Search Documents

By W. M. McKewan

Magnetite pellets were reduced in flowing hydrogen at pressures up to 40 atm over a temperature range of 350° to 500°C. The rate of weight loss of oxygen per unit area of the reaction surface was found to be constant with time at each temperature and pressure. The reaction rate was found to be directly proportional to hydrogen pressure up to 1 atm and to approach a maximum rate at high pressures. The results can be explained by considering the reaction surface to be sparsely occupied by adsorbed hydrogen at low pressures and saturated at high pressures. PREVIOUS investigation1,2 have shown that the reduction of iron oxides in hydrogen is controlled at the reaction interface. Under fixed conditions of temperature, hydrogen pressure, and gas composition, the reduction rate is constant with time, per unit surface area of residual oxide, and is directly proportional to the hydrogen pressure up to one atmosphere. The reduction rate of a sphere of iron oxide can be described3 by the following equation which takes into account the changing reaction surface area: where ro and do are the initial radius and density of the sphere; t is time; R is the fractional reduction; and R, is the reduction rate constant with units mass per area per time. The quantityis actually the fractional thickness of the reduced layer in terms of fractional reduction R. It was found in a previous investigation2 of the reduction of magnetite pellets in H2-H,O-N, mixtures, that the reaction rate was directly proportional to the hydrogen partial pressure up to 1 atm at a constant ratio of water vapor to hydrogen. Water vapor poisoned the oxide surface by an oxidizing reaction and markedly slowed the reduction. The enthalpy of activation was found to be + 13,600 cal per mole. It was also found that the magnetite reduced to meta-stable wüstite before proceeding to iron metal. The following equation was derived from absolute reaction-rate theory4,8 to expfain the experimental data: where Ro is the reduction rate in mg cm-2 min-'; KO contains the conversion units; Ph2 and PH2O are the hydrogen and water vapor partial pressures in atmospheres; Ke is the equilibrium constant for the Fe,O,/FeO equilibrium; Kp is the equilibrium constant for the poisoning reaction of water vapor; L is the total number of active sites; k and h are Boltzmann's and Planck's constants; and AF is the free energy of activation. Tenenbaum zind Joseph5 studied the reduction of iron ore by hydrogen at pressures over 1 atm. They showed that increasing the hydrogen pressure materially increased the rate of reduction. This is in accordance with the work of Diepschlag,6 who found that the rate of reduction of iron ores by either carbon monoxide or hydrogen was much greater at higher pressures. He used pressures as high as 7 atm. In order to further understand the mechanism of the reduction of iron oxide by hydrogen it was decided to study the effect of increasing the hydrogen pressure on rebduction rates of magnetite pellets. EXPERIMENTAL PROCEDURE The dense magnetite pellets used in these experiments were made in the following manner. Reagent-grade ferric oxide was moistened with water and hand-rolled into spherical pellets. The pellets were heated slowly to 550°C in an atmosphere of 10 pct H2-90 pct CO, and held for 1 hr. They were then heated slowly to 1370°C in an atmosphere of 2 pct H2-98 pct CO, then cooled slowly in the same atmosphere. The sintered pellets were crystalline magnetite with an apparent density of about 4.9 gm per cm3. They were about 0.9 cm in diam. The porosity of the pellets, which was discontinuous in nature, was akrout 6 pct. The pellets were suspended from a quartz spring balance in a vertical tube furnace. The equipment is shown in Fig. 1. Essentially the furnace consists of a 12-in. OD stainless steel outer shell and a 3-in. ID inconel inner shell. The kanthal wound 22 in. long, 1 1/2, in. ID alumina reaction tube is inside the inconel inner shell. Prepurified hydrogen sweeps the reaction tube to remove the water vapor formed during the reaction. The hydrogen is static in the rest of the furnace. The sample is placed at the bottom of the furnace in a nickel wire mesh basket suspended by nickel wire from the quartz spring. The furnace is then sealed, evacuated, and refilled with argon several times to remove all traces of oxygen. It is then evacuated, filled with

Jan 1, 1962

By Donald L. Katz

Charts for predicting the pressure to which natural gases may be expanded without hydrate formation have been prepared for gases of even gravity. Pressure-temperature curves for hydrate formation were established for gases having gravities from 0.6 to 1.0. These curves and the thermal behavior of the gases during free and adiabatic expansion were used to prepare the charts for estimating the permissible expansion of natural gases without hydrate formation. The problem was solved by L. F, Albright, W. T. Boyd, J. J. McKetta, G. Martin, P. Poettman. and A. P. Snyder.-, who are first-year graduate students in the department of Chemical and Metallurgical Engineering at the University of Michigan. This paper is essentially a summary of their results. Prediction of Conditions for Hydrate Formation in Natural Gases Each natural gas under a given pressure will form solid hydrates at a corresponding temperature provided sufficient water is present.1-5 The temperature of natural gases below about 5000 lb. per sq. in. decreases when the gases are expanded freely.6,7 This decrease in temperature may cause the expanding gas to enter the region of temperature and pressure at which hydrates will form' The final pressure to which a natural gas may 'be expanded without hydrate formation depends upon the initial temperature and pressure and the gas composition. This paper presents charts that give the final pressures to which gases of gravity 0.6 to 1.0 at given initial temperatures and pressures may be expanded without formation of hydrate. Hydrate-forming Temperatures and Pressures as a Function OF Gas -Gravity Experimental data of pressure versus temperature at which solid hydrate will form, provided sufficient water is present, are available for a series of gases.2,3 A method of predicting the pressure-temperature curve for a given gas composition has been reported.' The solution to this problem requires that these curves relating pressure to temperature be established for gases of given gravities.

