Search Documents

Jan 1, 1967

Jan 1, 1968

By J. N. Maycock, P. W. M. Jacobs

Previous measurements of the thermoelectric power of ionic crystals are reviewed briefly. It is concluded that, while extensive measurerements are available on systems in which the electrode M has a cation in cornon with the sall MX, there is as yet little modern work on systems in which the metal electrode M' does not haue a calion in common with the salt. We haue now measured the thermoelectric power of- single cryslals of KC1 and of KC1 + SrCl2 between plati.nu?n electrodes over a much wider range of temperature than before. individual ionic heats of transport, which, while probably not very accurate, are of a reasonable order of magnitude, are obtained from this data on the basis of an assumption that charge carriers do not cross the electrode/salt interface. RELATIVELY little work has been done on thermal diffusion in ionic crystals. Reinhold and coworkers1-I measured the thermoelectric power and Soret effect in silver and cuprous salts and their mixed crystals. One electrode was kept at constant temperature and electromotive force was measured as a function of the temperature gradient. This is not a satisfactory technique if the results are to be compared with theory; rather should the electromotive force be measured for small temperature differences as a function of the mean temperature of the two electrodes. They used electrodes having the same cation as the salt. Patrick and Lawsons measured the thermoelectric power of AgBr and of AgBr containing 0.25 mole pct CdBr2 using silver electrodes and temperature gradients of 10°C in the temperature range 100° to 400°C. The results were analyzed using the Teltow9 values of the ratio of the mobility of the two types of charge carrier (cation vacancies and interstitials) found from conductance measurements and the wagnerlo estimate of the heterogeneous contribution to the thermopower, Ohet They obtained values of qi = 0.017 ev and q$ = -0.385 ev for the heats of transport of interstitial Ag ions and cation vacancies, respectively. Their data has been reanalyzed by Haga using the corrections to the Wagner formula for ehet given by Howard andLidiard; Haga found ev. Christy et a1.14 have measured the thermopower of AgBr containing 0.01 to 1.0 mole pct CdBr,. They analyzed their results in terms of the theory of Howard and Lidiard and found that excellent agreement with the theory was obtained if q5 + : + hF was set equal to 0.70 ev at 175°C and equal to 0.58 ev at 250°C. Since Teltow's value for hF, the enthalpy of formation of a Frenkel defect pair, is 1.27 ev, this means that qt + q: increases in magnitude from -0.57 ev at 175°C to -0.69 ev at 250°C. This result is in poor agreement with Patrick and Lawson's value of -0.37 ev for pure AgBr (for which the corrections to the Wagner estimate for ehet are very small). christy1' has also reported thermopower measurements for pure silver halides and for the systems he finds that qr + qt for AgBr increases in magnitude from about -0.55 ev at 150°C to about -1.1 ev at 400°C. The temperature dependence of the sum of the heats of transport in AgCl is very similar in magnitude. The sum qi + q cannot be decomposed into the individual interstitial and vacancy heats of transport without a knowledge of the entropy contribution from the change in the lattice vibrational frequencies around the interstitial and vacancy. Despite this it seems an inescapable conclusion from Christy's analysis that and -6 = Q Ag are quite strongly temperature-de pendent and that -q: is much greater in magnitude than the corresponding activation energy for vacancy migration, +0.37 ev. It remains a mystery as to why the data for pure AgBr are fitted so well by the assumption of temperature-independent heats of transport if association of impurity ions and vacancies is neglected.l The values for q$ and q: so obtained are also much more in line with those expected from a simple kinetic interpretation of the heats of transport due to wirtz.17 Christy and Hsueh have also measured the thermopower of CuCl between copper electrodes; 0 for pure CuCl is comparable with that for the silver halides but, owing to the limited solubility of divalent cation impurities it was not found possible to deduce values for the heats of transport. In contrast to these extensive measurements on cells of the type M MX 1 M, there have been relatively few attempts to measure the thermoelectric power of cells of the form M' 1 MX I M'. (We specifically exclude from discussion cells of this type in which the metal electrodes M' are in contact with gas containing a controlled partial pressure of either M or X,, since in these cells the electrochemical reactions are analogous to those of the first type.) The thermoelectric power of Pb12, PbC12, TlC1, TlBr, TlI, NaNO3, and KNO 3 between platinum electrodes was measured by Thie1e.l3 In discussing these measurements Holtan20 asserts that the thermopotential initially fluctuated wildly and even changed sign before approaching a steady value. A high degree of irreproducibility is also evident in the work of Nikitinskaya and Murin21 who first studied the thermopower of NaCl and KC1 between platinum electrodes. Much better reproduci-bility was achieved in our earlier measurements on KC1;22 these were, however, confined to a relatively narrow temperature range and one of the objects of the work reported in this paper was to extend the temperature range of the measurements of the thermoelectric power 8 of KC1. The only other published

Jan 1, 1967

By S. W. Zehr, G. S. Murty, W. A. Backofen

AN observation by Squires, Weiner, and phillipsl has stimulated interest in a mechanism of deformation at high temperature (above -0.5 of the absolute melting point) that is not usually thought to be involved in the creep of metals. They found precipitate-free or "denuded" zones along grain boundaries normal to the stress axis in tensile specimens of a hydrided Mg-1/2 wt pct Zr alloy after slow straining at 450° and 500°C. Their suggestion that the zones were a result of directional diffusion of magnesium atoms was supported with calculations from Harris and Jones2 which also tended to identify the process as Nabarro-Herring (N-H) creep3,4—a process that is characterized by Newtonian viscosity, with stress (o) directly proportional to strain rate (C), and one that proceeds by lattice diffusion. Material transport by diffusion along grain boundaries is an alternative basis for Newtonian viscosity, as demonstrated by Coble,5 and is favored over N-H creep for fine grain size and lower temperature.6 In either case, the strain rate sensitivity of flow stress, defined as m = d log o/d log E (which commonly appears in the empirical a = KEW), is unity. The experiments to be described here gave metallo-graphic indications of diffusional creep which were no less clear than those just cited, but the associated m (as measured by the method of Ref. 7) was much more like that of a Bingham material. For true Bingham behavior, (a — ao) E, where oo is an initial yield stress. Therefore, even if flow after yielding should occur by diffusional transport, m must increase from 0 as < is raised to reach unity only in the limit as One result is that the resistance to tensile necking conferred by Newtonian viscosity is lost, which would become increasingly apparent through the formation of more sharply defined necks as 6 is lowered. That trend appeared in these experiments. Most of the work was done on an extremely finegrained alloy of magnesium with -6 wt pct Zn and ½ wt pct Zr (Mg ZK60); the initial mean-intercept grain diameter, L, was 0.55 µ. Shown in Fig. l(a) is a germanium-shadowed carbon replica of the surface of a specimen that was coated with silicone oil,* heated to 270°C under a helium atmosphere, and then stretched locally -200 pct at an initial E = 3.3 x 10-5 sec-1. Under

