Search Documents

By W. Bonfield

The microstrain characteristics of a polycrystal-line Cu 1.9 wt pet Be precipitation-hardening alloy have been determined for various conditions of aging. The friction stress remained constant for all the conditions investigated, whereas the microscopic yield stress (the stress to produce a plastic strain of 2 x 10-8 in. per in.) and the three-stage stress-strain curve in the microstrain region were sensitive to changes in dislocation and precipitate distribution. Correlations between the measurements of microplasticity and electron-nzicroscope observations of substructure are considered. ALTHOUGH the macroscopic mechanical properties of Cu 1.5 to 2.0 wt pet Be precipitation-harden ing alloys were established' in some detail, there has been no previous investigation of the nature of microyield-ing in these alloys. This paper describes a high-sensitivity extensometer determination of microplasticity in polycrystalline Cu 1.9 wt pet Be, in which the friction stress, the microscopic yield stress (the stress to produce a plastic strain of 2 x 10-6 in. per in.), and the rate of strain hardening in the micro-strain region were measured for various conditions of precipitation. The structural changes accompanying aging in this alloy were examined using transmission electron microscopy, a study which differed from previous investigations as, in order to minimize grain boundary precipitation effects,' the solution-treated alloy was cold-rolled to 40 pet reduction prior to aging. Hence the extent of recovery and recrystalliza-tion, as well as the variation of precipitate morphology and distribution, were assessed. From these results possible correlations between the microstrain characteristics and the observed precipitate and dislocation structure are considered. EXPERIMENTAL PROCEDURE The material investigated was a commercial copper beryllium alloy (Berylco 25), which had a com- position of 1.9 wt pet Be and 0.2 wt pet Co. The alloy was solution-treated at 800°C, quenched in water, and then cold-rolled to 40 pct reduction. Tensile specimens of gage length 1 in. and rectangular cross section of 0.18 by 0.06 in. were prepared from the solution-treated, cold-rolled material and aged for 15 min, 2, 24, and 100 hr at 315°C and 24 hr at 425°C to produce a range of precipitate structure. The hardness values associated with these conditions are listed in Table I. It can be seen that a maximum value is obtained after 2 hr at 315oC, which decreases with continued time at temperature to a minimum after 24 hr at 425°C. For comparison some as-solution-treated specimens were also aged for 2 hr at 315°C. The specimens heat-treated to a given condition were examined in two ways. First, the nature and distribution of the precipitate and dislocation structure was characterized using transmission electron microscopy. Thin foils were obtained from the specimens by electrolytic polishing in a 30 pet nitric acid-alcohol solution at -20oC, and were examined in an RCA EMU 3 electron microscope. Second, the mi-croplastic behavior of the specimens was measured with a Tuckerman strain gage, using the load-unload technique previously described2, 3 to determine the friction stress, the microscopic yield stress, and the variation of plastic microstrain with stress. RESULTS 1) Structural Changes During Aging. a) Annealing Processes. The solution-treated, cold-rolled Cu 1.9 wt pet Be had an irregular dislocation-cell structure,

Jan 1, 1968

By J. D. Pennock

The different samples of brick examined were Grecian magnesite, American magnesite; silica brick and coke-oven tiling made in Belgium and used in retort coke-ovens. The Grecian magnesite was furnished by a New Pork party. The American magnesite and the silica brick were furnished by a manufacturing company in Pittsburgh. From these brick were made cylindrical cores, '79 inches long and 15/8 inches in diameter. At one end of each was drilled a hole about 1/4-inch in diameter and 11/4 inches long, into which the thermometer was inserted during the experiment. Conductivity.—The apparatus used for determining the conductivity, as shown in Fig. 1, is a sheetriron drum, 18 inches in diameter and 8 inches high. In the center is a little combustion-chamber with walls of split fire-brick, 39 inches square and about 6 inches high. The fire-brick, however, pass through the drum to the table on which the drum stands. The cores are placed horizontally, half-way between the top and bottom of drum and on the line of diameters at right angles. In the four walls of the combustion-chamber are cut holes just large enough to allow the cores to pass through. The cores extend

Jan 1, 1897

By AIME AIME

CHARLIE WARNER, Chairman of the Petroleum Division, is no stranger to the problems of the oil industry or to those of the Petroleum Division, after more than 25 years of experience in locating and producing oil and more than 22 years of membership in the Institute. He was born at Jefferson, N. Y.. April 27, 1894, and educated in the public schools of New York State and at Cornell University where he studied geology and allied sciences from 1913 to 1917 and received a B.A. degree. Immediately upon completion of this training, he was employed by the Empire Gas & Fuel Co. as a field geologist in Oklahoma and Kansas. Two years later he became district geologist for the Emerald Oil Co. in Oklahoma and Kansas, and in 1920 he rejoined the Empire Gas & Fuel Co. in the capacity of district geologist in Oklahoma. In September of 1921 he began his association with the Houston Oil Co. of Texas. He was district manager for the company in the Mid-Continent area until 1932 when he was transferred to the head office at Houston, where he became superintendent of the land and lease department in 1934 and was elected a director of the company in 1941. In these capacities, and also as petroleum engineer for the company, he keeps in intimate touch with all phases of field activity and with the regulation of the industry by State and Federal agencies.

