By P. N. Richards, M. K. Ormay

Commercially hot-rolled low-carbon steel strip may have one of two basic types of orientation texture, depending upon the amount of a iron which was present during the finishing passes. The changes in these textures with varying amounts of cold reduction up to 95 pct have been determined for the sheet surface plane and for parallel planes down to the mid-plane. The development of cold reduction textures has been reassessed on the basis of (200), (222). and (110) stereographic pole figures and pole density or inverse pole figure values. In agreement with the literature, it is shown that the textures can be described in terms of partial fiber textures but alternative descriptions are given for one of the fiber textures, in order to more closely correlate with experimental data. One partial fiber texture consists of orientations of the type (hkk)[011] extending from (100)[011] to {322}(011) in agreement with the literature. At moderate amounts of cold reduction, a second partial fiber texture forms with a <331> fiber axis inclined 20 deg to the sheet normal and a range of orientations centered on one close to (1 11)[112] and reaching to (232)[101] or (322)[011]. An alternative description involves a (111) fiber axis parallel to the sheet normal but capable of rotation about the rolling direction with rotation about the fiber axis. ORIENTATIONS developed in low-carbon steel strip after cold reduction are of commercial importance because they control, in part, the final preferred orientations after subsequent annealing. The method of control however is not understood completely. Some preliminary work indicated that the cold-reduced orientations and the subsequent annealing textures of commercial low-carbon steel were dependent on the orientations present in the material before cold reduction, that is, those present in the hot-rolled strip but, to date, the effects of initial orientations have not been extensively investigated. For this reason, much of the information given in the literature on development of preferred orientation is difficult to assess as details of initial texture and processing conditions are often inadequate or are altered by a subsequent heat treatment such as normalizing.&apos; It is known2 that anomalous results for near surface orientations may be obtained if lubrication during cold rolling is not adequate but whether lubricant was used during the experiments has not always been given, nor has the exact depth below the surface at which determinations have been made. A comprehensive review of cold rolling textures has been made recently by Dillamore and Roberts&apos; and more restricted recent reviews are due to stickels4 and Abe.5 Based largely on the experimental work of Bennewitz,1 reviewers have accepted that the preferred orientations produced on cold reducing low-carbon steel can be described in terms of two partial fiber textures as follows: Partial Fiber Texture A which has a (011) direction in the rolling direction and includes orientations within the spread from (211)[011] through (100)[Oll] to (211)[011.]; there is some controversy as to whether it extends as far as the orientation (111)[011]. As Dillamore6 has observed, the extent of this partial fiber texture depends on the intensity levels selected. Partial Fiber -texture B which has a (011) direction located 60 den from the rolling direction in the plane containing the rolling direction and the sheet normal. There are two directions which satisfy these conditions and orientations in this partial fiber texture extend from (21l)[0ll] through (554)[225] to (121)[101]. The orientations {211}(011) are members of both partial fiber textures A and B and it can be noted that a variant of {554)<225> is within 6 deg of a variant of {111}(112). Barrett7 had postulated earlier that, in addition to orientations which would fall into partial fiber texture A, a true fiber texture with a (111) direction in the sheet normal was present after heavy cold reduction. This fiber texture would include orientations such as {111}(011) and {111}(112). Later investigators, notably Bennewitz,&apos; have discounted this, mostly on the ground that the partial fiber textures A and B, as described above, contain all the strong orientations that have been observed. However in other work it has been reported2 that (222) pole density or inverse pole figure values show a continuing increase with increasing reduction by cold rolling and give values considerably greater than for any other low indices plane. Thus it could be inferred that a (111) fiber texture as described by Barrett would be one which becomes more dominant with increasing cold reduction, whereas Bennewitz&apos; concluded that components such as {554)(225) in partial fiber texture B began to decrease in intensity at high reductions. Following Bennewitz, one would expect a decreasing (222) pole density value (parallel to the sheet normal) with increasing cold reduction. Because fiber textures consist of grains with a range of orientations that have one axis in common, it has been inferred that during deformation the crystal orientations rotate about the fiber axis&apos;74 and that the orientations of crystals that at one stage belong to one fiber texture can rotate on further cold reduction into the other fiber texture through an orientation in which the two fiber textures intersect.&apos; For example,