Jan 1, 1969

By A. Tanaka, K. G. Carroll

The existence of local room-temperature plastic flow in germanium, which has been a subject of controversy for nearly two decades, has recently received renewed attention, albeit no more agreement than hitherto. Phenomenologically one major facet of the problem has been reduced to the question whether or not indentation can be effected in germanium without the introduction of cracks. That plastic flow can be induced at room temperature by fracture appears to have been rather convincingly demonstrated recently by Suzuki and Kamada and by Noble and Henisch.1 The literature contains both direct and incidental references to Vickers and Knoop indentations showing no cracks, within resolution of optical microscopy. Recently, however, following a controversy on the subject,2,3 johnson4 made a study of indentations produced by spherical indenters and concluded that these are accompanied by cracking. This study in-

Jan 1, 1969

By R. D. Nelson

The purpose of this technical note is to briefly present some data on a phenomenon—recrystallization with concurrent deformation—that has been found to occur in a plutonium. This phenomenon is unusual because a plutonium is considered brittle, not easily deformed, and not easily recrystallized; the a phase is simple monoclinic having 8 atoms per unit cell and it is stable below about 115°C. The properties of the recrystallized metal were different from the as-cast metal. Even though a plutonium is difficult to deform, Ianniello successfully rolled it&apos; and he also observed some recrystallization at 120°C.2 Pavlick and Hanson3 detected some recovery at 109°C but they observed no recrystallization. Gardner4 and Bronisz5 studied the compression properties up to 100°C but they did not report having seen recrystallization. In the present deformation studies of electrorefined plutonium pronounced recrystallization took place concurrently with plastic deformation in compression between 24" and 115°C. The metal contained less than 300 ppm total impurities with the major impurities being 100 ppm Am, 30 ppm C, 40 ppm W, and 25 ppm U; all other impurities totaled less than 100 ppm. The compression specimens were machined to dimensions of 1.2 cm long and 0.8 cm diam from as-cast rods having a density of 19.65 g per cu cm. They were heated to the test temperature in a high-temperature silicone fluid that was evacuated to 10-4 Torr. With this procedure the specimens oxidized a negligible amount, and the temperature was maintained within ±0.2°C for times up to 3 weeks. Deformation and recrystallization

Jan 1, 1969

By R. G. Vardiman, M. R. Achter

Observations of dislocation structure in niobium are presented using two techniques. Triangular pits developed by electroetching are confined to orientations in the stereographic triangle between the (111) pole and planes of the (1ll) zone and require the presence of carbon. Some unusual electroetching phenomena at other orientations are noted. A chemical etch of dislocations decorated by the addition of carbon to 50 ppm reveals the complete dislocation line structure in a surface layer up to 30 p deep, with a resolution of less than 1 p. This effect is independent of surface orientation. The structure of subboundary nets may be resolved for misorientations up to about 1&apos;. Dislocation structures found in strain anneal grown crystals, such as helices, prismatic loops, and high-density areas, are observed. The measurement of dislocation density is discussed and values obtained in different ways are compared. IN the course of some work on the response of refractory metals to thermal-mechanical treatments, it was desired to examine the defect structure of relatively low dislocation density crystals of niobium in bulk form. Surface and bulk methods for the observation of dislocations have been reviewed by ~melinckx,&apos; and include etch pitting, decoration, and various X-ray techniques. The dislocation line structure has been developed by decoration in a few metals, although observations were limited to certain orientations, or by the coarseness and nonselectivity of the precipitate. The most commonly used technique is etch pitting. In niobium, etch pits have been developed chemically&apos;0," in material of high impurity content and electrolyti-cally&apos;&apos; in relatively pure material. In this paper, etch pits developed electrolytically, and the dislocation line structure of a surface layer developed by decoration and chemical etching, are examined, and observations are presented from both techniques. EXPERIMENTAL METHODS Our starting material was electron-beam-melted niobium, swaged to 4 or -in.-diam rod. Chemical analysis is given in Table I. Single crystals were grown by a strain anneal technique using 1 to 2.5 pct of strain and growth temperatures of 1700" to 2300"~.&apos;~ Some crystals grown by zone melting were also examined. The desired surface orientation was exposed either by spark machining or by sectioning with a cut-off wheel and prepared for etching by electro-polishing.

Jan 1, 1969

By J. Campbell

The hydrostatic tensions in pure metals and long freezing range alloys are evaluated theoretically considering the viscous flow of residual liquid and the general plastic collapse of the casting. The former mechanism operates until the radii of the remaining liquid channels are of the order of 10-3 cm radius, after which the second process limits the attainable negative pressures which range from —1500 to -4200 atm for nickel, aluminum, copper, and iron. In previous reports1&apos;2 the maximum possible hydrostatic tensions developed during solidification have been evaluated employing spherical symmetry. This inevitably involves the concept of totally confined liquid regions, the reality of which has recently been brought into serious doubt3 following observations of the freezing of various transparent materials. Regions of interdendritic liquid which are apparently about to be isolated by the growth of dendrite arms are observed not to be cut off because the advance of the dendrite tips is arrested until the region has completely solidified. Although this may be the result of the very low melting point liquid available at this late stage in freezing, or the result of a higher rate of heat transfer to the dendrite tips because of the acceleration in liquid flow rate near the completion of solidification, this point need not concern us. In this paper an attempt is made to approximate more closely to real conditions; thus the assumption of confined liquid regions is abandoned and cylindrical symmetry adopted. It has also been necessary, therefore, to consider the viscous flow of residual liquid through the remaining channels in the pasty zone. Furthermore, the rather special conditions of spherically symmetric solidification led to extremely high solidification rates and hence unusually high tensile stresses as solidification neared completion; the cylindrical Symmetry appears to yield solidification rates and stresses which are more typical of real castings. The rate of solidification is first considered since this critically affects both the flow of the liquid and the creep of the solid.