Jan 1, 1945

By C. H. Mathewson, Robert Maddin, W. R. Hibbard

A SATISFACTORY mathematical relationship between shear, elongation and change of orientation in the axial straining of a single crystalline rod or wire may be based on a simple model in which blocks, representing glide lamellae, glide over one another and rotate so as to maintain the original fixed position of the axis as the wire elongates.1 Obviously such a model gives no information concerning strain-hardening or the atomic adjustments at the sliding surfaces and their influence on the internal structure of the blocks. Moreover such an operation could be conducted with rigid blocks only by using self-aligning grips or a flexible attachment which would permit the adjacent blocks to freely assume their changing orientations. There are many unsolved problems (see Andrade2) concerning the manner in which nature departs from the simple model in permitting the essentials of slip, rotation and elongation to occur along with strain-hardening and the appearance of glide lamellae of various dimensions and special characteristics, not fully appreciated at the present time. This paper describes part of an extensive investigation on the development and characteristics of glide ellipses in single crystalline alpha brass rods and is especially concerned with the observation of cross-slip in crystals oriented wholly within the range of slip on a single system according to the generalizations first presented by Taylor and Elam in 1923.3 EXPERIMENTAL PROCEDURE Half inch rods of alpha brass (nominally 70 pct Cu, 30 pct Zn) * were converted into single crystals by melting and gradual solidification in a graphite mold according to the Bridgman method.' In order to remove any coring, the crystals were homogenized at 800°C for 16 hr and tested by etching with a 50 pct nitric acid solution. The back-reflection Laue technique as described by Greninger5 was used for determining the orientations of the crystals. Standard stereographic operations were employed to locate the specimen axis in a triangle of the Taylor and Elam3 projection so that the slip plane and direction could be predicted. The lineage structure reported by Buerger6 was present in the crystals used in this investigation. However, only crystals were used in which the internal differences in orientation did not exceed two degrees. Very little is known concerning the effect of the presence of a lineage structure on the detailed mechanism of plastic deformation.

Jan 1, 1948

By D. E. Wolfson, H. J. Gluskoter, M. R. Geer, John A. Harrison, H. F. Yancey, I. S. Latimer

When this chapter was prepared for the kst edition in 1942, continuous mining machines virtually were unknown, and hand loading in underground mines, which gave an opportunity to discard impurities, accounted for 55 percent of the production of bituminous coal and lignite as compared with the 1965 figure of 11 percent. Only 24 percent of the total production was cleaned mechanically, compared with the present (1965) figure of 65 percent. The amount of refuse discarded during preparation for the same period increased from 13 to 21 percent. Changes in the equipment used in the cleaning process were as follows: [ ] Unclassified nearly 8 percent. Data on the amount cleaned by flotation was not collected until 1960 when 1.8 million net tons was so treated. In 1965 this figure increased to 6.9 million tons. Although the great increase in mechanization and full seam mining has resulted in substantial increases in the impurity content of the raw coal as well as in a finer size consist, some phases of face preparation are still important, particularly the variability of the distribution and thickness of the interbedded impurities and the changes in the character of the roof and floor from place to place in the mine. Knowledge of these factors in relation to all phases of the mining operation, particularly selective mining, are still of importance to the treatment of raw coal in the preparation plant. The major characteristics of coal and impurities from the standpoint of mechanical cleaning are particle size composition, generally called size consist, density differences, the relative friability of the coal and of its associated impurities, hardness, and strength. Some of the other factors related to preparation are petrographic composition and rank. COAL PROPERTIES Rank Perhaps 95 percent or more of the coal cleaned mechanically is of bituminous rank. Only a very small tonnage is subbituminous and prac-

Jan 1, 1968

By William M. Bowron

Thirty years ago, when I stood on the cliff of red fossil iron-ore, on Red mountain, Jefferson county, Ala., I asked what were the geological relations of this remarkable deposit. In reply I was told that it was a limestone, colored and saturated by some unknown but wholly external influences, and that at a reasonable distance from the surface the color would disappear. I could find no satisfactory explanation, either of the nature of this wonderful external permeating influence, or of the cause of such a ferrous impregnation selecting this one particular bed of limestone, to the exclusion of the higher and lower beds of the same material which are not even stained. I. The Present Theory. Referring to this subject, Dana says :' "The clays, clayey sandstones and limestones of the Clinton epoch, through New York and the Appalachians, show that the mud-flats and sand-banks, and hence the shallow seas of the coast region, still continued.... The beds of argillaceous iron-ore, which spread so widely through New York and some of the other States, west and south, could not have been formed in an open sea; for clayey iron-deposits do not accumulate under such circumstances. They are proof of extensive marshes, and, therefore, of land near the sea-level. The fragments of crinoids and shells found in these beds are evidence that they were, in part at least, salt-water marshes, and that the tides sometimes reached them." At first, this explanation seemed satisfactory, but the more I studied the ore the less satisfying the explanation became. 1. In the ore itself, I found associated with the small particles of rounded matter (now consisting of iron oxide in which organic structure, if ever present, has become lost, though the

