By Bin Xu, Qian Li, Xin Min, Xiaoliang Liu, Yongbin Yang, Tao Jiang, Yan Zhang

The ringing characteristics of acid and alkaline iron ore pellets powder in kiln were studied by the thermodynamic calculation using software FactSage7.0, roasting experiments using briquetting method and analysis of SEM-EDS. The thermodynamic calculation demonstrated that liquid phase could be generated from alkaline pellets powder at a lower temperature and the amount of formed liquid phase was much more than that from acid pellets powder at the same temperature. Roasting experiments indicated that the compression strength of alkaline pellets powder briquettes were also higher than that of acid pellets powder briquettes. Additionally, the analysis of SEM-EDS suggested that the alkaline pellets powder briquette presented more liquid phase and a more compact structure comparing with the acid pellets powder briquette, which was consistent with the results of thermodynamic calculation and roasting experiments. Hence, in comparison with acid pellets powder, alkaline pellets powder is much easier to ring in the kiln.

Mar 1, 2017

By Jinsheng Wang, Wei Lv, Xuewei Lv, Pingsheng Lai, Jie Dang

The isothermal reduction kinetics of vanadium titanium magnetite sintering ore was investigated by thermo-gravimetric analysis at a temperature range of 1123–1223 K under 30% CO + 70% N2 gas mixtures. The apparent activation energy of reduction was calculated by iso-conversional method and its value is 36.7 kJ/mol. The model function describing the reduction mechanism was discussed by Sharp analysis and the results revealed that the reduction process is controlled first by random nucleation and nucleus growth mechanism (RNNGM) as reduction degree is lower than 0.5, followed by the mixed influence of RNNGM and phase boundary reaction when reduction degree is higher than 0.5.

Mar 1, 2017

By Mitsutaka Hino

The contents of gangue minerals, such as Al2O3. P2O5, crystalline water and so forth in the iron ore imported to Japan tend to increase year by year. Though the increments of such gangue contents arc approximately 0.1-0.2 mass%, some problems for the blast furnace operation in ironmaking process have already been reported, In order to clarify the mechanism of harmful effect caused by the small increment of gangue minerals, mainly Al2O3. on the blast furnace operation, the dripping behavior of Fe,O-CaO-SiO2-Al2O3-MgO slag from the iron funnel, which simulated the micro-porosity in sinter ore, has been observed with the wide range of basicity, Al2O3, Fe2O and MgO contents. The effect of MgO on the dripping behavior of slag has been summarized in this paper. It was found that the addition of 2mass% MgO resulted in large increase of hold-up on the most of the conditions. When Fe2O content was less than 20mass% and the basicity was lower than 0.8, MgO lowered the hold-up even if the slag contained 10mass% Ah03. Every slag hold-up showed the minimum at the basicity of less than unity on the conditions of constant Fe2O and Al2O3 contents, This trend became remarkable when the slag contained 2 mass% MgO.

Jan 1, 2003

By Klaus Bauckhage

Phase-Doppler-anemometry (PDA)-measurements have to be taken from representative measuring positions from inside the spray cone, helping - with the support of simulated data of improved process models - to describe the multiphase flow situations within the spray cone - and accordingly to that - the heat transfer conditions for the rapid cooling and (partly) solidifying melt droplets before their impact onto the substratddeposit. Simulations and PDA-measurements thus give the base to confirm the hypothesis of the existence of a semisolid mixed-layer and it's influence on the resulting material structure during compaction. The dispersed particles in the spray cone exhibit a cooling and solidification process within a split of a second, which leads - as far as the particles solidify - to a dendritic structure with very short dendritic arm spacings. This causes within the particles extremely short distances for the following equalizing diffision processes taking place on a high temperature level (between liquidus and solidus) in the semisolid mixed-layer of the deposit and explaining the short residence times within this zone of only seconds up to a few minutes. This and the fact that the globular structure of the mushy zone (in the semisolid mixed-layer) leads to an unidirectional crystallization process over very short distances also explains the chemical and morphological ,homogeneity of the sprayed material. The dynamics of these process steps, the very special buffer function of the mixing layer during parameter variations as well as the controlled cooling process of the preform in order to avoid hot cracks influence the quality of the material. Due to the necessity of measuring and controlling the particle bound mass-, momentum- and enthalpy- fluxes to the deposit the PDA-technique has been adapted and modified in order to receive in-line and (in the future) also on-line data from the dynamics of the multiphase flow conditions within the spray chamber.

