Search Documents

By R. M. Brick

AN increased demand for information in regard to the effect of gaseous elements in steel has accompanied the recognition of the importance of grain size. Attempts to correlate grain-size characteristics with gas con-tent, particularly oxygen in solution or in the form of included metallic oxides, have not been universally successful. Certain definite effects of dissolved gases are recognized; specifically, the role of hydrogen in causing internal cracks or "flakes" and that of nitrogen in preventing excessive grain growth of ferritic chromium steels. When irregular behavior or properties are found in a well-known steel and no definite cause for the abnormality may be assigned on the basis of chemical and metallographic tests, dissolved gases are frequently blamed as the culprits. The solubilities of hydrogen1 and nitrogen2 in pure liquid iron are known but of the ternary systems, iron-alloying element-gas, only the Fe-Si-N3 and Fe-Cr-N systems have received attention and here the study was confined to liquid alloys. Krivobok4 published a curve show-ing the solubility of nitrogen in liquid Fe-Cr alloys but gave no informa-tion on the experimental procedure employed. The considerable experimental work reported on the Cr-N binary alloys has been reviewed by Hansen.5 It is generally agreed that the nitride CrN is a stable phase although the existence of nitrides within limited temperature ranges of stability, viz., Cr3N2 and Cr2N, has been disputed, Adcock6 and others7 have reported a eutectic between Cr and CrN at 1580°C., although the supporting evidence is not complete.

Jan 1, 1940

NEW MEMBERS The following list comprises the names of those persons who became. members during the period Sept. 10, 1918, to Oct. 10, 1918. ADDISON, HERBERT, Vice-pres. and Mgr., Big Horn Collieries Co., 412 Colorado Bldg., Denver, Colo. ALLAN, .ANDREW, JR A. Allan & Son, Harrison, N. J. AMI, HENRY M., Charge of War Metals and Minerals, British Embassy, Washington, D. C. ALTHAR, HOMER C., Mill. Engr., The Lorain Coal & Dock Co., Bridgeport, Belmont Co., Ohio. BASER, JOHN T Pres., J. T. Baker Chemical Co., Phillipsburg, N. J. BARBA, W. P., Lieut. Colonel, Ordnance, U. S. A., 2301 Connecticut Ave., Washington, D. C. BENSON, JOHN PATS Min. Engr., Aurora Cons. Mines Co., Aurora, Nev., BOSWELL, H. F Resident Inspector, Southern Railway System, St. Louis, Mo. BRAUCHER, PETERS., Foundry Mgr., Philadelphia & Reading Ry. Co., Sixth & Perry St., Reading, Pa.

Jan 11, 1918

By Charles W. Tandy, Wm. I. Weisman

Sodium sulfate is an important industrial chemical, being one of perhaps a dozen or so chemical commodities that are produced and consumed in the United States in quantities exceeding one million short tons per year. In recent years over half of the country's production of sodium sulfate has come from natural sources, whereas 20 years ago only 25% was derived from these sources. Production of natural sodium sulfate from various types of deposits is the main source of this chemical in Canada and Mexico, and probably in Argentina, Chile, and the USSR. [Table 1] illustrates the growth in production of natural sodium sulfate in the United States. Mineralogy and Physical Properties Sodium sulfate is widespread in occurrence and is a common constituent of many mineral waters, as well as seawater. Many of the saline or alkali lakes throughout the world contain varying amounts of sodium sulfate. In its natural form it is found as the hydrous salt, mirabilite, commonly called Glauber's salt, and as thenardite, the anhydrous variety. The largest quantities occur in the form of mirabilite. Sodium sulfate is found in varying degrees of purity, from theoretically pure efflorescent crystals of mirabilite to combinations and admixtures of other salts and impurities. It is a common constituent of some brines, and it is from this source that much is extracted commercially. Sodium sulfate is also found combined with other compounds, such as the mineral glauberite, the double salt of anhydrous sodium and calcium sulfate, and blödite, the double salt of sodium sulfate and magnesium sulfate. While these and other minerals containing sodium sulfate are not economically important, they are of interest because of their frequent occurrence. The reader is referred to other publications (Cole, 1926; Dana, 1932; Grabau, 1920) for descriptions of these minerals. Only the two economically important minerals, mirabilite and thenardite, will be described herein. Mirabilite, Na2SO4 • 10H2O, contains 55.9% water of crystallization. It is noted for its efflorescence or spontaneous loss of water. On