Jan 1, 1969

By J. Campbell

Various models are discussed for the evaluation of the negative pressures which may occur in solidifying materials which exhibit various deformation modes: elastic-plastic, Bingham, viscous, or creep flow. The inadequacy of the previously proposed elastic-plastic solution for solidifying metals is revealed by comparison with the more reliable creep results which are given graphically for aluminum, copper, nickel, and iron. The maximum tensions experienced in the liquid phase of solidifying spheres ranging in size from large castings to submicron powders are in the range from —10&apos; to —105 atm for these metals. THERE has been much recent interest in the negative pressures associated with the volume change on solidification and in the possibility of the occurrence of cavitation. Considering the freezing of a highly supercooled liquid, an attempt to evaluate the stresses in the liquid ahead of the rapidly moving solidification front has been made by Horvay1 on a microscale and by Glicksman2 on a macroscale. In a casting of a wide freezing range alloy, the pressure differential due to viscous flow of residual liquid through the pasty zone has been discussed by Piwonka and Flemings,3 In a previous publication4 the author has attempted to estimate the negative pressure occurring in the residual liquid of a spherical casting, employing an elastic-plastic model to describe the collapse of the solidified shell under the internal tension. An earlier model assuming a rigid shell was shown to be inaccurate by many orders of magnitude. The elastic-plastic model is critically reviewed here, and other models are developed which are thought to be more closely related to metals and other materials near their melting points. The spherical geometry (Fig. 1) is chosen because the highest shrinkage pressures would be developed, although the analyses are readily adaptable to cylindrical geometry. A parallel sided casting experiences little internal tension because of the relatively easy dishing inward of the sides. (This commonly observed phenomenon has previously been attributed solely to atmospheric pressure.) Furthermore, small regions of confined liquid in a large solidified volume of a casting approximate reasonably well to spherical geometry. ELASTIC-PLASTIC MODEL The author has shown4 that as solidification proceeds the internal hydrostatic tension builds up until the elastic limit of the shell is exceeded. At this point the internal pressure is closely -2Y/3. Subsequently a plastic zone spreads from the inner surface toward the outer surface of the shell. When the whole casting is deforming plastically a rather more generalized analysis taking account of the externally applied pressure PA + 2y/b gives the internal pressure as: P = Pa + 2y/a + 2ys/b - 2 Y In(b/a) [1] The 2y/a and 2ys/b terms result from the tendency of the liquid-solid and solid-vapor interfaces to shrink, reducing their energy, and thereby helping to collapse the solid phase and compress the liquid phase. The 2y/b term would be important only for powders. The last term arises because of the plastic restraint of the solid, resisting collapse and so effectively expanding the residual liquid. From Eq. [I] it is easily shown that there is a minimum in the pressure at the radius amia= y/Y [2] which is of the order of 103K for the metals aluminum, copper, and iron, and corresponds to the minimum pressure Pmin = 2 Y[l-ln(bY/y [3] The results of a fully worked out elastic-plastic solution are given in a previous reporL4 The main criticism which may be leveled at this analysis when applied to metals at their melting points is the strong dependence of the yield stress on the strain rate. The strain rate varies with both solidification conditions (e.g., whether chill-cast or slowly cooled) and during solidification, as is indicated in the following section. Thus an appropriate choice of Y is very arbitrary. Before proceeding to a discussion of models which are strain-rate-dependent, it is necessary to evaluate the strain rate as a function of the rate of solidification. SOLIDIFICATION RATE Various empirical relations have been deduced5 for the rate of thickening of the solid shell by pour- out tests on partially solidified spheres. These, however, are unsatisfactory for our purposes since they become very inaccurate when the liquid core is very small. A theoretical approach is therefore necessary, and some solutions are set out below. Making the assumptions of constant surface temperature of the casting during freezing, no superheat, and a material freezing at a single temperature, Adams8 deduces the approximate solution: which becomes when b » a: Employing a semiempirical approach vallet6 finds:

Jan 1, 1969

By Amitava Gangulee, Michael B. Bever

The effects of changes in short-range order on some thermodynamic, electrical, and mechanical properties of the silver-rich Ag-Mg solid solutions have been investigated. The heats of formation at 273°K of several alloys after two different thermal treatments were measured by liquid metal solution calorimetry. Their electrical resistivities were measured at temperatures ranging from 4° to 773°k. Tensile tests and microhard-ness measurements were carried out at room temperature. An effective short-range order parameter and an effective interaction energy are defined. The measured changes in the properties are interpreted in terms of these quantities. The short-range order parameter is evaluated separately from calorimetric and X-ray data; the results are in fair agreement. Increasing short-range order lowers the resistivity of- the silver-rich Ag-Mg alloys but does not measurably affect the temperature dependence of the resistivity. Short-range order increases the yield stress of these alloys but does not affect the ultimate tensile stress. Changes in the effective short-range order parameter independently obtained from measured changes in the heat of formation, resistivity, and yield stress are in fair agreement. THE thermodynamic, electrical, and mechanical properties of solid solutions have been investigated as functions of composition in many alloy systems, but the effects of configurational variables, such as short-range or long-range order, on these properties have received much less attention. The silver-rich terminal solid solutions in the system Ag-Mg are well-suited for the investigation of the effects of order. The composition of these solid solutions may be varied over a range extending to about 27 at. pct Mg.1 Appreciable short-range ordering is likely to take place in these solid solutions; the degree of short-range order can be varied by suitable thermal treatments. In the alloy Ag3Mg long-range ordering is possible.2 This paper is primarily concerned with the effects of short-range order on some thermodynamic, electrical, and mechanical properties of the silver-rich Ag-Mg solid solutions.-The long-range ordering transition is the subject of a concurrent paper.3 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Specimens. Ag-Mg alloys containing up to 26.4 at. pct Mg were prepared by melting 99.99 pct pure Ag (obtained from Baker Chemical Co.) and 99.99 pct pure Mg (obtained from Eastman Chemi- cal Co. or Johnson Mathey & Co.) in graphite crucibles under molten potassium chloride. The solidified ingots were homogenized at 823°K for 10 days in evacuated Vycor capsules. A surface layer 6 in. thick was then removed by machining. The ingots were swaged into rods (2.5 mm diam) which were drawn into wires (1.0 mm diam). The wire specimens were annealed at 773°K for 24 hr in vacuum and either quenched into iced brine or cooled to room temperature over a period of 15 days. The average grain diameter (obtained from the linear intercepts) was about 0.1 mm. 1.2) Calorimetry. The heats of formation of the alloys were measured in a tin solution calorimeter as the difference in the heat effects of alternate additions of samples of an alloy and the mechanical mixture of its component elements. The additions were made from 273°K to the bath at about 623°K. The heat effect on addition of the alloys was approximately 5.5 kcal per g-atom. The procedure and the method of calculation have been described.4 1.3) X-Ray Diffraction. Short-range order parameters of two alloys were calculated from diffuse scattering intensities,&apos; obtained with briquettes made from powdered specimens. A GE-XRD 5 diffractometer with filtered copper radiation was used. The absolute intensities were based on calibrations with paraffin. 1.4) Resistivity Measurements. The electrical resistivities were measured by a potentiometric method in which the potential drop across the specimen was compared with that across a standard resistance. For measurements below room temperature, the specimens were immersed in liquid helium (4°K), liquid nitrogen (78°K), dry ice and trichloroethylene (195°K), or ice and water (273°K). Measurements above room temperature were made on specimens held in a furnace under helium or in vacuum. The resistivity measurements were reproducible to ±0.5 pct or less. 1.5) Mechanical Tests. Tensile tests were carried out at room temperature with a Tinius-Olsen XY elec-tromatic Universal testing machine. Wire specimens (nominal gage length 1 in.) were used. The strain was measured with an extensometer, which had a sensitivity of 4 x 10-5; the strain rate was 10-3 min-1. Microhard-ness measurements were made with a square-pyramid indenter and a 100-g load.11 2) RESULTS AND DISCUSSION All measurements were made on two parallel sets of specimens, one quenched and the other slowly cooled from 773°K. The reported values are the averages of at least three measurements. In the range of magnesium concentration substantially below that of the composition Ag3Mg, quenched alloys have less short-range order than slowly cooled alloys. As the magnesium concentration approaches that of Ag3Mg, slow cooling develops long-range order. Quenching sup-

