By K. Tanaka, J. D. Mote, J. E. Dorn

It) an attempt to ulLcoce.lP the operative strain-rate-contl-olliy: dislocation nieclzanistns, specially oviented sizgle clystals of the intel-nzediate 1zexagonal phase containing Ag plus 33 at. pct A1 were tested in tension over a wide range of temperatures. Slip was observed to take place by the {0001} <1120> {l100} mechani fracture took place across the(i100) plane and winning occurred by the (i01Z) ?lechanisn. Basal slip exhibited a strong yield point over the -alzge from 77 to 450°K, the upper ,esolved shear st]-ess having the exceptionally high value of 10,500 psi over this entire ?-a?zge of tenzpei,atuves. The critical 9-esolved shear stress for prismatic slip decreased f7-om 48,000 psi at 4.3"K to 23,000 psi at 170°K (Region 1) follozcirg zt:lzich it decl>eased sloz&ly to 21,500 psi at 475°K (Res&apos;on II); from 475" to 575°K (Regioz III), the c7-itical esolced shear stress dec&apos;-eased precipitously to 2000 psi; and from 575" to 750°K (Region IV) it decreased less afi&apos;dly to a low value of about 500 psi. Pvistintic slip in Region I was pobably controlled by the tliel-nally activated riecharzisui of nucleation and g,-ozcth of kinks in dislocations lying in Peierls potential troughs. In Region II for prismatic slip the critical 1-esolved shear stress was slzocn to be deteemined by sh0l.t-range 01-dering, Overall the forgiorz fo basal slip, 7.c.lre1-e a Strong yield-point phenorlienu ia7as observed, the critical vesolved slzea?-stress was shoztn to be determined by n conibirzation 0-f Szizuki locking and short-range-order Izavderzizg, The precipitous decrease in the critical resolved shear stress with increase in ter,/pe7-atrir-e over Region HI was tentatively ascribed to a decrease in the degree of slort-)ange 07-del;iqq (0)- clusteing) and also the effect of fluctuations the degree of o?der, It is at pgreser2t zrtzce)taitz as to 1t1hethe1- these or other possi1)le effects are also ,esponsible. fo- the data obsel-ved 172 Region IV. 1NTEREST in inter metallic compounds stems not only from their role in dispersion hardening of polyphase alloy ystems but equally from their potentialities for high strength, hardness, and stability not only at atmospheric temperatures but especially at elevated temperatures. As summarized in a re- cent symposium of the Electrochemical Society on "Mechanical Properties of Inter metallic Compound", most of the experimental evidence regarding the mechanical behavior of intermetallic compounds centers about the effect of temperature on the hardness and ductility of polycrystalline specimens. The available data reveal that the plastic behavior of intermetallic compounds might be rationalized in terms of the usual dislocation mechanisms appropriate to a solid solutions providing the additional complexities arising from crystal structure, long-range ordering, short-range ordering, and defect lattices are taken into consideration. It is apparent, however, in terms of the history on a solid solutions, that a complete detailed mechanistic rationalization of dislocation processes may not be possible until the deformation processes are studied in single crystals of intermetallic compounds. The present paper contains a preliminary report on the plastic behavior of single crystals of the hexagonal Ag-A1 intermetallic phase over a wide range of temperatures. The results confirm the thesis that single crystal data provide a most effective method of identifying operative dislocation mechanisms in intermetallic compounds. EXPERIMENTAL TECHNIQUES Several factors prompted the selection of the hexagonal Ag-A1 intermetallic phase for this preliminar investigation on the plastic properties of single crystals of intermetallic compounds: 1) This phase has a wide solubility range5 which would permit future investigations on the effect of composition and axial ratios on slip mechanisms. 2) Although it undoubtedly exhibits short-range ordering (or clustering) this intermetallic phase is free from complexities arising from long-range ordering.6 3) Since the atomic radii of aluminum and silver are practically identical, the possible complications due to Cottrell locking are minimized. 4)Whereas the dislocations on the basal planes are expected to dissociate into Shockley partials and are thus susceptible to Suzuki locking, those on the prismatic planes probably remain complete. 5) The axial ratio, being 1.61, is almost ideal, suggesting that short-range ordering may be almost spherically symmetrical. The present investigation was conducted exclusively with the hexagonal Ag-A1 alloy containing 33 at. pct Al. Preliminary investigations revealed that this alloy undergoes basal slip by the (0001)

Jan 1, 1962

By R. S. Hooper

In attempting to describe recent mining developments at the Bunker Hill mine, it may be well to recall first the old days of hand mining when holes were laboriously drilled by hand to a maximum depth of three feet, and were shot one or two at a time, in order that the miner could take advantage of every slip, crack or bedding plane, and so save as much drilling as possible. Broken muck, of course, was loaded by hand shoveling into wheelbarrows or small cars, and heading advances or stope tonnages were governed by the number of men that could find room to work in any given place. The first big improvement over these old methods was the introduction of the reciprocating type of air-powered rock drill. This innovation, crude as it was, enabled the miners to set up a machine and drill a complete round of holes in one shift; but broken muck was still loaded by hand, and the size and rate of advance in headings were limited by time required to remove the broken rock. The next improvement of consequence was the appearance of the hammer-type rock drill, which greatly increased drilling speed over the reciprocating type, and made possible the completion of a full cycle in one shift, by the use of crossbars in headings, and permitted drilling and mucking to be carried on at the same time. Rock drills continued to improve as time passed, and finally the smaller and more efficient mucking machines appeared on the scene, and it became possible to muck out a round of broken rock and have a clean setup for one or more drill columns and machines. A complete cycle of mucking, drilling, and blasting was completed in one shift with an average advance of five feet. These conditions prevailed for several years, but as the mine grew deeper, the distances to transport the workers grew longer, and this fact together with the shortening of the working day, soon presented the problem of attempting to complete a cycle of operations in a shift of only six hours at the working faces. Anticipating this condition, the operating heads at the Bunker Hill had started an intensive study of more and better mechanization, and over a period of comparatively few years have adopted and placed in service methods and machines that make it possible for a three-man crew to consistently advance headings seven by nine feet in cross section, at the rate of eight feet, and more, per shift, doing all the mucking, switching, drilling and loading. These improvements consist of the following major items: I. The development of a light, flexible, easily transported jumbo equipped with pneumatic columns (Fig I), that has decreased the "setting up" and "tearing down" time an average of 11/2 hr per shift, Or 25 PCt of the available working time. These jumbos were developed at the Bunker Hill mine by members of the staff and consist of two pneumatic columns attached to a suitable carriage. They fold

