By Huang Kai

By adding the solid oxalate acid powder into the solution of nickel chloride or its ammonia coordinated solution, the uniform compound particles were prepared and the precipitated particles were transferred to the mono-dispersed NiO particles by calcination. In this study, the various experimental conditions were investigated, the characteristics of the corresponding obtained particles were analyzed, and the formation mechanism of the particles was elucidated. It was found that the solid oxalate acid provided the solid-solution interface for the precipitation and induced the nucleation and growth of the product particles.

Jan 1, 2005

By M. Kargar Razi

According to the unique properties and many applications of nano silver powder, it was prepared from acid leaching tail solution. The low value residual gold and silver ions were occurred with fellow heavy metals as pollutants (Fe2+, Cu 2+and Zn2+) in acid leaching tail solution in Mouteh gold mine in Iran. Preparation of nano silver particles was achieved in two steps: first, by addition of ammonia as separation step and second by using different reagents as precipitation and extraction steps. Different controlled parameters were including pH, residence time and temperature, mixing time, and reducing reagents to metals molar ratio. Acid leaching process was carried out with sulphuric and nitric acid via suitable reductants. In order to remove copper, zinc, and silver ions from solution, all of the conditions were controlled. The optimum conditions for preparation of nano silver powder with less than 90 nm were pH 10.5, hydrazine/methanol to silver molar ratio of 3 to 4, and reduction time of 5 min in 45 °C. The results were evaluated via SEM, A.A and UV- Vis spectroscopy analytical methods.

Jan 1, 2014

By J. -S. Park, H. -S. Jeon

This study has been carried out to develop a relatively simple hydrometallurgical process for recovering nickel as nickel sulfate from the spent nickel-cadmium battery residue in which cadmium was removed by vacuum distillation. This residue is composed of 36 % nickel, 20 % iron, and other metals such as cobalt. First, crushing and selective classification were performed to separate iron to produce a nickel-rich product (over 40 % nickel). This product was dissolved in sulfuric acid to obtain a nickel sulfate solution. During the dissolution, nitric acid and air were added to the system to enhance the iron oxidation reaction rate. The free acid remaining in the dissolved solution was neutralized by adding nickel carbonate. Iron was precipitated as iron hydroxide and removed from the solution. The nickel sulfate solution was then fed to a vacuum evaporator to concentrate the solution by evaporation of water and crystallized at around 45°C to obtain nickel sulfate hexahydrate. A recrystallization process could remove other impurities such as zinc and manganese.

Jan 1, 2000

Discussion of the paper of S. E. Bretherton, presented at the Butte meeting, August, 1913, and printed in Bulletin No. 80, August, 1913, pp. 1481 to 1487. S. E., BRETHERTON, San Francisco, Cal.:-Since preparing my paper, our chemist, F. L. Wilson, has been experimenting with Leadville, Colo., oxidized zinc ore and Leadville zinc sulphides containing lead, operating upon 40-1b. lots at a time. His results on Leadville sulphides are as follows: The raw ore contained a trace of gold, 5.04 oz. of silver, 19.1 per cent of zinc, and 7.24 per cent of lead. After roasting the ore contained a trace of gold, 5.72 oz. of silver, 0.75 per cent of copper, 21.7 per cent of zinc, and 8.29 per cent of lead. The loss in weight by leaching was 38.8 per cent. The extraction was 42.8 per cent of the copper, 80.6 per cent of the zinc, 7.1 per cent of the lead, 0.64 per cent of the silver, and no gold. The little .silver that is extracted would be thrown down with the copper when precipitating it from the zinc and both thrown hack into the residue to be smelted. There would be no trouble in smelting the residue with nearly all the sulphur eliminated and containing less than 7 per cent. of zinc. On zinc carbonates containing silicates the results are not satisfactory. H. O. HOFMAN, Boston, Mass. (communication to the Secretary*) :¬The paper by Mr. Bretherton upon the application of ammonia and carbonic acid to the recovery of zinc as oxide from roasted sulphide ore is of interest to me, as the first installation of the Schnabel process for the extraction of zinc from a mixture of zinc oxide, lead oxide (with some cupric oxide), and pellets of enriched lead, produced in steaming liquated zinc-silver-lead crust of the Parkes process, was made at Lautenthal, Harz mountains, where I was chemist. In that capacity I carried out numerous experiments on the Schnabel process, was active in the erecting of the plant, and later had charge of it. After the Lautenthal plant had been in operation for some time a similar one was built at Hoboken-les-Anvers, but both have been abandoned, as the wet process could not compete with the distillation of the liquated zinc-silver-lead crust, now used universally in the Parkes process.