Jan 1, 1906

By P. G. Shewmon, F. N. Rhines

THE determination of the self-diffusion coefficient of magnesium has been made possible recently by discovery1-1 of a radioactive isotope, Mg28 having a half-life of 21.3 hr,1 and subject to manufacture in useful quantity. In the present research this material was condensed from the vapor phase upon a surface of high purity magnesium. The progress of diffusion of the tracer atoms into polycrystalline magnesium was followed by machining layers and measuring the change in the intensity of radiation as a function of the distance of each layer from the surface. The self-diffusion coefficient was found to be 2.1 X 10-8 sq cm per sec at 627°C, 3.6 X 10-9 sq cm per sec at 551°C, and 4.4 X 10-10sq cm per sec at 468°C; the activation energy is about 32,000 cal per mol. Experimental Procedure Since there was no other published measurement of a diffusion velocity in any magnesium-base material, is was necessary to employ a number of new experimental techniques. The short half-life of Mg28 made it necessary to complete the entire experimental procedure within three or four days. This meant that the work had to be done where a cyclotron was readily accessible and that all operations, prior to the diffusion heat treatment, had to be so designed as to minimize their time requirements. Unusual problems were imposed also by the chemical reactivity of magnesium, its high vapor pressure, and the fact that no satisfactory method for elec-trodepositing magnesium on magnesium is presently available. Finally, the machining and handling of the easily air-borne radioactive-magnesium chips involved certain health hazards, resulting in the need for further experimental restrictions. Preparation of Mg28 The Mg28 was produced in the Carnegie Institute of Technology syncrocyclotron by the neutron spallation of chlorine.5 his involved bombarding a 2 gram crystal of high purity NaCl with a beam of 350 mev protons for a period of 2 hr, after which the crystal was dissolved in warm water and the Mg28 was concentrated and purified by chemical means (see Appendix). About 50 microcuries of Mg28 thus were obtained in the form of magnesium oxinate (8 hydroxyquin-olatc?), which was ignited in air to produce MgO. This in turn was reduced to magnesium metal vapor, by the method of Russell, Taylor, and Cooper," in the vacuum apparatus shown schematically in Fig. 1. Here the essential part is a tantalum ribbon, slightly dished to receive the MgO. The ribbon, pre- viously outgassed at high temperature, is heated to about 1700°C by passing an electric current through it, whereupon tantalum oxide is formed, magnesium vapor is released almost instantaneously, and condensed partly upon the diffusion sample. Diffusion-Sample Preparation: Hot-extruded magnesium rod, 21/32 in. round was used in making the diffusion specimens. The magnesium analyzed as follows: 0.004 pct Al, 0.027 pct Fe, 0.040 pct Mn, 0.0004 pct Cu, 0.0002 pct Ni, and less than 0.01 pct Ca, 0.0004 pct Pb, 0.0011 pct Si, 0.001 pct Sn, and 0.001 pct Zn. A brief study of the crystal texture of this material revealed a sharp fiber texture with the (001) plane roughly parallel to the extrusion axis. Cylindrical samples 1/2 in. long by 5/8 in. were machined from this rod, the end faces dressed on 3/0 emery, and lightly etched with 20 pct HC1 in water. These samples then were annealed for at least twice the intended time of diffusion, at the intended diffusion temperature, in order to stabilize the grain structure at about 1 mm average diameter. The annealing treatments were conducted in argon in the same apparatus and in the same manner as the subsequent diffusion treatments, which will be described presently. Thus, a strain-free plane surface was produced, but there remained a layer of MgO which had largely to be removed before the layer of Mg28 was deposited. Most of this layer was taken off by two light passes over 3/0 emery paper. The balance of the oxide and a thin layer of metal were then removed by etching 5 to 10 min in 4 pct nital (4 pct HNO3 and 96 pct ethyl alcohol) made with absolute alcohol. There followed immediately three quick rinses in: 1-49 1/2 pct methanol, 49 1/2 pct acetone, and 1 pct formic acid, 2-50 pct methanol and 50 pct acetone, and 3-pure benzene. This procedure is essentially that of Sturkey.7 The resulting surface, which was of almost elec-tropolished brightness, remained plane and was free of cold work. It could be kept clean by storing under benzene, or in a desiccator; short exposure

Jan 1, 1955

By M. A. Orehoski, J. M. Hodge

It is now generally conceded that if a steel is to develop optimum physical properties in the conventionally quenched and tempered condition, the microstruc- ture after quenching should consist wholly of martensite; and that transformation of austenite to intermediate-temperature products during quenching will have a deleterious effect upon the physical properties, particularly the toughness, of the tempered material. This implies that, in order to obtain the optimum physical properties from a given steel, its "harden-ability " should be high enough to suppress all transformation except that to martensite under the heating and quenching conditions to which it will be subjected, and this premise is probably the most important reason for hardenability control. However, the criterion of hardenability that at present is most widely accepted and used is based on a microstructure of 50 per cent martensite. This criterion, which was suggested by Grossmann,' does have considerable justification. It may be readily measured by a fracture or etch test and, since it represents the point at which the hardness is changing most rapidly with variations in cooling rate, it may be determined empirically from a hardness-depth curve by determining the point of steepest slope (the inflection point). Furthermore, in plain carbon steels or in steels of low hardenability, the difference in hardenability expressed in

Jan 1, 1947

By J. M. Hodge, M. A. Orehoski

It is now generally conceded that if a steel is to develop optimum physical properties in the conventionally quenched and tempered condition, the microstruc- ture after quenching should consist wholly of martensite; and that transformation of austenite to intermediate-temperature products during quenching will have a deleterious effect upon the physical properties, particularly the toughness, of the tempered material. This implies that, in order to obtain the optimum physical properties from a given steel, its "harden-ability " should be high enough to suppress all transformation except that to martensite under the heating and quenching conditions to which it will be subjected, and this premise is probably the most important reason for hardenability control. However, the criterion of hardenability that at present is most widely accepted and used is based on a microstructure of 50 per cent martensite. This criterion, which was suggested by Grossmann,' does have considerable justification. It may be readily measured by a fracture or etch test and, since it represents the point at which the hardness is changing most rapidly with variations in cooling rate, it may be determined empirically from a hardness-depth curve by determining the point of steepest slope (the inflection point). Furthermore, in plain carbon steels or in steels of low hardenability, the difference in hardenability expressed in