Jan 1, 1970

By J. G. Faller, L. P. Skolnick

The distribution of cobalt and vanadium over non-equivalent crystallographic sites in C14-type Zr(VCo), alloys has been investigated. An anomalous X-ray scattering technique developed by Skolnick, Kondo. and lavine7 by which the separation in the scattering factors of two similar atoms can be enhanced was employed. Six alloys spanning the pseudobinary section ZrV1.6Co0.4-ZrVO.6CO1.4 at 10pct steps showed a nonrandom compositionally dependent distribution. Specifically, at high vanadium content cobalt preferentially occupied sites of type (6h) and vanadium, sites of type (2a; at low vanadium content the reverse was observed. In addition to the distribution fraction the structural parameters x and z were obtained. There was no significant deviation of these parameters from those obtained in the ideal C14 structure. Certain suggestions are made to account for the observed nonrandomness in the distribution of atoms on the two types of sites. INTERMETALLIC compounds of formula AB2 iso-morphous with MgCu2, MgZn2, and MgNi2 are known as Laves phases. Because Laves phases exhibit high symmetry and coordination numbers, the highest possible for an AB2-type compound,1 they are among the most frequently observed compounds in nature. In recent years interest has centered about the purely transition metal Laves phases2-&apos; in efforts to understand the function of atomic size and electronic structure in the formation of these compounds. It has been observed that pseudobinary Laves phase systems often show a variation of structure across the phase diagram. Such a system is the ZrV2-ZrCo2 in which the structure varies from cubic MgCu2 to hexagonal MgZn2 to cubic MgCu2.4 Some understanding about the conditions under which the second modification is stable can perhaps be gained by studying the distribution of cobalt and vanadium atoms on lattice sites in the MgZn2 modification of the system ZrV2-ZrCo2. In both the MgZn2 and MgNi2-types there exist nonequivalent positions open to occupancy by the B element, whereas in the MgCu2 prototype all sites are equivalent. Skolnick, Kondo, and La-vine7 have developed an anomalous scattering technique suitable for this type of investigation. Whereas the influence of size on the formation of a Laves phase is well recognized, no substantial evidence has been put forth in support of the size ratio dependence of a particular prototype. Berry and Raynor8 suggested that RA /RB ratio does indeed affect the type of structure that is chosen, MgZn2 compounds tending to cluster about 1.225 while MgCu2 compounds were found at larger deviations from this ratio. Dwight,3 however, from a study of 164 Laves phases does not believe this generalization to be justified. Electronic effects are certain to play a part in the stability of Laves phases in general and in the choice of a structure type in particular. For example, size along would favor the formation of Laves compounds of Ti, Zr, Hf, Ta, or Nb as the A element with nickel or copper as the B element. The absence of such is attributed to an unfavorable electron : atom ratio by Elliott and rostoker.4 Early experiments of Laves and witte9 with pseudobinary and pseudoternary systems of the three prototypes established the dependence of crystal structure upon electron: atom ratios. They observed that the MgCu2 structure dissolved elements of higher valency until the electron: atom ratio of =1.8 was reached; the MgZn2 likewise dissolved elements of lower valency replacing zinc. witte,6 from calculations of the electron : atom volumes of Brillouin Zones, obtained limits of stability for the prototypes MgCu2 and MgZn2. Elliott and Rostoker4 used these limits with considerable success in the all-transition element Laves phases they investigated. According to witte,6 compounds between the electron :atom ratios of 1.80 and 2.32 were of the MgZn2 type; those above and below exhibited the MgCu2-type structure. On the basis of these limits and an assumed valency of zirconium based upon the near tetra-valence of titanium, Elliott and Rostoker obtained valencies for the first transition series elements. For the Laves phases with which this investigation is concerned, ZrV2 and ZrCo2, the authors calculated electron :atom ratios of 2.54 and 1.56, respectively. These ratios are for the MgCu2-type structure and straddle the stability band of the MgZn2 modification. One could, therefore, predict that a pseudobinary system ZrV2-ZrCo2 should pass through the MgZn2 modification in traversing the composition diagram from one end to the other. Implicit in this assumption is a smooth change of the electron: atom ratio from 2&apos;54 to 1.56. MOSS10 states that his finding the low temperature structure of ZrCr2 to be C15 instead of C14 alters greatly Elliott&apos;s valency of zirconium and hence the assumed valencies of the other metals. Such a quantitative correlation of structure with electron : atom

Jan 1, 1963

By C. W. Haworth, M. G. Hall

THE diffusion of copper in silver has been studied by Sawatzky and Jaumot1 and Cahoon and Youdelis.2 Sawatzky and Jaumot measured tracer diffusion in single crystal specimens but the 12.9 h half-life of CU64 limited the time of the diffusion anneal to about 50 hr, and in consequence the minimum temperature of the investigation was 716°C. Cahoon and Youdelis employed polycrystalline diffusion couples, and measured the interdiffusion coefficient over the range 0 to 2 at. pct Cu. These experiments were performed at temperatures down to 630°C and a discontinuity in the Arrhenius plot was observed at -700°C. The high D-values at lower temperatures were attributed to the effect of grain boundary diffusion. The present experiments were undertaken to investigate this anomaly and study the low temperature region of the diffusion of copper in silver. The method employed single crystal samples and a plated source of copper. Silver single crystals 2½ by 4 in. sq were grown from zone-refined silver bar (>99.99 pct Ag) by the Bridgeman technique, and $ in. thick slices were cut by spark machining. The specimens were electro-polished, and a 2 µm layer of copper was electroplated on to the planar surface at one end of each specimen using a potentiostatic voltage source. The following solution was used for plating: CuSO4 . 5H2O 125 gm H2SO4 (S.G. 1.8) 53 ml H2O 1000 ml The diffusion couples were sealed in capsules, in an argon atmosphere, and were annealed at either 701, 597, or 498°C. The temperature measurements were made to an accuracy of *l°C After the anneal, the penetration of copper into the silver was determined using an electron probe micro-analyzer. 100 sec scaler measurements of the intensity of Cu Ka! X-radiation were performed at 2 to 5 µm intervals along a line normal to the source, with a beam potential of 25 kv. Allowances were made for the background radiation, and the dead-time of the counting system in the normal way, and the intensity ratios were corrected to weight concentration by the method of Duncumb & de-Casa.3 For the analysis of the diffusion profiles, it was first observed that the copper layer did not completely dissolve in the host crystal for the specimens annealed at 498 and 591 whereas for the specimen annealed at 701°C, a single phase solid solution was formed. For the 498" and 597°C specimens, the concentration of copper in the silver at the interface was therefore constant throughout the anneal and the analysis for a

