By C. G. Dunn

Many investigations have been made concerning the nature of plastic deformation and recrystallization of metals either in the form of polycrystalline materials or in the form of single crystals. However, similar work on strip materials composed of large grains as thick as the strip and having a high degree of preferred crystal oricntation has not been carried out extensively. Such materials are ideal not only for studying changes in single crystals under conditions where neighboring grains exert their influences but also for obtaining the complete change in orientation of a grain or group of grains during the course of plastic deformation and subsequent recrystallization. It is well known that first-order twins in the form of Neumann bands may be produced during the plastic deformation of ferrite crystals, particularly silicon ferrite crystals.l--3 Furthermore, it is believed that high-stress regions exist in the vicinity of these bands4. and it has been said that these banded regions would be active in recrystallization processes.5 Evidence to that effect in silicon ferrite had already been presented with photomicrographs showing recrystallization among Neumann bands during the early stages of recrystallizati~n.5,6 Similar evidence has been published for nonferrous metals5 Merging of fine parallel deformation bands during annealing to form twin bands of ordinary appearance in alpha brass has been offered not only as evidence of an active role being played by mechanical twins but also as evidence that such twins cxisted prior to recrystalli~ation.5 Proof that such new structures are actually first-order twins, or even twins at all, must be considered inadequate except for those cases where X-ray or optical data have been obtained to confirm the necessary oricntation relationship.7,8 A. B. Greninger has obtained excellent iliustrations of annealing twins in alpha iron.9 Since his material was previously deformed by sharp hammering, a process that generally induces Neumann bands, the existence of twins following annealing might suggest that they grew from mechanical twins. In connection with transformation twins in alpha iron, Greninger reported that grains containing three twin orientations occurred rarely and none occurred with three sets of well-developed bands.9 The work at the Pittsfield Works Laboratory on silicon ferrite in the form of large-grained strip steel deformed a small amount and annealed to partially recrystallize the grains indicates that the deformation and recrystallization processes that lead to annealing twins involvc more complex processes than the formation of Neumann bands and the growth of such bands. Some groups of annealing twins are obtained which contain not only three well-developed twin structures, but also contain more than one order of twins. It is also shown, in one case, that an interrelated group of twins did not arise within one single parent grain and, furthermore, orientations of grains in the group

Jan 1, 1944

By Walter S. McKee

When mixed with common cast steel in quantities ranging from 11 to 131/2 per cent. and properly treated, manganese increases the ductility of the metal and adds greatly to its toughness and resistance to abrasive action, which properties comprise the distinctive characteristics that make manganese steel so valuable for many purposes at the present time.. * At present the manganese-steel foundries of this country have an annual capacity of about 60,000 tons and most of the growth has occurred within the past 10 years. In the early days of the industry it was impracticable to make manganese castings weighing over a few thousand pounds, but at present crusher heads, rolling-mill pinions, and similar castings weighing up to 30,000 Ib. each are produced, and it does not appear that the limit of weight has been reached by a considerable margin. Manganese steel is similar in analysis to ordinary first-class converter metal except that it is high in carbon and contains from 11 to 13.5 per cent. of manganese. From one standpoint manganese steel is similar to malleable iron in that the casting as it comes out of the sand is hard and brittle and must be made ductile by a heat-treating process. The heat treatment is an essential part of the process of making manganese-steel castings and must be properly carried out to secure satisfactory results. The necessity for heat treatment limits the thickness of sections which may be made of manganese steel. Originally the annealing depth was comparatively small, but researches carried on during the past few years have resulted in an increase in the thickness of section up to 51/2 in., which it is possible to treat successfully. Large castings are cored out to a minimum thickness of 51/2 in., thus not only eliminating some of the internal stresses which are invariably set up in a very thick casting, but also reducing the weight and inertia of the piece, an important consideration if the casting is to be a moving part in a machine. At the same time, the thickness of 51/2 in. is sufficient to permit the use of manganese steel for the heaviest classes of machinery.

Jan 1, 1916

By W. E. Forsythe

WHEN measuring ordinary temperatures, the instrument is generally placed in very close contact with the body the temperature of which is desired. However, if the temperature of the source is continually raised, a point is soon reached where no known substance will, in general, remain constant in any of its temperature-measuring properties if placed in direct contact with the source. Also, it is occasionally necessary to measure the temperature of a source that 'is so small or so situated that it would be very hard to bring the measuring instrument into direct contact with the source. When these conditions exist, advantage is taken of the well-known fact that all bodies, when at sufficiently high temperatures, send out radiation in amounts readily measurable. This radiation has been found to be related to the temperature. The temperatures of very hot bodies have probably always been judged by the color, or the brightness, of the light given off. With practice, one can estimate probably within 50° to 100° C. of the correct value. However, if judgment is left to the eye alone, very much larger errors are sometimes made, due to