Jan 1, 1949

By G. W. Powell

G. W. Powell (Ohio State University)—Appleton and Bever measured the quantity Es which, for a solid torsion specimen, is basically an average quantity. Es is the amount of energy stored in a solid torsion specimen strained to a surface shear strain of divided by the total number of gram-atoms of alloy in the specimen. It would seem more meaningful and rigorous to deal instead with the quantity which is the energy stored per gram-atom of an alloy uniformly strained to the shear strain . The purpose of this discussion is to demonstrate that as a function of y is readily obtained from the torsion data. radius of the torsion specimen, shear strain at the surface of the torsion specimen density of the alloy, atomic weight of the alloy, and total energy stored in unit length of the torsion specimen. The energy stored in unit length of an elemental tubular section of the torsion specimen is, as given by Appleton and Bever, where E is expressed as calories per gram-atom. The energy stored in unit length of the torsion specimen is

Jan 1, 1963

By Max Barber

PRESENT equipment and practices in open-pit mines of the Lake Superior iron ranges have been described recently in some detail by A. H. Hubbell.1 It is anticipated that any further improvements will be the result of gradual evolution of present methods and equipment, just as those now used have been gradually evolved from earlier methods. An exception to the process of gradual evolution during the last decade has been the adoption of electric power for operating shovels and trains in open-pit mines, but it is not expected that any such revolutionary changes will be made in the future. The use of Diesel, engine equipment will gain considerable headway, no doubt, and will find favor in certain lines of operation as improvements and adaptations are evolved to meet particular requirements. The question of installing belt conveyors for handling material from deep mines of restricted area, where haulage grades become a serious consideration, or even for transferring earth, rock, or ore material for distances of several miles, is now being studied and some very interesting data are being obtained.

Jan 1, 1932

By David L. Holt

The contribution of grain boundary shear to total elongation, CS/E&apos;, has been measured in an Al-Zn eu-tectoid alloy that was quenched from above the invariant temperature, then annealed at 250° C to a grain size of&apos; 1.8 p. At 250°C, ks/E&apos; is low at both high and low strain rates, but reaches a maximum, estimated as 60 pct at an intermediate rate of 5 X 10 per rnin. Rate sensitivity, as measured by the index m = a log a/a log E&apos;, follows the same trend, and furthermore the maximum values of m and -cur at approximately the same strain rate. This result, combined with the metallographic observation that boundary migration enhances boundary shearing, is interpreted as supporting a previous suggestion that the high rate sensitivity characterizing super-plasticity is the result of combined boundary shearing and migration. It is suggested that the latter event relieves stress concentrations at triple points, and smoothes boundaries so that stress is governed largely by a viscous boundary shear. GrAIN boundary shear has been considered in relation to superplasticity in several recent papers.&apos; The problem has been to explain the high strain rate sensitivity of flow stress, and the variation of rate sensitivity with strain rate (E&apos;) and grain size (L). The requirements for superplasticity, small L and high T, suggest the reasonableness of an approach to high rate sensitivity involving grain boundary shear. Further support came from experiments on the A1-Cu eutectic alloy,&apos; where it was found that strain rate sensitivity of cast material annealed to produce an equiaxed, micron-size grain is always low; taking as an index of rate sensitivity m = a log a/a log <, m < 0.3. However, m in hot-worked alloy of comparable grain size can be as high as 0.7. In the cast and annealed material, each phase is a single crystal, the only boundaries are interphase boundaries, and it is, consequently, geometrically impossible for boundary shear to contribute to deformation in any major way. Other observations (for hot-worked material) were a-L at constant (low) strain rates and indications that the rate of recrystallization was enhanced as strain rate increased. As a result of this work, it was proposed that high rate sensitivity arises from a deformation mode of boundary shear associated with boundary migration. Migration serves to relieve stress concentrations at triple points, and smoothes boundaries so that they assume properties of fluid films. On the other hand, the low rate sensitivity observed at high and low strain rates reflects deformation of bulk material. Measurement of the variation of grain boundary shear with strain rate and m have not yet been made. Such measurements are important, especially in view of a proposal, differing in detail from the above, that high m arises merely from a transition between a grain boundary shear mode of deformation at low rates to a transgranular mode at high rates.2&apos;4 In the present work, the contribution of boundary shear to total deformation is measured and in addition metallographic observations are made on surfaces of deformed specimens to look at the interaction between boundary shear and migration. The Al-Zn eutectoid alloy was chosen for its homogeneous, fine-grained structure, which is obtained readily without hot-working. It has also been the subject of a previous phenom-enologically directed study. EXPERIMENTAL Material. Compression specimens, cross section 4 by + in., length \ in., were machined from a sand-cast ingot of composition 77.5 wt pct Zn, 22.5 wt pct Al. (The melt was prepared from 99.9 pct Zn and 99.99 pct Al.) After homogenization at 375°C for 50 hr, the specimens were quenched in brine and removed before the heat evolution that accompanies de -composition of the high-temperature phase.5&apos;6 The resulting microstructure, see Fig. l(a), was too fine for grain boundary sliding to be easily studied; coarser structures were obtained by annealing for various times at 2 50°C. Annealing was terminated by a brine quench. Final average intercept lengths between all grain boundaries (both interphase and those lying in a phase), L, were: 0.5 p [annealed for 15 min, Fig. (a)], 0.8, 1.1, and 1.8 p [Fig. l(b)l. Testing Procedure. An Instron machine was used for most of the compressive deformation. Tests were of two types: those in which crosshead velocity was changed in steps to measure m as a function of strain rate15 and tests at constant velocity to a fixed (engineering) strain of -0.2 (20 pct). Stress reached a steady-state value (a) which was plotted, on a logarithmic scale, against log strain rate (E&apos;). An alternate and equivalent evaluation of m was to take the slope of the log o vs log 6 curve. Time at temperature before testing was 15 min. Strain rates covered by the Instron (4 x lo-&apos; to 4 x 10&apos; per min) were insufficient; at a higher rate of 5 x lo2 per min a gas-operated testing machine was used, the gas driving a piston to compress the specimen at a controlled velocity.&apos; To obtain points on the log a vs log E&apos; curve at low rates, specimens were compressed by a dead weight. strain rate was an average value computed by dividing strain at the end of test by loading time. In some tests strain was measured at fractions of the loading time; creep rate was found to be reasonably constant.