Jan 1, 1969

By Amitava Gangulee, Michael B. Bever

The order-disorder transition in Ag-Mg alloys in the range 17 to 26 at. pct Mg was investigated and some thermodynamic, electrical and mechanical properties of ordered Ag-Mg alloys were measured. A modification of the phase diagram is proposed on the basis of measured transition temperatures. The stability of the ordered structure is analyzed in terms of the quasichemical theory. Kinetic aspects of the order-disorder transition were also investigated. The energies of ordering at 273°K of Ag-Mg alloys were measured by liquid metal solution calorimetry. The electrical resistivities and the tensile Properties of the ordered alloys were measured. The exothermic energy of ordering increased with magnesium concentration up to the composition Ag3Mg; it is discussed in terms of the quasichemical theory. Pronounced order hardening was observed and can be explained by several strengthening mechanisms, which are particularly effective because of a change in crystal structure associated with the ordering transition. IN silver-rich solid solutions containing approximately 17 to 26 at. pct Mg, long- range ordering may occur during appropriate therma1 treatments. Clare-brough and Nicholas1 first detected such long-range order in the solid solution of composition Ag3Mg and suggested that the unit cell of the superlattice contained 256 atoms. x-ray2 and electron diffraction3 investigations confirmed the occurrence of long-range order, but indicated a shifted Ll2-type structure. On the basis of recent X-ray measurements the crystal structure of ordered Ag3Mg has been confirmed as type D023.4 The present paper is concerned with the order-disorder transition in silver-rich Ag-Mg solid solutions and some thermodynamic, electrical, and mechanical properties of the ordered alloys. The effects of short-range order on the properties of silver-rich solid solutions containing up to 26 at. pct Mg are discussed in a concurrent paper.5 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Specimens. Specimens of Ag-Mg alloys containing from 18 to 26 at. pct Mg were prepared in the form of 1.0-mm-diam wires as described in Section 1.1 of Ref. 5. Disordered specimens were prepared by annealing at 773°K for 1 hr and quenching into iced brine. Ordered specimens were prepared by annealing at 773°K for 1 hr and slowly cooling to room temperature over a period of 15 days. The specimens were stored at 78°K. 1.2) Resistivity Measurements. Electrical resistivi- ties were measured by a potentiometric method.&apos; Equilibrium values were obtained at several temperatures. The kinetics of ordering were investigated by following the time-dependent changes of the resistivity of initially disordered specimens during annealing. The specimens were enclosed in copper capsules and immersed in salt pots; the heating up was accelerated by injecting preheated helium into the capsules. 1.3) Calorimetry. The energies of ordering of the alloys were measured in a tin solution calorimeter as the difference between the heat effects of additions of completely ordered and disordered specimens of the same composition. The procedure and the method of calculation have been described.6 Magnesium was used for thermal compensation in most calorimetric runs in order to improve the accuracy.677 1.4) Mechanical Tests. Tensile tests were carried out with wire specimens at room temperature as described in Section 1.5 of Ref. 5. Microhardness measurements were also made.? 2) RESULTS AND DISCUSSION The characteristics of the order-disorder transition of silver-rich Ag-Mg solid solutions will be discussed first. Some thermodynamic, electrical, and mechanical properties of the ordered alloys will then be considered and compared with the corresponding properties of dis-disordered alloys. 2.1) The Order-Disorder Transition. 2.1.1) Thermodynamic and Structural Aspects. The transition temperatures Tt were determined from discontinuities in the slope of the equilibrium resistivity vs temperature curves. Normalized curves for three compositions are shown in Fig. 1. The transition temperature increases with the magnesium concentration and reaches a maximum at the stoichiometric composition Ag3Mg. The transition temperature of the alloy Ag3Mg was measured as 665° ± 2°K and compares with published values of 660°,1 663°,8 and 66°k.3 In the slopes of the resistivity vs temperature curves of alloys containing 22.2 and 22.5 at. pct Mg, discontinuities were observed at two temperatures. Such upper and lower discontinuities indicate a two-phase field. A modified form of the published phase diagram9 is shown in Fig. 2. A two-phase field was found only on the low-magnesium side of the composition Ag3Mg. On the high-magnesium side, the existence of a two-phase field could not be established because of insufficient resolution, but such a field must be present. This part of the phase diagram can be made complete by a eutec-toid-type reaction a = (a&apos; + ß). The existence of a boundary between the two-phase fields (a + ß) and (a&apos; + ß) is also in accord with published lattice parameters.3 The crystal structure of ordered Ag3Mg (type Do23)