Jan 1, 1943

By F. R. Hensel

ACCORDING to statements by Guertler,1 Smith and Hamilton were the first to study the copper-titanium alloys, but owing to the presence of large amounts of impurities their data are inconclusive. M. A. Hunter and I. W. Bacon later investigated the electrical conductivity and the temperature coefficients at room temperature. The present writers reported their results2 in November, 1930. Recently Droll published data on copper-titanium alloys3 which agree closely with those obtained by the authors. MATERIAL TESTED The titanium used was in the form of square sintered rods, the analysis of which runs as follows: titanium, 95.4 per cent; silicon, 0.7; iron,1.8; aluminum, 1.4; copper, 0.1; manganese, 0.05. . The ingots were prepared in a high-frequency induction furnace in air atmosphere. Their analyses are given in Table 1. Up to 5 percent titanium the alloys could be forged. Above that amount they were red short and broke up easily. Owing to their rapid absorption of nitrogen and oxygen from the air, the alloys with the higher amounts of titanium tend to form surface films which greatly increase the casting difficulties, especially when small masses of metal are handled. It was, however, possible to prepare sound ingots up to 25 per cent titanium.

Jan 1, 1931

By Gene Long

10.4-1. Load Design and Construction. Surface mine haulage roads are used for transporting raw products to the mine site, preparation plant, or loading facilities, and to provide personnel and equipment an access to the pits and mine area. All of the aspects of highway engineering, including minimum slope inclines, properly banked curves, and adequate drainage, must be followed to facilitate construction of safe and efficient haulage roads for fast and economical transportation of the mined product to its destination. By maintaining good haulage roads, both truck and equipment maintenance will be kept to a minimum, resulting in reduced mining costs and subsequently higher profits. [ ] There are several basic considerations in haulage road planning. Most important, one must follow all safety procedures in both design and construction of the roadway. A maximum effort should be made to follow current mining plans when laying out and planning haulage roads (aerial photographs can be extremely useful in planning and routing of roadways). Grades, road widths, and curves must be maintained within limits of present and/or planned haulage equipment specifications, since all these factors can limit speed, and hence production (Table 10.4-1). Grades in most mining operations are adverse (against the loaded haul), which increases haul cost per mile. Operators must balance these increased

Jan 1, 1968

INDEX TO TRANSACTIONS After a delay of many months, which is very much regretted, but which, it is hoped, will be one means of insuring a volume of accuracy where accuracy is very important, the Institute now has for distribution copies of the index of Volumes XXXVI to LV, inclusive. This is more than a mere index off names of authors and titles of papers. Every important topic under consideration by author or discusser is introduced under such key-word as will enable an engineer to locate the desired information with the minimum expenditure of time. This index sells for $5* in half morocco binding and $4*. in paper covers. With the index of Volumes II to XXXV (which sells for $5 in half morocco and $4 in paper covers), it forms a complete index of the first fifty-five volumes of the Institute's Transactions. These collective indexes are very valuable to members of the Institute, enabling them to look up matters in their own library; if they have the volumes to which the indexes refer, they can get the information at once, and, if not, they can readily determine whether or not a visit to a nearby public library is desirable.

Jan 7, 1918

By A. T. Tye

WHEN the roughing tables operated in 1923 were abandoned, all the coarse iron pyrite for-merly removed by the tables had to be ground to flotation size, which caused an increased power con-sumption of 2 kw.-hr. per ton. Recently, by increasing the tonnage, this has been reduced to a total of 16.6 kw.-hr. per ton. The cost of repairs has been slightly reduced by using an alkaline circuit instead of the acid mine water used in 1923. Other economies from elim-inating roughing tables and the finishing tables have more than compensated for the extra grinding and the total costs have remained practically the same, until the first part of 1927, when, with increased tonnage, the total cost has decreased to 72 cents and the repair cost to 9 cents. In 1923, with a combined gravity and bulk flotation flowsheet, the grade of concentrate was only 4.38 per cent copper. With preferential flotation this has in-creased to over 17 per cent copper. The tailing has decreased from 0.29 per cent -copper to 0.18 per cent. The copper recovery, instead of decreasing; as might be expected, has increased from 87.4 per cent to, 91.5 per cent. The silver recovery has also increased from 88

Jan 8, 1927

By I. R. Kramer

The apparent activation energy, U, JOY plastic deformation of aluminium, copper, and gold single crystals and polycrystalline aluminum was found to he dependent upon surface condition. At low strains, the value for U for aluminum single crystals was 4200 cal per mole ; however, this value decreased to 920 cal per mole when the specimens were polished during the test at a rate of 50 X 10-5 win-1 The activated volume also was found to increase with the rate of metal removal. That the surface plays an important role in plastic-deformation processes has been adequately demonstrated.1-4 Of particular interest at this time are the observations4 that the creep rate of single crystals of fee metals is increased markedly when specimens are polished during the deformation process. These observations were interpreted in terms of a dislocation debris layer at the surface regions of the crystal. This layer, which appears to be a region containing a high concentration of dislocations or segments of dislocations, not only will impede the egress of dislocations on the primary slip system, but will also provide a barrier against which dislocations may pile up. By this means, a stress which opposes the motion of dislocations will be generated. It is considered that this stress must be taken into account in any theory which describes the plastic-deformation process. Although a detailed dislocation model cannot be given at this time, it may be stated that the stresses opposing the motion of dislocations arise from the dislocations in the debris layer, Ts, and ti due to the resistance to motion imposed by internal obstacles such as Lomer-Cottrell barriers, subgrain and grain boundaries, forest dislocations, and so forth, as well as the resistance due to the presence of jogs on dislocations and the interaction of the stress fields of dislocations, and so forth. In essence, we have added an additional term, ts, to the usual form of the equation T = Ta- Tb, where Tb is the back stress due to the various types of obstacles which impede the motion of dislocation. Accordingly, the net stress, t, acting on a dislocation may be written as where Ta is the applied shear stress. For deformation which occurs by a thermally activated process5,8 ?=Ae-u/kT = A e(u,-VT)/kT [2] and U = Uo- Vt PI where U = activation energy for plastic flow, y = shear strain rate, Uo = activated energy for plastic deformation in the absence of stress and depends upon the particular deformation process, V = activated volume, k = Boltzmann constant, T = temperature, OK, and A = frequency factor. From Eqs. [I] and [3], U = Uo- V(Ta - Ti - TS) [4] and it is seen that if Ts decreases, the activation energy, U, must decrease if V remains constant. However, as will be shown, V is a function of the surface conditions. In their work on aluminum, Lytton and coworkers7 reported that at low strains the activation energy was 3400 cal per mole and at high strains it was 28,000 cal per mole. The lower value was interpreted in terms of the energy necessary to overcome the Peierls force, while the higher value was associated with the energy necessary for dislocations to move by a cross-slip process. It will be shown that the lower activation energy is associated with the surface debris layer rather than with the Peierls force. EXPERIMENTAL PROCEDURE Single crystals having a nominal cross section of 1/8 in. and a 3-in. gage length were prepared by a modified Bridgman technique using a multiple-cavity graphite mold. The initial purity of the metals was 99.997, 99.999, and 99.999 pet for aluminum, copper, and gold, respectively. The orientation of the specimens is given in Fig. 1. The measurement of the activation energy as a

