By G. Sachs, G. Espey

SIMPLE methods can be used for the determination of the residual stresses in thin-walled tubing if the stresses consist of high tensile stresses at the one surface and high compressive stresses at the other surface Such a stress distribution is approximated in sunk tubing and in deep-drawn shells It is possible to cut sections from such articles in such a manner that a major part of the residual stress is relieved by a bending of the part that is separated from the adjacent metal The circumferential stress is evaluated from the change in diameter D, occurring on splitting a length of tubing (Fig Ib),1-5 or from deflection resulting from the cutting out of a circumferential tongue (Fig Ia) G The bending moment M released by such a flexure is [ ] The release of this bending moment corresponds to the release of stresses, which, in a thin section, vary linearly from one surface to the other, and have the following value in a particular fiber a certain distance (zx from the surface [ ] where C is the section modulus and d is the thickness of the section, the ratio AI C being d 2 for a rectangular section* The maximum stress values at the surfaces are [ ] For most purposes the simpler equations [ ] will be satisfactory, where Dm is the average of the mean diameters of the tubing

Jan 1, 1941

By R. J. Sherman, M. R. Achter

Creep rates have been measured for nickel at 1200°F in air and in vacuum, and related to the depth of surface cracks in the specimens tested in the two environments. The surface cracks were observed to grow faster in air than in vacuum in both short-time and long-time tests. Crack depths, however, could be correlated with creep rates only in the short-time tests. Although no cracks were observed in a relatively brittle Ni-Cr-A1 alloy creep tested at 1300°F, the appearance of alloy specimens fractured after interruption in creep indicated that there was a decrease of intergranular cohesion resulting from the diffusion of atmospheric gases into grain boundaries. PREVIOUS investigations1-3 have demonstrated that the effect of atmosphere on the high-temperature strength of nickel and nickel-base alloys may be reversed by changes in the stress or temperature of the test. At high stress and low temperature the creep-rupture life is longer in vacuum than in air, while at high temperature and low stress the relative strengths are reversed. A mechanism to explain this behavior was proposed based on two competing processes. Oxidation hardens and strengthens a metal, but adsorption of gas, by lowering surface energy, reduces the work required to propagate an intergranular crack. The controlling process is determined by temperature and stress. Basic to this mechanism is the concept that environment determines the ease of propagation of intergranular cracks and thus affects creep rate and rupture life. To explore the mechanism in greater detail, this investigation was undertaken to determine the effect of atmosphere on crack initiation and propagation rates in nickel1 and a relatively brittle Ni-Cr-A1 alloy.3 EXPERIMENTAL PROCEDURE The materials were the same as used previously. Nickel of 99.8 pct purity had the following impurity content: 0.02 pct Co, 0.03 pct Fe, 0.02 pct Mg, 0.03 pct Si, and 0.008 pct C. Rods were cold swaged from 1/2 in. to 3/8 in. in diam and machined into speci- mens with gage sections 1/4 in. in diam by 1-1/4 in. long. They were annealed in vacuum at 1600" F for 1 hr to achieve a grain size of 0.07 mm. The alloy was composed of 19.1 pct Cr, 3.6 pct Al, 1.7 pct Si, 0.57 pct Fe, 0.10 pct Mg, 0.027 pct C, 0.004 pct S, and the balance Ni. Sheet specimens of 0.500-in. width and 1.25-in. gage length were machined from 0.033-in.-thick strip and annealed in vacuum at 2000° F for 2 hr, resulting in a grain size of 0.036 mm. Large amounts of an intergranular phase were introduced as a result of the anneal. Creep tests on both materials, using equipment previously described by Shahinian; were conducted in air and in a vacuum of 1 x 10-5 mm Hg. They were continued to rupture and interrupted at various stages of the test. Although extensions were measured from dial gage readings of movement of the lever arm, it is considered that valid comparisons of creep rate may be made in this manner.l Two parameters were measured metallograph-ically* on longitudinal sections of nickel specimens interrupted during creep—the mean depth of surface cracks 2, and the density n as the number of cracks per unit length of surface. They were combined into one parameter by the relation p = n-d [1] As used here, p is equal to the total of crack depths per unit length of surface. RESULTS Nickel. It is well known that the incidence of intergranular cracking is increased with increasing rupture life. Indeed, it is evident in Tables I and I1