Jan 9, 1919

By John Hays Hammond

The Transvaal comprises about 120,000 square miles (nearly • the size of the United States Territory of New Mexico). Besides the famous Witwatersrand, which will here be de scribed in detail, there are two quartz-mining districts of some importance, viz., Lydenburg and De Kaap. The Lydenburg district first attracted attention in 1876, when the alluvial deposits of that section began to be exploited. At a later period vein-rnining was started, and at the present time several companies are operating in that district. The product in 1898 of five companies, running 137 stamps, was 154,560 tons of ore, yielding 108,884 crude ounces of gold (an average of 14.09 dwt. crude gold per ton) valued at £392,378. The De Eaap gold-fields were discovered in 1884. In 1898, seven companies, running 200 stamps, produced 89,760 crude ounces of gold, valued at £314,792. I. Mining Titles in the Transvaal. The mining laws of the Tranuvaal are most excellent in char acter, and while the claims cover every square foot of land for an area of nearly 40 miles long by from 2 to 3- miles wide, there have been practically no conflicts over extra-lateral rights. Notwithstanding the change in the political status of the Transvaal likely to follow the present war, it may be coufi dently assumed that the main features of the mining law of the South African Republic will be retained, and certain op pressive featureu of monopolies, etc., bearing with special weight on the mining industry, will be abolished. The dynamite mo nopoly was one that bore most heavily on the mining industry; and, according to the Reports of the State Mining Engineer, explosives, including fuse and detonators, amounted to nearly 10 per cent. of the total working costs of the mines. Further more, it was impossible to obtain the proper quality for the most economical working, and often 80-per-cent. or 40-per-cent. gelatine had to be used- in many instances where 60-per-cent.

Jan 1, 1902

By Oswald J. Heinrich

(Read at the Philadelphia Meeting, February, 1878.) DURING the last twenty years much has been done to investigate and define the Mesozoic formation of the United States along the Atlantic States, as well as in the Territories. The investigations of Professors Hitchcock, Emmons, Hayden, H. D. Rogers, and those now in progress in connection with the geological surveys of Penn-

Jan 1, 1878

By F. M. Simonds, E. Z. Burns

The Rawley property is located in the Kerber Creek mining-district, Saguache county, Colorado, at an elevation of 10,600 ft. (See sketch-map, Fig. 1.) Ore was found in this vicinity as early as 1880, and claims covering a large area were located and in many instances patented. The ores, however, being of comparatively low grade, and the nearest railway station, Villa Grove, being some 20 miles away, it is extremely doubtful whether any considerable amount of ore was ever handled at a profit. It is safe to say that several hundred thousand dollars were spent (a large part in building mills) previous to 1902-03. About that time a very capable promoter gathered together a group of these claims and interested some New York people, who had had no previous mining experience, in the purchase of these claims. Following the organization of a company, this promoter became General Manager. As often happens under such conditions, the first step was to erect a mill to treat 100 tons per day. It may not be fair to this enterprise to say that the failure which followed might have been foretold, simply on general principles, but this much is certain—the water supply fluctuates in the course of a season through a wide range and for a considerable portion of the year was inadequate to run this mill at capacity. Further, it is currently reported that some of the mill foundations were placed on ice. However true this statement may be, it is a fact that, when first inspected by us, many of the belts in the mill were held on'their pulleys by means of idlers. A shut-down followed, with a material re-adjustment of interests, at which time we became consulting engineers for the company.

Jan 1, 1914

By J. Campbell

Various models are discussed for the evaluation of the negative pressures which may occur in solidifying materials which exhibit various deformation modes: elastic-plastic, Bingham, viscous, or creep flow. The inadequacy of the previously proposed elastic-plastic solution for solidifying metals is revealed by comparison with the more reliable creep results which are given graphically for aluminum, copper, nickel, and iron. The maximum tensions experienced in the liquid phase of solidifying spheres ranging in size from large castings to submicron powders are in the range from —10' to —105 atm for these metals. THERE has been much recent interest in the negative pressures associated with the volume change on solidification and in the possibility of the occurrence of cavitation. Considering the freezing of a highly supercooled liquid, an attempt to evaluate the stresses in the liquid ahead of the rapidly moving solidification front has been made by Horvay1 on a microscale and by Glicksman2 on a macroscale. In a casting of a wide freezing range alloy, the pressure differential due to viscous flow of residual liquid through the pasty zone has been discussed by Piwonka and Flemings,3 In a previous publication4 the author has attempted to estimate the negative pressure occurring in the residual liquid of a spherical casting, employing an elastic-plastic model to describe the collapse of the solidified shell under the internal tension. An earlier model assuming a rigid shell was shown to be inaccurate by many orders of magnitude. The elastic-plastic model is critically reviewed here, and other models are developed which are thought to be more closely related to metals and other materials near their melting points. The spherical geometry (Fig. 1) is chosen because the highest shrinkage pressures would be developed, although the analyses are readily adaptable to cylindrical geometry. A parallel sided casting experiences little internal tension because of the relatively easy dishing inward of the sides. (This commonly observed phenomenon has previously been attributed solely to atmospheric pressure.) Furthermore, small regions of confined liquid in a large solidified volume of a casting approximate reasonably well to spherical geometry. ELASTIC-PLASTIC MODEL The author has shown4 that as solidification proceeds the internal hydrostatic tension builds up until the elastic limit of the shell is exceeded. At this point the internal pressure is closely -2Y/3. Subsequently a plastic zone spreads from the inner surface toward the outer surface of the shell. When the whole casting is deforming plastically a rather more generalized analysis taking account of the externally applied pressure PA + 2y/b gives the internal pressure as: P = Pa + 2y/a + 2ys/b - 2 Y In(b/a) [1] The 2y/a and 2ys/b terms result from the tendency of the liquid-solid and solid-vapor interfaces to shrink, reducing their energy, and thereby helping to collapse the solid phase and compress the liquid phase. The 2y/b term would be important only for powders. The last term arises because of the plastic restraint of the solid, resisting collapse and so effectively expanding the residual liquid. From Eq. [I] it is easily shown that there is a minimum in the pressure at the radius amia= y/Y [2] which is of the order of 103K for the metals aluminum, copper, and iron, and corresponds to the minimum pressure Pmin = 2 Y[l-ln(bY/y [3] The results of a fully worked out elastic-plastic solution are given in a previous reporL4 The main criticism which may be leveled at this analysis when applied to metals at their melting points is the strong dependence of the yield stress on the strain rate. The strain rate varies with both solidification conditions (e.g., whether chill-cast or slowly cooled) and during solidification, as is indicated in the following section. Thus an appropriate choice of Y is very arbitrary. Before proceeding to a discussion of models which are strain-rate-dependent, it is necessary to evaluate the strain rate as a function of the rate of solidification. SOLIDIFICATION RATE Various empirical relations have been deduced5 for the rate of thickening of the solid shell by pour- out tests on partially solidified spheres. These, however, are unsatisfactory for our purposes since they become very inaccurate when the liquid core is very small. A theoretical approach is therefore necessary, and some solutions are set out below. Making the assumptions of constant surface temperature of the casting during freezing, no superheat, and a material freezing at a single temperature, Adams8 deduces the approximate solution: which becomes when b » a: Employing a semiempirical approach vallet6 finds:

Jan 1, 1969

By R. S. Kinasevich, D. D. Crabtree, D. W. Fuerstenau, T. P. Meloy, A. L. Mular

This paper presents details of the concept that size reduction in comminution machines takes place by three mechanisms; namely impact, abrasion, and chipping grinding. Experimental evidence is presented to show that each of these comminution mechanisms produces particles of a characteristic size distribution. The actual product from a comminution device has been postulated to be the result of a composite of these three types of mechanisms. Composite curves are demonstrated for a material following the Gaudin-Schuhmann, Gaudin-Meloy, and Rosin-Rammler size distributions. About forty years ago, Gaudin1 showed that grinding may be considered a combination of impact and attrition. Since that time, major efforts have been devoted to studies, both experimental and theoretical, of impact and compression fracture, while attrition has been almost wholly neglected, at least quantitatively. A significant attempt to distinguish between attrition and impact grinding is the work of Tanaka2 in Japan. By means of an instrumented abrasion grinder and a drop weight device, he determined coefficients relating the increase in surface area of various materials to the energy expended by the two methods of comminution. He showed that physical properties of a material determine its response to attrition and impact grinding. By extending his ideas to ball milling, he concluded that to a large extent the basic comminution process in a ball mill is due to the impact of falling media. Because Tanaka used a mass of particles in his drop weight device, however, he did not obtain pure impact size reduction. The purpose of this paper is to define basic mechanisms of size reduction, to verify that each has a characteristic and meaningful distribution curve, and to show how a combination of these mechanisms results in a size distribution very like that produced by grinding mills. DEFINITION OF COMMINUTION MECHANISMS The product from a grinding device will be considered to be the sum of the contributions resulting from the action of three basic mechanisms of size reduction which operate in a ball and rod mill. These are impact grinding and two forms of attrition, namely abrasion grinding and chipping grinding. Each is defined below. Impact Grinding: If a straight line is obtained when the cumulative weight fraction finer than a given size is plotted on log-log paper as a function of that size, the slope of the line is defined as the distribution modulus. A number of investigators 3,4,5 have shown that impact fracture of single specimens of different composition and shape results in a distribution of daughter particles that exhibit a distribution modulus of unity. This has also been true for materials broken in slow compression. Moreover, under slow compression or impact fracture conditions, theoretical distribution equations6*' which approximate the Gaudin-Schuhmann distribution when the distribution modulus is close to unity agree reasonably well with the experimentally obtained products. If one now considers a comminution process where many impact or compression fracture events are taking place, then any rational summation of the individual events yields, in the finer size range, a Gaudin-Schuhmann distribution whose distribution modulus is also unity. If the size distribution of the product from a mill has a distribution modulus of unity, it is implied that particles are fractured in a manner which results in a comminution event having a distribution like that obtained for the breakage of single specimens. These impact events would occur when a particle is smashed between balls or between a ball and the mill liner. Attrition, on the other hand, is that form of grinding which cannot be called impact grinding, and comprises both abrasion and chipping grinding. Abrasion Grinding: Abrasion is a form of surface wear resulting when particles rub against each other or against balls or the mill liner of a tumbling mill, somewhat like a piece of wood being rubbed over a piece of sandpaper. The surface wears at a more or