Jan 1, 1999

By Hongfa Hu, Stavros A. Argyropoulos, Stephan Ferenczy

"Physical as well as mathematical modeling was carried out to investigate the exothermic mass transfer in liquid metal systems. In these systems, the exothermicity induces unique heat, mass and momentum transfer phenomena. Moreover, these phenomena are deeply coupled and they are further complicated by the presence of a moving boundary.In the physical model used, ice cylinders were immersed into sulfuric acid solutions, because the intermixing of ice with sulfuric acid is very exothermic. In this low temperature system, velocity and temperature measurements in the sulfuric acid were made as well as measurements of the ice melting in the sulfuric acid.The mathematical model developed solved simultaneously the heat, mass and momentum equations numerically, utilizing the control-volume finite difference approach. The enthalpy method was adopted to track the moving boundary. Predictions made by the mathematical model were in close agreement with the results obtained by the physical model.The results from the mathematical model were further validated with experiments involving high temperature liquid metals. Specifically, data were obtained in an experimental setup involving (a) dipping silicon cylinders into high carbon liquid iron and (b) dipping nickel cylinders into liquid aluminum. Results from these experimental studies supported the predictions of the mathematical model."

Jan 1, 1999

By J. D. Sloop

This paper discusses the current state of EAF dust recycling at AmeriSteel's Dust Processing Division in Jackson, Tennessee. Included are a brief history of the plant, a description of the facility, a description of the process, and operating data.

Jan 1, 2000

By Esperidiana A. B. Moura, Elizabeth Carvalho L. Cardoso, Glauson Aparecido F. Machado, René R. Oliveira

Plastics global annual production exceeds 250 million tons and more than 40% of the total plastic production is used as packaging materials. In recent years polymeric materials derived from biomass have received great attention due to scarce petroleum resources and environmental concerns. PLA is one of the most extensively studied bio-based and bio-compostable aliphatic polyesters; nevertheless, high brittleness and low toughness limits its application. Blending PLA with PBAT (Poly(butylene adipate-co-terephthalate)), an aliphatic-aromatic copolyester, was the solution found due to its high toughness and biodegradability. Differences between PLA and PBAT solubility parameter values lead to the formation of immiscible blends as well as reduction in their mechanical performance besides a poor morphology; so, 5% of pre-irradiated PLA and a previous compatibilized PLA/PBAT (EcovioTM) were added to PLA/PBAT blends in order to improve miscibility phases. Investigations were accomplished on phase morphology (SEM), mechanical properties, thermal behavior and X-ray diffractions (XRD).

Mar 1, 2017

By Cledwyn Mangunda

Mining operations generate Acid Mine Drainage (AMD) that poses a significant threat to the natural environment. AMD treatment using Ca(OH)2 leads to the precipitation of a sludge dominated by a mixture of ferri-oxyhydroxides. This sludge has poor dewatering tendencies and is deposited in landfills with potential for metal remobilization. This study investigated the dewatering behaviour of a precipitate formed during elevated temperature treatment of a primary, pre-settled sludge from the neutralisation of aqueous acidic Fe2(SO4)3 and Ca(OH)2 solutions in an MSMPR reactor. The resulting treated precipitates were analysed for micro-properties, with results showing that an increase in the secondary reactor temperature from 25 °C up to 50 °C led to an increase in mean particle size, a decrease in the number of particles and improved dewatering behaviour at a ferric concentration of 300 mg/L. This was ascribed to the attainment of a circum-neutral surface charge that favoured agglomeration and a change in micro and nano-structure that allowed for better water passage.

By J. A. Holmes

Due to varying and complex mineralogy, the flotation tailings from the Chingola Concentrator have, for some years, contained upwards of 0.4% acid soluble copper. In 1968, an investigation was initiated, to determine a method for recovering this acid soluble copper. This initial investigation concluded with a recommendation to install a leach-solvent extraction-electrowinning plant at Chingola, to treat up to 900 000 tonnes of material per month, for an additional copper production of some 4 500 tonnes per month. The process consists basically of six stages :- Materials reclamation handling and preparation, acid leaching in air agitated pachucas, solid-liquid separation by countercurrent washing in thickeners, solution concentration and purification by solvent extraction, copper recovery by electrowinning, and residue neutralisation and disposal. This paper describes the development of the main parameters for design of each of the six sections, and gives details of the final plant design. Problems encountered in commissioning and initial operations are commented on, particularly insofar as they indicated any errors or misjudgements in the design. The choice of materials of construction is commented on in some detail.