Jan 1, 1969

By A. U. Seybolt, R. E. Honnemon

THE purpose of this communication is to present activity data of nickel in the Ni-A1 binary system that was obtained for oxidation studies in this system. This data has been calculated from previous aluminum activity data at 1000°C1,2 by two types of Gibbs-Duhem integrations. These results should be of particular current interest to oxidation studies of aluminide coated nickel-base superalloys3 as well as other problems. The aluminum activity of Steiner and Komarek1 is plotted in Fig. 1 as a function of composition in Ni-A1 alloys at 1000°C. The dashed parts of the aluminum curves represent our approximate extrapolations from the directly measured regions. In the terminal solution regions (a and L phases) standard parabolic solution functions of the following form are assumed: where i is the component subscript, Ki is a constant at a fixed temperature, and xi is the atom fraction. The resultant nickel activity curve at 1000° C from the Gibbs-Duhem integration4 of the aluminum data is shown in Fig. 1. The solubility ranges of the phases present in the Ni-A1 binary at 1000°C are also denoted at the bottom of Fig. 1. Corresponding values of the nickel activity, aNi and yNi, are listed in Table I at useful compositional intervals. including phase boundary values. The aNi and yNi data listed in Table I are subject to the uncertainties present in the experimental aluminum activity data1 and to deviations from parabolic solution behavior in the terminal solutions. The errors introduced into aNi and yNi due to the parabolic solution assumption are expected to be relatively small (<20 pct of the values given) in all the phases except the liquid phase. Some deviation from parabolic solution behavior in the liquid phase is indicated

Jan 1, 1970

By H. J. Levinstein, H. J. Guggenheim

RbFeF3 is a transparent ferromagnet with a large faraday rotation which permits the direct observation of magnetic domain structures in bulk crystals. If the position of dislocations within the crystal were known a study of domain wall dislocation interactions would be possible. In this paper an etch pitting solution is described which gives a one-one correspondent between the etch pits and the dislocations intersecting the (100) surfaces of RbFeF3 crystals. In addition, RbFeF3 is shown to have sufficient plasticity so that known arrays of dislocaticms can be put into the crystal. It is concluded that RbFeF, is an ideal material for the investigation of domain wall dislocation interactions. THE influence of lattice defects on the motion of domain walls in ferromagnetic materials has been studied extensively both theoretically and experimentally.4 The experimental data obtained has been qualitative in nature due to the lack either of a quantitative knowledge of the magnetic domain array in the material or of the nature of the dislocation configuration in the material. At room temperature RbFeFJ has the cubic perovskite structure. It is ferromagnetic below 86°K.5,6 It is also transparent and has a large faraday rotation in the magnetic state.7 The domain structure of this material is observable in three dimensions in crystals which are millimeters in thickness.&apos; Since RbFeF3 satisfies the requirements of having an easily visible three-dimensional magnetic domain structure, it was of interest to determine if the dislocation structure of the material could be determined and if the material was sufficiently plastic so that dislocations could be introduced into the as grown crystals. This is a report of the results of that investigation. EXPERIMENTAL PROCEDURE The crystals of RbFeFs used in this experiment were grown by a technique described elsewhere.5 In order to obtain flat strain-free surfaces, the samples were first cut to the crystal orientation desired and the surfaces were polished by employing standard metallographic techniques. The samples were then immersed in a solution of 1 to 3 g of KOH in 100 ml of water. This solution removes the damaged surface layers uniformly leaving a film on the surface of the sample. Etch pits are obtained by immersing the sample in an approximately 50-50 solution of 30 pct peroxide and concentrated acetic acid. The film formed during the KOH treatment turns deep red in color in the etching solution and flakes off the sample. The etching time required depends upon the pit size desired and

Jan 1, 1970

By R. M. Asimow, J. J. Svitak

Tile crilical resoll,r,d shear stress, CRSS, for slip of slow1y cooled Ag-All single crystals was measured at 201K. Tlze importance of short-range order and Suzuki sogregalion was inrestigated by deter~rlining llze ciic.cl of quenching on the CRSS. Thr obserz.ed rfrtenching effects were generally small and indicate that short-range ordcr and Slczuki srgregation do no1 account for n significant portion of the solid-solution strengthening in this system. However, all alloys slzozcwi yield drops ulhich rilere heat- lreat nrenl-sensiline THERE have been a number of mechanisms proposed to explain alloy strengthening in the Ag-Au system. The effectiveness of some of the proposed mechanisms, especially those that depend on Suzuki segregation1" or on short-range order,2-6 SRO? should be strongly dependent on heat treatment. Since internal friction investigations in this system indicate that there is stress-induced order,&apos; we must also consider the possibility of local atomic rearrangement or short-range ordering in the stress field of a dislocation. There is not complete agreement whether these mechanisms should be most effective in raising the flow stress, in causing yield drops. or some combination of these two effects. This work was undertaken to determine the effects in the Ag-Au system of mechanisms that depend on segregation or order by using known but drastically different cooling rates following a high-temperature treatment. By comparing the critical resolved shear stress, CRSS, for slip measured after a very slow cool and again after a fast cool (quench) of the same crystal, it is possible to determine the effect of cooling rate on CRSS* and on yield drops. The single-crystal CRSS was determined at several compositions because there has been no data published across the phase field since the publication of room-temperature flow stress by Sachs and Weerts.&apos; EXPERIMENTAL PROCEDURE Starting with materials of 99.999 pct purity, single-crystal specimens of random orientation 1.25 mm square by 4 cm long were prepared with 0, 10, 14, 25, 30. 50, 70. 75. 80, 90. and 100 at. pct Au. Crystals were grown in an inert atmosphere using a modified Bridgman technique with a growth rate of 1.5 cm per hr in a gradient of 3°C per cm. To obtain a maximum practical degree of SRO, the crystals were cooled at a rate of 275&apos;C per hr to about 310°C and then cooled at 6°C per hr to approximately 200°C. Specimens were tested in tension immersed in an alcohol bath at -72°C (201°K) at a strain rate > = 0.003 mm"1 to determine the CRSS (7). The activation volume of several crystals was determined from the flow stress increment (72 - T1) for a tenfold increase in strain rate. The total shear strain varied from 0.05 to 2.3 pct but was generally less than 0.4 pct. After testing, each crystal was then held at 500°C for 10 min, quenched into brine at -35°C and. after storage at -71°C for 1 day, retested in tension using a procedure identical to that of the first test. The quenching apparatus, see Fig. 1, was designed to enable accurate temperature control and rapid quenching while preventing specimen contamination and accidental deformation. Test data from a specimen with a fine thermocouple spot-welded to it indicated a cooling rate of 104C per sec. The relatively low heat-treatment temperature was chosen to minimize quenching defects caused by a large vacancy