Jan 1, 1962

By R. W. Gurry

THERMODYNAMIC calculations indicate that boron is a better deoxidizer than silicon but probably is not quite as effective as aluminum. Boron should, therefore, be readily oxidized out of the open-hearth bath, which implies that it is not recovered in significant concentration from any scrap charged; also that, if added in the ladle, it tends to oxidize out during teeming unless protected by the presence of a. better deoxidizing agent. These conclusions do not apply to liquid cast iron, in which the oxygen content is much lower than in liquid steel. The possibility of conserving certain strategic alloying elements widely used in steelmaking, notably manganeie, chromium and molybdenum, by the use of boron, which in small concentration appears to be extraordinarily effective in promoting hardenability, raises a question as to what extent any boron present in the scrap charged into the open hearth is oxidized out during melting and subsequent refining. This question is significant because the optimum concentration of boron in the finished steel, which is fairly critical, would be very difficult to attain if the boron in the charge were largely retained in the metal. Moreover, unless boron is substantially eliminated in the open-hearth process its use on a large scale would eventually make it impossible to produce boron-free steel except by restricting the charge to virgin material. There is at present, unfortunately, virtually no satisfactory direct evidence to provide an answer to this question; but there are indications from practice that boron is oxidized out in the open hearth in the production of medium or low-carbon steel, although it may be retained if the carbon content remains fairly high; that is, if the oxygen is kept fairly low. In the absence of direct data, it is necessary to rely upon the indications of indirect evidence, the best approach now available being a thermodynamic calculation of the deoxidizing power of boron in liquid steel by the general method used so successfully by Chipman1 in his study of the reactions in the open-hearth process. The thermal data for boron, upon which such a calculation must be based, are reasonably satisfactory; the only quantities not directly determined are the entropy of melting of boron, the activity coefficient of boron in liquid steel, and the activity coefficient of B203 in an open-hearth slag; but these values may be estimated with ample accuracy. The results of this calculation, which is presented later, are given in Table I, together with corresponding data for other deoxidizing elements. This table shows the calculated residual content of oxygen in equilibrium with different residual concentrations of the deoxidizer in the metal;

Jan 1, 1943

By R. M. Fowler, H. L. Hamner

DURING the last 25 years, there appeared in the literature a number of papers describing equipment and operating techniques for the determination of total oxygen in iron and steel. In the early papers, comparatively little attention was paid to side reactions that occur when iron is saturated with carbon at a high temperature in a high vacuum. As more experience was gained with the new method, the limitations appeared. Metals, with a boiling point lower than iron, distilled out of the crucible, condensed in the cooler part of the furnace, and subsequently reacted with carbon monoxide to form oxides and carbon. Aluminum, manganese, and the alkaline earth metals proved troublesome in this respect. Modifications have been devised to overcome the difficulties due to aluminum and manganese, while the alkaline earth metals are not of too much concern as yet to the steel chemist. The reactions of sulphur have received less attention, although it is generally recognized that some carbon disulphide is probably formed. Liquid air traps have been used in some cases to prevent any carbon disulphide from entering the analytical train. Sulphur was not a particular problem at the Union Carbide and Carbon Research Laboratories until the analysis of the irons of higher than usual sulphur contents became necessary. In order to describe the procedure developed for such irons, it will be necessary to first describe the type of vacuum-fusion equipment employed because the operation of vacuum-fusion equipment is an art to a considerable extent. At the Laboratories, vacuum-fusion equipment has been in daily operation since about 1930. Over the years, the evolution of this apparatus has been governed by the versatility required to analyze a wide variety of materials. Since all types of materials from high purity metals to slags are analyzed and, since seldom more than a few samples of one type are analyzed in succession, the apparatus was designed for accuracy and flexibility rather than for speed. A general view of the equipment is shown in Fig. 1, while Fig. 2 shows the relationship of the various parts. In Fig. 2, A is a vertical double-glazed 24X27/8 in. OD silica tube heated with a 20 kva mercury-arc high frequency generator. The tube is closed with a water-cooled brass head attached with de Khotinsky cement. A turret cap fits on this head and is sealed with a 1/8x3 in. "0" ring. The head contains a sight glass and two 8 in. horizontal glass tubes, for sample storage, cemented in with de Khotinsky cement. B is a four-stage Gaede mercury diffusion pump connected to the water-cooled head with a 11/2 in. copper tube through a flange with an "0" ring. The output of the vacuum pump feeds into an automatic Toepler F pump which compresses the gas sample over mercury in the measuring burettes, G and H. There are bypasses in this line for a McLeod gage C and a Piranni gage D, a manometer E, and for initial pumping out of the system with a Cenco Megavac backing-up pump. The reduction crucible shown in Fig. 3 is machined of Tungar Bulb quality (A.G.K.T.E.-2) graphite. The sample is guided into the crucible with the graphite funnel depicted on this figure. The arrangement of the crucible, radiation screens, etc. in the furnace is as follows: A 1 15/16x61/2 in. Alundum thimble, porosity RA-84, with two 1/8 in. holes near the top and opposite each other which take a pair of special tongs used for lowering it in place, is prepared. A 3/4 in. layer of powdered graphite is placed in this Alundum thimble, and the graphite crucible containing 20 g of ingot iron and 0.5 g of carbon is carefully centered on this bed of graphite powder and graphite powder is packed around it to the top of the graphite cru-