Jan 1, 1970

By Arthur F. Taggart, A. W. Thomas, T.C. Fitt

It was noticed early by operators that high recoveries and flocculation of the sulphide minerals were closely correlated in agitation-froth flotation. Later, this readily visible flocculation was found almost invariably to be due to the binding together of the oiled sulphides by minute air bubbles, and is now known to be characteristic of pulps in which at least one of the mineral species is coated with an insoluble collecting oil. In 1930 it was reported1 that in differential flotation a correlation exists between Brownian movement of particles in the pulp and their nonfloatability, and that Brownian movement and dispersion are likewise correlated, whence it would appear to follow that dispersion of a mineral particle in a flotation pulp denotes a particle condition unfavorable to flotation. In 1934 it was postulated2 that Brownian movement, dispersion and nonfloatability all flow from the condition of the surface of the dispersed particles. It was also postulated at that time that the surfaces of dispersed particles are ionized, the ionized compound being a product of reaction between a component of the particle and a component of the pulp, of a mass solubility of the general order of a fraction of a milligram to I 5 to 20 mg. per liter. It was then further asserted, and has since been confirmed by Bankoff,3 that sulphides so conditioned with soluble collectors as to be floatable flocculate without the intervention of air bubbles as binding media. The present paper comprises an inquiry into the nature of the bound and counter ions in zinc sulphide dispersed by sodium arsenate. A part of its findings was mentioned in the 1934 paper above cited.= The tests show that: I. When powdered granular zinc sulphide is immersed in aqueous solutions of sodium arsenate, arsenate ion is abstracted from solution and anchored to the solid surface, while sulphate and lower sulphoxy ions are concurrently displaced therefrom in substantially stoichiometric quantities. 2. The ion counterbalancing the anchored arsenate ion is zinc. 3. Dispersion and Brownian movement of zinc sulphide are concurrently maxima at an arsenate-ion concentration lying between 0.01 and 0.001-molar sodium arsenate. 4. Any condition or reaction that tends. to remove the zinc arsenate coating from the zinc sulphide particles decreases dispersion and Brownian movement concurrently. Experimental Three samples of zinc sulphide were used. Lot I was C.P. zinc sulphide, washed well be~ond absence of chloride, as shown by test with silver ion. Lot 2 was prepared by precipitation from hydrochloric acid solution of arsenic-free zinc, and was washed as lot I. Lot 3 was prepared by heating a portion of lot 2 in absence of air at 1200° to r300°C. for one hour."

Jan 1, 1943

By Arthur F. Taggart, T. C. Fitt, A. W. Thomas

It was noticed early by operators that high recoveries and flocculation of the sulphide minerals were closely correlated in agitation-froth flotation. Later, this readily visible flocculation was found almost invariably to be due to the binding together of the oiled sulphides by minute air bubbles, and is now known to be characteristic of pulps in which at least one of the mineral species is coated with an insoluble collecting oil. In 1930 it was reported1 that in differential flotation a correlation exists between Brownian movement of particles in the pulp and their nonfloatability, and that Brownian movement and dispersion are likewise correlated, whence it would appear to follow that dispersion of a mineral particle in a flotation pulp denotes a particle condition unfavorable to flotation. In 1934 it was postulated2 that Brownian movement, dispersion and nonfloatability all flow from the condition of the surface of the dispersed particles. It was also postulated at that time that the surfaces of dispersed particles are ionized, the ionized compound being a product of reaction between a component of the particle and a component of the pulp, of a mass solubility of the general order of a fraction of a milligram to I 5 to 20 mg. per liter. It was then further asserted, and has since been confirmed by Bankoff,3 that sulphides so conditioned with soluble collectors as to be floatable flocculate without the intervention of air bubbles as binding media. The present paper comprises an inquiry into the nature of the bound and counter ions in zinc sulphide dispersed by sodium arsenate. A part of its findings was mentioned in the 1934 paper above cited.= The tests show that: I. When powdered granular zinc sulphide is immersed in aqueous solutions of sodium arsenate, arsenate ion is abstracted from solution and anchored to the solid surface, while sulphate and lower sulphoxy ions are concurrently displaced therefrom in substantially stoichiometric quantities. 2. The ion counterbalancing the anchored arsenate ion is zinc. 3. Dispersion and Brownian movement of zinc sulphide are concurrently maxima at an arsenate-ion concentration lying between 0.01 and 0.001-molar sodium arsenate. 4. Any condition or reaction that tends. to remove the zinc arsenate coating from the zinc sulphide particles decreases dispersion and Brownian movement concurrently. Experimental Three samples of zinc sulphide were used. Lot I was C.P. zinc sulphide, washed well be~ond absence of chloride, as shown by test with silver ion. Lot 2 was prepared by precipitation from hydrochloric acid solution of arsenic-free zinc, and was washed as lot I. Lot 3 was prepared by heating a portion of lot 2 in absence of air at 1200° to r300°C. for one hour."