Jan 1, 1964

By James Boyd

In critical times such as the present, when the whole world is agitated by the aftermath of war and the road to peace is blocked by seemingly insurmountable obstacles, it is fitting that we should pause to take inventory of the material resources essential to our national security. Our status as a world power, in peace as well as in war, is intrinsically bound to the availability of minerals, for the foundation of our industrial and economic structurewhich in turn largely determines our military potential and our limits of national prosperity-rests on our ready access to economic sources of iron, copper, lead, zinc, manganese, bauxite, and at least threescore of other metals, minerals, and mineral fuels. By applying the well-known facts of mineral resources to recognized fundamental concepts of preparedness, we can obtain a- clearer picture of the essential needs of our country. Historically, the lure of minerals and other raw material resources has all too frequently led nations to policies of imperialism and war. For more than a century the staking of colonial territory for new sources of raw materials has been a primary objective of many nations. These national policies. of aggrandizement were accelerated by increasing industrialization. The nations, in their aggressive search for

Jan 1, 1948

A. M. Strong, Bishop, Cal. (communication to the Secretary*) :—The paper of Mr. Eeyes gives us the most complete account of the geology of the borax-deposits in the Death Valley region that has yet been published, and is a valuable addition to the geological literature of a very interesting though little-known territory. During the past ten years I have been over much of the northern part of the country described by Mr. Eeyes and the region immediately north of it.

Jan 1, 1910

By Russell S. Sage

THE electric motor has steadily replaced the steam and air engine for use in mine hoists, until today a new installation with other than electric drive is a rarity. Much existing steam-driven equipment has been changed over to electric drive. Driving power has grown in capacity since the initial electric unit rated 10 hp installed at Aspen, Colorado, in 1888, to 3000 hp and 4000 hp in the United States, and to 5500 hp in Canada-the largest in the Western Hemisphere. Electric installations now total in the thousands of units, a growth largely made possible by the development of large central electric-power stations and the extension of electric-power service to more mining areas.

Jan 1, 1949

RUSSIA was the United States Number One source of manganese ore in 1948 when 34 pet of imports were received from that source, stated Norwood B. Melcher, assistant chief, ferrous metals and alloys branch, Bureau of Mines. In 1949, this country received only 20 pet of 1948 shipments from Russia, and only token amounts are now being received. Aggressive programming by industry and government resulted in prompt increases in shipments from major, producing sources; India, Gold Coast, and the Union of South Africa all increased exports to fill the vacuum left by Russia and provided an excess adequate to increase total imports approximately 290,000 short tons in 1949. Again in 1950, and with, even less ore from Russia, imports increased another 290,000 short tons. Since the shift from Russia as a source of manganese, the United States has received in total about 85 pet of its imports from India, Union of South Africa, Gold Coast, and Brazil in that order of importance. Producers of both home consumed and merchant ferromanganese have been able to adjust downward the manganese content of the home-consumed product and so obtain partial relief. Millions of tons of steel were produced in 1951 with a relatively low grade ferromanganese. This adjustment has been made without decreasing the quality of the steel, although with some increase in cost through introduction of new problems, including increased hand- . ding of material and additional removal of carbon. Forced into a pattern of price and grade structure such as exists today, the producer of ferromanganese must adopt one of three possible courses as a short-range program: 1-He may continue to deplete his stocks by producing standard (78 pet) ferromanganese and hope that the future will bring some form of relief; 2-he may attempt to produce 78 pet ferromanganese by paying higher prices for premium ores; or 3-he may drop the grade of ferromanganese and stretch stocks and future supplies of ore as far as possible. The present rundown condition of Indian railroads is attributed to the fact that the service has had no opportunity to recuperate since the beginning of World War II, while the demand for the movement of commodities has probably increased. The Union of South Africa has expanded its exports to the United States greatly since 1948, but, the showing of that country in 1951 was disappointing. Efforts have been made for some time by firms in the United States, at the urging of the manganese miners in the Union, to prevail on the railroad authority to grant and make available larger allocations of cars for manganese ore movement. As a whole, such efforts have been unsuccessful. Although the allocation of rail shipping has been the obvious factor in the decreased movement of ore, many other less determinate factors appear to be involved. Brazil, long an important supplier of manganese to the United States, has important manganese deposits in three areas, all of which are significant to this country. The Gold Coast is an important source of supply. Its metallurgical ore is particularly of significance because of its unusually high grade which permits considerable latitude in blending with the lower grade materials of South Africa and India. The Belgian Congo should have an output of 100,000 tons or more annually beginning this year. R. S. Dean presented two papers. One with K. M. Leute on hydrometallurgical methods for recovery of manganese from domestic ores and one as sole author on the so-called carbamate or Dean process. The two papers tied into each other. In the first mentioned he reviewed the various processes applicable to oxidized, and nonoxidized and reduced ores. The advantages of each .were pointed out. So far the only process tried on a substantial scale on oxidized ores was the SO2 process used at Las Vegas, Nev., on Three Kids ore during World War II. Many problems were encountered. Some of them were whipped while some of those remaining perhaps would have been whipped had time permitted. Since then work has been done elsewhere to avoid the formation of the troublesome thionates encountered at the Three Kids plant. Dean discussed the thionate and NO, processes as applied to oxidized ores. The only commercially used process on reduced ores is that of making electrolytic manganese. Among others that have been considered are the nitric acid process, the Bradley-Fitch ammonium sulphate process, and Dean's ammonium carbamate process. Dean's thesis was that extremely large tonnages of so-called low grade manganese ores are available, and that these should not be depleted in attempting to simulate a foreign metallurgical grade ore. He pointed out that the grade of the domestic manganese ores would be considered high if the same grade were found in copper ores. The selling price of electrolytic manganese and electrolytic copper are roughly the same. In addition to electrolytic manganese, he believes that domestic ores should be used to make exceptionally high grade products. These might be battery grade oxide or substantially pure oxide sinter, which might be used for high manganese alloys or for upgrading metallurgical grade manganese to produce a high manganese ferroalloy. The carbamate process is based on the fact that manganous oxide is readily soluble in concentrated ammonia solutions containing ammonium salts. In solutions of sufficiently high concentration the manganese exists as an anion. Lixiviants of ammonia and ammonium carbonate permit extraction of the manganese from reduced ores and the manganese can be recovered as carbonate by heating or by driving off ammonia. R. V. Lundquist presented a paper on upgrading high-silica ores or concentrates with sodium hydroxide to extract silica and to yield a product with a more favorable manganese: silica ratio. The NaOH is, regenerated in part by CaO.