Jan 1, 1953

By Ö. Valla, A. Muan, K. Grjotheim

The solid miscibility gap between CaO and "FeO" in the system CaO-"FeO" in contact with metallic iron gradually closes as MnO is added as a third component. On the liquidus surface of the system CaO-"FeO"-MnO, this situation gives rise to a boundary curve which originates in the bounding system CaO-''FeO", proceeds a short distance into the composition triangle of the ternary system, and then vanishes. A new approach has been used to follow the course of this boundary curve. It is shown that the curve vanishes at a much lower temperature and at much lower MnO contents than has been inferred previously. The oxides CaO, "FeO", and MnO together with SiO2 are the major components of the slag phase formed in the basic oxygen process. Hence, the system CaO-"Fe0"-MnO is of considerable technological interest. In addition, the system is theoretically interesting. The three oxides above all have sodium chloride structure. The size differences among the cations are such that in the bounding "binary"* systems CaO-MnO and "FeO"-MnO complete solid-solution series are formed,1,2 whereas in the system CaO-"FeO" there is only limited mutual solubility in the solid state,3 see Fig. 1. Hence, a solid miscibility gap exists in a part of the "ternary"* system Ca0-"Fe0"-Mn0, and a liquidus boundary curve originates at the peritectic point, point a in the insert in Fig. 1, in the system CaO-"FeO", extends a certain distance into the ternary system, and then vanishes. Very little quantitative information on the system Ca0-"Fe0"-Mn0 is available in previous literature. Fischer and Feischer4 sketched isothermal sections at 1600° and 1700°C, and estimated that the vanishing boundary curve extends to approximately 1650°C and a composition of 42 wt pct MnO. The work to be described in the following was aimed at locating experimentally the "vanishing" liquidus boundary curve, determining its end point, and deriving representative isothermal sections below and above the temperature of the end point of this curve. EXPERIMENTAL METHODS The phase relations were determined by the well-known quenching method. (For a description of this method as applied to oxide systems, see the original paper of Shepherd, Rankin, and wright.5) Prereacted oxide mixtures of desired compositions were contained in iron crucibles and heated in a vertical tube furnace in an atmosphere of purified nitrogen. After equilibrium was judged to have been attained, the samples were quenched to room temperature, the phases present were identified by microscopic and X-ray examination, and total iron oxide contents were determined by chemical analysis. "Fisher Certified" reagents (MnCO3, CaCO3, Fe2O3, and Fe) served as starting materials. The calcium carbonate and ferric oxide were heated in air at 400° and 800°C, respectively, for 24 hr prior to use. Manganese oxide was prepared by decomposing the carbonate in a graphite crucible in hydrogen atmosphere at 1000°C. The product was ground under acetone to -100 mesh. The iron powder was used directly without any preparation. Dicalcium ferrite was used as a starting material for some mixtures. It was made by mixing some of the above prepared CaCO3 and Fe2O3 in proportions corresponding to the formula 2CaO. Fe2O3. This mixture was then fired in air for

Jan 1, 1969

By Clarence P. Linville

In an article published in the Iron Trade Review,' I gave a convenient arrangement for the installation of wet and dry bulb thermometers for use in making moisture determinations in the air being blown into a blast furnace, and also gave a chart for use in obtaining moisture values from the thermometer readings. The data from which this chart was prepared were obtained from the tables in use by the U. S. Weather Bureau.2 The work of Carrier3 has shown that these tables are somewhat in error. He has recalculated the values for moisture as referred to wet and dry bulb thermometer readings, and he has prepared a psychrometric chart from the values thus obtained. This work has placed the subject of psychrometry upon a correct scientific basis. I think it is proper that we should recognize the importance of his work and give him credit for one of the most interesting and valuable researches that have been published in recent years. Blast-furnace men are not ready to use, as he suggests14 a value expressed in grains of water accompanying a pound of dry air. However convenient this may be for heating and ventilating work and other engineering problems, there are several reasons for preferring the use of a value expressed in grains of water in a cubic foot of mixed air and water vapor, in connection with combustion phenomena and the effects of moisture on blast-furnace operation. Previous papers presented to the Institute have used such values and we have

