By J. van der Merwe, D. Tharandt

The corrosion behaviour of 304L stainless steel laser-cladded with various amounts of ruthenium (Ru) was evaluated in solutions of sulphuric acid and sulphuric acid plus sodium chloride at 25°C and 45°C by open-circuit potential and cyclic potentiodynamic polarization tests. In general, the addition of Ru to the stainless steel increased its corrosion resistance in 1 M H2SO4, as well as in 1 M H2SO4 plus 1 wt% NaCl. This was observed for a number of parameters such as corrosion rate, corrosion potential, open-circuit potential, and current density. However, increasing the amount of Ru added beyond a certain level did not result in further improvement in corrosion protection. For each environment there is an optimal Ru concentration for the best corrosion protection. For example, in 1 M H2SO4 at 25°C, 2.44 wt% Ru shows the least active surface in terms of corrosion. Further research into ruthenium coatings on stainless steels is recommended.

Jan 1, 2015

By Rodrigo Perito Cardoso

Low-temperature nitriding of stainless steels is applied to obtain wear resistant surfaces without losing its corrosion resistance. The treatment consists in introducing nitrogen into the steel surface avoiding chromium nitride precipitation. The corrosion resistance of martensitic stainless steels is expected to be improved if the treatment parameters are correctly selected. It can be related to ?Fe2-3N and a'N phase formation on the treated surface. In the present work the influence of the pretreatment and treatment temperature on corrosion resistance of plasma nitrided AISI 420 steel samples is studied. Annealed, as-quenched and 400ºC-tempered samples were nitrided at 300, 350, 400, 450 and 500°C, for 6 h at 600 V. The pressure was 3 Torr and the gas mixture was composed of 70%N2, 20%H2 and 10%Ar, at a gas flow rate of 3.34×106 Nm3s-1. Plasma was generated using a square-wave pulsed DC power supply and the sample temperature was controlled by the duty cycle. The modified layers were characterized by optical microscopy, X-ray diffraction and microhardness measurement. The corrosion resistance was studied by electrochemical characterization, by means of Open circuit potential and Anodic polarization curves. The maximum surface hardness was achieved at 400°C. This temperature seems to be near the limit temperature for low-temperature treatment aiming to improve or at least to keep unaltered the corrosion resistance in relation to that verified for non-treated steel samples. Results confirm that the pretreatment and treatment temperature significantly affects the corrosion resistance of the treated surface.

Aug 8, 2018

By E. A. G. Colls

Discusses corrosion in Trail chemical plants producing ammonia, sulphuric, nitric and phosphoric acids, ammonium phosphates, sulphate and nitrate, together with miscellaneous allied material problems and their solution using erosion or corrosion proof materials. Conclusion, that for work of this nature, most costly material may well be cheapest in the long run.

Jan 4, 1950

By L. Cáceres, G. Leinenweber, P. Bustamante

"Given the severe scarcity of fresh water sources in Northern Chile the use of seawater has become the only alternative to allow mining expansion. This option however poses several technological challenges as a result of the high concentration of natural salts that promote various forms of metal corrosion. Therefore the steel piping protection has been a constant challenge for design engineers responsible for solving the problems of corrosion. Known protection alternatives are varied and expensive, a few of them are rubber coatings, protection based centrifuged concrete, extra wall thickness of pipes in combination with corrosion inhibitors, extra wall thickness of pipes without using corrosion inhibitors, and the use of highly corrosion resistant steel materials.In this framework the aim was to study the corrosion kinetics of carbon steel pipe API 5L X70 under electrochemical and weight loss testing. The test conditions include a range of seawater velocities between 0.2 to 3.0 m/s.For electrochemical experiments the API 5L X70 steel specimen was a 4 mm diameter disk embedded in an 8 mm diameter Teflon rod and exposed to seawater. Duplicated coupons were placed in a standard test apparatus that was built according to the standard ASTM D 2688 – 94.The main results were: a) corrosion mechanism explained in terms of the counterparts partial processes which are the hydrogen evolution and oxygen reduction reaction; b) for the test specimen a corrosion band like feature that suggest a lateral dispersion of aggressive solutions from corrosion pits; c) a range of corrosion rates between 1 and 1.96 mm/year for flow rates between 0.2 and 3.0 m/s; and d) a convenient inhibitor dose between 20–25 mg/L for optimum inhibition efficiency to obtain a maximum value of 80% for corrosion efficiency."