Jan 1, 1969

By D. W. Smith, C. H. Mathewson

In a series of papers published recently,&apos; R. F. Mehl and associates have studied the characteristics of form and orientation of many segregate structures and have found diversified conditions which can be explained only by postulating some specific kind of cooperative mechanism permitting the matrix lattice in some favorable region to transform into the segregate lattice in an adaptable region presenting a geometrically similar arrangement of atoms. We have collected the published data on crystallographic relationships of this sort, chiefly derived from Mehl&apos;s work, in Table 1. It is evident at once that the crystal structure of the matrix does not uniquely determine the location of the plate structures or other forms assumed by the segregate. Thus, the first seven items in the table represent precipitation of platelike forms from a matrix of face-centered cubic structure, but these plates are found stratified along planes of form {1111, {loo), {110) or another unidentified form, depending upon specific conditions involving the nature and concentration of the segregating substance. Again, in a matrix of body-centered cubic structure, plates, needles or stars have been found and the favored inner surface of segregation may be a plane of form (110), (112), {210), or indeed a surface without crystallographic indices defining a bundle of close-packed lattice lines (strings of atoms) taken more or less at random. Such a surface might be formed ideally by revolving one of these parallel strings of atoms around another as an axis. Hanemann and Schroder2 recently discussed these questions, principally with relation to original conceptions concerning the process of

Jan 1, 1932

By G. H. Anderson

During an investigation of the copper-rich portion of the copper-silicon-iron system as part of an extensive research program on P.M.G. alloys, which was begun in 1937 in the research laboratory of the Phelps Dodge Corporation, it became apparent that the binary copper-silicon system below 7 per cent Si needed revision, therefore an investigation was undertaken. Both X-ray methods and microscopic technique were employed. Despite the many investigations that have the clarification of this system as their object, no two successive reports on the system have agreed in placement of the alpha-phase solubility limit, and uncertainty about the secondary phase first to appear has been voiced several times.3,4,5 It was therefore not surprising, when T. Isawa&apos;s6 and M. Okamoto&apos;s7 works were reported at the time we were finishing up our experimental work, to find essential disagreement between their results and ours. But when C. 5. Smith&apos;s latest work on the copper-silicon systema was published just as we were finishing our laboratory report, it was indeed gratifying to find that the latter&apos;s diagram and ours checked in all essential features, except the temperature of the peritectoid line above 830" C. Many attempts were made to retain the beta phase during the present investigation, but none was successful. Isawa,6 however, reports that he has been able to obtain X-ray photograms of the beta phase. The structure, he states, is body-centcrcd cubic with a lattiee constant of 2.848 ,&. at 7.2 per cent Si. Okamoto7 and Smith8 both use the designation Kappa for the hexagonal phase, and to avoid confusion this designation will he adhered to in the present paper. Preparation of Samples The alloys were melted in vacuum in a high-frequency furnace. from copper cathodes containing 99.98 per cent Cu, and specially refined silicon supplied by The Electro Metallurgical Co. This silicon is stated

Jan 1, 1940

By G. H. Anderson

During an investigation of the copper-rich portion of the copper-silicon-iron system as part of an extensive research program on P.M.G. alloys, which was begun in 1937 in the research laboratory of the Phelps Dodge Corporation, it became apparent that the binary copper-silicon system below 7 per cent Si needed revision, therefore an investigation was undertaken. Both X-ray methods and microscopic technique were employed. Despite the many investigations that have the clarification of this system as their object, no two successive reports on the system have agreed in placement of the alpha-phase solubility limit, and uncertainty about the secondary phase first to appear has been voiced several times.3,4,5 It was therefore not surprising, when T. Isawa&apos;s6 and M. Okamoto&apos;s7 works were reported at the time we were finishing up our experimental work, to find essential disagreement between their results and ours. But when C. 5. Smith&apos;s latest work on the copper-silicon systema was published just as we were finishing our laboratory report, it was indeed gratifying to find that the latter&apos;s diagram and ours checked in all essential features, except the temperature of the peritectoid line above 830" C. Many attempts were made to retain the beta phase during the present investigation, but none was successful. Isawa,6 however, reports that he has been able to obtain X-ray photograms of the beta phase. The structure, he states, is body-centcrcd cubic with a lattiee constant of 2.848 ,&. at 7.2 per cent Si. Okamoto7 and Smith8 both use the designation Kappa for the hexagonal phase, and to avoid confusion this designation will he adhered to in the present paper. Preparation of Samples The alloys were melted in vacuum in a high-frequency furnace. from copper cathodes containing 99.98 per cent Cu, and specially refined silicon supplied by The Electro Metallurgical Co. This silicon is stated