Jan 1, 1914

By L. S. Darken

It has long been recognized that the driving force in an isothermal diffusion process may be regarded as the negative gradient of the chemical potential (partial molal free energy) of the diffusing substance. This equivalence is exactly analogous to the fact that a mechanical force is the negative gradient of the potential energy. Nernstl in 1888 expressed these driving forces in terms of osmotic pressure, which is directly related to the chemical potential and free energy. The relationship between the diffusivity, mobility and activity coefficient of electrolytes in aqueous solution has been developed in great detail by Onsager and FuossZ with results which have recently been confirmed experimentally by Harned and Nuttall. This interpretation of the driving force in isothermal diffusion has been discussed earlier by the author,4,5 who pointed out4 that "for a system of more than two components it.is no longer necessarily true that a given element tends to diffuse toward a region of lower concentration even within a single phase region"; departure from the behavior of an ideal solution may be so great that the concentration gradient and the chemical potential gradient, or activity gradient, may be of different sign, thus giving rise to "up hill" diffusion. Since, in the discussion of that paper,4 some skepti- cism as to the validity of this conclusion was expressed, it seemed desirable to adduce experimental evidence to support it. Evidence of such diffusion in nonmetallic systems has already been reported. For example, it was observed by Hartley" in a series of experiments in which sodium chloride diffused from a saturated solution in about 5 pct acetone in water into a solution virtually free of salt but with essentially the same acetone concentration. Specifically, a wine glass containing crystalline salt and saturated solution was totally immersed in a large glass cylinder containing the acetone-water solution without salt; the difference in specific gravity was such as to prevent convection. Diffusion of salt was accompanied by a marked depletion of acetone in the wine glass; after 3 days the acetone concentration decreased from 5.37 pct at the top of the glass, where the salt concentration was low (0.93 pct), to 1.84 pct at the bottom where the salt concentration was high (21.64 pct). This "uphill" diffusion was found to be such that the partial pressure (activity) of acetone was essentially equalized throughout the system when a steady state gradient of sodium chloride was maintained. In order to demonstrate the existence of such diffusion in metals, a series of four weld-diffusion experiments was made. In these measurements pairs of steel of virtually the same carbon content, but differing markedly in alloy content, were welded at the end and held at 10500 C for about two weeks. Subsequent analysis showed that carbon had diffused so as to produce an inequality

Jan 1, 1949

By A. S. Michaels, M. C. Porter, A. Stancell

Previous laboratory studies have demonstrated that the injection of small quantities of reverse wetting agents during water displacement can increase oil recovery from unconsolidated porous media.9 In the present investigation, an attempt has been made to determine more fully the effects of reverse wetting treatments and to clarify the mechanism by which increased oil recovery is effected. Water-oil displacements were performed in beds of 140-200 mesh silica sand. Hexylamine slugs (injected after 0.25 pore volume of water throughput), when adequate in size and concentration, were effective in promoting additional oil recovery. Their effectiveness increased with the quantity of amine injected. However, slugs of sufficient size and concentration to stimulate oil production at water flow rates of 34 ft/day did not do so at 4 ft/day. Visual studies in a glass grid micromodel have shown that the stimulation of oil production, via ayueous hexylamine, is a result of transient changes in the oil wettability of the pore walls. if the amine slug is of sufficient size and concentration to induce significant changes in the adhesion-tension, large continuous oil masses will be formed. if the superficial water velocity is high enough to result in rapid desorption of the amine, a favorable "wettobility gradient" may be established across the masses; under such conditions, high oil mobility is observed, and increased oil recovery results. INTRODUCTION It is generally agreed that the efficiency of oil displacement by water in porous media is limited in part by capillary forces which cause the retention of isolated masses of oil — resulting in the so-called "irreducible minimum oil saturation". Recent estimates10 indicate that there are about 220 billion bbl of petroleum in United States reservoirs which are not economically recoverable with present techniques (such as water flooding). This amounts to almost five times the known recoverable reserves. It has been recognized for some time that a suitable alteration in the water-oil interfacial tension and/or the contact angle, as measured between the water-oil interface and the solid surface, should result in better displacement efficiency. Surface active agents can be used as interfacial tension depressants to accomplish this objective,1,2,7 but unfortunately, the additional oil recovery is seldom commensurate with the treatment cost. In contrast to interfacial tension depressants, the effect of contact angle alterations on water-oil displacements has received relatively little attention in the literature. It is known that the wettability affects the displacement process.3,4,11 Displacements in water-wet systems generally result in lower residual oil saturations than those in oil-wet systems. The effect of "'transient" wettability alterations concurrent with the displacement process have been investigated by Wagner, Leach and coworkers,4,11 wherein it has been demonstrated that the establishment of water-wet conditions during water flooding of oil-wet, oil-saturated porous media is accompanied by significant increase in oil displacement efficiency. Michaels and Timminss studied the effects of transient contact angle alterations resulting from chromatographic transport of reverse wetting agents through unconsolidated sand. It was demonstrated that chromatographic transport of short-chain (C4 through C8) primary aliphatic amines can improve oil recovery and that the recovery increases with the quantity of amine injected (i.e., with either the amine concentration or the volume of the slug injected). Circumstantial evidence indicated that the increased displacement efficiency resulted primarily from transient changes in wettability of the porous medium. In the Present investigation. additional information has been obtained on the effects of reverse wetting treatments and the mechanism by which increased oil recovery is accomplished. Hexylamine slugs of varying size and concentration were chromato-