Jan 1, 1947

By Francis H. Crockard

During the past five years we have probably witnessed greater technological advances than in any similar period. Industry and science have steadily marched ahead. The makers of iron and steel products have watched with great interest the development of streamlined trains, faster and safer airplanes, the entirely new science of air-conditioning and the widespread use of stainless steels. Since 1930, we have witnessed the erection of the world's largest suspension bridge, the largest and fastest ocean liner and the spectacular Boulder Dam, while even greater things are planned in these particular fields. Other industries, too, have been moving ahead rapidly. This advance in a few years has been caused primarily by the fierce competition of the depression. Now, more than ever, is the emphasis placed upon quality and service. Makers of southern merchant pig iron have been no exception and have been confronted with increasingly strict chemical specifications and with much greater stress on physical characteristics than ever before. For example, sulfur in the iron must be held very low, competition demanding that it be in the 0.020's and low 0.030's; silicon content must be held within a very narrow range, and definite requirements of phosphorus and manganese are an essential part of the specifications. Physical characteristics are becoming of increasingly greater importance. The introduction of triple-skimmed, slow-cooled iron several years ago was the first step in this direction. Now there are a few customers who buy iron by chemical analysis and physical appearance, having found that the analysis alone is an insufficient guide to their requirements. In addition to questions of quality, the subject of cost has greatly altered the southern furnaceman's viewpoint on many things. Formerly we had low-grade but cheap raw materials, but recent developments, such as greatly increased labor rates, have raised the cost of the same

Jan 1, 1936

By Francis H. Crockard

During the past five years we have probably witnessed greater technological advances than in any similar period. Industry and science have steadily marched ahead. The makers of iron and steel products have watched with great interest the development of streamlined trains, faster and safer airplanes, the entirely new science of air-conditioning and the widespread use of stainless steels. Since 1930, we have witnessed the erection of the world's largest suspension bridge, the largest and fastest ocean liner and the spectacular Boulder Dam, while even greater things are planned in these particular fields. Other industries, too, have been moving ahead rapidly. This advance in a few years has been caused primarily by the fierce competition of the depression. Now, more than ever, is the emphasis placed upon quality and service. Makers of southern merchant pig iron have been no exception and have been confronted with increasingly strict chemical specifications and with much greater stress on physical characteristics than ever before. For example, sulfur in the iron must be held very low, competition demanding that it be in the 0.020's and low 0.030's; silicon content must be held within a very narrow range, and definite requirements of phosphorus and manganese are an essential part of the specifications. Physical characteristics are becoming of increasingly greater importance. The introduction of triple-skimmed, slow-cooled iron several years ago was the first step in this direction. Now there are a few customers who buy iron by chemical analysis and physical appearance, having found that the analysis alone is an insufficient guide to their requirements. In addition to questions of quality, the subject of cost has greatly altered the southern furnaceman's viewpoint on many things. Formerly we had low-grade but cheap raw materials, but recent developments, such as greatly increased labor rates, have raised the cost of the same

Jan 1, 1936

By James J. Halbouty

The restraining effects of war conditions on oil-field development are well illustrated by statistics on South Texas † fields for the year 1942. Statistics also show a decline in wildcatting, but this decrease is much smaller than that shown by field activity. In comparison with results in 1941, there was a reduction of about 44 per cent in the total number of wells drilled in the area (802 in 1942 against 1452 in 1941) This 44 per cent drop represents declines of 50.4 per cent in field wells and of 17.4 per cent in rank wildcats. Field wells (exclusive of 18 wildcats that discovered fields) totaled 598; also, 204 rank wildcats were drilled (see Tables 3 and 4). The corresponding figures for 1941 are 1205 field and extension wells and 247 rank wildcats. In this connection, it should be noted that whereas in 1941 the rank wildcats made up only 17 per cent of all wells drilled in the area, their percentage of the 1942 total was 25.4 per cent. In spite of the decrease of 43 in the number of rank wildcatst drilled, there were 18 new productive areas discavered, one more than the 17 new fields found in 1941. Thus the field-discovery rate for 1942, one new field for every 11.3 wildcats drilled, compares favorably with the I to 14.5 rate of 1941. Thirteen new producing levels were opened in fields; this includes the finding of 44' gravity crude on the west flank of the Sejita field in a 5700-ft. sand, which produccs distillate higher on the structure. Interesting, and showing the general scarcity of sand discoveries, is the fact that of the 13 new sands discovered, 7 were found in Jim Wells County. The year's sand-discovery rate of one new level for every 46 field wells compares very unfavorably with the I to 19.7 rate of 1941, during which 61 new producing horizons were found. Developmeilt of new fields was on a small scale. In several instances activity in these areas was not carried beyond the drilling of the discovery well. The field discoveries of 1942, together with the type of production obtained from the discovery wells and the total number of wells (productive and dry) drilled in them, are given below: Discovery Num- Field.I County Well her Produced Wells I. Cadena....... Duval Oil 2 a. Garza......... Duval Oil I 3. Dinn......... Duval Gas I 4. Keller......... Duval Gas I 5. East.......... Tim 0 11 I 6. Green Branch . McMullen Gas 3 7. Frost. .GreenBranch........ Starr Oil I 8. Garcia........ Starr Oil 6 9. Ulrich........ Starr Oil 4 10. Lykes......... Webb Oil 2 11. McLean....... Webb Oil 9 Iz. Alamo........ Hidalgo Distillate 2 and gas 13. Penitas....... Hidalgo Distillate 2 and gas 14. Xmpnan..... Jim wells i a 15. South Premont Jim Wells Distillate i and gas 16. Quinto Creek.. Jim Wells Gas 4 17. Roth.. . :..... Jim Wells Gas I I 18. South Sinton.. San Distillate I Patricio and gas . • See Table 2 for data on discovery wells and Table I for information on these fields. • See Table 4.

