequent combined blowing process such as KOBM that first commercially succeeded in injecting solids under a molten metal bath. The next progressive step from the injection of calcined lime in the technology development was the injection of coal for coal gasification as developed by Klöckner technologies being called KG, KSG and KMS and also the injection of coal for increased scrap melting.A paradigm shift in thought process to leap from steelmaking and coal gasification to direct smelting by injecting coal and iron ore into a molten metal bath in the correct stoichiometric ratio to maintain the bath at a constant temperature and carbon level was the true genesis .of HIsmelt.A good overview of the state of the art of tuyere type injection technology is given in Ref. 1."

Jan 1, 1996

By Cheng Pan, Qiugang Yuan, Xuewei Lv, Mei Liu, Enguang Guo

Land-based nickel resources include nickel sulfide and nickel laterite. With the consumption of high grade nickel sulfide, use of nickel laterite has received more and more attention. The mineralogy and sintering behavior of limonitic nickel laterite with high iron and low nickel and silica was studied to offer technical support for producing ferronickel through sintering–blast furnace route. The mineralogy results showed that the main phases in this kind of nickel laterite are goethite (FeO(OH)), gibbsite (Al(OH)3) and NiFe2O4. The TGA (Thermogravimetric Analysis) and DSC (Differential Scanning Calorimetry) revealed hydroxide minerals in addition to absorbed water. After the sintering experiments the chemical composition, phases present (XRD analysis) and physical properties of the sinter were studied. The content of FeO in the sinter increased with increasing basicity up to 1.3, and then decreased with further increase in basicity. The yield of sinter increased (from 73% to 80%) with increase in the basicity from 1.1 to 1.7, and then the yield decreased with the further increase in basicity. Mg(Ni)(Fe,Al)2O4 is the main phase in the sinter while MgCaSiO4 and Fe2SiO4 is the main binder phase when the basicity is 1.1~1.5, and MgCaSiO4, Fe2SiO4 and SFCA is the main binder phase when the basicity is 1.7~2.1.

Jan 1, 2014

By B. Farouk, Y. G. Kim, D. Apelian

"Continuous strip casting has received considerable attention in recent years due to its economic advantages with increased energy savings and the elimination of intermediate processing steps. A promising concept in strip casting is the twin-belt (Hazelett) process which incorporates two cooled continuously moving thin metal belts wrapped around pulleys which tension and drive the belts at a predetermined speed. Molten metal is introduced at the entry end of the caster through a tundish and feeding nozzle into the mold. The twin-belt process has been successfully used with non-ferrous metals such as aluminum, copper and brass, and is a prime candidate for strip casting of ferrous materials. A numerical model has been developed which predicts the interface locations, the temperature fields in the solid and liquid regions of the cast and the velocity fields of the liquid metal at the entrance region of the twin-belt caster. The process variables considered are the velocity and cooling conditions of the belt and the nozzle shape. A body fitted coordinate system is used to track the front locations and to solve .the Navier-Stokes equations in the liquid region. Results obtained can help design efficient casters for thin strip steel castings. The development of the numerical model is presented, and sample results are discussed. I. IntroductionContinuous strip casting of steel has attracted world-wide concerns in recent years due to its economic advantages with increased energy savings and the elimination of intermediate processing steps. New methods of thin strip casting of steel are developing. One of the promising concepts is the Hazelett process, which is being used in nonferrous applications. The process incorporates two continuously moving, intensely cooled, thin metal belts. Metal blocks linked together are sandwiched between the moving belts and form moving side mold walls.In this work, the freezing front position, the temperature field and the liquid region flow field will be analyzed for the strip casting of metal using the twin belt caster (the Hazelett process). Up to now almost all theoretical analyses undertaken of the continuous casting of metal [1-3] have used a heat conduction equation, assuming slug flow in the liquid region. The effect of convection in the liquid pool during continuous casting were first investigated by Szekely and Stanek [4]. They considered potential flow between the feed metal orifice and the liquidus front, and slug flow in the mushy and solid regions of a vertical static continuous casting process for steel. Viscous effects and natural convection affects were not included Kroeger and Ostrach [5] studied the effect of natural convection flow in the liquid pool during solidification for a pure metal."

Jan 1, 1986

By Jianhong Dong, Min Chen, Cuihuan Huang, Bo Li, Nan Wang

"Scale layer can be formed on the slab surface in the areas of secondary cooling and strand discharge during continuous casting process. From 1000 °C -1200 °C, the influence of steel composition on the stable oxide phases inside scale layer, particularly the types of alloying elements including aluminum, silicon and chromium, is investigated under different partial pressures of water vapor by the calculated predominance diagrams of iron oxide as well as its intermediate compounds formed with other metal oxides, and the stable oxide phase composition within scale layer under the working condition of secondary cooling is discussed. At lower partial pressure of water vapor, only a iron spinel (or ferrosilicate) phase is the stable phase with any alloying element contents in steel composition, whereas the stable phases are FeO and iron spine! (or ferrosilicate) inside the scale layer at higher partial pressures of water vapor .IntroductionOxide scale formation on the surface of cast and rolled products because of oxidation by the surrounding oxidizing atmosphere is a significant disturbance factor in steelmaking. The yield loss of iron because of scale formation is considerable during continuous casting and hot rolling process. Surface quality more often is impaired by scale property, which increasing the difficulty of quality assurance, dimensional accuracy and performance control. Furthermore, a potential source for subsequent surface cracking (hot shortness) can be caused by the enrichment of scrap residuals (Cu, As and Sn) at the steel substrate surface as a result of steel oxidation [1-2]. In flat products manufacture via thin slab casting technologies, these phenomena are particularly pronounced and require enhanced development efforts in descaling efficiency [3].Compared with the scale formation in continuous casting, the quantity of scale formed during hot rolling and reheating in the rolling mill is larger, and control of scale formation and descaling is a long-established task in hot rolling. Therefore, extensive research and development work have been carried out, including the effects of heating and rolling temperature on the thickness and microstructure of scale layer, heating time and furnace atmosphere, cooling mode, and steel composition on the scale formation, more attention has been given to the control of scale formation during reheating and hot-rolling process. On the other hand, hardly any specific efforts and countermeasures are taken in continuous casting, and very less research has been done despite the network-type crack on the as-cast strand surface caused by the subscale enrichment of scrap residuals [ 4-7]."

Jan 1, 2014

By Isıl Kerti, Sibel Daglılar, Sinem Yıldırım

In this study, effect of rolling and coiling temperature in thermo mechanical controlled process (TMCP), on the microstructure and mechanical properties of dual phase (DP) steel according to martensite volume fraction (MVF) rate was investigated. By using various finishing mill exit temperature and cooling conditions that is controlled laminar cooling system, the microstructural evolution of coil improves the mechanical properties with lower costs and higher productivities, in comparison to the heat treatment after rolling. The main part of the paper contains the result of tensile, yield and microstructure properties of DP600 steel produced on hot strip rolling plant and run- out table line. The results show that a higher MVF and an increasing cooling rate after the last deformation raised strength of the DP600 steel. The yield strength and ultimate tensile strength increase by decreasing coiling temperature.

Jan 1, 2015