Jan 1, 1965

By H. L. Sheakley, D. J. Coolidge

This paper does not deal with all sands used in the glass industry in Missouri; it covers only that used in the plate-glass factory at Crystal City. However, it is probably safe to say that other sands, pro- duced throughout the state for this purpose, are of identical nature. The glass sand used in Missouri is cornrnonly called the St. Peter deposit, which is ascribed to the Ordovician Rock series in the form of sandstone. This St. Peter deposit, aside from a few small outliers, covers a large area of eastern Missouri. It forms, through a broad curve, the northeast margin of the typical Ozark region between Cape Girardeau on the southeast and Mineola, Montgomery County, on the northwest. The belt is extremely irregular, varying from one to ten miles in width; its length is 150 miles in a straight line. The outcrop near the entrance to the Crystal City mine appears in the form of a sandstone bluff approximately 30 ft. high, running along Plattin Creek (Fig. I). Above the sand rock an overburden of Joachim limestone appears, which thickens to nearly 300 ft. and forms the hill commonly called Buck Knob. Test holes where drilled at various points and the drillers' log indicate that the St. Peter deposit ranges in thickness from 63 to 71 feet. Properties of the St. Peter Sand From an analysis of the glass sands of the St. Peter formation in Missouri, the follow-

Jan 1, 1948

By D. J. Coolidge, H. L. Sheakley

This paper does not deal with all sands used in the glass industry in Missouri; it covers only that used in the plate-glass factory at Crystal City. However, it is probably safe to say that other sands, pro- duced throughout the state for this purpose, are of identical nature. The glass sand used in Missouri is cornrnonly called the St. Peter deposit, which is ascribed to the Ordovician Rock series in the form of sandstone. This St. Peter deposit, aside from a few small outliers, covers a large area of eastern Missouri. It forms, through a broad curve, the northeast margin of the typical Ozark region between Cape Girardeau on the southeast and Mineola, Montgomery County, on the northwest. The belt is extremely irregular, varying from one to ten miles in width; its length is 150 miles in a straight line. The outcrop near the entrance to the Crystal City mine appears in the form of a sandstone bluff approximately 30 ft. high, running along Plattin Creek (Fig. I). Above the sand rock an overburden of Joachim limestone appears, which thickens to nearly 300 ft. and forms the hill commonly called Buck Knob. Test holes where drilled at various points and the drillers' log indicate that the St. Peter deposit ranges in thickness from 63 to 71 feet. Properties of the St. Peter Sand From an analysis of the glass sands of the St. Peter formation in Missouri, the follow-

Jan 1, 1948

By J. G. Mravec

The SO-called gas-tube method as developed by Hare, Peterson and Soler for determining the type and content of gases in molten steel is particularly adapted for determining the hydrogen content in molten steel. The development of this method has been quite completely discussed in a paper published by these co-workers in 1937.' The purpose of this paper, therefore, is to familiarize with this method those who arc not well acquainted with it. The principle of the gas-tube method is as fol1ows: One end of an evacuated gas tube is sealed with a very thin copper disk. when this end of the tube is immersed in a test spoonful of molten steel, the copper disk melts almost immediately, allowing a portion of the steel to be drawn up into the evacuated space. Any dissolved gases, and those produced by reactions between the components of the steel during freezing, are liberated into the unfilled portion of the sampling tube. A blob of steel that forms on the immersed end of the tube after the sample is drawn up seals up the end, making it airtight again. The evolved gases are subsequently drawn out of the gas tube through a suitable valve and analyzed by means of an Orsat apparatus. The volume of the sampling tube is sufficiently large so that a pressure considerably below atmospheric is produced after the gas evolution. The low pressure is necessary to effect a nearly complete removal of gases from the steel. Construction oF Sampling Tube The sampling gas-tube apparatus is illustrated in Fig. I. Seamless S.A.E. tubing used for section A is first cut into 7-ft. lengths. Through cxperiencc it was found necessary to use two sizes of tubing for this part, "is-in. and 3/4-in., respectively. The smaller tubing is generally used on the hotter or lower carbon steels. If the inside wall of the tube A is coated with grease or oil, it should be burned out before being machined as follows: One end is machined on the inside diameter to a depth of 34 in., so as to form a seat for a 7/8-in copper disk, which is stamped out from 0.005 to 0.007-in. thick copper sheet. The other end is machined on the outside diameter to a diameter of 1 5/16 in., to take a small reservoir or trap member I?. About 4 in. below the same end, a 1/2-in. hole is drilled to receive the 1/2-in. copper tubing leading to the large reservoir C. The inside of tube A is then thoroughly cleaned with a round wire brush, such as is generally used to clean out shotgun barrels. It is very important that the surface be absolutely free of rust or any nonmetallic coating. Next, the thin copper disk is soldered in place with low-melting silver solder.