Jan 1, 1943

By James J. Halbouty

The restraining effects of war conditions on oil-field development are well illustrated by statistics on South Texas † fields for the year 1942. Statistics also show a decline in wildcatting, but this decrease is much smaller than that shown by field activity. In comparison with results in 1941, there was a reduction of about 44 per cent in the total number of wells drilled in the area (802 in 1942 against 1452 in 1941) This 44 per cent drop represents declines of 50.4 per cent in field wells and of 17.4 per cent in rank wildcats. Field wells (exclusive of 18 wildcats that discovered fields) totaled 598; also, 204 rank wildcats were drilled (see Tables 3 and 4). The corresponding figures for 1941 are 1205 field and extension wells and 247 rank wildcats. In this connection, it should be noted that whereas in 1941 the rank wildcats made up only 17 per cent of all wells drilled in the area, their percentage of the 1942 total was 25.4 per cent. In spite of the decrease of 43 in the number of rank wildcatst drilled, there were 18 new productive areas discavered, one more than the 17 new fields found in 1941. Thus the field-discovery rate for 1942, one new field for every 11.3 wildcats drilled, compares favorably with the I to 14.5 rate of 1941. Thirteen new producing levels were opened in fields; this includes the finding of 44' gravity crude on the west flank of the Sejita field in a 5700-ft. sand, which produccs distillate higher on the structure. Interesting, and showing the general scarcity of sand discoveries, is the fact that of the 13 new sands discovered, 7 were found in Jim Wells County. The year's sand-discovery rate of one new level for every 46 field wells compares very unfavorably with the I to 19.7 rate of 1941, during which 61 new producing horizons were found. Developmeilt of new fields was on a small scale. In several instances activity in these areas was not carried beyond the drilling of the discovery well. The field discoveries of 1942, together with the type of production obtained from the discovery wells and the total number of wells (productive and dry) drilled in them, are given below: Discovery Num- Field.I County Well her Produced Wells I. Cadena....... Duval Oil 2 a. Garza......... Duval Oil I 3. Dinn......... Duval Gas I 4. Keller......... Duval Gas I 5. East.......... Tim 0 11 I 6. Green Branch . McMullen Gas 3 7. Frost. .GreenBranch........ Starr Oil I 8. Garcia........ Starr Oil 6 9. Ulrich........ Starr Oil 4 10. Lykes......... Webb Oil 2 11. McLean....... Webb Oil 9 Iz. Alamo........ Hidalgo Distillate 2 and gas 13. Penitas....... Hidalgo Distillate 2 and gas 14. Xmpnan..... Jim wells i a 15. South Premont Jim Wells Distillate i and gas 16. Quinto Creek.. Jim Wells Gas 4 17. Roth.. . :..... Jim Wells Gas I I 18. South Sinton.. San Distillate I Patricio and gas . • See Table 2 for data on discovery wells and Table I for information on these fields. • See Table 4.

Jan 1, 1943

By D. L. Garthwaite, F. M. Stewart, F. K. Krebill

Pressure has been maintained in the Elk Basin Ten-deep reservoir since the initiation of inert gas injection in Sept., 1949. Oil is being produced under conditions favorable for gravity drainage, including high angle of dip, appreciable structural closure, and fairly good per~neability. Results being obtained are high per cent recovery of oil-in-place, sustained field productivity, reduced operating problems, and recovery of plant products. The high recovery has been calculated by alpplication of the gravity drainage theory described in an earlier AIME paper.' It is also confirmed from field performance by comparing nil recovery to date with gas cap spuce voided. GENERAL INFORMATION The Elk Basin field lies in Park County, Wyo., and Carbon County, Mont., approximately 50 miles east of Yellowstone Park. Located at the northern end of the Big Horn Basin. the field is situated on an elongated asymmetrical anticline (Fig. 1). The pressure maintenance project covered by this paper involves the Embar-Tensleep reservoir in this multi-pay field. Discovered in Nov., 1942, it has a proved productive area of over 6,300 acres. It consists of the 210-ft thick Tensleep sandstone of Pennsylvanian Age overlain by 40 ft of Embar dolomite of Permian Age. The two formations apparently are in communication with each other and are produced as a common source of supply. As 98 per cent of the reserves are contained in the Tensleep sandFtone, in this paper the Embar-Tensleep reservoir will he called simply the Tensleep. The reservoir is found at an average depth of 4,900 it, is approximately 7 miles long and 2 miles wide, and has a maximum oil productive closure of 2,330 ft. The strata dip an average of 21" on the west flank and 45" on the east. There are presently 132 Tensleep wells in the field drilled on 40-acre spacing; of these, 17 are shut in because of high gas-oil ratio (GOR) and eight are gas injection wells. Rock characteristics and related information for the pay section follow: Porosity, avg 10.7 per cent Permeability (air) from cores, avg 118 mds Permeability from PI'S 91 mds Connate water, avg 8 per cent Initial pressure (-400 ft) 2,234 psia Pressure April 1954 (-400 ft) 1.327 psia At high structural positions much of the better sandstone has connate water content of only 2 to 5 per cent as indicated by the coring of wells with oil in nearby Tensleep fields. In special imbibition tests, samples readily imbibed oil but repelled water. In tests on crushed samples, the sand grains rapidly settled in oil and carbon tetrachloride but formed a stable unsinking floc in water. This information indicates that the Tensleep sand is preferentially oil wet. The oil produced averages 29' API gravity and has a high sulfur content. Extensive sampling and testing have established the fact that characteristics of reservoir oil in this field vary greatly with structure, see Fig. 2. Additional detail on the variation of oil characteristics with structure at Elk Basin may be found in Reference 2. At original reservoir pressure the oil was undersatu-rated with gas, the bubble point being 1,250 psi at the crest but only 500 psi at the lowest elevation sampled. As noted on Fig. 2, other fluid properties—reservoir volume factor. solution ratio, gravity, viscosity, and hydrogen sulfide content—likewise vary greatly. These variations complicate mathematical analysis, for it is necessary to average these characteristics in order to enter them into reservoir engineering expressions. To further complicate analysis, sand-face pressure also varies greatly because of the increase in fluid head down structure. As an approximation, average properties under initial conditions may be read from Fig. 2 at the -450-ft elevation.