Jan 1, 1970

By B. Chalmers, L. Bäckerud

The growth temperature of dendrite tips has been measured in a binary alloy system, Al-Cu, as a function of rate of formation of solid phase. Metallographic examination has rerealed the dendritic structure dereloped during different stages of the freezing process and factors influencing the undercooling, such as solute buildup, surface tension, and kinetic effects, have been estimated. Practical implications of the results are discussed. THE development of a dendritic growth pattern during the solidification of metals and alloys has an influence at least equal to that of grain size on the properties of the casting or ingot being produced. and consequently much interest has been devoted to the study of this phenomenon. A review of the knowledge gathered up to 1964 has been given by Chalmers.&apos; Among recent publications in the area the works of Jackson et al 2 and Flemings and his coworkers3,4 are of special interest. This work is an experimental study of the factors which influence the development of a dendritic pattern during the solidification of a typical binary alloy system, A1-Cu, when there is no heat source in the liquid. This means that the temperature and the temperature gradient are controlled by the heat extraction from and latent heat evolved by the growing crystals. EXPERIMENTAL PROCEDURE Samples were prepared from a master alloy made up of aluminum, 99.995 pct, and copper. 99.99 pct, of the concentrations given below and of sufficient size to fill cylindrical graphite molds of 35 mm ID and 35 mm height. Bottom. wall. and lid of the graphite molds were all of 6 mm thickness, Fig. 1. Thin ceramic thermocouple shields could be introduced at different positions in the sample through holes in the lid. The assembly was heated in a small vertical resistance furnace to a suitable temperature. 700° to 720°C. which is well above the melting point of the sample. It was thereafter taken out of the furnace and chilled at selected rates, and the temperature changes in the sample were recorded. For high sensitivity in the temperature recordings, a reference thermocouple was held in a solidifying pure aluminum melt. which was very well insulated and therefore was at a constant temperature. 660°C, for nearly half an hour. The thermocouples were connected so that the difference voltage was fed into the recorder of which the most sensitive range was 1 mV. Temperature variations could be read to within 0.l°C. The thermocouples used were of the Chromel-Alumel type (28- or 38-gage wires) and the recorder a two-pen Moseley strip chart recorder. The different rates of chilling were obtained in the following way. a) The graphite crucible was wrapped in one or two layers of an insulating. feltlike material (Fiberfrax paper from the Carborundum Co.). The drop in temperature per unit time after complete solidification could thereby be varied from 8" to 18°C per min. This corresponds to a rate of heat extraction in the given samples from 0.08 to 0.17 cal cm-&apos; sec-I. 6) The bare graphite mold was placed free on a piece of firebrick. The measured temperature drop was around 50°C per min (-0.5 cal cm-" &apos; sec- I). c) By blowing compressed air through a tube with many holes surrounding the mold in a ring shape. the rate of heat transfer could be raised to 150&apos; to 200°C per min (-1.7 cal cm-3 sec- I). d) Cooling rates around 1000 C per mill (-9.4 cal cm-3 sec-l) were obtained by substituting the air in the device used in c by water. The range of cooling rates used in these experiments correspond to technical casting processes from slow solidification as obtained in sand molds to very rapid freezing which occurs in some continuous casting and welding processes. EXPERIMENTAL RESULTS The A1-Cu system was chosen for the experiments: the relevant part of the phase diagram is reproduced in Fig. 2. Observation of the Center Temperature. When a thermocouple is inserted in the center of the melt. the type of cooling curves obtained at slow solidification rates differs little from numerous published curves from similar systems. and the solidification pattern

Jan 1, 1970

By Morris Cohen, Robert C. Ruhl

The phases in Fe-C alloys over a wide composition range have been studied after splal quenching from the liquid state. Binary alloys containing 0 to 5.1 wt pel C as /cell as a large number of ternary Fe-C-Si alloys with 2.5 to 5.0 wt pct C and 0.3 to 5.1 wt pct Si were attlong those sludied. Olher Fe-C-X alloys, zcilh X being Co, Cr, ,Wn, Ni, and Ru , were also inrestigated after splat quenching. At high carbon contents, a new hcp phase (designaled 6 phase, but different from e carbide) is retained upon splat quenching. The .fraction of this phase varies up lo 97 pcl for a Fe-4.K-1.9% alloy. The composition of the E phase ranges from about 3.8 10 4.8 wt pet C, and the corresponding laltice parameters increase linearly ulith carbon content, while the c/a ratio remains essentially conslc~nl. The E phrtse appears to he a solulion of carbon in E iron, the latler being nornially found only at high pressures. It is deduced that the unit cell of the E phase corresponds to the formula Fe12C3, and llzal il is relaled to tlie ordered slruclures 0.f 6 iron carbide and c iron nilride. The E phase is compared and contrasted to the olher known carbides and nitrides of iron and nickel. An exlrapolaTion of the atomic volume 1,s carhon conlent of /he E pllase lzcts giz.en a neu7 estitnale jor /he alomic volume of E iron, 11.30 cu A, a1 atmospheric pressure and temperature. Other alomic volume relalionships lead to /he co~zpositioti Fe2.iC tor E iron carbide, /he unit cell fortr~ula being -Fe2rClo The E phase undergoes a lulo-slage decomposition upon healing, .forrning firsl rnarlensile plus E carhide, a/ler 1 hr at 140" lo 200°C, slid then ferr ite Plus cementile, after 1 lir a1 330" to 460°C. A1 carbo,l contents between 1.5 and 3.0 LC/ pcl, (he predo.wirzar/t plzase alley quenching is fcc austenite. The retained carbon content of this phase increases with itlcreasing silicon in certain concentration ranges, reaching a maximum of 2.37 wt pct C itz a Fe-2.6C-4.OSi alloy. This is the highest carbon conten1 reLaitled in austenite to date. These high-carbon aus-tenites can be partially tm?zsforttled lo tnartensile hy severe deformation in the temperature range of — 190 to -50°C. TECHNIQUES for splat quenching from the liquid state have been utilized in numerous recent investigations to produce metastable phases in a variety of alloy systems. Among the several ways of splat quenching, the shock-tube method appears to yield the highest cooling rates1-3, 7, 8 and was adopted here. Estimated cooling rates attained in the present experiments ranged from 10&apos; to 10 80Cper sec.&apos; As a part of a research program on interstitial al- loy phases, the Fe-C system was selected for splat-quenching studies. It was hoped that splat quenching would allow high metastable supersaturations of carbon to be retained in solution. Also of considerable interest were the conditions governing the occurrence of the various intermediate phases upon solidification. The alloys investigated included both binary Fe-C compositions as well as six ternary Fe-C-X alloy systems. The known phases in the Fe-C system are summarized in Table I.* Only the ferrite and graphite are ent investigation.14 and is described in detail herein Table II summarizes corresponding data on Fe-N phases, which are also of interest here because of their similarity to the Fe-C phases. EXPERIMENTAL PROCEDURES Alloys were prepared by melting the elements. 99.9 pct purity, in an inert gas nonconsumable electrode arc furnace. The buttons. weighing about 5 g. were remelted twice. were then fragmented. and their interior surfaces were examined for uniformity: if any doubt existed. they were remelted again. Chemical analyses were performed on all the alloys. the accuracy being about k0.05 wt pct. At high temperatures, carbon-containing alloys react with alumina crucibles as follows: If the atmosphere in the splat-quenching furnace does not contain sufficient carbon monoxide the alloy can be depleted of carbon and contaminated with aluminum. Calculations and experimental observations showed that 50 to 100 torr CO partial pressure effectively blocked the above reaction in all the alloys investigated. The splat-quenching equipment in Figs. 1 and 2 provides for evacuation and back-filling with CO-Ar mixtures. The furnace is capable of operation up to 1650°C. and the gettering action of the graphite heating element reduces the oxygen partial pressure in the furnace atmosphere to below 10-5 torr, thus preventing oxidation of the specimens.