Jan 1, 1940

By Edward E. Hicke, Charles A. Stickels

The dihedral angle of liquid-lead inclusions in solid nickel has been measured as a function of temperature from 371 to 816 C at zero pressure. and as a function of pressure up to 50,000 psi at 317 and 593 C. Thermodynamic expressions are derived for the temperature and pressure coefficients of interfacial tensions in this system. A method is presented for obtaining relative tempmature and pressure coefficients from dihedral-angle data, and the resulting values are used in conjunction with the thermodynamic relations to calculate excess properties of the solid-liquid interface. Defining the position of the solid-liquid interface by the condition that the excess concentration of lead is zero, the excess concentration of nickel and the excess entropy at the solid-liquid interface are: where y(593) is the interfacial tension of the nickel grain boundary saturated with lead at 593C and zero pressure. These values are considered reliable to within a factor of two. While similar calculations are not possible for the nickel grain boundary, it is shown that the expwimental results imply that the excess concentration of nickel at the boundary and the excess entropy of the boundary are negative. THE temperature and composition dependencies of interfacial tensions in metal systems have been reported by several authors in the last 15 years.&apos;-&apos; No measurements of the effect of pressure on inter- facial tensions in metals have been reported, although measurements made on nonmetallic gas/liquid and liquid/liquid systems suggest that a measurable effect should exist.6-l2 The purpose of these experiments was to determine the influence of temperature and hydrostatic pressure on dihedral angles in the Pb-Ni system. The equilibrium dihedral angle is expressed as a ratio of interfacial tensions by2: where 8 is the dihedral angle, yGB is the Ni-Ni grain boundary tension, and SL is the solid Ni-liquid Pb interfacial tension. Three sets of ex- periments were run to determine: a) the effect of temperature from 371" to 816°C on the dihedral angle at zero pressure; b) the effect of pressure up to 50,000 psi on the dihedral angle at 371° and 593°C. THERMODYNAMICS The properties of interfaces of most direct concern are the interfacial tension, excess concentrations of various components at the interface and the excess entropy of the interface, S°. These quantities are defined following Gibbs. Consider an interface separating phases a and 0. Construct two surfaces C, and C such that all properties of phase a remain uniform up to C, and all properties of phase 0 remain uniform up to C. The region between C, and Cp is the interfacial region. Let a "dividing surface", D, be constructed in the interfacial region such that it passes through all points "similarly situated with respect to the condition of the adjacent matter."l3 Surface D divides the interfacial region into a portion a&apos; adjacent to phase adjacent to phase . Let a closed curve, C, enclose an area A in D. Erect normal lines to D along C; these lines and the surfaces C,, Cp, and D then enclose volumes V and V&apos; in the two halves of the portion of the

Jan 1, 1964

By R. F. Mehl, J. K. Stanley

THE recrystallization of cold-worked metals is studied ordinarily by determining the temperatures required for complete recrystallization to occur within a given arbitrary time period, usually within 15 min. to 2 hr. The results obtained are conventionally assembled in a three-dimensional diagram relating this temperature to the amount of cold-work (percentage deformation) and the resultant grain size, though sometimes other modes of representation are employed.1 Such three-dimensional diagrams are not complete, for the number of variables exceeds the number represented. The process of recrystallization is characterized by a time-rate, a fact that is not portrayed upon ordinary recrystallization diagrams. It is known that recrystallization consists in the formation of new nuclei and the growth of these nuclei, a process that continues until the matrix is completely consumed and the original set of grains entirely replaced by the new. This knowledge is old.2 Truly heterogeneous reactions invariably proceed by nucleation and growth; the decomposition of eutectoid solid solutions provides an example about which much is known,3 and freezing, originally studied by Tammann, provides the classic example. Although recrystallization is not a heterogeneous reaction .within the orthodox meaning of the term, the mechanism of the process is the same. As in eutectoid inversion and freezing, it should be possible to study the rate of isothermal recrystallization as a function of time, and it should also be possible to analyze the isothermal reaction curve into the component rates of nucleation and growth that determine them.* Other methods, not employing the rates of nucleation and growth, have been used to represent the rates of such reactions, but these in general have been artificial and have not led to progress.4,5? The theory of recrystallization is not in advanced state; if recrystallization data were obtained, in terms of the rate of isothermal recrystallization, and in terms of the rate of nucleation and the rate of growth of recrystallized grains, and in particular if the temperature coefficients of these rates were measured accurately, an adequate theory should be more readily developed.27 Such an effort requires proper experimental technique, but especially requires suitable methods of mathematical analysis to convert measurements made upon a surface of polish into values for the rate of nucleation and the rate of growth and to combine these into a rate of isothermal recrystallization. These methods are now