Jan 1, 1975

By H. W. Schreiber, G. R. Castle

INTRODUCTION The small mining company faces the dilemma of how to finance the development of its properties. Many of these small companies don't have the financial resources to pay for development costs from their own funds and frequently they do not even have the financial strength to permit them to borrow the money needed for development. A project financing can sometimes be arranged in such a way as to solve this dilemma. A typical project financing will not provide the answer to the "little guy's" problem because most project financings require that the sponsors of the project provide completion undertakings and sometimes other undertakings. These undertakings are often a prerequisite to obtaining financing, and if the sponsor is not financially strong enough to provide the comfort that the lenders require, then the sponsor will have difficulty obtaining financing no matter what undertakings are offered. However, with a little imagination and the right set of circumstances, a project financing can sometimes provide the solution to the small mining company's problem. The Strathcona Sound Project is unusually suited as a case study because the sponsor, Mineral Resources International Limited,(MRI) was able to arrange a project financing for the development of the project even though the lenders probably would not have been willing to loan a similar amount of money direct to MRI based on the full faith and credit of MRI's balance sheet. The way that MRI was able to arrange this financing makes for an interesting story. THE CASE In early 1974, MRI owned 100% of a small to medium sized zinc - lead - silver massive sulfide deposit (Property) located 475 miles north of the Arctic Circle less than two miles from deep water on Strathcona Sound which is a shipping zone in the Canadian Arctic. The Property was situated at a desolate location except for an Eskimo settlement (Arctic Bay) which was about 20 miles west of the Property. In other words, the project required that complete infrastructure would need to be installed in this far northern location. Independent reserve and feasibility studies (Study) had been completed on the Property which confirmed a total of 6,825,000 tons of reserves classified and summarized as shown below on Table I: [ ] These reserves were based on 229 diamond drill holes totalling 58,909 feet and were established on a cut-off grade of 7% zinc and a minimum mining height of seven feet. The overall mining recovery rate was estimated at not less than 85% and not more than 90%. The feasibility study indicated that it would cost an estimated $45,044,000 to develop an underground mine, a concentrator, a town-site, a power plant, storage facility, loading dock, a tailings disposal area and an airstrip on the Property with an annual capacity of 525,000 tons of ore per year. The construction period was expected to take two years and projected capital costs were broken down as set forth below on Table II:

Jan 1, 1985

By Kenneth K. Humphreys, Joseph W. Leonard, Robert L. Llewellyn, William F. Lawrence

INTRODUCTION Cleaning fine coal sizes utilizing air currents in machines as the primary separating medium is called dry concentration or pneumatic cleaning. In 1947 approximately 18 million tons (16.38 million mt) of bituminous coal were cleaned by air machines; in 1965, 25.4 million tons (23.1 14 million mt); but in 1975, only 7 million tons (6.37 million mt). Table 11-1 shows the tonnages cleaned of bituminous coal and lignite in the United States by various types of equipment from 1938-1963. Table 11-2 shows only tonnages cleaned by pneumatic methods from 1964-1975. The decrease in tonnage to approximately 7 million tons (6.3 million mt) is due to a higher moisture content in the mined coal and the greater difficulty in cleaning the coal by air. There also was a definite trend to load raw coal at the mines, especially the slack which is the most expensive to clean due to the dewatering and drying requirements. While there have not been any applications of pneumatic cleaning in the anthracite field, its use has not been fully explored. The same is true for lignite and subbituminous coals.

Jan 1, 1979

By Joseph Daniels

The Fritz Engineering Laboratory was built under the direction of John Fritz, and presented by him to the University. A view of the building, looking east, is shown in Fig. 1. The building was started in 1909, and completed in 1910, although all of the equipment was not placed until later. Mr. Fritz gave his personal attention to the details of construction and equipment, and it was his custom to drive over every day to the University from his home in Bethlehem and spend some hours watching the work, offering suggestions, making changes, and planning new work. The result is a building and an equipment which embody his practical ideas. The laboratory structure is of the steel mill-building type, of light-colored brick, 91 by 114 ft., of which a section is shown in Fig. 2 and the floor-plan in Fig. 3. The steel frame carries the roof and traveling crane-way. Ample light has been provided by numerous windows in the side and end walls, in the clerestory, and by a skylight 84 ft. long and 9 ft. wide in the north roof. The main aisle of the building is 49 ft. 2 in. between centers of crane-columns, and has a clear height of 40 ft. The remainder of the width is taken up by two side aisles, 18 ft. high. The laboratory consists of four sections: (1) A general testing-section containing the testing-machinery, a small machine shop, and an office; (2) a cement-testing room; (3) a room for making and storing concrete test-specimens; (4) a hydraulic section.