Jan 11, 1913

By Y. X. Yang

Porous silica was obtained by acid leaching of chrysotile. The porous silica had been characterized by chemical analysis, powder X-ray diffraction (XRD), Fourier transform infrared spectros-copy (FT-IR), and N2 adsorption-desorption techniques. It is shown in this study that the porous silica retains the nanofibrous morphology of the original chrysotile, and produces a high specific surface area (SBET) of 391. 8 m2/g and total pore volume of 1. 05 mL/g. The increase in SBET and the total pore volume of the porous silica reflect the formation of micropores of 1.2~1.5nm and meso-pores of 3.2~3.8nm in diameter inside the porous structure. The hysteresis loop of N2 adsorption-desorption curve indicates mainly slit-shaped pores. The porous silica is amorphous, but its structure is regular to some extent. The structural unit of silica from chrysotile is a SiO4 tetrahedron and six-member silicon-oxygen rings with the tetrahedral positioned alternately up and down in the six-member rings.

Jan 1, 2014

By Guomin Jiang

Potassium ferrate is an excellent multifunctional reagent for wastewater treatment, but its preparation is crucial. The improved hypochlorite oxidation method was used to prepare potassium ferrate in this study. Iron nitrate, the preferred iron source, was added into hypochlorite solution and then the stabilization agent was added during the purification process of product. The influence of available chlorine content, iron molecular proportion, reaction temperature and reaction time on potassium ferrate preparation was investigated. The optimal condition for potassium ferrate preparation is 15% of available chlorine content , 0.6 of iron molecular proportion , 30i of reaction temperature , 45min of reaction time. The yield of potassium ferrate is about 67% with high purity (> 99%). The structure and performances of the product was characterized by XRD, EDX, SEM, TG and IR and the results show that the prepared product is consistent with the properties of potassium ferrate(VI).

Jan 1, 2010

By Ahmed M. Yousif, Walid M. Abdellah, Galal M. Abdel Wahab, Amal E. Mubark

The present work is concerned with selective dissolution of niobium from Gabal El Faliq concentrate sample by using fluoridefree process. The chemical analysis of concentrate sample revealed the presence of high amount of ZrO2, Nb2O5, Re2O3, and HfO2 assaying 33.6, 1.99, 4.8, and 1.2%w/w respectively. Several economic minerals including zircon, samarskite, fergusonite, and xenotimewere recorded in the studied sample. About 98%of Nb content was selectively dissolved at the optimumconditions of 1:2 concentrate sample: KOH weight ratio, 2.5 h fusion time, and fusion temperature of 550 °C. Organic solvent extraction process using Aliquat 336S in xylene was effectively used for preparing pure Nb2O5 (98.95%).

Oct 22, 2019

By Hyung Sup Choi

The preparation of high-purity zirconyl compounds was studied in order to develop an economical process for obtaining pure zirconium via the caustic fritting of zircon sand. The direct dissolution of caustic frits with concentrated hydrochloric or nitric acid at 80c. followed by the addition of a small amount of acidified gelatin, gave high-purity zirconyl chloride or nitrate. The addition of a small amount of gelatin caused a mutual flocculation between colloidal silica and gelatin. The precipitation of this silica floc markedly lowered the content of silica in the product. The silica content of the compounds (or solution) so produced, generally less than 100 ppm., was sufficiently low for tributyl phosphate extraction for nitrate solutions. It was found that the degree of purification de-pends not only on the procedures employed but also on the nature of the frit itself. Silica was more effectively eliminated from the fritted product produced at higher temperatures, and less silica was present in the com-pound prepared from the frit produced in a shorter heating time. In order to ascertain the nature of the