Jan 1, 1942

By William Klement

THIS note reports the results of some attempts to metastably extend the primary solid solubilities of tin, antimony, and silicon in silver by rapidly quenching these binary alloys from the melt. The procedures employed for alloy preparation, quenching, and Debye-Scherrer X-ray diffraction measurements have been described elsewhere. The lattice parameters obtained for the fcc structures in Ag-Sn and Ag-Sb alloys are presented in Fig. 1, together with the results of Owen and Roberts.4 Alloy compositions are believed to be within ± 0.2 at. pct on the basis of negligible weight losses during preparation and reproducibility of the lattice spacings. Diffraction lines from hcp phases were also detected: the relative visual intensities of the fcc (200) and hcp (10.2) lines were estimated as shown in Table I. The intensities were m for the (200) and w for the (10.2) in a quenched 13.6 at. pct Sn alloy: a lattice spacing for the fcc structure could not be reliably obtained, however. As seen from Fig. 1, the lattice parameters vary linearly with composition up to 8., at. pct Sb and 13." at. pct Sn, respectively, which may be compared with the maximum equilibrium solid solubilities5 of 7.2 at. pct Sb and 11.5 at. pct Sn, respectively. The presence of the hcp phases, which were found together with the fcc phases, is a consequence of the competition1,3 in the nucleation and growth processes during solidification. Both the fcc and hcp phases must be of the same composition for those alloys in the range where lattice parameters increase linearly with solute concentration. Despite much effort with quenched alloys of several silicon concentrations, it has not been possible to obtain lattice spacings of sufficient precision to establish the variation of lattice parameter with composition or the maximum metastable solid solubility: the equilibrium data5 suggest little primary solid solubility of silicon in silver. For alloys containing less than 16 at. pct Si, the Si (111) diffraction line was not observed. For alloys containing 10 to 25 at. pct Si, faint low-angle lines were detected and these could be indexed as the (10.0), (00.2). and (10.1) reflections of an hcp structure with a = 2.87 + 3A. c = 4.52 ± 3A, and c/a = 1.57 ± 2. The 16 at. pct Si alloy was quenched to, and examined at. liquid nitrogen temperatures without any change observed in the proportion of the hcp phase. These experiments were jointly supported by the Atomic Energy Commission and Office of Naval Research under a program directed by Professor P. Duwez. The assistance of H.-L. Luo and A. Abu-Shumays is acknowledged. as is the support afforded

Jan 1, 1965

By Frank Foote, E. R. Jette

Precision lattice-constant measurements have been widely used in the study of cubic solid solutions but as yet have been rarely applied to noncubic solid solutions. (See, however, references I and 2.) With the high precision at present attainable in the measurement of lattice constants, the X-ray method should be readily applicable to noncubic solid solutions. In the work reported here, hexagonal close-packed magnesium was used as the solvent and either lead, bismuth or gold as the solute. In the magnesium-lead and magnesium-bismuth systems the a and c lattice constants were determined as a function of composition, densities were calculated from these lattice-constant data, these theoretical densities were compared with those directly measured and the solid solubility limit was determined on quenched specimens over a considerable range of temperature. In the magnesium-gold system, the solid solubility is very small but we have obtained an indirect check on the solubility limit previously reported. Materials and Preparation oF the Alloys The magnesium used was obtained from the Aluminum Company of America and was 99.987 per cent pure. Impurities as reported On the label were: Fe, Al, 0&apos;004 per cent; Si, 0.009 per cent; Zn, trace; Cu, Pb, nil. The bismuth was Merck&apos;s analytical grade, minimum purity 99.95 per cent. Maximum impurities as listed on the label were: Fe, 0.008 per cent; Pb, 0.010 per cent; Ag, 0.010 per cent; Cu, 0.005 per cent; Sn, 0.003 per cent; Sb, 0.00; As, 0.000; S, 0.01 per cent. The gold was purified by double precipitation with sulphur dioxide. The lattice constants of these three metals have been previously reported.3 The lead used was test lead, silver free and with a maximum of 0.10 per cent heavy metal impurities. The lattice constant 01 this lead has been measured and found to be 4.94057 ± 0.00016 at 25°C. The alloys were prepared by melting together weighed amounts of the constituent metals in magnesia-lined alundum crucibles under an atmosphere of hydrogen purified by passing over magnesium heated to 500°C. The magnesia lining prevented contamination 01 the alloys with aluminum. Vacuum melting could not be used because of the volatility of magnesium. A high-frequency induction furnace was used for the melting operation and the stirring action of the current resulted in thorough mixing of the constituents. The melts were allowed to freeze in the crucible, the ingots obtained weighed about 10 grams. An extremely thin white film formed on the surface of the melts, sometimes covering only a part of the exposed surface. The ingots were filed clean, placed in small iror crucibles with close-fitting lids and indi. vidually sealed into Pyrex glass tubes Before sealing off, the tubes were alter

Jan 1, 1941

By Frank Foote, E. R. Jette

Precision lattice-constant measurements have been widely used in the study of cubic solid solutions but as yet have been rarely applied to noncubic solid solutions. (See, however, references I and 2.) With the high precision at present attainable in the measurement of lattice constants, the X-ray method should be readily applicable to noncubic solid solutions. In the work reported here, hexagonal close-packed magnesium was used as the solvent and either lead, bismuth or gold as the solute. In the magnesium-lead and magnesium-bismuth systems the a and c lattice constants were determined as a function of composition, densities were calculated from these lattice-constant data, these theoretical densities were compared with those directly measured and the solid solubility limit was determined on quenched specimens over a considerable range of temperature. In the magnesium-gold system, the solid solubility is very small but we have obtained an indirect check on the solubility limit previously reported. Materials and Preparation oF the Alloys The magnesium used was obtained from the Aluminum Company of America and was 99.987 per cent pure. Impurities as reported On the label were: Fe, Al, 0&apos;004 per cent; Si, 0.009 per cent; Zn, trace; Cu, Pb, nil. The bismuth was Merck&apos;s analytical grade, minimum purity 99.95 per cent. Maximum impurities as listed on the label were: Fe, 0.008 per cent; Pb, 0.010 per cent; Ag, 0.010 per cent; Cu, 0.005 per cent; Sn, 0.003 per cent; Sb, 0.00; As, 0.000; S, 0.01 per cent. The gold was purified by double precipitation with sulphur dioxide. The lattice constants of these three metals have been previously reported.3 The lead used was test lead, silver free and with a maximum of 0.10 per cent heavy metal impurities. The lattice constant 01 this lead has been measured and found to be 4.94057 ± 0.00016 at 25°C. The alloys were prepared by melting together weighed amounts of the constituent metals in magnesia-lined alundum crucibles under an atmosphere of hydrogen purified by passing over magnesium heated to 500°C. The magnesia lining prevented contamination 01 the alloys with aluminum. Vacuum melting could not be used because of the volatility of magnesium. A high-frequency induction furnace was used for the melting operation and the stirring action of the current resulted in thorough mixing of the constituents. The melts were allowed to freeze in the crucible, the ingots obtained weighed about 10 grams. An extremely thin white film formed on the surface of the melts, sometimes covering only a part of the exposed surface. The ingots were filed clean, placed in small iror crucibles with close-fitting lids and indi. vidually sealed into Pyrex glass tubes Before sealing off, the tubes were alter