Jan 1, 1912

By Franz Wever

ACCORDING to Tammann,1 the explanation of the effect of mechanical deformation in producing changes in the properties of metals is one of the most important problems of physical metallurgy, taking rank with the study of the constitution of alloy systems; and this problem has long attracted-the attention of practitioner and scientist alike. Its solution was not advanced materially until Tammann2 set up his translation hypothesis with its crystallographic basis, while other hypotheses, such as the amorphous metal hypothesis of Beilby3 and Rosenhain,4 have been shown by more intensive studies to be less and less satisfactory. The principles of the Tammann translation hypothesis have proved to be useful even up to today and in spite of all of the recent accumulation of experimental data, while the differences of opinion which have arisen relate to the extent to which the hypothesis accounts for the observed changes in properties and to what extent further assumptions are necessary. Stimulated by the proposals of Tammann, there soon developed a lively experimental activity which aimed at the elucidation of the structural or crystallographic changes produced by the mechanical deformation of metals. Parallel movements of crystal "blocks" along definite crystal slip planes had already been observed by lowing and Rosenhain5 in 1900, in metals which had been moderately deformed but without shedding light on the crystallographic nature of the processes accompanying more severe deformation. The solution of this important problem was not advanced until a much later date, or until the methods of X-ray crystal analysis had become available. Shortly after the discovery of the diffraction of X-ray by crystals, symmetrical diffraction effects were

Jan 1, 1931

NEW MEMBERS The following list comprises the, names of those persons who became members during the period June 10 to July 10, 1914: Members ALDRICH, HAROLD W., Supt. of Leaching Plant, Washoe Red. Wks., Anaconda Copper Co., Anaconda, Mont. AYER, FRANK ASHTON, Mine Foreman.. ..Detroit Copper Co., Morenci, Ariz. BELL, ARTHUR F. L., Chief Engr., Associated Oil Co.., 817 Sharon Bldg., San Francisco, Cal. BERGMAN, JULIUS GUSTAF, Mech. Engr., Chief Draftsman, Arizona Copper Co. Morenci, Ariz. BURT, CURTIS F., Min. Engr., Pittsburg-Dolores Mining Co., Rockland, via Yerington, Nev. CALLAWAY SCOTT DAVID, Chem La Harpe Smelter Co., La Harpe, Kan. CAMPBELL, W. C., Min. Engr 4 Princess St., Roodeport, Transvaal, So. Af. CARROLL, GEORGE A., Genl. Mgr Kildare Min. Co., Manson, B. C., Canada. CARUTHERS, JOHN LYTLE, Min. Engr., Asst. Engr., St. Louis, Rocky Mountain & Pacific Co.. Raton. N. M.

Jan 8, 1914

By C. M. Schwartz, A. E. Austin, W. B. Wilson

High-temperature X-ray diffraction studies were conducted with Th-U alloys with up to 10 wt pet U. The solid solubility of uranium in thorium as a function of temperature was determined by the method of lattice parameters. Thorium will dissolve up to 2.5 wt pet U at 950°, 4.5 wt pet U at 1150°, and 7.5 wt pet U at 1250°C. Determinations were made of the temperature of the transition of thorium and of the effect of uranium upon the transition. The a to ß transition for thorium was observed to occur at 1330' ±20°C. Mean coefficients of expansion were calculated for thorium and two alloys, and for ThO2 in contact with the thorium, using X-ray lattice-parameter data. Values obtained at 950° C for thorium and Tho2 were 12.1 and 9.40 X 10-6 per OC, respectively. Impurities obtained during the X-ray exposure were identified by diffraction and were essentially Tho2 and ThC, with two additional unknown phases being detected. The effect of the impurities upon the results is discussed. DIRECT investigation (i.e., high-temperature X-ray diffraction studies) of the phase diagram of thorium-rich uranium alloys has been shown to be necessary since recent work1 - has disclosed the presence of an allotropic transformation near 1400°C in pure thorium with the room temperature face-centered-cubic phase transforming to a body-cen-tered-cubic structure at the elevated temperature. The effect upon the transition of the addition of uranium to thorium and of the solubility of uranium in thorium at high temperatures remained unknown, yet was of interest in understanding fabrication procedures and elevated temperature use. The present work was undertaken to provide information in this area by determining the transition temperature, the effect of uranium on the transition temperature, and the solubility of uranium in thorium as a function of temperature. Experimental Work The high-temperature diffraction data were obtained using a camera especially designed for the purpose3 and capable of reaching temperatures in excess of 2000°C at pressures as low as 1 x 10." mm Hg. Temperature regulation was provided by regulating the power input to ±0.1 pet variation, and by regulating the water flow through the camera jacket to provide a constant thermal load. The X-ray sample was a rod nominally 80 mil diam, which was further turned down to 20 mil and then etched to 18 mil over 1/2 in. of one end. This was placed in the sample holder and mounted on the camera so that the smaller part was surrounded by a cylindrical tantalum-sheet radiation-type heating element. Diffraction from the sample was recorded on film after passing through a slot in the heating element and radiation-baffle shield and through beryllium vacuum windows. The X-ray film mounting was of the Straumanis type4 with a camera diameter of 114.59 mm. Since previous work of Chiotti' indicated that impurities considerably alter the transition temperature, chemical analysis of the arc melted iodide crystal-bar thorium samples was obtained prior to testing. The analysis disclosed the material to contain as low as 0.001 ±0,0002 wt pet H and 0.007 ±0.001 wt pet 0. Carbon was 0.003 wt pet and nitrogen less than 0.002 wt pet. This material was sealed in mild steel in an inert atmosphere and subsequently hot rolled to 3/8-in. diam rods at a temperature of 732°C. Following removal of the jacket, the material was pickled and cold swaged to 1/8-in. rods, from which the diffraction samples were prepared. The alloys were similarly prepared, with the uranium being added during arc melting. The uranium analyses of the alloys prepared appear in Table I. The experimental procedure for diffraction examination of the three samples of high-purity thorium differed from those of the Th-U alloys. The original practice, later modified, consisted of pumping down the camera with the diffusion pump on and then admitting liquid nitrogen to the cold trap of the system. This was modified for the Th-U alloys by maintaining liquid nitrogen in the cold trap at all times before and while the diffusion pump was heated. This minor change produced a reduction in the amount of carbon pickup by the sample during exposure to the diffusion-pump vapors. The sample was brought to the desired test temperature and exposed for 21/2 hr at pressures which were usually 2 x 10-6 mm Hg, or lower. Exposures were made at