Jan 1, 1945

By D. R. Packard, J. D. Verhoeven

The resistivity us atom fraction relationships for dilute solutions of cadmium, mercury, and tin in molten sodium have been determined. With these data and the resistivity capillary-reservoir technique, the electro-transport mobilities, effective valences, and the diflusion coefficients of the three solutes have been determined. The mobilities are found to be higher than in other molten alloys by a factor of around 20. The results are compared to the Mmgelsdorf model for electrotrmtsport. The high values found for the mobility to diffusion coefficient ratio indicate that small quantities of the alkali metals should be susceptible to purification from many solutes by means of electrotransport. PASSAGE of a direct electric current through a liquid metal containing a solute will usually cause a relative motion between the solute and solvent atoms of the alloy. This electrotransport phenomenon may be described experimentally in terms of the mobility of the solute atoms, i.e., the drift velocity of the solute relative to the solvent per unit electric field. In dilute solutions of liquid alloys this relative mobility becomes a measure of the velocity of the solute with respect to the observer since the motion of the solvent is negligible. The mobility is a significant parameter in evaluating the potential usefulness of electrotransport for such things as purification or solute control upon solidification. Prior to around 1958, quantitative data for the mobility of solutes in liquid metals were restricted to some solutes in liquid mercury. Since that time ad- ditional data have been reported for the mobility of solutes in liquid mercury, bismuth, tin, and lead, as shown in Table I. In 1963 Drakin et al.11 reported some values of a transport number for mercury and thallium in molten sodium and potassium. When these values were converted to mobilities, it was found that the mobilities were higher than any of the previously reported values by a factor of around 20, as shown in Table I. Drakin's experimental technique did not eliminate the presence of back-diffusion and consequently his data were expected to be lower than the true values. The purpose of the present investigation was to determine the mobility of a number of solutes in molten sodium with an experimental technique which eliminates back-diffusion errors. EXPERIMENTAL The technique used to determine the mobility was a resistivity capillary-reservoir technique which had previously been used with a high degree of precision on Sn-Bi alloys.4 This technique consists of dipping the vertical Pyrex capillary cell shown in Fig. 1 into a molten bath of alloy while the bath and capillary are under vacuum. The capillary is then filled by intro-

Jan 1, 1969

By David H. Browne

One of the most difficult problems in the chemistry of iron-ore, and one, the solution of which, so far as I am aware, has never been attempted, is the distribution, throughout a given vein, of Bessemer ore, and its relation to the formation of the deposit. In those hematite-mines in which both Bessemer and non-Bessemer ore occur, the sorting of the ore as it lies in the deposit becomes a problem of much economic as well as scientific interest. It would seem, from a superficial examination. or, indeed, from any examination not conducted for this especial purpose, as if high- and low-phosphorus ores were mixed in inexplicable confusion ; and a mining-chemist is very apt to fall into a system of adventitious analyses, taking first-class ore wherever he can find it, and overlooking its relation to the formation and position of the vein. I hope that a few notes which I present on this subject may be found worthy of consideration, as throwing a new light upon this obscure topic. During the last three years, while acting as chemist of the Lumberman's Mining Co., I have made some 3000 analyses of iron-ore from the Ludington mine at Iron Mountain, Michigan. These analyses were necessary in order to separate Bessemer and non-Bessemer ore which occurred intermixed in the deposit. During the last year, I attempted in several ways to find some reason or method in the distribution of phosphorus, and have finally become cognizant of the arrangement herein outlined. I have been obliged to confine my attention to our new mine, and, in that, to that portion wherein