Jan 1, 1965

By Yuanbo Zhang, Mingjun Rao, Weiguang Tian, Huimin Tang, Guanghui Li, Lei Ye, Guoshen Liang, Zhiwei Peng, Foquan Gu, Tao Jiang

The amount of slag produced from a typical ferronickel smelting pro- cess is 4 to 6 times that of the metal product, and handling this slag is a huge challenge to the ferronickel industry. The feasibility of a technological route for preparing refractory materials from a ferronickel slag was verified in this study. Based on the thermodynamics analysis, the effect of the sintering temperature on the properties of refractory material from the slag was studied in the presence of magnesia. The results of thermodynamics calculation showed that the reaction of MgO with SiO generated forsterite and enstatite, whereas the reaction between 2 MgO and Fe O /Al O produced corresponding magnesia spinels. The experi- 2 3 2 3 mental results showed that a refractory material with refractoriness of 1580 °C, bulk density of 2.88 g/cm3, compressive strength of 106.9 MPa, and apparent porosityof 5.8%was obtained under the conditions ofmagnesia addition of 15 wt %, sintering temperature of 1350 °C and sintering time of 3 h. With increasing sintering temperature, the bulk density and the compressive strength of refractory material increased but the apparent porosity decreased, mainly attributed to the formation of the liquid phase which promoted the densification of the refractory material. (cid:1) (cid:1) (cid:1)

Mar 1, 2018

By Mei Yang, Wei Gao, Jian Yang, Qingcai Liu, Wenchang Xi

"TiO2 has been loaded on cordierite porous ceramic to prepare the SCR catalyst carrier by using both APCVD and sol-gel technology. In APCVD method, TiC14 and O 2 were used as reaction precursor. TiC14 was gasified by using N2 as carrier gas which was controlled to 500sccm. Its reaction temperature and reaction time were limited to 773K and 30min respectively. The physical properties, SEM and SEM-EDX of the TiO2-cordierite carrier and the properties of SCR catalysts prepared by these carriers have been tested. The tests showed that TiO2 loaded by APCVD method were of graininess shape and even accumulation. The loading rate of TiO2 and the specific area of carrier sample were increased 114% and 21 % respectively comparing with sol-gel technology. In the result of sol-gel method, the maximal difference of Ti content was 66.92%, while the result of APCVD method was 18.89%. It demonstrated that TiO2 was uniformly attached with the cordierite ceramic by using APCVD method, which would ensure more active ingredients well loaded on the Ti02-cordierite carrier. This difference made the denitrification ratio of catalyst prepared by APCVD method was 8.1 % higher than that of catalyst prepared by sol-gel method.IntroductionIn recent years, the emission of NOx, which were caused by coal-fired power plants, has gotten more and more attention. SCR (selective catalytic reduction) is the most effective technology to DeNOx [ll. The core technology of it is the catalyst. The SCR catalyst usually uses Ti02 as the carrier, and V2O 5 as the active component [2, 3] . However, the thermal stability and mechanical properties of TiO2 carrier are unstable, which would influence the performances of the catalyst. The commercial catalyst generally uses WO3 or MoO3 to promote its heat stability at present [4-7] Besides, TiO2 is expensive. Compared with TiO2, the cordierite is of good thermal stability and lower price. So loading Ti02 on cordierite porous ceramic as carrier to produce SCR catalyst is of good prospects [S, 91 • Currently, TiO2 is usually loaded on cordierite by the sol-gel method. But some research has shown that the sol-gel method easily reduced the loading performances of TiO2, such as distribution, combination, etc. APCVD (atmospheric pressure chemical vapor deposition) has many advantages to preparing TiO2 films, such as high bonding strength, fast reaction rate and so on [l0-13l_ In this paper, TiO2 has been loaded on cordierite porous ceramic to prepare the SCR catalyst carrier by using both APCVD and sol-gel methods. The properties of the carriers prepared by the two processes have also been compared."