Jan 1, 1952

By R. L. Schmidt, J. D. Verhoeven

The diffusion coefficients and electrotralzsport mobilities of aluminum, gallium, and arsenic have been determined in molten germanium with the capillary reservoir technique. The diffusion coefficients are slightly higher than those determined by the solidification technique of Brirton et a1.1 It was found that aluminium and gallium migrate to the cathode in molten germanium) whereas arsenic migrates to the anode under an electric field. A possible technique for producing p-n junctions by means of electric field freezing is discussed in view of the experimental data. In the past decade or so the literature has abounded with articles concerning the solid-state properties of the semiconducting elements germanium and silicon. It is surprising by comparison how little has been published concerning the liquid-state properties of these materials. In the production of doped germanium or silicon the diffusion coefficient of the dopant in liquid germanium or silicon is an important quantity. Yet, to the best of our knowledge, no one has ever made a direct measurement of the diffusion coefficient of solutes in either molten germanium or silicon. A number of authors'-4 have determined some diffusion coefficients by the indirect technique developed by Burton et al.1 This technique appears to give numbers of the correct order of magnitude but it does depend upon a number of assumptions in the analysis and also requires prior knowledge of the viscosity of the melt. In the present work a more direct measure of the diffusion coefficients of arsenic, gallium: and aluminum in molten germanium has been made. It has been shown independently by two groups of authors5, 6 that, when an electric current is passed through the interface of a solidifying metal containing an impurity, the resulting electrotransport in the liquid boundary layer at the interface offers a mechanism for control over the redistribution of the impurity accompanying the solidification. These authors show that the degree of control is proportional to the mobility, U of the impurity atoms in the liquid boundary layer, where the mobility is defined as the drift velocity relative to the solvent per unit electric field. In principle the results apply to the solidification of a doped semiconductor and offer an interesting technique for control of the doping of a semiconductor. In the present work the mobilities of aluminum, gallium, and arsenic were determined in molten germanium in order to evaluate the potential usefulness of electro-transport as a technique for solute control when applied to the solidification of doped germanium. EXPERIMENTAL PROCEDURE Both the diffusion coefficients and the mobilities were measured using high-purity alumina capillaries and a resistivity technique for analysis. A schematic diagram of the electrotransport apparatus is shown in Fig. 1 and the details of the cell design are shown in Fig. 2. For the mobility experiments electrical contact with the bottom of the capillary was made with graphite, as shown in Fig. 2. In order to prevent electrical contact with the melt the graphite was coated with a thin layer of alumina using a plasma spray torch. The cell assembly, a graphite electrode, and another assembly containing two blank capillaries were fastened to the lavite disk shown in Fig. 1. To make a run the system was evacuated and the doped germanium was outgassed at the operating temperature of 1030°C. The cell and blank capillaries were then submerged beneath the melt and a slightly positive pressure of helium was introduced to fill them. After passing current through the cell for a given time the cell and blank capillaries were raised from the melt and the furnace was shut off. The temperature of the cells dropped below the freezing point of germanium within 1 to 2 min after the furnace was shut off.