Jan 1, 1964

By I. Lowthian Bell

THERE has been probably no improvement introduced into the manufacture of iron which created more surprise in the minds of practical smelters and of scientific men than Neilson's discovery of the hot blast. In 1829, Messrs. Dunlop & Co. consumed at the Clyde Works, near Glasgow, nearly 7 3/4 tons of coal to make a ton of pig iron, of which about 20 cwts. was employed under the boilers of the blowing engines, leaving nearly 7 tons for the consumption of the furnace itself. In the year 1833, by heating the air to 612° F. (322° C.), they reduced the 7 3/4 tons to 3 tons by the mere burning of 8 cwts. of coal in the apparatus for raising the blast to this temperature. The statement just given is strictly true in a commercial sense, but when we come to consider the question as one of physical science, it is necessary to eliminate some of the conditions which conduced to so extraordinary a result. Anterior to Neilson's time the fuel employed in smelting iron was coke, and it was supposed at that period, erroneously, however, that coal in its raw state, when burned with cold air, was totally unfit for the purpose in question. This mineral, as it was obtained from the Lanarkshire coal-field, contained about 35 per cent. of volatile matter, but the process of charring it was performed in so unskilful a manner that instead of receiving 88 cwts. of coke from 135 cwts. of coal, 60 cwts. only was the product of the operation. Again, the reduced consumption of carbon in the furnace itself was accompanied by a corresponding diminution of blast, and this was followed by an economy of half a ton in engine coal. After making a proper allowance, however, for all these collateral circumstances, we are within the mark when we admit that in actual coke, which is really the form the fuel has to assume before it is burnt in the blast-furnace, not less than 30 cwts. was saved by heating the blast to 615° F. (322° C.). This unexpected economy, be it remembered, was obtained by the combustion of the 8 cwts. of coal, somewhat wastefully applied in the hot-air apparatus. Numerous have been the opinions advanced by different authorities in the scientific world to account for the apparent anomaly, but none,

Jan 1, 1877

By A. K. Mukherjee, J. E. Dorn

A modified Peierls model is Presented for the rationalization of the asymmetric plastic behavior of single crystals of bcc metals. The model assumes that the asymmetry of slip arises from a tendency toward asymnetric splitting of the a/2[111] screw dislocation. The approach differs from former theories however insofar as it assumes that the splitting is so minor ttut only the core energy is modified and that no real partial dislocations exist. As a consequence, the concepts of a line energy of a partial dislocation, interaction between partial dislocations, constriction energies, and stacking fault energies are not invoked. Instead the present analysis is based on a specialization of the Peierls mechanism which assumes an asymmetric dislocation core which is modified by the effective stress and permits cross slip. The theoretical predictions on the stress-temperature -strain rate and orientation relationship agree qualitatively with the limited experimental data that are currently available. Additional experimental work over wider ranges of conditions is suggested to provide more complete evaluation of the possible validity of this theory. RECENT experimental investigations on the low-temperature thermally activated deformation of bcc metals have confirmed the existence of several unique orientation effects. These will be described with the aid of the standard stereographic projection shown in Fig. 1. If slip were determined exclusively by crystal symmetry, the deformation characteristics would be symmetrical about X; = 0 and independent of whether the specimen were subjected to a tension or a compression stress, regardless of what combinations of slip planes might be operative. Experiments, however, reveal that neither of these symmetry based predictions are valid. A schematic representation of the commonly observed asymmetry of both the yield stress and the plane of slip is shown in Fig. 2. A reversal of the direction of stressing results in an inversion of the asvmmetric behavior. 1) Asymmetry bf Yielding. A detailed investigation on the asymmetric yielding in an Fe-2.7 pct Si alloy was repoEted by Tabka, Tikeuchi, and Furubayashi,1 Similar trends have been observed by Keh and Nakada on iron,' Stein on molybdenum,3 Bowen, Christian, and Taylor4 on columbium, Sherwood, Guiu, Kim, and pratt5 on Ta, Cb, and Mo. The degree of asymmetry not only depends on the atomic number and alloying but, in all cases that have been examined, it also increases with a decrease in the test temperature. 2) Asymmetry of the Slip Plane. Asymmetric $I-~: curves of the type shown in Fig. 2 have been found for several Fe-Si alloys6-8,1 and columbium.4 There is general agre_ement that near X: = 30 deg slip occurs by the [111](211) mode so that ?1 = 30 deg. As X; decreases it appears that [111](211) to [111](101) cross slip takes place leading to slip band traces on intermediate planes. And as xi approaches 0 deg, sharp