Jan 1, 1941

By Hsun Hu, R. S. Cline

In an earlier publication1 it was shown that a single crystal of Cu-4 wt pct Al cold-rolled in the (110)[112] orientation was stable up to 95 pct reduction, although the orientation spread was considerable larger than in a similarly oriented and cold-rolled copper single crystal. When rolled to 99 pct reduction, the copper crystal retained its initial orientation and a high degree of sharpness of texture, whereas the Cu-4 pct

Jan 1, 1969

By Erwin H. E. Gaertner

The brown-coal opencast mines in Germany&apos;s Rhineland have to cope with several problems. Predominant are densely populated areas with highly productive farmland, many railroads, highways, and rivers, as well as towns and farm settlements which have to be removed before or during the lifetime of a mine. Also the ground- water table has to be lowered to keep the deep opencast mines dry and stable. These problems urged a development towards deep opencast mines with powerful machines; the large material movement and the high coal production are the basis for the economic success in working the Rhenish brown-coal deposits. Up to now, bucket wheel excavators with a daily capacity of 100,000 m3 (130,000 cu yd) are in operation. Machines of twice this capacity are under construction. Corresponding to the excavators development, the stackers&apos; capacity has to be increased too. The new stackers will reach a daily capacity of 240,000 m3 (310,000 cu yd). The haulage in the mine is performed by conveyor belt systems, which are arranged in such a manner that the belt lines meet at a belt switching point. Here the incoming lines may be connected to the outgoing ones so as to direct the material flow to the desired receiving stations. At the moment there are conveyor belts in operation with a width of 2.2 m (7.2 ft); the new belts will have a layout for 37,000 t/h (40,770 stph), the width of which amounts to 3.0 m (9.8 ft). All belts and driving stations on benches are shiftable.

Jan 1, 1976

By Dale A. Vaughan, Oliver M. Stewart, Charles M. Schwartz

A. U. Seybolt (General Electric Research Laboratory)—The authors should be commended for adding some important information to our knowledge of the solubility of interstitial elements in metals. It is becoming increasingly evident that the effect of even traces of such elements have very far-reaching effects upon the mechanical properties of the body centered cubic metals. Those who have worked in this area know that the accurate determination of the small solid solubility limits in systems of the type reported by the authors is a quite difficult task, and it is therefore not surprising that frequently the results of different workers are not in agreement. It is instructive, and usually helpful, to plot the solubility results on log weight or atomic percent -1/T coordinates to find out if a straight line is obtained. A straight line is expected because in systems displaying solubilities of the order of 1 to 3 at. pet or less, Henry&apos;s law is usually obeyed—or at least well enough obeyed so that the deviation from linearity is not very appreciable. If Henry&apos;s law is obeyed, one canthen use the Van&apos;t Hoff Equation in the form In N = ?H/RT + C, where N is mole fraction, at. pet, or wt pet for small values, and AH is the partial molal heat of solution of the solute. R and T have the usual significance, and C is an integration constant. If one plots the reported nitrogen solubility values as indicated above, the three points fall reasonably well on a straight line. The oxygen values for the two upper temperatures fall very closely to the nitrogen values as shown in the authors&apos; Fig. 15. However, the value at 500°C departs widely from the straight line established by the data at 1500" and 1000°C. It is, of course, true that one cannot place too much emphasis on the significance of a line established by only three points, but in the absence of reasons for anticipating deviations, data exhibiting wide departures from linearity should at least be examined closely. Fig. 16 shows the log at. pct -1/T plots for the authors Ta-O and Ta-Ndata including a solid circle point at 500°C and 1.8 at. pet for Ta-O, which is simply extrapolated from the two higher temperature points. In addition, the data of R. P. Elliott9 for Nb-O are shown. These points were picked off his curve and are not very exact, but as can be seen they line up well on a straight line. It is interesting, and probably significant, that the slope of Elliott&apos;s results is not far from those of Vaughn, et al. This is probably to be expected because one would anticipate that the partial molal heats of solution of oxyten in these two very similar metals should be not too far apart. AH for Ta-O is about -1900 cal per mol, while for Nb-O it is near -2300 cal per mol. Hence, this lends some support to the thesis that the point at 500°C for Ta-O is much too high. The data of Gebhardt and Preisedanz10 are also plotted, and it is seen that their data while lying on a linear plot, have an appreciably steeper slope. The possible reasons for this will not be discussed here except to point out that their pressure-composition data show anomalies which suggest that they may have been dealing with a different equilibrium from that being discussed. There is another consideration which would also suggest that the solubility at 500°C is lower than shown. The solubility values were obtained by the classic method of first establishing a lattice parameter-composition curve. This the authors did, and there is probably little doubt that it is quite accurate. Such a plot is generally almost error-free because it has a self-correcting feature in that any deviation from linearity makes a data point immediately suspect, and subject to confirmation. Unfortunately, this is not true with respect to the actual solubility values. These are obtained ordinarily by taking an alloy containing more solute than is soluble at some temperature and then thermally