Jan 1, 1956

By J. W. Pugh

PREFERRED orientations in cold-rolled body-centered-cubic metals appear to have remarkable similarity. The as-cold-rolled textures in iron,1,2 silicon-iron,3 mild steel,4 molybdenum, vanadium,&apos; chromium,&apos; tantalum,&apos; tungsten,&apos; and a-zirconium-niobium alloys10 have been determined. These textures have, in some cases, been represented by congrUOUS pole figures and have all been described in one or both of two ways. They have frequently been reported as predominantly (100) <011> orientation

Jan 1, 1959

By H. E. Cline

Calculations of the formation and growth of faults caused by a variation in lumellar widths were made for a two-dimensioml three-plate problem. The angle between the a-ß boundary and the growth direction was allowed to vary and the time evolution was studied using a quasisteady state approach. At spacings smaller than a critical spacing given by X V = AO variations in the larrlellar widths grow in time to produce faults that coarsen the structure, while at spac-ings larger than this critical spacing, variations in the lamellar widths decay in time. If small plates are introduced into the structure they may grow only at large spacings to refine the structure. The time evolution and shape of faults were calculated for the three plate-problem and then the three dimensional problem and rod-like eutectic were qualitatively discussed. UNDERSTANDING of the mechanism by which the spacing of directionally solidified eutectics is determined may allow one to control their structure better. Steady state solutions for the growth of lamellar structures have been found for a range of lamellar spacings A and growth velocities V. To obtain a unique solution for the isothermal growth of pearlite, Zener1 assumed that growth occurs at a maximum velocity, while Tiller2 assumed that a eutectic alloy, grown under an imposed velocity, will choose a spacing corresponding to minimum undercooling. These assumptions are equivalent and have been referred to as "extremum growth". The extremum condition predicts the observed relation between velocity and spacing as given by V = constant [I] but does not provide a mechanism for changing the lamellar spacing. Jackson and Hunt3 calculated the interface shape by using solutions to the diffusion equation for a planar interface and a relation of the interface composition to the local curvature. If the spacing is much larger than the extremum spacing, the interface breaks down catastrophically to form forked plates. However, the catastrophic breakdown cannot account for the small adjustments in spacing that must occur in practice..3 Direct observations during the growth of organic eutectics4 and the Pb-Sn eutectic5 show that spacing changes occur by the formation of faults. A fault in a plate-like eutectic is the edge of a plate. Once the faults form, they may move to make small adjustments in the spacing.6,3 The motion of faults intersecting the growing interface was shown by an approximate analysis to give Eq. [I].6 A perfectly regular lamellar structure should be able to persist over a range of lamellar spacings. However, during growth small perturbations in the structure may occur. If the amplitude of the perturbation increases in time the structure is unstable, while if all possible perturbations decrease in time the structure is stable. In a previous paper7 variations in the shape of the solid-liquid interface were considered, while this paper considers only variations in lamellar widths while maintaining a macroscopically planar solid-liquid interface. Previously, theories of lamellar growth1"3 have artificially contrained the growth to give a regular periodic structure. To allow for a variation in spacing, the three phase intersections and groove angles were allowed to change with time as determined by assuming local equilibrium. THREE-PLATE PROBLEM Since the spacing changes in eutectics by local formation of faults,4&apos;5 it is suggested that local variations in spacing are responsible. The interaction between neighboring plates will be greatest because they have the smallest diffusion distance. For simplicity, as a nearest neighbor approximation, a three-plate problem will be considered, as illustrated in Fig. 1. The structure consists of a periodic array in which all the plates are allowed to vary in width. As in steady state growth it is assumed that the average composition in the solid remains constant. A variation in plate widths, that maintains the composition in the solid, was introduced by making the first a-phase plate thinner by an amount A, keeping the width of the second B-phase plate constant, and increasing the width of the third a-phase plate. If the structure were not perturbed, as in the regular two-plate problem previously described,&apos; then the groove angles at the three-phase junctions are the equilibrium angles, 0, and ? B, and the solid-solid boundary is normal to the interface. In the three-plate problem with a variation in plate widths the phase boundaries are assumed to be related to the three-phase junction by equilibrium angles, but the a/B boundaries may be rotated by an angle 0 from the growth direction. The angle H be-tween the tangent to the a/B boundary and the growth direction may vary during growth and determine the —> — — —.A_ Q-0 / 0 x, X2 Fig. 1—Schematic of the three-plate problem showing a variation in the spacing and the effect on the angles at the three phase intersections.

Jan 1, 1970

By O. Jay Myers

The war effort has furnished the necessary impetus for better magnesium foundry practice. Four or five years ago, there were but a few formulas in general use for core-sand mixtures for magnesium castings. Certain sands, binders, and inhibitors were specified and the proportions of these materials in each mixture were maintained between very narrow limits. As more and more war industries entered the field, much research was carried out and methods and practices were improved. Magnesium founding is still in a state of flux; therefore it is not uncommon to find one foundry spraying inhibitors on its cores, and another foundry using sand mixtures with incorporated protective agents. The basic core or dry-sand mold mixture for magnesium in use today is compounded with sand, core oil or resin binder, cereal, and moisture. Core oil or resin binder are added for baked strength while the cereal binder and moisture are for green strength. The normal mixtures (based on the weight of the sand) contain from o.5 to 1.5 per cent of both cereal binder and core oil, and the moisture content variesbetween 1.5 and 5 per cent. The ratio of core oil to cereal binder varies from 60:40 to 40:60, while the correct amount of moisture depends upon the method of coremaking. Protective Agents In all magnesium practice, protective agents are used in conjunction with the core and molding sands to prevent oxidation of the metal. The use of these inhibitors is not novel, but publications covering this field are not entirely adequate. Beck1 says: Magnesium alloys decompose water to form magnesium oxide, hydrogen being liberated in the process (Mg + H2O ? H2 ?+ MgO). This reaction results in the blackening of the skin and the appearance of areas of porosity on the casting surface, the cavities of which are filled with a grey oxide powder (these are termed &apos;burns&apos;). Although sand cores for magnesium castings are thoroughly dried during the baking cycle, burning will take place on the casting5 unless the metal is protected properly. This type of burning is more difficult to define than the "water-magnesium" reaction cited by Beckl A possible explanation may lie in the following equation: 2Mg + O2—> 2MgO Here, the source of the oxygen is not water, but the air in the mold cavity, together with the chemically combined oxygen in the core-binding media. Generally, two methods are used to prevent this reaction from taking place.