Jan 1, 1970

By W. H. Yarroll

This paper presents a general discussion of the utility of the statistical technique known as multiple correlation, and gives three specific examples of its application. The first demonstrates the most simple form, or straight-line, multiple correlation. The other two demonstrate multiple correlation analysis in best-fitting third-degree parabolas. With the increasing availability of digital computers, the method becomes entirely feasible where heretofore its use was impractical. The advantages of the method are discussed, and curves are presented which were developed by computerizing the regression equations developed in the examples. The method described in this paper is for use with complex systems, and the examples given are complex metallurgical systems. This subject falls under the general classification of cybernetics, which is defined' as "the science of control and communication, in the animal and the machine." Machine, in this case, can include chemical and physical processes which take place within machines and processing equipment of all kinds. The classical approach to scientific investigation has been the construction of simple models and the changing of variables one at a time. This method is wholly inadequate for obtaining useful information from the complex systems of modern technology including many of our flotation and hydrometallurgical processes. Cybernetics offers the method by which complex systems which have been implemented as an art in the past can now be analyzed with all the discipline of a science. Mathematical techniques for achieving multiple correlation analysis have decided advantages over some of the other statistical methods.2-4 Multiple correlation does not require a series of experiments that have been rigidly planned as do many of the other statistical methods. For this reason, it can be used effectively for interpretation of information from op- erating plants, where planned experiments are impractical, as well as for laboratory experiments. First-degree multiple correlation has been used for many years, and was useful, but limited to linear or nearly linear relationships. The technique described in this paper provides a method for analyzing systems which may be non-linear. This particular technique is multiple correlation analysis in best-fitting third-degree parabolas. It is quite possible that lack of reference to the technique has been due to the overwhelming mass of computations it requires even for relatively simple problems. With the advent of computers, however, its use has become entirely feasible. For the benefit of those who may not be familiar with the subject, it might be well to pause at this point to discuss multiple correlation analysis — what it is and what it achieves. To go back to the old familiar fitting of a set of points with a best-fitting straight line by the least squares procedure, it is conceded that this a good method where there is only one independent variable influencing the dependent variable under consideration, and providing that the relationship is linear. In most fields of investigation, however, there are usually a number of factors exerting important influence, and they frequently bear relationships with the dependent variable other than straight line. Under these conditions, it is easy to see how misleading a simple correlation study might be. Multiple correlation can be used for any number of variables. Within the experience of the writer, this technique has been used to establish regression equations for determination of carbon rate, burden permeability, and production rate on iron blast furnaces, production rate on open hearth steel furnaces, life of molds for steel ingots, rolled steel tensile strength and various defects in rolled products, the performance of ore dressing equipment, and optimization of extractive metallurgical process variables. The discovery of mathematical correlation does not prove, per se, true cause-and-effect relationship, but simply establishes a hypothesis. If the regression equation can be used to make successful predictions of what will happen with future arrays of independent variables, then one can feel reasonably assured that true cause-and-effect relationships have been discovered.

Jan 1, 1968

By H. E. McKinstry

Movement on a fracture of irregular shape can cause local widening of the fissure and thereby offer freer channelways for circulation of ore-depositing solutions. This influence: coupled with large areas of wall rock available for reacting with ore solutions in brecciated and shattered ground can account for locally active deposition of metals and the resulting ore shoots. Such irregularities in the fracture system may be caused by local variations in the strength of rocks and by pre-existing lines of weakness, especially if these stand at favorable angles to certain components of the fracturing stress. Therefore correct interpretation of the mechanics of fracturing should permit deductions as to structurally favorable places on unexplored portions of the vein system. Introduction It has long been recognized that movement on a curved or irregular fault surface is capable of separating the walls in certain portions of the fault, but until very recent years the importance of this mechanism as a factor in localizing ore shoots has escaped proper recognition. A short time ago W. H. Newhouse' presented a careful analytical study of displacements and their corresponding open spaces. For reasons that will be discussed later, it frequently happens that portions of the vein which are favorably oriented are not merely wider but also richer than the average. In many cases the widening with its accompanying richness coincides with very minor changes in the dip or strike of the vein, irregularities that commonly escape notice unless the vein is mapped in detail and a careful geometrical analysis made. While the relationship between the width of the vein and the changes in dip or strike has been recognized as a matter of observation, the irregularities have been accepted as more or less the result of accident. There has been very little effort except in isolated cases to find out the causes of these changes in dip or strike. Yet it is clear that if the causes can be recognized and expressed in terms of geologic structure the geologist will know where to look for repetitions of these favorable conditions either on extensions of the same vein or on adjoining veins. Any lack of understanding of the causes is due to the limitations of our ability to interpret our observations and not to the sheer capriciousness of

Jan 1, 1941

By H. E. McKinstry

Movement on a fracture of irregular shape can cause local widening of the fissure and thereby offer freer channelways for circulation of ore-depositing solutions. This influence: coupled with large areas of wall rock available for reacting with ore solutions in brecciated and shattered ground can account for locally active deposition of metals and the resulting ore shoots. Such irregularities in the fracture system may be caused by local variations in the strength of rocks and by pre-existing lines of weakness, especially if these stand at favorable angles to certain components of the fracturing stress. Therefore correct interpretation of the mechanics of fracturing should permit deductions as to structurally favorable places on unexplored portions of the vein system. Introduction It has long been recognized that movement on a curved or irregular fault surface is capable of separating the walls in certain portions of the fault, but until very recent years the importance of this mechanism as a factor in localizing ore shoots has escaped proper recognition. A short time ago W. H. Newhouse' presented a careful analytical study of displacements and their corresponding open spaces. For reasons that will be discussed later, it frequently happens that portions of the vein which are favorably oriented are not merely wider but also richer than the average. In many cases the widening with its accompanying richness coincides with very minor changes in the dip or strike of the vein, irregularities that commonly escape notice unless the vein is mapped in detail and a careful geometrical analysis made. While the relationship between the width of the vein and the changes in dip or strike has been recognized as a matter of observation, the irregularities have been accepted as more or less the result of accident. There has been very little effort except in isolated cases to find out the causes of these changes in dip or strike. Yet it is clear that if the causes can be recognized and expressed in terms of geologic structure the geologist will know where to look for repetitions of these favorable conditions either on extensions of the same vein or on adjoining veins. Any lack of understanding of the causes is due to the limitations of our ability to interpret our observations and not to the sheer capriciousness of