Jan 1, 2011

By Xianjun Lyu, Junxiang Wang, Peng Wu, Minjie Lian

"In recent years, the efficient cementation of mine tailings is a new way to manage mine solid wastes. The traditional cement materials have a slow setting time, large dosage and poor cementation strength for fine aggregate such as mine tailings. Therefore, the preparation of new type cementitious materials for the cementation of fine tailings has great potential in the treatment of mine waste solids. The paper mainly focuses on exploring the critical factors affecting the cementing performance of granulated blast furnace slag and its performance in the cementation of fine aggregate. Results indicate that the fineness of slag has a significant effect on its cementitious activity and Portland cement clinker has a better stimulation effect on the cementitious properties of slag than lime. And, anhydrite has a better early stimulation effect on the cementitious properties of alkali-activated slag compared to semi-hydrated gypsum and dihydrate gypsum. According to a series of tests on the cementation of fine iron tailings, the optimal ratio of slag, Portland cement clinker and anhydrite is determined as 60:30:10. Compared with P.O 42.5 ordinary Portland cement, the new slag based cementitious material shows much better cementing performance on fine tailings sample. Under the dosage of 12%, the compressive strength of fine tailings mortar using slag-based cementitious material in 3 curing days is increased to 168% that of using P.O 42.5 ordinary Portland cement, while the compressive strength in 28 days curing period is increased to 194%."

Jan 1, 2018

Sm-Co alloy is a kind of magnetic material with high power and has been applied in modern industry widely. In this study, the wet chemical co-precipitation was developed for synthesis of the Sm-Co alloy oxide precursor. The thermodynamic analysis of the studied system was done to clarify the solution behavior theoretically based on the thermodynamic equilibrium and simultaneous equilibrium. Then, the experiments were done to address the various effects on the wet chemical process, including solution pH, reactant concentration, dispersant, reaction temperature and time, etc. It is found that by precise control of the process, the Sm-Co alloy oxide precursor was synthesized with fine crystallization and special size & size distribution.

Jan 1, 2005

In this study, the method of chemical co-precipitation?reduction?diffusion was developed for the preparation of magnetic SmCo5 alloy. In the chemical co-precipitation process, the effects of solution pH, the reactant concentration, the dispersant on the process were investigated. The optimum conditions of the process were determined, and the SmCo5 alloy oxide precursor particles with fine crystalline structure, narrow size distribution was obtained. Then, by reduction-diffusion treatment of the precursor particles, the SmCo5 alloy with high quality was produced. It is anticipated that the co-precipitation-reduction-diffusion is a novel method available for SmCo5 alloy production.

Jan 1, 2006

By Sheng-hai Yang

The ultrafine, monodispersed, spherical cobalt powder has been fabricated by reducing cobalt hydroxide with glycol. It were investigated that the effect of NaOH concentration on the reaction rate and the effects of the concentration of cobalt hydroxide and surfactant on the morphology and particle size. The particles were characterized by the X-ray diffraction(XRD), scanning electron microscope(SEM), laser diffraction particle size analyzer and BET specific surface analyzer respectively. The XRD shows that the cobalt powders exist mostly in face centered cubic (fcc) structure, a little in simple hexagonal. The cobalt powders prepared at Co(OH)2150g/L, NaOH 40 g/L and surfactant 30g/L, its average particle size, specific surface area and cobalt content, were 0.88µm, 2.705m2/g. and more than 99.5% respectively.

Jan 1, 2006

By Xuling Chen, Zhiyun Ji, Min Gan, Tao Jiang, Liang Yin, Xiaohui Fan

Straw char exhibited considerably faster burning speed than coke breeze for its porosity, which significantly degraded sinter quality when it replacing coke breeze as sintering fuel. In this investigation, preforming technology has been employed to densify raw straw. The properties of straw char preformed show that its density was increased, and the structure was also densified, which made the difference of combustibility between the straw char and coke breeze smaller. The proper preforming temperature, residence time and pressure were 200℃, 1min and 120MPa respectively. Sinter pot trials show that the product carbonized from preformed straw made the proper replacement ratio to coke breeze increase from 20% to 40%, and the emission reduction of SOx, NOx in flue gas increase from 11.50%, 14.15% to 37.85%, 23.60% respectively, compared with non-preformed straw char.