Jan 1, 1943

By Albert C. Harding

For several years barite (BaSO4) production has topped such better known minerals as feldspar and fluorspar in annual tonnage and is now well established among our foremost nonmetallic industries. Description Of widespread occurrence in the United States, barite is relatively soft (hardness, 2.5 to 3.5), inert, heavy (specific gravity, 4.5), and is also called "barytes" (sometimes pronounced "bear-i-tease"), "heavy spar" and "tiff." It occurs with granular and earthy structure but usually has coarse, orthorhombic crystallization. It is commonly white, and although occurring in various shades of red, yellow, and gray, barite always gives a white streak and can be scratched by the ordinary prospecting pick. Its softness and weight are usually sufficient to establish field identification. Another aid is the "rotten egg" odor of H2S which sometimes emanates from freshly fractured surfaces. Barite can be readily distinguished from two other minerals which have somewhat similar occurrences and characteristics. The relatively rare celestite, strontium sulphate, has a specific gravity slightly less than 4.00 and gives a distinctively crimson color in a flame test. The very rare wither-ite, barium carbonate, has a specific gravity of 4.3 but readily effervesces with dilute hydrochloric acid. Occurrence All known commercially important barite deposits in the United States occur as re- placements or cavity fillings in schists, shales, limestones, dolomites, and quart-zites, or as residual deposits from such formations. In Georgia, Tennessee, North Carolina, and Missouri, high-grade barite is recovered as fragments from residual clays covering quartzites and dolomites. In Arkansas, Nevada, and California, barite, usually of lower grade, is mined from replacement deposits. These seven states contributed the entire production reported by the U. S. Bureau of Mines for 1945 as given in Table I. Table i—Crude Berile Sold or used by Producers in 1945 State Short Tons Arkansas................... 260.660 Missouri.................... 225.467 Georgia..................... 110,393 Tennessee................... 32,812 Nevada..................... 28,919 Other States............... 37,811 Total..................... 696,062 (&apos;other states,, included only california and North Carolina. Such a large part of this undistributed production came from California that that state probably outranked both Nevada and Tennessee. For the second consecutive year Arkansas was the leading producing state, particularly worthy of note because there was no commercial production of barite there prior to 1941 and because the entire production of Arkansas has come from one large deposit which is being operated by two companies. Consumption The 1945 consumption as reported by the Bureau of Mines was: 482,442 tons as ground barite 139,288 tons in making lithopone 99,173 tons in producing barium ------- chemicals Total 720,903 tons

Jan 1, 1949

By A. Patton

E. T. McCLEARY, Youngstown, Ohio (written discussion).-Perhaps there is no question before the steel manufacturers of America today that causes them more worry than that of maximum production, together with good quality, and Messrs. Patton and Speller have clearly shown in their excellent paper how this may be accomplished. Any operation that tends to uniformity is certainly conducive to good practice, and as the use of roll scale in the converter eliminates to a large extent the variations in temperature due to varying silicon content in the pig iron, it should certainly give a more uniform product. At the plant of The Youngstown Sheet & Tube Co. the use of roll scale was started in the year 1908. A great many tests have been con-

Jan 4, 1917

By Clarence M. Haight

The general practice in drill sharpening shops, of which descriptions have been written, is about as follows: The bit is heated to 1600" to 1900°F. Then when forged to the proper shape and size in the sharpening machine, the steel is allowed to cool; it is then passed to a hardening furnace where only the end is heated to about 1450" F., and then quenched in cold water, brine, or in brine with oil on top.

Jan 1, 1922

By J. C. Mertz

ACCURATE knowledge of the solid solubilities of the elements that dissolve in the important base metals is needed for guidance in the preparation and heat-treatment of the alloys derived from these compo-nents. While there is still difference of opinion concerning the merits of the X-ray and microscopic methods of determining such solubilities, it is certainly true that the recent extensive use of X-ray diffraction to review the existing constitutional data has revealed many glaring inaccu-racies and has brought about a much improved knowledge of phase-boundary locations, which will inevitably come to include all of the important alloy systems. When the work is done with all necessary precautions it appears that in the majority of cases where the solubilities extend beyond a few tenths of a per cent the X-ray back-reflection technique is capable of furnishing the best of information in this field. For the most prolonged and thorough studies it is obviously advisable to combine the results of several methods, in particular, to obtain an agreement between X-ray and microscopic data. This paper reviews the work previously done on the solubilities of phosphorus, arsenic, antimony and bismuth in copper and, in considera-tion of the uncertainties thus made apparent, presents, new X-ray data obtained with the first three members of this group.

Jan 1, 1936

By G. R. Speich, S. A. Kulin

R. C. Shnay (Dept. of Mines and Technical Surveys, Ottawa, Ont., Canada)-—The authors are to be congratulated on an interesting and informative paper. However, several questions arise when the isothermal formation of martensite .is considered in relation to the formation of bainite at temperatures near the M, point. The reactions in an alloy and in a plain carbon steel would appear to be comparable; and in the course of a recent investigation of the austenite-bainite transformation in a plain carbon steel,Ia the writer has obtained data at temperatures above and below the M, point. These data are in some respects similar to those of the authors and a comparison would seem justified. The steel used in this investigation had the nominal composition: C, 0.80 pct; Mn, 0.20; and Si, 0.20. The course of the transformation was followed by the use of a magnetic balance. The magnetic moment of the specimen as determined by this instrument is directly proportional to the percentage of the total volume of the specimen which has transformed to bainite. ~lf specimens were austenitized at 1850°F for 4 hr, quenched to the transformation temperature, and quickly transferred to the magnetic balance. Readings were taken at regular intervals until the transformation had stopped. A typical transformation curve is shown in Fig. 9. The preliminary curve preceding the S-shaped curve was found at all temperatures above the M, to around 600°F. Both the extent of this preliminary curve and the time interval between it and the S-shaped curve were found to decrease with increasing temperature as was suggested by Davenport and Bain.14 Therefore,

Jan 1, 1953

By Chase Palmer, Edson S. Bastin

While the reducing action of organic matter, of ferrous sulphate, and of hydrogen sulphide has frequently been invoked to account for the deposition of native gold and silver from ore-forming solutions, the high efficiency in this respect of certain of the metallic minerals which form the ore itself has not been suffciently recognized. If a little finely powdered chalcocite is placed in a test-tube arid 2 or 3 cc. of a dilute solution of gold chloride are poured over it, two or three shakes of the tube suffice to remove all the gold from the solution. The color of the solution changes from yellow to pale green, showing that copper is dissolved simultaneously with the precipitation of metallic gold. If a piece of chalcocite is hung in a dilute aqueous solution of silver sulphate (1/40 normal), a coating of silver begins immediately to form on the mineral, and within a few moments a beautiful silver tree has developed, similar to that formed when metallic zinc is immersed in a similar solution. When similar experiments are conducted with other sulphides and with certain arsenides and sulph-arsenides, especially those known to be commonly associated with native silver in ore deposits, it is found that these minerals differ greatly in their efficiency as precipitants, especially in their effect on silver solutions. The tests made with most of the minerals were qualitatipe only, but the reactions of a silver sulphate solution on chalcocite and niccolite were submitted to quantitative study to determine the nature of the reactions involved. Quantitative studies of the reactions with other minerals are now in progress