Jan 1, 1941

By R. D. Pehlke, W. M. Small

The effect of added alloying elements on the solubility of nitrogen in a liquid alloy of 74 wt pct Fe. 18 wt pct Cr, and 8 wt pct Ni has been studied. At 1600°C and 1 atm nitrogen pressure, aluminum, chromium, columbium, manganese, molybdenum, tantalum, and vanadium increase the solubility of nitrogen in the liquid 18 Cr-8 Ni alloy, whereas additions of cobalt, copper, nickel, silicon, tin, and tungsten decrease the solubility. Interaction parameters based on a constant ratio of iron, chromium , and nickel have been used to quantitatively define the changes in nitrogen solubility. INVESTIGATIONS on the solubility of nitrogen in liquid iron have usually treated the pure metal, and often the influence of a single added element. Pehlke and Elliott1 carried out a comprehensive study on the influence of alloying elements on nitrogen solubility in liquid iron, and compared their results with previous studies. Turnock and pehlke2 have recently reported a study on the solubility of nitrogen in multicomponent liquid iron alloys. The original interaction parameter proposed by wagner3 was successfully employed in these studies. The need for obtaining information on the gas solubility in more complex alloys is indicated by the increasingly significant role played by dissolved gases in the processing of iron-based materials. The commercial stainless steels, for example, represent an area where data on nitrogen solubilities are required as a function of composition, temperature, and gas pressure. The nitrogen solubility in liquid Fe-Cr-Ni alloys has been studied by Humbert and Elliott.4 Their investigation covered the entire ternary system, and attempted to use data from binary alloys to predict nitrogen contents in liquid ternary alloys. Langenberg,5 using a method developed by Morris and buehl,6 calculated the nitrogen solubilities in multicomponent iron alloys from data available on binary iron alloys at 1600°C. Nelson,7 using a regular-solution model, extended this prediction to include the effect of temperature. Chipman and corrigan8 and Turnock and pehlke2 also employed empirical methods to calculate nitrogen solubilities in liquid multicomponent iron alloys. In order to provide a basis for predicting nitrogen solubility in liquid stainless steels, and to extend the data available for thermochemically modeling systems of this type, the following investigation was carried out. The study involved measupements of nitrogen solubility in a nondilute alloy and examination of the influence of a small addition of an alloying element on the nitrogen solubility. The study was focused on a very narrow range Of composition in the vicinity of 18 wt pct Cr-8 wt pct Ni (herein referred to as 18-8) with special emphasis on the change of.nitrogen solubility with the addition of a fourth metallic element. EXPERIMENTAL PROCEDURE A Sieverts' apparatus, described previously,1,2 was used in this investigation. The charge materials were contained in a recrystallized alumina crucible and inductively melted. Additions were dropped from a glass side-arm. All materials were hydrogen-refined and vacuum-treated to eliminate or minimize the oxygen content. The source and purity of materials is given in Table I. The initial metallic charge was heated to approximately 1000°C and held under vacuum for 30 to 45 min as a means for removing hydrogen and adsorbed gases. Argon was used as the calibrating gas to determine the "hot volume". The average hot volume of the system was approximately 50 cu cm STP and a few experimental runs were made using a reaction bulb with a hot volume of 80 cu cm. The temperature range studied was from 1550° to 1700°C and the temperature was measured optically. THEORETICAL PRINCIPLES General Discussion. Nitrogen dissolves in liquid iron alloys according to the reaction: 1/2N2(g) = N (wt pct in solution) [l] The equilibrium constant, K1, for this reaction is written as:

Jan 1, 1969

By A. B. Kinzel

Precise knowledge regarding the effect of heat treatment on the properties of steel has made possible the detailed specifications and instructions covering optimum heat-treating temperatures and practices that are in current use. A distinct contrast is presented by the metallurgical treatment of steel adjacent to a fusion weld, as such steel is subjected to each temperature from room temperature to fusion temperature, and cooled at a rate that is not generally controllable but is predetermined by the nature of the assembly to be welded, the kind of welding used, and the surrounding conditions. This is true regardless of the type of fusion welding: oxyacetylene, electric arc, thermit or flash resistance. Therefore it seemed desirable to investigate the effect of this metallurgical treatment on the characteristics of carbon steels commonly used for welding, by a detailed study of metal subjected to each temperature range; i.e., each heat-affected zone. Oxyacetylene welding was chosen for the investigation because of the experimental facility of accurately segregating and studying each temperature zone. The nature of the zones produced by other types of welding is the same. The difference is primarily a matter of dimensions of each of the temperature zones involved. The advantages and disadvantages of the extent of the zone are of prime moment, and are discussed after the presentation of the detailed zone study. No mention is made of the fused metal proper, as this has been the subject of much published research and the nature of the solidified metal is fairly .ell known. General Method The scheme of procedure in the work herein reported involved the testing of the metal of each temperature zone adjacent to the weld in so