Jan 1, 2016

By A. -M. Lafront

The corrosion resistance of die-cast and freely-solidified and electromagnetically-stirred thixocast AZ91D alloy has been studied using electrochemical noise technique in a 0.05M NaCI solution at pH 6.1 and 25°C. Specimens polished at different depths were immersed for a period of 75 min in order to assess the influence of the microstructure on corrosion kinetics and morphology. At depths between 10 and 50 µm (skin), all specimens showed general non-uniform corrosion with the lowest corrosion resistance. Between 100 and 200 µmn (interior skin), the observed corrosion was accompanied by superficial undefined pits due to metastable pitting. The corrosion form for 100-200 µm gave the best corrosion resistance. Stable pitting corrosion was observed beyond 400 µm deep on the bulk specimens. The skin of all thixocast specimens prepared billets showed a more corroded surface than that of die-cast. The interior skin as well as the bulk specimens showed better performance than that of the die-cast specimens.

Jan 1, 2007

By R. F. Lynch, F. E. Goodwin, A. F. Skenazi

"The Gal/an alloy has been developed for continuous galvanizing of steel. The choice of the eutectic zinc-aluminum alloy with addition of misch metal gives a coating with specific characteristics as far as structure, analysis, surface chemistry and surface morphology are concerned. The performance of the uncoated Galfan coating is superior when compared to conventional galvanized particularly for corrosion resistance and ductility. For coil coating applications, these two assets are of the utmost importance but in order to benefit from these two advantages, good paint adherence and high resistance to edge creep and blistering have to be obtained. Despite Galfan's unique features compared to other zinc based or aluminum zinc based coatings, existing pretreatments and painting conditions are used with only minor modifications in order to assure good adherence and edge creep resistance. With compatible processing, Galfan can outperform galvanized and Galvalume as a substrate for coil coating as is demonstrated with various test results.IntroductionThe technical and commercial development of Galfan, a 95% zinc-5% aluminum-0.1% lanthanum-cerium hot-dip coating for steel, has been rapid. From its identification as a promising coating in late 1980, it has evolved from a research product to a fully commercial product with over 100 000 metric tons of coated sheet produced to date, and another 90 000 tons, at minimum, scheduled for 1986. The great majority of tonnage produced to date has been coil coated for use in building panel , appliance, and similar applications. Much technical work has been done to determine the suitability of Galfan for these applications and the proper way of processing sheet for best results. The present state of knowledge is discussed in this paper, along with some recent applications which are given asexamples"

Jan 1, 1987

By M. D. Crites

As part of a multi-year program for assessing the viability of chrome-free refractories in copper smelting, converting and refining furnaces, dynamic corrosion tests have been conducted on a series of refractories from the magnesia-alumina system, using a ferrous silicate slag. The corrosion rates of the test refractories are compared with those of a reference mag-chrome brick, and recommendations are made for more in-depth evaluations of the more corrosion-resistant materials.

Jan 1, 1999

By John L. Hatton

The author will introduce and describe the nature of Fiberglas-Reinforced Plastics. Successful applications of corrosion-resistant structures will be shown and described, including pipe, ducts, tanks and other equipment. These structures are generally designed to handle corrosive liquids and gases and have proved both satisfactory and economical in service in various industries in Canada. The specification of structures will be discussed in relation to materials, construction and workmanship, physical properties and methods of testing.

Jan 1, 1970

By P. -Q. Wu

A modified electrochemical noise (EN) technique has been applied to monitor corrosion wear of TiN-coated ASP23 steel and TiN-coated AISI 316 stainless steel sliding against corundum in 0.5 M H2SO4. Experimental results show that the EN technique can sensitively detect potential and current variations during a corrosion-wear process. Corrosion-wear mechanisms of TiN coatings depend on their substrate properties. If the substrate is passive, such as AISI 316 stainless steel, the potential and current variations reflect the properties of the coating. Depassivation and repassivation alternately take place on the tribo-activated wear area during the steady-state phase. If the substrate is active, such as ASP23 tool steel, the electrochemical noise is dominated by dissolution of the substrate at the pinholes and the hydrogen evolution all over the exposed surface.