Jan 1, 1968

By C. C. Martin, M. C. Fuerstenau, R. B. Bhappu

Experiments revealed that quartz could not be floated in conductivity water at any pH with a long-chained sulfonate as collector. Various cations, Fe+++, Al+++, Pb++, Mn++, Mg++, Ca++, are shown to function as activators when the pH is such that the cation hydrolyzes. As the solubility product of the various cation-sulfonates was exceeded at the concentrations involved, precipitated cation-hydroxy-sulfonates, e.g. Fe (RSO3)2OH must be functioning as the collector in these systems. A number of interesting and important phenomena were revealed during a study of the response of beryl to sulfonate flotation.' Perhaps the most important observation is the effect of various cations on flotation response. Experiments showed that in the vicinity of pH 3.0, about three ppm Fe+++ increased recovery of leached beryl from about 60 pct to 100 pct, whereas about four ppm Ca+ + reduced the recovery from 60 pct to 2 pct. With the exception of ferric iron, all of the other cations investigated reduced flotation recoveries drastically at this pH. As postulated in the paper Sulfonate Flotation of Beryl,' even with low concentrations of polyvalent cations and sulfonate (on the order of one ppm), cation-sulfonates are precipitated immediately in solution. That is, blueish-white clouds were noted to form after given additions of salts to known solutions of sulfonate. Furthermore, it was also shown that one-hundred-fold more ferric iron than necessary to form the precipitated cloud had to be added to effect complete flotation. In other words, some form of solid ferric sulfonate was found to function as the collector in these systems. The form of the compound was suggested to be Fe(RCO3)2OH and that bonding to the surface occurs through the hydrogen of the hy-droxyl. As the form of this compound was shown to be dependent on the extent of hydrolysis of ferric iron, it is to be expected that ferric iron will be unique in some pH region. Further, if the presence of hydroxyl in the neutral precipitated compound is of primary importance, then other cations should function similarly but at different values of pH, since they will hydrolyze at different concentrations of hydroxyl ion. To determine whether the premise of hydrolysis is correct, the study was extended to quartz systems in the presence of various cations at various values of pH. EXPERIMENTAL MATERIALS AND METHOD Sodium alkyl aryl sulfonate was chosen as the collector for the experimental work. The reagent, sup plied as a courtesy sample by the Shell Chemical Co., has the following physical properties: Physical form Solid — Finely ground Sulfonate content, pct wt 95 to 97 Molecular Weight 450 to 470 Number of carbon atoms in hydrocarbon chain 25 to 30 Melting Point, OF 250 to 260 Solubility Soluble in water with gel formation at concentrations higher than 25 pct by weight sulfonate This particular reagent was chosen because of its high active sulfonate content, long-chain length, and solid form. With the exception of the frother and sulfonate, all other chemicals were of reagent grade quality. Conductivity water was used in the experimental work. This water, made by passing distilled water through an ion exchange column, had an average measured conductivity of one micromho. Experiments were conducted at room temperature in a small glass flotation cell with the following procedure: 1) A redetermined amount of water and salt solution (e.g. CaC12 . 2H2O) were combined and the pH adjusted to a given value. 2) A given amount of sulfonate was added so that final solution volume was 130 cc. 3) One drop of Dow 250 frother was added. 4) Five g of quartz were added and the system conditioned for five minutes. 5) The pH of the system was measured (termed flotation pH).

Jan 1, 1963

By B. M. Larsen, T. E. Brower, J. W. Bain

A mass of circumstantial evidence is presented to indicate that the main source of alloy losses in open-hearth tapping is oxidation by air, with the steel apparently reacting with an amount of oxygen equivalent to about 30 times its own volume of air. The effect is erratic from heat to heat, depending largely on turbulence and distance of free fall of the stream of liquid metal. THIS paper reports another phase in a general study of oxidation in the open-hearth, various aspects of which have already been discussed in previous papers.1,2,3 It is based on experiments conducted on commercial, basic open-hearth furnaces at various times when opportunity offered, beginning about 1938, in an attempt to determine the mechanism and measure the amount of air oxidation during the flow of the tapping stream through the air into a ladle. This effect is closely connected, not only with alloy losses and control of chemical analysis, but possibly with various questions regarding inclusion content and steel quality and with a true picture of the deoxidation of steel in general. Thus it is believed that discussion of a large part of the results to date may be of assistance to others who are studying problems related to deoxidation or to steel cleanliness and quality. The literature reveals that strangely little attention has been devoted specifically to the effect of pouring steel through open air. Bardenheuer and Henke4 in 1939, in a paper devoted largely to overall losses of manganese in the basic open-hearth, reported that for a number of heats tapped into a tilted ladle held just beneath the runner so that the maximum distance of drop of the stream through the air was held to less than about 30 in., there was in most cases almost no loss of manganese from furnace to ladle. Hultgren,5 in 1945, showed that in high-carbon basic electric steel deoxidized in the furnace and containing no large inclusions as it left the furnace, large silicate inclusions, often rich in manganese oxide, were present in samples dipped from the pool in the ladle; also that the rise in content of large inclusions (above 0.01 mm dim) was greater when the metal stream was made to spray or flow in a turbulent manner. Our interest in this phase of oxidation in the open-hearth was first aroused by a study of alloy efficiencies on ladle additions. The frequency curves of manganese efficiency (net recovery of metal added in ladle) given in fig. 1 are of interest in this connection. Lowest, and also most variable (47 to 95 pct), recovery was in low-carbon heats having no coal additions to the ladle, progressing upward to a maximum average and least variable (82 to 97 pct) recovery in high-carbon heats killed with aluminum and silicon. Both coal additions and higher carbon contents in the tap stream, as well as additions of silicon and aluminum, help to lower the amount of manganese loss. But the most interesting point is the amount of manganese oxidized in many heats tapped at 0.50 to 1.06 pct carbon. It has been shown in a previous paper3 that the amount of oxygen in the tap stream in such heats is very small, usually below 0.01 pct, too small to oxidize any appreciable amount of manganese. Also, the fact that manganese should be oxidized at all in a metal solution containing such more stable oxide-forming elements as aluminum and silicon is an indication of some rather intense oxidizing effect such as could be caused by reaction with the air during ladle filling. Oxygen Balances from Tap Stream to Teeming Stream: Data in the form of alloy efficiencies, such as those shown in fig. 1, are not a proper measure of such a general oxidation effect. Having available