Jan 1, 1959

By Z. T. Bieniawski

Tunneling in coal mines includes driving the main haulageways or roadways which serve as the development entries. Although constituting the lifelines of these mines, little attention has been paid to development entries in the United States in terms of systematic pre-construction planning and design. Coal mine tunnels, as the terminology is used in Europe and elsewhere, are understood in the United States to be the main development entries, either in room-and-pillar mining or in longwall mining. These development entries are not tunnels in the traditional sense since they usually are of a multi-entry type involving entries and cross-cuts, and their intersections. Thus, the design of coal mine tunnels is intertwined with the design of coal pillars. This paper summarizes the results of a three-year research project aimed at improving the design of development entries in U.S. coal mining. A design approach has been developed for this purpose and design procedures for roof support in main entries and for pillar sizing are proposed.

Jan 1, 1984

Jan 1, 1913

By Y. C. Liu, H. Margolin

Investigation of martensite habit plane in water-quenched Ti-Mn alloys was carried out in the range of manganese contents between 4.35 and 5.25 pct. On the basis of 22 measurements, the poles were observed to fall into two groups, indicating the existence of two habit planes. The Miller indices of the poles close to these two groups were found to be <334>ß and <344>ß. TITANIUM has an allotropic transformation at 882.1° ± 0.5C1 by which the high temperature ß (body-centered cubic) phase changes to a (hexagonal close-packed) phase. It is well known, as in the case of low carbon steel, that the unalloyed high temperature ß phase cannot be retained no matter how rapid the cooling rate. However, the addition of alloying elements usually lowers the transformation temperature continuously and stabilizes the ß phase to a temperature much lower than the allotropic transformation temperature in pure titanium. A typical example of this behavior is found with manganese-alloying of titanium. Fig. 1 shows the titanium-rich Ti-Mn equilibrium diagram as established by Battelle Memorial Institute.&apos; The addition of manganese lowers the ß transus line and the eutectoid reaction takes place at 550°C, the eutectoid composition being 20 wt pct Mn. However, upon quenching to room temperature from the ß field, the ß phase can be completely retained with much less manganese, see Fig. 2. If the composition is less than that required to stabilize the ß phase completely, a plate-like structure, similar to that of martensite in other alloy systems, appears as shown in Fig. 3. Much lower alloying content merely intensifies the amounts of these transformed structures, as shown in Fig. 4. This paper presents the results of an investigation of the habit plane of these martensitic structures in Ti-Mn alloys. Experimental Procedure Investigation of the pole of a given platelet was made using the two-surface method of analysis." In order that a given martensite trace on two surfaces be readily recognized both at low and high magnifications, it is desirable that only a small amount of martensite be present. From a review of the data obtained at Battelle Memorial Institute4 on quench hardening in Ti-Mn alloys and the results of Duwez" on transformation in Ti-MO alloys, it was decided that the most appropriate Ti-Mn composition for this study would be about 6 pct Mn. A group of alloys containing from 3 to 10 pct Mn was made to bracket this composition. The choice of the 6 pct alloy was apparently proper, since it was later learned that approximately 5.5 to 6 pct Mn is required to stabilize the ß phase on water quenching.