Jan 1, 1976

By Muammer Kaya, Sait Kursunoglu

"The aim of this study was to investigate the effectiveness of ascorbic (C6H8O6) / oxalic (C2H2O4) acid as a reductant for the simultaneous recovery of zinc and manganese from a spent and mixed zinc-carbon and alkaline battery powder in sulphuric acid leaching. The effects of sulfuric acid concentration, ascorbic/oxalic acid dosages, reaction temperature and leaching time on the zinc and manganese dissolutions were investigated according to 2k full factorial experimental design; then, a simple optimization study was carried out for the best reductant. The optimum reductive acid leaching conditions were determined at 3 hours leaching time, 70°C leaching temperature, 0.5M sulfuric acid concentration, 13 g/L ascorbic acid dosage, 1/20 g/mL solid/liquid ratio and 200 rpm stirring speed. Under these conditions, the dissolution efficiencies were 99.9% for Zn and 99.3% for Mn. When our results were compared with the previous results, our findings were better than previous studies.In addition, the manganese dissolution kinetics was undertaken, and the activation energy was found to be 7.04 kJ/mol. Selective precipitations of Zn and Mn from acid solutions were carried out using NaOH and KOH. Using 3M NaOH as precipitating agent at room temperature and at pH 8; 95.4% of Zn and at pH 10; 93.7% of Mn were precipitated from the leaching solution. Under the same conditions, using 3 M KOH at pH 8; 91.6% of Zn and at pH 10, 96.4% of Mn were precipitated. Based on the experimental results obtained, an appropriate flow sheet was proposed to recover zinc and manganese."

Jan 1, 2012

By C. Damiani

The Chuquicamata smelter, operating since 1952, has gone through several developing stages which have been characterized by the addition of peak technology for copper concentrate smelting (Teniente converter and Outokumpu flash furnace) with an intensive use of technical oxygen, which has permit-ted to partially discontinue the reverberatory furnace utilization. This paper shows the main indicators and operational practices at present, as well as those concerning maintenance aspects. Finally, the most relevant topics related to the future development of the smelter are mentioned with special remarks on the Decontamination Plan, which allows US to keep the high level of production, reducing the emission of contaminants according to the legal requirements in force.

Jan 1, 1993

By Masaru Imaizumi, Hiroyuki Nomura, Mitsuharu Takita

"Cast iron possesses many superior characteristics caused from precipitated graphite structure, for example, castability, wear resistance, solid lubrication, damping capacity. But the more graphite hyper-eutectic cast iron contains, the lower its mechanical strength becomes, because graphite gives a negative effect to strength of cast iron. In addition, primary graphite tends to segregate during solidification, so uniform materials are difficult to be produced.In this study, authors introduced semi-solid processing in developing new and high quality cast iron. A series of semi-solid processing experiments were carried out to clarify the effect of stirring condition; solidification temperature and etc. on microstructures and characteristics of cast iron. In particular much attention is paid to the appearance of ternary eutectic zone at the final stage of solidification. As the results advanced hyper-eutectic cast iron was obtained with high quality of both the mechanical strength and wear resistance. As for the mechanical strength, 300MPa and 0.60% are obtained as the tensile strength and the elongation values, respectively, under the controlled stirring condition. This indicates that semi-solid processed hyper-eutectic cast iron is used prospectively without spheroidization.IntroductionCast iron has various good properties such as wear resistance, solid lubrication, damping capacity and machinability. The characteristics of cast iron are mainly decided by graphite structure, namely graphite shape and its distribution in the matrix. Mechanical strength of cast iron is large in the case of small quantity of graphite particles which are precipitated uniformly, however, it becomes small in the case of large quantity of graphite precipitated flakily."

Jan 1, 2000

By E. N. Mounsey

The paper addresses the design of the Zhong Tiao Shan Company (ZTS) Houma Ausmelt Technology copper smelter in People's Republic of China. The smelter represents the third copper smelter development using Ausmelt Technology, the first large scale (35,000 tpy blister copper) and the first smelter to use the Ausmelt Technology smelting and converting process steps in separate TSL vessels in a continuously operated process. The project will be realised through the combined efforts of ZTS, Ausmelt and ENFI, the Beijing Non-Ferrous Engineering Institute who provided partial detail engineering services in China. Ausmelt will provide the technology licence, basic and detailed furnace engineering packages and additional technical services including cold commissioning support and hot commissioning supervision.

Jan 1, 1999

By Germán Richter a

To comply with the chilean air quality regulation requirements, the Hernan Videla Lira Smelter which is a custom smelter having to cope with a wide variety of concentrates, has developed a two-step modernization plan. The main steps are: - A second acid plant of 80,000 Nm3/hr to be operating at the end of 1996. This will increase the sulphur capture from 43% to 701/o in association with the replacement of the Hoboken converter by a second PS-converter to reduce the operation problems resulting from the treating of high garde matte. - Oxygen enrichment, is going to be incorporated in 1998 in the Teniente Converter and PS-converters in association with tuyere injection of dry concentrates, increasing the sulphur capture to 90 - 93% of sulphur inputs. By this program, sulphur emissions will be decreased from 40,000 tpy today to less than 8,000 tpy and in this way to carry out the environmental regulations.