Jan 1, 2015

By Huimin Lu, Zhijiang Gao

Reduction reaction can happen among Al, V2O5 and TiO2 powders. Al can deoxidize metal V and Ti from the metal oxides. The electric igniter can be used to trigger the reduction. The reaction between Al and V2O5 is very intense and release large amounts of heat, but the heat which is needed to initiate the reaction between Al and TiO2 is not enough. These two reactions have been initiated first and V-Al and Ti-Al alloys can be obtained with a higher metal recovery percent. Through adjusting the ratio of Al, V2O5 and TiO2 powders, the system which combines these two reactions can ensured enough heat to react. KClO3 is added to the system, as the ignition agent, in order to make the reaction much complete. Finally, Ti-Al-V alloys can be obtained and need remelt to adjust the constituents.

Jan 1, 2016

By Fangqing Yin, Qingyu Deng, Zhengfeng Qu, Mengjun Hu, Meilong Hu

Titanium bearing blast furnace slag, which contains 20%-30% TiO2, is a valuable secondary titanium resource. Based on the thermodynamics calculation effect of the temperature on the reduction of the slag in vacuum were studied at certain vacuum degrees. The results show that magnesium vapor and silicon monoxide vapor can be obtained at the condition of high temperature and low pressure. The purity of TiC increases with temperature increasing. When the temperature arrives at 1623K TiC can be obtained besides the reductant carbon. XRD result of the powder collected from the furnace cover show that magnesium and silicon in the titanium bearing BF slag leave the slag system during carbothermal reduction in vacuum. From the above it can be concluded that TiC can be obtained from the titanium bearing BF slag and silicon and titanium in the slag can be separated by carbothermal reduction in vacuum and acid leaching.

Jan 1, 2016

By Run Huang, Xuewei Lv, Songli Liu, Chenguang Bai

"Titanium alloy was prepared from titania-bearing blast furnace slag (Ti-BF slag) by aluminothermic process in an induction furnace. The effects of aluminum amount on the titanium silicon yield and titanium recovery ratio were studied. The phase transformation and chemical composition of the prepared alloy were investigated by X-ray diffractometry (XRD) and X-ray fluorescence (XRF) respectively. It was found that the mass fraction of silicon and aluminum increased with increasing the aluminum amount, however, the mass fraction of titanium increased first and then decreased with increasing the aluminum amount. Furthermore, both the titanium alloy yield and titanium recovery ratio increased with the increase of aluminum amount. The main phases of the alloy were TixSiy and AlTi3. The titanium alloy samples prepared in various conditions had a composition (wt.%): 38–50% Ti, 29-34% Si, 4-11 Al%, 1.6-2.2 Mn%.IntroductionPanzhihua and Xichang regions in the southwest of China are rich in vanadium-titanium magnetite containing iron, vanadium, titanium and gangue. According to the characteristics of the resource, iron and vanadium are successfully recovered with a blast furnace process and a converter process. However, most content of titanium are entered in the blast furnace slag with TiO2 22% -26% and metallic Fe 2%–6% called Ti-BF slag. Due to the dispersed distribution of Ti in various fine grained mineral phases with a complex combination between Ca, Al and Si, it is difficult to recover the Ti components[1]. This slag is generated at a current rate of 3.6 million tons per year, which adds to the existing 70 million tons of slag produced so far[2]. The slag has had to be piled as large as the mountains, which not only waste of resources but also cause a pollution of the environment. Therefore, the study of integrated utilizing Ti-BF slag has become very significant."