Jan 1, 1914

By Charles R. Simcoe

The stress-strain curves in the microyield region for various Fe-C solid solutions shown by Davies and Ku are typical examples of parabolic curves defined by the expression a = kEn 111 These data, when replotted on log-log coordinates, as shown in Fig. 9, exhibit three essentially parallel straight lines. It is apparent that carbon increases the flow stresses, but does not affect the exponent n. In other words, the only factor in Eq. [1] affected by in in carbon content is the constant k. As Eq. [1] is written k is the stress at a strain of 1.0. This is unsatisfactory for examining data in the microyield region. Therefore, the equation can be altered to the form: to permit the use of the authors&apos; microyield stress at a strain of 10-6 as k. Extrapolating the curves in Fig. 9 to a strain of 10-6 gives stress values of 2000, 3200, and 5400 psi for 0.008, 0.014, and 0.02 pct C, respectively. These values do not agree exactly with the authors&apos; measured values, but this will not affect the following discussion. The effect of carbon content on the slopes of the stress-strain curves shown in Fig. 2 of the paper by Davies and Ku can be analyzed by differentiating Eq. [2] with respect to strain. Thus: where n is always less than 1.0. Since n is essen- tially constant as a function of carbon content for the data under discussion, the slopes of the stress-strain curves depend only on k and E. If the slopes are examined at various selected Plastic strains. i.e., 10-6, 10-5, and so forth, it follows from Eq. [3] that the dif-ferent slopes for the different carbon contents depend only on the different values of ke=10-6. Thus, the larger ke=10-6, the steeper the linear stress-strain curve will rise with increasing plastic strain. This

Jan 1, 1969

By A. Ahmadieh, J. E. Dorn, Jack Mitchell

A detailed investigation of the disloccrtion mechanisms controlling prismatic, slip in a solid solutions of magnesium containing up to 15.9 at. pel Li revealed that low-temperature prismatic slip is controlled by the Peicrl&apos;s mechanism for all alloy compositions. At higher temperatures slip in the 7.9 at. pet Li alloy was found to follow the diclates of the cross-slip mechanism from basal to prism planes, while the higlier-lilhium alloys exhibited an athermal dejormation process which might be due COARSE-GRAINED polycrystalline aggregates of distilled magnesium exhibit very limited ductility at low temperatures.&apos; The ductility of polycrystalline magnesium, however, is much improved by solid-solution additions in excess of about 8 at. pct to shot-range ordering. The major effect of lithium additions on the low-temperature Shear] stress. for prismatic slip appears to be due to its efftct in lowering the Peierl&apos;s stress whereas (1 increase in the shear stress with increased lithium conlent at higher temperatures might he due to short-range order strengthening. Additions rip to 7.9 (at. pel Li appear to have only minor effects on the slackiug-jaidt energy. Li.2 Although the relative amounts of basal slip and twinning are not materially altered by such alloying, a substantial change takes place in the relative amounts of prismatic slip. Whereas prismatic slip is negligible and limited to regions of high stress concentrations in the vicinity of the grain boundaries in pure magnesium, extensive prismatic slip over entire grains occurs in the higher lithium content alloys. Furthermore, as the lithium content is increased above 8 at. pct, the flow stress for polycrystalline aggregates decreases. Comparison of the single-crystal data on pure magnesium for basal slip by Sheely and Nash3 and those for prismatic slip by Flynn, Mote, and Dorn4 indicates that the critical resolved shear stress for prismatic slip is much above that for basal slip.

Jan 1, 1965

James W. Neill, Pasadena, Cal. (communication to the Secretary*):—Professor Hofnlan&apos;s paper brings the art up to date. As I was one of the pioneers in this business, I beg to give the following incomplete data regarding my efforts in this line. In the year 1883, while I was in charge of the smelting-operations at Mine La Motte, Mo., there mas at the concentrator an unusually large protluction of a middle product, locally called " iron," which carried considerable values in nickel and cobalt, and which it was desirable, for this reason, to treat by itself. The works could not spare a furnace for the purpose; and to handle this product I improvised a " roast-hearth " from an old " lead-hearth." This was a small cast-iron furnace of the uslial construction, about 2 by 4 ft. in dimensions, with a hollon- cast-iron back, through which the wind circulated before entering the tuyeres. I had a cast-iron grate made to fit this hearth, and placed it tlush with the lip, or apron, and above the tuybres. On this grate, which had round holes about 0.25 in. in diameter, and a total surface of about 20 by 40 in., I roasted the nickeliferous pyrite product; starting the fire with kindling, then adding charcoal, and then gradually feeding the sulphides with a shovel, so as to cover the fire, choke down blow-holes, and get an even bed. Blast at a pressure of 3 or 4 oz. was supplied by a Can-blower. When a cake of roasted material had formed, it was removed with a steel bar, or fork, to the lip of the furnace, and thence into a wheel-barrow. The fine material which had renlained unmelted, but very hot, on top of the cake would promptly ignite when the cake was broken up and removed. The fire would then be covered with fresh material and