Jan 1, 1954

By P. Pollard

A method has been developed for evaluating acid treatments in fractured limestone fields by breaking down pressure drawdown into three component parts: (I) pressure differcntial across "skin" near the borehole face, (2) pressure differential due to flow resistance in the coarse communicating fissures and (3) pressure differential between the fine voids and the coarse fissures. It is apparent that in most successful acid treatments the first term, skin resistance, has been reduced or eliminated. Further, it is often possible to estimate the volume of coarse fissures associated with the second term, coarse fissure flow resistance. In cases where this volume is comparable with practical acid volumes it seems likely that this resistance also may be attacked with a suitably retarded acid. INTROD UCTION Acid treatment has been successfully applied as a general practice in the limestone wells in the Mara/ Maracaibo districts of Venezuela for some 10 years. At the same time the need has been felt for a more precise method of: (1) evaluating the effect of an acid job and (2) selecting wells which should benefit from an acid treatment. The following method, based on an analysis of build-up curves for wells producing from fractured limestone, provides a means of forecasting the effect acid will have on a well and in many cases the probable order of production rate increase which may be expected. In certain cases it is also possible to calculate the fissure volume through which the acid has to be displaced for best results. Various approximations are introduced in the method, but within the limitations of these the analysis gives an indication of how a well, whether previously acidized or not, may be expected to respond to acid treatment. Suitable build-up curves cannot be obtained on "tight" wells which do not give sustained production and the method is not applicable to such wells. Figs. 1 through 7 illustrate various types of build-up curves obtained from limestone wells in Western Venezuela. Curves are included showing (1) both skin and coarse fissure resistance, (2) skin resistance only, (3 and 4) reduction of skin resistance by acidization, (5) fissure resistance only, (6) reduction of coarse fissure resistance by acidization, and (7) acidization failure. This theory has been successfully applied for over three years during which 22 acid treatments have been carried out specifically to reduce skin resistance and three treatments to reduce coarse fissure resistance. The method has been found to be a useful aid in the selection of wells for acidization.

By Bernard Moore

THE last few decades have witnessed the introduction of many new nonmetallic mineral products and changes in the use of many of those already well known. Among these is diatomite, formerly employed as a mild abrasive and, at one time, as the absorbent material in dynamite. Now nearly 100,000 tons a year are mined and milled into such things as filter aids, cement admixtures, insulants, fillers, absorbents, cosmetics, cleansers, etc. Pumice, commonly regarded as only an abrasive, is now also employed as an insulant, as light-weight aggregate and as a concrete admixture. With increasing use of insulants, light-weight aggregates, and acoustic stuccos and plasters in the building trades, both these mate-rials should find increased application. Very large deposits occur in eastern Oregon and have been studied by the U. S. Geological Survey in cooperation with the Oregon State Mining Board.

Jan 1, 1934

By J. W. Freeman, E. E. Reynolds, A. E. White

Fram a study of 63 systematic alloy modifications it was found that molybdenum, tungsten, and columbium, added individually or simultaneously, and increases in chromium cause major improvements in 1200°F rupture strengths of Cr-Ni-Co-Fe base alloys. Rupture strengths were a function of the effect of composition modifications on both the inherent creep resistance and the amount of deformation the alloy would tolerate before fracture. THIS paper describes the results of an investigation of a series of alloys with systematic variations of the chemical composition of the following basic alloy: C, 0.15: Mn, 1.7; Si, 0.5; Cr, 20.0; NI, 20.0: Co, 20.0: Mo, 3.0; W, 2.0; Cb, 1.0; N, 0.12; Fe, 32.0 pct. The 62 modifications of this alloy were produced under conditions which minimized all factors influencing properties at high temperatures except composition. Melting, fabrication, and heat treatment were carefully maintained constant. Stress-rupture properties at 1200°F were used as the primary criteria of evaluation of the alloy. The objective of the study was to obtain data for determining the fundamental role of the influence of alloying elements on properties of heat-resistant alloys at high temperatures. In addition the results should be useful in determining optimum chemical compositions, the sensitivity of properties to variations in composition, and the degree to which alloy content could be reduced while retaining worthwhile properties. It is difficult or impossible to develop correlations between properties at high temperatures and systematic variations in chemical composition from published data for wrought heat-resistant alloys developed for gas turbines.&apos; &apos; The main reason for this is the extreme dependence of the properties on conditions of treatment of the alloys." In most cases variation in final treatments between alloys so influences the properties that the influence of chemical composition is obscured. In addition it is recognized Table I. Basic Alloy and Some Modifications Used Basic AllOy, Variations in Element Pct Composition, Pct C 0.15 0.08. 0.40. 0.60 Mn 1.1 0.03,0.25.0.50,1.0,2.5 S1 0.50 1.2, 1.6 Cr 20.0 10, 30 Ni 20.0 0, 10,30 Co 20.0 0. 10, 30 MO 3.0 0. 1.2.3, 5, 7 W 2.0 0, 1, 5, 1 Cb 1.0 0.2,4,6 N 0.12 0.004, 0.08, 0.18 Fe 32.0 that variations exist between heats of the same alloy which are related to melting practice and that there is a strong possibility that conditions of hot working influence response to final treatments. The development of heat-resistant alloys has been based on the gradual accumulation of data roughly related to composition from extensive testing programs. There is every reason to believe that in most cases the optimum compositions have been achieved by this procedure in the alloys commercially available. There are, however, very little data showing the influence of systematic variations of composition free from the influence of other factors, particularly for alloys of the type investigated. Several investigators of cast alloys have demonstrated compositional effects, notably Grant,1-6 Epremian,t Guy,8 and Harder and Gow.9 Sykes10 eviewed the work on the wrought alloy Rex 78 and the systematic variations of carbon, copper, molybdenum, and cobalt leading to the development of the stronger Rex 337A alloy. From the papers by Wilson11 and Henry12 it is possible to deduce the beneficial effect of substituting cobalt for iron in 0.45 pct C-20 pct Cr-20 pct Ni-4 pct Mo-4 pct W- 4 pct Cb alloys. Wilson mentioned but did not present the extensive compositional studies involved in developing these alloys. Binder" showed optimum properties for 3, 2, and I pct, respectively, for molybdenum, tungsten, and columbium in 20 pct Cr-20 pct Ni-20 pct Co-30 pct Fe alloys for limited systematic variations of these