Jan 1, 1945

By E. C. Tveter, R. B. Tippin

The separation of minerals by heavy liquids is a standard laboratory technique which goes back at least 50 years, but commercially economic application of this principal to ore concenfration has been prevented by problems of liquid recovery. Recent investigations which demonstrate the different types of liquid-solid systems on various ores using the two major heavy liquids - methylene bromide and tetra-bromoelhane — are discussed in this article. As a result of these studies, over-all liquid recovery, and especially desorption of heavy liquid from the mineral surface, was improved by the use of surfactants as well as both thermal and mechanical energy. The examples given in the article indicate that heavy liquids which should find major commercial use in ore concentration are now available. The sink-float process using a heavy liquid medium has long been recognized as a nearly perfect method of mineral separation based on the differences in density of the minerals. The use of heavy liquid separation (HLS) offers the potential of an ore dressing method that provides the maximum possible natural concentrate grade and high recovery. In addi- tion the process requires no water, causes no waste disposal problems, and is extremely simple — the crushed ore is merely introduced into a liquid whose density is between that of the minerals to be separated. The minerals lighter than the liquid float while those heavier than the liquid sink. As such, HLS has become a standard laboratory tool but major commercial application has been prevented by the requirement for complete recovery of the heavy liquid, imposed by economics and materials handling hazards. Investigations, both in the United States and abroad, have shown that improved liquid stability as well as improved chemical engineering techniques brighten the future for HLS in ore dressing. The available commercial heavy liquids suitable for mineral separation cost from $2.00 to $20.00 per gallon1 and on this basis alone their complete recovery is economically desirable. Possibly of even greater importance is the fact that any residual heavy liquid remaining on the products could create a serious toxicity hazard. Consequently, to make the process commercially attractive requires (1) essentially complete removal of the liquid from the ore products and (2) optimum recovery of the liquid for reuse. Until recently these two stipulations have remained as obstacles but laboratory and pilot plant research now in progress suggests that these may soon be overcome. Various heavy liquid recovery systems have been proposed to meet these requirements and might be classified into one or more of the following three general classes: Solvent Wash (Fig. 1): The dissolution of the heavy liquid from the ore with a less expensive solvent,

Jan 1, 1969

By H. Larson, J. Chipman

The ferrous and ferric oxide concentrations of slags, expressed as j = Fe+++/(Fe+++ + Fe++), have been established through gas-slag equilibrium at 1550°C in a range of oxygen pressure of 10-I to 10-9 equilibriumatm. The value of j is increased by basic additions (BaO, CaO, MgO, MnO) and decreased by acidic oxides (SiO2 and TiO2). Oxygen pressure is shown graphically as a function of composition for slags which are analogous to those at the slag-gas interface of the open hearth furnace. THE progress which has been made in recent years in understanding the chemistry of metallurgical slags has been based largely on studies of slag-metal and slag-gas equilibria. There is a considerable body of knowledge which is applicable to reactions occurring at the slag-metal interface in open hearth steelmaking. There is little information concerning reactions of the slag with the furnace atmosphere and hence little basis for an understanding of the transfer of oxygen, sulphur, or hydrogen between gas and slag. The oxygen pressure of the open hearth atmosphere is normally of the order of 10-1 to 10-3 atm which differs by several orders of magnitude from that of about 10" atm at the slag-metal interface. The chemical properties of the slag, for example, the ratio of ferric to ferrous iron and the ability of the slag to hold sulphur in solution, are greatly affected by changes in oxygen pressure. This investigation was undertaken to enlarge our knowledge of the effect of oxygen Pressure on steel-making slags. Using air or controlled mixtures of CO a CO2 a range of oxygen Pressures from 10.&apos; to 10.&apos; was covered. Review of the Literature There are only a few references in the literature which pertain directly to this investigation. The most important is that of Darken and Gurry1,2 on the system iron-oxygen. This work included the determination of the phase diagram of the system and also a study of the field of homogeneous melts and their oxygen pressures. Their apparatus and procedure were very similar to that used in this study. Iron oxide was melted in a platinum crucible under an atmosphere of CO2:CO, CO2:H2, H2O, CO2, air or O2 depending upon the partial pressure of oxygen desired. After equilibrium was reached, the sample was quenched and analyzed for ferrous and ferric oxide. By appropriate calculations these authors were able to determine the oxygen and iron activities in the various slags, heats of formation of the oxides of iron, and heats of solution of iron and oxygen in the liquid slags. In a subsequent paper&apos; the same authors made a less thorough investigation of the effects of additions of lime and manganese oxide on the composition of iron oxide melts. Only a few experiments were made and those in a narrower range of temperature and oxygen pressure. Darken&apos; has investigated the fusion temperature of iron oxide in contact with silica under various atmospheres. He found that the temperature changes from 1120° to 1447°C as the gas composition changes from CO2/CO equal to 20.8 to pure oxygen. A comprehensive paper by White" predates the work of Darken and Gurry. The decomposition of ferric oxide into oxygen and lower oxides of iron was studied from 1000° to 1650°C and under oxygen pressures from 2 to 76 cm of mercury. The effect of