Jan 1, 1911

By Jean Howard, E. V. Walker

ManY papers have been published during the last few years on the formation of cube texture in 3 1/4 pct Si-Fe, e.g., those of Assmus, Detert, Dunn, and Walter.1,5 All are concerned with the formation of the texture by a process involving secondary re-crystallization and the relative surface energies of (100) and other planes under certain conditions of annealing. The authors have found that cube texture can also be produced by heavily cold rolling strip in which the cube-on-edge texture has first been formed. Cube texture develops on annealing, but in this case it is not accompanied by secondary recrystallization. The starting material is a sintered compact, the preparation of which has been described elsewhere. Using a conventional processing schedule employed for producing commercial silicon-iron with the cube-on-edge texture, the sintered compact is cold rolled to such a thickness that, after annealing in pure hydrogen for 24 hr at 1350&apos;~ to produce the cube-on-edge texture, the final thickness required can be obtained by giving a further cold reduction of 85 pct. Cube texture is developed by annealing at -900~~ in pure hydrogen: it has been produced in strip up to 0.024 in. thick. The microstructure of the strip consists of a mass of small primary grains within the boundaries of the much larger secondary grains which ex- hibited cube-on-edge texture before the final cold roll. If the strip is annealed at -1000 after the 85pct reduction, secondary recrystallization begins to take place, provided a strong cube texture is present. On raising the temperature more secondaries grow, complete secondary recrystallization being obtained on annealing at -1150&apos;. From this it is concluded that the secondary crystals are produced by the texture inhibition mechanism: they show (110) and (111) planes in the surface of the strip, the former being the more numerous. It has been observed that the more perfect is the (110) [001] texture prior to cold rolling by 85 pct, the further from the ideal is the (100) [oo].] texture. A similar treatment applied to high quality commercial grain-oriented silicon-iron strip failed to produce cube texture. The tilt and rotation of the [loo] from the rolling direction was less than 10deg, but (to within a few degrees) the planes (130), (450) and (210) lay in the surface of the strip. Acknowledgment is made to the Engineer-in-Chief of the British Post Office for permission to use the information contained in this note.

Jan 1, 1962

By W. M. Rust, W. D, D. W. Mounce

The almost universal acceptance of electrical logging by the petroleum industry calls for a critical examination of the physical bases of the common methods. This is particularly needed for the natural potential log. The conventional explanations are based on the phenomena of electrofiltration and electro-osmosis. However, experimental data show that they fail to give a basis that is quantitatively sound. Moreover, they lead to interpretations of details of electrical logs that are erroneous. It was found experimentally that when a plug of shale is placed in a chain of dissimilar electrolytes, a current flow results. Experiments on oil-well cores and fluids similar to those existing in wells show that potentials are set up which are in reasonable agreement with those encountered in electrical logging. Doubtless other sources of potential are important but this explanation not only accounts for much of the potential but also clarifies some fairly familiar examples of misinterpretations. Introduction The extraordinary value of electrical well logging as a tool for petroleum engineers and geologists is now so uni- versally recognized that it is not necessary to point out the ways in which it can be useful. It is sufficient to mention only the saving that has resulted from the elimination of much coring that would have been necessary under former practices and the considerable additions to reserves resulting from the discovery of sands missed in coring. Paradoxically, the very remarkable success that has resulted from the application of electrical logging to correlation and completion problems has cost some of its most consistent users dearly.&apos; The fact that some operators have placed unwarranted faith in erroneous interpretations of electrical logs does not reduce the value of the logs. It should, however, make one pause long enough to ask why experienced users should be misled. The answer to this question is not hard to find. In nearly every case, the fault has been oversimplification. This is illustrated very aptly by the familiar interpretation and theory of the natural potential log. Recording and Interpreting Logs The natural potential log is extremely simple to record precisely enough for all present-day uses. One needs only an electrode, a cable to lower the electrode through the drilling mud, a recording meter and a surface ground connection. The electrode can be elaborate but need not be. A simple brass rod 2 in, in diameter and 2 or 3 in. long is quite satisfactory. The cable need not be particularly well insulated, nor need it have a very low resistance. The recorder can be a vacuum-tube 1 References are at the end of the paper.