Jan 1, 1996

By Asmo Vartiainen

Background of Direct-to-Blister Flash Smelting is discussed; especially slag chemistry relating to copper solubility, slag fluidity and impurity behavior. In December, 2000, Mini-pilot Flash Smelting test runs were carried out at Outokumpu Research Oy to produce blister copper from Chilean concentrate and white metal and from a mixture of them. Tested slag types were iron silicate slag, ferrous calcium silicate slag and calcium ferrite slag with different slag compositions and different concentrate/white metal ratios. The test runs were successful. The fluxing effect of copper oxide was clearly demonstrated and ferrous calcium silicate slags remained fluid on a very wide liquidus range. The distribution of arsenic between ferrous calcium silicate slag and blister copper is much higher than between iron silicate slag and blister copper. This successful test run with the new slag type offer new possibilities in Direct-to-Blister process design.

Jan 1, 2003

By W. Persson

The first installation at a copper smelter of a Semtech OPC System for continuous, on-line production control of copper converting in PS converters took place in 1994. At present OPC systems are installed at 19 PS converters. The technology presents to the operator real-time information on the progress of the process he is controlling in the form of optical process parameters, thus facilitating dynamic process control. The optical process parameters are based on time- and wavelength resolved registrations of the light emitted by the off-gas flames and identification of correlation between these parameters and characteristic metallurgical process data. The present paper provides a description of the technology as seen by the furnace operators and a summary of operating experiences made during five years of full-scale, operation at various smelters, reviews influences from the technology on smelter operational practises and comments on recent developments as regards new applications of the technology.

Jan 1, 1999

By A. W. Worcester

The plant is designed to produce 60,000+ tons of refined lead per year from a nominal feed consisting of 110,000 tons of SLI and industrial batteries, and 10,000 tons of lead contained in drosses and scrap. The plant will also produce as by-products polypropylene chips and detergent grade sodium sulfate, using the Engitec Impianti CX Technology. The battery separation circuit will consist of a battery breaking hammermill and a vibrating screen with water sprays to separate the battery paste from the grid metal and other battery components. The battery components, consisting of ebonite, and separator materials, will be separated' from the grid metal and classified with the use of hydrodynamic water separators. The battery paste will be treated with sodium carbonate to produce a lead carbonate paste for smelting in a reverberatory furnace. The slag from the reverberatory furnace will be campaigned through a traditional primary blast furnace to produce hard lead. The sodium sulfate liquor from the lead carbonate filtration step will be crystallized to produce anhydrous sodium sulfate. The metallic grid metal will be treated through a small rotary smelter of the Engitec design to produce a hard antimonial lead. The plant's scheduled to be commissioned 12 months after receipt of all of the Federal and state permits. The plant will be integrated into the Buick Primary Lead Smelter, located in the center of Missouri's New Lead Belt, at Boss, Missouri. This will allow The Doe Run company to fully utilize all of its existing assets.

Jan 1, 1990

By R. M. Taylor

Lime addition to acid mine drainage (AMD) leads to precipitation, predominantly of metal hydroxides and calcium sulfate, and is the benchmark for remediation by precipitation. Geo2 Limited of Melbourne, Australia has developed and patented a novel alternative precipitation scheme based on the formation of mixed valency, M(I1)-M(III), hydroxide sulfate salts. When the composition of AMD is appropriate, the Green Precipitate Process provides a useful and more effective alternative to conventional liming. The characteristics and utility of the Green Precipitate Process are described in terms of the underlying chemistry, and a case study where the Green Precipitate process outperforms conventional liming. A mobile pilot pipe reactor rig which was built by Geo2 to demonstrate the process, and used successfully in both Australia and the United States, is described.

Jan 1, 1998

By R. Shimpo

Equilibrium calculations by a computer may sometimes fail in giving solutions when the system includes a large number of components and more than three phases, and especially when no definite information about stable phases is given. An improved method of calculation is presented in which the number of phases need not to be initially fixed, phases can appear or disappear in the course of' calculation and a new method is combined with the Newton-Raphson method to obtain solutions easily. The improved method is applied to the copper smelting operation and all the successive stages of the operation are successfully simulated.

Jan 1, 1983

By A. Rios

ENAMl's Paipote Smelter commenced operations in 1951. At present, it processes 230,000 tonnes/year of green feed in a conventional smelter, which comprises one reverberatory furnace, two Hoboken, one Peirce-Smith converters and one rotary anode furnace. The feed is composed of 83% copper concentrate and 17% metallic copper precipitates, which results in a feed average grade of 32% of copper content. The final products are 75,000 tonnes/year of copper anodes and 48,000 tonnes/year of sulphuric acid. At present, the plant is undergoing a modernization to expand the smelter capacity to 300,000 tonnes/year of green feed and increase the sulphuric acid production to 100,000 tonnes/year. This will be achieved with the installation of an El Teniente Converter and an expansion in the acid plant. The work began in November 1991 and is scheduled to be in operaton by March 1993. The paper provides an overview of the modernization plans and results achieved to-date.

Jan 1, 1993