Jan 1, 1951

By S. C. Sun, John A. L. Campbell

Objective of the ittvestigation was to determine the electrokinetic differences, if ally, of anthracite lithotypes and thus establish the feasibility of making a coqlstituent separation by froth flotation or other surface-dependent processes. The elec-trokinetic properties were determined by streaming potential methods. In addition, chemical and physical analyses of the lithotypes were made to establish nonsubjec-tive parameters for their diflerentiation. Electrokinetic results indicate a difference in the characteristics of the lithotypes. The isoelectric points of 4 anthracites and 12 lithotypes were obtained. It was suggested that the relative flotation rates of the lithotypes were pH dependent and that the maximum flotation rate of anthracite occurs in an acidic circuit. Although there has been an increased interest in the electrokinetic properties of coal,' research on the subject is still in an early stage of development."' To the authors' knowledge, no electrokinetic studies have been made on coal lithotypes, particularly anthracite litho-types. This paper presents the results of an investigation of the double layer properties displayed at the anthracite/water interface (whole coal and lithotypes) as determined by streaming potential methods. It is hoped that this investigation and related future investigations will provide correlations from which the surface properties of any coal can be predicted and then related to surface-dependent processes such as froth flotation and flocculation. Another aspect of this research, undertaken to determine the physical and chemical parameters necessary for anthracite lithotype differentiation, was previously published.? The number of parameters involved, lithologic, organic and inorganic, and the wide divergence of these parameters within an individual coal limits the practical utilization of the results; however, the result? are of value and of interest in guiding theoretical developments. Keeping the limitations in mind, the results are analyzed in terms of their application to froth flotation processes and are used to indicate the feasibility of making a lithotype separation by flotation. Experimental Procedure Prior to discussing the experimental work per se, it would be of value to establish an understanding of anthracite lithology. Anthracite Lithology: Coal seams display two different modes of variation, rank and type. A coal's position in the continuous series ranging from peats through anthracites determines its rank. The rank of the material under consideration is anthracite. The different bands of coal which constitute a coal seam are distinctly contrasted in regard to physical properties and chemical composition. These megascopic bands are the coal types and are termed lithotypes., A megascopic examination of 11 anthracites revealed three distinct, homogeneous, lithotypes. The classic description of bituminous coal lithotypes as proposed by Stope" was found to be quite adequate for recognizing the three lithotypes in anthracite, namely vitrain, durain, and fusain. The term vitrain describes the brilliant constituent of coal; durain describes dull coal; and fusain is the term applied to fossil charcoal. The anthracites studied were generally found to contain 60-80% vitrain, 10-30% durain, and 1-10% fusain. A complete description of the physical characteristics and chemical composition of the studied lithotypes can be found in a previous publication.' Sample Preparation: Nine of the anthracites used in the investigation were from Pennsylvania, one was from Russia, and one from Wales. Table 1 shows the various designations and sources of the employed anthracites. The letter V, D, or F added to the whole coal designation indicates respectively the vitrain, durain or fusain lithotype of that coal. The samples were carefully collected to avoid contamination. To insure against oxidation, the samples were obtained as fresh as possible and stored under nitrogen or water. Generally a representative sample of the seam and samples containing high concentrations of one or another of the petrographic constituents were secured for each coal. Pure lithotypes were prepared by manual separation and selection. The pure lithotypes and representative samples were ground to —35 mesh and screened to 35 x 48 mesh. The 35 x 48-mesh fraction was then passed over a magnet to remove iron contamination, washed with doubly

Jan 1, 1971

By Charles Stein

The effects of several different prior treatments an the creep behavior of 99.9995 pct aluminum at 260°C and 1000 psi canstant stress are compared with annealed specimens. Quenching from 538oC, irradiation with 2 mev electrons, and tension-compression room temperature fatigue damage were used to change the substructure of the specimens prior to their creep testing. The quenched and the irradiated specimens showed a larger primary and transient stage contribution to the creep curve than those specimens which were only annealed prim to creep testing. The specimen receiving prior fatigue damage at room temperature showed no first stage or transient creep when tested under identical conditions as the above specimens and had an average creep rate seven orders of magnitude lower than that of either the annealed, the quenched or the irradiated creep specimens. In a previous electron transmission microscopy investigationl of the substructure developed during the creep of pure aluminum at 0.57 Tm, it was noted that a large concentration of vacancy loops and dislocation loops were present in and near the subboundaries while the interior of the subgrains contained few of these defects and had a low dislocation density, see Fig. 1. Yim and Grant2 and Hazlett3 have shown that the presence in nickel of a substructure developed by prior cold work effectively reduces the primary and transient contributions to the creep curve. Hultgren,4 McLean,5 Gervais, Norton, and Grant,6 Chang and Grant,7 and others have shown the same effect with the higher stacking fault energy material, aluminum. However, the specific defect responsible for the change in the creep behavior developed by the prior cold work was not established. Specifically, what effectively interfered with dislocation motion in these materials at elevated temperatures? Was it jogs on dislocations produced by their interaction with other dislocations or with vacancy or dipole loops, see Fig. 1, or did the subgrain walls determine the mean free path for glissile dislocations? This would be a realistic possibility only if subgrain boundaries are effective barriers to dislocation motion. The ability of a subgrain boundary to act effectively against glissile dislocations depends on the number and the arrangement of dislocations in the subboundary,8 which in turn is a function of the creep strain.' This paper compares the creep rate of specimens possessing a large vacancy concentration to that of annealed specimens and with specimens having a stable subboundary wall containing Lomer locks produced by prior fatigue damage. EXPERIMENTAL PROCEDURE Vacancy Loops. Aluminum creep specimens, 99.9995 pct pure, were machined from zone refined rod to a 2-in. gage length and a cross-sectional area of 0.025 in. These specimens were annealed at 538oC, 1000°F, for 10 min and quenched into ice water. They were then reheated to the creep test temperature of 260°C, 500°F, and held at this temperature for 18 min to al-low for vacancy condensation and loop formation. The specimens were subsequently creep tested at 1000 psi constant stress at 260°C. The temperature along the gage length was monitored by three Pt-Pt, 13 pct Rh thermocouples, two embedded in the upper and lower shoulders of the specimen and one attached to the mid-point of the gage length- The temperature gradient was held to ± l°C or less throughout the Creep test. Elongations were measured by two LVDT's 'connected in an averaging 'On-figuration, with quartz extension arms placed against the specimen at the extremes of the 2-in. gage length. i K 3J?--' * *H - >^> - ' ^L r 77 . *y J OJL, J Fig. 1—Transmission electron micrograph of pure aluminum strained 8.2 pct at 260°C and 1000 psi constant stress. Note the presence of numerous loops near the light dislocation tangle