Jan 1, 1944

By R. D. Daniels, T. G. Oakwood

A study was made of the effects of small quantities of hydrogen on the mechanical properties of colum-bium. Tensile specimens, hydrogenated to concentrations of 20 to 200 ppm, were tested at temperatures of 300°, 191°, and 77°K. Although hydrogen was found to have little effect on the strength of columbium, the ductility of Cb-H alloys was found to be quite sensitive to both hydrogen concentration and temperature. At 300°K, an abrupt loss in ductility occurred at a critical hydrogen concentration, although some ductility was observed beyond the tolerance limit. A similar result was found at a lower hydrogen concentration at 191°K. At 77°K, however, a more gradual loss in ductility with increasing hydrogen concentration was observed. Hydrogenated columbium was thus observed to undergo a ductile-brittle-ductile transition. Metallographic examination of fractured specimens revealed extensive porosity at both 77° and300°K which was a distinct function of hydrogen content. At 191°K, although some secondary cracking was noted, the amount of observed porosity was minimal. These observations are interpreted in terms of hydrogen solubility and mobility as a function of temperature and in the role of hydrogen in promoting growth of microcracks. lHE effect of hydrogen on the mechanical properties of the refractory metals is not, at present, completely understood. A number of studies have shown these materials to be susceptible to hydrogen embrittlement. Roberts and Rogers1 have found that vanadium can be embrittled by hydrogen. It was further demonstrated that fracture undergoes a ductile-brittle-ductile transition as the temperature is lowered from 150° to -196°C; i.e., there is a ductility minimum observed at a certain temperature. The ductility is increased by either raising or lowering the temperature from this point. A more complete study by Eustice and Carlson2 on vanadium containing 10 to 800 ppm placed the ductility minimum at about -100°C with variations reportedly due to hydrogen content and strain rate. Ductility minima have also been found at certain temperatures for tantalum containing 7 ppm H3 and 140 ppm H.4 At hydrogen concentrations above 270 ppm, however, the ductility return at low temperatures was considerably reduced.4 In the case of columbium, some disagreement exists in the literature. Eustice and Carlson,5 Wilcox et al.,6 and Imgram et al.4 failed to find a ductility minimum although a composition-dependent ductile-brittle transition was observed. Hydrogen concentrations in these investigations were 20 ppm,5 1 to 30 ppm,6 and 200 to 390 ppm.4 However, Wood and Daniels7 observed a rather pronounced ductility minimum at hydrogen contents ranging from 19 to 252 ppm. Those theories of hydrogen embrittlement involving the precipitation of diatomic hydrogen which have been applies to ferrous metals8-12 do not seem to be applicable to the case of columbium and other exothermic occluders. Such theories propose that extensive crack formation and propagation occurs by the precipitation and expansion of diatomic hydrogen at internal voids and microcracks. However, photomicrographs of hydrogenated columbium do not show any evidence of damage introduced by the sorption and precipitation of diatomic hydrogen; rather, at high hydrogen concentrations, a hydrogen-rich second phase is precipitated.13&apos;14 In addition, a number of these theories require the development of high hydrogen pressures at voids in the structure.8&apos;10&apos;12 This does not appear to be feasible in the concentration ranges discussed in the aforementioned paragraphs. The possible interaction of atomic hydrogen with microcracks resulting from dislocation pile-ups15,16 remains in doubt since pile-ups have not been observed in bcc metals17 including columbium.18 Wood and Daniels7 have put forth the possibility that a hydride precipitation could be responsible for crack nucleation in columbium. Work by Longson19 has shown that hydrogen embrittlement of columbium parallels the bulk solubility limit; i.e., as the solubility increases, for instance with temperature, the amount of hydrogen necessary to cause embrittlement also increases. Although a hydride precipitation appears attractive as a means of nucleating microcracks in columbium, what require more intensive study are the low-temperature anomalies which have been observed, i.e., the ductile-brittle-d&apos;ictile transition characteristics. Also, the hydrogen concentrations where embrittlement occurs are often below the bulk solubility limits determined by Albrecht et al.13,14 and Walter and Chandler.20 This work is an attempt to determine more definitively the effects of concentration and temperature on the mechanical properties of dilute Cb-H alloys. EXPERIMENTAL PROCEDURE Ultrahigh-purity columbium rods, obtained from the Wah Chang Corp., were cold-reduced by rotary swaging. A chemical analysis is given in Table I. The material was cut into cylindrical blanks 1.50 ±0.005 in. long. Individual specimens were either given a stress relief anneal at 750°C or recrystal-lized at 1200°C. Resulting microstructures were either a "bamboo" structure characteristic of a wrought material or a recrystallized structure with a grain diameter of approximately 100 n. All heat treatments were carried out in a vacuum of 10-5 Torr or less.

Jan 1, 1969

By E. T. Stephenson

Wert and Marx1 pointed out that a straight-line relationship exists between the activation energy of a relaxation process and the temperature at which the maximum relaxation occurs. The data available at the time indicated that this relationship held for a number of Snoek peaks, several grain boundary peaks, and pair relaxation in a brass. Theoretical justification for the observed relationship was found in the following equation, which Wert and Marx derived from the theory of interstitial atomic diffusion coefficients:&apos; where AH is activation energy, R is the gas constant, T is the internal friction peak temperature, v is the interstitial atomic frequency, f is the frequency of the applied stress, S is entropy of activation. More accurate internal-friction data on interstitial diffusion in bcc metals have become available since Wert and Marx&apos;s paper. Table I gives activation energies calculated by several authors from a combination of elastic aftereffect data and the peak temperatures at several frequencies of measurement. (In the case of Fe-C and Fe-N, the referenced authors5&apos;7&apos;8&apos;10 also used high-temperature diffusion data.) However, diffusion experiments at 150°C and above1&apos;-13—rather than anelastic techniques—were used to determine the activation energy of hydrogen diffusion in Fe-H. In order to plot this recent data as a AH vs T graph we calculated the peak temperatures of the systems listed in Table I (with the exception of Fe-C, Fe-N, and Fe-H) by using published values3&apos;&apos; of AH and Do. These calculated peak temperatures varied by only a few degrees from experimentally determined peak temperatures. The calculated values were felt to represent the better average. A number of investigators have found the peak temperatures in Fe-C and Fe-N to be 38 to 40°C and 20° to 24°C, respectively. The values of 39" and 22°C (312° and 295°K in Table I) were determined by carefully executed experiments.6&apos;8 The hydrogen peak temperature has been measured at 1 cps,12 20 cps,14 and 35,000 cps.15 All hydrogen peak temperatures were adjusted to 1 cps for Table I using AH = 3000 cal per mole. As Fig. 1 shows, the data of Table I fit a straight line at least as well as the earlier data used by Wert and Marx. Linear-regression analysis was applied to the data in Table I. The Fe-H data was omitted because the activation energy has not been experimentally determined in the temperature range of the peak. The analysis yields the equation: with a standard error of 860 cal per mole. The agreement of the data in Table I with the Wert-Marx equation is excellent. Strict application of Eq. [I] forces the linear regression analysis through the origin. In this case, the analysis gives a slope of 62.1 cal per mole per deg, and a standard error of *890 cal per mole. With this value, it follows from internal-friction theory that Hence, Do varies by only 30 pct among these bcc-interstitial systems. Thus, a concept suggested originally by Wert and Marx1 is confirmed by recently published data. The