Jan 1, 1953

By Gerald G. Griswold, James O. Greenslade, Cherie Tilley, Richard Reseigh

INTRODUCTION The Harrison Western Corporation, a leading Denver based mine contracting and engineering concern, is presently engaged in sinking two 1,006 m (3,300 ft) shafts for the Phillips Uranium Corporation at their Nose Rock Project, approximately 13 miles northeast of the small community of Crownpoint in McKinley County, New Mexico. The Nose Rock Project is the first attempt by the Phillips Uranium Corporation to tap the deep uranium reserves in what has become known as the Grants Mineral Belt. (See Figure 1) Project Description Phillips Uranium Corporation&apos;s plan for the large 2700 metric ton per day (2950 tons/day) mining facility calls for a series of deep access and ventilation shafts ranging from 4.27 m (14 ft) to 5.49 m (18 ft) in diameter to approximate depths of 1,006 m (3,300 ft). The initial pair of shafts consists of one production shaft and one ventilation shaft separated by a distance of 91 m (300 ft). The interbedded layers of sedimentary sandstones and shales to be penetrated by the shafts contain several major water producing aquifers, the deepest being the mineralized zone called the Westwater Canyon Member of the Morrison Formation. A series of temporary and permanent water pumping stations is planned. Generally, the temporary stations are located above major aquifers to facilitate water removal while sinking through the aquifer and the permanent stations constitute what, in the final mode, will be the mine dewatering system. In addition, Phillips Uranium Corporation has In- stalled and is maintaining a system of depressurization wells that temporarily pump the major aquifers and considerably reduce the water inflows during shaft construction. The major aquifers are also chemically grouted prior to sinking. Site work for the project was initiated in the fall of 1976. Full scale shaft sinking commenced in November of 1977 on the 4.88 m (16 ft) diameter ventilation shaft and on the 5.49 m (18 ft) production shaft by another contractor. Harrison Western Corporation began work on the project on November 4, 1979 wlth the production shaft at a depth of 633 m (2,076 ft) and the ventilation shaft at a depth of 474 m (1,554 ft). This paper will address only the portion of shaft sinking completed by Harrison Western. Geology and Hydrology The Nose Rock Project is located on the Chaco Slope in the southern extreme of the San Juan Basin in northwest New Mexico. The southern San Juan Basin is generally bound by the Defiance Uplift to the west, the Zuni Uplift to the south and the Nacimiento Uplift to the east. The Grants Mineral Belt occupies most of the southern portion of the San Juan Basin and this project is located on the northern extreme of the Grants Mineral Belt. The San Juan Basin is comprised of sedimentary rock of continental, marginal-marine and marine origin, that dip northward from the Zuni Uplift and Chaco Slope into the interior of the San Juan Basin. (See Figure 2) Major Formations The major geologic formations to be penetrated range from mudstone and shales to siltstones and sandstones. The sandstones are highly productive aquifers which, under static conditions, would flow artesian. Water temperatures in the aquifers are high and therefore are a force to be dealt with. Temperatures range from 18ºC (65OF) in the upper aquifers to 48ºC (118º&apos;F) in the lower. The mudstones are generally bentonitlc. (See Figure 2) GALLUP SANDSTONE: The Gallup Sandstone is the first major regressive wedge in the San Juan Basin of the Cretaceous era and at this project is about 35 m (115 ft) thick. It is medium grained and prior to depressurization carried a hydrostatic water pressure of over 72.5 kg per cm2 (1,031 psi) which 1s artesian. Compressive strength ranges from 334.7 kg per cm2 (4,760 psi) to 421.8 kg per cm2 (6,000 psi). Water temperature is approximately 30°C (86°F).