Jan 1, 2005

By S. H. Ash

NINE-TENTHS of the total anthracite deposits of North America are in Pennsylvania. Corrosion of pumping equipment by acid mine waters has been experienced at tremendous cost by mining companies in the anthracite region of Pennsylvania, for many years in many ways. The design and specifications of the large centrifugal pumps as provided in the proposed mine-drainage system (7-35, 45, 46, 48, 54, 64, 70, 71)° make it imperative that a metal or alloy be recommended that has the highest corrosion resistance and, at the same time, acceptable properties suitable for general workability (welding and machining). This report presents data on the corrosive and erosive effects of acid mine waters in the anthracite region on metals and alloys for pumping equipment and drainage facilities necessary to remove or control this water.

Jan 1, 1955

By K. A. Natarajan

The relative significance of corrosive and erosive wear in magnetic taconite grinding is examined. The influence of different types of aeration, namely, nitrogen, air and oxygen on ball war was established for mild steel and high carbon low alloy steel balls. Ball wear data from dry and wet grinding tests are compared with those obtained in the presence of an organic solvent that does not promote electrochemical corrosion. 'Marked ball grinding, tests along with electrochemical measurements involving ball material and magnetite electrodes indicate that contribution from oxygen towards wear (corrosive wear) is relatively small and abrasive wear appears to be significant. Rheological properties of the slurry-appear to have an important bearing on the abrasive wear of grinding balls.

Jan 1, 1983

By K. A. Natarajan, S. C. Riemer, I. Iwasaki

The relative significance of corrosive and erosive wear in magnetic taconite grinding is examined. The influence of different types of aeration (nitrogen, air, and oxygen) on ball wear was established for mild steel and high carbon low alloy steel balls. Ball wear data from dry and wet grinding tests are compared with those obtained in the presence of an organic solvent that does not promote electrochemical corrosion. Marked ball grinding tests and electrochemical measurements involving ball material and magnetite electrodes indicate that contribution from oxygen toward wear (corrosive wear) is relatively small, and abrasive wear appears to be significant. Rheological properties of the slurry appear to have an important bearing on the abrasive wear of grinding balls.

Jan 1, 1985

By Dr. G. R. Hoey

"Abrasive wear and corrosive wear of carbon-steel grinding balls occurred simultaneously during the wet-grinding of hematite iron ore, and Ni-Cu sulphide ore, in laboratory ball mills. Two corrosion control methods, the use of corrosion inhibitors and pH control, were investigated and found to be effective means of reducing or preventing corrosive wear. Up to 50 % reduction of total ball wear resulted from the use of these methods.Corrosive wear is caused principally by the reaction of oxygen in air with the carbon-steel grinding balls, probably by the following reaction: 2Fe + O2 + 2H20 - 2Fe2 + 40H-.IntroductionA survey of corrosion problems in Canadian sulphide ore mines was completed and the findings were published in 197l(l). The corrosion survey was used to develop the present research program with the objective to find more economical and effective ways and means to reduce the corrosion that occurs in the mining and metallurgical industry. The purpose of this presentation is to review the projects being done by staff members of the Corrosion Section, Extraction Metallurgy Division, on corrosive wear and its control in wet-grind ball mills.Both abrasion and corrosion contribute to metal consumption during wet grinding of ores. The total wear of grinding media in this study is assumed to be equal to the sum of corrosive wear and abrasive wear. A great deal of research and development has been reported in the literature on ways to improve the abrasion resistance of grinding media but only a small number of studies has been reported on the corrosion resistance of conventional grinding media."