Jan 1, 1889

By Marie L. V. Gayler

Without diffusion taking place in liquid metals and alloys, no castings could be made; it is therefore the most important factor affecting the structure of metals. Diffusion involves the interchange of atoms, a process which takes place during the life history of an ingot. In the liquid, atoms are in a state of high thermal agitation, but this thermal vibration is reduced in amplitude with falling temperature. When solidification sets in, the atoms arrange themselves on an ordered space lattice and the changes in structure which take place in the solid are due to the interchange of atoms on this space lattice. The rate of atomic interchange—e.g., of diffusion—is most rapid at temperatures close to the melting point and decelerates as the temperature is lowered. At room temperature, the rate of diffusion is practically negligible in most alloys, and any change in structure can only be brought about by using methods which will accelerate the rate of diffusion. The rate of diffusion depends on three factors (I) temperature; (2) concentration gradient and (3) activation energy. The growth of grains and particles in the solid alloy also depend on these factors and are therefore intimately associated with diffusion. The rate of homogenization in a cast alloy depends on several factors, such as: (I) rate of solidification, which involves grain and particle size which, in their turn, depend on diffusion: (2) the nature of the constituents; (3) the temperature interval between the melting point of the metal or alloy and the temperature at which it is being heat-treated. It is well known that coarse, cast structures are extremely difficult—if possible— to homogenize, and the finer the grain size and particle size, the more readily solid solution will take place. The rate of diffusion depends, also, largely on the nature of the constituents; for instance, copper and magnesium form solid solutions with aluminum quite readily but nickel and iron do not; neither do certain intermetallic compounds, such as alpha and beta FeSi. Furthermore, the actual formation of intermetallic compounds may be a very slow process, particularly when they are formed in the solid state as equilibrium products. For example, BFeSi is formed in the solid as the result of the reaction aFeSi + A1 —+ PFeSi. The particles of aFeSi become surrounded with a reaction ring of PFeSi. This layer is formed as the result of diffusion of atoms taking place between the aluminum matrix and aFeSi. As the amount of aFeSi surrounding the core of aFeSi increases the concentration gradient becomes low and so the rate of diffusion of atoms also decreases until it practically ceases. This occurs after a comparatively thin layer of ßFeSi has been formed. It follows that when intermetallic compounds of this type are formed in the solid, as the result of diffusion, it is generally impossible ever to attain equilibrium, since the forma-

Jan 1, 1944

By Marie L. V. Gayler

Without diffusion taking place in liquid metals and alloys, no castings could be made; it is therefore the most important factor affecting the structure of metals. Diffusion involves the interchange of atoms, a process which takes place during the life history of an ingot. In the liquid, atoms are in a state of high thermal agitation, but this thermal vibration is reduced in amplitude with falling temperature. When solidification sets in, the atoms arrange themselves on an ordered space lattice and the changes in structure which take place in the solid are due to the interchange of atoms on this space lattice. The rate of atomic interchange—e.g., of diffusion—is most rapid at temperatures close to the melting point and decelerates as the temperature is lowered. At room temperature, the rate of diffusion is practically negligible in most alloys, and any change in structure can only be brought about by using methods which will accelerate the rate of diffusion. The rate of diffusion depends on three factors (I) temperature; (2) concentration gradient and (3) activation energy. The growth of grains and particles in the solid alloy also depend on these factors and are therefore intimately associated with diffusion. The rate of homogenization in a cast alloy depends on several factors, such as: (I) rate of solidification, which involves grain and particle size which, in their turn, depend on diffusion: (2) the nature of the constituents; (3) the temperature interval between the melting point of the metal or alloy and the temperature at which it is being heat-treated. It is well known that coarse, cast structures are extremely difficult—if possible— to homogenize, and the finer the grain size and particle size, the more readily solid solution will take place. The rate of diffusion depends, also, largely on the nature of the constituents; for instance, copper and magnesium form solid solutions with aluminum quite readily but nickel and iron do not; neither do certain intermetallic compounds, such as alpha and beta FeSi. Furthermore, the actual formation of intermetallic compounds may be a very slow process, particularly when they are formed in the solid state as equilibrium products. For example, BFeSi is formed in the solid as the result of the reaction aFeSi + A1 —+ PFeSi. The particles of aFeSi become surrounded with a reaction ring of PFeSi. This layer is formed as the result of diffusion of atoms taking place between the aluminum matrix and aFeSi. As the amount of aFeSi surrounding the core of aFeSi increases the concentration gradient becomes low and so the rate of diffusion of atoms also decreases until it practically ceases. This occurs after a comparatively thin layer of ßFeSi has been formed. It follows that when intermetallic compounds of this type are formed in the solid, as the result of diffusion, it is generally impossible ever to attain equilibrium, since the forma-

Jan 1, 1944

By L. H. Ketchum, T. L. Theis, W. H. Engelmann

The use of a suspended growth system of Thiobacillus ferrooxidans attached in a film to individual particles of bentonite and operated as a sequencing batch reactor is shown to be a practical way of oxidizing ferrous iron in acid mine drainage. This component, followed by limestone neutralization, is both a technically and economically feasible approach to treating these waste waters, compared to existing and other proposed methods. The advantages, in addition to less expense, are greater safety, acceptable treatment at a lower pH, lower solids buildup, less danger of overtreatment, and greater flexibility in operational characteristics. In this paper, data on the continuous bench scale operation of the system under a variety of conditions shows sustained levels of oxidation in excess of 98%. Capital and operating costs are projected to be $80/1000 m3 ($80 per 35, 000 cu ft) of waste water.