Jan 1, 1970

By J. L. Lytton, T. E. Tietz

The recovery of flour stress of recrylstallized are-cast molyhdenum after 10 pet prestrain at 150°C was studied for recovery temperatures of 725o 801o and 901oC. The yield phenomenon observed after recovery was such that the yield drop diminished and disappeared as recovery proceeded. A fractional flow-stress recovery parameter fr, was developed and it was shown that, independent of recovery ternperatzwe, equal f, values of about 0.16 produced superposition of stress-strain curves except for the initial yield phenomenon. The activation energy for low degrees oj recovery was found to he 32,600 cal per mole, in close agreement with a reported valzie for difjzdsion of carbon in molybdenum. For values of fr greater than about 0.15 where recovery was thought to predominate over strain aging, the activation energy varied from 43,600 to 82,500 cal per mole and increased with increasing recovery and recovery temperature. A 10 pet pre-strain shifted the ductile-brittle transition temperature, as indicated by tensile elongation, from 10°C. to about -22"C. A 100-hr recovery anneal at 801oC was shown to shift the transition temperature to about —5oC, the major shift occurring during the first hour of recovery. ThE recovery of cold-worked metals is accompanied by changes in the arrangement of the dislocations generated during cold work. In recent years, the use of transmission electron microscopy has allowed direct observation of some of the dislocation configurations formed, such as "tangles", networks, cells, subboundaries, and loops. These observations have recently been reviewed by Keh and Weissmann.' Accordingly, some understanding has been gained concerning the nature of the dislocation rearrangements involved. The relationship between recovery and the decrease of mechanical strength, however, has only recently been explored. Previous efforts of the authors were directed toward investigating the decrease of tensile flow stress of aluminum and Al-1 pet Mg during recovery2 and the effects of concurrent elastic and plastic strain on the flow-stress recovery of aluminum.3 In addition, an investigation of the effect of four different solute additions on the tensile flow-stress recovery of aluminum has been made.4 Many important metals, however, have the bee crystal structure, e.g., iron, molybdenum, tungsten, vanadium, columbium, tantalum, and chromium. These metals might be expected to behave differently during recovery from those with other crystal structures for two reasons. First, the previous and present investigations of aluminum and its alloys have shown that tensile flow-stress recovery is strongly affected by foreign atoms in the lattice. In the bee metals, interstitial impurities are usually present and might be expected to have various effects upon both flow behavior and recovery. For example, heterogeneous yielding might occur during prestraining. The diffusion of these interstitials can also relock dislocations during recovery so that a yield point might be obtained upon restraining (strain aging). Second, some of the bee metals (e.g., iron, molybdenum, and tungsten) undergo the familiar structure-sensitive ductility transition and exhibit brittle fracture at suitably low temperatures. It is of considerable interest to determine the effects of recovery on the transition temperature of such metals. The purpose of the present investigation was to extend our knowledge of flow-stress recovery to the bee metals and to study the effects of recovery on the ductile-brittle transition temperature. Unalloyed recrystallized are-cast molybdenum was chosen as a test material, since it exhibits a well-defined ductility transition near room temperature. As in the previous studies, the degree of recovery was measured in terms of the decrease of tensile flow stress. Prestraining and restraining were carried out at 150°C to avoid the possibility of brittle fracture. EXPERIMENTAL PROCEDURE The are-cast molybdenum sheet used in this investigation was obtained from the Climax Molybdenum Co. of Michigan. It was 0.060 in. thick by 10