Jan 1, 1974

By Freeman C, Dingley W

Addition of sodium nitrite-borax, sodium hydroxide, sodIUm carbonate, lime, or sodium silicate reduced wear of forged steel balls and cast iron slugs in wet grinding a complex zinc-lead-copper sulphide ore in laboratory ball mills. Maximum wear reductions were 27 per cent (forged steel balls) and 33 per cent (cast iron slugs) with sodium hydroxide and nitrite-borax additives respectively.Potential measurements of balls and slugs during grinding, and analysis of the data in terms of corrosion theory demonstrated that corrosive wear had been reduced or prevented by these additives. Actual per cent wear reductions were not equated to the rate of corrosive wear because of the undefined interdependence between abrasion and corrosion in wear processes. The investigation verifies that in laboratory ball mills corrosion is significant in the wear of grinding media and wear can be reduced by corrosion inhibition and pH adjustment.

Jan 1, 1978

By Shane Andrews, Gustavo Vasquez, S. K. Varma

"The effect of solutionizing time on the corrosive wear behavior of 2014 aluminum alloy has been studied using the impact and continuous mode of scratching techniques. The transient currents (TC) evolved during the scratching of the alloy shows a linear dependence between the TC and the solutionizing time. Higher TC values at longer solutionizing time may be associated with the changes in the concentration of quenched-in vacancies, grain sizes and dislocations generated during scratching. These factors can either create (a) anodic sites or (b) pitting corrosion resulting in the generation of transient currents. The results have been compared with the similar study carried out for 6061 aluminum alloys. This 6061 aluminum alloy shows similar behavior but the rate of TC generation per unit solutionizing time is much lower than 2014 aluminum alloy. The morphological changes in the impact scratches and the TEM investigation in the scratch have been presented in this paper.IntroductionThe technique of studying corrosive wear of composites of 6061 aluminum in the monolithic and reinforced forms has been reported in the literature [1]. Two modes of scratching, consisting of impact and continuous, in a corrosive environment indicate that the composites, containing 0.10 and 0.20 volume fractions of alumina particles (VFAP), have higher corrosive wear rates than the monolith. A graph between the transient current (TC) generated during the impact scratching as a function of solutionizing time at 540°C indicates linear relationship between them. A similar slopes for the composites were observed and the TC values were less for the composite containing lesser VFAP."

Jan 1, 1998

By Raphael França Assumpção

O aço inoxidável duplex (AID) vem sendo considerado uma excelente alternativa para aplicações que requerem alta resistência à corrosão e alta resistência mecânica. Portanto, a microestrutura e as propriedades dos aços dúplex permanecem como temas de grande interesse. Para este proposito, estudou-se o efeito da laminação a morno em um aço inoxidável duplex. O foco deste trabalho foi o AID 2205 que é um dos tipos mais comuns de AID. O objetivo deste estudo é avaliar o comportamento eletroquímico do AID 2205 laminado a morno no ambiente de íons de cloretos utilizando medidas de polarização potenciodinâmica. O aço inoxidável dúplex foi laminado a morno à 600°C para 60 e 80% de redução na espessura e submetido a testes eletroquímicos. As amostras apresentaram uma excelente resistência à corrosão em solução de NaCl 3,5%. Apesar da existência de certa similaridade entre os valores de potencial de circuito aberto e potenciais de pites obtidos para todas as amostras, o número de pites observado foi maior na amostra CF, seguida pelas amostras com 60 e 80% de redução.