Jan 1, 1962

By I. M. Bernstein

The steady-state creep behaviov of zirconium and zivcaloy-2 was examined in the temperature vatlge 520° to 620°C A1 low stresses the creep rates were cimracterized by a linear stress dependence; at highev stresses the stress dependence was much more pronounced. Temnperature-cycling tests yielded values for the aclivation enevgy for creep. Various tlzeories were examined in the ligltt of- the experimental re-sults and it mas concluded that the low-stress creep behavior is the result of the stress-direcled diffusion of vacancies along gain boundaries. It has been observed,"&apos; usually under conditions of high temperature and low stress, that creep deformation can occur for which the steady-state creep rate is linearly dependent on the applied stress. For magnesium and certain magnesium alloys, Harris and ones&apos; and ones&apos; have argued that this type of creep occurs by mass transfer as a result of the stress-induced generation and migration of vacancies, along a gradient defined by the stress direction. Jones&apos; demonstrated that the rate-controlling diffusion path is sensitive to grain size and temperature, and that by suitable control of these variables creep could occur by vacancy diffusion either predominately along grain boundaries or through the lattice. Recently, Jones3 suggested from an examination of limited high-stress data for zircaloy-2, composition in Table I, that significant diffusion creep could occur at low stresses, at least between 375" and 500°C, controlled by grain boundary vacancy diffusion. This process could have an important implication in assessing the role of zirconium alloys as a structural or cladding material in certain classes of nuclear reactors, since it predicts creep deformation far in excess of any estimates based on extrapolating slip creep data from higher stress levels. If the diffusion creep process occurs it should be possible to describe the total steady-state creep rate of zirconium and its alloys as the sum of two terms, Eq. [I]; the first term relates to a slip creep process important at high stresses and which is manifested by a much more pronounced dependence of creep rate on stress4 than diffusion creep and the second to a process controlled by mass transfer,5&apos;6 dominant at low stresses: where A and BI are parameters which can depend on structure, Ql and Q2 are the activation energies for the particular creep process occurring, and n describes the sensitivity of the creep rate on stress. It is the purpose of this paper to present some direct experimental evidence in support of this view. It is recognized that other analytical approaches have been proposed to explain data of this kind and these will also be discussed. 1) EXPERIMENTAL PROCEDURE Flat creep specimens (gage length 1 by 0.25 by 0.02 in. approx) were prepared from cold-rolled, argon-remelted, crystal bar zirconium and cold-rolled commercial-grade zircaloy-2, the analyses of which are given in Table I. The specimens were annealed at a pressure of < 10-5 Torr at temperatures from 625" to 675°C for 2 hr and slow-cooled. This treatment produced stable grains of average size (defined here by the average linear intercept) of for zirconium and -4xin. (-10 p) for zircaloy-2. The specimens were tested in a dead load tensile creep rig. The stress was maintained constant by adjusting the applied load after approximately each 1 pct of strain. The specimen temperature was controlled to better than +1°C. This system had a small thermal lag, so that rapid temperature changes were possible. To minimize corrosion, the specimens were tested in high-purity (99.95 pct) argon, further dried,

Jan 1, 1968

By L. W. Holm

This study shows that in the presence of foam, gas and liquid flow separately through porous media representative of reservoir rock. These results were obtained by using tracer techniques to measure the flow of the gas and liquid comprising the foam. Foam does not flow through the porous medium as a body even when the liquid and gas are combined outside the system and injected as foam. Instead, the liquid and gas forming the foam separate as the foam films break and then re-form in the porous system. Liquid moves through the porous medium via the film network of the bubbles and gas moves progressively through the system by breaking and re-forming bubbles throughout the length of the flow path. The flow rates of the gas and liquid are a function of the number and strength of the films in the porous medium. There is no free flow of gas; i.e., no continuous gas phase. On the basis of these results, foam can be expected to improve a water flood or gas drive by decreasing the permeability of the reseruoir rock to a displacing liquid or gas. This improves the mobility ratio and thus the conformance of the flood. INTRODUCTION Foam is formed when gas and a solution of a surface active agent are injected into a porous medium either simultaneously or intermittently. During the past few years, several papers have been published on the subject of foam flow in Dorous media. Foam has been used successfully in the removal of capillary water blocks from producing formations.&apos;&apos;2 The use of foam in gas storage reservoirs to reduce gas leaks and to increase storage capacity has been considered in recent years. Foam has also been investigated as an oil displacing agent,3-5 and as an agent to improve the mobility ratio in a waterflood.6-10 However, the mechanism by which the gas and liquid phases comprising the foam flow through a porous medium has nor been described adequately. Normally, when two immiscible phases (gas and liquid) flow concurrently through a porous medium, each phase follows separate paths or channels. At given saturations of the two phases, a certain number of channels are available to each phase, and as saturations change, the number and configuration of the channels available for each phase also change. The effective permeability of each phase is a function of the saturation of that phase only, and the flow of each phase can be described by Darcy&apos;s law. When foam is present, the effective permeability of the porous medium to each phase is greatly reduced compaced with permeabilities measured in the absence of foam.6,11-13 Based upon the observed flow of surfactant solutions and gas in capillaries, it has been concluded that the gas and liquid may flow separately or they may flow combined as foam. At least four mechanisms have been postulated to explain how fluids flow with foam present: 1. A large portion of the gas is trapped in the porous medium and a small fraction flows as free gas, following Darcy&apos;s law.9 2. The foam structure moves as a body; the rate of gas flow is the same as the rate of liquid flow. 6,13 3. Gas flows as a discontinuous phase by breaking and re-forming films. Liquid flows as a free phase.12 4. A portion of the liquid and gas move as a foam body while excess surfactant solution moves as a free phase.14 It also has been suggested that different flow mechanisms exist for high quality (dry) foams made from dilute surfactant solutions and for foams made from more concentrated solutions. Studies conducted on the flow of foam through capillaries have shown that a plug-type flow occurs and that foam flows as a body.6,15 Fried also has described the flow of foam through porous media as