Jan 1, 1985

By John H. Melvin

THE Omaha District, Corps of Engineers, has been doing subsurface exploration work for a number of years, both by contract and with its own forces. Certain practices and procedures concerning the recovery of large diameter cores have been developed which will be described in this paper. GEOLOGY Most of the drilling to date has been in connection with structures on the main stem of the Missouri River above Sioux City, Iowa. A wide variety of subsurface conditions has been encountered. The bedrock formations appear in regular order from the oldest to the youngest, traveling upstream; or in other words, the general regional dip is to the northwest. The oldest formation is the Carlile shale, a compaction or noncemented waxy shale of Cretaceous age. Because of its uncemented, soft nature this shale has a tendency to grind or wash away when drilled. It also has a tendency to rebound or expand when the overlying pressures are removed. A 25-ft bed of sharp, friable sandstone called the Codell member is present near the top of the Carlile shale. This member is a cemented sediment, but in drilling, many of the sand grains are broken loose and exert extensive abrasive action on the core barrel and bit. Above the Carlile shale is the Niobrara chalk, a soft calcareous deposit with shaly horizons and some thin beds of bentonitic clay. The average thickness of this deposit is about 145 ft. It is soft enough to be sawed or bored with ordinary woodworking tools, yet is compact enough to be used as building block. The Pierre shale, the formation above the Niobrara chalk, is over 800 ft in thickness and is the most widespread material in the area. It is a dark colored, compaction shale containing numerous thin bentonitic clay seams and at certain horizons, hard manganese concretions. The shale has numerous faults and in addition, along the valley walls, has undergone considerable - slumping. Joints, fault planes and slickensided surfaces are common features encountered in drilling and add to the difficulties of high core recovery. East of the Missouri River the bedrock is generally covered with from 100 to 200 ft of glacial till, composed of clays, silts, sands, gravels and boulders. The valley itself is filled with alluvial deposits, mostly of the sand and gravel sizes, and contains a buried preglacial or interglacial channel over 100 ft in depth. The overburden deposits require sampling in connection with engineering studies and must also be cased before the underlying bedrock can be cored. The diameter of the required overburden samples can thus have an indirect effect on the size of core recovered from the bedrock. West of the river, which in most cases is the western boundary of glaciation,

Jan 1, 1947

THE good and lofty men of intelligence are constantly discoverers of many beautiful things, because of their kindness or because they are driven by necessity. Either they shorten the method of making them after they have seen them, or they think how they can be increased in power or how they can be used for various effects in addition to the one intended by the inventor. Certainly all the effects described to you in this Tenth Book derive from gunpowder. When so many proper- ties and so much strength were observed in this, it was thought that by enclosing it in some strong thing that had the power to resist it, gunpowder would produce a marvelous effect. And thus they made a tube of bronze or iron [160v] which they closed with a wooden plug. They applied fire, and when they saw how forcefully this plug issued they thought of making one that would come out and strike in order to destroy things. They made an instrument of bronze or of iron and put some powder and a round stone inside, and called it a spingard. Developing then from this,

Jan 1, 1942

By J. C. Savins, G. C. Wallick, W. R. Foster

The dual differentiation-integration method of rbeological analysis is applied to Couette flow. Using machine processing techniques, a spectrum of characteristic derivative functions for a variety of ideal Generalized Newtonian and viscoplastic models has been developed; As for the case of Poiseuille flow the functions for Generalized Newtonian models as a class are strikingly different from the corresponding functions for the class of viscoplastic models. It is shown that this dual scheme of analysis is a highly sensitive analytic method for dotermining the applicable range if a rbeoloaical model. The unique characteristics of this function in the case of viscoplastics may lead to a more precise detection and evaluation of the yield point or yield stress in these materials. INTRODUCTION It has been shown 1,2 that the dual differentiation-integration method of analysis is a discriminating and flexible method for interpreting flow behavior and determining the applicable range of a particular model from Poiseuille flow experiments. In the preceding paper3 the basic equations governing the Couette flow experiment were reviewed and the significance of changes in boundary conditions on data analysis in the case of the viscoplaaic discussed. In this paper the dual method of analysis is applied to Couette flow using the suites of rheological models considered previously.

Tars Committee is the result of a desire of the authorities in charge of the publications of the four national engineering societies to co-operate in this matter. The members of the Committee are the following: Charles WarreN Hunt, Secretary of the American Society of Civil Engineers. D. S. Jacobus, Vice-President of the American Society of Mechanical Engineers. Joseph Struthers, Assistant Editor of the American Institute of Mining Engineers. CaRy T. Hutchinson, Chairman of The Editing Committee of the American Institute of Electrical Engineers. This Committee has held several meetings; it seemed advisable, at the outset, to limit its discussions closely to the general subject of abbreviations. Further, it seemed best to formulate a few general rules to be followed in making abbreviations, rather than to compile a list of forms to be recommended. The Committee decided to limit the subject more narrowly by considering only abbreviations to be used in the text, or general reading-matter, arid not those to be used in special matter,

Jan 1, 1905