Jan 1, 1965

By D. B. Jugle, J. B. Darby, O. J. Kleppa

A systematic study has been made of the kinetics of solution under steady state, dynamic conditions of titanium, vanadium, chromium, iron, cobalt, and nickel in liquid aluminum. It was found that the temperature dependence of the solution rate obeyed an Arrhenius-type rate equation, and that at a given temperature the rate of solution of the various solutes correlates quantitatively with the equilibrium solubility of the solute in liquid aluminum. These results are consistent with a mechanism where the rate-controlling step is the diffusion of solute atoms through a liquid boundary layer. THE present study was initially started in order to explore the feasibility of liquid-metal solution calorimetry for transition metals and alloys. Previous work1 in this field employing liquid tin as a solvent at temperatures in the 500&apos; to 600&apos; range had indicated that the rates of solution of most transition metals in tin are very low. Under such conditions effective solution calorimetry is difficult. The objective of the present investigation was two-fold: a) To obtain, as far as possible, quantitative data on the rates of solution of a series of transition elements in liquid aluminum. b) To explore whether liquid aluminum might be a suitable solvent for liquid-metal calorimetry. In the course of this work a comprehensive set of data was obtained on the steady state rates of solution of transition metals in a common liquid-metal solvent. The results are consistent with the boundary layer model, which assumes that the rate-controlling step consists of diffusion of solute atoms through a viscous liquid layer. EXPERIMENTAL PROCEDURE A vacuum-tight stainless steel vessel was surrounded by a resistance furnace, as shown in Fig. 1. In all experiments the temperature of the liquid solvent was controlled to 2.5&apos; by means of a Micromax controller. A high-vacuum manifold connected to the vessel maintained a vacuum of 1 x 105 mm of Hg or better. The vacuum vessel was equipped with a charging section isolated from the working chamber by a vacuum-tight gate valve. This arrangement allowed the specimen holder to be removed or inserted into the apparatus without removal of the liquid metal bath. The specimen holder was suspended from a closed end stainless steel tube, which also served as the thermocouple protection tube. The portion of the tube that was below the solvent level was surrounded by an alumina protection tube to isolate it from the liquid metal bath. The stainless steel tube was connected through a rotary vacuum seal and a gear train to a fractional horsepower motor. For most experiments the tube was rotated at a constant

Jan 1, 1963

By D. H. Shaffer, W. F. Harris, W. M. Hickam, M. H. Loeffler

Experiments have been performed on the quantitative addition to niobium of enriched isotopes 018 and 017 at the 0.1 - 40 micro-gram level and their subsequent recovery. A measured quantity of molecular oxygen of known isotopic concentration is added to niobium metal by oxidation. Recovery of the enriched isotopes as carbon monoxide is by the vacuum fusion technique. Quantitative determinations of the enriched isotopes are made in standard volumes at constant temperature using accurately calibrated micromanometers and the mass spectrometer as pressure measuring instruments. THE presence of low concentrations of nonmetallic impurities in metals can often adversely affect the physical properties of the metal. The increase in hardness and the embrittlement of refractory metals due to oxygen is well known. In metallurgical studies dealing with the diffusion rates or the effect of oxygen on the physical properties of refractory metals, it is often necessary to add small quantities of oxygen to the metal and later recover the total quantity present. It is desirable, therefore, to establish the accuracy with which microgram quantities of oxygen can be added to niobium and recovered by vacuum fusion. The successful addition of microgram quantities of oxygen to metals by the usual manometric techniques and the subsequent recovery by vacuum fusion is difficult because of the uncertainty in the accurate determination of the quantity of oxygen originally present in the metal and because of the chance of contamination by atmospheric oxygen. In order to minimize these uncertainties earlier workers have added quantities of O16 at levels much higher than the oxygen concentrations that are of interest.&apos;-3 In order to eliminate the uncertainty associated with the O16 additions to metals at low microgram levels, experiments have been performed on the quantitative addition of oxygen highly enriched in O17 and O18 at the 0.1 to 40 pg level to niobium and the subsequent quantitative recovery of the isotopes by vacuum fusion. Since the natural abundance of O17 is 0.04 pct and of 0" is 0.2 pct this enriched oxygen provides a uniqueness from interference not achieved in earlier work.&apos;-= A measured quantity of molecular oxygen of known isotopic concentration is diffused into the metal. Recovery of the isotopes in the form of carbon monoxide is by vacuum fusion. The total quantity of gas is determined in standard volumes at constant tempera- ture using accurately calibrated Consolidated Electrodynamics micromanometers and the mass spectrometer for pressure measurements. The molecular and isotopic composition is determined mass spectrometrically. APPARATUS A schematic of the oxygen addition apparatus is shown in Fig. 1. Take-offs are provided for the attachment of the isotope container and for sample bulbs which are used to transfer samples to the mass spectrometer. Metal valves are used throughout the system including the sample bulbs in order to achieve a vacuum of 10"6 mm Hg. Evacuation is accomplished with a 3-stage oil-diffusion pump backed by a mechanical pump. A liquid nitrogen trap is used to remove condensables and to prevent oil vapor from entering the system. A micromano-meter is used for pressure measurements. The furnace assembly is shown in Fig. 2. It consists of a quartz tube joined to the apparatus through a 40/W joint with Apiezon W low-pressure wax. The furnace cap, also a 40/W pyrex joint, is provided with a pyrex hook. The sample is suspended from this hook with a platinum wire. The total volume of the furnace section is 435 ml. All volumes were determined by expanding a known volume of gas at a known pressure into the evacuated system and re-measuring the pressure. Both the micromanometer used on the oxygen addition system and the micromanometer used on the mass spectrometer were compared to a precision

Jan 1, 1961