Jan 1, 1982

By D. E. Light, J. Y. Somnay

The use of alkyl acid phosphates and their alkali salts as collectors for the uranium minerals brannerite and uranothorite was investigated. In particular a detailed flotation study was carried out using isooctyl acid phosphate as a promoter. Tests were conducted on an Elliot Lake ore analyzing 0.11% U 3 O 8, chiefly as brannerite, and approximately 9% pyrite. Pyrite was floated with conventional reagents; the flotation of brannerite from the sulfide tails was studied to determine the optimum pH and pulp density to employ with isooctyl phosphate. 4 uranium recovery of over 90% was possible with a selectivity index of 8.95 when these tails were floated at 17% solids and a pH of 1.7. The effect of various modifying agents was also investigated. Aluminum sulfate, lactic acid and sodium silicate improved the selectivity of collection yielding selectivity indices of 9.5 to 11.5. Ferric chloride was found to be a depressant for brannerite. A Bancroft ore which analyzed 0.13% U308, and contained uranothorite was also amenable to flotation using isooctyl acid phosphate. The composite uranium concentrate obtained assayed 0.41% U308 at a recovery of 95.3% and a ratio of concentration of 3.24. Previous investigations1,2 on the flotation of brannerite, pitchblende, uraninite and/or uranothorite from various Canadian ores showed that fatty acids, including oleic acid and tall oils, petroleum sulfo-nates and alkyl acid phosphates, were suitable collectors for these uranium minerals. Additional work carried out by the Mines Branch in Ottawa on brannerite ores from the Elliot Lake area3 used the tall oil Acintol FA-1, or FA-2, as a collector. A recovery of 92% of the uranium in a concentrate which contained about 55% of the weight and assayed 0.2% U3O8 was obtained from a feed of 0.1% U308 in this latter instance. Eigeles et a1.4 carried out flotation on pitchblende ores and found that the most promising results were obtained with alkyl acid phosphates and their alkali salts as collectors. Within the homologous series of alkyl phosphates, the best flotation characteristics were displayed by isooctyl phosphates. Further, isooctyl phosphate derivatives were much less sensitive to hardness forming salts than oleic acid, enabling all flotation tests to be made with tap water. This paper describes tests employing alkyl acid phosphates for the flotation of ores containing brannerite and uranothorite. The flotation work described herein was conducted in conjunction with the development of a leaching process for Elliot Lake, Ontario, brannerite ores. In this process pyrite in the ore was concentrated by flotation and roasted, providing sulfur dioxide which was used to produce sulfuric acid in situ in a liquid-solid extraction process. A 40% conversion to sulfuric acid was indicated at a leaching temperature of 80°C; this resulted in the extraction of 93% of the total uranium after a contact period of 6 hr. A rotary kiln was used as a leaching vessel. Preconcentration by flotation was studied in conjunction with the above process to reduce the bulk of solids for leaching and, consequently, capital expenditure. The materials and methods used in this study will be described initially. Then the results will be presented in two sections, the first dealing with the brannerite ore, and the second with the uranothorite. Finally an economic analysis of the results on the brannerite material will be made. MATERIALS AND METHODS The two ore samples examined were from uranium-producing mines. One was a brannerite ore, a uraniferous quartz pebble conglomerate from the Elliot Lake area, which contained 0.11% U3O8, 4.3% S and 4.5% total Fe. Mineralogical studies of similar samples indicated the presence of quartz, microcline, sericite, pyrite and minor quantities of rutile, pyrrho-tite and zircon. The other ore was from a biotite-rich pegmatite in the Bancroft area; feldspar, quartz and biotite formed the major gangue components. Uranothorite was the principal uranium mineral; the head assay was 0.13% U 3 O 8. Preparation of Feed: The ores were crushed to —10

Jan 1, 1963

Sec. 1. The membership of the Institute shall comprise six classes, namely: 1. Members; 2. Honorary Members; 3. Senior Members; 4. Associates; 5. Junior Members; 6. Rocky Mountain Members. All shall be equally entitled to the privileges of membership, excepting that no member of any class whom residence shall be outside of the United States of America, except those residing in Mexico and Canada, shall be entitled to vote. SEC. 2. Members: A person to be eligible for election or transfer into the claw of Member must be at least 27 years of age and must have had at least six years&apos; employment in the practice of engineering, mining, geology, metallurgy, or chemistry, during at least three years of which he must have held positions of responsibility in one or more of these fields. This shall not apply to Rocky Mountain members.