Jan 1, 1935

By A. B. Kinzel

Precise knowledge regarding the effect of heat treatment on the properties of steel has made possible the detailed specifications and instructions covering optimum heat-treating temperatures and practices that are in current use. A distinct contrast is presented by the metallurgical treatment of steel adjacent to a fusion weld, as such steel is subjected to each temperature from room temperature to fusion temperature, and cooled at a rate that is not generally controllable but is predetermined by the nature of the assembly to be welded, the kind of welding used, and the surrounding conditions. This is true regardless of the type of fusion welding: oxyacetylene, electric arc, thermit or flash resistance. Therefore it seemed desirable to investigate the effect of this metallurgical treatment on the characteristics of carbon steels commonly used for welding, by a detailed study of metal subjected to each temperature range; i.e., each heat-affected zone. Oxyacetylene welding was chosen for the investigation because of the experimental facility of accurately segregating and studying each temperature zone. The nature of the zones produced by other types of welding is the same. The difference is primarily a matter of dimensions of each of the temperature zones involved. The advantages and disadvantages of the extent of the zone are of prime moment, and are discussed after the presentation of the detailed zone study. No mention is made of the fused metal proper, as this has been the subject of much published research and the nature of the solidified metal is fairly .ell known. General Method The scheme of procedure in the work herein reported involved the testing of the metal of each temperature zone adjacent to the weld in so

Jan 1, 1935

By W. P. Saunders, W. R. Hibbard, G. H. Eichelman

Interest in the various products of the austenite eutectoid transformation in iron-carbon alloys, particularly as produced by the isothermal sub-critical techniques introduced by Davenport and Bain,' has resulted in the application of similar heat treatments to other eutectoid transformations. Studies o f the beta copper-aluminum alloy eutectoid transformation revealed microstructures very similar to those found in iron-carbon alloys. Investigations5t6 of the kappa phase in the copper-silicon alloy system have established the eutectoid type transformation of this phase into terminal alpha and intermediate gamma phases. This transformation has been reported5 as forming a eutectoid type structure in a very sluggish manner by a long time isothermal treatment. The purpose of the present investigation is to study the products of the kappa eutectoid transformation as affected by transformation temperatures by means of microscopic and hardness methods. Preparation of Alloys The copper-silicon alloy equilibrium diagram is shown in Fig 1. The kappa field converges to a minimum silicon solubility at the eutectoid composition and all other completely kappa alloys are hypereutec-toid. Thus, kappa decomposition involves first the proeutectoid precipitation of gamma, followed by the eutectoid transformation of a lower silicon content kappa (5.2 pct) Smith6 has indicated that alloys containing between 5.4 and 5.7 pct silicon could be hot rolled, but that the latter composition was desirable in order to permit a wider kappa temperature range. The alloy was prepared by adding Baker's commercially pure silicon to an ingot of copper-silicon alloy containing 2.34 pct silicon remaining from the investigation of Brick, Martin and Angier.' Following the casting techniques of Krynitsky, Saunders and Stern,s the ingot was melted under a heavy layer of dried charcoal in a clay-graphite crucible in a gas-fired pot furnace. Small lumps of silicon were held under thc melt surface with a graphite rod. After the silicon had dissolved, the alloy was chill-cast and then remelted without a cover, stirred thoroughly, skimmed and poured into a preheated cast iron mold. The cast microstructure is shown in Fig 2. The casting, 10 X 4 X K in., was annealed at 750°C for 21 hr and furnace cooled, About }{& in. was milled from all surfaces. The plate was cut in half longitudinally and the bottom half analyzed by A.S.T.M. and The composition by weight was as follows: copper 94.24 pct, silicon 5.56 pct, iron 0.11 pct.

Jan 1, 1949

By J. P. Morris

PREVIOUS investigations1,2 have shown that alloying elements in liquid iron influence the thermodynamic activity of sulphur and thereby affect the partition of sulphur between metal and slag in the desulphurization process. For example, the greater efficiency of desulphurization in the blast furnace as compared to the open hearth can be attributed in part to a higher level of sulphur activity in blast-furnace metal due to the higher concentration of carbon and silicon. In the present investigation, a short study was made of the influence of manganese on the activity of sulphur in liquid iron and iron-carbon alloys. In contrast to carbon and silicon, manganese was found to decrease the activity coefficient of sulphur; and in iron-carbon alloys it counteracts to some extent the influence of carbon. However, at manganese concentrations normally present in the blast furnace or open hearth, the effect of manganese is small. Since manganese sulphide has a limited solubility in iron, manganese can act, under certain conditions as a desulphurizing agent. Considerable data on the manganese-sulphur product in carbon-saturated melts were obtained in the investigation and have been included in this report. The experimental procedure was the same as that used in the earlier investigations on the effect of silicon' and carbon' on sulphur activity. Briefly, the method was as follows: The molten alloy, contained in a graphite or sintered alumina crucible, was brought to equilibrium at a constant temperature with a mixture of hydrogen and hydrogen sulphide of constant composition by bubbling the gas through the metal. Samples of' the melt were taken for analysis at regular intervals by suction through a 2 to 3 mm bore silica tube dipped into the metal. The experiments were run in a graphite spiral resistance furnace with melts weighing 50 to 60 g. The gas bubbling tubes were made of sintered alumina and were 5/16 in. OD, 1/16 in. ID, and 24 in. long. Equilibrium was assumed to have been attained when the sulphur content of the liquid metal reached a constant value. During an experiment there was a rapid loss of manganese from the melt by volatilization. To offset this loss, small additions of manganese were made periodically. The rate of manganese addition needed to maintain a constant manganese concentration was determined in preliminary tests. In all of the experiments, deposits of manganese sulphide formed above the melts in a cooler region of the furnace. Apparently, these deposits resulted from a reaction between manganese vapor and hydrogen sulphide in the gas. To prove that manganese sulphide did not volatilize from the melts to a measurable extent, an experiment was run in which helium was bubbled through liquid iron containing both manganese and sulphur. Although manganese volatilized rapidly in this test, there was no appreciable loss of sulphur. Volatilization of manganese sulphide from a melt would have led to an apparent equilibrium condition in which the sulphur content of the metal was lower than the true equilibrium value. The experimental results are shown in the first seven columns of Table I. The data in the last two columns were obtained from the previous work on the effect of carbon' and show what the results would have been in the absence of manganese but with temperature, gas composition, and carbon content of the metal remaining the same. Comparison of the last four columns show that, in the presence of manganese, the sulphur content of the metal increased at equilibrium and the activity coefficient of sulphur decreased. However, the results show that, for manganese concentrations below 3 pct, the effect of manganese is small. The values for activity coefficient of sulphur given in Table I were calculated from the following relations: S (in liquid metal) + H2 (gas) = H2S (gas) [l] K ph2s/?s X %S X phg = 0.00251 [2] where K is the equilibrium constant for the reaction, PH2S and ph2 are the partial pressures of hydrogen sulphide and hydrogen, respectively, and ?s is the activity coefficient of sulphur. The standard state for sulphur was taken to be a 1 pct solution of sulphur in pure iron. The numerical value for K at 1600°C was determined in the earlier work. For the purpose of showing graphically the results of the tests run at 1600°C, the activity coefficients of sulphur were recalculated so as to correspond to a manganese concentration in the metal of 2 pct in each case. In the calculation it was assumed that the increase in sulphur content of the metal at equilibrium caused by the presence of manganese