Jan 1, 1964

By P. A. Beck, Hsun Hu

It has been known for many years that in cold drawn polycrystalline aluminum the recrystallization texture is practically identical with the deformation texture.l,2,3 V. Goeler and Sachs4 stated that in cold rolled polycrystalline aluminum, too, the deformation texture is retained upon recrystallization. This behavior was interpreted by Dehlinger9 as an indication that each recrystallized grain inherits the orientation of the matrix in which it grew. However, Burgers and Basart showed6 that in deformed aluminum single crystals the orientation of the recrystallized grains strongly deviates from that of the matrix. Barrett demonstrated8 that even in deformed polycrystalline aggregates the local orientation within each deformed grain changes on recrystallization. No explanation has as yet been offered of how the aggregate texture can be retained, while the local texture is everywhere changing. According to Burgers and Louwerse6 the orientation change on recrystallization in compressed and rolled aluminum single crystals corresponds to a rotation around [112] axes lying in the active slip planes and perpendicular to active slip directions. This orientation change was rationalized by them on the assumption that the orientation of the recrystallized grains is determined by the orientation of the available nuclei, and that these nuclei are small fragments of the deformed crystal, rotated in the deformation process. Barrett pointed out,? however, that these assumptions were by no means proven, and that the total volume of material necessary for the nuclei is so small, that it must be available in any orien- tation whatever. It is, therefore, unlikely that an "oriented nucleation" theory could satisfactorily explain the orientation changes in recrystallization of a deformed crystal. Furthermore, in contradiction to Burgers and LOU-werse's conclusions, Barrett's results for the orientation change could be best expressed in terms of rotations around. [Ill] axes. Thus agreement is lacking not only in the interpretations but apparently even in the experimental results contributed by the various investigators. The orientation relationships on coarsening* in a highly oriented polycrystalline matrix were first investigated by Burgers and Basart.5 They produced a fine grained highly oriented matrix by the recrystallization of a compressed or rolled single crystal of aluminum, and studied the orientation relationships in three successive generations of crystals: the "deformation texture" in the single crystal, the recrystallization texture, and the coarsening texture. Burgers24 showed that the preferred orientation of each successive generation was almost always widely different from that of the preceding one, but that the coarse grains often approximately reverted to the orientation of their grandparent, the deformed single crystal. This observation, and the idea that the orientation of the coarse grains is determined by that of the available "nuclei," led to the concept that the coarse grains are nucleated by the remnants of the deformation texture.12,15 On the other hand, Bowles and Boas16 found, in a carefully conducted experiment, that in recrystallized fine grained copper of cube texture coarse grains grow in orientations which can be derived from the orientation of the recrystallized matrix by rotation around a [lll].] direction: the coarsening texture here does not appear to be related in any simple manner to the original rolling texture from which the cube texture had been obtained by recrystallization. It may be assumed that in a recrystallized material, even with a strong texture, there always are present some grains of practically any orientation. These may serve as "nuclei" for the coarse grains, provided that the conditions are favorable for their growth. The existence of a coarsening texture may be considered as an indication that grains with certain relative orientations with respect to the preferred orientation of their neighbors can grow much faster than others. This "oriented growth" theory was briefly suggested by van Arkel, as early as 1936,13 and it was mentioned by Burgers." Recently, C. G. Dunn produced direct

Jan 1, 1950

By C. L. Meyers, A. V. Levy, G. Y. Onoda, R. J. Kotfila

This paper presents the hypothesis that solid-solution hardening of regions in the order of tens of angstroms thick along grain boundaries is the most important mechanism controlling the ductile -brittle transition behavior of poly crystalline bcc refractory metals. Further, a physical model is developed and a general equation is derived to describe the dependence of the solute concentration at grain boundaries on temperature, nominal impurity concentration, thermal treatments, vain size, and prior plastic deformation. Analytical curves of the solute concentration at grain boundaries us temperature, calculated by means of the derived equation, are found to have the same general form as curves of ductility us temperature plotted from experimental data. Senziquantitative relationships between the transition temperature and metallurgical variables can he determined by using the physical model. The room-temperature brittleness of the poly-crystalline refractory metals (tungsten, molybdenum, and chromium) is a result of their high ductile-brittle transition temperatures. Recently studies on single crystals have revealed that, when sufficiently pure, these crystals have much lower transition temperatures than polycrystalline specimens of similar purity.'-3 For example, the transition temperature (measured by reduction in area in tensile tests) for very high-purity tungsten crystals has been reported to be as low as -50°F whereas polycrystalline specimens of similar purity had a transition temperature near 400" ~.' These results suggest that the ductile-brittle transition behavior of these polycrystalline metals can be attributed principally to the influence of grain boundaries on plastic flow and fracture. This paper contains a discussion of the manner in which grain boundaries influence the ductility of the poly-.crystalline bcc refractory metals and proposes that the segregation of impurities to grain boundaries is the most important mechanism for controlling the ductile-brittle transition behavior of these metals. Further, this paper contains an analysis of the effect of the compositional and structural variables on the grain boundary-ductility relationship, and introduces a semiquantitative model that can provide a foundation for more theoretical treatment to describe the influence of these variables on ductile-brittle transition behavior. PHYSICAL MODEL FOR PREDICTING DUCTILE-BRITTLE TRANSITION BEHAVIOR Grain Boundary Segregation of Impurities. Based on their own observations and on theoretical grounds, numerous investigators have suggested that impurities segregate to the grain boundaries. Such segregation would be expected because regions exist where both large and small foreign atoms fit with less strain than within the undistorted crystal structure. Therefore, the concentration of impurities should be higher at boundaries than within the grain body. TO estimate the degree (i.e., the ratio of grain boundary to nominal bulk concentration) to which an interstitial solute tends to segregate at boundaries within a solvent metal, the solubility rather than the size misfit could be used as a guide because solubility expresses the joint effect of both elastic and electronic factors.5 The solubilities of interstitial elements such as carbon, hydrogen, nitrogen, and oxygen are low in the group V-A metals and very low in the group VI-A metals.6 These low solubilities suggest that segregation to grain boundaries should occur for each of these solutes in both refractory metal groups. The difference between the ductility of single-crystal and polycrystalline bcc refractory metals can be described in terms of two distinct effects.4 The first of these is the general observation that grain boundaries hinder slip within grains and slip transfer between grains, and the second is that deformation is more complex in each grain of a polycrystalline specimen than it is in a single crystal. Mc Lean has pointed out, furthermore, that strong slip-hindrance effects at grain boundaries should occur in metals having strong segregation of impurities to grain boundaries. Therefore, the effect of grain boundaries on the hindrance of slip is expected to be the dominating influence on the ductile-brittle transition behavior of these polycrystalline refractory metals. cahn5 has suggested that temperature and solute mobility should influence solute equilibrium segregation at grain boundaries, and Fig. 1 illustrates

Jan 1, 1965