Jan 1, 1970

By G. L. F. Powell, L. M. Hogan

Samples of silver and Ag-O alloy, 0.12 wl pet, have been undercooled to a maximum of 250°C by melting in a slag of commercial soda-lime glass. Grain refinement occurred in undercooled silver samples whet the degree of undercooling exceeded a critical value which varied from 153° to 175°C, depending on the melting conditions. In under cooled Ag-0 samples, the grain structure was fine and equiaxed at degrees of undercooling larger than 50oC. The grain refinement in both silver and Ag-0 alloy samples was the result of recrystallization during or immediately following freezing. When the oxygen content was increased, the degree of undercooling at which recrys-tallization occurred decreased. INVESTIGATIONS of the grain structure of strongly undercooled melts of nickel and cobalt1-4 have revealed a change in room-temperature grain size as a function of undercooling. At large degrees of undercooling the grain size was fine, but samples undercooled by smaller amounts exhibited a much coarser grain structure. The reported undercooling at which this grain size transition occurred in nickel varied between 140° and 175&apos;C undercooling. Walker1 attributed this grain size change to an enhanced nuclea-tion rate. Cavitation at a melt-solid interface was con sidered to generate a high-pressure wave. This, in turn, produced nucleation in the liquid as a result of an elevated freezing point increasing the undercooling in the melt. A similar grain size transition was observed in undercooled silver between 133° and 153°C undercooling.5 The grain size transition in undercooled silver was found to be dependent on oxygen con tent. More recently, the authors5 showed that a simila transition occurred in an undercooled Cu-O alloy, =0.08 pet, but not in oxygen-free copper undercooled more than 200°C. The transition was attributed to recrystallization of the solidified grains after freezing; the greater the degree of undercooling, the more complete the recrystallization. In view of this effect of oxygen content on grain size transition, additional undercooling experiments were carried out with silver. This paper reports the results of these studies on silver and Ag-O alloys undercooled more than 50°C EXPERIMENTAL 1) Materials. The silver was supplied by Matthey Garrett Pty., Ltd., as fine granulate, silver mini&apos; mum 99.9 pet, and contained the trace impurities shown in Table I. The silver originated from two different refineries resulting in the difference in impurity content shown in Table I. However, the variation in composition had no discernible effect on the undercooling behavior. Samples of the silver were melted in an open-ended, vertical, cylindrical resistance furnace, wound with Kantha] wire, the temperature of which was adjusted by means of a variable transformer, 2) Melting and Undercooling. Bulk samples of silver were undercooled by preoxidation and removal of oxidized impurities in a glass slag, as previously described,5 but special precautions were necessary to allow comparison between oxygen-free silver and a Ag-O alloy. Samples free of oxygen were prepared by first melting weights of granulate varying from 200 to 400 g in clean vitreous silica crucibles in air for approximately 15 min. A sample was frozen and a complete glass cover formed over the top surface by adding granulated glass rod. The sample was then melted and frozen several times until no oxygen bubbles appeared in the glass slag. Subsequent thermal analysis indicated that the oxygen content was negligible. The glass acted as an efficient barrier to absorption of oxygen from the air. Ag-O alloys were prepared by melting silver in silica crucibles with only a partial cover of glass, so that the top surface of the melt was in contact with air. The silver was held molten in air for several hours at 1000° to 1050°C, in the expectation that the oxygen in solution would reach equilibrium with atmospheric oxygen. At T - 1000°C the equilibrium oxygen content was calculated as 0.12 wt pet O, using Sieverts law and Eq, [l], derived by Mizikar et a!.7 from the data of Sieverts and Hagenacker8 for 1 atm of oxygen:

Jan 1, 1970

By Jameel Menashi

Aqueous solutions of Na2Cr04 can be reduced with CO to produce hydrous Cr203 and NaHCO3/Na2CO3. CH3OH, HCOO and HCHO in the presence of CO2 also reduce Cr 6+ and yield similar products. It is shown that the rate of Cr6+ reduction can be represented by the expression -d[Cr6+]/dt=k[Cr6+)1/2[R] where [R] is the aqueous phase concentration of CH3OH, HCOO- or CO. With these three reductants, the activation energies for the reduction processes are comparable and are of the order of 100 kJ/mole. Rapid reduction rates are attained at temperatures in excess of 220°C and, with these three reductants, a green acid-insoluble readily filterable hydrous Cr203 is formed. With HCHO significant reduction of Cr6+ occurs at about 80-100°C and an acid-soluble violet modification of hydrous Cr2O3 is formed. The reduction process is reasonably selective: solutions of Na2CrO4 contaminated with Mo6+ and W6+ can be reduced to yield a Cr2O3 product with significantly reduced contaminant levels. These findings are utilized as a basis for a process for recovering chromium from secondary source materials.