Jan 1, 1953

By A. J. McEvily, R. C. Boettner, C. Laird

The processes leading to fatigue failure in the low-cycle range were studied to obtain an understanding of the basis of Coffin's law. Particular attention was paid to the manner of mack nucleation and to the determination of the portion of the total lifetime spent in crack propagation. It was observed that cracks are nucleated at surface notches meated during reversed plastic deformation, Principally at grain boundaries, and that crack growth occupies greater than 75 pct of the fatigue life. When inclusions are present, they are often the primary sites of crack initiation. From consideration of the incremental distances advanced by a crack in each cycle and of the lifetimes of different materials, it appears that the universality of Coffin's law arises from the similarity of crack-tip strain for a given applied strain amplitude, irrespecti7:e of material. STUDIES of low-cycle fatigue have been particularly rewarding in that a simple correlation between fatigue lifetime and plastic-strain range has been shown to exist. This empirical relationship takes the forml,2 Nner=C [1] where N is the number of cycles to failure, Er is the plastic-strain range defined as the total plastic strain per cycle (the sum of the tensile plastic strain plus the compressive plastic strain), n, the exponent, is a constant independent of the material to a first-order approximation and often has a value of about 0.5, and C is a constant which for a number of ductile and metallurgically stable materials is approximately 0.65 for fully reversed strain.3 This relationship has been shown to be valid for a wide variety of metals and alloys and is often referred to as Coffin's law. However, it is yet not clear why so many different metals and alloys exhibit the same over-all behavior in the low-cycle range. Less is known about the mechanisms of fatigue failure in the low-cycle range than in the high-cycle range, but it is expected that the processes would have much in common. For example, an important characteristic common to both high-and low-cycle ranges is that fatigue crack propagation can occupy a considerable portion of the total lifetime. This has been shown by Laird and smith4 by a count of the number of ripples present on the fracture surface of copper specimens, each ripple corresponding to one cycle of load. On the other hand, some marked differences have been noted. For example, in copper,5 nickel, and aluminum4 there is a greater tendency for grain boundary cracking to occur as the strain amplitude is increased. The purpose of the present work was to study further the processes leading to fatigue failure in the low-cycle range and to obtain an understanding of the basis for the validity of Coffin's law. Particular attention has been paid to the manner of crack initiation and to the determination of the portion of total lifetime spent in crack propagation. MATERIALS A number of metals and alloys were tested, although more attention was focused on a particular few, once general trends had become apparent. Alloys were selected so as to investigate the effects of crystal structure, number of phases, stacking-fault energy, and impurity content. The materials in this grouping were: high-purity copper OFHC copper 1100 aluminum (commercially pure) 70-30 brass (Cu-30 wt pct Zn)

Jan 1, 1965

By James Herbert Bartlett

The MANUFACTURE of Iron in the PROVINCE of Quebec. The St. Maurice Forges.—The deposits of iron-ore in the St. Maurice district, in the rear of Three Rivers, were probably known to the Indians and .Jesuits, but it is not till 1667 that any discovery is reported. The affairs of the colony were then in the control of the " West India Company," who amongst other monopolies had a right to all mines and minerals." Specimens of the iron-ore were examined in Quebec. in 1668 by the Sieur la Potardière, who reported unfavorably on them. In 1671, Louis de Buade, Comte de Frontenac, was appointed governor of La Nouvelle France ; and in the original manuscripts relating to his administration some allusion is occasionally found to the St. Maurice iron mines.? In a letter to the Imperial Government, dated 2d November, 1672, he says: "The iron mine of which I have already spoken is of great consequence. I have visited it myself, in order that I may be enabled to give a more accurate account of its nature. I am gratified to learn that another mine has been discovered in Champlain, which is much richer than the Cap de la Madelaine mine, and the ore is in greater

Jan 1, 1886