Oct 30, 2017

By Benjamin A. Allou

La seule production de columbo-tantalite réalisée en Côte d?Ivoire est effectuée dans les éluvions et alluvions du gisement d?Issia, localisé au Centre- Ouest de la Côte d?Ivoire. Même si un lien direct avec les roches granitiques est suspecté, aucune attention particulière n?a été accordée à l?étude de la minéralisation primaire en relation avec l?évolution des granites et des pegmatites associées. Ces granites, qui sont en intrusion dans les roches sédimentaires du Protérozoïque inférieur, comprennent : le granite orienté à deux micas (Lobo), le granite orienté à muscovite dominante (Bitapia) et le granite porphyroïde non orienté à muscovite dominante (Issia). Les résultats de cette étude indiquent que les pegmatites à Nb-Ta-Be-Li sont liées au granite de type Issia. Les observations de terrain et les analyses sur roche totale des granites montrent que: (1) les trois principaux granites de la région sont de type- S et peralumineux dans leur composition, (2) ils ont été formés pendant la période tardi- à post-Éburnéenne, (3) le granite d?Issia fut le dernier à se mettre en place. Les pegmatites liées au granite d?Issia ont été classées en quatre types : Apegmatites stériles; B- pegmatites à Be; C- pegmatites zonées à Nb-Ta-Be; et Dpegmatites zonées à Be-Nb-Ta-Li. Les pegmatites zonées comprennent les zones suivantes: I- zone à aplite; II- zone graphique; III- zone à albite, microcline, béryl et columbo-tantalite; IV - zone à microcline massive; V- zone à quartz. Ces pegmatites présentent une zone d?altération métasomatique externe. La minéralisation de Ta, Nb et Be est liées à la zone III des pegmatites de types C et D, et celle de Li est associée aux greisens qui peuvent être observés n?importe où dans les pegmatites de type D. Les données de terrain et de laboratoire indiquent que le granite d?Issia est la roche parentale des pegmatites à éléments rares de la région. Les pegmatites minéralisées sont distribuées seulement autour du granite d?Issia et les patrons des terres rares des granites et ceux des pegmatites à éléments rares sont très similaires. Les analyses de la composition totale montrent un lien génétique entre le granite d?Issia et les pegmatites à éléments rares. Il est suggéré que les pegmatites ont été formées durant le transport et la cristallisation fractionnée du magma.

May 1, 2003

By Bill Birch, Toby White, Ian Brown

costs/benefits of electronic detonators and measure their effects on primary crusher productivity. 9 blasts (3 shock tube blasts, 6 electronic blasts). Measured electricity consumption & primary crusher throughput. Change to Electronic Detonators resulted in a 7% reduction in primary electricity costs and a 15% increase in primary crusher productivity.

Feb 1, 2020

By J. A. Bullington

Mr. Chairman and Gentlemen: Some of you men may know who are familiar with what we have been doing in the C. F. & I. the last three years, that we have revamped our entire method of cost accounting from the pit bosses' report through to the final report of the president. The basic ideas involved in our cost system are not ours. They were given us by one of the best management and industrial engineering concerns in the country-at least they have that reputation. All I can do now is to try to pass on to you some of the ideas we have from various sources and the methods we have used in teaching those ideas to our coal men on cost accounting. This will not be a technical paper. I tried to put it in language we could all understand, and I hope I will be talking the same language that you gentlemen talk when you think about the cost of your coal in your own mines. Accounting of all kinds is classed as overhead expense, and as overhead expense we must justify its cost by the service it gives the rest of the organization. That brings us up to the problem of making the cost department pay its own way, just the same as the power plant has to pay its own way, and we have gotten away from the old idea of cost accounting in that it is sufficient within itself. The cost sheets are only so good as they enable the operating man to reduce his costs. The cost sheets are only just so much work for the cost department, and if they do not help the operating man to control his costs, we figure that is so much work wasted. The cost department works for the operating department.

Jan 1, 1931

By P. K. Chatterjee, G. D. Just

Sublevel open stoping is a low-cost method that has been successfully employed in many large underground mining operations. Where ore body characteristics are suitable, extensive mechanization and the use of large-scale stoping techniques can considerably reduce operating costs. However, careful long-term planning of mine layouts and large capital commitments in development are required prior to production. Implementing precise mine design procedures and carefully controlling operations can result in considerable benefits. This article describes methods to achieve these objectives based largely on mining operations at Mount Isa, where sublevel open stoping has been used since 1932. Ore won by this method accounted for a very large percentage of the total tonnage produced at Mount Isa. Major costs associated with sublevel open stoping can be classified as drilling, explosives and charging, and LHD costs. In this article, analyses of these costs are made with particular reference to stope design. Parameters such as burden, drill hole diameter, explosive density, specific charge, etc., are considered in establishing the interrelationship of unit operating costs, as well as total costs of sublevel open stoping.

Jan 10, 1981