Jan 1, 2012

By Zhang Hanbo, Niu Liping, Zhang Zhiqi, He Jicheng, Dou Zhihe

"Rutile, ilmenite and Al-Ca complex reducer were used to prepare high titanium ferrous alloy by enhanced reduction-SHS method. The effects of the complex reducer compositions and slag types on the enhanced reduction-SHS process were investigated. The high titanium ferrous alloys were characterized by XRD and SEM. The results indicate that the high titanium ferrous alloys consist mainly of TiFe2, AlTi3 and Al2O3. The oxide inclusions exist resulting in directly the high oxygen content and micro-structural defects in the alloys. The titanium and oxygen contents decrease, but the aluminum content in the alloy increases while the mass ratio of calcium in the Al-Ca complex reducers increases. When the mass ratio of Al/Ca in the Al-Ca complex reducer is 6:1, titanium, oxygen and aluminum contents are 63.75%, 3.01% and 10.72% respectively. When the mass ratio of Al/Ca is 5:1 titanium content is 55.00% nearly and aluminum content is higher than 14.00%, but oxygen content is lower than 2.0%.1. IntroductionThe high titanium ferroalloys with 65%~75% titanium have the advantages of low melting point and high titanium content. They are widely used in special steel refining, while they are also a kind of very important quality orientation alloys in the rage of aviation and aerospace. At present, the methods of preparing high titanium ferroalloy include vacuum remelting and thermit reduction. The alloys prepared by the vacuum remelting method have good qualities and low oxygen content, so it is widely used in Russia, Western Europe and other developed countries. In China, there are abundant rutile resources, but waste titanium is lack, therefore, the preparation method is the thermit reduction. But there are many quality defects in the high ferrotitanium alloy, including high oxygen content, unstable quality and so on. In order to improve the qualities of the high titanium ferroalloy, especially to reduce oxygen content, the domestic and overseas have done a lot of further researches. For example, Sichuan E-mei ferroalloy plant and Beijing Nonferrous Metal Research Institute have prepared high titanium ferrous with 73.77% titanium with natural rutile, but the oxygen content is high. Through controlling the quality of raw material, they obtained the better qualities, but the oxygen content is still very high. South Africa Mintek company have prepared high titanium ferrous alloy with low nitrate by plasma heating under the isolation air conditions, but they couldn’t also remove effectively oxygen in the alloy. The oxygen exists in the form of Al2O3 and titanium protoxide. So it can be speculated that except TiO2 not being fully reduced, the no-sufficient alloy-slag separation is the direct reason resulting in high oxygen and poor microstructure. In view of present technical difficulties during preparing high titanium ferroalloy by thermit reduction, this paper proposed a new method of preparing high titanium ferrous with low oxygen by enhanced reduction-SHS with Al-Ca complex reducer. Ca in Al-Ca complex reducer has stronger reductive ability, it can effectively strengthen the reductive degree of TiO2. The slagging agent CaO CaF2 and MgO can effectively reduce the viscosity of Al2O3 slag to improve its liquidities to strengthen alloy-slag separation effects so that to remove inclusions and oxygen. In this paper, effects of slagging agent type on the reduction and the qualities of high-titanium ferroalloy were studied."

Jan 1, 2012

By W. Z. Yin

It is investigated systemically in this paper that the granularity of the precursor, ZnC2O4?2H2O, is influenced by synthetic conditions. Instantaneously adding of precipitation agent is able to control the mean size of precursor ZnC2O4?2H2O under 300nm, which has great function to obtain well-dispersed ZnO nanoparticles in the next step, pyrolysis. The pyrolysis kinetics model of ZnC2O4?2H2O powder is obtained. Two steps take place during the pyrolysis. The first is dehydration, which the pyrolysis kinetic model is 2(1-a)2/3(chemical reaction), A=8.3×108s-1, E=(75.82±3.00) KJ/mol. The second is formation of ZnO, which the pyrolysis kinetic model is (1-a) (random nucleation and latter growth), A=8.45×1028s-1, E=(360.54±12.00)KJ/mol. ZnO nanoparticles obtained by pyrolysis take on self-growth behavior. It is resulted that for precursor ZnC2O4?2H2O pyrolysis time takes obvious influence on the partilces size under 420?, 500? and 600?. Finally, a new flow sheet for synthesis of ZnO nanoparticles is investigated, in which blendes is used as raw material and hydrometallurgy is introduced into it. The whole flow sheet has no industrial wastes, that is all byproducts can be used in the flow sheet recycled, resulted in the de-crease of productive cost and industrial wastes.

Jan 1, 2014