Jan 1, 1944

By N. J. Grant, D. Carne, J. B. Seabrook

IT is unnecessary to review much of the literature on hydrogen embrittlement of steel since several excellent reviews and bibliographies exist.1-3 Hot acid pickling and cathodic charging have been known to cause hydrogen embrittlement of steel and have been used as laboratory methods to charge steels with hydrogen.4-8 Experimental Procedure The problem of prime concern in all instances, except in the work of Sims and coworkers,10 is that at no time was there a definite known hydrogen value reported which could be related to a particular value of the degree of embrittlement. It was the purpose of this research to determine the relationship between hydrogen content and degree of em-brittlement quantitatively. The 1020 stock used for the specimens was hot-rolled 7/16 in. diam rod of the following analysis: 0.19 pct C, 0.40 pct Mn, 0.012 pct P, 0.036 pct S&apos; Vacuum-fusion analyses for nitrogen and oxygen gave 0.014 pct O2 and 0.0011 pct N2. Cathodic charging was used to cause embrittle-ment. The advantages of this method were that no quenching was necessary, the impregnation was reasonably controllable, and representative samples for analysis could be prepared simultaneously with the charging of the tensile bars. Analyses for hydrogen were made in a vacuum-fusion type of apparatus which extracted gas from the samples by fusion in a molten tin-iron bath&apos; This apparatus, which has recently been described in detail elsewhere, will not be discussed here.". " Consecutive samples can be analyzed every 15 min with an accuracy of 0&apos;03 ppm. A A from an electrolytic or pickling bath can be charged for analysis in about 3 min, and analysis completed in 15 min. Samples of as-received 1020 stock were analyzed and found to contain a negligible amount of hydrogen (0.06 ppm). Preliminary pickling and electrolytic charging gave highly variable results. Cold-worked samples showed higher values but ranged from 0.6 to 6.0 ppm of hydrogen. Charging at 90°C gave higher values of charged hydrogen, but troublesome films on many of the specimens resulted. It was not until a few drops of a catalytic poison, prepared from 2 g of yellow phosphorus dissolved in 40 ml of carbon disulphide,8 was added to the electrolytic cell that fairly consistent high values of hydrogen could be charged into the as-received 1020 steel at room temperature. The cell used is sketched in fig. 1. The anode and fixture for the tensile specimens were fastened to the cell cover as shown, and the specimen was screwed in place, centrally located with respect to the anode. At first, anodes of lead and graphite were tried, but they contaminated the electrolyte and gave a slight deposit on the specimen. Later, a platinum wire was used in the form of a uniform helix. A current of 2 amp, corresponding to about 0.5 amp per sq in. of cathode, was used for most specimens. The electrolyte was 4 pct H2SO4 solution. Fig. 1 shows the form of the special tensile bar, the main portion of which was an ordinary 1/4 in. diam, 1 in. gauge length test bar, except that two to four small cylinders of stock were left attached by small links to the bottom end of the tensile bar for the purpose of providing samples for hydrogen analysis. Thus the bars and samples were charged with hydrogen simultaneously and an analysis could be made while the bar was being tested mechanically. Experiments were performed to determine how representative the test cylinders were of the middle of the test bar proper. While the bar center was being analyzed, the small cylinder was stored in dry ice, since it had been shown that such storage prevents loss of hydrogen for many hours.12 The results of these checks are shown in table 1. The checks are very good (0.3 ppm) and indicate that it is permissible to use the small end cylinders to establish the hydrogen content of the tensile test bar proper-

Jan 1, 1951

By Sidney Powers

CONTENTS PAGE Distribution of fields 4 History of development 6 Origin of oil 7 Structure,, accumulation and migration 8 Reservoir rocks 9 Methods of drilling and exploration to Oil-field statistics 12 Description by regions: United States: Appalachian region 12 East-central states 17 Kansas 18 Oklahoma 19 Texas 24 Arkansas 32 Louisiana 33 Mississippi -.. 34 Rocky Mountain region 34 California : 37 Canada 41 Mexico 43 Cuba 46 Bibliography 46 THE purpose of this brief account of the occurrence of petroleum in North America is to make available to those who have a knowledge of geology, but who are not engaged in the petroleum industry, a few salient facts about the location of oil and gas fields, their productivity, the important structural types of accumulation and the age of the rocks containing petroleum. A few useful data and statistics are furnished, yet not complete statistics that are available elsewhere. Geology has been treated in simple terms because the reader is presumed to have little interest in the names of formations and of oil sands. Mineral deposits are more or less analogous. Whether oil or metals, minerals are found in rocks, largely in sedimentary rocks which carry water or have at one time carried it. A genetic or accumula-

Jan 1, 1931