Jan 1, 1984

By E. R. Dean

A wire-feed mechanism has been employed to fabricute metal alloy film resistors to various sheet resistivities on oxidized silicon substrates. The effect of several thousand hours storage in air at elevated temperatures on the resistance and temperature coefficient of resistance is presented. Unprotected films of- sheet resistivity between 100 and 500 ohms per sq fabricated at 300°C substrate tenzperatures were unstable when stored at 150°Cfor extended periods. The higher sheet resistivity films exhibited the greatest instability; however, even the 100 ohms per sq films drijted excessively for device application. When stored at still higher temperatures, the normalized resistance increases to maximum, then decreases until a minimum value is obtained, then finally increases in resistance until open. The use of a protective overcoating of SiO has had considerable benejicial effects on the film stability, so that 250 ohms per sq films deposited on 300°C substrates are now stable after 1000 hr storage at 250°C and possess a temperature coefficient of resistance less than 200 ppm per C. The use of a low substrate temperature during depositon (100°C) enables the preparation oj resistors with very low tenperature coefficients of resistance (10 to 20 ppnl per &apos;C). However, these films are less stable than their higher substrate temperatuve counterparts. During extended storage, the resistance of the protected films always decreases with lower substrate films exhibiting larger normalized resistance decreases. This resistance decrease is accompanied by a linearly related increase in the temperature coefficient of resistance. The electrical behavior of these films may be explained by postulating That the structure of the films is in the transition region between thick continuous films and ultrathin island structure films so that the conductivity is the restlt of both electron scattering and tunneling-activated charge carrier creation between neighboring grains. The annealing behavior when thermally aged is the result of defect anneal, grain growth, and selective oxidation. TheRE is a considerable interest in thin metallic films for use as resistor elements in microelectronic circuits.1,2 These resistor films must be stable when exposed to elevated-temperature storage or operating ambient, possess low temperature coefficients of resistance (hereafter referred to as T.C.R.), and be of a high enough sheet resistivity to be useful. The resistivity and T.C.R. of a thin metallic film are determined by the structure and thickness of the film. Hence the stability of the film when exposed to stress would depend on the stability of the structure. The resistivity of a thin film is the result of the electrons&apos; interaction with the lattice vibrations (electron-phonon scattering), scattering of electrons due to impurities, defects, and grain boundaries and specula reflection from the film surfaces.3&apos; All of these effects serve to reduce the electron mean free path and result in a resistivity higher than the ideal bulk. In ultrathin films possessing essentially an island structure consisting of a planar array of aggregates separated by a few to a few tens of angstroms, conduction is dominated by a combination of tunneling and activated charge carrier reation. Thin films would be characterized by relatively low resistivity, positive T.C.R., and reasonable structure stability whereas ultrathin films possess unstable structures, negative T.C.R., and exhibit high resistivity. Feldman6 has investigated films intermediate between the two regions and postulates that the resistivity of a film in the transition region is composed of two linearly additive parts: that due to the resistance of the grains and that due to the gaps. The grain resistivity would represent the scattering of the conduction electrons by defects, surfaces, and phonon interaction while the gap term represents the tunneling contribution. For gold and platinum films, he found as the film structure becomes progressively less continuous, corresponding to thinner films, the absolute value of the T.C.R. becomes progressively smaller until negative values are observed with respective zero T.C.R.&apos;s at about 35 and 150 ohm per sq, respectively. Recently the author7 investigated the behavior of a multicomponent alloy of nickel, chromium, and iron and found the T.C.R.&apos;s of these films decrease with decreasing substrate temperature during deposition. The lower T.C.A. associated with lower substrate temperatures was attributed to an increased contribution to the total resistivity from the negatively temperature-dependent gap tunneling since it is well-known that thin films deposited on low-temperature substrates consist of a higher density of smaller grains than the same sheet resistivity films deposited on higher-temperature substrates. Under conditions of thermal anneal, the author found that, when various sheet resistivity films fabricated at 300°C substrate temperature are exposed to extended storage in air at 300°C, the thinner films increase in resistance until open, while the thicker films

Jan 1, 1967

By K. E. Manchester, C. B. Sibley

The feasibility of doping silicon to produce device structres by directly implanting impurity atoms has been demonstrated. Both phosphors and boron ions have been successfully implanted in silicon to produce electrical junctions. Junctions as deep as 1.2 p have been produced by phosphorus ions having energies the order of 80 kev. An electromagnetic separator has been used to controllably produce uniform, large-area implantations for evaluation experimentation. Correlations between junclion depths and ion energies huve been obtained. Orientation effects have been observed and it has been found that the (110) direction is the easy direction for implanting. Monitoring of thermal treatments oj implanted substrates by sheet-resistance measurement indicates a very mild thermal anneal removes most of the damage done during the implantation. These indications are further substantiated by reverse-current measurements of j,inctions Produced by implantation. Electrical characteristics of implanted junctions are compared with those of diffused junctions. We have been interi n the interaction of energetic ions in the III-V groups, in particular boron and phosphorus, with single-crystal silicon to produce type conversion for possible device use. A number of investigators, a few of whom are avies, Kornelson,3 and so forth, have reported on penetration of energetic ions into both amorphous and crystalline solids. While most work has been done with ions of the rare gas and alkali metal groups, some work has been reported by ing, erber,&apos; and others6 in which ions of the 111-V groups have been implanted in single-crystal silicon. A large amount of this work has been done with ion energies in the 100-kev to 1.5-Mev range. An excellent review article has been written by caldin. We have concentrated on ion energies which are in the 10 to 80 kev range, with which over 1500 implanted junctions such as the one shown in Fig. 1 have been produced in silicon substrates with both phosphorus and boron ions. Fig. 1 is a 3-deg angle lap in which the n type area produced by 66 kev P is delineated and the junction is 9500A below the surface. EXPERIMENTAL Implantations reported in this paper were made with the ion source adjusted to produce ion currents in the range of 1 to 2 pa with accelerating voltages varied from 10 to 40 kv. When using doubly charged ions this produced 10 to 80 kev ions. This allowed substrate temperatures to remain below 100°C. Sam- ple movement resulted in beam impingement angle variation of 7 deg from the normal to the substrate surface. Substrate resistivities have been varied through the range of 0.001 to 500 ohm-cm and specimens oriented in three directions, (110), (Ill), and (loo), within 12 deg. RESULTS For the purpose of this paper, discussion of results will be limited to phosphorus implantations with mention of results for boron-implanted silicon. Similar results have been obtained for boron and will be reported at a later date. In Figs. 2, 3, and 4 depth penetration is shown

Jan 1, 1967