Jan 1, 1954

By M. Garfinkle, W. D. Klopp, W. R. Witzke

The tensile properties of binary W-Re alloys containing up to 33 at. pct Re were determined at temperatures from 78" to 3630°F. Elongations as high as 260 pct were observed in electron-beam-melted tungsten containing 23 at. pct Re when tensile-tested at 3630°F after a 1-hr anneal at 3090°F. All alloys tested under these conditions with rhenium contents between 20 and 28 at. pct exhibited elongations of at least 200 pct. These alloys also showed enhanced grain growth rates. The values of strain-rate sensitivity ranged between 0.2 and 0.3 for the alloys exhibiting high elongations. Houlezler, for swaged alloys tested just above the re-crystallization temperature, strain-rate sensitivities as high as 0.8 were observed. The high-temperature strengths of the high-rhenium-content alloys were also less than those of alloys with intermediate rhenium contents. ALLOYING with rhenium has two distinct effects on the mechanical properties of tungsten. One effect occurs in dilute solid solutions and is most clearly seen in the lowering of the hardness and of the ductile-brittle transition temperature at about 5 at. pct Re.1-3 The second effect occurs in the concentrated solid solution at about 25 at. pct Re, and is characterized by twinning and a larger decrease in the ductile-brittle transition temperature. An aspect of the high-rhenium-content alloy which has received little attention is the higher-than-usual tensile ductility at 3500°F.3 Anomalous high ductility has been observed in several other alloy systems. usually associated with a phase transformation or a solid-solubility limit.4&apos;5 The phenomenon is now commonly termed superplasticity. High-strain-rate sensitivities6 and grain boundary sliding7 have been reported for materials that undergo superplastic deformation. Also, it has been found that superplastic materials usually have a very fine grain structure (less than 10 pm).8 and it has been proposedg that such a structure alone is sufficient for superplasticity. The purpose of the present study was to further characterize the high-temperature tensile properties of W-Re alloys to determine the conditions under which they might be superplastic. Tensile and selected strain-rate sensitivity tests were conducted on alloys containing 0 to 33.3 at. pct Re at temperatures from 78" to 3630°F. Grain-growth rates were also determined on most alloys at 3630°F. Fig. 1 indicates the compositions evaluated and their locations relative to the solvus line in the tungsten-rich end of the W-Re phase diagram. Twelve binary W-Re alloys containing up to 33.3 at pct Re were double electron-beam-melted and subsequently fabricated to 0.3-in. rod by extrusion and swaging. The starting materials were commercial powders of tungsten and rhenium with impurity levels as listed in Table I. The various blended W-Re compositions were hydrostatically pressed at 70 ksi. The pressed bars were drip-melted into 1.5-in.-diam ingots and then remelted into 2-in.-diam ingots at a chamber pressure of 10~5 torr. The ingots were canned in molybdenum and extruded to round bar at a reduction ratio of 6:l. The alloy extrusions were swaged to about an 80 pct reduction at 2100" to 2900°F. Buttonhead tensile specimens with a reduced section diameter of 0.16 in. and a gage length of 1.0 in. were centerless-ground from the swaged bars

Jan 1, 1970

By Tibor Stefansky, John E. Dorn

MOTT and Nabarro1-5 were first to illustrate the importance of the flexibility of dislocations in accounting for the strengthening that metals undergo due to the presence of internal-strain centers. Such strain-centers might arise from a number of causes such as radiation damage, the presence of semicoherent and coherent precipitates and clusters, as well as individually dispersed interstitial and misfit substitutional solute atoms. Each strain-center induces positive and negative shear stress fields on the slip planes of the surrounding alloy matrix. In order to effect plastic deformation, therefore, the alloy must be subjected to sufficiently high applied shear stresses to push dislocations past all such internal stress fields. If dislocations were inflexible and moved as rigid lines, they would be equally pushed and pulled by internal stress fields. At this extreme the strengthening would be vanishingly small. Dislocations, however, are not rigid; they are flexible and extensible. They wiggle between positive and negative strain-centers, thus increasing their line energy at the expense of their interaction energy with strain-centers. cottrel16 and Friedel7,8 have independently presented lucid reviews of the significance of the Mott-Nabarro dislocation-flexibility concept to the strain-center strengthening of alloys. Their analyses however were only semi-quantitative. There is evidence in the recent literature of renewed interest in a more rigorous analysis of flexibility. Thus, Gleiter9 and Gerald" have shown that the calculated strain-energy interaction between a dislocation and the stress fields of coherent precipitates can be seriously in error if the flexibility of the dislocation is not taken into account. This report will be concerned with a more detailed analysis of the problem based on the following approximations: 1) Although many types of strain-centers exist, the following analysis will be limited to the case of solute-atom strain-centers in fcc substitutional alloys. 2) To facilitate the analysis by avoiding statistical considerations, the strain-Centers are assumed to be in regular arrays on the slip plane. Although the quantitative results are somewhat dependent on the type of array that is assumed, the qualitative trends are similar for various arrays that were studied. 3) An adjustment of the results from those for square arrays to those for the more realistic case of a random distribution of strain-centers is accomplished by adopting the interesting statistical theory first introduced by Kochs,11,12 elaborated on by Dorn, Guyot, and stefansky,13 and analyzed by Foreman and Makin14 in their computerized experiments. 4) For simplicity the dislocation lines are taken to wiggle about their edge orientation and no correction is applied to their line energy for deviations from edge configurations or for the elastic interaction between segments of the now curved dislocation. It will be shown that for extremely low concentrations of atomic strain-centers the strengthening increases with the square root of their concentration. For slightly higher concentrations the strengthening rate becomes less rapid. At a critical concentration a maximum strength is obtained and a decrease in the strengthening takes place as the concentration of solute atoms is further increased. These trends are a direct consequence of dislocation flexibility. They arise from changes in the amplitude of the waviness of the dislocation line at the yield stress with solute atom concentration. Despite the simplifying assumptions that were made, the results agree qualitatively with appropriate experimental data. I) STRESS FIELDS ON SLIP PLANES Internal stresses are introduced in a lattice whenever a host atom of radius ro is replaced by another that has a different atomic radius. According to the classical theory of linear elasticity,15 the stress field about a solute atom at the origin of a spherical coordinate system is given by arr=-4G€(?_0)3 ffflfl ="W =2G€{t) f°rr^ro(l+e) UJ where G is the shear modulus of elasticity and Y, = ro(l + E) is the radius in situ, of the substituted atom. As shown by ~shelb~,&apos;~ this approximation assumes that the bulk modulus of elasticity of the substituted atom is identical with that of the host species. ~abarro&apos;~ suggested that the strain E can be deduced

Jan 1, 1970