Jan 1, 1969

By C. K. Eilerts

Finite difference equations were programmed and used to integrate the second-order, second-degree, partial differential equation with variable coefficients that represents the transient linear flow of gas-condensate fluids. Effect was given to the change with pressure of the compressibility factor, the viscosity, and the effective permeability and to change of the absolute permeability with distance. Integrations used as illustrations include recovery of fluid from a reservoir at a constant production rate followed by recovery at a declining rate calculated to maintain a constant pressure at the producing boundary. The time required to attain such a limiting pressure and the fraction of the reserve recovered in that time vary markedly with properties of the fluid represented by the coefficients. Fluid also is returned to the reservoir at a constant rate, until initial formation pressure is attained at the input boundary, and then at a calculated rate that will maintain but not exceed the limiting pressure. The computing programs were used to calculate the results that would be obtained in a series of back-pressure tests made at selected intervals of reservoir depletion. If effect is given to the variations in properties of the fluid that actually occur, then a series of back- pressure curves — one for each stage of reserve depletion — is required to indicate open-flow capacity and related flow characteristics dependably. The isochronal performnce method for determining flow characteristics of a well was simulated by computation. INTRODUCTION The back-pressure test procedurel is based on a derivation of the equation for steady-state radial flow of a gas, the properties of which are of necessity assumed to remain unchanged in applying the test results. The properties of most natural gases being recovered from reservoirs change as the reserve is depleted and pressures decline, and the results of an early back-pressure test may not be dependable for estimating the future delivery capacity of a well. The compressibility factor of a fluid under an initial pressure of 10,000 psia can change 45 per cent and the viscosity can change 70 per cent during the productive life of the reservoir. There are indications that the effective permeability to the flowing fluid can become 50 per cent of the original absolute permeability before enough liquid collects in the structure about a well as pressure declines to permit flow of liquid into the well. The advent of programmed electronic computing made practicable the integration of nonlinear, second-order, partial differentia1 equations2.3 pertaining to flow in reservoirs. Aronofsky and Porter4 represented the compressibility factor and the viscosity by a linear relationship, and integrated the equation for radial flow of gas for pressures up to 1,200 psi. Bruce, Peaceman, Rachford and Rice5 integrated the partial differential equations for both linear and radial unsteady-state flow of ideal gas in porous media. Their published results were a substantial guide in this study of integration of the partial differential equation of linear flow with coefficients of the equation variable. The computing program was developed to treat effective permeability as being both distance-dependent and pressure-dependent. In this study all examples of effective permeability are assumptions designed primarily to aid in developing programs for giving effect to this and other variable coefficients. The accumulation of data for expressing the pressure dependency of the effective permeability is the objective of a concurrent investigation. FUNDAMENTAL DIFFERENTIAL EQUATIONS DIFFERENTIAL EQUATION OF FLOW Linear transient fluid flow is represented by the partial differential equation,

Jan 1, 1965

By K. O. Stamm, B. A. Rogers

Because it is the basis of the economically important operation of hardening steel by quenching, the A3 transformation in iron has been the subject of numerous investigations. Although the contributions to this subject are interesting, no general review will be given here. Readers who care to follow the matter further are referred to the comprehensive summary by Cleaves and Thompson,l which covers the literature to about 1935. Their references to 53 papers on the subject suggest that further investigation is hardly justifiable. However, considerable interest has devel oped recently concerning the reversibility of the transformation. From thermo-dynamic considerations, the transition ought to occur at the same point on heating or cooling, if the change of temperature is sufficiently slow. Yet all of the earlier investigators found a difference of several degrees. Burgess and Crowe,2 who used thermal methods, obtained average temperatures of 912" for Ac3 and 900°C. for Ar3 on electrolytic iron. Their data indicate a considerable range of temperature over which the change occurs, both on heating and on cooling. Terry3 measured the susceptibility in the critical range and estimated from the steepest parts of his curves that Ac3 came at 9I8° and Ar3 at 903°C. Ishiwara4 was one of the first investigators to report a shorter interval between the temperature of the change in the two directions. He measured the change of susceptibility of kaolin-coated samples of steel, in a hydrogen atmosphere, at rater of heating and cooling so low that about 3 or 4 hr. were required for the transformation to complete itself. His results show some variability between samples, but indicate that the difference between Ac3 and Ar3 is in the vicinity of 6°C. Roberts and Davey5 measured the space lattice in pure iron in the vicinity of 900°C. and concluded that a change occurs reversibly between 907&apos; 3" and 910" 3°C., probably between 907" and 910°C. Wells, Ackley, and Meh16 made dilatometric determinations of the Ac3 and Ar3 points in samples of hydrogen-treated carbonyl iron maintained under a vacuum. They used three rates of heating and cooling: 2°, ½°, and .?°C. per min. and found the spread between the two points decreased with low rates. At the slowest rate, the Ac3 transition occurred at 909° to 909. 5°C. and the Ar3 change at 907°C. in three of the samples believed to contain the lowest percentages of alien elements. They concluded that if the rate of temperature change and the content of alien eiements were low enough, the A3 transformation would be completely reversible at 909.50 + 1°C. The question of reversibility is an interesting one and when some iron with especially small percentages of alien elements became available the opportunity to conduct an investigation was welcomed. This iron was prepared by the Division of

Jan 1, 1942